Patent Application
20210269718
The present invention relates to the use of foaming additives in liquid, paste or powder form to condition soil excavated with a tunnel boring machine. Said additives can be classified as readily biodegradable and are characterised by a lower ecotoxicological impact than commercial products.
Currently, tunnels can be excavated by two main technologies:
The first method involves cyclical application of the operations described below:
Said method is based on eliminating the right portion of rock so as to redistribute forces around the excavation, resulting in the “arch effect”, which partly supports the consolidating action of the reinforcing rods and shotcrete.
The second construction technique can be divided into two main categories: the partial-face system and the full-face system (which involves excavating the entire tunnel diameter at the same time). In the first case, operations proceed as already described for the conventional method with roadheaders and rock breakers (instead of explosive), gradually forming the shape of the tunnel which will subsequently be lined with reinforced concrete. In the second case the advance is effected with a complex machine called a Tunnel Boring Machine (TBM), also known as a “mole” which, as well as performing the excavation, supports and prevents collapses of the face, carries away muck (by means of a screw and a conveyor belt), and places the final tunnel lining, consisting of prefabricated reinforced concrete segments. This type of machine can excavate nearly all types of geological material, including compact rock (hard-rock TBM), fractured rock (double-shield TBM), loose soil and under aquifers (EPB—Earth Pressure Balance machine).
A TBM consists of:
The cutterhead is fitted with tools called cutters, namely steel discs, which are designed to demolish the soil. Scrapers convey the soil to the conveyor belt that carries it out of the tunnel.
The advance must take place with the excavation chamber constantly and completely full of suitably conditioned excavated material, in order to guarantee homogenous, uniform distribution of soil pressure on the tunnel face and prevent pressure drops between one push and the next. Said machines operate well when the layers through which the tunnel is driven are relatively hard and rigid, but do not perform so well when soft, friable soils are excavated. One technique used to overcome this problem is to apply a conditioning agent to the soil through the cutterhead. This stabilises the soil and facilitates excavation and soil extraction.
In the latest developments of this technology, polymer foams have been suggested. They have the considerable advantage that they considerably reduce the input of water into the soil. A standard foaming agent formulation comprises a foaming agent and a stabilising agent.
Thus, in operation, the foam is directly injected into the cutterhead at the excavation interface.
The excavated soil is thus characterised by an organic content, deriving from the use of said additives, which interferes with the ecosystem.
This influence is defined by ecotoxicological tests conducted on the products “as is” or on matrices conditioned with the additives according to the invention.
The foaming products generally used contain anionic surfactants. Said anionic surfactants are usually C12-16 alcohol ethoxylate (1-4 ethoxylation groups) sulphates. They are salified organic compounds, generally as sodium salts.
Examples of foaming additives available on the market are:
The product which is currently most widely used is called Polyfoamer ECO 100, comprising 10 to 20% by weight of a mixture of linear alcohols with a C12-C14 alkyl ethoxylate chain, sulphonated and salified with sodium.
EP 1027528 illustrates a boring method wherein the composition of the aqueous material injected into the tunnel face consists of a polyethylene oxide with a molecular weight ranging between 2 and 8 million and an anionic surfactant containing sulphate.
U.S. Pat. No. 6,172,010 discloses an aqueous foaming additive consisting of a surfactant and a polymer characterised by opposite charges, to obtain a stable foam.
U.S. Pat. No. 6,802,673 discloses an aqueous foaming additive consisting of an anionic surfactant and a β-naphthalene sulphonate formaldehyde condensate.
U.S. Pat. No. 4,442,018 discloses the composition of an additive for the production of a stable foam in aqueous phase consisting of an acrylic acid polymer, a C12-C14 and C16 alcohol, a C4 and C5 alcohol, sodium lauryl sulfate or alpha-olefin sulphonate, and water.
The present invention relates to the use as conditioning foaming additive of a salified alkyl ether sulphate having a straight or branched C7-C11 alkyl chain and a degree of ethoxylation ranging between 4 and 9 as conditioning agent able to generate foam during mechanised soil excavation with a TBM. The additive, in liquid, paste or powder form, generates foam when added in percentages of 0.1-4% by weight to an aqueous solution used on the tunnel face to soften the soil and allow faster extraction, and in the conditioning chamber to maintain the stability of the tunnel face.
The use of a salified alkyl ether sulphate having a branched C7-C11 alkyl chain and a degree of ethoxylation of 7-9 is preferred. The alkyl ether sulphate is preferably a sodium or potassium salt.
The salified alkyl ether sulphate can be used in addition to an aqueous solution in a percentage by weight of 0.1-4.0%.
The salified alkyl ether sulphate can also be used in admixture with one or more surfactants selected from acyl glutamates and alkyl polyglucosides, in particular in admixture with an acyl glutamate selected from cocoyl glutamate, lauroyl glutamate, myristoyl glutamate, capryloyl glutamate, caproyl glutamate and the sodium salts thereof or in admixture with an alkyl polyglucoside selected from decyl glucoside, capryl glucoside, lauryl glucoside and cocoyl glucoside. Lauroyl glutamate, in particular in the form of sodium salt, and capryl glucoside, are particularly preferred.
The percentages by weight of the total surfactant(s) present in the conditioning additive can range from 30 to 100% for alkyl ether sulphate, 0 to 50%, preferably 5 to 50%, for acyl glutamates, and 0 to 50%, preferably 10 to 50%, for alkyl polyglucoside, obviously on the proviso that the total is 100.
