Flushable wipe and method of forming the same

Information

  • Patent Grant
  • 11391000
  • Patent Number
    11,391,000
  • Date Filed
    Monday, May 18, 2015
    8 years ago
  • Date Issued
    Tuesday, July 19, 2022
    a year ago
Abstract
A multi-ply flushable wipe includes a ply having first and second exterior layers and a middle layer disposed therebetween. Each of the exterior layers includes at least 50% by weight natural fibers. When foam-formed, the middle layer includes at least 25% by weight natural fibers. In embodiments, the middle layer may include at least 75% by weight natural fibers. The middle layer also includes synthetic fibers that have a length within the range of 1 mm and 20 mm. The wipe may have a length weight weighted average fiber length of less than 4 mm and a wet CD strength of greater than 20 N/m. Each ply of the wipe may be formed by wetlaying the first and second exterior layers and a foam formed middle layer to form a web, imprinting the web with a structured fabric, and drying the web. The plies are then attached using a binder.
Description
FIELD OF THE INVENTION

The present invention is directed to wipes, and in particular to wipes having one or more multi-layer plies, such as disposable, hygienic wipes.


BACKGROUND

In recent years, a growing number of people have begun to use value added consumer disposable items like facial cleaning wipes, moist towelettes, personal hygiene wipes, and time-saving products like household cleaning wipes. The market for wipes is forecast to rise significantly in the coming years.


Once dominated by baby care, the wipes market has branched out into applications targeted for specific uses like personal hygiene and household cleansing. Personal care wipes currently represent approximately 60% of the North American market for wipes and is inclusive of baby wipes, various targeted personal hygiene cleansing wipes (hands, face, wounds, flushable adult wipes), feminine hygiene, and adult incontinence. Household wipes currently represent approximately 25% of the market and are inclusive of targeted cleansing wipes for the kitchen, bathroom, windows, and even automobiles. Industrial wipes represent the remaining approximately 15% of the market and are used for industrial equipment cleaning.


A key consumer demand is for greener or more eco-friendly wipe products. This necessitates developing biodegradable products with minimal environmental footprint through all levels of the supply chain, including raw materials, packaging, transportation, and overall manufacturing operations.


“Flushability” has become a critical issue for wipes manufacturers as well. Wastewater treatment facilities have been focusing their attention on wipes as they are clogging piping and pumps at the treatment plants. INDA has been working with wipes manufacturers, wastewater treatment facilities and local government officials to address this growing issue.


Utilization of the appropriate technology and fiber sources to create wipe products that are low cost, eco-friendly, and of high quality are therefore mandatory for success in today's marketplace.


Currently available flushable wipe products are not truly flushable because they do not disperse well in all conditions that wipes encounter in the household toilet/septic systems. Most of these products are size-based flushable wipes and pass through plumbing systems without breaking down into smaller pieces or fiber clusters. As a result, even though they pass through the piping systems immediately after flushing, they often plug up the sewage systems and the effluent clarifier's controlled by the city/municipal systems. In addition, the fibers used in the manufacture of these types of products are not all natural fibers. Almost every flushable product available has a significant amount of synthetic fibers, such as polyethylene, polypropylene, or polyester, in the form of single component or bicomponent fibers. Almost all products that are claimed as flushable wipes may pass the INDA flushability guidelines but are not truly flushable because they do not disperse adequately to pass through smaller pipes and other types of restrictions in sewage treatment systems.


SUMMARY OF THE INVENTION

An object of the present invention is to provide a true flushable wipe that disintegrates when flushed and does not plug up city/municipal sewage systems (i.e., the wipe is septic safe).


Another object of the present invention is to provide a flushable wipe that is biodegradable.


Another object of the present invention is to provide a flushable wipe that includes a binder that allows the wipe to be pre-moistened without losing its functional strength properties.


A flushable wipe according to an exemplary embodiment of the present invention is a three layer wipe having external layers and an internal, core layer. The external layers are composed primarily of natural fibers, and in an exemplary embodiment the external layers are made up of 50% to 100% by weight natural fibers. The core layer is composed of a foam-formed fiber blend of natural fibers and long synthetic fibers. The synthetic fibers are non-thermoplastic fibers. In an exemplary embodiment, the core layer is made up of 25% to 75% by weight natural fibers and 1% to 75% by weight long synthetic fibers. The basis weight of the wipe is within the range of 20 gsm to 100 gsm.


A flushable wipe according to another exemplary embodiment of the present invention has more than four layers, with each layer containing a mixture of cellulosic fiber and bi-component fibers. The flushable wipe may contain water soluble binders with a trigger component. This trigger component is a controlled concentration of salt in the wetting solution that insolubilizes the binder and allows it to function as an adhesive for the substrate. When the controlled concentration of salt is diluted, the binder becomes soluble and starts to drop strength below a critical level.


A flushable wipe according to another exemplary embodiment of the present invention has two layers, where the first layer is spun or melt blown with the forming wire stretched and de-stretched during the production process to give the substrate some stretch. The second layer is foam formed and the fibers are much smaller than the first layer and the two layers are plied via hydroentangling.


In embodiments, the flushable wipe of the present invention may be single ply. In other embodiments, the flushable wipe may comprise two or more plies.


The present invention also encompasses a method of manufacturing such flushable wipes and an apparatus for manufacturing such flushable wipes.


In embodiments, a multi-ply flushable wipe comprises two or more plies with at least one of the two or more plies comprising first and second exterior layers and a foam-formed middle layer disposed between the first and second exterior layers. Each of the exterior layers comprises at least 50% by weight natural fibers. The middle layer comprises synthetic fibers and at least 25% by weight natural fibers, the synthetic fibers having a length within the range of 1 mm and 20 mm. In embodiments, at least one of the first and second exterior layers is also foam formed. The at least one other ply of the wipe may be substantially identical in structure to the at least one ply.


The natural fibers of the multi-ply flushable wipe may comprise fibers of the type selected from the group consisting of: softwood fibers, hardwood fibers, elephant grass, nettle, buntal, buri, soybean protein, milvet milk, abaca, bagasse, bamboo, coir, cotton, flax, linen, hemp, jute, kapok, kenaf, pina, raffia, ramie, sisal, oxidized natural fibers and combinations thereof. The natural fibers may be or may include alternate natural fibers of the type selected from the group consisting of: abaca, bamboo, coir, flax, linen, kapok, pina, raffia, ramie, sisal, nettle, buntal, buri, cotton, kenaf, elephant grass, jute, hemp, bagasse fibers and combinations thereof. The synthetic fibers, which may be or may include semi-synthetic fibers, may comprise fibers of the type selected from the group consisting of: acrylic, aramid, para-aramid, meta-aramid, modacrylic, nylon, olefin, polyester, polyethylene, ultra-high molecular weight polyethylene, polyester-polyurethane copolymer, polyvinyl alcohol, polyvinyl chloride, poly(p-phenylene-2,6-benzobisoxazole), polypropylene, ethylene vinyl alcohol and combinations thereof, and/or may comprise semisynthetic fibers of the type selected from the group consisting of: regenerated cellulose, rayon, lyocell, polylactic acid, polyvinyl alcohol and combinations thereof. The synthetic fibers of the flushable wipe are generally non-thermoplastic. An average fiber length of the multi-ply flushable wipe is less than 5 mm.


The multi-ply flushable wipe has at least one of the following properties: a porosity below 40 cfm, a basis weight below 90 gsm, a machine direction tensile strength within the range of 30 N/m to 250 N/m, or preferably a machine direction tensile strength within the range of 50 N/m to 150 N/m, a cross direction tensile strength within the range of 30 N/m to 250 N/m, or preferably a cross direction tensile strength within the range of 50 N/m to 150 N/m, and a thickness within the range of 300 to 1500 microns, preferably a thickness within the range of 400 to 1250 microns.


At least one ply of the multi-ply flushable wipe may be comprised of one or more of the following combinations: a combination of softwood fibers and alternate natural fibers; a combination of softwood fibers and modified rayon fibers; a combination of softwood fibers and renewable polymeric fibers; a combination of softwood fibers and water based polyvinyl alcohol (PVA) fibers; a combination of softwood fibers, renewable polymeric fibers and polyvinyl alcohol (PVA) fibers; and a combination of softwood fibers, modified rayon fibers, renewable polymeric fibers, water-based polyvinyl alcohol (PVA) fibers and alternate natural fibers.


In embodiments, at least one ply of the multi-ply flushable wipe comprises rayon fibers at an inclusion rate within the range of 10% to 50% by weight. The modified rayon fibers may have shaped fibers having tri-lobal or star-shaped cross-sections. The modified rayon fibers may be viscose rayon fibers, such as lyocell fibers.


Also, in embodiments, at least one ply of the multi-ply flushable wipe may comprise water-based polyvinyl alcohol (PVA) fibers at an inclusion rate of 10% to 50% by weight. The water-based polyvinyl alcohol (PVA) fibers are shaped fibers may be tri-lobal or star-shaped cross-sections.


In embodiments, at least one ply of the multi-ply flushable wipe may comprise polylactic acid (PLA) fibers at an inclusion rate of 1% to 25% by weight. The polylactic acid (PLA) fibers are shaped fibers may have tri-lobal or star-shaped cross-sections.


A slurry from which the multi-ply flushable wipe is formed may comprise additives, enzymes, and/or fillers. The additives may comprise additives of the type selected from the group consisting of: urea formaldehyde, melamine formaldehyde, poly amide poly amine epichlorohydrin, polyethlyenimine, starch, starch derivatives, aldehyde functionalized starches, chitosan, aldehyde functionalize polyacrylamides, glyoxalated polyacrylamide, glyoxalated copolymer, carboxyl methyl cellulose, polyvinyl alcohol, polyvinyl acetate, polyvinyl amine, polyamide resins, polyacrylamide resins, galactomannan gums, acrylic emulsions, styrene-butadiene latexes, vinyl acetate polymers, ethylene-vinyl acetate copolymers, vinyl chloride polymers, vinylidene chloride polymers, vinyl chloride-vinylidene copolymers, acrylo-nitrile copolymers, ethylene-acrylic copolymers, latex emulsions, acrolein copolymers and combinations thereof. The enzyme may comprise, for example, oxidoreductase enzymatic systems. The fillers may comprise, for example, at least one of calcium carbonate particles, clay particles or talc particles. The multi-ply flushable wipe may also include filler material, such as at least one of super absorbent polymers and encapsulated polymers.


The multi-ply flushable wipe may include a binder between the two or more plies. The binder may be of a type selected from the group consisting of: poly(vinyl) alcohol, poly(vinyl)acetate, poly (ethylene) (vinyl) alcohols, poly (ethylene) (vinyl)acetate, copolymers of vinyl acetate-ethylene, starch based chemistries and combinations thereof. The binder may further comprise a cross-linking agent, ion sensitive polymers, a trigger chemistry, such as boric acid, and/or a trigger salt chemistry, such as sodium chloride. The two or more plies of the wipe may be held together by embossments.


In embodiments, the multi-ply flushable wipe also comprises a cleansing solution and/or a wetting/cleaning solution. A cleansing solution may include glycol based cross-linking chemistry, anhydrides and epoxy groups, cyclo-dextrins adapted to release fragrances, and/or at least one of aloe or shea butter. The cleansing solution may be present in the amount of 40% to 80% by weight. A wetting/cleaning solution may include purified water and a combination of one or more of the following: humectants, preservatives, moisturizers, surfactants, chelating agents, pH buffer and aromatic compounds.


The resulting multi-ply flushable wipe desirably has a basis weight within the range of 20 gsm to 100 gsm.


In another exemplary embodiment in accordance with the present invention, a multi-ply flushable wipe comprises two or more plies with at least one of the two or more plies comprising first and second exterior layers and a middle layer disposed between the first and second exterior layers. Each of the exterior layers comprises at least 50% by weight natural fibers. In this embodiment, the middle layer comprises synthetic fibers and at least 75% by weight natural fibers, the synthetic fibers having a length within the range of 1 mm and 20 mm. The ply has an average fiber length (LWW) of less than about 4 mm. The wipe has a cross direction wet strength greater than 20 N/m and the wipe is dispersible. In embodiments, at least one of the two or more plies of the wipe comprises greater than 80% pulp fibers. This multi-ply flushable wipe may further a cleansing solution and/or a binder between the two or more plies. The wipe may have at least one of the following properties: a porosity below 40 cfm, a basis weight below 90 gsm, a machine direction tensile strength within the range of 30 N/m to 250 N/m, or preferably a machine direction tensile strength within the range of 50 N/m to 150 N/m,


The present invention further comprises a method of forming a multi-ply flushable wipe, that includes forming two or more plies. Each ply is formed by wetlaying first and second exterior layers and a foam formed middle layer so as to form a web, where each of the first and second exterior layers comprises at least 50% by weight natural fibers and the foam-formed middle layer comprises synthetic fibers and at least 25% by weight natural fibers, the synthetic fibers having a length within the range of 1 mm and 20 mm. The web is then imprinted with a structured fabric and dried. The two or more plies are attached together using a binder to form the multi-ply flushable wipe. The drying step may include a through air drying process in which the web is dried on a steam heated cylinder, and may include use of a belt press. The method may further include a step of removing the dried web from the steam heated cylinder, such as by creping or by blowing the dried web off the steam heated cylinder. Additionally, the method may include the step of pre-drying the web after imprinting.


Other features and advantages of embodiments of the invention will become readily apparent from the following detailed description, the accompanying drawings and the appended claims.





BRIEF DESCRIPTION OF THE DRAWINGS

Exemplary embodiments of the present invention will be described with references to the accompanying figures, wherein:



FIG. 1 is a schematic diagram of a three layer ply of a wipe formed by a wet laid process in accordance with an exemplary embodiment of the present invention;



FIG. 2 is a block diagram of a system for manufacturing a single ply wipe according to an exemplary embodiment of the present invention;



FIG. 3 is a block diagram of a system for manufacturing a multi-ply wipe product according to an exemplary embodiment of the present invention; and



FIG. 4 shows an embodiment of a wipe that has an embossment pattern in accordance with an exemplary embodiment of the present invention.





DETAILED DESCRIPTION

The present invention is directed to a flushable and dispersible wipe including a core layer that may be composed of a foam-formed fiber blend of natural fibers (which may be or include alternative natural fibers) and long synthetic fibers (which may be or include semi-synthetic fibers). For the purposes of the present disclosure, the term “long fiber” is intended to mean fibers having a length of at least 1 mm, preferably within the range of 1 mm and 20 mm, more preferably within the range of 3 mm and 15 mm. Also, for the purposes of the present disclosure, the term “flushable” is intended to mean that the wipe is able to be disposed of through sanitation fixtures, such as toilets, without clogging or otherwise interfering with the disposal process. The current measure of flushability is set by the 3rd edition of the INDA/EDANA Flushability Guidelines (Guidance Document for Assessing Flushability of Nonwoven Disposable Products (June 2013)). A wipe is considered “dispersible” if it passes the Slosh Box Disintegration Test set forth in INDA FG502. Unless otherwise specified, for the purposes of the present invention, weight percentages are given relative to the dry weight of the final product (i.e, prior to application of lotions or other post formation additives).



FIG. 1 shows a three layer ply of a wipe, generally designated by reference number 1, according to an exemplary embodiment of the present invention. The wipe 1 has external layers 2 and 4 as well as an internal, core layer 3. External layers 2 and 4 are composed primarily of natural fibers 20, and in an exemplary embodiment the external layers 2 and 4 are made up of 50% to 100% by weight natural fibers. (The remaining fibers can be synthetic or semisynthetic fibers.) In an exemplary embodiment, the external layers 2 and 4 are made up of 90% by weight natural fibers. (The remaining fibers can be synthetic or semisynthetic fibers.) The core layer 3 is composed of water or foam-formed fiber blend of natural fibers 20 and long synthetic fibers 21. The synthetic fibers 21 are non-thermoplastic fibers. In an exemplary embodiment, the core layer 3 is made up of 25% to 75% by weight natural fibers and 1% to 75% by weight long synthetic fibers. (The remaining fibers can be short synthetic or semisynthetic fibers.) In an exemplary embodiment, the core layer 3 is made of 50% by weight natural fibers and 50% by weight long synthetic fibers. The basis weight of the wipe 1 is within the range of 20 gsm to 100 gsm, and in an exemplary embodiment has a basis weight of 50 gsm. The average fiber length of the long synthetic fibers that are used in wipe 1 is, in embodiments, less than 5 mm, and may be more preferably less than 4 mm.


