Fluorinated electrolyte compositions

Information

  • Patent Grant
  • 9979050
  • Patent Number
    9,979,050
  • Date Filed
    Friday, August 31, 2012
    12 years ago
  • Date Issued
    Tuesday, May 22, 2018
    6 years ago
Abstract
Electrolyte compositions containing a solvent mixture comprising 2,2,-difluoroethyl acetate and ethylene carbonate are described. The electrolyte compositions are useful in electrochemical cells, such as lithium ion batteries.
Description
TECHNICAL FIELD

The disclosure hereof relates to electrolyte compositions containing 2,2,-difluoroethyl acetate and ethylene carbonate, which are useful in electrochemical cells, such as lithium ion batteries.


BACKGROUND

Carbonate compounds are currently used as electrolyte solvents for non-aqueous batteries containing electrodes made from alkali metals, alkaline earth metals, or compounds comprising these metals, for example lithium ion batteries. Current lithium ion battery electrolyte solvents typically contain one or more linear carbonates, such as ethyl methyl carbonate, dimethyl carbonate, or diethylcarbonate; and a cyclic carbonate, such as ethylene carbonate. However, at battery voltages above 4.4 V these electrolyte solvents can decompose, which can result in a loss of battery performance. Additionally, there are safety concerns with the use of these electrolyte solvents because of their low boiling point and high flammability.


To overcome the limitations of commonly used non-aqueous electrolyte solvents, various fluorine-containing carboxylic acid ester electrolyte solvents have been investigated for use in lithium ion batteries (see, for example, Nakamura et al in JP 4/328,915-B2, JP 3/444,607-B2, and U.S. Pat. No. 8,097,368). Although these fluorine-containing carboxylic acid ester electrolyte solvents can be used in lithium ion batteries having high voltage cathodes, such as the 4.7 V LiMn1.5Ni0.5O4 cathode, cycling performance can be limited, particularly at high temperatures.


Despite the efforts in the art as described above, a need remains for electrolyte solvents, and compositions thereof, that will have improved cycling performance at high temperature when used in a lithium ion battery, particularly such a battery that operates at high voltage (i.e. up to about 5 V), or that incorporates a high voltage cathode.


SUMMARY

In one embodiment, there is provided herein an electrolyte composition comprising:


(a) at least one electrolyte salt; and


(b) a solvent mixture comprising ethylene carbonate and CH3CO2CH2CF2H.


In another embodiment, there is provided herein an electrolyte composition comprising:


(a) at least one electrolyte salt; and


(b) a solvent mixture comprising ethylene carbonate at a concentration of about 10% to about 50% by weight of the solvent mixture; and CH3CO2CH2CF2H at a concentration of about 50% to about 90% by weight of the solvent mixture.


In yet another embodiment, there is provided herein an electrochemical cell comprising the electrolyte composition disclosed herein.


In a further embodiment, the electrochemical cell is a lithium ion battery.





BRIEF DESCRIPTION OF THE DRAWINGS


FIGS. 1-3 are voltage vs. capacity curves for the first charge and discharge cycles for full cells containing the electrolyte compositions disclosed herein, as described in Examples 5-6 and Comparative Example 2, respectively.





DETAILED DESCRIPTION

As used above and throughout the description of the invention, the following terms, unless otherwise indicated, shall be defined as follows:


The term “electrolyte composition” as used herein, refers to a chemical composition suitable for use as an electrolyte in an electrochemical cell. An electrolyte composition typically comprises at least one solvent and at least one electrolyte salt.


The term “electrolyte salt” as used herein, refers to an ionic salt that is at least partially soluble in the solvent of the electrolyte composition and that at least partially dissociates into ions in the solvent of the electrolyte composition to form a conductive electrolyte composition.


The term “anode” refers to the electrode of an electrochemical cell, at which oxidation occurs. In a galvanic cell, such as a battery, the anode is the negatively charged electrode. In a secondary (i.e. rechargeable) battery, the anode is the electrode at which oxidation occurs during discharging and reduction occurs during charging.


The term “cathode” refers to the electrode of an electrochemical cell, at which reduction occurs. In a galvanic cell, such as a battery, the cathode is the positively charged electrode. In a secondary (i.e. rechargeable) battery, the cathode is the electrode at which reduction occurs during discharging and oxidation occurs during charging.


The term “lithium ion battery” refers to a type of rechargeable battery in which lithium ions move from the anode to the cathode during discharge, and from the cathode to the anode during charge.


Disclosed herein are electrolyte compositions comprising a fluorine-containing carboxylic acid ester and ethylene carbonate. The electrolyte compositions are useful in electrochemical cells, particularly lithium ion batteries. Specifically, the electrolyte compositions disclosed herein comprise at least one electrolyte salt, and a solvent mixture comprising CH3CO2CH2CF2H (2,2,-difluoroethyl acetate, CAS No. 1550-44-3), and ethylene carbonate (also referred to as 1,3-dioxolan-2-one, CAS No. 96-49-1).


In one embodiment, ethylene carbonate comprises about 10% to about 50% by weight of the solvent mixture. In another embodiment, ethylene carbonate comprises about 20% to about 40% by weight of the solvent mixture. In another embodiment, ethylene carbonate comprises about 25% to about 35% by weight of the solvent mixture. In another embodiment, ethylene carbonate comprises about 30% by weight of the solvent mixture.


In an alternative embodiment, 2,2,-difluoroethyl acetate comprises about 50% to about 90% by weight of the solvent mixture. In another embodiment, 2,2,-difluoroethyl acetate comprises about 60% to about 80% by weight of the solvent mixture. In another embodiment, 2,2,-difluoroethyl acetate comprises about 65% to about 75% by weight of the solvent mixture. In another embodiment, 2,2,-difluoroethyl acetate comprises about 70% by weight of the solvent mixture.


Ethylene carbonate of suitable purity for use in the electrolyte compositions disclosed herein may be obtained from commercial sources such as Novolyte (Independence, Ohio). The 2,2,-difluoroethyl acetate may be prepared using methods known in the art. For example, acetyl chloride may be reacted with 2,2-difluoroethanol (with or without a basic catalyst) to form 2,2-difluoroethyl acetate. Additionally, 2,2-difluoroethyl acetate may be prepared using the method described by Wiesenhofer et al. (WO 2009/040367 A1, Example 5). Alternatively, 2,2-difluoroethyl acetate can be prepared using the method described in the examples herein below. It is desirable to purify the 2,2-difluoroethyl acetate to a purity level of at least about 99.9%, more particularly at least about 99.99%. The 2,2-difluoroethyl acetate may be purified using distillation methods such as vacuum distillation or spinning band distillation.


The electrolyte compositions disclosed herein also contain at least one electrolyte salt. Suitable electrolyte salts include without limitation


lithium hexafluorophosphate,


LiPF3(CF2CF3)3,


lithium bis(trifluoromethanesulfonyl)imide,


lithium bis(perfluoroethanesulfonyl)imide,


lithium (fluorosulfonyl) (nonafluorobutanesulfonyl)imide,


lithium bis(fluorosulfonyl)imide,


lithium tetrafluoroborate,


lithium perchlorate,


lithium hexafluoroarsenate,


lithium trifluoromethanesulfonate,


lithium tris(trifluoromethanesulfonyl)methide,


lithium bis(oxalato)borate,


lithium difluoro(oxalato)borate,


Li2B12F12-xHx where x is equal to 0 to 8, and mixtures of lithium fluoride and anion receptors such as B(OC6F5)3.


Mixtures of two or more of these or comparable electrolyte salts may also be used. In one embodiment, the electrolyte salt is lithium hexafluorophosphate. The electrolyte salt can be present in the electrolyte composition in an amount of about 0.2 to about 2.0 M, more particularly about 0.3 to about 1.5 M, more particularly about 0.5 to about 1.2 M, and more particularly about 1.0 to about 1.2 M.


The electrolyte composition disclosed herein may further comprise at least one additional co-solvent. Examples of suitable co-solvents include without limitation one or more carbonates. Suitable carbonates include ethyl methyl carbonate, dimethyl carbonate, diethyl carbonate, propylene carbonate, vinylethylene carbonate, fluoroethylene carbonate, 2,2,2-trifluoroethyl carbonate, and methyl 2,2,3,3-tetrafluoropropyl carbonate. In other embodiments, suitable co-solvents include without limitation those selected from the group consisting of ethyl methyl carbonate, dimethyl carbonate, diethyl carbonate, propylene carbonate, vinylethylene carbonate, 2,2,2-trifluoroethyl carbonate, and methyl 2,2,3,3-tetrafluoropropyl carbonate. It is desirable to use a co-solvent that is battery grade or has a purity level of at least about 99.9%, and more particularly at least about 99.99%. When an additional co-solvent is used, the co-solvent comprises about 10% to about 40% by weight, or about 15% to about 35% by weight, or about 20% to about 30% by weight, of the solvent mixture.


