Patent Application
20230340778
The present invention relates to foams that are used to fill cavities, cracks, and crevices to enhance the sealing and insulating properties of buildings and, more particularly, to a foamable system that is contained within an enclosed envelope such as a tube that can be placed within the volume to be sealed. Such a system which reduces the installation time as well as the amount of foam raw material waste is desired by the market.
U.S. Pat. No. 10,384,378 to O'Leary et al describes a system for sealing large volumes or gaps that includes a flexible envelope that can assume the shape of the volume when filled with a foaming composition and that expands the envelope to the boundaries of the volume. The foaming composition may be integral with the envelope or delivered in bulk by an external device. The foaming composition may be one or multiple parts, typically two parts such as a polyisocyanate and a polyol, in which case it is necessary to keep the two parts separate until foaming is desired. Separation may be accomplished by providing multiple compartments that deliver components via a mixing device into the interior. The envelope may include ribs for structural strength and shaping and leak pores around its perimeter to enhance bonding and sealing. It may also include perforations for bulk, modular seals or for separation of portions of the envelope to seal irregular shapes.
U.S. Pat. No. 8,882,483 to O'Leary et al describes a system for sealing or insulating a large volume. The system includes an envelope having walls defining an interior. The interior is configured to receive a foaming composition. The envelope is initially configured in a retracted configuration. A foaming composition is configured for insertion into the interior of the envelope. The envelope is configured such that the foaming composition expands the envelope such as to fill a large gap.
U.S. Pat. No. 9,561,606 to O'Leary et al discloses a system for sealing large volumes or gaps and includes a flexible envelope that can assume the shape of the volume when filled with a foaming composition that expands the envelope to the boundaries of the volume. The foaming composition may be integral with the envelope or delivered in bulk by an external device. The foaming composition may be one or multiple parts, typically two parts such as a polyisocyanate and a polyol, in which case it is necessary to keep the two parts separate until foaming is desired. Separation may be accomplished by providing multiple compartments that deliver components via a mixing device into the interior. The envelope may include ribs for structural strength and shaping, and leak pores around its perimeter to enhance bonding and sealing. It may also include perforations for bulk, modular seals or for separation of portions of the envelope to seal irregular shapes.
United States Patent Application Publication Nr. 20210198411 to Certain Teed LLC teaches methods, devices and systems for insulation, e.g., of cavities associated with walls, ceilings, floors and other building structures, with foam insulation. In one aspect, the disclosure provides a method for providing a cavity of a building with an expanded foam insulation. The method includes dispensing an amount of an expanding foam insulation into the cavity, the expanding foam insulation being dispensable and expandable to provide the expanded foam insulation material, the expanding foam insulation material formed from a premix comprising at least one polyol, at least one polyisocyanate, a blowing agent, and an encapsulated catalyst, the encapsulated catalyst comprising a plurality of catalyst capsules, each comprising an amount of catalyst and a capsule shell encapsulating the catalyst, wherein the dispensing is performed to apply a force to the encapsulated catalyst sufficient to break capsules and release catalyst, the released catalyst initiating reaction between the at least one polyol and the at least one isocyanate; and then allowing the dispensed amount of expanding foam insulation to substantially finish expanding after it is dispensed in the cavity, thereby forming the expanded foam insulation in the cavity.
PCT Publication Number WO 2020123232 to Davlin et al discloses a method and system for the application of foam insulation onto a surface or into a cavity includes a sheet with an aperture where the sheet covers or partially covers the surface or a cavity with the aperture adjacent to the surface or cavity. A pressure-activated foam generator which generates foam is coupled with the sheet. The pressure-activated foam generator includes a frangible output seal with a ruptured position. The pressure-activated foam generator is positioned so that in the ruptured position the foam has a path from the frangible output seal through the aperture and onto the surface or into the cavity. The sheet is connected to cover or partially cover the surface or cavity, and the pressure-activated foam generator is activated and the foam flows onto the surface or into the cavity.
This invention pertains to an article 10 comprising a tube 11 having a length L, a width W and a height H and at least one thermoplastic pouch 12 having a length l and a width w inserted within the tube wherein
As shown in
The tube has a through-thickness direction Gurley air permeability of from 1 to 2000 seconds when measured according to EN ISO5636-5:2013. This range is sufficient to allow gas escape during the foam expansion process.