The wipe 1 may be produced using a single layered headbox wherein the above mentioned natural and synthetic fibers, or combinations thereof may be used in the forming section. Alternatively, wipe 1 may be produced using a stratified headbox to form multiple layers simultaneously.


The natural fibers/alternate natural fibers 20 used to form the wipe 1 may be composed of natural cellulose fibers derived from, for example, softwood, hardwood, kenaf, elephant grass, esparto grass, sisal, abaca, jute, hemp, kemp, bagasse, cotton linters, soybean protein, milvet milk, abaca, bamboo, coir, flax, linen, kapok, pina, raffia, ramie, sisal, nettle, buntal, buri, other lignaceous and cellulose fibers, or other oxidized natural fibers that increase acid group content greater than 5.5 meq/100 g (meq=milliequivalents of solute), or combinations thereof. For example, the combination of natural fibers that are used may be a combination of softwood and hardwood fibers, or a combination of softwood fibers and alternate natural fibers.


The synthetic fibers 21 used to form the core layer 3 may be, for example, rayon fibers, renewable polymeric fibers, water-based polyvinyl alcohol (PVA) fibers, acrylic, aramid, Twaron, Kevlar, Technora, Nomex, Microfiber, Modacrylic, Nylon, Olefin, Polyester, Polyethylene, Dyneema, Spectra, Spandex, Vinylon, Vinyon, Zylon, Polypropylene, or Ethylene Vinyl Alcohol, or combinations thereof. The semi-synthetic fibers that can be used to form the core layer 3 may be, for example, modified rayon fibers, regenerated cellulose (from any source such as bamboo, wood, modal, acetate, diacetate, or triacetate), polylactic acid, or polyvinyl alcohol, or combinations thereof. Thus, the core layer 3 may include, for example, one or more natural fibers, such as softwood fibers, and one or more of these synthetic or semisynthetic fibers.


If modified rayon fibers are used as the synthetic fibers 21, the modified rayon fibers may be composed of viscose rayon, lyocell (e.g., Tencel®, manufactured by Lenzing AG of Lenzing, Austria), or combinations thereof and may have an inclusion rate within the range of 10% to 50% by weight, and preferably 25% by weight of the entire tissue. The modified rayon fibers have a length within the range of 1 to 20 mm. The modified rayon fibers may be shaped fibers, such as, for example, fibers having multi-lobal or star-shaped cross sections.


If water-based PVA fibers are used as the synthetic fibers 21, the water-based PVA fibers may be added at an inclusion rate of 10% to 50% by weight, and preferably 25% by weight. The water-based PVA fibers have a length within the range of 4 mm to 20 mm, and may be shaped fibers, such as, for example, fibers having multi-lobal or star-shaped cross sections.


If renewable polymeric fibers are used as the synthetic fibers 21, the renewable polymeric fibers may be composed of poly(lactic acid) (PLA) and may have an inclusion rate within the range of 10% to 50% by weight, and preferably 25% by weight. The renewable polymeric fibers have a length within the range of 4 mm to 20 mm. The renewable polymeric fibers may be shaped fibers, such as, for example, fibers having multi-lobal or star-shaped cross sections.


Wet-end additives may be included in the layers of the wipe 1. In this regard, as known in the art, pulp mixes are subjected to a dilution stage in which water is added to the mixes so as to form a slurry. After the dilution stage but prior to reaching the headbox, each of the pulp mixes are dewatered to obtain a thick stock of about 95% water. In an exemplary embodiment of the invention, wet end additives are introduced into the thick stock pulp mixes of all layers, and in an exemplary embodiment the wet end additives may only be introduced into the thick stock pulp mixes of only the external layers. Suitable wet-end additives include temporary wet strength additives, such as, for example, water-based PVA, glyoxalated polyacrylamide (commonly known as GPAM), carboxyl methyl cellulose (CMC), and combinations thereof, such as a combination of GPAM and CMC. If GPAM is used as the wet-end additive, the GPAM may be present at concentrations ranging from 0.01% to 4% of the weight of the fibers of the wipe 1, and in an exemplary embodiment is present at a concentration of 0.5% of the weight of the fibers of the wipe 1. If carboxyl methyl cellulose is used as the wet-end additive, the carboxyl methyl cellulose may be present at concentrations ranging from 0.01% to 1% of the weight of fibers of the wipe 1, and in an exemplary embodiment is present at a concentration of 0.25% of the weight of fibers of the wipe 1.


Enzymes may also be added to the slurry as a wet-end additive to refine, de-ink and/or bleach recycled pulp. Such enzymes may be present at concentrations ranging from 0.1% to 2% of the weight of fibers. An example of a suitable enzyme is oxidoreductase, which requires a small dose of hydrogen peroxide initiator or ammonium per sulfate.


In an exemplary embodiment, a dry strength additive is added to the thick stock mix for at least one of the layers of the tissue. The dry strength additive may be, for example, amphoteric starch, added in a range of about 1 kg/ton to 15 kg/ton to the thick stock mix.


As an alternative or in addition to the use of wet end additives, the wipe of the present invention may be treated with topical or surface deposited additives. Examples of surface deposited additives include temporary wet strength additives such as GPAM and/or CMC. The temporary wet strength additive may be sprayed directly on the wipe basesheet during the converting process with an add-on up to 1% to 2% of the weight of the fibers of the wipe 1.


Other examples of surface deposited additives include softeners for increasing fiber softness and skin lotions. Examples of topical softeners include but are not limited to quaternary ammonium compounds, including, but not limited to, the dialkyldimethylammonium salts (e.g. ditallowdimethylammonium chloride, ditallowdimethylammonium methyl sulfate, di(hydrogenated tallow)dimethyl ammonium chloride, etc.). Another class of chemical softening agents include the well-known organo-reactive polydimethyl siloxane ingredients, including amino functional polydimethyl siloxane. zinc stearate, aluminum stearate, sodium stearate, calcium stearate, magnesium stearate, spermaceti, and steryl oil. The softener additive may be applied to the basesheet by, for example, spraying, roll coating/anilox roll set up or flexographic/gravure roll coating the wipes when they are a wet laid asset or after the wipes are dried but before wetting solution is added to the package.


In addition to the above, other additives can be incorporated into the slurry prior to deposition onto the forming surface, sprayed onto the web during the wet-laid process or added during the plying step after the web has fully dried. In embodiments, the additives can be added in an amount up to 5% of the weight of fibers of the wipe 1.


The additives can be one or a combination of the following: urea formaldehyde, melamine formaldehyde, poly amide poly amine epichlorohydrin, polyethlyenimine, starch and starch derivatives, aldehyde functionalized starches, chitosan, aldehyde functionalize polyacrylamides, glyoxalated polyacrylamide, glyoxalated copolymer, carboxyl methyl cellulose, polyvinyl alcohol, polyvinyl acetate, polyvinyl amine, polyamide resins, polyacrylamide resins, galactomannan gums such as guar guam and locus bean gum, acrylic emulsions, styrene-butadiene latexes, vinyl acetate polymers, ethylene-vinyl acetate copolymers, vinyl chloride polymers, vinylidene chloride polymers, vinyl chloride-vinylidene copolymers, acrylo-nitrile copolymers, ethylene-acrylic copolymers, latex emulsions, and acrolein copolymers. In embodiments, when added to the slurry, these additives can be added at a concentration ranging from 0.1 to 4% of the weight of fibers, more preferably about 0.5% of the weight of fibers.


The additives can also be a combination of the following: starch and starch derivatives, aldehyde functionalized starches, chitosan, aldehyde functionalize polyacrylamides, glyoxalated polyacrylamide, glyoxalated copolymers, carboxyl methyl cellulose, polyvinyl alcohol, polyvinyl acetate, polyvinyl amine, polyamide resins, polyacrylamide resins, galactomannan gums such as guar guam and locus bean gum, acrylic emulsions, styrene-butadiene latexes, vinyl acetate polymers, ethylene-vinyl acetate copolymers, vinyl chloride polymers, vinylidene chloride polymers, vinyl chloride-vinylidene copolymers, acrylo-nitrile copolymers, ethylene-acrylic copolymers, latex emulsions, and acrolein copolymers. In embodiments, when added to the slurry, these additives can be added at a concentration ranging from 0.1 to 4% of the weight of fibers of the wipe 1, more preferably about 0.5% of the weight of fibers of the wipe 1.


The additives can alternatively be one or a combination of the following: starch and starch derivatives, aldehyde functionalized starches, chitosan, aldehyde functionalize polyacrylamides, glyoxalated polyacrylamide, glyoxylated copolymers, carboxyl methyl cellulose, polyvinyl alcohol, polyvinyl acetate, polyvinyl amine, polyamide resins, polyacrylamide resins, galactomannan gums such as guar guam and locus bean gum. In embodiments, when added to the slurry these additives can be added at a concentration ranging from 0.1 to 4% of the weight of fibers of the wipe 1, more preferably about 0.5% of the weight of fibers of the wipe 1.


The additives can alternatively be one or a combination of the following: starch and starch derivatives, aldehyde functionalized starches, chitosan, aldehyde functionalize polyacrylamides, glyoxalated polyacrylamide, glyoxylated copolymers, carboxyl methyl cellulose, polyvinyl alcohol, polyvinyl acetate, polyvinyl amine, polyamide resins, and polyacrylamide resins. In embodiments, when added to the slurry these additives can be added at a concentration ranging from 0.1 to 4% of the weight of fibers of the wipe 1, more preferably about 0.5% of the weight of fibers of the wipe 1. A cleansing solution may be topically applied to the wipe. Examples of cleansing solutions include glycol-based cross-linking chemistry including anhydrides and epoxy groups, cyclo-dextrins with the ability to release fragrances, aloe (such as Aloe E) and shea butter. The cleansing solution can be composed of 90-99.9% water with the remainder being preservative, humectants, moisturizers, pH buffers, surfactants, or aromatic compounds. In embodiments, the aloe or shea butter may be applied in a concentration of up to 0.5% of the cleansing solution. In embodiments, the wet wipe may contain as much as 40% to 90%, by weight of cleansing solution in the final product, and more preferably 70% by weight of cleansing solution in the final product.


Fillers may also be added to the slurry at addition rates of 0.1% to 1% of the weight of the fibers of the wipe 1, more preferably about 0.5% by weight of fibers of the wipe 1. Fillers may be, for example, calcium carbonate particles, clay particles and/or talc particles. Fillers may also be superabsorbent polymers or encapsulated polymers.


The absorbent products or structures that are used for each of the webs for the one or more plies can be manufactured by any known or later-discovered wet-laid method that uses water to form a web. Examples of some known wet-laid technologies that may be used to form a cellulosic (or other natural or synthetic fiber type) web include Through Air Drying (TAD), Uncreped Through Air Drying (UCTAD), Conventional Wet Crepe (CWC), Conventional Dry Crepe (CDC), Advanced Tissue Molding System (ATMOS), NTT, and ETAD.


The Through Air Drying (TAD) and Uncreped Through Air Drying (UCTAD) processes are wet-laid technologies that avoid compaction of the web during drying and thereby produce absorbent products of superior thickness and absorbency when compared to absorbent products of similar basis weight and material inputs that are produced using the CWC or the CDC process. Other wet-laid processes, such as ATMOS, ETAD, and NTT, utilizes some pressing to dewater the web, or a portion of the web, resulting in absorbent products with absorbent capacities that correlate to the amount of pressing utilized when all other variables are the same. Some wet-laid processes are discussed below.


Wet-Laid Processes

Tissue papermaking is a complex process where specific control over product quality attributes is critical. Arguably, the most critical pieces of equipment used to control these quality attributes are the fabrics utilized in the papermaking machines. The various papermaking machine technologies are conventional dry crepe, through air drying (TAD), or hybrid technologies such as Metso's NTT (Metso Corp., Helsinki, Finland), Georgia Pacific's ETAD (Georgia Pacific LLC, Atlanta, Ga.), or Voith's ATMOS process (Voith GmbH, Heidenheim, Germany). All these technologies utilize fabrics at various stages in the process to influence tissue web properties and overall asset productivity.


The predominant manufacturing method for making a tissue web is the conventional dry crepe process. The major steps of the conventional dry crepe process involve stock preparation, forming, pressing, drying, creping, calendering (optional), and reeling the web.


The first step of stock preparation involves selection, blending, mixing, and preparation of the proper ratio of wood, plant, or synthetic fibers along with chemistry and fillers that are needed in the specific tissue grade. This mixture is diluted to over 99% water in order to allow for an even fiber formation when deposited from the machine headbox into the forming section. There are many types of forming sections used in conventional papermaking (inclined suction breast roll, twin wire C-wrap (with a solid or suction forming roll), twin wire S-wrap, suction forming roll, and Crescent formers) but all are designed to retain the fiber, chemical, and filler recipe while allowing the water to drain from the web. In order to accomplish this, fabrics, referred to as “forming fabrics,” are utilized.


Forming fabrics are woven structures that utilize monofilaments (yarns, threads) composed of synthetic polymers (usually polyethylene, polypropylene, or nylon). The forming fabric has two surfaces: the sheet side and the machine or wear side. The wear side is in contact with the elements that support and move the fabric and are thus prone to wear. To increase wear resistance and improve drainage, the wear side of the fabric has larger diameter monofilaments compared to the sheet side. The sheet side has finer yarns to promote fiber and filler retention on the fabric surface.


In order to control other properties such as: fabric stability, life potential, drainage, fiber support, and clean-ability, different weave patterns are utilized. Generally, forming fabrics are classified by the number of layers utilized in their construction. There are three basic styles of forming fabrics: single layer, double layer, and triple layer. A single layer fabric is composed of one CD (shute) and one MD (warp) yarn system. The main problem of single layer fabrics is lack of dimensional stability. The double layer forming fabric has one layer of warp yarns and two layers of shute yarns. This multilayer fabric is generally more stable and resistant to stretching. Triple layer fabrics have two separate single layer fabrics bound together by separated yarns called binders. Usually the binder fibers are placed in cross direction but also can be oriented in the machine direction. Triple layer fabrics have further increased dimensional stability, wear potential, drainage, and fiber support than single or double layer fabrics.


The manufacturing of forming fabrics comprises the following operations: weaving, initial heat setting, seaming, final heat setting, and finishing. The fabric is made in a loom using two interlacing sets of monofilaments (or threads or yarns). The longitudinal threads are called the warp and the transverse threads are called shute threads. After weaving, the forming fabric is heated to relieve internal stresses to enhance dimensional stability of the fabric. The next step in manufacturing is seaming. This step converts the flat woven fabric into and endless forming fabric by joining the two MD ends of the fabric. After seaming, the final heat setting is applied to stabilize and relieve the stresses in the seam area. The final step in the manufacturing process is finishing, where the fabric is cut to width and sealed.


There are several parameters and tools used to characterize the properties of the forming fabric: mesh and count, caliper, frames, plane difference, open area, air permeability, void volume and distribution, running attitude, fiber support, drainage index, and stacking. None of these parameters can be used individually to precisely predict the performance of a forming fabric on a paper machine, but together the expected performance and sheet properties can be estimated.


