Patent Application
20050258400
An ever-increasing number of applications of LCDs, for example use in automobiles, in which a temperature range of from −40° C. to 100° C. can quite possibly exist, but also portable units such as cellphones and notebook PCs, requires liquid-crystal mixtures which have firstly a very wide working temperature range and secondly a minimum threshold voltage.
There is therefore a continuing demand for novel, suitable liquid-crystal mixtures and mixture components. As described in Ichinose et al. (IDW'00, Abstr. LCT4-3) or in DE-A 10050071, materials are being sought in which there is coexistence of high optical anisotropy (Δn) and low rotational viscosity, although other parameters such as high absolute values of dielectric anisotropy (Δε) are likewise preferentially required, in addition to further parameters relevant to the application.
Fluorinated phenanthrenes are known, for example, from DE-C 195 00 768, EP-B-0 837 851, EP-B-0 946 473 or WO 01/10803, and what are known as the wing groups, i.e. the alkyl and alkyloxy groups which are substantially responsible for the liquid-crystalline properties and the compatibility with other components of liquid-crystal mixtures, in the 2 and 7 positions of the particular phenanthrene skeletons are fixed in all cases.
However, since the manufacturers of liquid-crystal displays have a constant interest in improved liquid-crystal mixtures, there is still a need for further components of liquid-crystal mixtures, with which individual parameters relevant to the application, for example the dielectric anisotropy (Δε) or the optical anisotropy (Δn), but also the position of mesophase transitions and the solubility of similar structures, can be optimized.
It is therefore an object of the present invention to provide novel components for use in nematic or cholesteric or chiral-smectic liquid-crystal mixtures which have high absolute values of dielectric anisotropy combined with a favorable ratio of viscosity to clearing point. In addition, the compounds should to a high degree preferably be light- and UV-stable, and also thermally stable. In addition, they should be suitable for realizing a high voltage holding ratio (VHR). In addition, they should have good synthetic accessibility and therefore potentially be inexpensive.
According to the invention, the objects are achieved by compounds of the formula (I)
in which
The provisos b1), b2) and c) define that fluorine atoms may be present in the compounds of the formula I on the phenanthrene ring only above or below a theoretical axis running through Y2 and X5, including a possible further fluorine atom on this axis, i.e. in Y2 or X5.
Preference is given to compounds of the formulae (Ia) to (It):
in which:
The provision of compounds of the formula (I) in a quite general sense considerably broadens the range of liquid-crystalline substances which are suitable for producing liquid-crystalline mixtures from different performance aspects.
In this context, the compounds of the formula (I) have a broad field of application. Depending on the selection of the substituents, they may be added to other classes of compound, in order, for example, to influence the dielectric and/or optical anisotropy of such a dielectric. They may also serve to optimize its threshold voltage and/or its viscosity. The compounds may also serve to increase the mesophase range or to adjust individual mesophases to parameters relevant to the application.
The compounds of the formula (I) are particularly suitable, even in small amounts in the mixture, for influencing the dielectric anisotropy (Δε) and/or the optical anisotropy Δn of liquid-crystal mixtures. The compounds of the formula (I) are particularly suitable, even in small amounts in the mixture, for reducing the response time of ferroelectric liquid-crystal mixtures. The compounds of the formula (I) are likewise particularly suitable for adjusting the broadness of the SC or N phase to application requirements. The addition of the inventive mixtures can also lead to the solubility limit of fluorinated derivatives of phenanthrene having wing groups in the 2 and 7 positions, as described in the introduction to the description, being raised, and to the proportion of compounds having a high absolute contribution to the dielectric anisotropy thus rising.
The present invention thus provides compounds of the formula (I) and for the use of these compounds as components of liquid-crystalline mixtures and liquid-crystalline mixtures comprising one or more compounds of the formula (I).
