Claims
- 1. A fluorine-containing water- and oil-repellent composition comprising a fluorine-containing polymer which comprises
- (i) 10 to 90 mole % of a monomer represented by the formula: ##STR15## wherein X.sup.3 is a fluorine atom, or --CFX.sup.4 X.sup.5 group (wherein X.sup.4 and X.sup.5 are the same or different and are each a hydrogen atom or fluorine atom), and R.sup.1 is alkyl having 1 to 20 carbon atoms, alicyclic group, aromatic group or aralkyl;
- (ii) 10 to 80 mole % of a monomer represented by the formula: ##STR16## wherein X.sup.6 is a hydrogen atom or methyl, Y is alkylene having 1 to 3 carbon atoms --CH.sub.2 CH.sub.2 N(R)SO.sub.2 --group (wherein R is alkyl having 1 to 4 carbon atoms) or --CH.sub.2 CH(OZ)CH.sub.2 --(wherein Z is a hydrogen atom or acetyl), and Rf.sup.3 is fluoroalkyl having 3 to 21 carbon atoms, or fluoroalkyl having 3 to 21 carbon atoms and 1 to 10 oxygen atoms in its carbon chain (wherein no two oxygen atoms are present adjacent to each other); and
- (iii) 0 to 50 mole % of other copolymerizable ethylenically unsaturated monomer, the combined amount of the monomers (i) to (iii) being 100 mole %.
- 2. A composition as defined in claim 1 wherein the group Rf.sup.3 in the fluorine-containing acrylate represented by the formula (4) is a group represented by the formula:
- --((CF.sub.2 CF.sub.2).sub.m (O).sub.n).sub.q CF(Rf.sup.4)CF.sub.3
- wherein m is an integer of from 1 to 5, n is 0 or 1, q is an integer of from 1 to 5, and Rf.sup.4 is a fluorine atom or trifluoromethyl, those represented by the formula ##STR17## wherein p is an integer of from 0 to 5, and Rf.sup.4 is as defined above, or those represented by the formula:
- --Ph--Rf.sup.5
- wherein Ph is phenylene, and Rf.sup.5 is perfluoroalkyl having 5 to 15 carbon atoms.
- 3. A composition as defined in claim 1 which is in the form oa s solution.
- 4. A composition as defined in claim 1 which is in the form of an aqueous dispersion.
Priority Claims (2)
| Number |
Date |
Country |
Kind |
| 56-122920 |
May 1986 |
JPX |
|
| 56-238535 |
Oct 1986 |
JPX |
|
Parent Case Info
This application is a continuation, of application Ser. No. 07/165,174 filed 03/07/88 now abandoned which is a division of application Ser. No. 07/050,018 filed 05/15/87 now abandoned.
The present invention relates to fluorine-containing water- and oil-repellent compositions which exhibit good adhesion to the articles to be treated.
It is known that fluorine-containing polymers, such as some fluoroalkyl methacrylate polymers, are usable as water- and oil-repellent agents (see, for example, Examined Japanese Patent Publication SHO 47-40467). However, the known polymers having water- and oil-repellent properties have poor compatibility with the article to be treated and further have the problem that the coating of the polymer readily peels when lightly rubbed because of low adhesive strength.
The main object of the present invention is to provide a fluorine-containing water- and oil-repellent composition for giving uniform tough coatings exhibiting high adhesion to the article to be treated.
Other objects and features of the invention will become apparent from the following description.
The present invention provides a fluorine-containing water- and oil-repellent composition (hereinafter referred to as Composition A) comprising a fluorine-containing polymer which comprises at least 10 mole % of a fluorine-containing acrylate represented by the formula: ##STR2## wherein X is a fluorine atom or --CFX.sup.1 X.sup.2 group (wherein X.sup.1 and X.sup.2 are the same or different and are each a hydrogen atom or fluorine atom), Y is alkylene having 1 to 3 carbon atoms, --CH.sub.2 CH.sub.2 N(R)SO.sub.2 --group (wherein R is alkyl having 1 to 4 cabron atoms) or --CH.sub.2 CH(OZ)CH.sub.2 - (wherein Z is a hydrogen atom or acetyl), and Rf is fluoroalkyl having 3 to 21 carbon atoms, or fluoroalkyl having 3 to 21 carbon atoms and 1 to 10 oxygen atoms in its carbon chain (wherein no two oxygen atoms are present adjacent to each other).