In a conventional process, after web formation and drainage (to around 35% solids) in the forming section (assisted by centripetal force around the forming roll, and vacuum boxes in several former types), the web is transferred to a press fabric upon which the web is pressed between a rubber or polyurethane covered suction pressure roll and Yankee dryer. The press fabric is a permeable fabric designed to uptake water from the web as it is pressed in the press section. It is composed of large monofilaments or multi-filamentous yarns, needled with fine synthetic batt fibers to form a smooth surface for even web pressing against the Yankee dryer.


After pressing the sheet, between a suction pressure roll and a steam heated cylinder (referred to as a Yankee dryer), the web is dried from up to 50% solids to up to 99% solids using the steam heated cylinder and hot air impingement from an air system (air cap or hood) installed over the steam cylinder. The sheet is then creped (i.e. removed) from the steam cylinder using a steel or ceramic doctor blade. This is a critical step in the conventional dry crepe process. The creping process greatly affects softness as the surface topography is dominated by the number and coarseness of the crepe bars (finer crepe is much smoother than coarse crepe). Some thickness and flexibility is also generated during the creping process. If the process is a wet crepe process, the web must be conveyed between dryer fabrics through steam heated after-dryer cans to dry the web to the required finished moisture content. After creping, the web is optionally calendered and reeled into a parent roll and ready for the converting process.


The through air dried (TAD) process is another manufacturing method for making a tissue web. The major steps of the through air dried process are stock preparation, forming, imprinting, thermal pre-drying, drying, creping, calendering (optional), and reeling the web. The stock preparation and forming steps are similar to conventional dry creping.


Rather than pressing and compacting the web, as is performed in conventional dry crepe, the web undergoes the steps of imprinting and thermal pre-drying. Imprinting is a step in the process where the web is transferred from a forming fabric to a structured fabric (or imprinting fabric) and subsequently pulled into the structured fabric using vacuum (referred to as imprinting or molding). This step imprints the weave pattern (or knuckle pattern) of the structured fabric into the web. This imprinting step has a tremendous effect on the softness of the web, both affecting smoothness and the bulk structure. The design parameters of the structured fabric (weave pattern, mesh, count, warp and weft monofilament diameters, caliper, air permeability, and optional over-laid polymer) are, therefore, critical to the development of web softness. The manufacturing method of an imprinting fabric is similar to a forming fabric, except for an additional step if an overlaid polymer is utilized. These type of fabrics are disclosed in patents such as U.S. Pat. Nos. 5,679,222; 4,514,345; 5,334,289; 4,528,239 and 4,637,859, hereby incorporated by reference. Essentially, fabrics produced using these methods result in a fabric with a patterned resin applied over a woven substrate. The benefit is that resulting patterns are not limited by a woven structure and can be created in any desired shape to enable a higher level of control of the web structure and topography that dictate web quality properties.


After imprinting, the web is thermally pre-dried by moving hot air through the web while it is conveyed on the structured fabric. Thermal pre-drying can be used to dry the web to over 90% solids before it is transferred to a steam heated cylinder. The web is then transferred from the structured fabric to the steam heated cylinder though a very low intensity nip (up to 10 times less than a conventional press nip) between a solid pressure roll and the steam heated cylinder. The only portions of the web that are pressed between the pressure roll and steam cylinder rest on knuckles of the structured fabric, thereby, protecting most of the web from the light compaction that occurs in this nip. The steam cylinder and an optional air cap system, for impinging hot air, then dry the sheet to up to 99% solids during the drying stage before creping occurs. The creping step of the process again only affects the knuckle sections of the web that are in contact with the steam cylinder surface. Due to only the knuckles of the web being creped, along with the dominant surface topography being generated by the structured fabric, and the higher thickness of the TAD web, the creping process has much smaller effect on overall softness as compared to conventional dry crepe. After creping, the web is optionally calendered and reeled into a parent roll and ready for the converting process from a basesheet to a multi-ply material, if desired. Some TAD machines utilize fabrics (similar to dryer fabrics) to support the sheet from the crepe blade to the reel drum to aid in sheet stability and productivity. Examples of creped through air dried products are described in U.S. Pat. Nos. 3,994,771; 4,102,737; 4,529,480 and 5,510,002, hereby incorporated by reference.


A variation of the TAD process where the sheet is not creped, but rather dried to up to 99% using thermal drying and blown off the structured fabric (using air) to be optionally calendered and reeled also exits. This process is called UCTAD or un-creped through air drying process. An example of an uncreped through air dried product is described in U.S. Pat. No. 5,607,551, hereby incorporated by reference.


A newer process/method and paper machine system for producing tissue has been developed by the Voith GmbH and is being marketed under the name ATMOS. The process/method and paper machine system has several patented variations, but all involve the use of a structured fabric in conjunction with a belt press. The major steps of the ATMOS process and its variations are stock preparation, forming, imprinting, pressing (using a belt press), creping, calendering (optional), and reeling the web.


The stock preparation step is the same as a conventional or TAD machine would utilize. The purpose is to prepare the proper recipe of fibers, chemical polymers, and additives that are necessary for the grade of tissue being produced, and diluting this slurry to allow for proper web formation when deposited out of the machine headbox (single, double, or triple layered) to the forming surface. The forming process can utilize a twin wire former (as described in U.S. Pat. No. 7,744,726) a Crescent Former with a suction Forming Roll (as described in U.S. Pat. No. 6,821,391), or preferably a Crescent Former (as described in U.S. Pat. No. 7,387,706). The preferred former is provided a slurry from the headbox to a nip formed by a structured fabric (inner position/in contact with the forming roll) and forming fabric (outer position). The fibers from the slurry are predominately collected in the valleys (or pockets, pillows) of the structured fabric and the web is dewatered through the forming fabric. This method for forming the web results in a unique bulk structure and surface topography as described in U.S. Pat. No. 7,387,706 (FIG. 1 through FIG. 11). The fabrics separate after the forming roll with the web staying in contact with the structured fabric. At this stage, the web is already imprinted by the structured fabric, but utilization of a vacuum box on the inside of the structured fabric can facilitate further fiber penetration into the structured fabric and a deeper imprint.


The web is now transported on the structured fabric to a belt press. The belt press can have multiple configurations. A belt press configurations used in conjunction with a structured fabric can be viewed in U.S. Pat. No. 7,351,307, incorporated by reference herein, where the web is pressed against a dewatering fabric across a vacuum roll by an extended nip belt press. The press dewaters the web while protecting the areas of the sheet within the structured fabric valleys from compaction. Moisture is pressed out of the web, through the dewatering fabric, and into the vacuum roll. The press belt is permeable and allows for air to pass through the belt, web, and dewatering fabric, into the vacuum roll enhancing the moisture removal. Since both the belt and dewatering fabric are permeable, a hot air hood can be placed inside of the belt press to further enhance moisture removal as shown in FIG. 14 of U.S. Pat. No. 7,351,307. Alternately, the belt press can have a pressing device arranged within the belt which includes several press shoes, with individual actuators to control cross direction moisture profile, (see FIG. 28 in U.S. Pat. No. 7,951,269 or 8,118,979, or FIG. 20 of U.S. Pat. No. 8,440,055, each of which are hereby incorporated by reference) or a press roll (see FIG. 29 in U.S. Pat. No. 7,951,269 or 8,118,979, or FIG. 21 of U.S. Pat. No. 8,440,055, each of which are hereby incorporated by reference). The preferred arrangement of the belt press has the web pressed against a permeable dewatering fabric across a vacuum roll by a permeable extended nip belt press. Inside the belt press is a hot air hood that includes a steam shower to enhance moisture removal. The hot air hood apparatus over the belt press can made more energy efficient by reusing a portion of heated exhaust air from the Yankee air cap or recirculating a portion of the exhaust air from the hot air apparatus itself (see U.S. Pat. No. 8,196,314, hereby incorporated by reference). In further embodiments of the drying system composed of the hot air apparatus and steam shower in the belt press section are described in U.S. Pat. Nos. 8,402,673, 8,435,384 and 8,544,184 (each of which are hereby incorporated by reference).


After the belt press is a second press to nip the web between the structured fabric and dewatering felt by one hard and one soft roll. The press roll under the dewatering fabric can be supplied with vacuum to further assist water removal. This preferred belt press arrangement is described in U.S. Pat. No. 8,382,956, and 8,580,083, each of which are hereby incorporated by reference, with FIG. 1 showing the arrangement. Rather than sending the web through a second press after the belt press, the web can travel through a boost dryer (FIG. 15 of U.S. Pat. No. 7,387,706 or 7,351,307, each of which are hereby incorporated by reference), a high pressure through air dryer (FIG. 16 of U.S. Pat. No. 7,387,706 or 7,351,307, each of which are hereby incorporated by reference), a two pass high pressure through air dryer (FIG. 17 of U.S. Pat. No. 7,387,706 or 7,351,307, each of which are hereby incorporated by reference) or a vacuum box with hot air supply hood (FIG. 2 of U.S. Pat. No. 7,476,293, hereby incorporated by reference). In addition, U.S. Pat. Nos. 7,510,631, 7,686,923, 7,931,781 8,075,739, and 8,092,652 (each of which are hereby incorporated by reference) further describe methods and systems for using a belt press and structured fabric to make tissue products each having variations in fabric designs, nip pressures, dwell times, etc. and are mentioned here for reference. A wire turning roll can be also be utilized with vacuum before the sheet is transferred to a steam heated cylinder via a pressure roll nip (see FIG. 2a of U.S. Pat. No. 7,476,293, hereby incorporated by reference).


The sheet is now transferred to a steam heated cylinder via a press element. The press element can be a through drilled (bored) pressure roll (FIG. 8 of U.S. Pat. No. 8,303,773, hereby incorporated by reference), a through drilled (bored) and blind drilled (blind bored) pressure roll (FIG. 9 of U.S. Pat. No. 8,303,773, hereby incorporated by reference), or a shoe press (see U.S. Pat. No. 7,905,989, hereby incorporated by reference). After the web leaves this press element to the steam heated cylinder, the % solids are in the range of 40-50% solids. The steam heated cylinder is coated with chemistry to aid in sticking the sheet to the cylinder at the press element nip and also aid in removal of the sheet at the doctor blade. The sheet is dried to up to 99% solids by the steam heated cylinder and installed hot air impingement hood over the cylinder. This drying process, the coating of the cylinder with chemistry, and the removal of the web with doctoring is explained in U.S. Pat. Nos. 7,582,187 and 7,905,989, each of which are hereby incorporated by reference. The doctoring of the sheet off the Yankee, creping, is similar to that of TAD with only the knuckle sections of the web being creped. Thus the dominant surface topography is generated by the structured fabric, with the creping process having a much smaller effect on overall softness as compared to conventional dry crepe.


The web is now optionally calendered, slit, and reeled in preparation for the converting process.


The ATMOS manufacturing technique is often described as a hybrid technology because it utilizes a structured fabric like the TAD process, but also utilizes energy efficient means to dewater the sheet like the Conventional Dry Crepe process. Other manufacturing techniques which employ the use of a structured fabric along with an energy efficient dewatering process are the ETAD process and NTT process. The ETAD process and products are described in U.S. Pat. Nos. 7,339,378, 7,442,278, and 7,494,563, each of which are hereby incorporated by reference. This process can utilize any type of former such as a Twin Wire Former or Crescent Former. After formation and initial drainage in the forming section, the web is transferred to a press fabric where it is conveyed across a suction vacuum roll for water removal, increasing web solids up to 25%. Then the web travels into a nip formed by a shoe press and backing/transfer roll for further water removal, increasing web solids up to 50%. At this nip, the web is transferred onto the transfer roll and then onto a structured fabric via a nip formed by the transfer roll and a creping roll. At this transfer point, speed differential can be utilized to facilitate fiber penetration into the structured fabric and build web caliper. The web then travels across a molding box to further enhance fiber penetration if needed. The web is then transferred to a Yankee dryer where is can be optionally dried with a hot air impingement hood, creped, calendared, and reeled. The NTT process and products are described in International Patent Application Publication No. WO 2009/061079 A1, hereby incorporated by reference. The process has several embodiments, but the key step is the pressing of the web in a nip formed between a structured fabric and press felt. The web contacting surface of the structured fabric is a non-woven material with a three dimensional structured surface comprised of elevation and depressions of a predetermined size and depth. As the web is passed through this nip, the web is formed into the depression of the structured fabric since the press fabric is flexible and will reach down into all of the depressions during the pressing process. When the felt reaches the bottom of the depression, hydraulic force is built up which forces water from the web and into the press felt. To limit compaction of the web, the press rolls will have a long nip width which can be accomplished if one of the rolls is a shoe press. After pressing, the web travels with the structured fabric to a nip with the Yankee dryer, where the sheet is optionally dried with a hot air impingement hood, creped, calendered, and reeled.


In embodiments, the fabric in the inner position of a former, such as the Crescent former, is a structured fabric. Structured fabrics can be manufactured using 3D printing techniques and materials that can be utilized with 3D printers. The structured fabric may comprise a cast or extruded polymer film with holes produced using a laser. The structured fabric may be a woven structure that utilizes monofilaments (yarns, threads) made of synthetic polymers (usually polyethylene, polypropylene, or nylon) that may be overlaid with a patterned polymer resin. The structured fabric may be produced using any of various processes for making a three-dimensional object primarily through additive processes in which successive layers of material are laid down under computer control. These processes are generally classified as 3-D printing technologies and include but are not limited to any of the following: Fused Deposition Modeling (FDM), PolyJet Technology, Selective Laser Melting (SLM), Direct Metal Laser Sintering (DMLS), Selective Laser Sintering (SLS), Stereolithography (SLA), or Laminated Object Manufacturing (LOM).


In Conventional Dry Crepe and Conventional Wet Crepe methods, a nascent web is formed in a forming structure, the web is transferred to a dewatering felt where it is pressed to remove moisture, and the web is then adhered to a Yankee Dryer. The web is then dried and creped from the Yankee Dryer and reeled. When creped at a solids content of less than 90%, the process is referred to as Conventional Wet Crepe. When creped at a solids content of greater than 90%, the process is referred to as Conventional Dry Crepe.


Additional processes for manufacturing wetlaid tissue can be found in U.S. Pat. No. 8,968,517, issued Mar. 3, 2015 and entitled “Soft Through Air Dried Tissue” and Ser. No. 14/561,802, filed Dec. 5, 2014, and entitled “Towel with Quality Wet Scrubbing Properties at Relatively Low Basis Weight and an Apparatus and Method for Producing Same.”


Single Ply Product


FIG. 2 is a block diagram of a system for manufacturing a single ply of a wipe, generally designated by reference number 100, according to an exemplary embodiment of the present invention. The system 100 includes a first exterior layer fan pump 102, a core layer fan pump 104, a second exterior layer fan pump 106, a headbox 108, a forming section 110, a drying section 112 and a calendar section 114. The headbox 108 is a stratified headbox (e.g., a triple layer headbox for a three layer ply, a double layer headbox for a two layer ply) to form multilayer plies. Alternatively, multiple headboxes may be provided, with a separate headbox corresponding to a separate layer of the multi-layer wipe. In embodiments, all three headbox layers may be formed using foam forming. In other embodiments, only the core layer is formed using foam forming. In another exemplary embodiment of the invention, long fibers may be incorporated via a regular water forming headbox separate from headbox 108.


