FLUORINATED ACRYLATE BLOCK COPOLYMERS WITH LOW DYNAMIC SURFACE TENSION

Abstract
The present invention relates to a composition, comprising a binder resin,a block copolymer which comprises at least a block A and a block B, wherein the block A comprises monomer units derived from a compound selected from (meth)acrylic acid, a (meth)acrylic acid ester, a (meth)acrylamide, a vinyl aromatic compound, or any mixture thereof,the block B comprises monomer units derived from a compound selected from a fluorinated (meth)acrylic ester having the following formula (I):
Description
BACKGROUND OF THE INVENTION

The present invention relates to a composition which comprises a block copolymer having fluorinated monomer units and to the use of said block copolymer as substrate wetting, anti-cratering and/or leveling agent for coating, ink and/or adhesive compositions.


Smooth and crater free surfaces are important for almost all coating, ink and adhesive applications; they provide not only a visually appealing film but serve also as a protective barrier for the substrate as well as homogenous bond strength throughout the film.


When e.g. the coating is not homogenous and some parts of the surface are only thinly, or not all, coated it leads to poor protection of the substrate. As a result, substrate wetting, anti cratering and leveling agents are added to all sorts of coatings. These difficulties in application of coaling resin, particularly in liquid systems, occur particularly when the surface tension of the liquid system is high and the surface tension of the substrate, or contaminants on the substrate, is much lower. The addition of substrate wetting and anti cratering additives reduces both the dynamic and static surface tension of the liquid coating, leading to smoother film formation.


As long as the viscosity of the coating formulation is low, sufficient substrate wetting and leveling can be achieved with commercially available additives. Large problems can be observed in the cases of high solids coatings, powdered coatings and high speed coating processes. There is a strong demand for substrate wetting and anti-cratering additives with a very low dynamic surface tension, which can provide smooth and uniform films in these highly demanding applications.


The same reasoning applies also for inks and adhesives.


Long chain perfluoro chemicals, typically with perfluorinated chains of length C8 and longer, are used as anti-cratering and leveling agents for coating compositions but are know to form very environmentally persistent degradation products, including perfluoro-octanoic acid (PFOA). Thus, there is a need for alternatives which do not form such environmentally persistent degradation products. However, any improvement in degradation properties should not be achieved at the expense of properties which are relevant for leveling agent such as low dynamic surface tension. In general, the effect on dynamic surface tension reduction is believed to decrease with the order of the perfluorinated unit.


WO 2005/059048 describes coating compositions containing leveling agents prepared by nitroxide mediated polymerization. Monomer units may be substituted by fluoro or perfluoro.


WO 2009/103613 describes the use of short perfluorinated chains in copolymers prepared by nitroxide mediated polymerization for the use of leveling agents.


SUMMARY OF THE INVENTION

It is an object of the present invention to provide a polymeric leveling and anti-cratering agent which does not form environmentally very persistent degradation products such as perfluoro-octanoic acid but still enables manufacturing of coating, ink or adhesive compositions having very low dynamic surface tension.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 shows a graph of dynamic surface tension relative to bubble life time obtained for embodiments of the invention.





DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

According to a first aspect of the present invention, the object is solved by providing a composition, comprising

    • a binder resin,
    • a block copolymer which comprises at least a block A and a block B, wherein
      • the block A comprises monomer units derived from a compound selected from (meth)acrylic acid, a (meth)acrylic acid ester, a (meth)acrylamide, a vinyl aromatic compound, or any mixture thereof,
      • the block B comprises monomer units derived from a compound selected from a fluorinated (meth)acrylic ester having the following formula (I):





H2C═CR1(C(O)ORF−1)  (I)

    • wherein
    • R1 is H or methyl; and
    • RF−1 is an organic residue containing a perfluorinated C4-6 alkyl group, i.e. —(CF2)3-5—CH3,
    • a fluoridated alpha-olefin having the following formula (II):





H2C═CH(RF−2)  (II)

    • wherein RF−2 is an organic residue containing a perfluorinated C4-6 alkyl group, i.e. —(CF2)3-5—CF3
    • or any mixture thereof.


A perfluorinated C4-6 alkyl group is represented by the formula —(CF2)3-5—CF3.


Preferably, RF−1 and RF−2, which can be the same or different, have the following formula (III):





—(R2)x—(CF2)3-5—CF3  (III)

    • wherein x is 0 or 1; and R2 is a divalent non-fluorinated C1-4 alkylene group, which can be substituted or unsubstituted.


In a preferred embodiment, R2 in formula (III) is —(CH2)1-4—; such as —CH2—; —CH2—CH2—; —CH2CH2—CH2; or —CH2CH2—CH2—CH2—.


In a preferred embodiment, the fluorinated (meth)acrylic ester compound of formula (I) is selected from 3,3,4,4,5,5,6,6,7,7,8,8,8-tridecafluoroctyl acrylate, 3,3,4,4,5,5,6,6,6-nonafluorohexyl-acrylate, or mixtures thereof.


Preferred fluorinated alpha-olefins of formula (II) include e.g.


3,3,4,4,5,5,6,6,7,7,8,8,8-tridecafluoro-1-octene,


3,3,4,4,5,5,6,6,6-nonafluoro-1-hexene, or any mixture thereof.


The block B may consist of monomer units derived from the fluorinated (meth)acrylic ester compound of formula (I) or from the fluorinated alpha-olefin of formula (II).


Alternatively, the block B may contain two or more different monomer units.


If the block copolymer contains two or more blocks of type “B”, they may differ in block length (i.e. different number of monomer units), but preferably have the same arrangement or sequence of monomer units.


Preferably, the block B of the block copolymer has an average number of monomer units which are derived from the fluorinated (meth)acrylic ester compound of formula (I) and/or from the fluorinated alpha-olefin of formula (II) of at least 0.25, more preferably at least 0.5, or at least 1.


If the average number of monomer units of a specific block is below 1, this means that, statistically, not every polymer chain contains monomer units of said block. However, when using the block copolymer of the present invention, a reduced dynamic surface tension is still obtained at such low amount of fluorinated monomer units.


In a preferred embodiment, the block B of the block copolymer has an average number of monomer units which are derived from the fluorinated (meth)acrylic ester compound of formula (I) and/or from the fluorinated alpha-olefin of formula (II) of from 0.25 to 40, more preferably 0.5 to 30, even more preferably 1 to 20.


