Patent Application
20160199272
The present invention relates in general to protecting and repairing teeth that have been bleached, and particularly to a protective wax coating that maintains, protects, repairs, and preserves bleached teeth prolonging their white appearance.
An embodiment of the invention provides a formulation incorporating sodium fluoride or other fluoride compounds that is particularly beneficial to the health and restoration of tooth enamel.
The public today is concerned about their appearance, youth, and especially about their smile. There is much that has been accomplished in dentistry today that enhances the ability of the teeth to become white as the teeth once were in the persons youth. This can be accomplished by the use of crowns, veneers and bleaching. As a result, cosmetic dentistry has become very popular. Many people would like to have whiter and brighter teeth. As a result whitening or bleaching of teeth has become very common. However, all these means require a substantial investment on the part of the person.
The maintenance of the crowns and veneers, once they have been restored with porcelain, is slight because of the sealed surface of the porcelain. This is not true of natural teeth that have been whitened or bleached. The surface of bleached teeth reveals a surface that is full of cracks and crevices that is the result of the bleaching process. Therefore, these damaged surfaces are able to easily pickup pigments that are in our food, beverages, and habits. Some of these pigments or staining products are; red wine, coffee, energy drinks, tea, lipstick, nicotine from smoking, food with any color. All these things have a tendency to stain and color the teeth that have been bleached. The solution to this is to re-bleach these teeth. The problem is that this will cause further damage to the previously bleached enamel and continual bleaching may lead to serious damage to the teeth and even result in the need for a root canal in order to save them.
Generally, the tooth bleaching process uses a form of hydrogen peroxide which whitens, and oxidizes the enamel of the tooth opening the enamel permitting it to be easily stained. In order to maintain their whiteness teeth must be periodically bleached. Repeated bleaching may potentially damage the enamel of the teeth. Often this damage creates pits and fissures in the enamel resulting in porosity that results in the teeth being more easily stained and discolored.
There have been coatings placed on teeth in an effort to provide a bacteria inhibiting film. One such protective coating is disclosed in U.S. Pat. No. 5,665,333 entitled “Methods, Compositions, and Dental Delivery Systems for the Protection of the Surface of Teeth”, issuing to Homola et al. on Sep. 9, 1997, which is herein incorporated by reference. Therein disclosed is a protective coating particularly adapted to provide a bacteria inhibiting film on the surface of a tooth. A transfer agent and barrier material is used to improve the adhesion of the protective coating on the surface of the tooth.
Other coatings or materials have also been applied to teeth. One such material is amorphous calcium phosphate or ACP which has been applied to teeth to remineralize the teeth. The use of a ACP to remineralize teeth is disclosed in U.S. Pat. No. 5,037,639 entitled “Methods and Compositions for Mineralizing Calcified Tissues” issuing to Tongue on Aug. 6, 1991, which is herein incorporated by reference. Therein disclosed is a method of applying a composition containing amorphous calcium phosphate or ACP to teeth to remineralize the teeth.
While the prior protective coatings are well adapted to provide a bacteria inhibiting film or remineralizing of teeth, they are not necessarily suitable for use in maintaining whiter teeth and protecting whitened teeth. Therefore, there is a need to provide a protective coating specifically adapted for maintaining the whiteness of teeth and protecting them from damage when they have been bleached.
There is also a need, irrespective of the whitening of teeth, to improve and restore the health of tooth enamel. Improving the health of tooth enamel strengthens teeth and helps to prevent decay.
The present invention is a protective coating applied to teeth that have been whitened that maintains their whiteness and helps to repair damage caused by the whitening or bleaching of the teeth. A microcrystalline wax is mixed with vitamin E, mineral oil, and amorphous calcium phosphate providing a smooth consistent wax material that may be easily applied to whitened teeth. The protective coating prevents staining and the amorphous calcium phosphate helps to repair the damaged tooth surface caused by the repeated whitening of the teeth.
In another embodiment of the present invention sodium fluoride is incorporated into the formulation or composition and synergistically reacts with the amorphous calcium phosphate to aid in re-mineralization of tooth enamel.
Accordingly it is an object of the present invention to maintain the color of whitened teeth.