When fluoroethylene carbonate (also referred to herein as 4-fluoro-1,3-dioxolan-2-one, CAS No. 114435-02-8) is used as the co-solvent, it can if desired be used in an amount of about 0.01% to less than 2%, more particularly about 0.1% to about 1.8%, more particularly about 0.5% to about 1.5%, and more particularly about 1% by weight of the total electrolyte composition. It is desirable to purify the fluoroethylene carbonate to a purity level of at least about 99.0%, more particularly at least about 99.9%. Purification may be done using known methods, as described above. Fluoroethylene carbonate is available from companies such as China LangChem INC. (Shanghai, China) and MTI Corp. (Richmond, Calif.).


In a further alternative embodiment, ethylene carbonate comprises about 10% to about 50% by weight of the solvent mixture; and 2,2,-difluoroethyl acetate comprises about 50% to about 90% by weight of the solvent mixture.


In a further alternative embodiment, ethylene carbonate comprises about 20% to about 40% by weight of the solvent mixture; and 2,2,-difluoroethyl acetate comprises about 60% to about 80% by weight of the solvent mixture.


In a further alternative embodiment, ethylene carbonate comprises about 25% to about 35% by weight of the solvent mixture; and 2,2,-difluoroethyl acetate comprises about 65% to about 75% by weight of the solvent mixture.


In a further alternative embodiment, ethylene carbonate comprises about 10% to about 50% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 50% to about 90% by weight of the solvent mixture; and a co-solvent comprises about 10% to about 40% by weight of the solvent mixture.


In a further alternative embodiment, ethylene carbonate comprises about 10% to about 50% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 50% to about 90% by weight of the solvent mixture; and a co-solvent comprises about 15% to about 35% by weight of the solvent mixture.


In a further alternative embodiment, ethylene carbonate comprises about 10% to about 50% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 50% to about 90% by weight of the solvent mixture; and a co-solvent comprises about 20% to about 30% by weight of the solvent mixture.


In a further alternative embodiment, ethylene carbonate comprises about 10% to about 50% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 50% to about 90% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.01% to less than 2% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 10% to about 50% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 50% to about 90% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.1% to less than 1.8% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 10% to about 50% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 50% to about 90% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.5% to about 1.5% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 20% to about 40% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 60% to about 80% by weight of the solvent mixture; and a co-solvent comprises about 10% to about 40% by weight of the solvent mixture.


In a further alternative embodiment, ethylene carbonate comprises about 20% to about 40% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 60% to about 80% by weight of the solvent mixture; and a co-solvent comprises about 15% to about 35% by weight of the solvent mixture.


In a further alternative embodiment, ethylene carbonate comprises about 20% to about 40% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 60% to about 80% by weight of the solvent mixture; and a co-solvent comprises about 20% to about 30% by weight of the solvent mixture.


In a further alternative embodiment, ethylene carbonate comprises about 20% to about 40% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 60% to about 80% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.01% to less than 2% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 20% to about 40% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 60% to about 80% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.1% to less than 1.8% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 20% to about 40% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 60% to about 80% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.5% to about 1.5% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 25% to about 35% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 65% to about 75% by weight of the solvent mixture; and a co-solvent comprises about 10% to about 40% by weight of the solvent mixture.


In a further alternative embodiment, ethylene carbonate comprises about 25% to about 35% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 65% to about 75% by weight of the solvent mixture; and a co-solvent comprises about 15% to about 35% by weight of the solvent mixture.


In a further alternative embodiment, ethylene carbonate comprises about 25% to about 35% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 65% to about 75% by weight of the solvent mixture; and a co-solvent comprises about 20% to about 30% by weight of the solvent mixture.


In a further alternative embodiment, ethylene carbonate comprises about 25% to about 35% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 65% to about 75% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.01% to less than 2% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 25% to about 35% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 65% to about 75% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.1% to less than 1.8% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 25% to about 35% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 65% to about 75% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.5% to about 1.5% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 10% to about 50% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 50% to about 90% by weight of the solvent mixture; a co-solvent comprises about 10% to about 40% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.01% to less than 2% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 10% to about 50% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 50% to about 90% by weight of the solvent mixture; a co-solvent comprises about 10% to about 40% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.1% to about 1.8% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 10% to about 50% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 50% to about 90% by weight of the solvent mixture; a co-solvent comprises about 10% to about 40% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.5% to about 1.5% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 10% to about 50% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 50% to about 90% by weight of the solvent mixture; a co-solvent comprises about 15% to about 35% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.01% to less than 2% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 10% to about 50% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 50% to about 90% by weight of the solvent mixture; a co-solvent comprises about 15% to about 35% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.1% to about 1.8% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 10% to about 50% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 50% to about 90% by weight of the solvent mixture; a co-solvent comprises about 15% to about 35% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.5% to about 1.5% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 10% to about 50% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 50% to about 90% by weight of the solvent mixture; a co-solvent comprises about 20% to about 30% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.01% to less than 2% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 10% to about 50% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 50% to about 90% by weight of the solvent mixture; a co-solvent comprises about 20% to about 30% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.1% to about 1.8% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 10% to about 50% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 50% to about 90% by weight of the solvent mixture; a co-solvent comprises about 20% to about 30% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.5% to about 1.5% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 20% to about 40% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 60% to about 80% by weight of the solvent mixture; a co-solvent comprises about 10% to about 40% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.01% to less than 2% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 20% to about 40% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 60% to about 80% by weight of the solvent mixture; a co-solvent comprises about 10% to about 40% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.1% to about 1.8% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 20% to about 40% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 60% to about 80% by weight of the solvent mixture; a co-solvent comprises about 10% to about 40% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.5% to about 1.5% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 20% to about 40% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 60% to about 80% by weight of the solvent mixture; a co-solvent comprises about 15% to about 35% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.01% to less than 2% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 20% to about 40% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 60% to about 80% by weight of the solvent mixture; a co-solvent comprises about 15% to about 35% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.1% to about 1.8% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 20% to about 40% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 60% to about 80% by weight of the solvent mixture; a co-solvent comprises about 15% to about 35% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.5% to about 1.5% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 20% to about 40% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 60% to about 80% by weight of the solvent mixture; a co-solvent comprises about 20% to about 30% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.01% to less than 2% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 20% to about 40% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 60% to about 80% by weight of the solvent mixture; a co-solvent comprises about 20% to about 30% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.1% to about 1.8% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 20% to about 40% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 60% to about 80% by weight of the solvent mixture; a co-solvent comprises about 20% to about 30% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.5% to about 1.5% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 25% to about 35% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 65% to about 75% by weight of the solvent mixture; a co-solvent comprises about 10% to about 40% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.01% to less than 2% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 25% to about 35% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 65% to about 75% by weight of the solvent mixture; a co-solvent comprises about 10% to about 40% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.1% to about 1.8% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 25% to about 35% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 65% to about 75% by weight of the solvent mixture; a co-solvent comprises about 10% to about 40% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.5% to about 1.5% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 25% to about 35% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 65% to about 75% by weight of the solvent mixture; a co-solvent comprises about 15% to about 35% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.01% to less than 2% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 25% to about 35% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 65% to about 75% by weight of the solvent mixture; a co-solvent comprises about 15% to about 35% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.1% to about 1.8% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 25% to about 35% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 65% to about 75% by weight of the solvent mixture; a co-solvent comprises about 15% to about 35% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.5% to about 1.5% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 25% to about 35% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 65% to about 75% by weight of the solvent mixture; a co-solvent comprises about 20% to about 30% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.01% to less than 2% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 25% to about 35% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 65% to about 75% by weight of the solvent mixture; a co-solvent comprises about 20% to about 30% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.1% to about 1.8% by weight of the total electrolyte composition.


In a further alternative embodiment, ethylene carbonate comprises about 25% to about 35% by weight of the solvent mixture; 2,2,-difluoroethyl acetate comprises about 65% to about 75% by weight of the solvent mixture; a co-solvent comprises about 20% to about 30% by weight of the solvent mixture; and fluoroethylene carbonate comprises an amount of about 0.5% to about 1.5% by weight of the total electrolyte composition.


In another embodiment, the invention provides an electrochemical cell comprising a housing, an anode and a cathode disposed in the housing and in conductive contact with one another, an electrolyte composition, as described above, providing an ionically conductive pathway between the anode and the cathode, and a porous separator between the anode and the cathode. The housing may be any suitable container to house the electrochemical cell components. The anode and the cathode may be comprised of any suitable conducting material depending on the type of electrochemical cell. Suitable examples of anode materials include without limitation lithium metal, lithium metal alloys, lithium titanate, aluminum, platinum, palladium, graphite, transition metal oxides, and lithiated tin oxide. Suitable examples of cathode materials include without limitation graphite, aluminum, platinum, palladium, electroactive transition metal oxides comprising lithium, indium tin oxide, and conducting polymers such as polypyrrole and polyvinylferrocene.