The compounds of the formula (I) may be used in various liquid-crystal mixtures, for example chiral-smectic, nematic or cholesteric liquid-crystal mixtures. In the case of nematic mixtures, they are particularly suitable for active matrix displays (AM-LCD) (see, for example, C. Prince, Seminar Lecture Notes, Volume I, p. M-3/3-M-22, SID International Symposium 1997, B. B. Bahadur, Liquid Crystal Applications and Uses, Vol. 1, p. 410, World Scientific Publishing, 1990, E. Lüder, Recent Progress of AMLCD's, Proceedings of the 15th International Display Research Conference, 1995, p. 9-12) and in plane-switching displays (IPS-LCD), and, in the case of smectic liquid-crystal mixtures, for smectic (ferroelectric or antiferroelectric) displays. Further display possibilities are the ECB and VA display mode in the case of nematic and cholesteric LC mixtures.
Further components of liquid-crystal mixtures which comprise inventive compounds of the formula (I) are preferably selected from the known compounds having smectic and/or nematic and/or cholesteric phases. Mixture components suitable in this context are listed in particular in WO 00/36054, DE-A-19 531 165 and EP-A-0 893 424, which are explicitly incorporated herein by way of reference.
The present invention therefore also provides liquid-crystal mixtures, which comprise at least one compound of the formula (I), preferably in an amount of from 1 to 40% by weight, based on the liquid-crystal mixture. The mixtures preferably comprise at least 3 further components of smectic and/or nematic and/or cholesteric phases in addition to compounds of the formula (I). The invention additionally provides electrooptical display elements (liquid-crystal displays) which comprise the inventive mixtures.
Preference is given to displays which comprise the inventive nematic or smectic (ferroelectric or antiferroelectric) mixtures in combination with active matrix elements.
The inventive displays are typically constructed in such a way that one liquid-crystal layer is enclosed on both sides by layers which are typically, in this sequence starting from the LC layer, at least one alignment layer, electrodes and a boundary layer (for example of glass). In addition, they may comprise spacers, adhesive frames, polarizers and thin color filter layers for color displays. Further possible components are antireflection, passivation, compensation and barrier layers, and also electrically nonlinear elements such as thin-film transistors (TFT) and metal-insulator-metal (MIM) elements. The construction of liquid-crystal displays has already been described in detail in relevant monographs (see, for example, E. Kaneko, “Liquid Crystal TV Displays: Principles and Applications of Liquid Crystal Displays”, KTK Scientific Publishers, 1987).
Examples of possible synthetic routes to compounds of the formula (I) are specified in the schemes which follow, although other processes are also feasible and possible.
The following abbreviations are used:
Scheme 1 describes the synthesis of the compounds (Ik); the reactants required therefor E1 4-bromo-2-fluorophenol [2105-94-4] and E2 1-bromo-3,4-difluorobenzene [348-61-8] are commercially available.
When a compound E4 is used instead of E2 for reaction stage c), it is possible to prepare the compounds of the type (Ij) by the procedure of Scheme 1.
The reactants E4 where Y22=methyl is known from the literature [202865-83-6] and commercially available. Reactants E4 where Y22=alkyl can be prepared from the compound E4 where Y22=CHO [188813-O2-7] which is known from the literature by Wittig reaction with alkyltriphenylphosphonium halides and subsequent hydrogenation; alternatively, the commercially available compound where Y22=CN [179898-34-1] can be reacted with alkylmagnesium halides and subsequently processed reductively to give the target compounds. Reactants E4 where Y22=OMe [29578-39-0] and OEt [212307-87-4] are known from the literature; higher homologs may be obtained, for example, from 3-bromo-5-fluorophenol (E4 where Y22=OH) [433939-27-6] by Williamson etherification with alkyl bromides.
When the reactant E5 (instead of Z1) is used in reaction stage b) and subsequently reacted with E2, it is possible by the procedure of Scheme 1 to prepare the compounds of the type (Ii). The 4-alkyl- or 4-alkyloxybromobenzenes (E5 where R2=alkyl or alkyloxy) are commercially available or can be prepared by a multitude of methods known to those skilled in the art.
