Patent Grant
7989376
1. Field of Invention: This invention relates to novel compositions of doped fluorophosphates glass. The new and improved glass compositions are particularly useful in laser glass, amplifiers and high density optical storage applications and are based on or contain Ba (PO3)2, AL(PO3)3, BaF2 or related fluorides and MnO; or oxides or fluorides of rare earth elements: Nd, Er, Tm, Ho, Pr, Tb, Yb, Sm and Eu; mixtures thereof.
2. Description of Related Art: Presently most optical laser glasses are manufactured on a SiO2 base. The SiO2 based laser glasses have a limited refractive index of nD=1.40 to 1.45 and a limited infrared transmission spectrum. These limitations prohibit use of SiO2 based glasses in applications for modern laser applications such as the need for glass with efficient transparency in the near and mid infrared frequency range.
There are disclosures of fluorophosphates glass compositions in existing art; however, none of the existing glass compositions provide the efficient transmission qualities of the present invention in the near and mid infrared frequency range used in modern laser applications. Fluorophosphate laser glasses have a higher refractive index and dispersion than glasses with silicon dioxide. The fluorophosphates glasses generally have a refractive index of nD=1.6344 to 1.6412. They can be used as the basis for creating high power lasers.
Fluorophosphate glasses are close to the phosphate glasses in terms of the degree of covalence of the dopant-ligand bond. This has been confirmed by comparison of the Racha coefficient, B, for these glasses. The magnitude of B decreases with a decrease in size of the effective nuclear charge of free ions. The boundaries of glass formation for fluorophosphate glasses with metaphosphates of barium and aluminum and with fluorides of alkaline earth elements create a wide domain of glass forming fluorophosphates that increase in the following order Ba>Sr>Ca>Mg. The presence of barium fluoride, BaF2, with RFx where RFx is from the group MgF2, CaF2, PbF2 and BiF3 effectively increases chemical durability of laser materials.
The phosphate laser glasses of varying composition due to thermal expansion and hardness properties and to low chemical durability or stability are not suited for the laser applications anticipated for the instant invention. These limitations are generally due to the presence of metaphosphates of lithium, sodium and potassium, U.S. Pat. No. 3,846,142.
Existing fluorophosphates laser glass such as the system BaPO3F—MgF2—Nd2O3—Ga2O3—MnO have a high rate of inactive absorption of wavelength 1,064 nm, which reduces the luminescence of glass dopants. There also exist a class of fluorophosphate laser glasses that were developed on a base of metaphosphate aluminum and fluorides of metal from the first and second group of the periodic elements. The optical constant for these glasses are in the range (nD) from 1.45 to 1.59 whereas the instant invention exceeds 1.60 for greater laser efficiency, U.S. Pat. No.'s 2,511,225; 2,511,227; 2,481,700 and 2,430,539.
There are several publications that discuss compositions of fluorophosphates glass; however, they do not disclose or anticipate the specific composition of the present invention. Example text references are: Journal De Physique V 4n4, April 1994, Pages 509-512, article of R. Balda, J. Fernandez and A. DePablos.; Journal of Non-Crystalline Solids, Vol. 213-214, June 1997, pages 245-250, article of J. L. Adam, N. Henry Duhamel and J. Y. Allain; and Journal of Chinese Physics Lasers, Chin. Phys. Lasers, Vol. 16., No. 4, April 1989, pages 227-232.
This invention is related to fluorophosphates glass compositions that are used for laser applications, amplifiers and high density optical storage. Fluorophosphate glasses offer many advantages over crystalline materials. Due to unique spectroscopic properties the fluorophosphates vitreous materials can be used for ultraviolet, visual and near infrared optics in the band of 250 to 3,500 nm.
The fluorophosphate glass contains the components Ba(PO3)2, Al(PO3)3, BaF2 and RFx where RFx is from the group MgF2, CaF2, PbF2 and BiF3 or related fluorides and MnO; oxides or fluorides of rare earth elements: Nd, Er, Tm, Ho, Pr, Tb, Sm, Eu and Yb; mixtures thereof. This composition of glass has a high level of chemical durability, laser efficiency and luminescence of dopants.
These and other features, aspects and advantages of the present invention will become better understood with reference to the following drawings, description and claims.
The following detailed description is the best currently contemplated modes for carrying out the invention. The description is not to be taken in a limiting sense, but is made merely for the purpose of illustrating the general principles of the invention.
The preferred material for the present invention are glasses based on or containing Ba(PO3)2, 5 to 60 mol %; Al(PO3)3, 5 to 60 mol %; BaF2+RFx, 10 to 90 mol %; and MnO; or oxides or fluorides of rare earth elements: Nd, Er, Tm, Ho, Pr, Tb, Yb, Sm, and Eu; mixtures thereof, 2 to 20 weight %. The raw compounds used for glass formation are: Metaphosphate Barium, Ba(PO3)2, and Aluminum, Al(PO3)3, which are considered chemically stable substances. When MnO or Yb2O3 are used as co-dopant sensitizers the range of dopant is 1 to 20 weight %.
