Patent Grant
10826060
The present invention relates to a negative electrode and to an alkaline electrochemical cell comprising the negative electrode, wherein the negative electrode includes zinc as an active material and further includes a hydrogen gas inhibiting surfactant. More particularly, the invention discloses an alkaline electrochemical cell that is capable of providing improved service when utilized by high drain devices.
The alkaline zinc air cell system is particularly sensitive to zinc stability and low gassing rates. Any buildup of either hydraulic or pneumatic pressure within the anode compartment can result in failure of the air electrode as electrolyte is forced into the critical solid-gas-liquid reaction sites. Excessive electrolyte within the air electrode further leads to a decrease in its tensile strength, which can result in a higher resistance in the electrode to can contact as well as an oxygen diffusion barrier film at the PFTE membrane to electrode interface. This is typically observed as a sloping end of life discharge as polarization increases from lack of effective oxygen reduction within the air electrode matrix.
The alkaline battery industry has a long history of defining anode additives, with the intent of stabilize or minimizing zinc corrosion. This is particularly true since the elimination of mercury from alkaline battery products. For the most part corrosion has been controlled through the addition of surfactants also referred to as wetting and dispersing additives. Identifying and qualifying new additives is challenging since it is not the intent of the manufacturers of these surfactants that they be used as film formers on the surface of zinc or at zinc grain boundaries, or minimizing the reaction of water and zinc, particularly with high surface area zinc alloys. The selection of the preferred additive is further complicated by the fact that different zinc based chemistries, cell form factors, application drains, shelf life claims, sensitivities to gas generation, and anode processing differences such as gels and powdered forms has led to a wide variation in specifications. Surfactants and dispersion aids can serve more than one function. Some additives are used primarily to influence rheology properties while possessing a secondary effect of reducing zinc corrosion.
U.S. Pat. No. 4,777,100 relates to reportedly reducing corrosion in aqueous electrochemical cells having zinc anodes comprised of single crystal zinc particles by the addition of small amounts of a gas inhibiting surfactant, for example, an organic phosphate inhibitor such as RA600 from GAF Corp. to the cell. A synergistically lowered rate of corrosion and cell gassing is reportedly obtained even with reduction of mercury content.
U.S. Pat. No. 5,401,590 relates to a method for inhibiting the occurrence of load voltage instability in zinc anodic alkaline cells. The anode active material contains a gelled slurry of zinc alloy particles, a gelling agent, an aqueous alkaline solution and a mixed surfactant containing an anionic surfactant and a nonionic surfactant. The gelled anode active material reportedly inhibits the occurrence of load voltage instability and reportedly simultaneously reduces hydrogen evolution even though the cell contains no added amounts of mercury.
U.S. Pat. No. 6,551,742 relates to an anionic fluorosurfactant, such as an anionic fluoroaliphaticcarboxylate, can be added to the anode mixture of a zinc/air cell. The addition of the surfactant and a heat treated anode casing eliminates the need to add mercury to the anode material.
U.S. Pat. No. 6,872,489 discloses a sulfonic acid type organic surfactant which is incorporated into the gelled anode of an alkaline electrochemical cell, optionally with an organic phosphate ester surfactant. When the two surfactants are provided in a gelled anode in combination, discharge leakage is reportedly reduced and gel gassing is reportedly suppressed relative to that of gels lacking both surfactants. Additionally, cell discharge performance is reportedly improved relative to that of cells lacking both surfactant additives.
U.S. Pat. No. 7,008,723 relates to a method of manufacturing an anode composition for use in an electrochemical cell, in which the anode comprises an electrochemically active material, the method comprising the steps of mixing the electrochemically active material with an alkaline electrolyte solution, an organic surfactant, an indium compound, and a gelling agent, such that the indium compound or a portion thereof is added in an alkaline environment.
U.S. Pat. No. 7,993,508 discloses an alkaline zinc air cell that contains either a surfactant Carbowax c 550, or a surfactant Disperbyk r D102.