When the reactants E6 (instead of E2) are used in reaction stage c), it is possible by the procedure of Scheme 1 to prepare the compounds of the type (Ih). E6 where Y22=ethyl [627463-25-6] is known from the literature; homologs can be prepared analogously. E6 where Y22=methoxy [103291-07-2] is likewise known from the literature; the homologization is familiar to those skilled in the art.
When the reactants E7 (instead of E2) are used in reaction stage c), it is possible by the procedure of Scheme 1 to obtain the compounds of the type (It). E7 where Y11=methoxy [202865-58-5] and hexyloxy [260260-81-9] are known from the literature, the former even commercially available. The preparation of homologs is familiar to those skilled in the art. After ether cleavage of the methoxy group (for example by means of HBr/glacial acetic acid or boron tribromide), conversion of the free OH group to the triflate and performance of suitable coupling reactions (for example Hagihara), it is also possible to prepare the derivatives where Y11=alkyl. Equally 3,4-difluoro-6-methoxybenzaldehyde which is known from the literature can be converted to compounds E7 where Y11=alkyl via the reaction sequence of Wittig reaction of alkyltriphenylphosphonium halides and hydrogenation; the OMe group becomes amenable to the coupling reaction stage c) by ether cleavage and conversion to the triflate.
When the reactant E5 (instead of Z1) is used in reaction stage b) and subsequently reacted with E7 in reaction stage c), it is possible by the procedure of Scheme 1 to prepare the compounds of the type (Is). The 4-alkyl- or 4-alkyloxybromobenzenes (E5 where R2=alkyl or alkyloxy) are commercially available or can be prepared by a multitude of methods known to those skilled in the art.
Chromatographic methods, combined with recrystallizations, allow the regioisomers which occur in different amounts depending on the substitution pattern at the stage of the photocyclization (e) to be removed from the particular target products, either at the stage e) or its subsequent stages.
When reactants E8 (instead of E2) and E9 (instead of Z1) are used in reaction stages b) and c), it is possible by the procedure of Scheme 1 to obtain the compounds of the formula (Ia); hydrogenation (analogously to DE-A 19500768) affords therefrom the compounds of the type (Ib). E8 where Y22=methyl is known from the literature [59907-12-9]; alkyl homologs can be prepared by methods including oxidation (for example by means of Cr(VI)) of this compound to the corresponding aldehyde, Wittig reaction with alkyltriphenylphosphonium bromides and subsequent hydrogenation. E9 where R2=methoxy [458-50-4] or propyl [167858-56-2] are commercially available, the preparation of homologs of other chain lengths is familiar to those skilled in the art.
Scheme 3 describes the synthesis of the compounds of the type (If). The reactant E10 where R2=methyl is known from the literature [202865-83-6] and commercially available; reactants E10 where R2=alkyl can be prepared from the compound E10 where R2=CHO [188813-O2-7] which is known from the literature by Wittig reaction with alkyltriphenylphosphonium halides and subsequently hydrogenation; alternatively, the commercially available compound where R2=CN [179898-34-1] may be reacted with alkylmagnesium halides and subsequently processed reductively to the target compounds.
Reactants where R2=OMe [29578-39-0] and OEt [212307-87-4] are known from the literature; higher homologs may be obtained, for example, from 3-bromo-5-fluorophenol (E1 where R2=OH) [433939-27-6] by etherification with alkyl bromides.
The reactants E11 where Y22=methyl [7697-23-6] and Y22=methoxy [394-42-3] are known from the literature; the latter may serve for homologization in the manner described above (ether cleavage, subsequent reaction to give alkyl or else alkyloxy derivatives).
When reactants E12 (instead of Z9) are used in reaction stage k), it is possible by the procedure of Scheme 3 to obtain the compounds of the formula (Id).