Characteristics of the glass compositions indicate the duration of luminescence for neodymium ions in the laser wavelength 1064 nm is 420 to 450 msec and the half width of luminescence is 160 to 165 cm−1. For erbium ions, the duration of luminescence in the laser wavelength 1535 nm is 480 to 500 msec and the half width of luminescence is 150 to 155 cm−1.
A neodymium and erbium doped athermal fluorophosphate glass results from the high neodymium and erbium oxide or fluoride concentration of 5 to 20 weight %. Erbium doped fluorophosphate laser glass is more efficient than erbium doped silicate laser glass. Erbium doped fluorophosphate laser glass also has an eye safe operating wavelength of 1535 nm which makes it useful for specialized medical apparatus as well as for range finding equipment. The combination of the base materials and dopants provide an efficient laser glass in the infrared region for laser use.
The preferred glass forming compounds, Ba(PO3)2 and Al(PO3)3 are characterized as chemically stable substances. In combination they create a significant free or open volume structure due to the large ionic radii of barium (1.38° A) as in Ba(PO3)2 and BaF2+RFx. This allows the homogenous and regular distribution of dopant ions in a glass matrix.
The presence of BaF2+RFx effectively increases the chemical durability of the laser material. In the grouping of glasses according to chemical stability of non-silicate glasses relating to humidity or moisture, these glasses are considered to be stable glasses. During the melting process a chemical integration between Ba(PO3)2 and BaF2 creates BaPO3F, monofluorophosphate barium.
The melting process is conducted in the temperature range of 1,200° C. to 1,250° C. in vitreous carbon crucibles in a dry argon atmosphere for 4 to 5 hours followed by an annealing temperature range of 320° C. to 340° C. for 8 to 10 hours. In the system of Ba(PO3)2—Al(PO3)3—BaF2—RFx with dopants R, including sensitizers MnO and Yb2O3, two separate glass forming ranges were discovered as illustrated in Table I.
Examples of effective compositions and properties of the fluorophosphates laser glass for the composition Ba(P03)2—Al(PO3)3—BaF2—RFx—Nd2O3—Er2O3 are illustrated in Table II based on mol percent and weight percent.
In the examples of TABLE II MnO and Yb2O3 would be used as dopant sensitizers.
While the invention has been particularly shown and described with respect to the illustrated and preferred embodiments thereof, it will be understood by those skilled in the art that the foregoing and other changes in form and details may be made therein without departing from the spirit and scope of the invention.
This is a continuation-in-part of application Ser. No. 09/892,238 filed on Jun. 26, 2001 which application now abandonned.
| Number | Name | Date | Kind |
|---|---|---|---|
| 2430539 | Sun | Nov 1947 | A |
| 2481700 | Sun et al. | Sep 1949 | A |
| 2511225 | Sun | Jun 1950 | A |
| 2511227 | Sun | Jun 1950 | A |
| 3846142 | Buzhinsky et al. | Nov 1974 | A |
| 3941672 | Tanaka et al. | Mar 1976 | A |
| 4040846 | Broemer et al. | Aug 1977 | A |
| 4120814 | Izumitani et al. | Oct 1978 | A |
| 4142088 | Hirsch | Feb 1979 | A |
| 4182664 | Marklad et al. | Jan 1980 | A |
| 4225459 | Faulstich et al. | Sep 1980 | A |
| 4386163 | Kodama | May 1983 | A |
| 4620863 | Tomozawa et al. | Nov 1986 | A |
| 4642297 | Mennemann et al. | Feb 1987 | A |
| 4771020 | Omata et al. | Sep 1988 | A |
| 4962067 | Myers | Oct 1990 | A |
| 4990468 | Komiya et al. | Feb 1991 | A |
| 5017520 | Otsuka et al. | May 1991 | A |
| 5032315 | Hayden et al. | Jul 1991 | A |
| 5068209 | Meinert et al. | Nov 1991 | A |
| 5526369 | Hayden et al. | Jun 1996 | A |
| 5635109 | Otsuka | Jun 1997 | A |
| 5755998 | Yamazaki et al. | May 1998 | A |
| 5809199 | Tran | Sep 1998 | A |
| 5846638 | Meissner | Dec 1998 | A |
| 6429162 | Prassas | Aug 2002 | B1 |
| 6430349 | Hyden et al. | Aug 2002 | B1 |
| 6495481 | Margaryan | Dec 2002 | B1 |
| 7088903 | Ishioka | Aug 2006 | B2 |
| 20030040421 | Margaryan | Feb 2003 | A1 |
| 20050058424 | Ishioka | Mar 2005 | A1 |
| 20050188724 | Ikenishi et al. | Sep 2005 | A1 |
| 20050259944 | Anderson et al. | Nov 2005 | A1 |
| 20060033983 | Dai et al. | Feb 2006 | A1 |
| 20060245460 | Luo et al. | Nov 2006 | A1 |
| 20070010390 | Margaryan et al. | Jan 2007 | A1 |
| 20090255297 | Margaryan et al. | Oct 2009 | A1 |
| Number | Date | Country |
|---|---|---|
| WO 9913541 | Mar 1999 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20030040421 A1 | Feb 2003 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 09892238 | Jun 2001 | US |
| Child | 10054328 | US |