Preferably, block A comprises monomer units derived from a compound selected from C1-18 (meth)acrylates, more preferably C1-10 (meth)acrylates, especially meth(meth)arcylate (MMA), ethyl(meth)acrylate, n-butyl(meth)acrylate, iso-butyl(meth)acrylate, t-butyl(meth)acrylate, 2-ethylhexyl(meth)acrylate, isodecyl(meth)acrylate, hydroxyl-functional (meth)acrylates like 2-hyrdoxyethyl(meth)acrylate, hydroxypropyl(meth)acrylate, acid functional (meth)acrylic monomers like acrylic acid or methacrylic acid, sulphonic acid containing monomers like 2-acrylamido-2-methylpropane sulfonic acid (AMPS), aminofunctional (meth)acrylates like dimethylaminoethylmethacrylate (DMAEMA), epoxy functional (meth)acrylates like glycidylmethacrylate (GMA), (meth)acrylates containing siloxane groups, vinyl aromatic compounds such as styrene, or any mixture thereof.


The block A may consist of monomer units derived from a compound selected from (meth)acrylic acid, a (meth)acrylic acid ester, a (meth)acrylamide, or a vinyl aromatic compound.


Alternatively, the block A may contain two or more different monomer units.


If the block copolymer contains two or more blocks of type “A”, they may differ in block length (i.e. different number of monomer units), but preferably have the same arrangement or sequence of monomer units.


Preferably, the block A of the block copolymer has an average number of monomer units which are derived from a compound selected from (meth)acrylic acid, a (meth)acrylic acid ester, a (meth)acrylamide, or a vinyl aromatic compound, of at least 5, more preferably at least 10, even more preferably at least 15. In a preferred embodiment, the block A of the block copolymer has an average number of monomer units which are derived from a compound selected from (meth)acrylic acid, a (meth)acrylic acid ester, a (meth)acrylamide, or a vinyl aromatic compound, of from 5 to 1000, more preferably from 10 to 500, even more preferably from 15 to 300.


Preferably, the block copolymer has a number average molecular weight Mn of from 1000 to 100,000 g/mol, more preferably from 2,000 to 50,000 g/mol, even more preferably 3,000 to 25,000 g/mol. Other appropriate Mn ranges that can be used in the present invention are e.g. from 3,000 to 100,000 g/mol, or from 4,000 to 100,000 g/mol, or from 6,000 to 50,000 g/mol.


Preferably, the block copolymer comprises the monomer units derived from the fluorinated (meth)acrylic ester of formula (I) and/or from the fluorinated alpha-olefin of formula (II) in an amount of from 0.1 wt % to 70 wt %, more preferably from 0.5 wt % to 50 wt %, even more preferably from 1 wt % to 25 wt %.


Preferably, the block copolymer has a fluorine content of from 0.05 wt % to 35 wt %, more preferably from 0.25 wt % to 25 wt %, even more preferably from 0.5 wt % to 17 wt %.


Preferably, the block copolymer has a polydispersity index PDI (i.e. Mw/Mn) of less than 1.90, more preferably of less than 1.60, even more preferably of less than 1.40, or even less than 1.30.


The polydispersity index PDI may depend on the number of blocks being present and their arrangement in the block copolymer. If the block copolymer is linear with one block of A and one block of B, PDI may preferably be less than 1.40, more preferably less than 1.30. If the block copolymer is linear with one block of A and two blocks of B, or alternatively with one block of B and two blocks of A, PDI may preferably be less than 1.60, more preferably less than 1.50.


The block copolymer is preferably obtained by a controlled free radical polymerization (sometimes also referred to as “controlled radical polymerization”).


Methods of “controlled free radical polymerization” are generally known to the skilled person.


In a preferred embodiment, the controlled free radical polymerization is selected from nitroxide-mediated controlled polymerization (NMP), atom transfer radical polymerization (ATRP), or from reversible addition-fragmentation chain transfer polymerization (RAFT). These polymerization methods and variants thereof are generally known to the skilled person.


The reversible addition-fragmentation chain transfer polymerization RAFT using chain transfer agents which react by reversible addition-fragmentation chain transfer is described, for example, in WO-A-98/01478, WO-A-99/05099, WO-A-99/31144, and WO 2009/103613.


RAFT describes a method of polymer synthesis by radical polymerization in the presence of a free radical source and using chain transfer agents which react by reversible addition-fragmentation chain transfer. The chain transfer agent is, for example,

    • 2-phenylprop-2-yl dithiobenzoate (Ph—C(CH3, CH3)—S—C(S)—Ph) or benzyl dithioacetate Ph—CH2—S—C(S)—CH3 as described in WO 98/01478,
    • carbamates such as benzyl 1-pyrrolecarbodithioate, as described in WO99/31144;
    • alkylxanthates such as ethyl α(O-ethylxanthyl propionate), as described in WO 98/58974.


WO 96/30421 discloses a controlled polymerization process of ethylenically unsaturated polymers, such as styrene or (meth)acrylates, by employing the Atomic transfer Radical Polymerization (ATRP) method. This method produces defined oligomeric homopolymers and copolymers, including block copolymers. Initiators are employed, which generate radical atoms, such as .Cl, in the presence of a redox system of transition metals of different oxidation states, e.g. Cu(I) and Cu(II), providing “living” or controlled radical polymerization.


Details about nitroxide-mediated controlled polymerization are described e.g. in WO 2005/059048 and WO 2009/103613. The initiator compounds described therein can be used in the present invention as well.


More preferably, the controlled radical polymerization is selected from nitroxide-mediated controlled polymerization (NMP) and atom transfer radical polymerization (ATRP), even more preferably from NMP.


In a preferred embodiment, the controlled radical polymerization is a nitroxide-mediated controlled polymerization, which preferably uses a polymerization regulator system based on polymerization regulator compounds being preferably selected from one of the following formulas (IV), (V) and (VI) or based on the corresponding stable free nitroxyl radicals in conjunction with a radical source.