When the reactants E 13 (instead of E11) and E12 (instead of Z9) are used in reaction stage k), it is possible by the procedure of Scheme 3 to obtain the compounds of the formula (Ic). When the reactants E13 (instead of E11) and Z9 are used in reaction stages i), k) and n), it is possible by the procedure of Scheme 3 to obtain the compounds of the formula (Ie).
Of the reactants E12, the compounds where R2=ethyl [17070-97-2] and R2=methoxy [36942-56-0] are known from the literature; homologs can be prepared analogously.
Reactants E13 are commercially available as 4-alkylbenzoic acids or 4-alkyloxybenzoic acids.
Reactants E14 can be obtained by ortho-boronation (J. Org. Chem. 56, 3763 (1991)) from 2-Y11-substituted N,N-dialkylbenzamides which may in turn be obtained from the 2-Y11-substituted benzoic acids, for example commercially available 2-ethylbenzoic acid [612-19-1] or commercially available 2-dodecyloxybenzoic acid [143269-37-8] by conversion to the acid chloride and reaction with N,N-dialkylamine.
Reactants E15 where R11=alkyloxy are obtained by Williamson ether synthesis from commercially available 5-bromo-2,3-difluorophenol [186590-26-1]; reactants E15 where R11=alkyl can be obtained by analogy to Scheme 1, stage g).
When the reactants E14 (instead of Z11) and Z9 are used in reaction stage k), it is possible by the procedure of Scheme 3 to obtain the compounds of the formula (Ir, where n=0). These may be converted according to Scheme 3 to the compounds of the formula (Ip).
When the reactants E14 (instead of Z11) and E15 are used (after carrying out stage j) in reaction stage k), it is possible by the procedure of Scheme 3 to obtain the compounds of the formula (Ir, n=1). These may be converted according to Scheme 3 to the compounds of the formula (Iq).
When the reactants E14 (instead of Z11) and E12 are used in reaction stage k), it is possible by the procedure of Scheme 3 to obtain the compounds of the formula (Im).
The compounds of the type (Io) are obtainable by the procedure of Scheme 4.
When the reaction sequence of Scheme 4 is started with the reactants E10 (instead of E15), it is possible to obtain the compounds of the formula (In).
The invention is illustrated in detail by the examples which follow.
A solution of 8.5 g of the compound Z4 (Scheme 1) and approx. 0.8 g of iodine in 8 l of cyclohexane was irradiated at room temperature in a UV irradiation apparatus (Heraeus laboratory UV reactor system 2 with TQ 100 mercury medium-pressure radiator, 150 watts, 200-280 nm) for 8 h. In the course of this, the solution was pumped in circulation through the reaction vessel (volume 0.7 l) via a 10 l aspirator bottle. After the end of the reaction, 150 ml of water and approx. 50 g of sodium sulfite were added, so that the solution was decolorized. After drying over sodium sulfate, the solvent was removed on a rotary evaporator and the residue was chromatographed using silica gel with 10:1 (v/v) heptane/ethyl acetate. After the solvents had been distilled off, the product-containing fractions were recrystallized from acetonitrile. 2.8 g of 3,4,5-trifluoro-6-methoxyphenanthrene were obtained.
A solution of 11 mmol of n-butyllithium (1.6 M solution in hexane) in 20 ml of dry tetrahydrofuran was cooled to ≦−70° C. and admixed dropwise under a protective gas atmosphere with a solution of 11 mmol of potassium tert-butoxide in 12 ml of the same solvent. After stirring for 15-30 min, a solution of 2.8 g of 3,4,5-trifluoro-6-methoxyphenanthrene in 20 ml of tetrahydrofuran was added dropwise in such a way that the internal temperature was always below −70° C. Subsequently, stirring was continued at this temperature for 2 h. 2.5 g of 1-bromopropane were then added slowly and the mixture was subsequently brought slowly to −10° C. It was admixed at −10° C. with 6 ml of water and acidified to pH 1 with concentrated hydrochloric acid. 100 ml of tert-butyl methyl ether were added, the phases were separated, and the organic phase was washed with saturated sodium chloride solution and dried over sodium sulfate. The solvents were removed under reduced pressure, and the residue was chromatographed using silica gel with 9:1 (v/v) heptane/ethyl acetate. The product-containing fractions were combined, the solvent was distilled off under reduced pressure and the residue was recrystallized from acetonitrile. 1.1 g of 3,4,5-trifluoro-6-methoxy-2-propylphenanthrene were obtained.