U.S. Pat. No. 8,586,244 relates to electrochemical cells wherein the negative electrode includes zinc as an active material and further includes a reported synergistic combination of a solid zinc oxide and a surfactant.
WO 2003052843 A2 relates to an alkaline electrochemical cell that contains an oxazoline surfactant additive.
According to a first aspect of the present invention, an embodiment of the invention can include any one or a combination of the following features: An alkaline electrochemical cell, comprising a container; a negative electrode, a positive electrode, wherein the negative electrode and the positive electrode are disposed within the container and, a separator located between the negative electrode and the positive electrode, and an alkaline electrolyte, wherein the negative electrode comprises zinc, and a sulfotricarballylate surfactant. The sulfotricarballylate surfactant is a fluorosurfactant is of the formula (I)
where the groups Zi(Z1, Z2, and Z3) are, independently of one another, branched or unbranched alkyl groups or groups of the structure Ri(A(CR1R2)ci—(CR3R4)c′i)di—, where the respective indices ci and c′i are, independently of one another, 0-10, and di=0-5, where Ri is a branched or unbranched, fluorine-containing alkyl radical, R1 to R4 are, independently of one another, hydrogen or a branched or unbranched alkyl group, ci and c′i are not simultaneously 0, and A=O, S and/or N. Y1 is an anionic polar group and Y2 is a hydrogen atom, or vice versa, X is a cation, and at least one of the groups Zi is a group of the structure Ri(A(CR1R2)ci—(CR3R4)c′i)di—. The sulfotricarballylates surfactant preferably has a molecular weight of about between 800 and 1320.
In another embodiment, the sulfotricarballylate surfactant included to suppress corrosion of the zinc in the negative electrode of the alkaline cell is characterized by the formula (Ia)
and where Z1=Z2=Z3=F3C(CF2)ai(CH2)bi(O(CH2)ci)di—, where ai=1-2, bi=1-2, ci=2, di=1-3. Alternatively, Z1=Z2=Z3=F3C(CF2)CH2)(O(CH2CHCH2CH3)).
In the embodiment, the sulfotricarballylates contains more than one fluorinated end groups, and all of the fluorinated end groups can be identical. Preferably the sulfotricarballylate surfactant comprises three fluorinated end groups. Each fluorinated end group can include a fluorinated carbon chain such as F3C(CF2)2 and F3C(CF2). In the embodiment wherein the sulfotricarballylate surfactant comprises three fluorinated end groups, each end group can comprise such a fluorinated carbon chain.
The sulfotricarballylates surfactant is in the form of a mixture, and added so as to be present in the cell in an amount from 10 to 1000 ppm based on the total weight of the zinc. Preferably the concentration of the sulfotricarballylate in the cell is present in an amount from 10 to 200 ppm, or 10 to 100 ppm based on the total weight of the zinc, and most preferably in an amount from 10 to 40 ppm based on the total weight of the zinc. When added to the negative electrode of the alkaline electrochemical cell the sulfotricarballylate surfactant can form a monolayer on the surface of the zinc so as to inhibit corrosion of the zinc.
These and other features, advantages, and objects of the present invention will be further understood and appreciated by those skilled in the art by reference to the following specification, claims, and appended drawings.
In the drawings:
As shown in an example of an electrochemical cell according to the invention is shown in
A catalytic layer 121 contains a catalytic composition that includes composite particles comprising nano-catalyst particles adhered to (e.g., adsorbed onto) the external and internal surfaces (including surfaces of open pores) of highly porous carbon substrate particles.
Examples of zinc air cell cathode construction that can be used in conjunction with the present invention are disclosed in U.S. Patent Application Publication No. 2008/0155813 A1.
The anode casing 126 forms the top of the cell and has a rim 135 which is flared outward at its open end. Alternatively, a cell can have a refold anode casing in which the rim is folded outward and back along the side wall to form a substantially U-shaped side wall with a rounded edge at the open end of the casing, or the anode casing can have essentially straight side walls and that has a rim with little or no outward flare.
