Patent Grant
11905207
The present invention relates to glass ceramics and glasses which contain europium and are suitable in particular for the production of dental restorations, the fluorescence properties of which largely correspond to those of natural teeth. The invention also relates to a process for the preparation of the glass ceramics and glasses according to the invention as well as their use as dental material and in particular for the preparation of dental restorations.
Glass ceramics are used in dentistry because of their good mechanical and optical properties in particular for the production of dental crowns and small bridges.
It is known from W. Buchalla, “Comparative Fluorescence Spectroscopy Shows Differences in Non-Cavitated Enamel Lesions”, Caries Res. 2005, 39, 150-156 that, under ultraviolet light, natural teeth exhibit a bluish-white fluorescence with wavelengths in the range of from 400 to 650 nm.
Rukmani et al., J. Am. Ceram. Soc. 2007, 90, 706-711, describe the influence of V and Mn colorants on the crystallization behaviour and the optical properties of Ce-doped lithium disilicate glass ceramics. For the production of glass ceramics, a mixture of the starting materials SiO2, ZrO2, Li2CO3, K2CO3, MgCO3 and Al(PO3)3 with CeO2, V2O3 and MnO2 is produced, the mixture is melted in platinum crucibles at 1500° C., cooled and then subjected to several heat treatments in a tube furnace with an air supply.
EP 0 877 071 A1 and corresponding U.S. Pat. No. 6,010,644, which is hereby incorporated by reference in its entirety, describes glasses and glass ceramics which contain inter alia Eu2O3 ions and exhibit long-lasting phosphorescence.
DE 10 2009 013 377 A1 describes the use of a borosilicate glass which is doped with CeO2 or at least one oxide of another lanthanoid, inter alia Eu2O3, for increasing antiforgery security of a package by emission of electromagnetic radiation in the range between 300 and 700 nm when irradiated with UV light.
WO 2015/173230 A1 and corresponding U.S. Pat. No. 10,131,569, which is hereby incorporated by reference in its entirety, describes a method for the production of a lithium silicate glass or a lithium silicate glass ceramic, in which a melt of a starting glass which contains cerium ions is exposed to reducing conditions. Ce4+ ions contained in the starting glass are thereby said to be completely or partially reduced to Ce3+ ions which, because of 5d→4f transitions, exhibit a fluorescence in the wavelength range from 320 to 500 nm. A corresponding process for the production of a glass ceramic with SiO2 as main crystal phase or of a glass which contains nuclei for the crystallization of SiO2, is known from WO 2017/080853 A1 and corresponding U.S. Pat. No. 10,414,688, which is hereby incorporated by reference in its entirety.
However, it has been shown that the glasses and glass ceramics known from the state of the art have unsatisfactory fluorescence properties and, in particular under UV light, cannot adequately imitate the fluorescence properties of natural tooth material. In particular, the known materials do not exhibit the required fluorescence at all the relevant wavelengths in the UV range. Dental restorations produced from such glass ceramics are thereby recognizable as restorations, in particular under the influence of UV light, or are perceived as missing teeth or defects. Moreover, in the case of the glasses and glass ceramics produced in this way, considerable impairment of the fluorescence properties results through heat treatments under oxidizing conditions, for example during sintering.
The object of the invention is to provide glass ceramics and glasses which, at excitation wavelengths throughout the entire relevant UV range, above all in the range of from 250 nm to 430 nm and in particular in the range of from 360 nm to 430 nm, exhibit fluorescence and are thus suitable in particular for the production of dental restorations which not only have good mechanical properties, but can also largely imitate the fluorescence properties of natural tooth material at excitation wavelengths throughout the entire relevant UV range. In particular, the glass ceramics and glasses should also be suitable as blending components for setting the fluorescence properties of other glasses and glass ceramics.
This object is achieved according to the invention by a glass or a glass ceramic with europium content, which comprise the following components:
It has surprisingly been shown that the glass according to the invention and the glass ceramic according to the invention exhibit improved fluorescence properties compared with the state of the art at excitation wavelengths in the range of from 250 to 430 nm and in particular also at excitation wavelengths in the range of from 360 to 430 nm and these fluorescence properties are, in addition, largely stable towards heat treatments and oxidizing conditions.