It is another object of the present invention to extend the time between teeth whitening procedures.
It is yet another object of the present invention to protect teeth and repair damage to teeth that have been whitened.
It is an advantage of the present invention that it reduces the need to repeatedly whiten teeth.
It is another advantage of the present invention that it is easy to apply to the teeth.
It is a feature of the present invention that it has a creamy consistency and is easy to apply.
It is another feature of the present invention that it contains amorphous calcium phosphate.
It is yet another object of the present invention to improve the health and strength of tooth enamel.
It is yet another advantage of the present invention that the composition has a formulation that permits prolonged contact with the tooth and a slow release of the ingredients.
It is yet another feature of the present invention that the sodium fluoride and the amorphous calcium phosphate are simultaneously dissolved by saliva forming a precipitate of calcium onto the tooth improving re-mineralization.
These and other objects, advantages, and features will become more readily apparent in view of the following more detailed description.
The present invention is a protective coating material specifically adapted for maintaining and protecting bleached teeth so as to seal and prevent teeth from being exposed to stains. The protective coating material of the present invention is easy to apply and adheres to the teeth for a prolonged period of time. The present invention also may help to strengthen tooth enamel and possibly reverse the damage caused by bleaching. The present invention uses a mixture of microcrystalline wax, oils, such as vitamin E and mineral oil, amorphous calcium phosphate, fluoride compounds, and aromatic or flavoring oils such as peppermint. Amorphous calcium phosphate is a material that has been shown to repair damaged tooth enamel. The microcrystalline wax has fine crystals and is tackier and more elastic than paraffin waxes. Therefore, the microcrystalline wax is particularly well-suited for applying to teeth.
A preferred formulation that has proven to work particularly well on bleached teeth is described below.
The process of making the protective coating material consisted of heating and melting 30 grams of microcrystalline wax to a temperature of 180° C. Once the microcrystalline wax was melted, 12 mL of vitamin E were mixed until the mixture was water clear. 40 mL of mineral oil was added to the melted wax and mixed until water clear. The wax mixture was taken off the heat and 1 gram of amorphous calcium phosphate dissolved in 2 to 4 mL of acetone was added. The solution of amorphous calcium phosphate was poured into the wax mixture and stirred until the mixture was uniformly white in color and the wax mixture began to solidify. The wax mixture was then cooled and solidified to a creamy consistency.
In another procedure or method of making the protective coating material, the amorphous calcium phosphate, rather than being dissolved in the acetone, may be suspended in the mineral oil. This eliminates the need for the acetone.
After cooling the protective coating material is applied in a thin coat to the bleached teeth. The protective coating material can be applied by any means, such as a brush, Q-tip, or any other applicator to evenly distribute the protective coating material to the bleached teeth. The protective coating material may also be applied by a finger or lipstick-like container. The protective coating material may be applied once every two to three days to protect the teeth and prevent the teeth from staining so as to maintain their whiteness. For best results, apply the coating before eating or drinking.
Illustrative Example 1 below indicates the desired formulation for a protective coating material that has proven to work especially well in protecting and maintaining teeth white after whitening or bleaching.
The formulation indicated in the above table has proven to result in a desirable consistency and color or transparency of the protective coating material. However, it should be appreciated that the formulation may be modified as desired to provide a desired consistency or texture for a particular circumstance or application. Accordingly, if the oil content is reduced the viscosity and hardness will increase and may make the protective coating material more difficult to apply. If the amorphous calcium phosphate, ACP, is increased an opaque protective coating material may result changing the visual color of the teeth. If the oil content is increased the protective coating material may become runny and unmanageable.
The protective coating material of the present invention greatly facilitates the maintaining of white teeth and prevents the need for frequent repeated bleaching, which may damage the teeth.
Studies have been performed in which the protective coating material of the invention has prevented teeth from staining as well as etching. The protective coating material of the present invention is safe and can be easily applied by an individual. The protective coating material of the invention may be sold in a kit together with or without a tooth whitening or bleaching material.
The invention provides a simple relatively easily manufactured protective material coating that is easily and safely applied to whitened teeth so as to prolong their whiteness. The invention is safe and effective and can be applied as often as desired in order to maintain whiter teeth. The invention may also repair damaged tooth enamel due to the harsh chemicals used in whitening teeth. The protective material coating may also be provided together with a whitening agent in a single package or kit as a convenience to the user.