The anode casing 126 can be formed from a substrate including a material having a sufficient mechanical strength for the intended use such as stainless steel, mild steel, cold rolled steel, aluminum, titanium or copper. Preferably the anode casing includes one or more additional layers of material to provide good electrical contact to the exterior surface of the anode casing 126, resistance of the external surface to corrosion, and resistance to internal cell gassing where the internal surface of the anode casing 126 comes in contact with the anode 128 or electrolyte. Each additional layer can be a metal such as nickel, tin, copper, or indium, or a combination or alloy thereof, and layers can be of the same or different metals or alloys. Examples of plated substrates include nickel plated steel, nickel plated mild steel and nickel plated stainless steel. Examples of clad materials (i.e., laminar materials with at least one layer of metal bonded to another layer of metal) include, as listed in order from an outer layer to an inner layer, two-layered (biclad) materials such as stainless steel/copper, three-layered (triclad) materials such as nickel/stainless steel/copper and nickel/mild steel/nickel, and materials with more than three clad layers.
The anode casing 126 can include a layer that is post-plated (i.e., plated after forming the anode casing into its desired shape). The post-plated layer is preferably a layer of metal with a high hydrogen overvoltage to minimize hydrogen gassing within the cell 110. Examples of such metals are copper, tin, zinc, indium and alloys thereof. A preferred metal is tin, and a preferred alloy is one comprising copper, tin and zinc.
Cell 110 also includes a gasket 130 made from an elastomeric material which serves as the seal. The bottom edge of the gasket 130 has been formed to create an inwardly facing lip 132, which abuts the rim of anode casing 126. Optionally, a sealant may be applied to the sealing surface of the gasket, cathode casing and/or anode casing. Suitable sealant materials will be recognized by one skilled in the art. Examples include asphalt, either alone or with elastomeric materials or ethylene vinyl acetate, aliphatic or fatty polyamides, and thermoplastic elastomers such as polyolefins, polyamine, polyethylene, polypropylene and polyisobutene.
During manufacture of the cell, anode casing 126 can be inverted, and then a negative electrode composition or anode mixture 128 and electrolyte put into anode casing 126. The anode mixture insertion can be a two-step process wherein dry anode mixture materials are dispensed first into the anode casing 126 followed by KOH solution dispensing. Alternatively, the wet and dry components of the anode mixture are preferably blended beforehand and then dispensed in one step into the anode casing 126. Electrolyte can creep or wick along the inner surface 136 of the anode casing 126, carrying with it materials contained in anode mixture 128 and/or the electrolyte.
An example of an anode mixture 128, for a button cell comprises a mixture of zinc, electrolyte, and organic compounds. The anode mixture 128 preferably includes zinc powder, a binder such as CARBOPOL® 940 or CARBOPOL® 934, and a gassing inhibitor such as indium hydroxide (In(OH)3) in amounts of about 99.7 weight percent zinc, about 0.25 weight percent binder, and about 0.045 weight percent indium hydroxide. CARBOPOL® 934 and CARBOPOL® 940 are acrylic acid polymers in the 100% acid form and are available from Noveon Inc. of Cleveland. Ohio.
The electrolyte composition for a button cell can be a mixture of about 97 weight percent potassium hydroxide (KOH) solution where the potassium hydroxide solution is 28-40 weight percent, preferably 30-35 weight percent, and more preferably about 33 weight percent aqueous KOH solution, and about 3.00 weight percent zinc oxide (ZnO).
The electrolyte composition for a prismatic cell can be a mixture of about 97 weight percent potassium hydroxide (KOH) solution where the potassium hydroxide solution is about 28 to about 40 weight percent, preferably about 30 to about 35 weight percent, and more preferably about 33 weight percent aqueous KOH solution, and about 1.00 to 3.00 weight percent zinc oxide (ZnO).
Preferred zinc powders are low-gassing zinc compositions suitable for use in alkaline cells with no added mercury. Examples are disclosed in U.S. Pat. No. 6,602,629 (Guo et al.), U.S. Pat. No. 5,464,709 (Getz et al.) and U.S. Pat. No. 5,312,476 (Uemura et al.), which are hereby incorporated by reference.