This invention further provides a fluorine-containing water- and oil-repellent composition (hereinafter referred to as Composition B) comprising a fluorine-containing polymer which comprises
We prepared various fluorine-containing acrylate polymers and checked the polymers for adhesion to articles, consequently finding that polymers containing a specific acrylate has outstanding properties for use as a water- and oil-repellent agent. The present invention has been accomplished based on this novel finding.
The Rf group in the fluorine-containing acrylate (1) to be used in Composition A of the invention preferably contains a number of fluorine atoms at least twice the number of carbon atoms contained therein. More preferred examples of such Rf groups are those represented by the formula:
More specific examples of monomers (1) are CH.sub.2 .dbd.CF--COOCH.sub.2 CH.sub.2 C.sub.7 F.sub.15, CH.sub.2 .dbd.CF--COOCH.sub.2 C.sub.2 F.sub.5, CH.sub.2 .dbd.CF--COOCH.sub.2 C.sub.8 F.sub.16 CF(CF.sub.3).sub.2, CH.sub.2 .dbd.CF--COOCH.sub.2 --CF(CF.sub.3)OCF.sub.2 --CF(CF.sub.3)OC.sub.3 F.sub.7, CH.sub.2 .dbd.CF--COOCH.sub.2 --CF(CF.sub.3)OC.sub.3 F.sub.7, CH.sub.2 .dbd.CF--COOCH.sub.2 CH.sub.2 --N(CH.sub.3)SO.sub.2 C.sub.8 F.sub.17, CH.sub.2 .dbd.CF--COOCH.sub.2 CH(OH)CH.sub.2 C.sub.9 F.sub.19 and the like.
Examples of monomers, other than the fluorine-containing acrylate (1), which can be incorporated into the fluorine-containing polymer used in Composition A are monomers represented by the formula: ##STR6## wherein A is a hydrogen atom, chlorine atom or methyl and B is alkyl having 1 to 10 carbon atoms, fluoroalkyl having 1 to 10 carbon atoms, or alicyclic group having 6 to 8 carbon atoms. Also useful are other ethylenically unsaturated monomers including ethylene, propylene, styrene, and acrylates and methacrylates which have a functional group such as vinyl, hydroxyl, carboxyl, glycidyl, dialkylamino or trialkoxysilyl.
Examples of acrylates or methacrylates having a functional group are CH.sub.2 .dbd.C(CH.sub.3)COO(CH.sub.2 CH.sub.2 O).sub.10 COC(CH.sub.3).dbd.CH.sub.2, CH.sub.2 .dbd.C(CH.sub.3)COO(CH.sub.2).sub.10 COC(CH.sub.3).dbd.CH.sub.2, CH.sub.2 .dbd.C(CH.sub.3)COOCH.sub.2 CH--(OCOC(CH.sub.3).dbd.CH.sub.2)CH.sub.2 OCOC(CH.sub.3).dbd.CH.sub.2, CH.sub.2 .dbd.CHCOOCH.sub.2 CH.sub.2 OH, CH.sub.2 .dbd.CHCOO--R.sup.A (wherein R.sup.A is glycidyl), CH.sub.2 .dbd.C(CH.sub.3)COO--CH.sub.2 CH.sub.2 CH.sub.2 Si(OCH.sub.3).sub.3, etc.
More specific examples of monomers (2) are CH.sub.2 .dbd.CHCOOCH.sub.3, CH.sub.2 .dbd.CHCOOC.sub.12 H.sub.25, CH.sub.2 .dbd.CHCOO--R.sup.B (wherein R.sup.B is cyclohexyl), CH.sub.2 .dbd.C(CH.sub.3)COOCH.sub.3, CH.sub.2 .dbd.C(CH.sub.3)COOC.sub.8 H.sub.37, CH.sub.2 .dbd.C(CH.sub.3)COOCH.sub.2 CH.sub.2 C.sub.7 F.sub.15, CH.sub.2 .dbd.C(C1)COOCH.sub.3, etc.