embedded image


wherein

    • R is hydrogen, C1-18alkyl which is uninterrupted or interrupted by one or more oxygen atoms, cyanoethyl, benzoyl, glycidyl, a monovalent radial of an aliphatic carboxylic acid having 2 to 18 carbon atoms, of a cycloaliphatic carboxylic acid having 7 to 15 carbon atoms, or an α,β-unsaturated carboxylic acid having 3 to 5 carbon atoms or of an aromatic carboxylic acid having 7 to 15 carbon atoms;
    • R101 is C1-12alkyl, C5-7cycloalkyl, C7-8aralkyl, C2-18alkanoyl, C3-5alkenoyl or benzoyl;
    • R102 is C1-18alkyl, C5-7cycloalkyl, C2-8alkenyl, which can be unsubstituted or substituted by a cyano, carbonyl or carbamide group, or is glycidyl, a group of the formula —CH2CH(OH)—Z or of the formula —CO—Z or —CONH—Z wherein Z is hydrogen, methyl or phenyl;
    • G6 is hydrogen,
    • G5 is hydrogen or C1-4alkyl,
    • G1 and G3 are methyl,
    • G2 and G4 are ethyl or propyl, or G1 and G2 are methyl and G3 and G4 are ethyl or propyl; and
    • X is selected from —CH2-phenyl, CH3CH-phenyl, (CH3)2C-phenyl, (C5-6cycloalkyl)2CCN, (CH3)2CCN,




embedded image




    •  —CH2CH═CH2, CH3CH—CH═CH2, (C1-4alkyl)CR20—C(O)-phenyl, (C1-4)alkyl-CR20—C(O)—(C1-4)alkoxy, (C1-4)alkyl-CR20—C(O)—(C1-4)alkyl, (C1-4)alkyl-CR20—C(O)—N-di(C1-4)alkyl, (C1-4)alkyl-CR20C(O)—NH(C1-4)alkyl, (C1-4)alkyl-CR20—C(O)—NH2, wherein R20 is hydrogen or (C1-4)alkyl; and

    •  wherein any of the alkyl groups can be unsubstituted or substituted, e.g. by one or more functional groups such as hydroxyl, amino, carboxylic acid, halide, cyano, and/or carbonyl.





The above polymerization regulator compounds as well as their corresponding stable free nitroxl radicals and their preparation are described in GB 2 335 190 and GB2 361 235.


As known to the skilled person, controlled free radical polymerization may involve using an initiator fragment IN for initiating the radical polymerization. The initiator fragment can be released from a polymerization regulator compound IN-E, e.g. from one of those described above. In formulas (IV) to (VI), radical X represents the initiator fragment IN, whereas the nitroxide radical would represent the group E.


The block copolymer can be a diblock copolymer, a triblock copolymer, or multiblock copolymer.


The block copolymer can be linear, or branched (such as star-shaped, comb-shaped, etc.).


In the present invention, the term “block copolymer” also includes a gradient and/or tapered block copolymer. This type of structured copolymer is also generally known to the skilled person. In a gradient or tapered block copolymer, there is a gradient compositional transition between blocks A and B.


In a preferred embodiment, a block can also be defined as a region of the polymer chain that is richer in fluorinated monomer than another block.


In the block copolymer of the present invention, two neighbouring blocks can be directly linked to each other. Alternatively, two neighbouring blocks can be linked to each other via a linking group LG, e.g. -A-LG-B-; -B-LG-B-; -A-LG-A—


The linking group LG can be any divalent group which may form a covalent bond to blocks A and B. Appropriate linking groups are known to the skilled person.


In a preferred embodiment, the linking group LG has the following formula (VII):





—IN1′—Y′—IN2′—  (VII)

    • wherein the IN1′ and IN2′ groups, which can be the same or different, are derived from the initiator fragments IN1 and IN2 of the controlled free radical polymerization, and Y′ is a divalent group covalently linked to the IN1′ and IN2′ groups or represents a covalent bond (e.g. σ-bond or π-bond) between the IN1′ and IN2′ groups.


Preferably, the initiator fragments IN1 and IN2 are the same and, consequently, the IN1′ and IN2′ groups are the same as well.


The divalent group Y′ can be derived from a compound Y having at least two functional groups which may react with the initiator fragments IN1 and IN2. Appropriate compounds having at least two functional groups are e.g. diisocyanate compounds (such as toluene diisocyanate), aliphatic polyisocyanates or isocyanurate compounds.


The linking group LG of formula (VII) can be obtained by using, in the controlled free radical polymerization, an initiator fragment IN having at least one functional group, such as hydroxyl, ammo, carboxylic acid, halide, cyano, and or carbonyl. After having initiated controlled free radical polymerization, the initiator fragment IN is covalently bonded to one end of the polymer chain. In the presence of a compound Y having two functional groups, a chemical reaction between said compound Y and two IN groups of two different polymer chains may take place, thereby bonding these polymer chains to each other via a linking group of formula (VII).


The block copolymer of the present invention may contain only one block A, or may contain two or more blocks of A. The blocks may have the same number of monomer units or may differ in block length (i.e. different number of monomer units).


The block copolymer of the present invention may contain only one block B, or may contain two or more blocks of B. The blocks may have the same number of monomer units or may differ in block length (i.e. different number of monomer units).


If the block copolymer contains at least two blocks of A and at least two blocks of B, the block copolymer may comprise the following structural element:





-B-A-LG-A-B- or A-B-LG-B-A—


wherein LG is the linking group described above, which is preferably of formula (VII).


Preferably, the amount of the block copolymer, relative to the total composition, is from 0.05 wt % to 15 wt %, more preferably from 0.075 wt % to 10 wt % and most preferred from 0.1 wt % to 5 wt %.


The binder resin can be selected from those commonly used for coating compositions. Appropriate binder resins are known to the skilled person.


The binder resin can be selected from solvent based resins, water based resins, emulsion polymers, solution polymers, or any mixture thereof.


The binder resins comprise all kinds of crosslinking mechanism and coating systems based on one-component multi-component systems, e.g. thermosetting resins, room temperature curable resins, radiation-curable resins. Also included are physically drying coating systems like thermoplastic acrylic resins.


The resins comprise state of the art polymer chemistry used in coatings, inks and adhesive; e.g. saturated polyesters, unsaturated polyesters, polyacrylates, styrene-acrylic resins, polyurethanes, epoxy resins, nitrocellulose resins, hybrid systems like polyester/polyurethanes, polyacrylate/poly-urethanes, alkyd/melamine, polyester/CAB/melamine, polyacrylate/CAB/melamine, etc. Preferred binder resins comprise ponder coating resins, i.e. resin systems which are solid at room temperature and do not include a liquid carrier, e.g. thermosetting powder coatings or radiation curable powder coatings like polyester/PRIMID, polyester/TGIC, epoxy-functional polyacrylates with acidic crosslinker components, etc.


The weight ratio the block copolymer to binder resin can be varied over a broad range. Preferably, the weight ratio of block copolymer to binder resin is within the range of from 0.001 to 0.5 more preferably from 0.005 to 0.3 even more preferably from 0.01 to 0.1.


Preferably, the composition is a coating composition, an ink composition or an adhesive composition.