The tube must be sufficiently flexible to expand during the foaming process but not to an extent where the tube bursts. Tubes having a tensile modulus in the L direction of from 300 to 450 MPa and from 200 to 320 MPa in the W direction according to EN ISO 527-1:2019 meet this requirement. In some embodiments, the tube has a tensile modulus in the L direction of from 340 to 440 MPa and from 205 to 305 MPa in the W direction.
Except when the tube has a circular cross section, the upper and lower section 13 and 14 are of the same dimension and the inner and outer sections 15 and 16 are also of the same dimension but of a dimension less than that of the upper and lower sections 13 and 14. Preferably the ratio of the width of the tube W to the height of the tube H is from 20:1 to 2.3:1.
In some embodiments, the tube has, in the upper section 13 of the tube, two spaced apart flow restrictors 19a and 19b extending along the length of the tube that are attached to the outer surface 20 of the outer layer 18 of the tube. These flow restrictors are shown in both
In other embodiments, the tube has in the lower section 14 of the tube two spaced apart flow restrictors 19c and 19d extending along the length of the tube that are attached to the outer surface 20 of the outer layer 18 of the tube. These flow restrictors are shown in
In yet another embodiment, the tube has two spaced apart flow restrictors 19a and 19b the upper section and two spaced apart flow restrictors 19c and 19d in the lower section 14 of the tube, these four flow restrictors extending along the length of the tube and are attached to the outer surface 20 of the outer layer 18 of the tube.
The tube has a plurality of holes, shown as black dots in
In a preferred embodiment, the inner layer 17 of the tube 11 is a nonwoven fabric of spunbonded polypropylene fiber, an exemplary material being available under the tradename Typar® also from DuPont de Nemours Inc., Wilmington, DE. In some embodiments, the polymer of the fiber has a density of from 240 to 430 kg/m3
In another embodiment, the outer layer 18 is a nonwoven sheet of flash spun polyethylene fiber, an exemplary material being available under the tradename Tyvek® also from DuPont. In some embodiments, the polymer of the fiber has a density of from 930 to 970 kg/m3
The pouch 12 is thermoplastic and, as shown in
The pouch 12 contains a foamable composition.
Preferably, there are a plurality of pouches 12 within the tube 11. The spacing between adjacent pouches can vary but typically can be between 50 to 1000 mm, preferably from 400 to 600 mm and more preferably from 450 to 550 mm or even 300 to 500 mm. Preferably adjacent pouches are connected to each other by a connecting means such as a thermoplastic tape or ribbon.
In one embodiment all the components of the foamable composition are in one pouch but remain inactive until a reaction initiation step is activated. Reaction initiation may be by means such as ultrasonic, gas pressure blast, thermal heat or suitable frequencies in the electromagnetic spectrum such as infra-red or ultra-violet.
In another embodiment, as shown in
In one embodiment, the first and second compartments C1 and C2 are each about 70 mm long, 30 mm wide and 12 mm thick. In some embodiments, the first and second compartments may be of different lengths.
Where there are a plurality of pouches, they may be of the same or differing lengths.
By frangible barrier we mean a material that separates the two compartments but may be easily broken by a breaking means to allow the chemical components of the two compartments to be intimately mixed and react to form a foam. Suitable materials for the frangible barrier include ethylene copolymer ionomer such as Surlyn® which is available from Dow, Midland, MI. Suitable breaking means include mechanical, ultrasonic, gas pressure blast, thermal heat, or suitable frequencies in the electromagnetic spectrum such as infra-red or ultra-violet. Exemplary mechanical breaking means are hand manipulation, a hammer, roller or rod pulling.
In one embodiment as depicted in
A suitable adhesive is Bynel®. Another exemplary structure comprises a Surlyn® layer, a Bynel® adhesive layer, an ethylene vinyl alcohol (EVOH) copolymer layer, a Bynel® adhesive layer, a low density polyethylene (LDPE) layer and an oriented polyethylene (OPET) layer.
Preferably, as shown at 32 in
By foamable composition is meant a composition that when all the ingredients are combined and a reaction initiated or activated, the components of the foamable composition within the pouch 12 react to form an expandable foam, the foam then bursting the pouch 12, expanding the tube 11 and escaping through the tube holes in the upper section 13 and/or lower section 14 of the tube and, when present, between the two spaced apart flow restrictors 19a and 19b and/or 19c and 19d that extend along the length of the tube so as to fill, as in
In an embodiment where the pouch comprises first C1 and second C2 compartments, the first foamable composition component in the first compartment C1 comprises isocyanate and the second foamable composition component in the second compartment C2 comprises polyol. The isocyanate composition may be formulated to have a monomeric diisocyanate content of less than 1 weight percent or even less than 0.1 weight percent, such formulations being well known in the trade. The second foamable composition component may further comprise a catalyst and/or a blowing agent.