The first and second exterior layer fan pumps 102, 106 deliver the furnish of the first and second external layers 2, 4 to the headbox 108, and the core layer fan pump 104 delivers the foamed furnish of the core layer 3 to the headbox 108. The foamed furnish includes a dispersion of fibers in a foamed liquid containing water and a surfactant. The foam forming surfactants could be anionic, cationic, non-ionic or amphoteric depending on their ability to generate a foamed dispersion. Some examples of anionic surfactants include sodium dodecyl sulfate (SDS), sodium alkyl ether sulphate (SAES) and alkyl ketene dimer (AKD) based labile surfactant. A typical example of ionic surfactants is alpha olefin sulfonate and some examples of non-ionic surfactants include alkyl glucosides and ethoxylated alcohols such as a peg-6 lauramide. The following steps are performed:


Deposition of Slurry from Headbox onto Forming Surface:


As is known in the art, the headbox delivers a wet web of pulp onto a forming wire, such as a Fourdrinier wire or a twin wire former, within the forming section 110. The wet web is delivered to the forming wire with the foamed core layer 3 disposed between the first and second external layers 2, 4. The laying down of the foamed core layer 3 results in a foam formed fibrous web disposed between the first and second external layers 2, 4. The foam forming may be accomplished in a single layer or multilayer headbox using surfactants injected into the thin stock loop and modified pumping systems specifically designed to handle entrained air.


Drainage of Slurry Across Forming Surface to Dewater the Nascent Web:


At least some dewatering may occur in the forming section 110. Water and surfactant removed from the foam formed core layer 3 during dewatering may be recycled.


Imprinting the Web Using a Structured Fabric and Pre-Drying the Web:


After formation in the forming section 110, the wet web may be imprinted with a structured fabric and, in embodiments, may be pre-dried.


Drying the Web Upon a Steam-Heated Cylinder:


Next, the web is transferred to the drying section 112. Within the drying the section 112, the wet web may be dewatered using an ATMOS system, such as a twin wire ATMOS system as described in U.S. Pat. No. 7,744,726, the disclosure of which is incorporated herein by reference in its entirety, or an NTT system, available from Valmet Corporation, of Espoo Finland. After dewatering, the dewatered web may be dried using a Yankee drying drum. Drying is completed using hot air impingement produced through TAD technology.


As noted in regards to an ATMOS drying process, the web is pressed against a dewatering fabric across a vacuum roll by an extended nip belt press. The vacuum roll applies negative pressure to a surface of the permeable dewatering fabric which is opposite to a surface of the permeable dewatering fabric which contacts the web, drawing moisture from the web through the dewatering fabric into the vacuum roll. The vacuum roll may have a diameter of between approximately 1000 mm and approximately 2500 mm. In addition, in embodiments, the permeable dewatering fabric comprises a felt with a batt layer. The fabric may have a caliper of between approximately 0.1 mm and approximately 15 mm, a permeability value of between approximately 1 cfm and approximately 500 cfm, an overall density of between approximately 0.2 g/cm3 and approximately 1.1 g/cm3 and a weight of between approximately 350 g/m2 and approximately 3000 g/m2. Also, in embodiments, an extended nip belt press comprises a permeable belt with a tension of between approximately 20 kN/m and approximately 100 kN/m, a permeability value of between approximately 100 cfm and approximately 1200 cfm, a surface contact area of the paper web side that is between approximately 0.5% and approximately 90% when not under tension, and an open area of between approximately 1.0% and approximately 85%. In embodiments, the extended nip of the belt press has an angle of wrap of between approximately 30 degrees and approximately 180 degrees, and, in embodiments, the extended nip has a nip length of between approximately 800 mm and approximately 2500 mm.


A hot air impingement hood may be installed inside of the belt press, and a steam shower may be installed inside the hot air impingement hood. Where the hood is used, a portion of exhaust air from an air cap installed over the steam heated cylinder is utilized as makeup air for the installed hood inside the belt press. Additionally, shoe presses may be installed inside the hot air impingement hood or may be installed inside of the belt press rather than a hot air impingement hood. Alternatively, a press roll may be installed inside of the belt press rather than installing shoe presses or a hot air impingement hood.


Creping the Web from the Steam-Heated Cylinder:


In an exemplary embodiment, a creping adhesive is applied to the drum prior to the dewatered web contacting the drum. After drying, a creping blade is used to remove the wipe from the Yankee drying drum, such as with a steel or ceramic doctor blade. The creping may be performed with or without a hot air impingement hood. At that point, the web has a solids content of approximately 15% to 1% solids.


Optionally Calendering the Web:


The wipe may then be calendered in a subsequent stage within the calender section 114. According to an exemplary embodiment, calendering may be accomplished using a number of calender rolls (not shown) that deliver a calendering pressure in the range of 0-100 pounds per linear inch (PLI). In general, increased calendering pressure is associated with reduced caliper and a smoother tissue surface.


Reeling the Web onto a Parent Roll and Unwinding the Web:


The formed web may be reeled on a parent roll, such as one of the parent rolls 208, 209 shown in FIG. 3. For a single ply wipe, the parent roll is unwound while a binder is applied to the roll.


To meet the “flushability” requirements of INDA and to reduce the events of pluggage within household sanitation systems as well as wastewater treatment facilities, nonwoven wipes can incorporate unique binders. The binders allow the wipe to be pre-moistened and retain its strength, but the binder will dissociate causing the nonwoven to lose its strength and disperse when flushed into a toilet. The binder may be used as an adhesive or as part of the adhesive to hold the multiple plies together before the wipe is disposed of.


Some examples of these binders are polymers that are insoluble in warm water, but are soluble in cold water, such as found in a toilet. An example of a nonwoven product incorporating this type of binder is shown in U.S. Pat. No. 5,509,913. Other types of binders are polymers that are ion sensitive. When a wipe is pre-moistened with a solution containing a high ion concentration the binder remains insolvent and the nonwoven retains its strength. When flushed into a toilet the containing soft water, the binder dissociates and the wipe can disperse. Other types of binders suitable for wipes that may be “flushable” by INDA standards are known, such as binders described in U.S. Pat. Nos. 5,281,306 and 7,157,389.


The binder may applied via roll coating such as with a roto-gravure or flexographic coating that is applied to the web. As another alternative, the application of the binder may be performed via spray coating or spin disc coating equipment. The binder may be applied in a particular pattern with surface coverage of the web ranging from 0 to 100%, and more preferably 50% surface coverage. The pattern may be a repeating pattern with each component of the pattern defining an open area free of binder. Exemplary patterns include polygonal-shaped patterns, such as diamond or triangular shaped patterns.


When pre-moistening the wipe, the binder contributes to retaining the integrity of the wipe prior to disposal. The particular binder that is used may be, for example, a polyethylene, vinyl acetate ethylene copolymers, vinyl-based or acrylic binders, or combinations thereof. Thus, possible binders may include a poly(vinyl) alcohol, poly(vinyl)acetate, poly (ethylene) (vinyl) alcohols, poly (ethylene) (vinyl)acetate, copolymers of vinyl acetate-ethylene, starch based chemistries or combinations thereof. The binder may also contain additional components such as a cross-linking agent including epoxy, amide and anhydride based chemistries, or ion sensitive polymers comprising acrylic acid, alkyl or aryl acrylates, terpolymers which comprise partially neutralized acrylic acid, butyl acrylate and 2-ethylhexyl acrylate. The binder also may comprise of additional trigger chemistries such as boric acid at concentrations ranging from 0.1 to 5% by weight, as well as additional trigger salt chemistries such as sodium chloride. The trigger chemistries, such as boric acid, can alternatively or also be included in the cleansing solution that is applied to the wipe 1.


After being applied, the binder may be cured at high temperatures in the range of 200 to 250° F. using methods such as infrared, UV, or other non-contact heating devices.


After that, the single ply wipe may be cut, folded and packaged with wetting, cleansing solution.


Multi-Ply Product

In another exemplary embodiment, a wipe according to the present invention may comprise two or more plies formed from two webs formed according to the process described with respect to FIG. 2 that are laminated together to create a multi-ply wipe. Each ply of a multi-ply wipe of the present invention may be made of the same type(s) of fibers or different fibers may be used in some or all of the plies. In a preferred embodiment, the plies have the same multi-layer tissue structure and composition.


Where the wipe is to be formed of two plies, the wipes are obtained by applying a binder between the two or more plies, embossing the plies, and then using a marrying roll following the embossment.



FIG. 3 shows an apparatus for manufacturing a laminate of two plies of a wipe that are joined to each other, in a face-to-face relationship, using an exemplary embodiment of the present invention. As shown in the figure, each of two webs 200, 201 of single ply web, which may be manufactured, for example, according to a method described above, is unwound and fed from each of parent rolls 208, 209 to respective pairs of mated pressure rolls 203, 205 and substantially axially parallel embossing rolls 204, 206. A first web 200 is thus fed through a nip 202a formed by pressure roll 203 and embossing roll 204 (also known as a pattern roll) and a second web 201 is likewise fed through a nip 202b between pressure roll 205 and embossing roll 206. The embossing rolls 204, 206, which rotate in the illustrated directions, impress an embossment pattern onto the webs as they pass through nip 202a and 202b. An exemplary embossment pattern for the wipe is shown in FIG. 4. After being embossed, each ply may have a plurality of embossments protruding outwardly from the plane of the ply towards the adjacent ply. The adjacent ply likewise may have opposing protuberances protruding towards the first ply. If a three ply product is produced by adding a third pair of mated pressure and embossing rolls, the central ply may have embossments extending outwardly in both directions.


To perform the embossments at nips 202a and 202b, the embossing rolls 204, 206, which may be hard or soft covered, have embossing tips or embossing knobs that extend radially outward from the rolls to make the embossments. In embodiments, the depth of the knobs may be between 25 to 1000 thousandths of an inch. In the illustrated embodiment, embossing is performed by nested embossing in which the crests of the embossing knobs on one embossing roll intermesh with the embossing knobs on the opposing embossing roll and a nip is formed between the embossing rolls. As the web is fed through nips 202a and 202b, a pattern is produced on the surface of the web by the interconnectivity of the knobs on an embossing roll with the open spaces of the respective pressure roll.


An adhesive applicator roll 212 is positioned upstream of the nip 213 formed between the two embossing rolls and is aligned in an axially parallel arrangement with one of the two embossing rolls to form a nip therewith. A binder is fed from a tank 207 via a conduit 210 to applicator roll 212. The applicator roll 212 transfers a binder to an interior side of embossed ply 200 to adhere the at least two plies 200, 201 together, wherein the interior side is the side of ply 200 that comes into a face-to-face relationship with ply 201 for lamination. The binder is applied to the ply at the crests of the embossing knobs 205 on embossing roll 204. The binder may alternatively or in addition applied via roll coating such as with a roto-gravure or flexographic coating that is applied to the one or two webs (or more webs, when present) before the webs are pressed together between the embossing rolls 204 or 206 to be plied. As another alternative to the use of an applicator roll 212 to apply the binder or in addition to that, the application of the binder may be performed via spray coating or spin disc coating equipment to the one or two webs before the webs are pressed together between the two embossing rolls. As described previously in regards to the single ply wipe, the binder may be applied in a particular pattern with surface coverage of the web ranging from 0 to 100%, and more preferably 50% surface coverage.


After being applied, the binder may be cured at high temperatures in the range of 200 to 250° F. using methods such as infrared, UV, or other non-contact heating devices.


The webs are then fed through the nip 213 where the embossing patterns on each embossing roll 204, 206 mesh with one another. After application of the embossments and the binder, a marrying roll 214 is used to apply pressure for lamination. The marrying roll 214 forms a nip with the same embossing roll 204 that forms the nip with the applicator roll 212, downstream of the nip formed between the two embossing rolls 204, 206. The marrying roll 214 is generally needed because, in nested embossing, the crests of the nested embossing knobs 205 typically do not touch the perimeter of the opposing roll 206 at the nip 213 formed therebetween.


The specific pattern that is embossed on the absorbent products can improve the adhesion properties of the plies. In an exemplary embodiment, the embossed area (or “bond area”) on any ply may cover between approximately 5 to 15% of the surface area of the ply. The size of each embossment may be between approximately 0.04 to 0.08 square centimeters. The depth of each embossment may be between 0.28 and 0.43 centimeters (0.110 and 0.170 inches) in depth.



FIG. 4 shows a sample pattern embossed on a wipe 250 according to an embodiment of the present invention. In the illustrated pattern, the embossed area covers approximately 13% of the surface, the embossment depth is approximately 0.34 centimeters (0.135 inches), and the embossment diameter is approximately 0.92 centimeters (0.115 inches).


The laminate is then cut, folded and packaged.


In exemplary embodiments, the following properties may be exhibited by flushable and dispersible multi-ply wet wipes made using a TAD process:


(1) Air Porosity: Below 40 cfm with a basis weight below 90 gsm;


(2) MD Tensile Strength: Between 30 N/m to 250 N/m, preferably between 50 N/m to 150 N/m;


(3) CD Tensile Strength: Between 30 N/m to 250 N/m, preferably between 50 N/m to 150 N/m;


(4) Caliper: Between 300 to 1500 microns, preferably between 400 to 1250 microns.


In exemplary embodiments, the following properties may be exhibited by single ply wipes and multi-ply flushable and dispersible wet wipes made using a UCTAD process:


(1) Air Porosity: Below 40 cfm;


(2) MD Tensile Strength: Between 30 N/m to 250 N/m, preferably between 75 N/m to 150 N/m;


(3) CD Tensile Strength: Between 30 N/m to 250 N/m, preferably between 75 N/m to 150 N/m;


(4) Caliper: Between 500 to 1500 microns, preferably between 750 to 1250 microns.


The following discussion describes the techniques that were used to determine the basis weights, fiber length, MD and CD stretch and tensile strength, caliper, and air porosity in connection with the present invention.


Basis Weight

The basis weight for the present invention was measured in grams/m2 using the following process. Using a dye and press, six approximately 76.2 mm by 76.2 mm (approximately 3 inch×3 inch) square samples were cut from each two-ply product that was tested with care being taken to avoid any web perforations in the sample. The samples were placed in an oven at 105 degrees Celsius for 5 minutes and were thereafter weighed on an analytical balance to the fourth decimal point. The weight of the sample in grams was then divided by (0.0762 m)2 to determine the basis weight in grams/m2.


Fiber Length Measurements

Fiber lengths and other fiber morphology of a pulp sample, such as coarseness, kink, and curl may be measured. The test uses a standard disintegrator capable of operating at 3,000 RPM, a Fiber Quality Analyzer, an oven as well as the standard supplies for consistency determination, a bucket and beaker set for dilution, and a desiccator with active desiccant crystals. (Ensure that the crystals are not saturated with moisture.)


To prepare the sample, determine the sample's consistency and weigh out the equivalent of 3 grams (o.d. basis). (If the sample is in dry sheet form, assume a 10% moisture content and tear 3.3 grams from the sheet. Do not use cut edges, and be careful to take the fill thickness of the sheet. Any dry samples must be soaked in water for no less than 4 hours, and as long as overnight.) Dilute the samples to 2 liters (2,000 ml) using water, and disintegrate in the standard disintegrator at 3,000 RPM for 1 minute.


If the sample is softwood, tare a clean bucket on the lab balance, add the disintegrated pulp and add water to make up the total sample weight to 8,000 grams. This will set the consistency at approximately 0.0375%. If the sample is hardwood, tare a clean bucket on the lab balance, but only add 1 liter (1,000 ml) of the disintegrated pulp. Again, add water to make up the total sample weight to 8,000 grams. This will set the consistency at approximately 0.0188%. If a coarseness measurement is not required, skip to dilution testing. If a coarseness measurement is required, a consistency determination is performed as follows.


Oven dry two filter papers and cool them in the desiccator for 2 minutes before weighing them. Label these as Consistency 1 and Consistency 2, and record their weights on the back of the filter paper. Mix the diluted sample thoroughly, in a FIG. 8 motion or an irregular motion. (Circular mixing will cause larger fibers to separate out towards the outer perimeter of the container.) With constant mixing, quickly withdraw two 1,000 gram samples, record their exact weights, and filter them on the two pre-weighted filter papers. (Note that very precise consistency is required. Take special care to rinse fibers from the sides of the funnel and the edges of the filter paper.)