The porous separator serves to prevent short circuiting between the anode and the cathode. The porous separator typically consists of a single-ply or multi-ply sheet of a microporous polymer such as polyethylene, polypropylene, or a combination thereof. The separator may also be a polyimide nanoweb (EP 2037029; U.S. Patent Application No. 2011/0143217 A1). The pore size of the porous separator is sufficiently large to permit transport of ions, but small enough to prevent contact of the anode and cathode either directly or from particle penetration or dendrites which can form on the anode and cathode.


In another embodiment, the electrochemical cell is a lithium ion battery. Suitable cathode materials for a lithium ion battery include without limitation electroactive transition metal oxides comprising lithium, such as LiCoO2, LiNiO2, LiMn2O4 or LiV3O8; oxides of layered structure such as LiNixMnyCozO2 where x+y+z is about 1, LiCo0.2Ni0.2O2, LiFePO4, LiMnPO4, LiCoPO4, LiNi0.5Mn1.5O4, or LiVPO4F; mixed metal oxides of cobalt, manganese, and nickel such as those described in U.S. Pat. No. 6,964,828 (Lu) and U.S. Pat. No. 7,078,128 (Lu); nanocomposite cathode compositions such as those described in U.S. Pat. No. 6,680,145 (Obrovac); lithium-rich layered-layered composite cathodes such as those described in U.S. Pat. No. 7,468,223; and cathodes such as those described in U.S. Pat. No. 7,718,319 and the references therein (each of the above mentioned U.S. patents being by this reference incorporated in its entirety as a part hereof for all purposes).


In another embodiment, the cathode in the lithium ion battery hereof comprises a cathode active material exhibiting greater than 30 mAh/g capacity in the potential range greater than 4.6 V versus lithium metal. One example of such a cathode is a manganese cathode comprising a lithium-containing manganese composite oxide having a spinel structure as cathode active material. The lithium-containing manganese composite oxide in a cathode suitable for use herein comprises oxides of the formula

LizMn1.5NixMyO4-d,  (Formula I)

wherein M is at least one metal selected from the group consisting of Al, Cr, Fe, Ga, Zn, Co, Nb, Mo, Ti, Zr, Mg, V and Cu, 0.38≤x<0.5, 0<y≤0.12, 0≤d≤0.3, and 0.00<z≤1.1, and z changes in accordance with release and uptake of lithium ions and electrons during charge and discharge.


In one embodiment, M in the above formula is Fe; in another embodiment, M in the above formula is Ga; and in another embodiment, M is the above formula is Fe and Ga. In the various embodiments hereof, the values of x and y can be selected from any one of the members of the group of couples consisting of: x=0.38/y=0.12, x=0.39/y=0.11, x=0.40/y=0.1, x=0.41/y=0.09, x=0.42/y=0.08, x=0.43/y=0.07, x=0.44/y=0.06, x=0.45/y=0.05, x=0.46/y=0.04, x=0.47/y=0.03, x=0.48/y=0.02, x=0.49/y=0.01.


In one embodiment, z has a value given by 0.03≤z≤1.1. In another embodiment, z has a value given by 0.03≤z≤1.0. In one embodiment, M in the above formula is at least one metal selected from the group consisting of Al, Cr, Fe, Ga and Zn, 0.4≤x<0.5, 0<y≤0.1, z=1 and d=0.


The lithium cathode material described above is believed to be stabilized by the presence of the M component in the compound. Manganese cathodes stabilized by other systems may also comprise spinel-layered composites which contain a manganese-containing spinel component and a lithium rich layered structure, as described in U.S. Pat. No. 7,303,840.


A cathode active material suitable for use herein can be prepared using methods such as the hydroxide precursor method described by Liu et al (J. Phys. Chem. C 13:15073-15079, 2009). In that method, hydroxide precursors are precipitated from a solution containing the required amounts of manganese, nickel and other desired metal(s) acetates by the addition of KOH. The resulting precipitate is oven-dried and then fired with the required amount of LiOH.H2O at about 800 to about 950° C. in oxygen for 3 to 24 hours, as described in detail in the examples herein. Alternatively, the cathode active material can be prepared using a solid phase reaction process or a sol-gel process as described in U.S. Pat. No. 5,738,957 (Amine).


A cathode, in which the cathode active material is contained, suitable for use herein may be prepared by methods such as mixing an effective amount of the cathode active material (e.g. about 70 wt % to about 97 wt %), a polymer binder, such as polyvinylidene difluoride, and conductive carbon in a suitable solvent, such as N-methylpyrrolidone, to generate a paste, which is then coated onto a current collector such as aluminum foil, and dried to form the cathode.


A lithium ion battery as disclosed herein can further contain an anode, which comprises an anode active material that is capable of storing and releasing lithium ions. Examples of suitable anode active materials include without limitation lithium alloys such as lithium-aluminum alloy, lithium-lead alloy, lithium-silicon alloy, lithium-tin alloy and the like; carbon materials such as graphite and mesocarbon microbeads (MCMB); phosphorus-containing materials such as black phosphorus, MnP4 and CoP3; metal oxides such as SnO2, SnO and TiO2; and lithium titanates such as Li4Ti5O12 and LiTi2O4. In one embodiment, the anode active material is lithium titanate or graphite.


An anode can be made by a method similar to that described above for a cathode wherein, for example, a binder such as a vinyl fluoride-based copolymer is dissolved or dispersed in an organic solvent or water, which is then mixed with the active, conductive material to obtain a paste. The paste is coated onto a metal foil, preferably aluminum or copper foil, to be used as the current collector. The paste is dried, preferably with heat, so that the active mass is bonded to the current collector. Suitable anode active materials and anodes are available commercially from companies such as NEI Inc. (Somerset N.J.), and Farasis Energy Inc. (Hayward Calif.).


A lithium ion battery as disclosed herein also contains a porous separator between the anode and cathode. The porous separator serves to prevent short circuiting between the anode and the cathode. The porous separator typically consists of a single-ply or multi-ply sheet of a microporous polymer such as polyethylene, polypropylene, polyamide or polyimide, or a combination thereof. The pore size of the porous separator is sufficiently large to permit transport of ions to provide ionically conductive contact between the anode and cathode, but small enough to prevent contact of the anode and cathode either directly or from particle penetration or dendrites which can from on the anode and cathode. Examples of porous separators suitable for use herein are disclosed in U.S. application Ser. No. 12/963,927 (filed 9 Dec. 2010), which is by this reference incorporated in its entirety as a part hereof for all purposes.


The housing of the lithium ion battery hereof may be any suitable container to house the lithium ion battery components described above. Such a container may be fabricated in the shape of small or large cylinder, a prismatic case or a pouch.


The lithium ion battery hereof may be used for grid storage or as a power source in various electronically-powered or -assisted devices (“Electronic Device”) such as a transportation device (including a motor vehicle, automobile, truck, bus or airplane), a computer, a telecommunications device, a camera, a radio or a power tool.


EXAMPLES

The subject matter disclosed herein is further defined in the following examples. It should be understood that these examples, while describing various features of certain particular embodiments of some of the inventions hereof, are given by way of illustration only.


The meaning of abbreviations used is as follows: “cm” means centimeter(s), “mm” means millimeter(s), “μm” means micrometer(s), “g” means gram(s), “mg” means milligram(s), “kg” means kilogram(s), “μg” means microgram(s), “L” means liter(s), “mL” means milliliter(s), “μL” means microliter(s), “mol” means mole(s), “mmol” means millimole(s), “M” means molar concentration, “h” means hour(s), “min” means minute(s), “s” means second(s), “wt %” means percent by weight, “Hz” means hertz, “mS” means millisiemen(s), “mA” mean milliamp(s), “mAh means milliamp 20 hour(s), “mAh/g” means milliamp hour(s) per gram, “mAh/cm2” means milliamp hour(s) per cm, “V” means volt(s), “dc” means direct current, “x C” refers to a constant current that can fully charge/discharge the cathode in 1/x hours, “kPa” means kilopascal(s), “rpm” means revolutions per 25 minute, “psi” means pounds per square inch.


Materials and Methods


Purification of 2,2-Difluoroethyl Acetate (DFEA)


2,2-Difluoroethyl acetate, obtained from Matrix Scientific (Columbia, S.C.), was purified by spinning band distillation twice to 99.99% purity, as determined by gas chromatography using a flame ionization detector.