Exemplary compositions include a solvent-based coating composition, a water-based coating composition, a high solids coating composition, a powder coating composition, a solvent-borne ink composition, a water-borne ink composition, a UV-curable ink composition, or a UV-curable coating composition, or combinations thereof.


According to a further aspect, the present invention is directed to the use of the block copolymer described above as an anti-cratering and/or leveling and/or substrate wetting agent in coating compositions, ink compositions, or adhesive compositions.


As the block copolymer of the present invention provides a significant reduction in dynamic surface tension, it is preferably used as an anti-cratering and/or leveling agent in challenging coating systems, such as high solids coatings, powder coatings, solvent-borne inks, water-borne inks, UV inks, UV coatings and/or in high speed coating processes.


According to a further aspect, the present invention is directed to the use of the block copolymer described above for reducing dynamic surface tension in a coating composition, ink composition or adhesive composition, such as high solids coating compositions and powder coating compositions, ink compositions such as solvent-borne inks, water-borne inks, UV inks, UV coatings.


Preferably, the term “reducing dynamic surface tension” means that dynamic surface tension is lower if compared to a random but otherwise identical copolymer.


EXAMPLES
I. Measuring Methods

If not indicated otherwise, parameters defined in the present application are measured by the measuring methods described below:


Number Average Molecular Weight Mn, Polydispersity Index PDI

Mn and PDI are measured by gel permeation chromatography (GPC) with polystyrene standards. The eluent is THF.


Amount of F (in wt %) and Amount of Fluorine-Containing Monomer Units (in wt %) in the Block Copolymer

Determined by 1H NMR, 400 MHz.


II. Preparation Examples
Inventive Example 1
Synthesis of a Linear A-B Block-Copolymer of n-Butyl Acrylate (nBA) and 3,3,4,4,5,5,6,6,7,7,8,8,8-Tridecafluoroctyl Acrylate (TFOA)
Synthesis of A Block



embedded image


In a 5000 mL glass reactor with overhead mechanical stirrer, condenser, metering pumps, computerized temperature control and data acquisition, the following A-blocks are synthesized.


GK3023-360 (10 Units nBA)

1816.70 g of n-Butyl Acrylate (nBA, 128.7 g/mol), 150.00 g of the initiator compound NOR 1 (317.48 g/mol) and 271.38 g of ethyl acetate (EtAc, Mw 88.11 g/mol) are mixed together, purged with N2 and reacted for 3 h at 120° C. Residual monomer and ethyl acetate is distilled off at 105° C. and 20 mbar.


Yield: 33.3%; GPC (THF, PS-Standard, Mn=1706 g/mol, PDI=1.26, liquid)


GK3023-264 (20 Units)

1211.13 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol) and 60.00 g of the initiator compound NOR 1 (317.48 g/mol) are mixed together, purged with N2 and reacted for 3.5 h at 115° C. Residual monomer is distilled off at 105° C. and 20 mbar.


Yield: 42.83%; GPC (THF, PS-Standard, Mn=2435 g/mol, PDI=1.36, viscous liquid)


GK3023-335 (35 Units)

1383.92 g of n-Butyl Acrylate (nBA, 128.7 g/mol), 40.00 g of the initiator compound NOR 1 (317.48 g/mol) and 206.70 g of ethyl acetate (EtAc Mw 88.11 g/mol) are mixed together, purged with N2 and reacted for 3 h at 120° C. Residual monomer and ethyl acetate is distilled off at 105° C. and 20 mbar.


Yield: 38.3%; GPC (THF, PS-Standard, Mn=3649 g/mol, PDI=1.44, viscous liquid)


GK3023-387 (75 Units)

1211.13 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol) and 60.00 g of NOR 1 (317.48 g/mol) are mixed together, purged with N2 and reacted for 1.5 h at 115° C. A feed of 2422.26 g of nBA is fed to the reactor over 3 hours. At 125° C., and the reaction continues for a further 4.5 h. Residual monomer is distilled off at 105° C. and 20 mbar.


Yield: 50.36%; GPC (THF, PS-Standard, Mn=9650 g/mol, PDI=1.21, viscous liquid)


Synthesis of B Block



embedded image


In a 5-necked 100 mL Sulfier flask with an overhead stirrer, thermometer, cooler and septum, A g of Poly-nBA (see table) and B g of 3,3,4,4,5,5,6,6,7,7,8,8,8-Tridecafluoroctyl Acrylate (TFOA, Mw 418.15 g/mol) are mixed together, purged with N2 for 30 minutes and polymerized for 8 hours at 128° C. Residual monomer is distilled off at 105° C. and 20 mbar. The polymer is characterized by GPC (THF and with PS-Standards; note: the refractive index of TFOA is negative) and 1H-NMR (in CDCl3).






