One example of a low-gassing zinc is ZCA grade 1230 zinc powder from Zinc Corporation of America, Monaca, Pa. which is a zinc alloy containing about 400 to about 550 parts per million (ppm) of lead. The zinc powder preferably contains a maximum of 1.5 (more preferably a maximum of 0.5) weight percent zinc oxide (ZnO). Furthermore, the zinc powder may have certain impurities. The impurities of chromium, iron, molybdenum, arsenic, antimony, and vanadium preferably total 25 ppm maximum based on the weight of zinc. Also, the impurities of chromium, iron, molybdenum, arsenic, antimony, vanadium, cadmium, copper, nickel, tin, and germanium preferably total no more than 68 ppm of the zinc powder composition by weight. More preferably, the zinc powder contains no more than the following amounts of iron, cadmium, copper, tin, chromium, nickel, molybdenum, arsenic, vanadium, antimony, and germanium, based on/the weight of zinc: Fe—3.0 ppm, Cd—8 ppm, Cu—8 ppm, Sn—1 ppm, Cr—1 ppm, Ni—1 ppm, Mo—0.25 ppm, As—0.1 ppm, Sb—0.2 ppm, V—1 ppm, and Ge—0.06 ppm.
In another embodiment, the zinc powder preferably is a zinc alloy composition containing bismuth, indium and aluminum. The zinc alloy preferably contains about 100 ppm of bismuth, 200 ppm of indium, and 100 ppm of aluminum. The zinc alloy preferably contains a low level of lead, such as about 35 ppm or less. In a preferred embodiment, the average particle size (Dso) is about 90 to about 120 microns. Examples of suitable zinc alloys include product grades NGBIA 100, NGBIA 115, and BIA available from N.V. Umicore, S.A., Brussels, Belgium.
The selection of zinc additives, for corrosion control, can be very challenging. Since these additives are often surfactants which have interactions with other components, they can influence viscosity and rheology properties. Surfactants form films on the zinc surface which impact cell impedance and rate capability, and can influence the solubility of ZnO. They are often extremely concentration dependent which further complicates their evaluation. Surfactants used in zinc air cell anode formulations such as Disperbyk 102 and Carbowax 550 are extremely concentration sensitive and have significant impact on front end rate capability and cell impedance. It is desired to use a zinc additive which forms a thin but dense film on the zinc surface and is robust to concentration effects above the monolayer requirement.
In order to find a zinc additive that provides a thin but dense film on the surface of zinc which effectively reduces corrosion without having a negative impact on cell impedance and high rate performance, a sulfotricarballylate which is a fluorosurfactant with short chain, branched fluorocarbon end groups and carboxylate acid anchor groups was used as a zinc additive in an alkaline zinc air cell. The sulfotricarballylate is available as Tivida L2300 from EMD Millipore, also known as Merck Millipore outside the United States and Canada.
A first embodiment relates to alkaline cells with zinc additive compounds of the formula (I).
where the groups Zi(Z1, Z2, and Z3) are, independently of one another, branched or unbranched alkyl groups or groups of the structure Ri(A(CR1R2)ci—(CR3R4)c′i)di—, where the respective indices ci and c′i are, independently of one another, 0-10, and di=0-5, where Ri is a branched or unbranched, fluorine-containing alkyl radical, R1 to R4 are, independently of one another, hydrogen or a branched or unbranched alkyl group, ci and c′i are not simultaneously 0, and A=O, S and/or N, Y1 is an anionic polar group and Y2 is a hydrogen atom, or vice versa, X is a cation, and at least one of the groups Zi is a group of the structure Ri(A(CR1R2)ci—(CR3R4)c′i)di—. It is preferred for formula (I) that di>0 if Z1, Z2, and Z3 are all a group of the structure Ri (O(CH2)c′i)di and all Ri are selected from CF3CF2CH2—, CF3CF2CH2CH2—, CF3CF2CF2CH2— or H(CF2)4CH2—.