Dry the consistency pads in a speed dryer for approximately five minutes, then transfer to an oven for 10 minutes at 105° C. Do not place additional wet material in the oven during this process. Cool the pads in the desiccator, and weigh to an accuracy of at least 3 decimal places. Repeat the drying/cooling/weighing procedure until a constant weight is achieved, and record those weights to an accuracy of 0.001. If the weights of Consistency 1 and Consistency 2 are not within ±0.001% of each other, repeat the consistency determination until they are. Average the two weights to obtain a final result.


To perform a dilution test, take 500 grams of the thoroughly mixed sample and dilute it to 1,000 grams with water. Record the precise weight. Calculate the actual concentrations using values of 0.0188 g/L for softwood, or 0.0094 g/L for hardwood. Take 100 grams of the diluted sample, and dilute that to 1,000 grams with water. Again, record the exact weights, and calculate the actual concentrations; this time, use values of 0.00188 g/L for softwood, or 0.00094 g/L for hardwood. The target weight for measurement is 1.25 mg for softwood, and 0.50 mg for hardwood. This should yield calculations of 0.00125/0.0188=66.49 g for softwood, and 0.0005/0.0094=53.19 g for hardwood. Thoroughly mix the sample, quickly pour it into a beaker, and record the pour weight, calculating the exact amount used.


Prepare duplicate samples for each test, and measure samples within two hours of dilution (as over time, the fibers may straighten out, or the microfibrils may detach from the fibers; either of these will change the fiber length distribution and coarseness values).


Stretch & MD, CD, and Wet CD Tensile Strength Testing

An Instron 3343 tensile tester, manufactured by Instron of Norwood, Mass., with a 100N load cell and 25.4 mm rubber coated jaw faces was used for tensile strength measurement. Prior to measurement, the Instron 3343 tensile tester was calibrated. After calibration, 8 strips of 2-ply product, each 2.54 cm by 10.16 cm (one inch by four inches), were provided as samples for each test. When testing MD (Material Direction) tensile strength, the strips are cut in the MD direction. When testing CD (Cross Direction) tensile strength, the strips are cut in the CD direction. One of the sample strips was placed in between the upper jaw faces and clamp, and then between the lower jaw faces and clamp with a gap of 5.08 cm (2 inches) between the clamps. A test was run on the sample strip to obtain tensile and stretch. The test procedure was repeated until all the samples were tested. The values obtained for the eight sample strips were averaged to determine the tensile strength of the tissue. When testing CD wet tensile strength, the strips are placed in an oven at 105 degrees Celsius for 5 minutes and saturated with 75 microliters of deionized water immediately prior to pulling the sample.


Caliper Testing

A Thwing-Albert ProGage 100 Thickness Tester, manufactured by Thwing Albert of West Berlin, N.J. was used for the caliper test. Eight 100 mm×100 mm square samples were cut from a 2-ply product. The samples were then tested individually and the results were averaged to obtain a caliper result for the base sheet.


Porosity (Air Permeability) Testing

For oven-drying: 5 sheets of each sample were placed in an oven at 105° C. and dried for 6 hours. The wipes were allowed to equilibrate at room conditions overnight before testing.


For washing and oven-drying: 5 sheets of each sample were rinsed thoroughly with 500 mL of room temperature deionized (DI) water, then placed in an oven at 105° C. and dried for 6 hours. The wipes were allowed to equilibrate at room conditions overnight before testing.


The equipment used was a Textest FX3300 Air Permeability Tester using ATSM procedure D737. All data was in cubic feet of air per minute (cfm).


The following Examples illustrate the advantages of the present invention.


Single Ply Examples
Example 1

Multiple hand sheets were produced using TAD/ATMOS technology. The samples were formed on a dynamic sheet former with basis weight ranging from 50 gsm to 70 gsm. The basesheet was produced with 70 to 100% softwood fibers and 0 to 30% tencel fibers. The tissue samples according to Example 1 were produced with addition of a temporary wet strength additive at a concentration of 0.01 to 0.5% range, Hercobond 1194 (Ashland, 500 Hercules Road, Wilmington Del., 19808) to the thick stock.


Example 2

Multiple hand sheets were produced using TAD/ATMOS technology. The samples were formed on a dynamic sheet former with basis weight ranging from 50 gsm to 70 gsm. The sample basesheets were produced with 70 to 100% softwood fibers, 0 to 30% tencel fibers and 0 to 20% hemp fibers. The tissue samples according to Example 2 were produced with addition of a temporary wet strength additive at a concentration of 0.1 to 0.5% range, Hercobond 1194 (Ashland, 500 Hercules Road, Wilmington Del., 19808) to the thick stock.


Example 3

Multiple hand sheets were produced using TAD/ATMOS technology. The samples were formed on a dynamic sheet former with basis weight ranging from 50 gsm to 70 gsm. The basesheet samples were produced with 70 to 100% softwood fibers and 0 to 30% tencel fibers. The tissue samples according to Example 3 were produced with addition of a temporary wet strength additive at a concentration of 0.1 to 0.5% range, Hercobond 1194 (Ashland, 500 Hercules Road, Wilmington Del., 19808) to the thick stock and carboxyl methyl cellulose (CMC) from Ashland Inc., at a concentration of 0 to 0.25% on the weight of fiber.


Example 4

Multiple hand sheets were produced using TAD/ATMOS technology. The samples were formed on a dynamic sheet former with basis weight ranging from 50 gsm to 70 gsm. The basesheet samples were produced with 70 to 100% softwood fibers, 0 to 30% tencel fibers and 0 to 20% hemp fibers. The tissue samples according to Example 4 were produced with addition of a temporary wet strength additive at a concentration of 0.1 to 0.5% range, Hercobond 1194 (Ashland, 500 Hercules Road, Wilmington Del., 19808) to the thick stock and carboxyl methyl cellulose (CMC) from Ashland Inc., at a concentration of 0 to 0.25% on the weight of fiber.


Comparative Example 1

Multiple hand sheets were produced using TAD/ATMOS technology. The samples were formed on a dynamic sheet former with basis weight ranging from 50 gsm to 70 gsm. The basesheet samples were produced with 70 to 100% softwood fibers and 0 to 30% tencel fibers.


Table 1 shows specifications and physical properties for Comparative Examples 1A-1D as compared to Examples 1A-1D.














TABLE 1







BW
Additive
Conc.
SW:Tencel






















Comparative
50
None
n/a
90/10



Example 1A



Comparative
60
None
n/a
90/10



Example 1B



Comparative
60
None
n/a
85/15



Example 1C



Comparative
60
None
n/a
80/20



Example 1D



Example 1A
50
GPAM
0.25
90/10



Example 1B
60
GPAM
0.25
90/10



Example 1C
60
GPAM
0.25
85/15



Example 1D
60
GPAM
0.25
80/20


















TABLE 2








Flushable


















Hydraspun
GP-
KC-





Test Parameter
Method
UOM
(Suominen)
AirSpun
Cottonelle
Ex. 2
Ex. 3
Ex. 4


















Basis Weight
WSP 130.1
g/m2
60
75
80
60
60
60


Thickness
WSP 120.1
mm
0.44
0.49
0.47
0.31
0.35
0.35


(Wet/Converted)










Tensile Strength
ERT 20.2-89
N/5 cm
8
5
10
4
4
5


MD (Wet)










Tensile Strength
ERT 20.2-89
N/5 cm
5
3
8
2
2
3


CD (Wet)









The results summarized in Table 2 suggest that the basesheet produced in accordance with the present invention has lower bulk than competitor products and matches close on the tensile strength with the airspun web made by Georgia Pacific even though the basis weight is lower than GP's Airspun product.


Comparative Example 2

Multiple hand sheets were produced using TAD/ATMOS technology. The samples were formed on a dynamic sheet former with basis weight ranging from 50 gsm to 70 gsm. The basesheet samples were produced with 70 to 100% softwood fibers, 0 to 30% tencel fibers and 0 to 20% hemp fibers. Table 3 compares Example 2 with Comparative Example 2, which is a commercial flushable wipe sold by Kimberly-Clark.
















TABLE 3










MD dry

Wet




%
%
GPAM
Strength,
MD wet
sheet


Cell
% SW
Hemp
Tencel
Spray, %
N/m
Strength
Stretch %






















Comparative
80
0
20
0
1252
149.5
17.4


Example 2









Example 2A
60
20
20
0
1705
56.9
5.5


Example 2B
60
20
20
0.25
2105
61.3
3.3



















TABLE 4






Wet Strength




Sample
Ball Burst Maximum Force
GSM
Bulk


















Cottonelle Kleenex K.C
1.275
75 gsm
463.6


Pull-ups Big Kid K.C.
1.4
75 gsm
450.3


Example 2B - un-creped
0.7
55 gsm
299.1


Example 2B - creped
0.9
55 gsm
308.8









The results summarized in Table 4 suggest that the basesheet produced in accordance with the present invention has lower bulk than competitor products and has lower wet ball burst strength than competitor products, making it easily flushable and dispersible compared to competitor products.


Multi-Ply Examples

The following three Examples were performed on two-ply samples formed in accordance with the present invention and on wipes available from other sources further illustrate advantages of the present invention. Test results for the examples are listed in Tables 5, 6 and 7 below.


Example 5

A flat pack of 2-ply pre-moistened wipes (30% solids) with dimensions of 5.25 inches by 7 inches were manufactured using the wet-laid TAD process and laminated using the DEKO emboss method with a vinyl acetate-ethylene copolymer binder. The resulting 2-ply product, as shown in Table 5, has the following product attributes: Basis Weight 85 g/m2, Caliper 0.625 mm, MD tensile of 75 N/m, CD tensile of 62 N/m, an MD stretch of 15.5%, and CD stretch of 8%.


The wipe web was formed on a wet laid TAD asset with a twin wire solid C-wrap former with a 3 layer headbox. The furnish to each outer layer was composed of 50% El Dorado Eucalyptus pulp, 40% Grand Prairie NBSK, and 10% 6 mm Lyocel. The NBSK and Lyocell were co-refined in a conical refiner imparting 80 kwh/ton. The center layer was composed of 80% Grand Prairie NBSK and 20% 6 mm Lyocell fiber co-refined in a conical refiner imparting 80 kwh/ton. Three kg/ton of a copolymer of glyoxal (DPD-589 from Solenis, 500 Hercules Road, Wilmington Del., 19808) was added to the co-refined NBSK and Lyocell at the discharge of the refiner. The fiber and chemicals mixtures were diluted to a solids of 0.5% consistency and fed to separate fan pumps which delivered the slurry to the triple layered headbox. The headbox pH was controlled to 7.0 by addition of a caustic to the thick stock before the fan pumps. The headbox deposited the slurry to a nip formed by a forming roll, an outer forming wire, and an inner fabric. The slurry was drained through the outer wire, which was a KT194-P design from Asten Johnson of Charleston, S.C., and transferred to a plain weave inner wire. The web was then transferred to a structured TAD fabric with a 10 shed weave, 0.35 mm warp and 0.50 mm shute monofilament, at 15% wire crepe. A single slotted vacuum box of 18 mm with 35 kPa of vacuum was used to facilitate transfer to the structured fabric upon which the web traveled over a four slotted, each at 19 mm molding box, with 80 kPa of vacuum. The web was dried using two through air drier drums to 90% solids before being transferred to a steam heated yankee dryer cylinder. The Yankee dryer had 18 mg/m2 of a PAE based adhesive applied as well as 45 mg/m2 of a polyvinyl alcohol and 3 mg/m2 of a release oil applied using a double overlap spraybar. The sheet was creped from the Yankee dryer using a 45 degree ceramic blade at 98% solids and reeled into parent rolls.


Two wipe parent roll webs were laminated together using embossing in the DEKO configuration (only the top sheet is embossed with binder applied to the inside of the top sheet at the high points derived from the embossments using a binder supplied by an applicator roll) with the second exterior layer of each web facing each other. The top sheet emboss roll was a flat roll with no embossments leading to 100 contact with the applicator roll. The binder used was a copolymer of vinyl acetate-ethylene dispersion purchased from Wacker of Munchen, Germany under the product name of VINNAPAS® EP907. The binder was diluted to 25% solids and mixed with boric acid at a concentration of 0.5% to prevent the binder from dissolution when saturated in a wetting solution. The laminated wipes were then cut to size and packaged in a wetting solution to a solids concentration of 30%. The wetting solution was 98% purified water, with the remainder a mixture of humectants, preservatives, moisturizers, surfactants, chelating agents, pH buffer, and aromatic compounds.


Example 6

A flat pack of 2-ply pre-moistened wipes (30% solids) with dimensions of 5.25 inches by 7 inches were manufactured using the wet-laid TAD process and laminated using the DEKO emboss method with a vinyl acetate-ethylene copolymer binder. The resulting 2-ply product, as shown in Table 5, has the following product attributes: Basis Weight 84 g/m2, Caliper 0.744 mm, MD tensile of 63 N/m, CD tensile of 55 N/m, an MD stretch of 13.4%, and CD stretch of 8.7%.


The wipe web was formed on a wet laid TAD asset with a twin wire solid C-wrap former with a 3 layer headbox. The furnish to each outer layer was composed of 50% El Dorado Eucalyptus pulp, 40% Grand Prairie NBSK, and 10% 6 mm Lyocel. The NBSK and Lyocell were co-refined in a conical refiner imparting 80 kwh/ton. The center layer was composed of 80% Grand Prairie NBSK and 20% 6 mm Lyocell fiber corefined in a conical refiner imparting 80 kwh/ton. Three kg/ton of glyoxalated polyacrylamide (Hercobond 1194 from Solenis of Wilmington, Del.) was added to the corefined NBSK and Lyocell at the discharge of the refiner). The fiber and chemicals mixtures were diluted to a solids of 0.5% consistency and fed to separate fan pumps which delivered the slurry to the triple layered headbox. The headbox pH was controlled to 7.0 by addition of a caustic to the thick stock before the fan pumps. The headbox deposited the slurry to a nip formed by a forming roll, an outer forming wire, and an inner fabric. The slurry was drained through the outer wire, which was a KT194-P design from Asten Johnson of Charleston, S.C., and transferred to a plain weave inner wire. The web was then transferred to a structured TAD fabric with a 10 shed weave, 0.35 mm warp and 0.50 mm shute monofilament, at 15% wire crepe. A single slotted vacuum box of 18 mm with 35 kPa of vacuum was used to facilitate transfer to the structured fabric upon which the web traveled over a four slotted, each at 19 mm molding box, with 80 kPa of vacuum. The web was dried using two through air drier drums to 90% solids before being transferred to a steam heated Yankee dryer cylinder. The Yankee dryer had 18 mg/m2 of a PAE based adhesive applied as well as 45 mg/m2 of a polyvinyl alcohol and 3 mg/m2 of a release oil applied using a double overlap spraybar. The sheet was creped from the Yankee dryer using a 45 degree ceramic blade at 98% solids and reeled into parent rolls.


Two wipe parent roll webs were laminated together using embossing using the DEKO configuration (only the top sheet is embossed with glue applied to the inside of the top sheet at the high points derived from the embossments using an adhesive supplied by an applicator roll) with the second exterior layer of each web facing each other. The top sheet emboss roll used a pattern with 12.6% coverage with round elements 0.115 inches diameter and 0.135 inches in depth as shown in FIG. 4. The binder used was a copolymer of vinyl acetate-ethylene dispersion purchased from Wacker of Munchen, Germany under the product name of VINNAPAS® EN1267. The binder was diluted to 12.5% solids and cured at 105° C. in a heated chamber for approximately 15 minutes to prevent the binder from dissolution when saturated in a wetting solution. The laminated wipes were then cut to size and packaged in a wetting solution to a solids concentration of 30%. The wetting solution was 97.5% purified water, with the remainder a mixture of humectants, preservatives, moisturizers, surfactants, chelating agents, pH buffer, and aromatic compounds


Example 7

A flat pack of 2-ply pre-moistened wipes (30% solids) with dimensions of 5.25 inches by 7 inches were manufactured using the wet-laid TAD process and laminated using the DEKO emboss method with a vinyl acetate-ethylene copolymer binder. The resulting 2-ply product, as shown in Table 5, has the following product attributes: Basis Weight 86 g/m2, Caliper 0.720 mm, MD tensile of 114 N/m, CD tensile of 105 N/m, an MD stretch of 16.0%, and CD stretch of 8.48%.