Without being limited to a specific theory, it is assumed that an equilibrium between Eu2+ and Eu3+ ions is formed in the glasses and glass ceramics according to the invention. Because of 5d→4f transitions, the Eu2+ ions exhibit a fluorescence at excitation wavelengths throughout the entire range of from 250 to 430 nm which is particularly suitable for imitating the fluorescence properties of natural tooth material, in particular in the case of excitation in the UV range.
According to the invention, it is preferred that the glass and the glass ceramic comprise 32.0 to 72.0, in particular 35.0 to 65.0 and preferably 38.0 to 50.0 wt.-% SiO2.
It is further preferred that the glass and the glass ceramic comprise 15.0 to 40.0, in particular 20.0 to 40.0, preferably 25.0 to 40.0 and particularly preferably 30.0 to 40.0 wt.-% Al2O3.
The glass and the glass ceramic preferably comprise 0.1 to 4.0, in particular 0.3 to 3.0, preferably 0.5 to 2.0, more preferably 0.6 to 1.0 and particularly preferably 0.65 to 0.85 wt.-% europium, calculated as Eu2O3.
It is further preferred that the glass and the glass ceramic comprise 8.0 to 30.0 wt.-%, in particular 12.0 to 29.0, preferably 15.0 to 28.0 and particularly preferably 20.0 to 27.0 wt.-% MeIIO, wherein MeIIO is selected from MgO, CaO, SrO and/or ZnO. In a preferred embodiment, the glass and the glass ceramic comprise 8.0 to 30.0, in particular 12.0 to 29.0, preferably 15.0 to 28.0 and particularly preferably 20.0 to 27.0 wt.-% CaO and/or SrO.
Glasses and glass ceramics which comprise at least one and preferably all of the following components in the specified amounts are particularly preferred:
It is furthermore preferred that the glass and the glass ceramic comprise 0 to 10.0, in particular 0 to 5.0 and preferably 0 to 1.0 wt.-% BaO, and most preferably are substantially free from BaO.
In a preferred embodiment, the glass and the glass ceramic comprise 0 to 2.0, in particular 0.1 to 1.2 and preferably 0.3 to 0.7 wt.-% tin, calculated as SnO.
Preferably, the glass and the glass ceramic further comprise 0 to 5.0, preferably 0.5 to 4.0 and preferably 1.0 to 3.0 wt.-% cerium, calculated as CeO2.
The glass and the glass ceramic can further comprise alkali metal oxide MeI2O in an amount of from 0 to 15.0, in particular 0 to 10.0, preferably 0 to 5.0, particularly preferably 0 to 1.0 and most preferably 0 to 0.5 wt.-%, wherein this MeI2O is selected in particular from Li2O, Na2O, K2O, Rb2O and Cs2O and is preferably selected from Li2O, Na2O and K2O. Particularly preferably, the glass and the glass ceramic comprise at least one and in particular all of the following alkali metal oxides MeI2O in the specified amounts:
The glass and the glass ceramic can, furthermore, comprise 0 to 10.0, in particular 0 to 4.0 and preferably 0 to 2.5 wt.-% further oxide of trivalent elements MeIII2O3. The term “further oxide of trivalent elements MeIII2O3” denotes trivalent oxides with the exception of B2O3, Al2O3, Eu2O3 and Ce2O3, wherein this MeIII2O3 is selected in particular from Y2O3, La2O3, Ga2O3 and/or In2O3. Particularly preferably, the glass and the glass ceramic comprise at least one and in particular all of the following further oxides of trivalent elements MeIII2O3 in the specified amounts:
It is furthermore preferred that the glass and the glass ceramic comprise 0 to 3.0, in particular 0 to 2.0 and preferably 0 to 1.0 wt.-% B2O3, and most preferably are substantially free from B2O3.