Preparation of LiMn1.5Ni0.42Fe0.8O4 (Fe-LNMO) Cathode Active Material


For the preparation of LiMn1.5Ni0.42Fe0.08O4, 401 g manganese (II) acetate tetrahydrate (Aldrich, No. 63537), 121 g nickel (II) acetate tetrahydrate (measured to have 4.8 water of hydration) (Aldrich, No. 72225) and 15.25 g iron (II) acetate anhydrous (Alfa Aesar, Ward Hill, Mass., No. 31140) were weighed into bottles on a balance then dissolved in 5.0 L of deionized water. KOH pellets were dissolved in 10 L of deionized water to produce a 3.0 M solution inside a 30 L reactor. The acetate solution was transferred to an addition funnel and dripped into the rapidly stirred reactor to precipitate the mixed hydroxide material. Once all 5.0 L of the acetate solution was added to the reactor, stirring was continued for 1 h. Then, stirring was stopped and the precipitate was allowed to settle overnight. After settling the liquid was removed from the reactor and 15 L of fresh deionized water was added. The contents of the reactor were stirred, allowed to settle again, and the liquid was removed. This rinse process was repeated. Then, the precipitate was transferred to two (split evenly) coarse glass frit filtration funnels covered with Dacron® paper. The solids were rinsed with deionized water until the filtrate pH reached 6 (i.e., the pH of deionized rinse water), and a further 20 L of deionized water was added to each filter cake. Finally the cakes were dried in a vacuum oven at 120° C. overnight. The yield at this point was typically 80-90%.


The hydroxide precipitate was next ground and mixed with lithium carbonate. This step was done in 50 g batches using a Pulverisette automated mortar and pestle (Fritsch GmbH, Idar-Oberstein, Germany). For each batch the hydroxide mixture was weighed, then ground alone for 5 min in the Pulveresette. Then, a stoichiometric amount with small excess of lithium carbonate was added to the system. For 50 g of hydroxide 10.5 g of lithium carbonate was added. Grinding was continued for a total of 60 min with stops every 10-15 min to scrape the material off the surfaces of the mortar and pestle with a sharp metal spatula. If humidity caused the material to form clumps, it was sieved through a 40 mesh screen once during grinding, then again following grinding.


The ground material was fired in an air box furnace inside shallow rectangular alumina trays. The trays were 158 mm by 69 mm in size, and each held about 60 g of material. The firing procedure consisted of ramping from room temperature to 900° C. in 15 h, holding at 900° C. for 12 h, then cooling to room temperature in 15 h.


Preparation of an Iron-Doped, Lithium, Nickel, Manganese Oxide (Fe-LNMO) Cathode


A cathode paste was prepared from: 3.12 g Fe-LNMO (prepared as described above), 0.390 g carbon black (acetylene black, uncompressed, Denka Corp., New York, N.Y.), 3.24 g of polyvinylidene difluoride (PVDF) solution, 12% in N-methylpyrrolidone (NMP) (KFL #1120, Kureha America Corp., New York, N.Y.) and of 6.17 g NMP. The Fe-LNMO was ground using a mortar and pestle and sifted through a 400 mesh sieve. The carbon black, 5.82 g of NMP, and the PVDF solution were combined in a plastic vial and mixed using a planetary centrifugal mixer (THINKY ARE-310, THINKY Corp., Japan) for 1 min at 2000 rpm. The vial was removed from the mixer, allowed to briefly cool, and the mixing was repeated two more times for a total of three times. The Fe-LNMO and 0.35 g of NMP were then added and centrifugally mixed three times for 1 min at 2000 rpm each time. The vial was mounted in an ice bath and homogenized twice using a rotor-stator (model PT 10-35 GT, 7.5 mm diameter stator, Kinematicia, Bohemia, N.Y.) for min each at 6500 rpm and then twice more for 15 min at 9500 rpm.


The paste was cast using a 50 mm wide doctor blade with a 0.19 mm gate height onto untreated aluminum foil. The electrode was dried in a mechanical convection oven (model FDL-115, Binder Inc., Great River, N.Y.) for 15 min at 100° C. The loading of Fe-LNMO was about 3 mg/cm2. The resulting 50-mm wide electrode was placed between 250 μm thick brass sheets and passed through a calender using 102 mm diameter steel rolls at ambient temperature with a nip force of 330 kg. The electrode was further dried in a vacuum oven at 90° C. at −25 inches of Hg (−85 kPa) for 15 h.


Preparation of a Lithium Titanate (LTO) Anode


The following were used to make the anode paste: 4.16 g Li4Ti5O12 (LTO, Nanomyte™ BE-10, NEI Corporation, Somerset, N.J.), 4.00 g PVDF solution, 12% in NMP (KFL #1120, Kureha America Corp.), 0.52 g carbon black (acetylene black, uncompressed, Denka Corp., New York, N.Y.), and 9.50 g NMP. The carbon black, PVDF solution, and 8.04 g of the NMP were first combined in a plastic vial and centrifugally mixed (THINKY ARE-310, THINKY Corp., Japan) for 60 s at 2000 rpm. The vial was removed from the mixer, allowed to briefly cool, and the mixing was repeated two more times for a total of three times. The LTO powder, along with the additional NMP, were added to the carbon black and PVDF mixture, and the paste was centrifugally mixed three times for 60 s each time. The vial was mounted in an ice bath and homogenized twice using a rotor-stator (model PT 10-35 GT, 7.5 mm diameter stator, Kinematicia, Bohemia, N.Y.) for 15 min each at 6500 rpm and then twice more for 15 min at 9500 rpm. The paste was cast using a 50 mm wide doctor blade with a 0.25 mm gate height onto untreated aluminum foil. The electrode was dried in a mechanical convection oven (model FDL-115, Binder Inc., Great River, N.Y.) for 15 min at 100 CC. After removal of NMP, the anode consisted of 80:10:10 LTO:PVDF:Carbon Black. The loading of LTO was about 4 mg/cm2. The resulting 50-mm wide electrode was placed between 250 μm thick brass sheets and passed through a calender using 102 mm diameter steel rolls at ambient temperature with a nip force of 250 kg. The electrode was further dried in a vacuum oven at 90° C. at −25 inches of Hg (−85 kPa) for 15 h.


Fabrication of LiMn1.5Ni0.42Fe0.08O4/Li4Ti5O12 Full Cells


A LiMn1.5Ni0.42Fe0.08O4, cathode, prepared as described above, a Celgard® separator 2325 (Celgard, LLC. Charlotte, N.C.), a Li4Ti5O12 anode, prepared as described above, and a few drops of the electrolyte composition of interest, as described below, were sandwiched in 2032 stainless steel coin cell cans to form the LiMn1.5Ni0.42Fe0.08O4/Li4Ti5O12 full cells.


Circular pieces of the separator were cut with a ⅝ inch arch punch and the pieces were transferred to a glovebox. Circular sections of LiMn1.5Ni0.42Fe0.08O4 cathodes were cut with a ½ inch arch punch. The cells were cathode limited; that is, the anode loading was high enough such that a circular area of the same size could incorporate more lithium than could be released by the cathode based on conversion of Li4Ti5O12 to Li7Ti5O12.


Circular sections of the Li4Ti5O12 anodes were cut with a 9/16 inch arch punch. The pre-cut cathode and anode sections were heated to 90° C. for 12 h under vacuum in an antechamber, and then transferred to a glovebox.


The coin cells consisted of coin cell cases (SUS316L), spacer disks, wave springs, and caps, and a polypropylene gasket, all obtained from Hohsen Corp. (Osaka, Japan). The coin cell components were sonicated in ultra-high purity water with detergent for one hour, rinsed with ultra-high purity water for 60 min, and then dried at 90° C. under house vacuum. The cleaned coin cell components were transferred to a glovebox.


A spacer disk and a gasket were placed in the coin cell case and 90 μL of the electrolyte composition to be tested, as described below, was added. A circular separator was then placed on the wetted cathode. An additional 90 μL of electrolyte was added onto the separator. The circular anode section was placed on top of the separator. The spacer disk was set on the anode and all layers were aligned in the center of the coin cell case. The wave spring was set on top of the spacer disk and aligned. The cap was set on top of the wave spring and manually pushed into the gasket. The assembly was placed in an automated coin cell battery crimper (Hohsen Corp. Model SAHCC-2032, Osaka, Japan) and pressure was applied to seal the coin cell.


Comparative Example 1 and Working Examples 1-3
Preparation of Electrolyte Compositions

These Examples describe the preparation of electrolyte compositions containing lithium hexafluorophosphate salt and solvent mixtures comprising 2,2-difluoroethyl acetate (DFEA) and ethylene carbonate (EC); 2,2-difluoroethyl acetate and fluoroethylene carbonate (FEC); and 2,2-difluoroethyl acetate, ethylene carbonate and a small amount of fluoroethylene carbonate.