The wipe web was formed on a wet laid TAD asset with a twin wire solid C-wrap former with a 3 layer headbox. The furnish to each layer was composed of 80% Grand Prairie NBSK and 20% 4 mm Lyocell fiber co-refined imparting 80 kwh/ton. 6 kg/ton of glyoxalated polyacrylamide (Hercobond 1194 from Solenis of Wilmington Del.) was added to the co-refined NBSK and Lyocell at the discharge of the refiner). The fiber and chemicals mixtures were diluted to a solids of 0.5% consistency and fed to separate fan pumps which delivered the slurry to the triple layered headbox. The headbox pH was controlled to 7.0 by addition of a caustic to the thick stock before the fan pumps. The headbox deposited the slurry to a nip formed by a forming roll, an outer forming wire, and an inner fabric. The slurry was drained through the outer wire, which was a KT194-P design from Asten Johnson, and transferred to a plain weave inner wire. The web was then transferred to a structured TAD fabric with a 10 shed weave, 0.35 mm warp and 0.50 mm shute monofilament, at 15% wire crepe. A single slotted vacuum box of 18 mm with 35 kPa of vacuum was used to facilitate transfer to the structured fabric upon which the web traveled over a four slotted, each at 19 mm molding box, with 80 kPa of vacuum. The web was dried using two through air drier drums to 90% solids before being transferred to a steam heated Yankee dryer cylinder. The Yankee dryer had 18 mg/m2 of a PAE based adhesive applied as well as 45 mg/m2 of a polyvinyl alcohol and 3 mg/m2 of a release oil applied using a double overlap spraybar. The sheet was creped from the Yankee dryer using a 45 degree ceramic blade at 98% solids and reeled into parent rolls.


Two wipe parent roll webs were laminated together using embossing using the DEKO configuration (only the top sheet is embossed with glue applied to the inside of the top sheet at the high points derived from the embossments using an adhesive supplied by an applicator roll) with the second exterior layer of each web facing each other. The top sheet emboss roll used a pattern with 13% coverage with round elements 0.115 inches diameter and 0.135 inches in depth. The binder used was a copolymer of vinyl acetate-ethylene dispersion purchased from Wacker of Munchen, Germany under the product name of VINNAPAS® EN1267. The binder was diluted to 25% solids and cured at 105° C. in a heated chamber for approximately 15 minutes to prevent the binder from dissolution when saturated in a wetting solution. The laminated wipes were then cut to size and packaged in a wetting solution to a solids concentration of 30%. The wetting solution was 98% purified water, with the remainder a mixture of humectants, preservatives, moisturizers, surfactants, chelating agents, pH buffer, and aromatic compounds.


All of the wipes formed in accordance with the present invention and described in Examples 5 to 7 above passed the slosh box disintegration test described in INDA FG502. They also passed a dispersion test method in which a wipe was placed in a 1 liter container filled with 500 ml of room temperature tap water, and the container with the lid secured was shaken for 30 seconds. In both tests, the samples disintegrated as intended.


Table 5 show comparative test results for the products made in accordance with the present invention that were tested in Examples 5, 6 and 7, and for commercially available products identified in the Table. The test results are shown for dry basis weight (i.e., without a wetting solution), wet basis weight (i.e., after the addition of a wetting solution), wet bulk, and Dry and Wet MD and CD strength and stretch.


The tests confirm that the present invention is advantageous as it provides a wet wipe that is strong and stretchable when dry as the sample wipes had a relatively high Dry MD and




















TABLE 5






Dry
Wet



Wet
Wet







Basis
Basis
Wet
Dry MD
Dry MD
MD
MD
Dry CD
Dry CD
Wet CD
Wet CD



wt
wt
Bulk
Strength
Stretch
Strength
Stretch
Strength
Stretch
Strength
Stretch


Sample ID
(gsm)
(gsm)
(microns)
(N/m)
(%)
(N/m)
(%)
(N/m)
(%)
(N/m)
(%)


























Ex. 5
84.93
318.88
622.30
826.89
14.61
74.78
15.57
797.41
7.09
61.48
8.25


Ex. 6
83.75
306.80
744.10
647.33
11.35
63.27
13.37
629.67
6.55
55.25
8.72


Ex. 7
86.43
336.87
721.10
>1000
n/a
114.51
15.97
>1000
n/a
104.80
8.48


Dynarex
48.97
157.90
367.63
312.90
 8.66
112.47
21.07
168.58
23.62
56.19
38.71


July-Aug 2014













Cottonelle
78.61
237.19
408.73
>1000
n/a
127.60
14.03
522.34
12.98
62.79
19.73


FC-Jan 2015













Kirkland-Jan 2015
68.51
216.85
468.93
480.47
10.96
268.31
30.66
237.48
26.03
157.51
60.83









Table 6 shows air porosity test results for the for the products made in accordance with the present invention that were tested in Examples 5, 6 and 7 as compared to test results for the commercially available products identified in the Table.


The air porosity test results highlight an advantage of the present invention. A flushable wipe needs to behave like a conventional bath tissue in the sense that it should sink and keep moving through the pipes, rather than linger in a particular spot where fibers can accumulate and eventually cause a blockage. The relatively low porosity offered by product formed in accordance with the present invention thus prevents clogged pipes. By comparison, commercially-available products with long fiber lengths may be classified as flushable and dispersible, but because of their long fiber lengths which take time to break up and the high cfm (cubic feet of air per minute) porosity values, they can cause sewer blockages.

















TABLE 6







Costco
Walmart








Flush
Kirkland
Great Value








Away
Wipes
Wipes
Cottonelle regular
Cottonelle refill
Ex 5
Ex 6
Ex 7























Test 1
162.00
125.00
212.00
334.90
48.00
59.40
25.30
30.80


Test 2
160.00
146.00
187.00
326.00
47.90
57.80
25.90
30.90


Test 3
151.00
130.00
207.00
315.00
40.40
29.30
25.50
31.80


Test 4
144.00
126.00
206.00
307.00
39.80
55.30
24.20
30.50


Test 5
156.00
144.00
210.00
346.00
42.80
56.40
26.30
31.50


Test 6
158.00
125.00
183.00
347.00
43.40
55.70
26.50
30.70


average (cfm)
155.17
132.67
200.83
329.32
43.72
52.32
25.62
31.03


stdev
6.65
9.75
12.51
16.35
3.55
11.38
0.83
0.50









Table 7 shows the length weight weighted (LWW) average fiber length fiber for the products made in accordance with the present invention that were tested in Examples 5, 6 and 7 and for commercially available products. These measurements were made using the Fiber Quality Analyzer, as described in the Fiber Lengths Measurements test described above. The manufacturing processes described above are simplified by using materials with relatively short fiber length (as shown in Table 7) for the wet-laid process so that a stratified headbox can be used. Also, the relatively short fiber lengths avoid clogging and improve dispersability as compared to conventional flushable wipes.

















TABLE 7








Walmart









Costco
Great








Flush
Kirkland
Value
Cottonelle
Cottonelle





Sample
Away
Wipes
wipes
regular
refill
Ex. 5
Ex. 6
Ex. 7







LWW
>10 mm
>10 mm
>10 mm
>10 mm
>10 mm
3.9 mm
3.6 mm
3.6 mm


(mm)









While particular embodiments of the invention have been illustrated and described, it would be obvious to those skilled in the art that various other changes and modifications may be made without departing from the spirit and scope of the invention. It is therefore intended to cover in the appended claims all such changes and modifications that are within the scope of this invention.

Claims
  • 1. A multi-ply flushable wet wipe comprising: two plies each comprising a tissue sheet made by a through air drying papermaking process, at least one of the two plies comprising: first and second exterior layers each comprising at least 50% by weight natural fibers; anda foam-formed middle layer disposed between the first and second exterior layers and comprising synthetic fibers and at least 25% by weight natural fibers, the synthetic fibers having a length within the range of 1 mm and 20 mm; andcleansing solution in an amount of 40% to 90% by weight of the wipe,wherein a binder is applied in a pattern on a surface of only one of the two plies,the multi-ply flushable wet wipe having a thickness of 400 microns to 744 microns,the wipe has a cross direction wet strength greater than 20 N/m, andthe wet wipe is dispersible as determined by the Slosh Box Disintegration Test set forth in INDA FG502.
  • 2. The multi-ply flushable wet wipe of claim 1, wherein at least one of the first and second exterior layers are foam formed.
  • 3. The multi-ply flushable wet wipe of claim 1, wherein the synthetic fibers are non-thermoplastic.
  • 4. The multi-ply flushable wet wipe of claim 1, wherein an average fiber length of all fibers of the multi-ply flushable wipe is less than 5 mm.
  • 5. The multi-ply flushable wet wipe of claim 1, wherein the natural fibers comprise fibers of the type selected from the group consisting of: softwood fibers, hardwood fibers, elephant grass, nettle, buntal, buri, soybean protein, milvet milk, abaca, bagasse, bamboo, coir, cotton, flax, linen, hemp, jute, kapok, kenaf, pina, raffia, ramie, sisal, oxidized natural fibers and combinations thereof.
  • 6. The multi-ply flushable wet wipe of claim 1, wherein the synthetic fibers comprise fibers of the type selected from the group consisting of: acrylic, aramid, para-aramid, meta-aramid, modacrylic, nylon, olefin, polyester, polyethylene, ultra-high molecular weight polyethylene, polyester-polyurethane copolymer, polyvinyl alcohol, polyvinyl chloride, poly(p -phenylene-2,6-benzobisoxazole), polypropylene, ethylene vinyl alcohol and combinations thereof.
  • 7. The multi-ply flushable wet wipe of claim 1, wherein the synthetic fibers comprise semisynthetic fibers of the type selected from the group consisting of: regenerated cellulose, rayon, lyocell, polylactic acid, polyvinyl alcohol and combinations thereof.
  • 8. The multi-ply flushable wet wipe of claim 1, wherein the multi-ply flushable wet wipe has a porosity below 40 cfm.
  • 9. The multi-ply flushable wet wipe of claim 8, wherein the multi-ply flushable wet wipe has a basis weight below 90 gsm.
  • 10. The multi-ply flushable wet wipe of claim 1, wherein the multi-ply flushable wet wipe has a machine direction tensile strength within the range of 30 N/m to 250 N/m.
  • 11. The multi-ply flushable wet wipe of claim 1, wherein the multi-ply flushable wet wipe has a machine direction tensile strength within the range of 50 N/m to 150 N/m.
  • 12. The multi-ply flushable wet wipe of claim 1, wherein the multi-ply flushable wet wipe has a cross direction tensile strength within the range of 30 N/m to 250 N/m.
  • 13. The multi-ply flushable wet wipe of claim 1, wherein the multi-ply flushable wet wipe has a cross direction tensile strength within the range of 50 N/m to 150 N/m.
  • 14. The multi-ply flushable wet wipe of claim 1, wherein the at least one ply comprises a combination of softwood fibers and fibers of the type selected from the group consisting of: abaca, bamboo, coir, flax, linen, kapok, pina, raffia, ramie, sisal, nettle, buntal, buri, cotton, kenaf, elephant grass, jute, hemp, bagasse fibers and combinations thereof.
  • 15. The multi-ply flushable wet wipe of claim 1, wherein the at least one ply comprises a combination of softwood fibers and modified rayon fibers.
  • 16. The multi-ply flushable wet wipe of claim 1, wherein the at least one ply comprises a combination of softwood fibers and renewable polymeric fibers.
  • 17. The multi-ply flushable wet wipe of claim 1, wherein the at least one ply comprises a combination of softwood fibers and water-based polyvinyl alcohol (PVA) fibers.
  • 18. The multi-ply flushable wet wipe of claim 1, wherein the at least one ply comprises a combination of softwood fibers, renewable polymeric fibers and polyvinyl alcohol (PVA) fibers.
  • 19. The multi-ply flushable wet wipe of claim 1, wherein the at least one ply comprises a combination of softwood fibers, modified rayon fibers, renewable polymeric fibers, water-based polyvinyl alcohol (PVA) fibers and fibers of the type selected from the group consisting of: abaca, bamboo, coir, flax, linen, kapok, pina, raffia, ramie, sisal, nettle, buntal, buri, cotton, kenaf, elephant grass, jute, hemp, bagasse fibers and combinations thereof.
  • 20. The multi-ply flushable wet wipe of claim 1, wherein the at least one ply comprises modified rayon fibers at an inclusion rate within the range of 10% to 50% by weight of fibers in the ply.
  • 21. The multi-ply flushable wet wipe of claim 20, wherein the modified rayon fibers are shaped fibers having tri-lobal or star-shaped cross-sections.
  • 22. The multi-ply flushable wet wipe of claim 20, wherein the modified rayon fibers are viscose rayon fibers.
  • 23. The multi-ply flushable wet wipe of claim 20, wherein the viscose rayon fibers are lyocell fibers.
  • 24. The multi-ply flushable wet wipe of claim 1, wherein the at least one ply comprises water-based polyvinyl alcohol (PVA) fibers at an inclusion rate of 10% to 50% by weight.
  • 25. The multi-ply flushable wet wipe of claim 24, wherein the water-based polyvinyl alcohol (PVA) fibers are shaped fibers having tri-lobal or star-shaped cross-sections.
  • 26. The multi-ply flushable wet wipe of claim 1, wherein the at least one ply comprises polylactic acid (PLA) fibers at an inclusion rate of 1% to 25% by weight.
  • 27. The multi-ply flushable wet wipe of claim 26, wherein the polylactic acid (PLA) fibers are shaped fibers having tri-lobal or star-shaped cross-sections.
  • 28. The multi-ply flushable wet wipe of claim 1, wherein the at least one ply comprises alternate natural fibers comprising fibers of the type selected from the group consisting of: abaca, bamboo, coir, flax, linen, kapok, pina, raffia, ramie, sisal, nettle, buntal, buri, cotton, kenaf, elephant grass, jute, hemp, bagasse fibers and combinations thereof.
  • 29. The multi-ply flushable wet wipe of claim 1, wherein a slurry from which the multi-ply flushable wipe is formed comprises additives.
  • 30. The multi-ply flushable wet wipe of claim 29, wherein the additives comprise additives of the type selected from the group consisting of: urea formaldehyde, melamine formaldehyde, poly amide poly amine epichlorohydrin, polyethlyenimine, starch, starch derivatives, aldehyde functionalized starches, chitosan, aldehyde functionalize polyacrylamides, glyoxalated polyacrylamide, glyoxalated copolymer, carboxyl methyl cellulose, polyvinyl alcohol, polyvinyl acetate, polyvinyl amine, polyamide resins, polyacrylamide resins, galactomannan gums, acrylic emulsions, styrene-butadiene latexes, vinyl acetate polymers, ethylene-vinyl acetate copolymers, vinyl chloride polymers, vinylidene chloride polymers, vinyl chloride-vinylidene copolymers, acrylo-nitrile copolymers, ethylene-acrylic copolymers, latex emulsions, acrolein copolymers and combinations thereof.
  • 31. The multi-ply flushable wet wipe of claim 1, further comprising one or more fillers.
  • 32. The multi-ply flushable wet wipe of claim 31, wherein the one or more fillers comprise at least one of calcium carbonate particles, clay particles or talc particles.
  • 33. The multi-ply flushable wet wipe of claim 1, wherein the cleansing solution comprises a glycol based cross-linking agent.
  • 34. The multi-ply flushable wet wipe of claim 1, wherein the cleansing solution comprises anhydrides and epoxy groups.
  • 35. The multi-ply flushable wet wipe of claim 1, wherein the cleansing solution comprises cyclo-dextrins adapted to release fragrances.
  • 36. The multi-ply flushable wet wipe of claim 1, wherein the cleansing solution comprises at least one of aloe or shea butter.
  • 37. The multi-ply flushable wet wipe of claim 1, wherein the cleansing solution is present in the amount of 40% to 80% by weight.
  • 38. The multi-ply flushable wet wipe of claim 1, wherein the multi-ply flushable wet wipe has a basis weight within the range of 20 gsm to 100 gsm.
  • 39. The multi-ply flushable wet wipe of claim 1, further comprising filler material.
  • 40. The multi-ply flushable wet wipe of claim 39, wherein the filler material comprises at least one of super absorbent polymers and encapsulated polymers.
  • 41. The multi-ply flushable wet wipe of claim 1, wherein the binder is disposed between the two plies.
  • 42. The multi-ply flushable wet wipe of claim 41, wherein the binder comprises a binder of a type selected from the group consisting of: polyvinyl alcohol, polyvinyl acetate, poly ethylene vinyl alcohols, poly ethylene vinyl acetate, copolymers of vinyl acetate-ethylene, starch based chemistries and combinations thereof.
  • 43. The multi-ply flushable wet wipe of claim 42, wherein the binder further comprises a cross-linking agent.
  • 44. The multi-ply flushable wet wipe of claim 42, wherein the binder further comprises ion sensitive polymers.
  • 45. The multi-ply flushable wet wipe of claim 42, wherein the binder further comprises a trigger component.
  • 46. The multi-ply flushable wet wipe of claim 45, wherein the trigger component comprises boric acid.
  • 47. The multi-ply flushable wet wipe of claim 45, wherein the trigger component comprises a trigger salt component.
  • 48. The multi-ply flushable wet wipe of claim 47, wherein the trigger salt component comprises sodium chloride.
  • 49. The multi-ply flushable wet wipe of claim 1, further comprising a wetting/cleaning solution comprising purified water and a combination of one or more of the following: humectants, preservatives, moisturizers, surfactants, chelating agents, pH buffer and aromatic compounds.
  • 50. The multi-ply flushable wet wipe of claim 1, wherein the two plies are held together by embossments.
  • 51. The multi-ply flushable wet wipe of claim 1, further comprising a third ply substantially identical in structure to the at least one ply.
  • 52. A multi-ply flushable wet wipe comprising: two plies each comprising a tissue sheet made by a through air drying papermaking process, at least one of the two plies comprising: first and second exterior layers each comprising at least 50% by weight natural fibers; anda middle layer disposed between the first and second exterior layers and comprising synthetic fibers and at least 75% by weight natural fibers, the synthetic fibers having a length within the range of 1 mm and 20 mm and an average fiber length (LWW) less than about 4 mm; andcleansing solution in an amount of 40% to 90% by weight of the wet wipe,wherein the wet wipe has a cross direction wet strength greater than 20 N/m and the wet wipe is dispersible as determined by the Slosh Box Disintegration Test set forth in IVDA FG502;a binder is applied in a pattern on a surface of only one of the two plies, andthe multi-ply flushable wet wipe has a thickness of 400 microns to 744 microns.
  • 53. The multi-ply flushable wet wipe of claim 52, wherein at least one of the two plies comprises greater than 80 wt % pulp fibers.
  • 54. The multi-ply flushable wet wipe of claim 52, wherein the multi-ply flushable wet wipe has a porosity below 40 cfm.
  • 55. The multi-ply flushable wet wipe of claim 52, wherein the multi-ply flushable wet wipe has a basis weight below 90 gsm.
  • 56. The multi-ply flushable wet wipe of claim 52, wherein the multi-ply flushable wet wipe has a machine direction tensile strength within the range of 30 N/m to 250 N/m.
  • 57. The multi-ply flushable wet wipe of claim 52, wherein the multi-ply flushable wet wipe has a machine direction tensile strength within the range of 50 N/m to 150 N/m.
  • 58. The multi-ply flushable wet wipe of claim 1, wherein the binder covers 5% to 15% of the surface area of the only one of the two plies.
  • 59. The multi-ply flushable wet wipe of claim 1, wherein the only one of the two plies comprises embossments.
  • 60. The multi-ply flushable wet wipe of claim 59, wherein the binder is applied to high points of the embossments.
CROSS-REFERENCE TO RELATED APPLICATION