The fluorine-containing polymer to be used for Composition A is usually in the range of from 10,000 to 4,000,000 in number average molecular weight (as measured by gel permeation chromatography) and in the range of from 0.25 to 2.0, in intrinsic viscosity [.eta.] (as measured at a temperature of 35.degree. C. using m-xylene hexafluoride, methyl ethyl ketone, chloroform, 1,1,1-trichloromethane or like solvent). If the molecular weight is too small, the resulting coating has low strength and is liable to peel off the article treated, whereas if it is too great, the resulting composition is difficult to apply to articles owing to increased viscosity or low free-flowing properties.
The fluorine-containing polymer used in Composition A and comprising 10 to 90 mole % of a fluorine-containing acrylate (1), especially such an acrylate wherein X is a fluorine atom, exhibits high adhesion to the article to be treated, forming a tough and flexible coating.
The monomers represented by the formula (2) and inexpensive monomers, such as ethylene, propylene and styrene, are useful for reducing the cost of the fluorine-containing polymer and act to impart hardness to the fluorine-containing polymer. The monomers of the formula (2) and other monomers, such as ethylene, propylene and styrene, are used usually in an amount of up to 90 mole %.
The fluorine-containing polymer, when containing a functional group, exhibits improved adhesion to the article to be treated. Further the functional group can be utilized for crosslinking the fluorine-containing polymer. For the crosslinking, methods which are usually used in the art can be resorted to (see, for example, Unexamined Japanese Patent Publication SHO 47-42880). Usually up to 30 mole % of acrylate or methacrylate is used which has the functional group to be introduced into the fluorine-containing polymer.
Composition B comprising a fluorine-containing polymer which comprises 10 to 90 mole % of monomer represented by the formula (3), 10 to 80 mole % of monomer represented by the formula (4) and 0 to 50 mole % of other copolymerizable ethylenically unsaturated monomer also exhibits excellent water- and oil-repellent propoerties.
Examples of groups R.sup.1 in the formula (3), which are not limited specifically, are alkyl groups such as methyl, ethyl, butyl and stearyl; halogenated (but not fluorinated) alkyl groups such as 2-chloroethyl; cycloalkyl groups such as cyclohexyl, bornyl and adamantyl; aromatic groups such as phenyl and naphthyl; silicon-containing groups such as trimethylsilyl and trimethylsilylpropyl; phosphorus-containing groups such as dimethylphosphateethyl; groups having an unsaturated bond such as allyl; groups having a functional group, such as cyanoethyl and glycidyl; groups having dialkylamino such as dimethylaminoethyl; groups having an ether group such as tetrahydrofurfuryl; etc.
More specific examples of monomers (3) are CH.sub.2 .dbd.CFCOOCH.sub.3, CH.sub.2 --CFCOOC.sub.2 H.sub.5, CH.sub.2 .dbd.CFCOOC.sub.3 H.sub.7, CH.sub.2 .dbd.CFCOOC.sub.4 H.sub.9, CH.sub.2 .dbd.CFCOOCH(CH.sub.3).sub.2, CH.sub.2 .dbd.CFCOOC.sub.12 H.sub.25, CH.sub.2 .dbd.CFCOOC.sub.16 H.sub.37, CH.sub.2 .dbd.CClCOOCH.sub.2 CH.sub.2 Cl, ##STR7## CH.sub.2 .dbd.CClCOOCH.sub.3, CH.sub.2 .dbd.CClCOOC.sub.2 H.sub.5, CH.sub.2 .dbd.CClCOOC.sub.3 H.sub.7, CH.sub.2 .dbd.CClCOOC.sub.4 H.sub.9, CH.sub.2 .dbd.CClCOOCH(CH.sub.3).sub.2, CH.sub.2 .dbd.CClCOOC.sub.12 H.sub.25, CH.sub.2 .dbd.CClCOOC.sub.16 H.sub.37, ##STR8## CH.sub.2 .dbd.CClCOOCH.sub.2 CH.sub.2 OH, ##STR9## CH.sub.2 .dbd.CClCOOCH.sub.2 Si(CH.sub.3).sub.3, CH.sub.2 .dbd.CFCOOCH.sub.2 CH.sub.2 OP(.dbd.O)(OCH.sub.3).sub.2, CH.sub.2 .dbd.CClCOOCH.sub.2 CH.sub.2 CN, CH.sub.2 .dbd.CFCOOCH.sub.2 CH.dbd.CH.sub.2, etc.