Furthermore, the glass and the glass ceramic can comprise further oxide of tetravalent elements MeIVO2 in an amount of 0 to 15.0, in particular 0 to 4.0 and particularly preferably 0 to 2.5 wt.-%. The term “further oxide of tetravalent elements MeIVO2” denotes tetravalent oxides with the exception of SiO2, SnO2, CeO2 and TiO2, wherein this MeIVO2 is selected in particular from ZrO2 and/or GeO2. Particularly preferably, the glass and the glass ceramic comprise at least one and in particular all of the following further oxides of tetravalent elements MeIVO2 in the specified amounts:
It is furthermore preferred that the glass and the glass ceramic comprise 0 to 5.0, in particular 0 to 2.5 and preferably 0 to 1.0 wt.-% TiO2 and most preferably is substantially free from TiO2.
Moreover, the glass and the glass ceramic can comprise oxide of pentavalent elements MeV2O5 in an amount of 0 to 6.0 and in particular 0 to 5.0 wt.-%, wherein this MeV2O5 is selected in particular from P2O5, V2O5, Ta2O5 and/or Nb2O5. Particularly preferably, the glass and the glass ceramic comprise at least one and in particular all of the following further oxides of pentavalent elements MeV2O5 in the specified amounts:
In addition, the glass and the glass ceramic can comprise 0 to 6.0 wt.-% oxide of hexavalent elements MeVIO3, wherein this MeVIO3 is selected in particular from WO3 and/or MoO3. Particularly preferably, the glass and the glass ceramic comprise at least one and in particular all of the following MeVIO3 oxides in the specified amounts:
The glass and the glass ceramic can, furthermore, comprise oxides of further f-elements, such as oxides of Pr, Nd, Gd, Tb, Dy, Er and Yb and in particular oxides of Tb and/or Dy.
Furthermore, the glass and the glass ceramic can comprise 0 to 5.0 and in particular 0 to 1.0 wt.-% fluorine.
A glass and a glass ceramic which comprise at least one and preferably all of the following components in the specified amounts are particularly preferred:
wherein MeI2O, MeIIO, MeIII2O3, MeIVO2, MeV2O5 and MeVIO3 have in particular the meanings specified above.
In a further particularly preferred embodiment, the glass and the glass ceramic comprise at least one and preferably all of the following components in the specified amounts:
The glass ceramic according to the invention preferably comprises at least one aluminosilicate as crystal phase and in particular as main crystal phase. In a further preferred embodiment, the glass ceramic according to the invention comprises a calcium aluminosilicate or strontium aluminosilicate or a mixture thereof, preferably a calcium aluminosilicate or strontium aluminosilicate, as crystal phase and in particular as main crystal phase. Without being limited to a specific theory, it is assumed that in the glass ceramics according to the invention Eu2+ ions are incorporated into the crystal lattice of the above-named crystal phases, and the fluorescence properties thereof are thereby further improved and stabilized.
The term “main crystal phase” denotes the crystal phase which has the highest proportion by mass of all the crystal phases present in the glass ceramic. The masses of the crystal phases are determined using in particular the Rietveld method. A suitable method for the quantitative analysis of the crystal phases using the Rietveld method is described e.g. in M. Dittmer's doctoral thesis “Gläser and Glaskeramiken im System MgO—Al2O3—SiO2 mit ZrO2 als Keimbildner” [Glasses and glass ceramics in the MgO—Al2O3—SiO2 system with ZrO2 as nucleating agent], University of Jena 2011.
It is further preferred that the glass ceramic according to the invention comprises at least 5 wt.-%, in particular at least 10 wt.-% and preferably at least 20 wt.-% aluminosilicate as crystal phase, in particular in the form of calcium aluminosilicate, strontium aluminosilicate or mixtures thereof.
The type and the amount of the crystal phases formed can be controlled in particular by the composition of the starting glass used, as well as the heat treatment which is used for the production of the glass ceramic from the glass. The examples illustrate this by varying the composition and the heat treatment used.