This application claims the benefit of U.S. provisional application Ser. No. 61/994,563 filed May 16, 2014, and entitled “WIPE AND METHOD OF FORMING THE SAME,” which is incorporated by reference herein.

US Referenced Citations (453)
Number Name Date Kind
2919467 Mercer Jan 1960 A
2926154 Keim Feb 1960 A
3026231 Chavannes Mar 1962 A
3049469 Davison Aug 1962 A
3058873 Keim et al. Oct 1962 A
3066066 Keim et al. Nov 1962 A
3097994 Dickens et al. Jul 1963 A
3125552 Loshaek et al. Mar 1964 A
3143150 Buchanan Aug 1964 A
3186900 Young Jun 1965 A
3197427 Schmalz Jul 1965 A
3224986 Butler et al. Dec 1965 A
3224990 Babcock Dec 1965 A
3227615 Korden Jan 1966 A
3227671 Keim Jan 1966 A
3239491 Tsou et al. Mar 1966 A
3240664 Earle, Jr. Mar 1966 A
3240761 Keim et al. Mar 1966 A
3248280 Hyland, Jr. Apr 1966 A
3250664 Conte et al. May 1966 A
3252181 Hureau May 1966 A
3301746 Sanford et al. Jan 1967 A
3311594 Earle, Jr. Mar 1967 A
3329657 Strazdins et al. Jul 1967 A
3332834 Reynolds, Jr. Jul 1967 A
3332901 Keim Jul 1967 A
3352833 Earle, Jr. Nov 1967 A
3384692 Galt et al. May 1968 A
3414459 Wells Dec 1968 A
3442754 Espy May 1969 A
3459697 Goldberg et al. Aug 1969 A
3473576 Amneus Oct 1969 A
3483077 Aldrich Dec 1969 A
3545165 Greenwell Dec 1970 A
3556932 Coscia et al. Jan 1971 A
3573164 Friedberg et al. Mar 1971 A
3609126 Asao et al. Sep 1971 A
3666609 Kalwaites et al. May 1972 A
3672949 Brown Jun 1972 A
3672950 Murphy et al. Jun 1972 A
3773290 Mowery Nov 1973 A
3778339 Williams et al. Dec 1973 A
3813362 Coscia et al. May 1974 A
3855158 Petrovich et al. Dec 1974 A
3877510 Tegtmeier et al. Apr 1975 A
3905863 Ayers Sep 1975 A
3911173 Sprague, Jr. Oct 1975 A
3974025 Ayers Aug 1976 A
3994771 Morgan, Jr. Nov 1976 A
3998690 Lyness et al. Dec 1976 A
4038008 Larsen Jul 1977 A
4075382 Chapman et al. Feb 1978 A
4088528 Berger et al. May 1978 A
4098632 Sprague, Jr. Jul 1978 A
4102737 Morton Jul 1978 A
4117187 Adams et al. Sep 1978 A
4129528 Petrovich et al. Dec 1978 A
4147586 Petrovich et al. Apr 1979 A
4161195 Khan Jul 1979 A
4184519 McDonald et al. Jan 1980 A
4190692 Larsen Feb 1980 A
4191609 Trokhan Mar 1980 A
4252761 Schoggen et al. Feb 1981 A
4320162 Schulz Mar 1982 A
4331510 Wells May 1982 A
4382987 Smart May 1983 A
4440597 Wells et al. Apr 1984 A
4501862 Keim Feb 1985 A
4507351 Johnson et al. Mar 1985 A
4514345 Johnson et al. Apr 1985 A
4515657 Maslanka May 1985 A
4528239 Trokhan Jul 1985 A
4529480 Trokhan Jul 1985 A
4537657 Keim Aug 1985 A
4545857 Wells Oct 1985 A
4637859 Trokhan Jan 1987 A
4678590 Nakamura et al. Jul 1987 A
4714736 Juhl et al. Dec 1987 A
4770920 Larsonneur Sep 1988 A
4780357 Akao Oct 1988 A
4808467 Suskind et al. Feb 1989 A
4836894 Chance et al. Jun 1989 A
4849054 Klowak Jul 1989 A
4885202 Lloyd et al. Dec 1989 A
4891249 McIntyre Jan 1990 A
4909284 Kositake Mar 1990 A
4949668 Heindel et al. Aug 1990 A
4949688 Bayless Aug 1990 A
4983256 Combette et al. Jan 1991 A
4996091 McIntyre Feb 1991 A
5059282 Ampulski et al. Oct 1991 A
5143776 Givens Sep 1992 A
5149401 Langevin et al. Sep 1992 A
5152874 Keller Oct 1992 A
5211813 Sawley et al. May 1993 A
5239047 Devore et al. Aug 1993 A
5279098 Fukuda Jan 1994 A
5281306 Kakiuchi et al. Jan 1994 A
5334289 Trokhan et al. Aug 1994 A
5347795 Fukuda Sep 1994 A
5397435 Ostendorf et al. Mar 1995 A
5399412 Sudall et al. Mar 1995 A
5405501 Phan et al. Apr 1995 A
5409572 Kershaw Apr 1995 A
5429686 Chiu et al. Jul 1995 A
5439559 Crouse Aug 1995 A
5447012 Kovacs et al. Sep 1995 A
5470436 Wagle et al. Nov 1995 A
5487313 Johnson Jan 1996 A
5509913 Yeo Apr 1996 A
5510002 Hermans et al. Apr 1996 A
5529665 Kaun Jun 1996 A
5581906 Ensign et al. Dec 1996 A
5591147 Couture-Dorschner et al. Jan 1997 A
5607551 Farrington, Jr. et al. Mar 1997 A
5611890 Vinson et al. Mar 1997 A
5628876 Ayers et al. May 1997 A
5635028 Vinson et al. Jun 1997 A
5649916 Dipalma et al. Jul 1997 A
5671897 Ogg et al. Sep 1997 A
5672248 Wendt et al. Sep 1997 A
5679222 Rasch et al. Oct 1997 A
5685428 Herbers et al. Nov 1997 A
5728268 Weisman et al. Mar 1998 A
5746887 Wendt et al. May 1998 A
5753067 Fukuda et al. May 1998 A
5772845 Farrington, Jr. et al. Jun 1998 A
5806569 Gulya et al. Sep 1998 A
5827384 Canfield et al. Oct 1998 A
5832962 Kaufman et al. Nov 1998 A
5846380 Van Phan et al. Dec 1998 A
5855738 Weisman et al. Jan 1999 A
5858554 Neal et al. Jan 1999 A
5865396 Ogg et al. Feb 1999 A
5865950 Vinson et al. Feb 1999 A
5893965 Trokhan et al. Apr 1999 A
5913765 Burgess et al. Jun 1999 A
5942085 Neal et al. Aug 1999 A
5944954 Vinson et al. Aug 1999 A
5948210 Huston Sep 1999 A
5980691 Weisman et al. Nov 1999 A
6036139 Ogg Mar 2000 A
6039838 Kaufman et al. Mar 2000 A
6048938 Neal et al. Apr 2000 A
6060149 Nissing et al. May 2000 A
6106670 Weisman et al. Aug 2000 A
6149769 Mohammadi et al. Nov 2000 A
6162327 Balia et al. Dec 2000 A
6162329 Vinson et al. Dec 2000 A
6187138 Neal et al. Feb 2001 B1
6200419 Phan Mar 2001 B1
6203667 Huhtelin Mar 2001 B1
6207734 Vinson et al. Mar 2001 B1
6231723 Kanitz et al. May 2001 B1
6287426 Edwards et al. Sep 2001 B1
6303233 Amon et al. Oct 2001 B1
6319362 Huhtelin et al. Nov 2001 B1
6328850 Phan Dec 2001 B1
6344111 Wilhelm Feb 2002 B1
6420013 Vinson et al. Jul 2002 B1
6420100 Trokhan et al. Jul 2002 B1
6423184 Vahatalo et al. Jul 2002 B2
6458246 Kanitz et al. Oct 2002 B1
6464831 Trokhan et al. Oct 2002 B1
6473670 Huhtelin Oct 2002 B1
6521089 Griech et al. Feb 2003 B1
6537407 Law et al. Mar 2003 B1
6547928 Barnholtz et al. Apr 2003 B2
6551453 Weisman et al. Apr 2003 B2
6551691 Hoeft et al. Apr 2003 B1
6572722 Pratt Jun 2003 B1
6579416 Vinson et al. Jun 2003 B1
6602454 McGuire et al. Aug 2003 B2
6607637 Vinson et al. Aug 2003 B1
6610173 Lindsay et al. Aug 2003 B1
6613194 Kanitz et al. Sep 2003 B2
6660362 Lindsay et al. Dec 2003 B1
6673202 Burazin et al. Jan 2004 B2
6701637 Lindsay et al. Mar 2004 B2
6755939 Vinson et al. Jun 2004 B2
6773647 McGuire et al. Aug 2004 B2
6797114 Hu Sep 2004 B2
6797117 McKay et al. Sep 2004 B1
6808599 Burazin et al. Oct 2004 B2
6821386 Weisman et al. Nov 2004 B2
6821391 Scherb et al. Nov 2004 B2
6827818 Farrington, Jr. et al. Dec 2004 B2
6863777 Kanitz et al. Mar 2005 B2
6896767 Wilhelm May 2005 B2
6939443 Ryan et al. Sep 2005 B2
6998017 Lindsay et al. Feb 2006 B2
6998024 Burazin et al. Feb 2006 B2
7005043 Toney et al. Feb 2006 B2
7014735 Kramer et al. Mar 2006 B2
7105465 Patel et al. Sep 2006 B2
7155876 VanderTuin et al. Jan 2007 B2
7157389 Branham et al. Jan 2007 B2
7182837 Chen et al. Feb 2007 B2
7194788 Clark et al. Mar 2007 B2
7235156 Baggot Jun 2007 B2
7269929 VanderTuin et al. Sep 2007 B2
7294230 Flugge-Berendes et al. Nov 2007 B2
7311853 Vinson et al. Dec 2007 B2
7328550 Floding et al. Feb 2008 B2
7339378 Han et al. Mar 2008 B2
7351307 Scherb et al. Apr 2008 B2
7387706 Herman et al. Jun 2008 B2
7399378 Edwards et al. Jul 2008 B2
7419569 Hermans et al. Sep 2008 B2
7427434 Busam et al. Sep 2008 B2
7431801 Conn et al. Oct 2008 B2
7432309 Vinson Oct 2008 B2
7442278 Murray et al. Oct 2008 B2
7452447 Duan et al. Nov 2008 B2
7476293 Herman et al. Jan 2009 B2
7484276 Jeambar Feb 2009 B2
7494563 Edwards et al. Feb 2009 B2
7510631 Scherb et al. Mar 2009 B2
7513975 Burma Apr 2009 B2
7563344 Beuther et al. Jul 2009 B2
7582187 Scherb et al. Sep 2009 B2
7611607 Mullally et al. Nov 2009 B2
7622020 Awofeso et al. Nov 2009 B2
7662462 Noda et al. Feb 2010 B2
7670678 Phan Mar 2010 B2
7683126 Neal et al. Mar 2010 B2
7686923 Scherb et al. Mar 2010 B2
7687140 Manifold et al. Mar 2010 B2
7691230 Scherb et al. Apr 2010 B2
7732357 Annis Jun 2010 B2
7744722 Tucker et al. Jun 2010 B1
7744726 Scherb et al. Jun 2010 B2
7799382 Payne et al. Sep 2010 B2
7811418 Klerelid et al. Oct 2010 B2
7815978 Davenport et al. Oct 2010 B2
7823366 Schoeneck Nov 2010 B2
7842163 Nickel et al. Nov 2010 B2
7867361 Salaam et al. Jan 2011 B2
7871692 Morin et al. Jan 2011 B2
7887673 Andersson et al. Feb 2011 B2
7905989 Scherb et al. Mar 2011 B2
7914866 Shannon et al. Mar 2011 B2
7931781 Scherb et al. Apr 2011 B2
7951269 Herman et al. May 2011 B2
7955549 Noda et al. Jun 2011 B2
7959764 Ringer et al. Jun 2011 B2
7972475 Chan et al. Jul 2011 B2
7989058 Manifold et al. Aug 2011 B2
8034463 Leimbach et al. Oct 2011 B2
8051629 Pazdemik et al. Nov 2011 B2
8075739 Scherb et al. Dec 2011 B2
8092652 Scherb et al. Jan 2012 B2
8118979 Herman et al. Feb 2012 B2
8147649 Tucker et al. Apr 2012 B1
8152959 Elony et al. Apr 2012 B2
8196314 Munch Jun 2012 B2
8216427 Klerelid et al. Jul 2012 B2
8236135 Prodoehl et al. Aug 2012 B2
8303773 Scherb et al. Nov 2012 B2
8382956 Boechat et al. Feb 2013 B2
8402673 Da Silva et al. Mar 2013 B2
8409404 Harper et al. Apr 2013 B2
8435384 Da Silva et al. May 2013 B2
8440055 Scherb et al. May 2013 B2
8445032 Topolkaraev et al. May 2013 B2
8454800 Mourad et al. Jun 2013 B2
8470133 Cunnane et al. Jun 2013 B2
8506756 Denis et al. Aug 2013 B2
8544184 Da Silva et al. Oct 2013 B2
8574211 Morita et al. Nov 2013 B2
8580083 Boechat et al. Nov 2013 B2
8728277 Boechat et al. May 2014 B2
8758569 Aberg et al. Jun 2014 B2
8771466 Denis et al. Jul 2014 B2
8801903 Mourad et al. Aug 2014 B2
8815057 Eberhardt et al. Aug 2014 B2
8822009 Riviere et al. Sep 2014 B2
8968517 Ramaralnam et al. Mar 2015 B2
8980062 Karlsson et al. Mar 2015 B2
9005710 Jones et al. Apr 2015 B2
D734617 Seitzinger et al. Jul 2015 S
9095477 Yamaguchi et al. Aug 2015 B2
D738633 Seitzinger et al. Sep 2015 S
9382666 Ramaralnam et al. Jul 2016 B2
9506203 Ramaratnam et al. Nov 2016 B2
9580872 Ramaratnam et al. Feb 2017 B2
9702089 Ramaratnam et al. Jul 2017 B2
9702090 Ramaratnam et al. Jul 2017 B2
9719213 Miller, IV et al. Aug 2017 B2