The radicals Ri are branched or unbranched, fluorine-containing alkyl groups. The radicals Ri may be partly or perfluorinated and preferably contain terminal perfluorinated groups. Preference is given to branched or unbranched, fluorine-containing alkyl groups having 1 to 10 C atoms. Unbranched fluorine-containing alkyl groups preferably contain 1 to 6 C atoms, in particular 1-4 C atoms. Branched fluorine-containing alkyl groups preferably contain 3 to 6 C atoms, in particular 3-4 C atoms. The branched fluorine-containing alkyl groups used are preferably (CF3)2—CH— or (CF3)3—C— groups.
Another embodiment relates to alkaline cells with zinc additive compounds of the formula (Ia)
are, in particular, compounds in which all variables have the preferred meanings. Preference is explicitly given to compounds in which Z1=Z2=Z3=F3C(CF2)ai(CH2)bi(O(CH2)ci)di—, where ai=1-2, bi=1-2, ci=2, di=1-3, and the anionic polar grout is a sulfonate group —SO3—, and associated with a sodium ion.
Still another embodiment relates to alkaline cells with zinc additive compounds of the formula (Ib).
Preferred compounds of the formula (Ib) where Z1=Z2=Z3 and all Zi are selected from Ri(O(CH2)ci)di—, where ci=2, di=1-3, and Ri═CF3CF2CH2— or CF3CF2CF2CH2—.
The compounds of the formulas I, Ia and formula Ib are referred to in the present invention as sulfotricarballylates and are based on esters of aconitic acid, onto the double bond of which a sulfonate group has been added. In particular, sulfotricarballylates containing three fluorinated end groups according to the invention are preferred. The compounds of the formula (I) according to the invention can also be in the form of mixtures, particularly also in the form of isomer mixtures (constitutional and/or configurational isomer mixtures). In particular, diastereomer and/or enantiomer mixtures are possible. Examples of sulfotricarballylates and their synthesis are disclosed in U.S. Patent Application Publication No. 2012/0111233 A1.
The sulfotricarballylate compounds of the formulas I, Ia and formula Ib containing more than one fluorinated end groups are preferred. The sulfotricarballylate compounds can have a molecular weight preferably between 800 and 1320, most preferably between 850 and 1000. The sulfotricarballylate compounds when added to an alkaline zinc electrode form a monolayer on the surface of the zinc the width of which can be estimated. It is preferred that this monolayer be as thin as possible so as to minimize polarization. Long chain surfactants because of their structure will have much thicker monolayers. Preferred monolayer thickness is less than 50 Angstroms, and it is most preferred to have a monolayer thickness less than 25 angstroms.
A number of approaches have been proposed to screen zinc corrosion reduction additives. These include: a gel expansion test, a zinc gas generation test, measurement of anode impedance at both low and high frequency which provides information on the thickness and ion mobility associated with film formation on the surface of zinc, SEM images of zinc morphology, and whole cell performance and shelf characterization.
The following non-limiting examples are provided to further illustrate the present disclosure.
Zinc additives of interest were assembled and associated hydrogen generation was measured per a ten gram gassing test. Average gas generation was measured for ten grams of zinc over three days at 45 C and reported as ul/g/day. The ten gram gassing test consists of measuring the gas generation of zinc (with or without a zinc additive) in an electrolyte solution. The electrolyte solution is prepared by first taking 500 ml of 45% KOH solution and then adding 160 mls of water and 75 grams of ZnO. Ten grams of the zinc along with any zinc additive are added to a reaction vessel along with 5 ml of the electrolyte solution and a small amount of light mineral oil. The reaction vessel is adapted so that evolved hydrogen gas can be measured. The reaction vessel is added to a 45 C water bath and allowed to come up to temperature. After three days the hydrogen gas is measured and recorded and ul/g/day is calculated. The additives studied are shown in Table 1.
The above zinc additives evaluated at different concentrations. In all experiments the surfactant concentration is relative the weight of the zinc powder. Two zincs were used: Mitsui 81207-21 zinc, with full particle size distribution, and Grillo BIA zinc which is pre-screened to be greater than 300 microns in particle size.