Electrolyte compositions containing DFEA, EC and 1.0 M LiPF6; and DFEA, FEC and 1.0 M LiPF6 were prepared by weighing predetermined amounts of the components into vials in a dry box. The lithium hexafluorophosphate (LiPF6) (battery grade, Stella Chemifa Corp., Tokyo, Japan) was weighed into each vial to give a final concentration of 1.0 M. Then, the first electrolyte solvent (DFEA, prepared as described above) and the second electrolyte solvent (EC, battery grade, obtained from Novolyte Corp. Cleveland, Ohio; or FEC, obtained from LongChem, Shanghai, China, and purified by vacuum distillation) were weighed into each vial to give the desired weight percent (wt %) of each component. An electrolyte composition containing DFEA, EC, 1.0 M LiPF6, and 1% FEC was prepared by weighing a predetermined amount of FEC and adding it to a predetermined amount of the electrolyte composition containing DFEA, EC and 1.0 M LiPF6. The components of the electrolyte compositions are summarized in Table 1.









TABLE 1







Electrolyte Compositions













First






Electrolyte
Second




LiPF6
Solvent
Electrolyte
Additive


Example
(M)
(wt %) a
Solvent (wt %) a
(wt %) b





1
1.0
DFEA (80%)
FEC (20%)
0%


Comparativec






1
1.0
DFEA (80%)
EC (20%)
0%


2
1.0
DFEA (70%)
EC (30%)
0%


3
1.0
DFEA (70%)
EC (30%)
FEC (1%)






a Weight percent solvent as a percentage of the total solvent mixture (does not include salt or additive)




b Weight percent in final electrolyte composition (includes both solvents, salt, and additive)




cElectrolyte composition as described in U.S. Pat. No 8,097,368, Example 1.







Example 4
Ionic Conductivity of Electrolyte Compositions

The electrical conductivity of the electrolyte compositions described in Comparative Example 1 and Working Examples 1-3 was measured using ac impedance spectroscopy over the frequency range of 0.1 to 1,000,000 Hz. The impedance results were fit with an equivalent circuit model to yield the dc resistance.


An electrical probe containing two wires was first calibrated over the conductivity range of 10 to 100,000 Hz using standard aqueous solutions of sodium chloride. Then, the electrical probe was placed in the electrolyte compositions to be measured. Ionic conductivity measurements were recorded at temperatures of 22 to 25° C. in a dry box. Results were extrapolated to 25° C. using the temperature dependence of 2.0%/° C. The results summarized in Table 2 are reported at 25° C.









TABLE 2







Ionic Conductivity of Electrolyte Compositions at 25° C.










Electrolyte Composition
Ionic Conductivity (mS/cm)







Comparative Example 1
7.00, 6.95



Example 1
7.65



Example 2
8.02, 7.97, 8.24, 8.10



Example 3
7.83










Electrolytes with high ionic conductivity are desired since low conductivity decreases battery performance at high rates of charging and discharging. Replacing the 20 wt % FEC in Comparative Example 1 with EC while maintaining the LiPF6 salt molarity constant (Example 1) increases the conductivity from 6.98 to 7.65 mS/cm. The conductivity can be further increased to 8.08 mS/cm by changing the ratio of the two solvents from 80:20 DFEA:EC to 70:30 DFEA:EC (Example 2). Adding 1% FEC to the 70:30 DFEA:EC and 1.0 M LiPF6 composition (Example 3) reduced the conductivity slightly to 7.83 mS/cm.


Working Examples 5-6, and Comparative Example 2
Formation Processing (Slow Cycling) of LiMn1.5Ni0.42Fe0.08O4/Li4Ti5O12 Full Cells

Lithium ion batteries are often cycled before use at a slow rate for one or more cycles, a process that is referred to as “formation”. Each coin cell, prepared as described above, was first charged at 0.1 C from its open circuit voltage to 3.4 V at room temperature using a commercial battery tester (Series 4000, Maccor, Tulsa, Okla.). This was followed by discharging each cell at 0.1 C from 3.4 V to 1.9 V. The 0.1 C charge and discharge were then repeated a second time between 1.9 and 3.4 V. Results for the formation process are compiled in FIGS. 1-3 and Table 3.


The three coin cells had similar first cycle charge capacities, with the small differences attributed to variations in the cathode loadings. The first cycle discharge capacity was much lower for the 80:20 DFEA:FEC and 1.0 M LiPF6 electrolyte composition (Comparative Example 2) than for the 70:30 DFEA:EC and 1.0 M LIPF6 electrolyte composition (Example 5) and the 70:30 DFEA:EC, 1.0 M LiPF6 and 1% FEC electrolyte composition (Example 6).


Although the general shape of the voltage vs. capacity curves was similar for charging all three cells (FIGS. 1-3), there was a notable difference in the discharge curves. Both the 70:30 DFEA:EC and 1.0 M LIPF6 electrolyte composition (Example 5, FIG. 1) and the 70:30 DFEA:EC, 1.0 M LiPF6 and 1% FEC electrolyte composition (Example 6, FIG. 2) yielded discharge curves in which the tail end of the capacity contained a shoulder at the 2.5 V plateau, which was also present during the charging process. This shoulder was not present for the 80:20 DFEA:FEC and 1.0 M LiPF6 electrolyte composition (Comparative Example 2, FIG. 3) due to the reduced first cycle discharge capacity for this inferior electrolyte. The reduced first cycle discharge capacity also corresponds to a loss in capacity for further cycling. This is demonstrated by the lower second cycle charge and discharge capacities for the cell containing 80:20 DFEA:FEC and 1.0 M LiPF6 electrolyte composition (Comparative Example 2) compared to the cells containing the other two electrolyte compositions (Examples 5 and 6), as shown in Table 3.









TABLE 3







Results of Initial Cycling of LiMn1.5Ni0.42Fe0.08O4/Li4Ti5O12 Full Cells


at C/10 and Room Temperature














First
First
Second
Second




Cycle
Cycle
Cycle
Cycle




Charge
Discharge
Charge
Discharge



Electrolyte
Capacity
Capacity
Capacity
Capacity


Example
Composition
(mAh)
(mAh)
(mAh)
(mAh)















5
Example 2
0.513
0.450
0.466
0.449


6
Example 3
0.504
0.429
0.447
0.429


Compar-
Comparative
0.525
0.330
0.421
0.363


ative 2
Example 1













Working Examples 7-8, and Comparative Example 3
Cycling of LiMn1.5Ni0.42Fe0.08O4/Li4Ti5O12 Full Cells at Elevated Temperature

Following the two-cycle formation process at room temperature, each cell was cycled in a commercial battery tester (Series 4000, Maccor, Tulsa, Okla.) at 55° C. between 1.9 V and 3.4 V using a cycling protocol in which the cell was cycled at constant current at C/2 for 29 cycles followed by a single cycle at constant current at C/5. This (29×C/2+1×C/5) cycling procedure was repeated times, for a total of 300 charge-discharge cycles. As a part of the cycling protocol, the impedance at 1000 Hz was measured following the completion of each charge step and the completion of each discharge step. Results are shown in Table 4.









TABLE 4







Results of Cycling LiMn1.5Ni0.42Fe0.08O4/Li4Ti5O12


Full Cells at 55° C.












Capacity
Coulombic




Retention
Efficiency



Electrolyte
for Cycle
for Cycle


Example
Composition
No. 299
No. 299





7
Example 2
44.4%
99.5%


8
Example 3
38.0%
98.9%


Comparative
Comparative
 7.8%
93.0%


Example 3
Example 1









The electrolyte composition containing 70:30 DFEA:EC and 1.0 M LiPF6 retained 44.4% of its initial capacity after 299 cycles at 55° C. (Example 7 in Table 4). After the first 50 cycles, the Coulombic efficiency stayed above 99% for the remaining cycles at C/2 and was 99.5% for the 299th cycle.


The electrolyte composition containing 70:30 DFEA:EC, 1.0 M LiPF6 and 1% FEC retained 38.0% capacity after 299 cycles at 55° C. (Example 8 in Table 4). The Coulombic efficiency was 98.7% at the 50th cycle and stayed above this value for the remaining cycles at C/2, reaching a value of 98.9% at the 299th cycle.


The electrolyte composition containing 80:20 DFEA:FEC and 1.0 M LiPF6 performed poorly in comparison to the other two electrolyte compositions that contained EC (Comparative Example 3 in Table 4). The capacity dropped quickly during the early stages of cycling, dropping below 50% by the 25th cycle. The capacity retention for the 299th cycle was 7.8%. The Coulombic efficiency was poor, never exceeding 96% for the cycles at C/2 and dropping to 93.0% by the 299th cycle.