The invention likewise relates to precursors with a corresponding composition from which the glass ceramic according to the invention can be produced by heat treatment. These precursors are a glass with a corresponding composition (also referred to as starting glass) and a glass with a corresponding composition with nuclei. The term “corresponding composition” means that these precursors comprise the same components in the same amounts as the glass ceramic, wherein the components with the exception of fluorine are calculated as oxides, as is customary in the case of glasses and glass ceramics.
The invention likewise relates to a glass according to the invention which comprises nuclei for the crystallization of an aluminosilicate and in particular of calcium aluminosilicate and/or strontium aluminosilicate. Through heat treatment of the glass according to the invention, the glass with nuclei according to the invention can first be produced, which in turn can be converted through further heat treatment into the glass ceramic according to the invention, in particular with an aluminosilicate as crystal phase and preferably as main crystal phase.
The glass according to the invention is produced in particular in such a way that a mixture of suitable starting materials, such as carbonates, oxides, phosphates and fluorides, is melted at temperatures of in particular from 1500 to 1800° C., for 0.5 to 10 h, and the glass melt obtained is introduced in water in order to produce a granulate. This granulate can be pressed, after grinding, to form a blank, a so-called powder compact, or processed to form a powder.
The invention is therefore likewise directed to a process for the preparation of the glass ceramic according to the invention, in which the glass, in particular the glass with nuclei, is subjected to at least one heat treatment at a temperature of from 1000 to 1500° C., preferably 1050 to 1450° C., for a duration of in particular 10 to 720 min and preferably 30 to 120 min.
Thus, in a preferred embodiment, the invention relates to a process for the preparation of the glass ceramic according to the invention, in which
A nucleation can optionally be carried out before the heat treatment in step (b).
The melt of the starting glass can optionally be reacted with at least one reducing agent. In principle, all the agents which are able to reduce Eu3+ ions to Eu2+ ions under the conditions of the process come into consideration as reducing agents. Those reducing agents are preferred which can be removed from the glass melt residue-free after the reduction.
In particular, gaseous reducing agents, as well as reducing agents which, after the reduction, are burnt out from the glass melt under the conditions of the process according to the invention, are preferred. Examples of gaseous reducing agents are gases which comprise hydrogen and preferably mixtures of hydrogen and nitrogen. Furthermore, examples of reducing agents are substances which comprise at least one oxidizable carbon atom, in particular carbon, for example graphite, organic salts, carbohydrates and cereal flours.
According to a preferred embodiment, the melt of the starting glass is formed from a glass-forming composition which comprises at least one reducing agent. As the at least one reducing agent, a compound is preferred, which comprises at least one oxidizable carbon atom and is preferably selected from the group consisting of organic salts, carbohydrates and cereal flours. Acetates are examples of particularly suitable organic salts.
In a particularly preferred embodiment, a europium acetate, in particular europium(III) acetate hydrate, is used as reducing agent.
According to a further preferred embodiment, the at least one reducing agent is a reducing gas, wherein the gas preferably comprises hydrogen and preferably comprises hydrogen and nitrogen. Mixtures of hydrogen and nitrogen which comprise about 5 vol.-% hydrogen and are also referred to as forming gas are particularly suitable. The extent of the reduction can be controlled via the amount of the gas supplied and in particular via the flow rate and duration of the gas supply. Preferably, the amount of the effective component of the reducing gas, preferably hydrogen, is 0.05 to 5 l/min, in particular 0.1 to 1 l/min and preferably 0.2 to 0.5 l/min, for a duration of 10 to 180 min, in particular 20 to 120 min and preferably 30 to 90 min.
The invention further relates to a glass according to the invention and a glass ceramic according to the invention, which have a whitish-blue fluorescence in the CIE colour space.