In some embodiments, the composition may also comprise particles having a major dimension no greater than 1 mm to act as nuclei for cell formation thus yielding smaller pore sizes in the expanded foam. Exemplary particles are graphite, micro-balloons and calcite. For a polyurethane foam composition, these additional particles are incorporated into the second foamable composition component (polyol). Non-polyurethane two part chemistries are also suitable as foaming compositions, for example one based on an epoxy system or one based on a silicon system. In this instance the nucleating particles are kept separate from both major components until the time for mixing. This requires that these particles are located in a third compartment such as is shown between the two frangible barriers 21a and 21b in
Other functionality enabling additives are flame retardants, pigments and fillers such as fibers, filaments, fibrils and pulps such as those of glass or aramid. In some embodiments, the addition of p-aramid pulp present in an amount of from 0.05 to 3.0 weight percent of the foamed composition has been shown to be beneficial. This type of pulp comprises highly fibrillated chopped p-aramid fibers having a length no greater than 1,000 micrometers. Preferably the fiber diameter is about 50 micrometers. The pulp may be added to either the first foamable composition component, the isocyanate, or the second foamable composition component, the polyol. Foamed polyurethane compositions incorporating p-aramid pulp exhibits increased compressive strength and compressive modulus with similar expansion and acceptable flexibility when compared with foamable compositions in which the pulp additive is absent. This increased compression or modulus enhances shock absorption properties in sealed gaps in fenestrations, a desirable feature in buildings where, for example, window expansion occurs in hot weather.
A desired property of the expanded foam is that it should be sufficiently flexible to compress to at least 10%, more preferably to at least 20% or even to at least 50% when tested according to standard EN 826:2013.
Another desired feature of the foam is that one week after expansion, the foam shrinkage should be no more than 20% and preferably no more than 10% of the original expanded foam dimensions when tested based on methods disclosed in standard EN 1604:2013. This evaluation is carried out at ambient temperature as well as in temperature cycles from −10 to +50° C.
In some embodiments, the foamable materials contained in each pouch are the same. In some other embodiments, the foamable materials contained in one pouch are different from the foamable materials contained in another pouch, for example, some pouches may contain foamable materials that on reacting provide a foam that is of higher density but lower expansion than foams created from other pouches wherein the foamable materials contained in these other pouches are of a different chemical composition. Such a feature could reduce or even eliminate the need for mechanical fixation of windows by nails or screws.
The invention described above finds utility in new construction or in refurbishment of existing buildings where there is a gap to be filled. Typical applications include sealing of air gaps between a window and wall, between a door and wall, between a wall and roof, between two walls and gap sealing between two adjacent pre-fabricated building panels or modules. These are sometimes referred to as building interfaces.
In one embodiment, a method for sealing an air gap 26 between building interfaces 24 and 25 comprises the steps of:
In some embodiments, the foamable materials contained in one pouch differ from the foamable materials contained in another pouch,
An optional step in the above method is, prior to inserting the tube 11 into the air gap 26, to apply a bonding means to either the lower section 14 of the tube 11 or the upper surface 23 of the building interface. This bonding means which may be for example a double sided tape or a hot melt adhesive helps to hold the tube in the correct position.
In an alternative embodiment, a method for sealing an air gap 26 between building interfaces 24 and 25 comprises the steps of:
activating the foamable composition within the pouch by breaking the frangible barriers 21 or 21a and 21b separating the first C1 and second C2 sections of each compartment of the pouch 12 by a breaking means thereby allowing the first and second compositions to mix, react and form an expandable foam, the foam then bursting the pouch 12, expanding the tube 11 and escaping through the tube holes located in the upper section 13 and/or lower section 14 of the tube 11 and, when present, between the two spaced apart flow restrictors 19a and 19b and/or 19c and 19d that extend along the length of the tube 11 so as to fill the air gap 26 between the building interfaces 24 and 25 of the building structure and then cure in situ into a foam structure that provides an air tight and water impermeable seal.