In Table 2, results from a continued gas generation experiment are shown as a percent of control. In general the Grillo zinc demonstrated much lower gassing rates, about 35% of Mitsui, and thus the additives had less impact when evaluated with the Grillo zinc.
This gas generation test was interpreted strictly as a screen with results sensitive to the zinc and with considerable test to test variation. The reported values represent the average of three tests per additive. While it is the goal to minimize zinc corrosion it should be understood that the most effective additives will most likely have a negative impact on cell impedance and high rate performance. Thus the goal is to find a zinc additive that meets the objective of reducing zinc corrosion while enabling cell performance.
Referring to
Since all of the additives demonstrated a reduction in zinc corrosion, they were all evaluated in AZ13 size air cells at a concentration of 40 ppm. This level was chosen at twice the typical level to magnify the impact on cell characteristics. It may be noted that the level of sulfotricarballylates in the following summaries may be shown at either 100 ppm or 50 ppm and 40 ppm or 20 ppm. The sulfotricarballylates supplied under the Tivida trade name was supplied in a carrier solvent at about 50% concentration.
Impedance results were summarized at two weeks of product age for true IR at 50 KHz impedance measured on a Quadtech instrument (See
The 50 KHz impedance was overlapping for all surfactants except the controls, D102 and Carbowax 550, at the 40 ppm concentration level. The 50 KHz impedance also shows that a small change in concentration can have a significant impact on cell properties. The ideal surfactant would be one in which after the critical concentration required to protect the zinc surface was achieved the system would be robust to excess quantities. One reason that this is a difficult balance is that excess surfactant can alter the viscosity of the electrolyte and the rheology properties of the anode binder.
Perhaps more important than the cell resistance, is the polarization which is associated with film formation on the surface of the zinc and ion mobility. The difference between low frequency impedance linked to charge transfer and true resistance can be illustrated in a 40 Hz minus 50 KHz test.
In
AZ13 size air cells were characterized on three application tests: 3 mA continuous, 3 mA background with a 12 mA pulse for 100 msec—IEC, and a 3 mA background with a 5 mA extended pulse for 15 minutes—wireless. Results are shown below in Table 3 in mAh, in order of worst to best performance. The Control is again an identical sample with no surfactant added. In
From this performance testing, some observations were made. The controls were never the best performing product. Tivida is statistically always one of the best performing additives. Based on the results of this screening process Tivida was selected for additional characterization and concentration optimization studies.
AZ13 size air cells were prepared using conventional anode dry powder processing. In the cell builds, the Tivida concentration was varied from 10, 20, 50, and 100 ppm. A control cell using the D102 zinc additive was also prepared. The prepared air cells were characterized on two application tests: 3 mA background with a 12 mA pulse for 100 msec—IEC, and a 3 mA background with a 5 mA extended pulse for 15 minutes—wireless. Results are shown below in Table 4 in minutes service to various functional end points. The service data once again shows an advantage for Tivida over D102 by about 15% for wireless and about 10% for IEC. It also supports the conclusion that the cell is robust to excess surfactant which provides a wide window for formulations. Tivida can be added well above the monolayer concentration without having a negative impact on electrolyte viscosity or low frequency impedance. Higher concentrations may actually be beneficial perhaps increasing ZnO solubility, hydroxyl ion distribution in combination with the binder, and improving high rate performance.
While the invention has been described in detail herein in accordance with certain preferred embodiments thereof, many modifications and changes therein may be affected by those skilled in the art without departing from the spirit of the invention. Accordingly, it is our intent to be limited only by the scope of the appending claims and not by way of the details and instrumentalities describing the embodiments shown herein.