The glasses and glass ceramics with europium content according to the invention are, in particular, suitable as blending components for adjusting the fluorescence properties of other glasses and glass ceramics. A glass or a glass ceramic comprising the glass with europium content according to the invention or the glass ceramic with europium content according to the invention, therefore represent a further subject of the invention. A glass and a glass ceramic are particularly preferred, which comprise the glass with europium content according to the invention or the glass ceramic with europium content according to the invention in an amount of from 0.1 to 50 wt.-%, in particular 0.2 to 40 wt.-%, preferably 0.5 to 30 wt.-%, particularly preferably 1 to 20 wt.-% and more preferably 5 to 10 wt.-%.
The glass with europium content according to the invention or the glass ceramic with europium content according to the invention can in particular be used as component of an inorganic-inorganic composite or in combination with a variety of other glasses and/or glass ceramics, wherein the composites or combinations can in particular be used as dental materials. Particularly preferably, the composites or combinations can be present in the form of sintered blanks. Examples of other glasses and glass ceramics for the production of inorganic-inorganic composites and of combinations are disclosed in DE 43 14 817 A1, DE 44 23 793 C1, DE 44 23 794 C1, DE 44 28 839 A1, DE 196 47 739 A1, DE 197 25 552 A1, DE 100 31 431 A1, EP 0 827 941 A1, EP 0 916 625 A1, WO 00/34196 A2, EP 1 505 041 A1, EP 1 688 398 A1, EP 2 287 122 A1, EP 2 377 831 A1, EP 2 407 439 A1, WO 2013/053863 A2, WO 2013/053864 A2, WO 2013/053865 A2, WO 2013/053866 A2, WO 2013/053867 A2, WO 2013/053868 A2, WO 2013/164256 A1, WO 2014/170168 A1, WO 2014/170170 A2, WO 2015/067643 A1, WO 2015/155038 A1, WO 2015/173394 A1, WO 2016/120146 A1, WO 2017/032745 A1 WO 2017/055010 A1 U.S. Pat. No. 10,457,589, US 2018244563, U.S. Pat. No. 8,759,237, US 2011256409, U.S. Pat. No. 10,501,366, which US patents and published applications are hereby incorporated by reference in their entirety. These glasses and glass ceramics belong to the silicate, borate, phosphate or aluminosilicate group. Preferred glasses and glass ceramics are of the SiO2—Al2O3—K2O type (with cubic or tetragonal leucite crystals), SiO2—B2O3—Na2O type, alkali-silicate type, alkali-zinc-silicate type, silico-phosphate type and/or SiO2—ZrO2 type. Particularly preferred are lithium-silicate glass ceramics and in particular glass ceramics which comprise lithium metasilicate or lithium disilicate as main crystal phase and optionally further crystal phases such as apatite, diopside, quartz and/or wollastonite, as well as glass ceramics which comprise SiO2, in particular in the form of low quartz, as main crystal phase. By mixing such glasses or glass ceramics with the glasses and/or glass ceramics with europium content according to the invention, the fluorescence properties can in particular be set as desired.
The glass ceramics according to the invention and the glasses according to the invention, in particular in the form of composites and combinations, are present in particular in the form of powders, granulates or blanks in any shape and size, e.g. monolithic blanks, such as platelets, cuboids or cylinders, or powder compacts, in unsintered, partially sintered or densely sintered form. In these forms, they can easily be further processed, e.g. to form dental restorations. However, they can also be present in the form of dental restorations such as inlays, onlays, crowns, partial crowns, bridges, veneers, facets or abutments.
Dental restorations, such as inlays, onlays, crowns, partial crowns, bridges, veneers, facets or abutments, can be produced from the glass ceramics according to the invention and the glasses according to the invention, in particular in the form of composites and combinations. The invention therefore relates to the use thereof as dental material and in particular the use thereof for the preparation of dental restorations. It is preferred that the glass ceramic or the glass is given the shape of the desired dental restoration by pressing or machining.
The pressing is usually effected under increased pressure and at increased temperature. It is preferred that the pressing is effected at a temperature of from 700 to 1150° C. and in particular 700 to 1000° C. It is further preferred to carry out the pressing at a pressure of from 10 to 30 bar. During pressing, the desired shape change is achieved by viscous flow of the material used. The glass according to the invention and the glass with nuclei according to the invention as well as preferably the glass ceramic according to the invention can be used for the pressing. The glasses and glass ceramics according to the invention can be used in particular in the form of blanks in any shape and size, e.g. monolithic blanks or powder compacts, e.g. in unsintered, partially sintered or densely sintered form.