In various embodiments of the lithium ion battery hereof, pairs of dopant metals and fluorinated solvent systems may be formed from (i) any one or more of all of the members of the total group of dopant metals disclosed herein (Al, Cr, Fe, Ga, Zn, Co, Nb, Mo, Ti, Zr, Mg, V and Cu), selected as described above as a single member or any subgroup of any size taken from the total group of doping metals in all the various different combinations of individual members of that total group, together with (ii) any one or more of all of the members of the total group of the fluorinated solvent systems disclosed herein, selected as described above as a single member or any subgroup of any size taken from the total group of those fluorinated solvent systems in all the various different combinations of individual members of that total group. Subgroups of the members of the groups of dopant metals or fluorinated solvents may be formed by omitting any one or more members from the respective whole groups as set forth above. As a result, the dopant metal or fluorinated solvent system (or pair thereof) may not only be the members of any subgroup of any size that may be formed from the whole group from all the various different combinations of individual members of the groups as set forth in the list above, but may also be made in the absence of the members that have been omitted from the whole group to form the subgroup. The subgroup formed by omitting various members from the whole group in the lists above may, moreover, be an individual member of the whole group such that the dopant metal or fluorinated solvent system (or pair thereof) may be selected in the absence of all other members of the whole group except the selected individual member.


In this specification, unless explicitly stated otherwise or indicated to the contrary by the context of usage, where an embodiment of the subject matter hereof is stated or described as comprising, including, containing, having, being composed of or being constituted by or of certain features or elements, one or more features or elements in addition to those explicitly stated or described may be present in the embodiment. An alternative embodiment of the subject matter hereof, however, may be stated or described as consisting essentially of certain features or elements, in which embodiment features or elements that would materially alter the principle of operation or the distinguishing characteristics of the embodiment are not present therein. A further alternative embodiment of the subject matter hereof may be stated or described as consisting of certain features or elements, in which embodiment, or in insubstantial variations thereof, only the features or elements specifically stated or described are present.


Where a range of numerical values is recited or established herein, the range includes the endpoints thereof and all the individual integers and fractions within the range, and also includes each of the narrower ranges therein formed by all the various possible combinations of those endpoints and internal integers and fractions to form subgroups of the larger group of values within the stated range to the same extent as if each of those narrower ranges was explicitly recited. Where a range of numerical values is stated herein as being greater than a stated value, the range is nevertheless finite and is bounded on its upper end by a value that is operable within the context of the invention as described herein. Where a range of numerical values is stated herein as being less than a stated value, the range is nevertheless bounded on its lower end by a non-zero value.


In this specification, unless explicitly stated otherwise or indicated to the contrary by the context of usage,

    • (a) lists of compounds, monomers, oligomers, polymers and/or other chemical materials include derivatives of the members of the list in addition to mixtures of two or more of any of the members and/or any of their respective derivatives; and
    • (b) amounts, sizes, ranges, formulations, parameters, and other quantities and characteristics recited herein, particularly when modified by the term “about”, may but need not be exact, and may also be approximate and/or larger or smaller (as desired) than stated, reflecting tolerances, conversion factors, rounding off, measurement error and the like, as well as the inclusion within a stated value of those values outside it that have, within the context of this invention, functional and/or operable equivalence to the stated value.

Claims
  • 1. An electrolyte composition comprising: (a) at least one electrolyte salt;(b) a solvent mixture comprising ethylene carbonate at a concentration of about 10% to about 50% by weight of the solvent mixture; and CH3CO2CH2CF2H at a concentration of about 50% to about 90% by weight of the solvent mixture; and(c) fluoroethylene carbonate at a concentration of about 0.01% to less than 2% by weight of the electrolyte composition.
  • 2. The electrolyte composition of claim 1, wherein the electrolyte salt is selected from one or more members of the group consisting of: lithium hexafluorophosphate,LiPF3(CF2CF3)3,lithium bis(trifluoromethanesulfonyl)imide,lithium bis (perfluoroethanesulfonyl)imide,lithium (fluorosulfonyl) (nonafluorobutanesulfonyl)imide,lithium bis(fluorosulfonyl)imide,lithium tetrafluoroborate,lithium perchlorate,lithium hexafluoroarsenate,lithium trifluoromethanesulfonate,lithium tris (trifluoromethanesulfonyl)methide,lithium bis(oxalato)borate,lithium difluoro(oxalato)borate,Li2B12F12-xHx where x is equal to 0 to 8, anda mixture of lithium fluoride and an anion receptor.
  • 3. The electrolyte composition of claim 2 wherein the electrolyte salt is lithium hexafluorophosphate.
  • 4. The electrolyte composition of claim 1, wherein the ethylene carbonate comprises about 30% by weight of the solvent mixture and the CH3CO2CH2CF2H comprises about 70% by weight of the solvent mixture.
  • 5. The electrolyte composition of claim 1, wherein the fluoroethylene carbonate comprises about 1% by weight of the electrolyte composition.
  • 6. An electrochemical cell comprising: (a) a housing;(b) an anode and a cathode disposed in said housing and in conductive contact with one another;(c) an electrolyte composition disposed in said housing and providing an ionically conductive pathway between said anode and said cathode, wherein the electrolyte composition comprises: (i) at least one electrolyte salt;(ii) a solvent mixture comprising ethylene carbonate at a concentration of about 10% to about 50% by weight of the solvent mixture; and CH3CO2CH2CF2H at a concentration of about 50% to about 90% by weight of the solvent mixture; and(iii) fluoroethylene carbonate at a concentration of about 0.01% to less than 2% by weight of the electrolyte composition; and(d) a porous separator between said anode and said cathode.
  • 7. The electrochemical cell of claim 6, wherein the ethylene carbonate comprises about 30% by weight of the solvent mixture and the CH3CO2CH2CF2H comprises about 70% by weight of the solvent mixture.
  • 8. The electrochemical cell of claim 6, wherein the fluoroethylene carbonate comprises about 1% by weight of the electrolyte composition.
  • 9. The electrochemical cell of claim 6, wherein said electrochemical cell is a lithium ion battery.
  • 10. An electronic device comprising an electrochemical cell according to claim 6.
Parent Case Info

This application claims priority under 35 U.S.C. § 119(e) from, and claims the benefit of, U.S. Provisional Application No. 61/530,545, filed 2 Sep. 2011, which is by this reference incorporated in its entirety as a part hereof for all purposes.