Description



A-block
A (g





wt % F
(units of



Poly-
of A
B (g
Yield
Mna

wt. %
in
nBA:units


Product
nBA
block)
TFOA)
(%)
(g/mol)
PDIa
TFOAb
polymerb
of TFOA)b
























GK3479-
GK3023-
10.00
13.94
82.59
2029
1.29
50.90
30.03
10:3.96


039
360


GK3479-
GK3023-
15.00
12.54
88.56
2035
1.23
40.40
23.87
10:2.59


040
360


GK3479-
GK3023-
20.00
5.58
89.12
1771
1.22
19.07
11.25
10:0.90


041
360


GK3479-
GK3023-
27.00
3.00
87.93
2055
1.21
7.51
4.43
10:0.31


076
360


GK3479-
GK3023-
27.90
2.10
88.40
2016
1.22
5.91
3.49
10:0.24


077
360


GK3479-
GK3023-
20.00
13.94
95.01
3510
1.20
36.93
21.79
20:4.03


044
264


GK3479-
GK3023-
20.00
8.36
92.01
3121
1.22
24.97
14.73
20:2.29


046
264


GK3494-
GK3023-
30.00
4.18
92.44
3377
1.24
10.30
6.07
20:0.79


071
264


GK3494-
GK3023-
30.00
20.91
94.96
4331
1.22
37.22
21.96
20:4.08


014
264


GK3479-
GK3023-
45.00
5.00
93.31
2949
1.26
6.26
3.70
20:0.46


080
264


GK3479-
GK3023-
46.50
3.50
93.57
3012
1.26
4.97
2.93
20:0.36


081
264


GK3479-
GK3023-
30.00
7.84
94.09
4476
1.17
17.36
10.24
35:2.41


043
335


GK3494-
GK3023-
30.00
13.07
91.04
5068
1.16
28.26
16.67
35:4.53


028
335


GK3479-
GK3023-
30.00
2.61
96.33
5218
1.19
6.29
3.71
35:0.77


070
335


GK3479-
GK3023-
27.00
3.00
96.90
4869
1.20
6.21
3.66
35:0.76


079
335


GK3494-
GK3023-
50.00
10.59
94.47
8638
1.16
14.89
8.78
75:4.15


026
387


GK3494-
GK3023-
50.00
20.91
91.77
9119
1.18
24.86
14.67
75:7.85


027
387


GK3479-
GK3023-
50.00
6.27
98.86
8223
1.19
10.22
6.03
75:2.70


042
387


GK3479-
GK3023-
50.00
2.09
98.93
8012
1.19
3.65
2.16
75:0.90


047
387


GK3479-
GK3023-
45.00
5.00
97.24
9907
1.23
7.81
4.61
75:2.01


078
387


GK3479-
GK3023-
40.00
14.65
83.99
7803
1.19
5.19
3.06
75:1.30


48c
387


GK3479-
GK3023-
46.50
3.50
98.11
9476
1.22
5.80
3.42
75:1.46


082
387






aby GPC with polystyrene standards




bby H1 NMR




cPolymerization at 115° C. for 2 hours.







Comparative Example 2
Synthesis of a Linear, Low Polydispersity, Random Copolymer of n-Butyl Acrylate (nBA) and 3,3,4,4,5,5,6,6,7,7,8,8,8-Tridecafluoroctyl Acrylate (TFOA)
GK3479-027



embedded image


In a 5-necked 100 ml Sulfier flask with an overhead stirrer, thermometer, cooler and septum, C 65.70 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol), D 3.70 g of 3,3,4,4,5,5,6,6,7,7,8,8,8,-Tridecafluoroctyl Acrylate (TFOA, Mw 418.15 g/mol) and E 2.50 g of NOR 1 (317.48 g/mol) are mixed together, purged with N2 for 30 minutes and polymerized for 3-4 hours at 125° C. Residual monomer is distilled off at 95° C. and 10 mbar. The polymer is characterized by GPC (THF and with PS-Standards) and 1H-NMR (in CDCl3).





















C (g of
D (g of
E (g
Yield
Mna

wt. %
wt % F in


Product
nBA)
TFOA)
NOR1)
(%)
(g/mol)
PDIa
TFOAb
polymerb























GK3479-
65.70
3.70
2.50
60.14
3724
1.20
8.02
4.73


027


GK3479-
6.00
7.40
2.50
61.80
4031
1.23
14.27
8.42


026


GK3479-
58.00
11.40
2.50
60.71
3814
1.25
19.46
11.48


024


GK3479-
47.79
2.67
2.50
44.87
2217
1.30
12.55
7.41


022


GK3479-
45.06
5.40
2.50
47.76
2298
1.27
17.73
10.46


021


GK3479-
42.38
8.08
1.50
46.11
2296
1.28
21.53
12.70


020






aby GPC with polystyrene standards




bby H1 NMR







Comparative Example 3
Synthesis of Random Copolymer of n-Butyl Acrylate (nBA) and 3,3,4,4,5,5,6,6,7,7,8,8,8-Tridecafluoroctyl Acrylate (TFOA) by Free Radical Polymerization
GK3365-133

In a 5-necked 2 mL Snifter flask with an overhead stirrer, thermometer, cooler and septum, 50.00 g of sec-Butanol (Mw 74.12 g/mol) is purged with N2 for 30 minutes and heated to 100° C. A premixed feed of A 5.00 g of 3,3,4,4,5,5,6,6,7,7,8,8,8-Tridecafluoroctyl Acrylate (TFOA, Mw 418.15 g/mol), B 88.54 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol) and C 6.46 g of tert-butyl Peroxy-2ethylhexanoate (tBpOEH, Mw 216.32 g/mol) is fed to the reactor over 3 hours. After the completion of the feed, the reaction continues to react for a further 3 hours. The solvent is distilled off at 100° C. and 10 mbar. The polymer is characterized by GPC (THF and with PS-Standards) and 1H-NMR (in CDCl3).




















B (g of
A (g of
C (g of
Mna

wt. %
wt % F in


Product
nBA)
TFOA)
tBpOEH)
(g/mol)
PDIa
TFOAb
polymerb






















GK3365-
88.54
5.00
6.46
2065
1.56
5.35
2.95


133


GK3365-
83.54
10.00
6.46
2072
1.56
10.69
5.90


134


GK3365-
78.54
15.00
6.46
2043
1.50
16.04
8.85


135


GK3365-
88.54
5.00
3.00
2604
1.70
5.35
2.95


136









Inventive Example 4
Synthesis of a Linear B-A-B Block-Copolymer of n-Butyl Acrylate (nBA, A-Block) and 3,3,4,4,5,5,6,6,7,7,8,8,8,-Tridecafluoroctyl Acrylate (TFOA, B-Block)
Synthesis of A (Interior) Block



embedded image


In a 5000 mL glass reactor with overhead mechanical stirrer, condenser, metering pumps, computerized temperature control and data acquisition, the following A-blocks-precursors are synthesized.


GK3023-389 (75 Units)

2165.22 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol) and 80.00 g of the initiator compound NOR 2 (342.48 g/mol) are mixed together, purged with N2 and reacted for 1.5 h at 115° C. A feed of 1624.54 g of nBA was led to the reactor over 5 hours. At 125° C., the reaction continues for a further 2 h. Residual monomer is distilled off at 105° C. and 20 mbar.


Yield: 50.29%; GPC (THF, PS-Standard, Mn=10740 g/mol, PDI=1.19, viscous liquid)


GK3023-287 (15 Units)

2944.4 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol) and 180 g of NOR 2 (342.48 g/mol) are mixed together, purged with N2 and reacted for 3.5 h at 115° C. Residual monomer is distilled off at 105° C. and 20 mbar.


Yield: 28.84%; GPC (THF, PS-Standard, Mn=2172 g/mol, PDI=1.25, viscous liquid)


GK3023-101 (35 Units)

In a 2000 mL glass reactor with overhead mechanical anchor stirrer, condenser and metering pumps 561.36 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol) and 50.00 g of NOR 2 (342.48 g/mol) are mixed together, purged with N2 and reacted for 2 h at 115° C. A feed of 748.48 g of nBA is fed to the reactor over 6 hours. At 120° C., the reaction continues for a further 6 h. Residual monomer is distilled off at 105° C. and 20 mbar.