[Compound (If) where Y22=CH3 and R11=OCH3]
A solution of 50 mmol of diisopropylamine in 25 ml of tetrahydrofuran was cooled to −30° C. and admixed under a protective gas atmosphere with 50 mmol of n-butyllithium (1.6 M solution in hexane). The mixture was stirred at this temperature for 15-30 min and then allowed to thaw to 0° C. Subsequently, a solution of 20 mmol of the compound Z12 (Scheme 3, Y22=CH3 and R2=OCH3) in 40 ml of tetrahydrofuran was added dropwise at 0° C. The mixture was stirred at room temperature for a further 3 h, then the reaction mixture was hydrolyzed with 10 ml of sat. ammonium chloride solution and acidified slightly with dil. hydrochloric acid. The mixture was extracted with 200 ml of tert-butyl methyl ether, and the organic phase was washed with saturated sodium chloride solution and dried over sodium sulfate. The residue obtained after the solvents had been distilled off under reduced pressure was subjected to flash chromatography (silica gel, dichloromethane). The Z13-containing eluate was concentrated by evaporation under reduced pressure, dissolved in 50 ml of DMF and admixed with 8.8 g of Selectfluor reagent in portions with stirring within 30 min and subsequently stirred up to the end of the reaction (detection by means of TLC). The mixture was then admixed with double the amount of ethyl acetate, washed twice with 25 ml of water each time and dried over sodium sulfate, and the solvents were distilled off under reduced pressure. The residue was subjected to flash chromatography (silica gel, 10:1 (v/v) heptane/ethyl acetate), after the solvents had been distilled off, 2.8 g of the compound Z14 (Y22=CH3 and R2=OCH3) were obtained. This was dissolved in 10 ml of toluene, admixed with 4 ml of Deoxofluor reagent [i.e. bis(2-methoxyethyl)aminosulfur trifluoride] and a pipette-tip of BF3.Et2O, and heated to 60° C. up to the end of the reaction (detection by means of TLC). After cooling to 0° C., 1 ml of methanol and subsequently 100 ml of saturated aqueous sodium hydrogencarbonate solution were added. After 30 ml of toluene had been added, the organic phase was removed, washed with water and dried over sodium sulfate, and the solvent was distilled off under reduced pressure. After chromatographic purification (silica gel, 10:1 (v/v) heptane/dichloromethane), 2.1 g of the compound (Ig) (Y22=CH3 and R2=OCH3) were obtained. This was dissolved in 20 ml of THF, admixed with 30 ml of aqueous ammonia solution (30%) and 3 g of zinc dust, and stirred at 30° C. up to the end of the reaction (detection by means of TLC). After filtration, the mixture was admixed with 50 ml of dichloromethane, the phases were separated, and the organic phase was washed twice with 20 ml each time of water and dried over sodium sulfate. After the solvents had been distilled off under reduced pressure, the residue was chromatographed using silica gel with 10:1 (v/v) heptane/ethyl acetate. The product-containing fractions were combined, the solvents were distilled off under reduced pressure and the residue was recrystallized from acetonitrile; 1.1 g of 1,8,9,10-tetrafluoro-6-methoxy-2-methylphenanthrene were obtained.
A chiral-smectic C mixture consisting of
is admixed with 5% of the compound from Example 1. This results in a mixture which, as demonstrated by
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2004 022 728.4 | May 2004 | DE | national |