The breaking means may be mechanical, ultrasonic, gas pressure blast, thermal heat, or suitable frequencies in the electromagnetic spectrum such as infra-red or ultra-violet. Exemplary mechanical breaking means include hand manipulation, a hammer, roller or rod pulling.
In some embodiments, the foamable materials contained in one pouch differ from the foamable materials contained in another pouch.
An optional step in the above method is, prior to inserting the tube 11 into the air gap 26, to apply a bonding means to either the lower section 14 of the tube 11 or the upper surface 23 of the building interface. This bonding means which may be for example a double sided tape or a hot melt adhesive helps to hold the tube in the correct position.
Free rise density of the foam was measured according to ASTM D7487-13: Standard Practice for Polyurethane Raw Materials: Polyurethane Foam Cup Test.
Dynamic compressive strength and compressive modulus of the foam was measured according to EN ISO 844-2021: Rigid Cellular Plastics.
All parts and percentages are by weight unless otherwise indicated. Examples prepared according to the current invention are indicated by numerical values. Control or Comparative Examples are indicated by letters.
The article of Example 1 may be evaluated in an air gap space between two building components. This space has nominal dimensions of a length of 4.2 m, a width of 77 mm and a thickness of 25 mm.
Comparative Example A was evaluated in an air gap space between two building components. This space had nominal dimensions of a length of 4.2 m, a width of 77 mm and a thickness of 25 mm.
In Example 1, the outer layer 18 may be Tyvek® window tape grade 1310PT, a polyethylene terephthalate—polyamide nonwoven film available from DuPont de Nemours Inc, Wilmington, DE. The inner layer 17 may be a 60 gsm sheet of Typar® SF20 which is also from DuPont. Example 1 had 2 mm diameter holes arranged in two separated lines in a zig-zag pattern in the upper section 13 of the tube.
The foamable material can consist of four pouches of Instapak® QuickRT® packaging foam from Sealed Air Corporation, Elmwood Park, NJ. Each pouch comprises two compartments separated by a frangible barrier, one compartment comprising polyol and the other compartment comprising isocyanate. Two of the pouches comprise 75 g of reactive material and two of the pouches comprise 100 g of reactive material giving a total foamable composition of 350 g. The frangible barrier may be broken by hand manipulation thus allowing the reagents to react and form the foam.
Comparative Example A represents the current state of art in the trade and consisted of injecting a one component polyurethane foam sealant, InstaStik Flex+ from DuPont, into the gap and allowing the foamable material to expand, cure and harden. Any foam extending beyond the plane of the exterior surfaces of the two building components was removed and smoothed flush. A DuPont Tyvek® window tape sealant grade 1310 PT was then applied over the smoothed foam to overlap the building components. The foam amount was 375 g.
Measured installation time included preparation work, installing the pouches, foam activation or application, foam expansion and cure, finishing steps and application of flashing. Examples were considered to be satisfactory and beneficial to the trade if the installation time was 30 minutes or less. Example 1 will have an installation time of less than 30 minutes while the installation time for Comparative Example A was about 60 minutes.
An advantage of obtaining enhanced compressive tensile and modulus performance from the cured foam was achieved by the addition of p-aramid pulp to the foamable composition. The pulp which was DuPont merge 1K1957 had a nominal fiber diameter of 50 micrometers and fiber length of less than 1 mm. The pulp was added to the polyol component of an isocyanate-polyol foamable composition such that it comprised 0.4 (Example 2) or 0.8 weight percent (Example 3) of the composition. The isocyanate (Voronate™ M230) comprised 60 weight percent of the foamable composition with the polyol component comprising the remaining 40 weight percent. The polyol component comprised 32 weight percent of Voranol™ polyether polyol, 6 weight percent of water and 2 weight percent of catalyst. The amount of polyol was reduced by 0.4 or 0.8 weight percent in the examples comprising the p-aramid pulp. The sample without the pulp ingredient was a control example (Comparative Example B). These compositions were foamed and test coupons subjected to compression and modulus tests. The resultant values were normalized to address variations in foam density (free rise density) of the test samples.
The basis for the testing was EN ISO 844-2021. The foamed test samples were 16 mm thick and each was compressed by 3 mm. The dynamic compressive strength was determined by applying a strain of 18.75% then the compressive load was released for 60 seconds. This procedure was repeated four more times. The compressive modulus is determined as per the EN ISO 844-2021 standard. The results are shown in Table 1.