This application is a continuation of U.S. application Ser. No. 15/516,811 filed Apr. 4, 2017, which is a National Stage Application, filed under 35 U.S.C. § 371, of International Application No. PCT/US2015/054489, filed Oct. 7, 2015, which claims priority to U.S. Provisional Application No. 62/061,348, filed Oct. 8, 2014; the contents of each of which are hereby incorporated by reference in their entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4195120 | Rossler et al. | Mar 1980 | A |
| 4777100 | Chalilpoyil et al. | Oct 1988 | A |
| 5300394 | Miller et al. | Apr 1994 | A |
| 5312476 | Uemura et al. | May 1994 | A |
| 5378562 | Passaniti et al. | Jan 1995 | A |
| 5401590 | Chalilpoyil et al. | Mar 1995 | A |
| 5419977 | Weiss | May 1995 | A |
| 5464709 | Getz et al. | Nov 1995 | A |
| 5677084 | Tsukamoto et al. | Oct 1997 | A |
| 6203943 | Bennett et al. | Mar 2001 | B1 |
| 6551742 | Huq et al. | Apr 2003 | B1 |
| 6602629 | Guo et al. | Aug 2003 | B1 |
| 6780347 | Ndzebet | Aug 2004 | B2 |
| 6872489 | Armacanqui et al. | Mar 2005 | B2 |
| 6939630 | Sotomura et al. | Sep 2005 | B2 |
| 6967038 | O'Brien | Nov 2005 | B2 |
| 7005213 | Ndzebet et al. | Feb 2006 | B2 |
| 7008723 | Daniel-Ivad et al. | Mar 2006 | B2 |
| 7208248 | Hayashi et al. | Apr 2007 | B2 |
| 7563537 | Pratt et al. | Jul 2009 | B2 |
| 7615508 | Kaplan et al. | Nov 2009 | B2 |
| 7754381 | Fujino et al. | Jul 2010 | B2 |
| 7993508 | Stimits et al. | Aug 2011 | B2 |
| 8586244 | Fensore et al. | Nov 2013 | B2 |
| 8652685 | Guo | Feb 2014 | B2 |
| 8945736 | Uensel et al. | Feb 2015 | B2 |
| 8999874 | Kishimoto et al. | Apr 2015 | B2 |
| 9136540 | Padhi et al. | Sep 2015 | B2 |
| 20040229107 | Smedley | Nov 2004 | A1 |
| 20050123833 | Schubert et al. | Jun 2005 | A1 |
| 20050287438 | Bernard | Dec 2005 | A1 |
| 20060068288 | Johnson | Mar 2006 | A1 |
| 20070048576 | McKenzie et al. | Mar 2007 | A1 |
| 20070092429 | Mao et al. | Apr 2007 | A1 |
| 20070122699 | Pratt | May 2007 | A1 |
| 20070154704 | Debergalis et al. | Jul 2007 | A1 |
| 20070160898 | Takamura et al. | Jul 2007 | A1 |
| 20080096074 | Wu | Apr 2008 | A1 |
| 20080155813 | Dopp et al. | Jul 2008 | A1 |
| 20080241683 | Fensore | Oct 2008 | A1 |
| 20090320718 | Hierse et al. | Dec 2009 | A1 |
| 20110033747 | Phillips et al. | Feb 2011 | A1 |
| 20110143253 | Miyata et al. | Jun 2011 | A1 |
| 20110265669 | Padberg | Nov 2011 | A1 |
| 20110287305 | Scordilis-Kelley | Nov 2011 | A1 |
| 20120111233 | Hierse et al. | May 2012 | A1 |
| 20130162216 | Zhamu | Jun 2013 | A1 |
| 20140099539 | Yamazaki | Apr 2014 | A1 |
| 20140170478 | Liao | Jun 2014 | A1 |
| 20140239239 | Cha et al. | Aug 2014 | A1 |
| 20150244000 | Ozaki et al. | Aug 2015 | A1 |
| 20170012317 | Fukuta | Jan 2017 | A1 |
| 20170237133 | Marple | Aug 2017 | A1 |
| Number | Date | Country |
|---|---|---|
| 2005225138 | May 2006 | AU |
| 2004210507 | Oct 2009 | AU |
| 2216823 | Mar 1998 | CA |
| 2716012 | Oct 2009 | CA |
| 2321313 | Dec 2009 | CA |
| 2795492 | Oct 2011 | CA |
| 2472557 | Dec 2014 | CA |
| 102006031143 | Jan 2008 | DE |
| 2053674 | Dec 2012 | EP |
| 2654107 | Oct 2013 | EP |
| WO 2003052843 | Jun 2003 | WO |