The Rf.sup.3 group in the fluorine-containing acrylate (4) to be used in Composition B in the invention preferably contains a number of fluorine atoms at least twice the number of carbon atoms contained therein. More preferred examples of such Rf.sup.3 groups are those represented by the formula:
More specific examples of monomer (4) include CH.sub.2 .dbd.CHCOOCH.sub.2 CH.sub.2 C.sub.7 F.sub.15, CH.sub.2 .dbd.CHCOOCH.sub.2 C.sub.2 F.sub.5, CH.sub.2 .dbd.C(CH.sub.3)--COOCH.sub.2 C.sub.8 F.sub.16 CF(CF.sub.3).sub.2, CH.sub.2 .dbd.CHCOOCH.sub.2 CF(CF.sub.3)OCF.sub.2 CF(CF.sub.3)OC.sub.3 F.sub.7, CH.sub.2 .dbd.C(CH.sub.3)COOCH.sub.2 CF(CF.sub.3)OC.sub.3 F.sub.7, CH.sub.2 .dbd.CHCOOCH.sub.2 --CH.sub.2 N(CH.sub.3)CO.sub.2 C.sub.8 F.sub.17, CH.sub.2 .dbd.C(CH.sub.3)COOCH.sub.2 CH(OH)CH.sub.2 C.sub.9 F.sub.19, CH.sub.2 .dbd.CHCOOCH.sub.2 CH.sub.2 C.sub.8 F.sub.19, CH.sub.2 .dbd.CHCOOCH.sub.2 CF(CF.sub.3)OC.sub.3 F.sub.7, CH.sub.2 .dbd.C(CH.sub.3)COOCH.sub.2 CH.sub.2 C.sub.7 F.sub.15 and the like.
Examples of copolymerizable ethylenically unsaturated monomers, other than the monomers (3) and (4), which can be incorporated into the fluorine-containing polymer in Composition B include acrylates and methacrylates having a functional group such as vinyl, hydroxyl, carboxyl, glycidyl, dialkylamino or trialkoxysilyl, CH.sub.2 .dbd.CH.sub.2, ##STR11## CH.sub.2 .dbd.CHCH.sub.3, CH.sub.2 .dbd.CHCOOCH.sub.3, CH.sub.2 .dbd.C(CH.sub.3)COOCH.sub.3, ##STR12## CH.sub.2 .dbd.C(CH.sub.3)COOC.sub.18 H.sub.37, CH.sub.2 .dbd.CHCOOC.sub.12 H.sub.25, ##STR13## etc.
The fluorine-containing polymer to be used for Composition B is usually in the range of from 10,000 to 4,000,000 in number average molecular weight (as measured by gel permeation chromatography) and in the range of from 0.25 to 3.0, preferably from 0.5 to 2.0, in intrinsic viscosity [.eta.] (as measured at a temperature of 35.degree. C. using m-xylene hexafluoride, methyl ethyl ketone, chloroform, 1,1,1-trichloromethane or like solvent). If the molecular weight is too small, the resulting coating has low strength and is liable to peel off the article treated, whereas if it is too great, the resulting composition is difficult to apply to articles owing to increased viscosity or low free-flowing properties.
The fluorine-containing polymer used in Composition B and comprising 10 to 90 mole % of an fluorine-containing acrylate (3), especially such an acrylate wherein X.sup.3 is a fluorine atom or chlorine atom exhibits high adhesion to the article to be treated, forming a tough and flexible coating.
Composition B comprising a fluorine-containing copolymer containing 10 to 80 mole % of an acrylate (4) gives a coating excellent in water- and oil-repellent properties.
Other copolymerizable ethylenically unsaturated monomer, when incorporated into composotion B, acts to impart improved hardness to the coating of composition.
The fluorine-containing polymers of the present invention can be prepared by radical polymerization (e.g. solution, bulk or emulsion polymerization) or anionic polymerization.
Examples of solvents useful for solution polymerization are fluorine-containing solvents such as m-xylene hexafluoride and trichlorotrifluoroethane, hydrocarbon solvents such as ethyl acetate, methyl isobutyl ketone, acetone, toluene and xylene, etc. The polymer obtained by solution polymerization can be used in the form of a solution which is prepared by separating the polymer from the solvent and dissolving the polymer in a solvent after drying, or in the form of a solution which is prepared by merely diluting the resulting reaction mixture.
The polymer obtained by bulk polymerization is usable as dissolved in a solvent after drying.