The machining is usually effected by material-removal processes and in particular by milling and/or grinding. It is particularly preferred that the machining is carried out as part of a CAD/CAM process. The glass according to the invention, the glass with nuclei according to the invention as well as the glass ceramic according to the invention can be used for the machining. The glasses and glass ceramics according to the invention can be used in particular in the form of blanks, e.g. monolithic blanks or powder compacts, e.g. in unsintered, partially sintered or densely sintered form. The glass ceramic according to the invention is preferably used for the machining. The glass ceramic according to the invention can also be used in a not fully crystallized form, which has been produced by heat treatment at a lower temperature. This offers the advantage that an easier machining and thus the use of simpler apparatus for the machining are possible. After the machining of such a partially crystallized material, the latter is regularly subjected to a further heat treatment in order to bring about further crystallization.
The glass ceramics according to the invention and the glasses according to the invention, in particular in the form of composites and combinations, are however also suitable as coating material for e.g. ceramics, glass ceramics and metals. The invention is therefore likewise directed towards the use of the glasses according to the invention or the glass ceramics according to the invention for coating in particular ceramics, glass ceramics and metals.
The invention also relates to a process for coating ceramics, glass ceramics and metals, in which glass ceramic according to the invention or glass according to the invention, in particular in the form of composites and combinations, is applied to the ceramic, the glass ceramic or the metal and exposed to a temperature of at least 600° C.
This can be effected in particular by sintering-on and preferably by pressing-on. In the case of sintering-on, the glass ceramic or the glass is applied in the usual way, e.g. as powder, to the material to be coated, such as ceramic, glass ceramic or metal, and then sintered. In the case of the preferred pressing-on, glass ceramic according to the invention or glass according to the invention is pressed on, e.g. in the form of powder compacts or monolithic blanks, at an increased temperature of e.g. from 700 to 1150° C. and in particular 700 to 1000° C., and with application of pressure, e.g. from 10 to 30 bar. For this, the methods described in EP 231 773 and the press furnace disclosed there can in particular be used. Suitable commercial furnaces are the Programat-type furnaces from Ivoclar Vivadent AG, Liechtenstein.
Because of the above-described properties of the glass ceramics according to the invention and the glasses according to the invention, these are suitable in particular for use in dentistry. A subject of the invention is therefore also the use of the glass ceramics according to the invention or the glasses according to the invention, in particular in the form of composites and combinations, as dental material and in particular for the preparation of dental restorations or as coating material for dental restorations, such as crowns, bridges and abutments.
The invention therefore also relates to a process for the preparation of a dental restoration, in particular an inlay, onlay, crown, partial crown, bridge, veneer, facet or abutment, in which the glass ceramic according to the invention or the glass according to the invention, in particular in the form of composites and combinations, is given the shape of the desired dental restoration by pressing, sintering or machining, in particular in a CAD/CAM process.
The invention is described in further detail in the following with reference to non-limitative examples.
A total of 21 glasses according to the invention were produced with the compositions specified in Table I, wherein the oxidation states of the specified oxides relate to the oxidation states of the raw materials used. The glasses were crystallized to form glass ceramics according to Table II. Herein,
Tg denotes glass transition temperature, determined by means of DSC
Ts and ts denote temperature and time used for melting
TSinter and tsinter denote temperature and time used for sintering.
In addition, the glasses or glass ceramics according to Table III were mixed with further glasses and sintered to form glass ceramic bodies.