PCT Information
Filing Document Filing Date Country Kind 371c Date
PCT/US2012/053415 8/31/2012 WO 00 2/28/2014
Publishing Document Publishing Date Country Kind
WO2013/033579 3/7/2013 WO A
US Referenced Citations (164)
Number Name Date Kind
2824141 Zisman et al. Feb 1958 A
3006964 Oesterling Oct 1961 A
5273840 Dominey Dec 1993 A
5352548 Fujimoto et al. Apr 1994 A
5446134 Armand et al. Aug 1995 A
5534634 Appel et al. Jul 1996 A
5561232 Hao et al. Oct 1996 A
5659062 Yokoyama et al. Aug 1997 A
5738957 Amine et al. Apr 1998 A
5847156 Eldin et al. Dec 1998 A
5847188 Yokoyama et al. Dec 1998 A
5925283 Taniuchi et al. Jul 1999 A
5962166 Ein-Eli et al. Oct 1999 A
6168878 Fauteux et al. Jan 2001 B1
6337158 Nakajima et al. Jan 2002 B1
6420069 Amine et al. Jul 2002 B2
6465135 Nishimura et al. Oct 2002 B1
6495293 Arai et al. Dec 2002 B1
6506516 Wietelmann et al. Jan 2003 B1
6506524 McMillan et al. Jan 2003 B1
6534220 Garbe Mar 2003 B2
6680145 Obrovac et al. Jan 2004 B2
6723473 Oura et al. Apr 2004 B1
6878492 Takeuchi et al. Apr 2005 B2
6958198 Iwamoto et al. Oct 2005 B2
6964828 Lu et al. Nov 2005 B2
7026070 Noguchi et al. Apr 2006 B2
7078128 Lu et al. Jul 2006 B2
7229718 Yamaguchi et al. Jun 2007 B2
7303840 Thackeray et al. Dec 2007 B2
7312001 Kim et al. Dec 2007 B2
7381496 Onnerud et al. Jun 2008 B2
7416813 Fujihara et al. Aug 2008 B2
7468223 Thackeray et al. Dec 2008 B2
7491471 Yamaguchi et al. Feb 2009 B2
7541114 Ohzuku et al. Jun 2009 B2
7635536 Johnson et al. Dec 2009 B2
7718319 Manthiram et al. May 2010 B2
7754389 Yamaguchi et al. Jul 2010 B2
7790308 Johnson et al. Jul 2010 B2
7981544 Morishima Jul 2011 B2
8092942 Chen et al. Jan 2012 B1
8097368 Chiga et al. Jan 2012 B2
8158285 Im et al. Apr 2012 B2
8178246 Shima May 2012 B2
8216726 Wakita et al. Jul 2012 B2
8277973 Kawashima Oct 2012 B2
8288039 Im et al. Oct 2012 B2
8367254 Im et al. Feb 2013 B2
8372549 Im et al. Feb 2013 B2
8389160 Venkatachalam et al. Mar 2013 B2
8394534 Lopez et al. Mar 2013 B2
8415056 Koh et al. Apr 2013 B2
8435680 Park et al. May 2013 B2
8455143 Lee et al. Jun 2013 B2
8535832 Kandasamy et al. Jul 2013 B2
8518525 Dennes et al. Aug 2013 B2
8530099 Chen et al. Sep 2013 B2
8546024 Jeon et al. Oct 2013 B2
8557447 Lee Oct 2013 B2
8586245 Yamaguchi et al. Nov 2013 B2
8668838 Takahashi et al. Mar 2014 B2
8673506 Jeon et al. May 2014 B2
8715852 Kim et al. May 2014 B2
8715865 Xu et al. May 2014 B2
8735005 Holstein et al. May 2014 B2
8795903 Smart et al. Aug 2014 B2
8871384 Koh et al. Oct 2014 B2
8877389 Koh et al. Nov 2014 B2
8945781 Chiga et al. Feb 2015 B2
8946452 Dietz et al. Feb 2015 B2
9093718 Dietz et al. Jul 2015 B2
9105943 Jeon et al. Aug 2015 B2
9246191 Jeon et al. Jan 2016 B2
20030180618 Inoue et al. Sep 2003 A1
20030190529 Kim et al. Oct 2003 A1
20040157133 Kim et al. Aug 2004 A1
20050196670 Yamaguchi et al. Sep 2005 A1
20060051671 Thackeray et al. Mar 2006 A1
20060115739 Yamaguchi et al. Jun 2006 A1
20060147808 Xiao et al. Jul 2006 A1
20060154149 Arai et al. Jul 2006 A1
20060216612 Jambunathan et al. Sep 2006 A1
20070042267 Kim et al. Feb 2007 A1
20070148540 Chiga et al. Jun 2007 A1
20070178379 Tamura et al. Aug 2007 A1
20070190412 Chiga et al. Aug 2007 A1
20070224504 Kita et al. Sep 2007 A1
20070287071 Chiga et al. Dec 2007 A1
20080102375 Shima May 2008 A1
20080131772 Jambunathan et al. May 2008 A1
20080145763 Koh et al. Jun 2008 A1
20080292971 Iharu et al. Nov 2008 A1
20090142663 Takeuchi et al. Jun 2009 A1
20090253044 Nogi et al. Oct 2009 A1
20090253048 Shima Oct 2009 A1
20100035162 Chiga Feb 2010 A1
20100047695 Smart et al. Feb 2010 A1
20100062344 Koh et al. Mar 2010 A1
20100081062 Chiga et al. Apr 2010 A1
20100108934 Flynn et al. May 2010 A1
20100119956 Tokuda et al. May 2010 A1
20100183926 Kim et al. Jul 2010 A1
20100190055 Khakhalev Jul 2010 A1
20100266904 Jeon et al. Oct 2010 A1
20100266905 Jeon et al. Oct 2010 A1
20100273064 Jeon et al. Oct 2010 A1
20110008684 Jeon et al. Jan 2011 A1
20110111305 Jeon et al. May 2011 A1
20110111307 Koh et al. May 2011 A1
20110123872 Koh et al. May 2011 A1
20110143217 Arora et al. Jun 2011 A1
20110171539 Patoux et al. Jul 2011 A1
20110195317 Koh et al. Aug 2011 A1
20110256458 Tani Oct 2011 A1
20110311866 Lim et al. Dec 2011 A1
20120009485 Xu Jan 2012 A1
20120136175 Fuseya et al. May 2012 A1
20120149852 Dennes et al. Jun 2012 A1
20120164519 Lee et al. Jun 2012 A1
20120164542 Iwaya Jun 2012 A1
20120196190 Jeon et al. Aug 2012 A1
20120208093 Ihara et al. Aug 2012 A1
20120219866 Onuki et al. Aug 2012 A1
20120301795 Kaneko et al. Nov 2012 A1
20120321965 Fujikawa et al. Dec 2012 A1
20120328938 Geiculescu et al. Dec 2012 A1
20130029230 Park et al. Jan 2013 A1
20130029231 Jeon et al. Jan 2013 A1
20130149602 Luski et al. Jun 2013 A1
20130189591 Nishimura et al. Jul 2013 A1
20130309564 Yoshida et al. Nov 2013 A1
20130337342 Hallac et al. Dec 2013 A1
20140017559 Kawasaki et al. Jan 2014 A1
20140017572 Uehara et al. Jan 2014 A1
20140045002 Yokoyama et al. Feb 2014 A1
20140045034 Kondo et al. Feb 2014 A1
20140045049 Iyori et al. Feb 2014 A1
20140045050 Hattori et al. Feb 2014 A1
20140045051 Hattori et al. Feb 2014 A1
20140045057 Tode et al. Feb 2014 A1
20140045077 Minami et al. Feb 2014 A1
20140079990 Yanagida et al. Mar 2014 A1
20140120415 Surugo et al. May 2014 A1
20140141323 Saruwatari et al. May 2014 A1
20140178772 Jeong et al. Jun 2014 A1
20140227584 Holstein et al. Aug 2014 A1
20140234701 Tanaka et al. Aug 2014 A1
20140243561 Mueller et al. Aug 2014 A1
20140248529 Chen et al. Sep 2014 A1
20140302401 Burkhardt et al. Oct 2014 A1
20140302402 Chen et al. Oct 2014 A1
20140308578 Onizuka et al. Oct 2014 A1
20140322579 Mitsuhashi et al. Oct 2014 A1
20140322616 Onizuka et al. Oct 2014 A1
20140329141 Onizuka et al. Nov 2014 A1
20150049642 Eng et al. Feb 2015 A1
20150086862 Osada et al. Mar 2015 A1
20150111112 Petrov et al. Apr 2015 A1
20150140444 Dubois et al. May 2015 A1
20150171467 Dubois et al. Jun 2015 A1
20150303521 Sasaki et al. Oct 2015 A1
20160049691 Suzuki et al. Feb 2016 A1
20160087307 Burkhardt et al. Mar 2016 A1
Foreign Referenced Citations (94)
Number Date Country
101617432 Dec 2009 CN
102790236 Nov 2012 CN
102983358 Mar 2013 CN
103117414 May 2013 CN
103165939 Jun 2013 CN
103682440 Mar 2014 CN
103730688 Apr 2014 CN
103943884 Jul 2014 CN
103972588 Aug 2014 CN
0924788 Jun 1999 EP
1890357 Feb 2008 EP
2037029 Mar 2009 EP
2365573 Sep 2011 EP
2378602 Oct 2011 EP
2535975 Dec 2012 EP
2571089 Mar 2013 EP
2626943 Aug 2013 EP
2339684 Sep 2013 EP
62290072 Dec 1987 JP
620719 Jan 1994 JP
3444607 Jan 1994 JP
08298134 Nov 1996 JP
H9-199168 Jul 1997 JP
3311611 May 1998 JP
10116627 Jun 1998 JP
1186901 Mar 1999 JP
2000188128 Jul 2000 JP
2001345120 Dec 2001 JP
2002124263 Apr 2002 JP
2003100342 Apr 2003 JP
2003282138 Oct 2003 JP
2004047131 Feb 2004 JP
2009123465 Jun 2004 JP
2004281185 Jul 2004 JP
2004241339 Aug 2004 JP
2005078820 Mar 2005 JP
2005293920 Oct 2005 JP
2006032300 Feb 2006 JP
2006140115 Jun 2006 JP
2006172721 Jun 2006 JP
2006172950 Jun 2006 JP
2006331866 Jul 2006 JP
2006210022 Aug 2006 JP
2008123714 May 2008 JP
2008159419 Jul 2008 JP
2008288144 Nov 2008 JP
4328915 Sep 2009 JP
2011049153 Mar 2011 JP
2011071098 Apr 2011 JP
2011082033 Apr 2011 JP
2012094491 May 2012 JP
5201364 Jun 2013 JP
5321063 Jun 2013 JP
5235437 Jul 2013 JP
2015005443 Jan 2015 JP
100908570 Aug 2005 KR
20130134237 Dec 2013 KR
20140083170 Jul 2014 KR
20140106355 Sep 2014 KR
20150106557 Sep 2015 KR
101561646 Oct 2015 KR
9744842 Nov 1997 WO
2008079670 Jul 2008 WO
2008153309 Dec 2008 WO
2009022848 Feb 2009 WO
2009035222 Mar 2009 WO
2009038358 Mar 2009 WO