9725853 Ramaratnam et al. Aug 2017 B2
20010018068 Lorenzi et al. Aug 2001 A1
20020028230 Eichhorn et al. Mar 2002 A1
20020060049 Kanitz et al. May 2002 A1
20020061386 Carson et al. May 2002 A1
20020081930 Jackson Jun 2002 A1
20020098317 Jaschinski et al. Jul 2002 A1
20020110655 Seth Aug 2002 A1
20020115194 Lange et al. Aug 2002 A1
20020125606 McGuire et al. Sep 2002 A1
20020166646 Drew Nov 2002 A1
20030024674 Kanitz et al. Feb 2003 A1
20030056911 Hermans et al. Mar 2003 A1
20030056917 Jimenez Mar 2003 A1
20030070781 Hermans et al. Apr 2003 A1
20030114071 Everhart et al. Jun 2003 A1
20030159401 Sorensson et al. Aug 2003 A1
20030188843 Kanitz et al. Oct 2003 A1
20030218274 Boutilier et al. Nov 2003 A1
20030220042 Lostocco Nov 2003 A1
20040013859 Annis Jan 2004 A1
20040024377 Karami Feb 2004 A1
20040058606 Branham Mar 2004 A1
20040087237 Garnier May 2004 A1
20040118531 Shannon et al. Jun 2004 A1
20040123963 Chen et al. Jul 2004 A1
20040126601 Kramer et al. Jul 2004 A1
20040126710 Hill et al. Jul 2004 A1
20040168784 Duan et al. Sep 2004 A1
20040173333 Hermans et al. Sep 2004 A1
20040221975 Hernandez-Munoa Nov 2004 A1
20040234804 Liu et al. Nov 2004 A1
20050016704 Huhtelin Jan 2005 A1
20050069679 Stelljes et al. Mar 2005 A1
20050069680 Stelljes et al. Mar 2005 A1
20050098281 Schulz May 2005 A1
20050112115 Khan May 2005 A1
20050123726 Broering et al. Jun 2005 A1
20050130536 Siebers et al. Jun 2005 A1
20050136222 Hada et al. Jun 2005 A1
20050148257 Hermans et al. Jul 2005 A1
20050150626 Kanitz et al. Jul 2005 A1
20050166551 Keane et al. Aug 2005 A1
20050241786 Edwards et al. Nov 2005 A1
20050241788 Baggot et al. Nov 2005 A1
20050252626 Chen et al. Nov 2005 A1
20050280184 Sayers et al. Dec 2005 A1
20050287340 Morelli et al. Dec 2005 A1
20060005916 Stelljes et al. Jan 2006 A1
20060013998 Stelljes et al. Jan 2006 A1
20060019567 Sayers Jan 2006 A1
20060037724 Akai Feb 2006 A1
20060083899 Burazin et al. Apr 2006 A1
20060090867 Herman et al. May 2006 A1
20060093788 Behm et al. May 2006 A1
20060113049 Knobloch et al. Jun 2006 A1
20060130986 Flugge-Berendes et al. Jun 2006 A1
20060135018 Brennan Jun 2006 A1
20060194022 Boutilier et al. Aug 2006 A1
20060269706 Shannon et al. Nov 2006 A1
20070020315 Shannon et al. Jan 2007 A1
20070062657 Scherb Mar 2007 A1
20070131366 Underhill et al. Jun 2007 A1
20070137813 Nickel et al. Jun 2007 A1
20070137814 Gao Jun 2007 A1
20070170610 Payne et al. Jul 2007 A1
20070224419 Sumnicht Sep 2007 A1
20070240842 Scherb et al. Oct 2007 A1
20070251659 Fernandes et al. Nov 2007 A1
20070251660 Walkenhaus et al. Nov 2007 A1
20070267157 Kanitz et al. Nov 2007 A1
20070272381 Elony et al. Nov 2007 A1
20070275866 Dykstra Nov 2007 A1
20070298221 Vinson Dec 2007 A1
20080035289 Edwards et al. Feb 2008 A1
20080076695 Uitenbroek et al. Mar 2008 A1
20080156450 Klerelid et al. Jul 2008 A1
20080199655 Monnerie et al. Aug 2008 A1
20080221003 Meine Sep 2008 A1
20080245498 Ostendorf et al. Oct 2008 A1
20080302493 Boatman et al. Dec 2008 A1
20080308247 Ringer et al. Dec 2008 A1
20090020248 Sumnicht et al. Jan 2009 A1
20090056892 Rekoske Mar 2009 A1
20090061709 Nakai et al. Mar 2009 A1
20090104430 Cordial Apr 2009 A1
20090136722 Nyangiro May 2009 A1
20090205797 Fernandes et al. Aug 2009 A1
20090218056 Manifold et al. Sep 2009 A1
20090246492 Bishop Oct 2009 A1
20090297781 Huss Dec 2009 A1
20100065234 Klerelid et al. Mar 2010 A1
20100119779 Ostendorf et al. May 2010 A1
20100224338 Harper et al. Sep 2010 A1
20100230064 Eagles et al. Sep 2010 A1
20100236034 Eagles et al. Sep 2010 A1
20100236740 Mourad Sep 2010 A1
20100239825 Sheehan et al. Sep 2010 A1
20100272965 Schinkoreit et al. Oct 2010 A1
20110027545 Harlacher et al. Feb 2011 A1
20110180223 Klerelid et al. Jul 2011 A1
20110189435 Manifold et al. Aug 2011 A1
20110189442 Manifold et al. Aug 2011 A1
20110206913 Manifold et al. Aug 2011 A1
20110223381 Sauter et al. Sep 2011 A1
20110253329 Manifold et al. Oct 2011 A1
20110265967 Phan Nov 2011 A1
20110303379 Boechat et al. Dec 2011 A1
20120107568 Manifold May 2012 A1
20120144611 Baker et al. Jun 2012 A1
20120152475 Edwards et al. Jun 2012 A1
20120177888 Escafere Jul 2012 A1
20120199301 Strandqvist Aug 2012 A1
20120227203 Ouellette Sep 2012 A1
20120234333 Jenkins Sep 2012 A1
20120244241 McNeil Sep 2012 A1
20120267063 Klerelid et al. Oct 2012 A1
20120297560 Zwick et al. Nov 2012 A1
20130008135 Moore et al. Jan 2013 A1
20130029105 Miller et al. Jan 2013 A1
20130029106 Lee et al. Jan 2013 A1
20130133851 Boechat et al. May 2013 A1
20130150817 Kainth et al. Jun 2013 A1
20130160960 Hermans et al. Jun 2013 A1
20130209749 Myangiro et al. Aug 2013 A1
20130248129 Manifold et al. Sep 2013 A1
20130327487 Espinosa et al. Dec 2013 A1
20140004307 Sheehan Jan 2014 A1
20140041820 Ramaratnam et al. Feb 2014 A1
20140041822 Boechat et al. Feb 2014 A1
20140050890 Zwick et al. Feb 2014 A1
20140053994 Manifold et al. Feb 2014 A1
20140096924 Rekokske et al. Apr 2014 A1
20140182798 Polat et al. Jul 2014 A1
20140242320 McNeil et al. Aug 2014 A1
20140272269 Hansen Sep 2014 A1
20140272747 Ciurkot Sep 2014 A1
20140284237 Gosset Sep 2014 A1
20140360519 George et al. Dec 2014 A1
20150059995 Ramaralnam et al. Mar 2015 A1
20150102526 Ward et al. Apr 2015 A1
20150129145 Chou et al. May 2015 A1
20150211179 Alias et al. Jul 2015 A1
20150241788 Yamaguchi Aug 2015 A1
20160060811 Riding et al. Mar 2016 A1
20160090692 Eagles et al. Mar 2016 A1
20160090693 Eagles et al. Mar 2016 A1
20160130762 Ramaratnam et al. May 2016 A1
20160145810 Miller, IV et al. May 2016 A1
20160159007 Miller, IV et al. Jun 2016 A1
20160160448 Miller, IV et al. Jun 2016 A1
20160185041 Topolkaraev et al. Jun 2016 A1
20160185050 Topolkaraev et al. Jun 2016 A1
20160273168 Ramaratnam et al. Sep 2016 A1
20160273169 Ramaratnam et al. Sep 2016 A1
20160289897 Ramaratnam et al. Oct 2016 A1
20160289898 Ramaratnam et al. Oct 2016 A1
20170044717 Quigley Feb 2017 A1
20170101741 Sealey et al. Apr 2017 A1
20170167082 Ramaratnam et al. Jun 2017 A1
20170226698 LeBrun et al. Aug 2017 A1
20170233946 Sealey et al. Aug 2017 A1
20170253422 Anklam et al. Sep 2017 A1
20170268178 Ramaratnam et al. Sep 2017 A1
Foreign Referenced Citations (42)
Number Date Country
2168894 Aug 1997 CA
2795139 Oct 2011 CA
1138356 Dec 1996 CN
1207149 Feb 1999 CN
1244899 Feb 2000 CN
1268559 Oct 2000 CN
1377405 Oct 2002 CN
2728254 Sep 2005 CN
4242539 Aug 1993 DE
0097036 Dec 1983 EP
0496524 Jul 1992 EP
0979895 Feb 2000 EP
1911574 Jan 2007 EP
1339915 Jul 2007 EP
2123826 May 2009 EP
946093 Jan 1964 GB
2013208298 Oct 2013 JP
2014213138 Nov 2014 JP
9606223 Feb 1996 WO
9922059 May 1999 WO
200382550 Oct 2003 WO
200445834 Jun 2004 WO
2007070145 Jun 2007 WO
2008019702 Feb 2008 WO
2009006709 Jan 2009 WO
2009061079 May 2009 WO
2009067079 May 2009 WO
2011028823 Mar 2011 WO
2012003360 Jan 2012 WO
2013024297 Feb 2013 WO
2013136471 Sep 2013 WO
2014022848 Feb 2014 WO
201500755 Jan 2015 WO
2015176063 Nov 2015 WO
2016077594 May 2016 WO
2016086019 Jun 2016 WO
2016090242 Jun 2016 WO
2016090364 Jun 2016 WO
2016085704 Jun 2016 WO
2017066465 Apr 2017 WO
2017066656 Apr 2017 WO
2017139786 Aug 2017 WO
Non-Patent Literature Citations (28)
Entry
AWA Paper and Technological Company, Inc., website, “Plant Fibers” (https://www.awapaper.co.jp/e/products/detail/s_m01a.html) p. 1. (Year: 2018).
Derwent abstract: Derwent-ACC-No. 2012-M11761 for US 20120234333 A1 (Jenkins) (Year: 2012).
Renewable, Definitionof, Merriam-Webster, www.merriam-webster.com/dictionary/renewable, retrieved Sep. 16, 2019.
International Search Report for PCT/US16/56871 dated Jan. 12, 2017.
Written Opinion of International Searching Authority for PCT/US16/56871 dated Jan. 12, 2017.
International Search Report for PCT/US2016/057163 dated Dec. 23, 2016.
Written Opinion of International Searching Authority for PCT/US2016/057163 dated Dec. 23, 2016.
International Search Report for PCT/US2017/029890 dated Jul. 14, 2017.
Written Opinion of International Searching Authority for PCT/US2017/029890 dated Jul. 14, 2017.
International Search Report for PCT/US2017/032746 dated Aug. 7, 2017.
Written Opinion of International Searching Authority for PCT/US2017/032746 dated Aug. 7, 2017.
International Search Report for PCT/US17/17705 dated Jun. 9, 2017.
Written Opinion of International Searching Authority for PCT/US17/17705 dated Jun. 9, 2017.
Supplementary European Search Report of EP15792709 dated Nov. 13, 2017.
International Preliminary Report on Patentability of PCT/US2013/053593 dated Feb. 3, 2015.
Supplementary European Search Report of EP 13 82 6461 dated Apr. 1, 2016.
International Search Report of PCT/US15/031411 dated Aug. 13, 2015.
Written Opinion of PCT/US15/031411 dated Aug. 13, 2015.
Written Opinion of International Searching Authority for PCT/US15/62483 dated May 6, 2016.
International Search Report for PCT/US15/63986 dated Mar. 29, 2016.
Written Opinion of International Searching Authority for PCT/US15/63986 dated Mar. 29, 2016.
International Search Report for PCT/US15/64284 dated Feb. 11, 2016.
Written Opinion of International Searching Authority for PCT/US15/64284 dated Feb. 11, 2016.
International Search Report for PCT/US13/53593 dated Dec. 30, 2013.
Written Opinion of International Searching Authority for PCT/US13/53593 dated Dec. 30, 2013.
International Search Report for PCT/US15/60398 dated Jan. 29, 2016.
Written Opinion of International Searching Authority for PCT/US15/60398 dated Jan. 29, 2016.
International Search Report for PCT/US15/62483 dated May 6, 2016.
Related Publications (1)
Number Date Country
20150330029 A1 Nov 2015 US
Provisional Applications (1)
Number Date Country
61994563 May 2014 US