A) Preparation of Glasses According to the Invention
In the examples, starting glasses with the compositions specified in Table I were first melted on a scale of from 100 to 200 g from usual raw materials at the temperature Ts for a duration ts. Glass frits were produced by pouring the molten starting glasses into water. The fluorescence properties of the glass frits thus obtained at excitation wavelengths of 254, 366, 395 and 430 nm were determined visually by means of a UV lamp and are reproduced in Table II. According to this, all the glasses obtained in the examples exhibited a fluorescence, in particular at excitation wavelengths of 366, 395 and 430 nm.
The three method variants B) to D) specified below were used for the further processing of the glass frits:
B) Preparation of Glass Ceramics According to the Invention
In Examples 1 to 13, the glass frits obtained were ground to a grain size of <45 μm in a zirconium oxide mill. About 4 g of these powders were then pressed to form cylindrical blanks and, according to Table II, sintered at a temperature Tsinter and for a holding time of tsinter to form dense glass ceramic bodies, wherein this was effected for sintering temperatures of up to 1200° C. in a vacuum in a Programat®-type sintering furnace (Ivoclar Vivadent AG), and for sintering temperatures above 1200° C. in a normal atmosphere in an LHT 02/16-type sintering furnace (Nabertherm). The fluorescence properties of the glass ceramics thus obtained at excitation wavelengths of 254, 366, 395 and 430 nm, respectively, were determined visually by means of a UV lamp and are reproduced in Table II. According to this, the glass ceramics obtained exhibited a fluorescence, in particular at excitation wavelengths of 366, 395 and 430 nm.
C) Glasses According to the Invention as Blending Components
The glass frits obtained in Examples 14 to 21 were comminuted and sieved to a grain size of <25 μm. The glass powders obtained were added to pulverized lithium silicate glasses according to Table III. In each case about 4 g of these mixtures were then pressed to form cylindrical or disc-shaped blanks and sintered in a sintering furnace (Programat® from Ivoclar Vivadent AG) to form dense glass ceramic bodies. The fluorescence properties of the glass ceramic bodies thus obtained at excitation wavelengths of 254, 366, 395 and 430 nm, respectively, were determined visually by means of a UV lamp and are reproduced in Table III. According to this, all the glass ceramic bodies obtained exhibited a fluorescence, in particular at excitation wavelengths of 366, 395 and 430 nm.
D) Glass Ceramics According to the Invention as Blending Components
The glass ceramics obtained in Examples 1, 2, 4 and 9 and the glass ceramic obtained after sintering at 1110° C. in Example 5 were comminuted and sieved to a grain size of <25 μm. The glass ceramic powders obtained were added to pulverized lithium silicate glasses according to Table III. In each case about 4 g of these mixtures were then pressed to form cylindrical or disc-shaped blanks or to form pressed stubs and sintered in a sintering furnace (Programat® from Ivoclar Vivadent AG) or hot-pressed to form dense glass ceramic bodies. The fluorescence properties of the glass ceramic bodies thus obtained at excitation wavelengths of 254, 366, 395 and 430 nm, respectively, were determined visually by means of a UV lamp and are reproduced in Table III. According to this, all the glass ceramic bodies obtained exhibited a fluorescence, in particular at excitation wavelengths of 366 nm. As crystal phases, calcium aluminosilicates such as anorthite were obtained in CaO-containing compositions, and strontium aluminosilicates such as slawsonite were obtained in SrO-containing compositions.