| WO 2008051508 | May 2008 | WO |
| WO 2009016521 | Feb 2009 | WO |
| WO 2016065230 | Apr 2016 | WO |
| Entry |
|---|
| International Preliminary Report on Patentability (Chapter I) for International Application No. PCT/US2015/054489, dated Apr. 11, 2017, 7 pages. |
| International Search Report and Written Opinion for International Application No. PCT/US2015/057063, dated Jan. 22, 2016, 6 pages. |
| Usui, Hiroyuki, et al., “Novel Composite Thick-Film Electrodes Consisted of Zinc Oxide and Silicon for Lithium-Ion Battery Anode”, International Journal of Electrochemical Science, May 1, 2012, pp. 4322-4334, vol. 7, retrieved from < Novel Composite Thick-Film Electrodes Consisted of Zinc Oxide and Silicon for Lithium-Ion Battery Anode > on Apr. 19, 2017. |
| International Search Report and Written Opinion for International Application No. PCT/US2015/054489, dated Dec. 29, 2015, 8 pages. |
| Schellenberger, Steffen, et al., “A New Generation of High-Speed Fluorosurfactants”, PCI Magazine, May 1, 2013 (previously published in European Coatings Journal on Nov. 2012), 7 pages, retrieved from < http://www.pcimag.com/articles/97759-a-new-generation-of-high-speed-fluorosurfactants > on Mar. 9, 2017. |
| Basf, “Kollicoat IR: Polyvinyl alcohol-polyethylene glycol graft copolymer for instant-release coatings and quick-dissolving formulations,” BASF Technical Information, Feb. 2013, 14 pages, retrieved from <https://www.google.com/?gws_rd=ssl#q=kollicoat+ir+technical+information+basf+2013> on Jan. 14, 2017. |
| Toon, John, “Smart Hydrogel Coating Creates “Stick-slip” Control of Capillary Action,” Georgia Tech News Center, Jul. 27, 2015, 5 pages, retrieved from <http://www.news.gatech.edu/2015/07/25/smart-hydrogel-coating-creates-%E2%80%9Cstick-slip%E2%80%9D-control-capillary-action> on Jan. 14, 2017. |
| Pfeffer, Robert, et al., “Synthesis of Engineered Particulates with Tailored Properties Using Dry Particle Coating,” Powder Technology 117, 2001, 40-67. |
| Yang, Jun, et al., “Dry Particle Coating for Improving the Flowability of Cohesive Powders,” Powder Technology 158, 2005, 21-33. |
| Neburchilov, Vladimir, et al., “A Review on Air Cathodes for Zinc-Air Fuel Cells,” Journal of Power Source-195, 2010, 1271-1291. |
| Pund, K., “Recovery Act: Nanoengineered Ultracapacitor Material Surpasses the $/kW Threshold for Use in EDV' s,” EnerG2, May 16, 2012. http://www1.eere.energy.gov/vehiclesandfuels/pdfs/merit_review_2012/energy_storage/arravt011_es_pund_2012_p.pdf. |
| ENERG2 Press Release “EnerG2 nano-structured hard carbon boosts Li-ion anode capacity by >50% compared to standard graphite,” Mar. 27, 2013, http://www.greencarcongress.com/2013/03/energ2-20130327.html. |
| U.S. Appl. No. 15/516,811, Non-Final Office Action dated Jul. 27, 2018. |
| U.S. Appl. No. 15/521,223, Non-Final Office Action dated Jul. 27, 2018. |
| Office Action for U.S. Appl. No. 15/516,811 dated Jan. 11, 2019, 10 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20190363355 A1 | Nov 2019 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62061348 | Oct 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15516811 | US | |
| Child | 16437429 | US |