Examples of polymerization initiators useful for solution polymerization and bulk polymerization are azo compounds such as azobisisobutyronitrile, peroxide compounds such as benzoyl peroxide and the like.
For solution polymerization and block polymerization, mercaptans such as laurylmercaptan and thiphenol are usable as chain transfer agents.
In either of these two processes, the polymerization temperature is preferably 30.degree. to 100.degree. C.
Before application to the article to be treated, the fluorine-containing polymer prepared by solution or bulk polymerization is dissolved in a dissolving solvent capable of thoroughly dissolving the polymer and further diluting the solution with a diluting solvent capble of dissolving the polymer without permitting the dissolved polymer to separate out. Like usual water- and oil-repellent agents, the resulting composition is applied to the article by dipping, brushing, spraying or otherwise. Preferably the concentration of the composition is 0.1 to 30 wt.% for brush coating or about 0.05 to about 2 wt.% for spray coating. The coating is dried at room temperature to 150.degree. C.
Examples of useful dissolving solvents are fluorine-containing solvents such as m-xylene hexafluoride and trichlorotrifluoroethane, chlorine-containing solvents such as trichloroethane, etc. Examples of useful diluting solvents are chlorine-containing solvents such as tetra-chloroethylene and trichloroethylene, ketone solvents such as acetone, ester solvents such as ethyl acetate, aromatic solvents such as toluene, etc. The dissolving solvent is usable also as the diluting solvent.
Nonionic compounds are desirable as emulsifiers for emulsion polymerization, while cationic emulsifiers are also usable.
The polymerization initiator to be used for emulsion polymerization is preferably a water-soluble compound. Examples of such compounds are azo compounds such as azobisisobutyroamidine hydrochloride, peroxide compounds such as succinic acid peroxide, etc. The emulsion polymerization temperature is preferably 30.degree. to 100.degree. C.
The fluorine-containing polymer prepared by emulsiton polymerization is usable as an aqueous composition. Usually, the emulsifier need not be removed from the reaction mixture. The aqueous water- and oil-repellent composition is usable in the same manner as above. Since the aqueous composition contains water, it is desirable to heat the coating thereof at 100.degree. to 150.degree. C. for drying.
When the fluorine-containing acrylate of the formula (1) wherein X is trifluoromethyl is to be singly polymerized, it is preferable to resort to anionic polymerization in view of the velocity of polymerization.
Examples of polymerization initiators usable for anionic polymerization are alkali metals, metallic hydrides, sodium amide, Grignard reagents, metal alkyl, pyridine and the like.
Examples of solvents usable for anionic polymerization are aromatic solvents such as toluene, ether solvents such as tetrahydrofuran, etc.
Anionic polymerization is conducted usually in a high vacuum of about 1.times.10.sup.-6 mm Hg or in a dry inert gas atmosphere. The polymerization temperature is usually -100.degree. to 70.degree. C.
The polymer prepared by anionic polymerization can be applied to the article to be treated in the same manner as the one prepared by solution polymerization.
The water- and oil-repellent composition of the present invention is usable for giving water- and oil-repellent properties to various solid articles which must be resistant to abrasion, such as tents, sheet covers, umbrellas, raincoats, shoes, caps to hats, bags, jackets, jumpers, aprons, blazers, slacks, skirts, other garments, carpets, sofas, curtains, etc. Further, the composition of the invention is useful as an agent for preventing the adhesion of liquid polymers such as epoxy resin.
The water- and oil-repellent composition of the invention comprises a polymer which contains as a component thereof a specific fluorine-containing acrylate having a fluorine atom or fluorine-containing group at the .alpha.-position. The present composition is superior to conventional water- and oil-repellent compositions in adhesion to the article to be treated and has high durability against laundry.
US Referenced Citations (1)
| Number |
Name |
Date |
Kind |
| 3393186 |
Groves |
Jul 1968 |
|
Non-Patent Literature Citations (2)
| Entry |
| Hawley's Chemical Dictionary, Eleventh Ed., p. 854. |
| Grant & Hackh's Chemical Dictionary, Fifth Ed., p. 24. |
Divisions (1)
|
Number |
Date |
Country |
| Parent |
50018 |
May 1987 |
|
Continuations (1)
|
Number |
Date |
Country |
| Parent |
165174 |
Mar 1988 |
|
Patent Grant
5021527