| Number | Date | Country | Kind |
|---|---|---|---|
| 19157306.2 | Feb 2019 | EP | regional |
This application is a divisional application of and claims priority to U.S. patent application Ser. No. 16/784,824 filed on Feb. 7, 2020, which claims priority to European patent application No. 19157306.2 filed on Feb. 14, 2019, the disclosures of which are incorporated herein by reference in their entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3522191 | Turner et al. | Jul 1970 | A |
| 4102805 | Mizzoni et al. | Jul 1978 | A |
| 5432130 | Rheinberger et al. | Jul 1995 | A |
| 5618763 | Frank et al. | Apr 1997 | A |
| 5698019 | Frank et al. | Dec 1997 | A |
| 5925180 | Frank et al. | Jul 1999 | A |
| 6010644 | Fu et al. | Jan 2000 | A |
| 6204211 | Ohara et al. | Mar 2001 | B1 |
| 6455451 | Brodkin | Sep 2002 | B1 |
| 8047021 | Schweiger et al. | Nov 2011 | B2 |
| 8263508 | Bolle et al. | Sep 2012 | B2 |
| 8759237 | Ritzberger et al. | Jun 2014 | B2 |
| 9321674 | Ritzberger et al. | Apr 2016 | B2 |
| 9402699 | Ritzberger et al. | Aug 2016 | B2 |
| 9403714 | Ritzberger et al. | Aug 2016 | B2 |
| 9688567 | Rampf et al. | Jun 2017 | B2 |
| 9695082 | Ritzberger et al. | Jul 2017 | B2 |
| 9757311 | Rampf et al. | Sep 2017 | B2 |
| 9764982 | Ritzberger et al. | Sep 2017 | B2 |
| 9776912 | Ritzberger et al. | Oct 2017 | B2 |
| 9878939 | Ritzberger et al. | Jan 2018 | B2 |
| 10131569 | Krolikowski et al. | Nov 2018 | B2 |
| 10227255 | Ritzberger et al. | Mar 2019 | B2 |
| 10376343 | Rheinberger et al. | Aug 2019 | B2 |
| 10414688 | Rampf et al. | Sep 2019 | B2 |
| 10457589 | Rampf et al. | Oct 2019 | B2 |
| 10501366 | Ritzberger et al. | Dec 2019 | B2 |
| 20110256409 | Ritzberger et al. | Oct 2011 | A1 |
| 20170119508 | Dittmer et al. | May 2017 | A1 |
| 20180244563 | Dittmer et al. | Aug 2018 | A1 |
| 20190315651 | Rampf et al. | Oct 2019 | A1 |
| Number | Date | Country |
|---|---|---|
| 233427 | Mar 1985 | CS |
| 19647739 | Mar 1998 | DE |
| 19725552 | Dec 1998 | DE |
| 10031431 | Jan 2002 | DE |
| 20041040759 | Mar 2006 | DE |
| 102004040759 | Mar 2006 | DE |
| 102009013377 | Sep 2010 | DE |
| 0827941 | Mar 1998 | EP |
| 0916625 | May 1999 | EP |
| 1688398 | Aug 2006 | EP |
| 2002025040 | Jan 2002 | JP |
| 2002255585 | Sep 2002 | JP |
| 2002260216 | Sep 2002 | JP |
| 1096242 | Oct 1982 | SU |
| 1096242 | Jun 1984 | SU |
| Entry |
|---|
| DE-102004040759-A1 machine translation (Year: 2006). |
| SU1096242A1 machine translation (Year: 1982). |
| Zhang, Yaming et al., “Effect of Added Mullite Whisker on Properties of Lithium Aliminosilicate (LAS) Glass-Ceramics for Dental Restoration,” Journal of Biomedical NanoTechnology. 14.11, 1944-1952. 2018. |
| Ozawa, Lyuji, “Emission and excitation spectra of Eu2O3 compared with Y2O3: Eu phosphor,” Japanese Journal of Applied Physics. 5.8, 740. 1966. |
| Buchalla, W., Comparative Fluorescence Spectroscopy Shows Differences in Non-Cavitated Enamel Lesions, Caries Research, 2005, vol. 39, pp. 150-156. |
| Rukmani, S.J., et al., Effects of V and Mn Colorants on the Crystallization Behavior and Optical Properties of Ce-Doped Li-Disilicate Glass-Ceramics, J. Am. Ceram. Soc., 2007, vol. 90, No. 3, pp. 706-711. |
| Qiu, J., et al., Blue emission induced in Eu2+-doped glasses by an infrared femtosecond laser, Journal of Non-Crystalline Solids, 1999, vol. 244, Nos. 2-3, pp. 185-188. |
| Number | Date | Country | |
|---|---|---|---|
| 20220204383 A1 | Jun 2022 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16784824 | Feb 2020 | US |
| Child | 17694741 | US |