Yield: 49.67%; GPC (THF, PS-Standard, Mn=7739 g/mol, PDI=1.14, viscous liquid)


Coupling to Synthesize Difunctional A-Blocks



embedded image


In a 5-necked 200 mL Sulfier flask with an overhead stirrer, thermometer, cooler and septum, F g of Poly-nBA precursors (see table) and G g of tolylene-2,4-diisocyanate (TDI, Mw 174.16 g/mol) are mixed together and purged with N2 for 30 minutes. The inner temperature is raised to 60° C. and a few drops of dibutyltin dilaurate (DBTL, Mw 631.56, 10% solution in butyl acetate) are added. The coupling reaction continues for 4 hours at 60° C. The polymer is characterized by GPC (THF and with PS-Standards and 1H-NMR (in CDCl3).
























Description (units



A-block Poly-
F (g of A
G (g
Mna

of nBA:units of


Product
nBA
block)
TDI)
(g/mol)
PDIa
TFOA)b





















GK3041-283
GK3023-389
1200
11.00
17592
1.21
NOR-BA(150)-








NOR


GK3479-061
GK3023-010
120
2.39
8947
1.17
NOR-BA(70)-








NOR


GK3479-062
GK3023-287
100
4.79
4186
1.13
NOR-BA(30)-








NOR









Synthesis of B Block



embedded image


In a 5-necked 100 mL Sulfier flask with an overhead stirrer, thermometer, cooler and septum, H g of di-functional poly nBA (see table) and I g of 3,3,4,4,5,5,6,6,7,7,8,8,8-Tridecafluoroctyl Acrylate (TFOA, Mw 418.15 g/mol) are mixed together, purged with N2 for 30 minutes and polymerized for 8 hours at 128° C. Residual monomer is distilled off at 105° C. and 20 mbar. The polymer is characterized by GPC (THF and with PS-Standards; note: the refractive index of TFOA is negative) and 1H-NMR (in CDCl3).






















A-block
H (g





wt % F
Idealized



Poly-
of A
I (g
Yield
Mna

wt. %
in
Description


Product
nBA
block)
TFOA)
(%)
(g/mol)
PDIa
TFOAb
polymerb
(TFOA:nBA:TFOA)b
























3479-
GK3041-
40.00
5.02
95.02
14434
1.40
6.49
3.83
2.93:150:2.93


072
283


3479-
GK3041-
40.00
8.36
91.92
16021
1.40
10.02
5.91
4.89:150:4.89


073
283


3479-
GK3041-
40.00
1.67
99.53
16734
1.24
3.55
2.10
0.98:150:0.98


074
283


3479-
GK3041-
30.00
7.52
83.87
15757
1.36
4.67
2.75
5.86:150:5.86


075c
283


3479-
GK3479-
30.00
7.53
81.23
8445
1.45
1.59
0.94
2.79:70:2.79


067
061


3479-
GK3479-
30.00
15.06
83.84
9071
1.47
20.59
12.15
5.59:70:5.59


068d
061


3479-
GK3479-
15.00
8.36
94.04
4749
1.39
31.72
18.71
2.79:30:2.79


065
062


3479-
GK3479-
20.00
3.72
94.70
3815
1.44
10.96
6.47
0.93:30:0.93


066
062






aby GPC with polystyrene standards




bbased on solids content




cPolymerized with a maximum temperature of 115° C. in 1 hour.




dPolymerized with a maximum temperature of 115° C. in 22 hours.







Inventive Example 5
Synthesis of a Linear A-B Block-Polymer of n-Butyl Acrylate (nBA) and 3,3,4,4,5,5,6,6,6-Nonafluorhexyl Acrylate (NNFHA)
Synthesis of A Block



embedded image


The same A-blocks as those described in Example 1 are used as the starting block for the chain extension with NFHA monomer.


Synthesis of B Block



embedded image


In a 5-necked 100 mL Sulfier flask with an overhead stirrer, thermometer, cooler and septum, A g of Poly-nBA (see table) and B g of 3,3,4,4,5,5,6,6,6-Nonafluorhexyl Acrylate (NFHA, Mw 318.13 g/mol) are mixed together, purged with N2 for 30 minutes and polymerized for 8 hours at 128° C. Residual monomer is distilled off at 105° C. and 20 mbar. The polymer is characterized by GPC (THF and with PS-Standards; note: the refractive index of NFHA is negative) and 1H-NMR (in CDCl3).






























Description



A-block
A (g





wt % F
(units of



Poly-
of A
B (g
Yield
Mna

wt. %
in
nBA:units


Product
nBA
block)
NFHA)
(%)
(g/mol)
PDIa
NFHAb
polymerb
of NFHA)b
























GK3479-
GK3023-
10.00
10.60
92.25
2803
1.22
29.78
45.78
10:4.24


143
360


GK3479-
GK3023-
15.00
9.54
91.54
2496
1.21
19.29
32.74
10:2.39


144
360


GK3479-
GK3023-
20.00
7.85
89.70
2281
1.24
13.12
23.12
10:1.51


186
360


GK3479-
GK3023-
20.00
4.24
88.60
2057
1.25
6.10
11.46
10:0.65


185
360


GK3479-
GK3023-
30.00
14.00
91.55
3664
1.25
14.20
26.79
20:3.31


183
264


GK3479-
GK3023-
30.00
9.54
92.36
3386
1.26
11.74
22.72
20:2.66


184
264


GK3479-
GK3023-
30.00
8.75
93.49
5620
1.18
6.49
13.87
35:2.43


181
335


GK3479-
GK3023-
30.00
5.96
93.06
5405
1.18
3.37
7.48
35:1.22


182
335


GK3479-
GK3023-
35.00
11.13
94.43
11084
1.28
8.55
18.35
75:7.01


145
387


GK3479-
GK3023-
50.00
11.82
95.24
11016
1.3
7.09
15.50
75:5.72


179
387


GK3494-
GK3023-
50.00
7.95
96.20
98040
1.29
9.07
4.81
75:3.11


50
387


GK3479-
GK3023-
50.00
7.03
95.43
2803
1.22
3.80
8.67
75:2.96


180
387






aby GPC with polystyrene standards




bby H1 NMR







Comparative Example 6
Synthesis of a Linear, Low Polydispersity, Random Copolymer of n-Butyl Acrylate (nBA) and 3,3,4,4,5,5,6,6,6-Nonafluorhexyl Acrylate (NFHA)
GK3479-202



embedded image


In a 5-necked 100 mL Sulfier flask with an overhead stirrer, thermometer, cooler and septum, C 50.86 g of n-Butyl Acrylate (nBA, Mw 128.7 g/mol), D 9.70 g of 3,3,4,4,5,5,6,6,6-Nonafluorhexyl Acrylate (NFHA, Mw 318.13 g/mol) and E 3.00 g of NOR 1 (317.48 g/mol) are mixed together, purged with N2 for 30 minutes and polymerized for 3-4 hours at 125° C. Residual monomer is distilled off at 95° C. and 10 mbar. The polymer is characterized by GPC (THF and with PS-Standards) and 1H-NMR (in CDCl3).





