Another embodiment of the present invention utilizes the simultaneous release of sodium fluoride and amorphous calcium phosphate (ACP) to form a precipitate of calcium fluoride aiding in the re-mineralization of a tooth.
Illustrative Example 2 below is a desired formulation for a tooth coating material that has proven to work especially well in protecting and strengthening teeth.
The composition created by the above formulation in Example 2 provides a desirable uniform consistency that is transparent and easily applied to the teeth. This composition is easily applied as a coating to the tooth surface. This composition includes the addition of fluoride and a thickener, such as guar gum. In this embodiment the composition may be rubbed or brushed on to the tooth surface. The composition may also have the consistency of a gum or putty that may be chewed so as to coat the teeth and release the ingredients over time. Example 2 illustrates the fluoride as sodium fluoride. However, other fluoride compounds may be used, such as caesium fluoride (CsF), tin (II) fluoride or stannous fluoride (SnF2), zinc fluoride (ZnF2), zirconium fluoride (ZrF4), antimony trifluoride (SbF3), potassium fluoride (KF), and other fluoride compounds.
The microcrystalline wax serves as a carrier and when dissolved or chewed inside the mouth is gradually reduced to expose and release the embedded fine particles of sodium fluoride. The sodium fluoride is then dissolved in the saliva in the mouth and releases ionic fluoride. The amorphous calcium phosphate, ACP, is in the form of a fine powder that is also released and dissolves in the saliva simultaneously with the sodium fluoride. This releases ionic calcium. Both the ionic calcium and the ionic fluoride are held in the saliva so as to contact the tooth surface for a relatively long period of time due to the thickener or guar gum.
A reaction between the loosely bonded ionic calcium in the ionic fluoride results in the precipitation of calcium fluoride which is deposited onto the tooth surface. This deposit results in and facilitates re-mineralization of the tooth enamel.
With the composition of Example 2, increased fluoride deposition on the tooth is achieved. The increased fluoride deposition is attributed to the in situ reaction caused by the precipitate of fluoride from the dissolved sodium fluoride and amorphous calcium phosphate, ACP, at the surface of the tooth and the immediate interacting with the tooth enamel.
This in situ reaction between the calcium and fluoride at the tooth surface has been found to be significantly more effective than the use of sodium fluoride as a mouth rinse. The ionic fluoride requires a calcium source in order to create calcium fluoride precipitate, which the composition in Example 2 provides.
In the embodiment of Example 2, the sodium fluoride and amorphous calcium phosphate, ACP, are in a solid-state such as a fine powder and are carried by the microcrystalline wax. The sodium fluoride powder and the amorphous calcium phosphate, ACP, powder does not react until both are dissolved in saliva. The release of the sodium fluoride and the amorphous calcium phosphate, ACP, occurs simultaneously when the microcrystalline wax is dissolved in the saliva in the mouth.
The composition in the embodiment of the present invention according to the formulation of Example 2 makes possible a slower longer release of sodium fluoride and amorphous calcium phosphate, ACP, providing prolonged contact with the surface of a tooth facilitating re-mineralization. This re-mineralization repairs and strengthens the tooth enamel. This results in a healthier tooth that is more resistant to decay.
The composition of Example 2 may be applied to the tooth by rubbing or brushing as illustrated in
While the preferred embodiments and methods of the present invention have been shown and described herein, it will be apparent to those skilled in the art that various modifications and variations may be made without departing from the spirit and scope of the invention as claimed herein.
This application is a continuation-in-part of U.S. application Ser. No. 14/552,936 filed Nov. 25, 2014 which is a continuation of International Application PCT/US2013/043504, with an international filing date of May 31, 2013, which claims the benefit of U.S. Provisional Application No. 61/654,578 filed Jun. 1, 2012, all of which are herein incorporated by reference.
| Number | Date | Country | |
|---|---|---|---|
| 61654578 | Jun 2012 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/US2013/043504 | May 2013 | US |
| Child | 14552936 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14552936 | Nov 2014 | US |
| Child | 15078941 | US |