2009040367 Apr 2009 WO
2011051275 May 2011 WO
2011099580 Aug 2011 WO
2012046514 Apr 2012 WO
2012132059 Oct 2012 WO
2012132060 Oct 2012 WO
2012132976 Oct 2012 WO
2012005945 Dec 2012 WO
2012170240 Dec 2012 WO
2012176873 Dec 2012 WO
2013010985 Jan 2013 WO
2013033595 Mar 2013 WO
2013137351 Sep 2013 WO
2013180781 Dec 2013 WO
2013180782 Dec 2013 WO
2013180783 Dec 2013 WO
2013184881 Dec 2013 WO
2014080871 May 2014 WO
2014165748 Oct 2014 WO
2015046174 Apr 2015 WO
2015051131 Apr 2015 WO
2015051141 Apr 2015 WO
2015121731 Aug 2015 WO
2015179205 Nov 2015 WO
2015179210 Nov 2015 WO
2016025589 Feb 2016 WO
2016044088 Mar 2016 WO
Non-Patent Literature Citations (49)
Entry
US 8,372,547, 02/2013, Koh et al. (withdrawn)
Machine Translation of Abstract, JP3444607B2, espacenet.com.
Machine Translation of Abstract, JPH08298134A, espacenet.com.
Machine Translation, JP3311611B2 (JPH10116627A), Questel's orbits.com.
Machine Translation, JP2003100342A, Questel's orbits.com.
Machine Translation of Abstract, JP2009123465, Patent Abstracts of Japan.
Lee et al., SEI Layer-Forming Additives for LINI0.5MN1.504/Graphite 5 V Li-Ion Batteries, Electrochemistry Communications (2007), vol. 9, pp. 801-806.
Liu et at., Understanding The Improved Electrochemical Performances of Fe-Substituted 5 V Spinel Cathode LIMN1.5NI0.5O4, J. Phys. Chem. C. (2009), vol. 113, pp. 15073-15079.
Smart et al., Li-Ion Electrolytes Containing Ester Co-Solvents for Wide Operating Temperature Range, ECS Transactions (2008) vol. 11, No. 29, pp. 99-108.
Smith et al., Electrolytes Containing Fluorinated Ester Co-Solvents for Low-Temperature Li-Ion Cells, ECS Transactions (2008), vol. 11, No. 29, pp. 91-98.
Zhong et al., Effects of A1 Substitution for Ni and Mn on The Electrochemical Properties LINI0.5MN1.5O4, Electrochimica Acta (2011), vol. 56, pp. 6554-6561.
International Search Report, Corresponding PCT Application No. PCT/US2012/053415 (E. I. Du Pont De Nemours and Co.,), dated Jan. 22, 2013.
Related U.S. Appl. No. 14/241,898 (Chen et al.,), filed Aug. 31, 2012.
International Search Report, Releated PCT Application No. PCT/US2012/0534239 (E. I. Du Pont De Nemours and Co.,), dated Jan. 22, 2013.
Bessler et al., “Boron Complexes with Dicarboxylic Acids”, Zeitschrift fuer Naturforschung, Teil B: Anorganische chemie, Organische Chemie, vol. 37B, Issue 8, pp. 1020-1025, Journal, 1982, CODEN: ZNBAD2, issn: 0340-5087. See also English abstract.
Henne, A.L, “A New Fluorination Method”, J Am. Chem. Soc., 60(7), 1938, 1569-1571.
Hine, J. et al., “Methylenes as Intermediates in Polar Reactions. XXI. A Sulfur-containing Methylene”, J. Amer. Chem. Soc. 82, 6118, 1960.
Jeong, S.-K., et al, “Surface Film Formation on a Graphite Negative Electrode in Lithium-Ion Batteries: Atomic Force Microscopy Study on the Effects of Film-Forming Additives in Propylene Carbonate Solutions”, Langmuir, 2001, 17, 8281-8286.
Jung, H.M., et al., “Fluoropropane Sultone as an SEI-forming Additive that Outperforms Vinylene Carbonate”, J. Mater. Chem. A, 2013, 1, 11975.
Kudryavtsev, I.Y., et al, “Catalytic Phosphorylation of Polyfluoroalkanols”, Izvestiya Akademii Nausk SSSR, Seriya Khimicheskaya, 1982, 11, 2535-2540. Translation.
McMillan, R. et al., “Fluoroethylene Carbonate Electrolyte and its Use in Lithium Ion Batteries with Graphite Anodes”, J Power Sources 81-82 (1999) 20-26.
Mogi, Ryo et al, “Effects of Some Organic Additives on Lithium Deposition in Propylene Carbonate”, J. Electrochem. Soc., 2002, 149(12), A1578-A1583.
Nagasubramanian, G. “Fluoro-Carbonate Solvents for Li-Ion Cells”, Proc. Electrochem. Soc., 2000, 99(25), 434-439.
Nakajima, T. et al., “Effect of Fluoroesters on the Low Temperature Electrochemical Characteristics of Graphite Electrode”, J Fluorine Chem 87 (1998) 221-227.
Rajeshwaran, G. G., et al, “Lewis Acid-Mediated Michaelis-Arbuzov Reaction at Room Temperature: A Facile Preparation of Arylmethyl/Heteroarylmethyl Phosphonates”, Org. Lett., 2011, 13, 1270-1273.
Sasaki, Y. et al, “Physical and Electrolytic Properties of Partially Fluorinated Organic Solvents and its Application to Secondary Lithium Batteries: Partially Fluorinated Dialkoxyethanes”, ECS Transactions, 16, (35), 2009, 23-31.
Schmitz, R.W. et al, “Investigations on Novel Electrolytes, Solvents and SEI Additives for Use in Lithium-ion Batteries: Systematic Electrochemical Characterization and Detailed Analysis by Spectroscopic Methods”, Progress Solid State Chem., 42 (2014) 65-84.
Sekiya, A. et al, “The Potential of Hydrofluoroethers to Replace CFCs, HCFCs, and PFCs”, J Fluorine Chem, 101 (2000) 215-221.
SynQuest Laboratories, Inc. Research Chemicals Catalog, 2003, pp. 128-129.
Tarrant, P. et al, “Some Reactions of Fluoroethanes with Sodium Ethoxide”, J. Am. Chem. Soc., 75, (1953), 932-934.
Von Cresce, A. et al, “Electrolyte Additive in Support of 5 V Li Ion Chemistry”, J Electrochem. Soc., 158 (3), A337-A342 (2011).
Wachtler, M. et al., “The Behaviour of Graphite, Carbon Black, and Li4Ti5O12 in LiBOB-Based Electrolytes”, J. Applied Electrochemistry (2006) 36: 1199-1206.
Xu et al, “Sulfone-Based Electrolytes for Lithium-Ion Batteries”, Journal of the electrochemical Society, 2002, A920-A926, 149 (7).
Xu, K. “Nonaqueous Liquid Electrolytes for Lithium-Based Rechargeable Batteries”, Chem. Rev., 2004, 104, 4303-4418.
Yamaki, J.-I. et al, “Thermal Studies of Fluorinated Ester as a Novel Candidate for Electrolyte Solvent of Lithium Metal Anode Rechargeable Cells”, J Power Sources, 102 (2001) 288-293.
Yang, L. et al., “Effect of Impurities and Moisture on Lithium Bisoxalatoborate (LiBOB) Electrolyte Performance in Lithium-Ion Cells”, J. Power Sources 195 (2010) 1698-1705.
Yoon, S. et al, “Sb-Mox-C (M =Al, Ti, or Mo) Nanocomposite Anodes for Lithium-Ion Batteries”, Chem. Mater. 2009, 21, 3898-3904.
Zaharov et al., “A New Method of Phosphorylation of Polyfluorinated Aliphatic Alcohols”, Izvestiya Akademii Nausk USSR, Seriya Khimicheskaya, No. 8, p. 1860, 1969, Translation.
Zhang, S.S., “A Review on Electrolyte Additives for Lithium-Ion Batteries”, J Power Sources, 162 (2006) 1379-1394.
International Search Report and Written Opinion, Corresponding PCT International Application PCT/US2013/029815 dated Jun. 6, 2013.
International Search Report and Written Opinion, Corresponding PCT International Application PCT/US2013/029818 dated May 14, 2013.
International Search Reportand Written Opinion, Corresponding PCT International Application PCT/US2013/029825 dated May 14, 2013.
International Search Report and Written Opinion, Corresponding PCT International Application PCT/US2014/058845 dated Dec. 11, 2014.
International Search Report and Written Opinion, Corresponding PCT International Application PCT/US2014/058859 dated Feb. 25, 2015.
International Search Report and Written Opinion, Corresponding PCT International Application PCT/US2014/032961 dated Jul. 15, 2014
International Search Report and Written Opinion, Corresponding PCT International Application PCT/US2015/030785 dated Jul. 16, 2015.
International Search Report and Written Opinion, Corresponding PCT International Application PCT/US2015/030807 dated Jul. 17, 2015.
International Search Report and Written Opinion, Corresponding PCT International Application PCT/US2015/044844 dated Dec. 22, 2015.
International Search Report and Written Opinion, Corresponding PCT International Application PCT/US2015/049642 dated Dec. 22, 2015.
Related Publications (1)
Number Date Country
20140227584 A1 Aug 2014 US
Provisional Applications (1)
Number Date Country
61530545 Sep 2011 US