C (g of
D (g of
E(g
Yield
Mna

wt. %
wt % F in


Product
nBA)
NFHA)
NOR1)
(%)
(g/mol)
PDIa
NFHAb
polymerb























GK3479-
50.86
9.70
3.00
50.79
2786
1.25
21.01
11.14


202


GK3479-
54.07
6.48
3.00
51.94
2896
1.19
17.39
9.22


203


GK3479-
57.35
3.20
3.00
49.08
2847
1.23
12.36
6.55


204


GK3479-
50.86
9.70
0.95
49.75
8146
1.18
19.62
10.40


205


GK3479-
54.07
6.48
0.95
51.24
8189
1.19
18.96
10.05


206


GK3479-
57.35
3.20
0.95
52.87
8552
1.21
5.36
2.84


207






aby GPC with polystyrene standards




bby H1 NMR







Comparative Example 7
Synthesis of Random Copolymer of n-Butyl Acrylate (nBA) and 3,3,4,4,5,5,6,6,6-Nonafluorhexyl Acrylate (NFHA) by Free Radical Polymerization
GK3365-207

In 5-necked 200 mL Sulfier flask with an overhead stirrer, thermometer, cooler and septum, 50.00 g of sec-Butanol (Mw 74.12 g/mol) is purged with N2 for 30 minutes and heated to 100° C. A pre-mixed feed of A 5.00 g of 3,3,4,4,5,5,6,6,6-Nonafluorhexyl Acrylate (NFHA, Mw 318.13 g/mol), B 88.54 g of n-Butyl Acrylate (nBA, Mw 1.287 g/mol) and 6.46 g of tert-butyl Peroxy-S-ethylhexanoate (tBpOEH, Mw 216.32 g/mol) is fed to the reactor over 3 hours. After the completion of the feed, the reaction continues to react for a further 3 hours. The solvent is distilled off at 100° C. and 10 mbar. The polymer is characterized by GPC (THF and with PS-Standards) and 1H-NMR (in CDCl3).




















B









(g of
A (g of
Yield
Mna

wt. %
wt % F in


Product
nBA)
NFHA)
(%)
(g/mol)
PDIa
NFHAb
polymerb






















GK3365-
88.54
5.00
6.46
1656
1.59
5.35
2.84


207


GK3365-
83.54
10.00
6.46
1666
1.60
10.69
5.67


208


GK3365-
78.54
15.00
6.46
1699
1.61
16.04
8.50


209


GK3365-
73.54
20.00
6.46
1606
1.65
21.38
11.33


210


GK3365-
88.54
5.00
2.00
2501
2.16
5.35
2.84


211


GK3365-
83.54
10.00
2.00
2318
1.92
10.69
5.67


212









Inventive Example 8
Synthesis of a Linear A-B Block-Copolymer of n-Butyl Acrylate (nBA) and 3,3,4,4,5,5,6,6,7,7,8,8,8-Tridecafluor-1-octene (TFO)
Synthesis of A Block



embedded image


The same A-blocks as those described in Example 1 are used as the starting block for the chain extension with TFO monomer.


Synthesis of B Block



embedded image


In a 5-necked 200 mL Sulfier flask with an overhead stirrer, thermometer, cooler and septum, A g of Poly-nBA (see table), B g of 3,3,4,4,5,5,6,6,7,7,8,8,8-Tridecafluor-1-octene (TFO, Mw 346.09 g/mol) and C g of toluene are mixed together, purged with N2 for 30 minutes and polymerized for 6 hours at reflux (106-110° C.). Residual monomer and solvent is distilled off at 120° C. and 20 mbar to >99%. The polymer is characterized by a mass balance of the distillate.




















A (g



wt %



A-block
of A
B (g
C (g
wt. %
F in


product
Poly-nBA
block)
TFO)
Toluene)
TFO
polymer





















GM0800-
GK3023-360
30.00
69.22
30.00
17.81
12.64


0012


GM0800-
GK3023-360
25.00
115.36
25.00
17.81
12.64


0013









III. Application Examples

Static Surface Tension:


Static surface tension is measured, using an OCA 20 (Dataphysics) at concentrations from 1-10 w% in xylene using the hanging-drop method.









TABLE 1.1







Static surface tension












surface
surface




tension
tension



w % TFOA
(mN/m)
(mN/m)















Example
conc (w %)

10
1


type


comparative
Xylol

28.62
28.62



(blank)



GK3479/022
12.6
28.45
28.98



GK3479/021
17.7
27.83
29.03



GK3479/020
21.5
27.1
28.93


inventive
GK3479/047
3.7
28.22
28.98



GK3479/042
10.2
20.76
25.93



GK3494/026
14.9
18.55
21.29



GK3494/027
24.9
18.34
19.62









At comparable amounts of TFOA w% (GK3479/022 as a comparative example and GK3479-042 as an inventive example), a much lower static surface tension in xylene are clearly observed (28.98 mN/m and 25.93 mN/m respectively at 1 w% in xylene).


Dynamic Surface Tension:


(i) With block B containing fluorinated (meth)acrylic ester derived units


Dynamic surface tension is measured using a bubble pressure tensiometer (Sita) at concentrations of 0.25% 0.5 w% in the A component of a solvent based 2K-PU. Bubble life times are measured from 80 msec up to 10 sec.


A component 2K PU:









TABLE 2.1







2K-PU Component A















Weight
0.25 wt %
0.5 wt %



Raw material
Identity
in g.
Additive
Additive

















Macrynal
Acrylic
89.0





SM510/60LG
resin




solution



Butyl acetate
Solvent
11.0



Efka ® 2018N

8.0



Formulation

108.0
7.38
7.36



Additive


0.025
0.05



Sample size


7.405
7.41







Efka 2018N is a commercially available defoamer.






At a very short bubble life time, a clear advantage (lower dynamic surface tension values) could be observed looking at same w% F-Monomer and 0.5 w% addition levels.















Inventive examples













GK3479/
GK3494/
GK3494/



GK3479/047
042
026
027















DST at 80 ms, 0.5 w
73.1
63.3
56.2
55.2


% addition level


w % TFOA
3.7
10.2
14.9
24.9






















Comparative examples













GK3479/
GK3479/
GK3479/
Efka
GK3365/



022
021
020
3600
135
















DST at 80 ms,
74.7
70.8
64.9
72.8
65.1


0.5 w % addition


level


w % TFOA
12.6
17.7
21.5
14.2
16









(ii) With block B containing fluorinated alpha-olefin derived units


Dynamic surface tension is measured using a bubble pressure tensiometer (Sita) at concentrations of 0.1% 1.0 w% in the A component of a solvent based 2K-PU. Bubble life times are measured from 80 msec up to 10 sec. In the following test series the commercial leveling additive EFKA 3600N is used a reference.


A component 2K PU:









TABLE 2.1







2K-PU Component A














Weight
0.25 wt %



Raw material
Identity
in g.
Additive
















Macrynal
Acrylic
89.0




SM510/60LG
resin




solution



Butyl acetate
Solvent
11.0



Formulation

100.0
19.95



Additive


0.05



Sample size


20.00










At a very short bubble life time, a clear advantage (lower dynamic surface tension values) could be observed compared to the commercial benchmark at 0.25 w% addition levels.
















Inventive examples











GM800-012
GM800-013















DST at 80 ms, 0.25 w
72.4
70.9



% addition level























Comparative examples



Efka 3600N



















DST at 80 ms, 0.25 w
80.3



% addition level










The results are also shown in FIG. 1.


Anticratering Test:


The formulation, according to table 3.1, is treated for about one hour on the roll bench and finally shaken by hand until homogenous. The amount of component A indicated in table 3.2 is added in 20 ml glass jar with the appropriate amount of component B. The sample is immediately shaken by hand until homogenous and applied on a PET foil. A draw down of the mixture with 75 μm wire bar at speed 20 mm/sec is prepared. The sample is checked for craters and haze on the panels after drying over night.









TABLE 3.1







2K-PU Component A
















Weight
0.1 wt %
0.25 wt %
0.5 wt %
0.75 wt %
1 wt %


Raw material
Identity
in g.
Additive
Additive
Additive
Additive
Additive

















Macrynal
Acrylic
89.0







SM510/60LG
resin



solution


Butyl acetate
Solvent
10.5


Tinstab BL
Di-n-
0.5


277
Butyltin


1% in Butyl
dilaurate


acetate


Efka ® 2018N

8.0


Formulation

108.0
7.39
7.38
7.36
7.35
7.33


Additive


0.01
0.025
0.05
0.075
0.1


Sample size


7.40
7.405
7.41
7.425
7.43
















TABLE 3.2







2K-PU Component B














Raw


0.1 wt %
0.25 wt %
0.5 wt %
0.75 wt %
1 wt %


material
Identity
blank
Additive
Additive
Additive
Additive
Additive

















Desmodur
Hardener
2.60
2.60
2.59
2.59
2.57
2.57


N75
(Resin)


Component A

7.40
7.40
7.405
7.41
7.425
7.43


Sample size

10
10
10
10
10
10





Mixing ratio: A:B = 100:35 (36 round)













TABLE 3.3







Anticrater performance in 2K-PU












0.1 wt %
0.25 wt %
0.5 wt %
1.0 wt %

















Examp.

wt %

Gloss

Gloss

Gloss

Gloss


Type
Sample
TFOA
Craters
20°
Crat.
20°
Crat.
20°
Crat.
20°




















comparative
Blanka

8
158









GK3479/
21.5
1
165
1
93.7
1
164
1
80.2



020



GK3479/
17.7
4
165
1
162
1
125
1
118



021



GK3479/
12.6
8
165
8
98.1
8
125
2
109



022


inventive
GK3494/
24.9
n/a
150
2
105
3
122
3
143



027



GK3494/
14.9
2
163
3
136
3
92
3
150



026



GK3479/
10.2
3
148
2
127
1
155
1
93.7



042



GK3479/
3.7
8
163
4
163
2
128
2
148



047


comparative
GK3365/
16.1
2
158
7
138
7
157
4
123



135



GK3365/
10.7
8
164
5
158
3
152
1
162



134



GK3365/
5.3
8
163
6
130
3
163
2
159



133






aBlank contains no additive.



1 indicates no craters and 8 indicates many craters.





Claims
  • 1-15. (canceled)
  • 16. A method to lower the dynamic surface tension of a composition in a coating process, wherein the composition is one selected from the group consisting of a coating composition, an ink composition and an adhesive composition, the method comprising:adding from 0.05 to 15 wt % relative to the weight of the composition of a block copolymer; andapplying the composition comprising the block copolymer to a substrate in a high speed coating process;wherein the block copolymer comprises:a block A and a block B, whereinthe block A comprises monomer units derived from a compound selected from (meth)acrylic acid, a (meth)acrylic acid ester, a (meth)acrylamide, a vinyl aromatic compound, or a mixture thereof, andthe block B comprises monomer units derived from a compound selected from a fluorinated (meth)acrylic ester having the following formula (I): H2C═CR1(C(O)ORF−1)  (I)whereinR1 is H or methyl, andRF−1 is an organic residue containing a perfluorinated C4-6 alkyl group,a fluorinated alpha-olefin having the following formula (II): H2C═CH(RF−2)  (II)wherein RF−2 is an organic residue containing a perfluorinated C4-6 alkyl group, or a mixture thereof.
  • 17. The method to lower the dynamic surface tension of a composition according to claim 16, wherein the composition is one composition selected from the group consisting of a high solids coating composition, a powder coating composition, a solvent-borne ink, a water-borne ink, a UV ink and a UV coating.
Priority Claims (1)
Number Date Country Kind
12156662.4 Feb 2012 EP regional
CROSS REFERENCE TO RELATED APPLICATIONS

This application is a divisional application of prior U.S. application Ser. No. 14/375,670, filed Jul. 30, 2014, the disclosure of which is incorporated herein by reference in its entirety. The parent application is the National Stage of PCT/EP13/053567, filed Feb. 22, 2013, the disclosure of which is incorporated herein by reference in its entirety. PCT/EP13/053567 is the non-provisional application from prior U.S. Provisional Application No. 61/602,096, filed Feb. 23, 2012, the disclosure of which is incorporated herein by reference in its entirety. The parent application claims priority to European Application No. 12156662.4, filed Feb. 23, 2012, the disclosure of which is incorporated herein by reference in its entirety.

Provisional Applications (1)
Number Date Country
61602096 Feb 2012 US
Divisions (1)
Number Date Country
Parent 14375670 Jul 2014 US