The surfactants according to the invention are classifiable as readily biodegradable according to the OECD 301 guidelines.
The additives can also contain foam stabilisers able to increase the half-lives of the foams generated. The stabilisers can be biopolymers. The term “biopolymers” refers to polymers degradable due to the effect of micro-organisms such as bacteria, fungi or seaweed. They are mainly water-soluble polysaccharides able to increase the viscosity of an aqueous system in a pH range between 4 and 12. The preferred biopolymers are xanthan gum and guar gum.
The additives are characterised by a lower ecotoxicological impact than the products commercially available and used in mechanised excavations.
The foaming additive can also contain other compounds useful to deal with specific problems such as clogging due to clayey soils, to prevent high consumption of the cutters fitted in the cutterhead, or to reduce the quantity of soluble salts in the water present in the excavation soil.
The characteristics and advantages of the use according to the invention are more particularly described in the examples below. The percentages of the ingredients are expressed by weight.
Column A shows the composition by weight expressed as a percentage of the formulation, while column B shows the weight percentage of the single compound as a percentage of the active content. The stability of the foam generated by an aqueous solution prepared by adding 2% by weight of foaming additive to 5000 g of water is evaluated. The stability is expressed as the half-life, which indicates the time required for the weight of the foam to halve. The test is conducted by evaluating the time in which water amounting to half the weight/volume of the foam is released in a 250 ml cylinder. The foam is formed by a generator that conveys the flow of liquid at a constant airflow into a glass ball mixer.
The data set out in Table 2 demonstrate that the stability of the foams generated with the products of lower ecotoxicological impact have half-lives comparable to or better than that of the foam generated with the commercial product.
The conditioning capacity of the additives of Example 1 was evaluated with a stabilised soil called “Vitali” (particle size 0.075-25 mm). The foam used to condition the matrix is generated from an aqueous solution prepared by adding 2% by weight of foaming additive to 5000 g of water. The foam is formed by a generator that conveys the flow of liquid at a constant airflow into a glass ball mixer. The evaluation involves adding the foams generated with the additives to three 11 kg samples of aggregate, and homogenising the mixture in an IMER 5140 cement mixer (drum capacity 138 lt) for 5 minutes. The matrix conditioning is scored as a slump class. The results are set out in Table 3:
The data demonstrate the good conditioning capacity of the new formulations.
Column A shows the composition by weight expressed as a percentage of the formulation, while column B shows the weight percentage of the single compound as a percentage of the active content. Sample no. 4 was formulated without straight Cl 2-C14 alcohol ethoxylate (2-3 moles of ethylene oxide) and sodium sulphate.
The stability of the foam generated by an aqueous solution prepared by adding 2% by weight of foaming additive to 5000 g of water is evaluated. The stability is expressed as the half-life, which indicates the time required for the weight of the foam to halve. The test is conducted by evaluating the time in which water amounting to half the weight/volume of the foam is released in a 250 ml cylinder.
The foam is formed by a generator using a constant airflow.
The data demonstrate an increase in the stability of the foam.
The foaming additives have the following compositions:
Column A shows the composition by weight expressed as a percentage of the formulation, while column B shows the weight percentage of the single compound as a percentage of the active content. Sample no. 7 was formulated without straight C12-C14 alcohol ethoxylate (2-3 moles of ethylene oxide) and sodium sulphate, which is always present as foam generator in commercial products.
The stability of the foam generated by an aqueous solution prepared by adding 2% by weight of foaming additive to 5000 g of water is evaluated. The stability is expressed as the half-life, which indicates the time required for the weight of the foam to halve. The test is conducted by evaluating the time in which water amounting to half the weight/volume of the foam is released in a 250 ml cylinder. The foam is formed by a generator using a constant airflow.
The data set out in Table 7 demonstrate an increase in the stability of the foam.
The conditioning capacity of the additive of Example 3 was evaluated by the method described in Example 2. The results are set out in Table 8:
The data demonstrate the good conditioning capacity of sample no. 4, formulated without straight C12-C14 alcohol ethoxylate (2-3 moles of ethylene oxide) and sodium sulphate, which is always present as foam generator in commercial products.
The toxicity in an aquatic environment of the additives called “Polyfoamer ECO 100” and “sample 1”, described in Table 1, was evaluated according to the OECD Guidelines on acute toxicity in fish (OECD 203), algae (OECD 201) and daphnia (OECD 202). The data are expressed as:
The data are summarised in Table 9 below:
The data demonstrate the lower ecotoxicological impact of sample 1. By replacing part of the straight C12-C14 alcohol ethoxylate (2-3 moles of ethylene oxide) and sodium sulphate with branched C9-C11 alcohol ethoxylate (7 moles of ethylene oxide) sodium sulphate, a foaming additive with lower aquatic excitoxicity is obtained.
The acute toxicity in fish of the additives called “Polyfoamer ECO 100”, “sample 2” and “sample 3”, described in Table 1, was evaluated. The data, obtained according to OECD guideline 203, are expressed as:
The data demonstrate the lower ecotoxicological impact of samples 2 and 3. By replacing the C12-C14 alcohol ethoxylate (2-3 moles of ethylene oxide) sodium sulphate with the surfactants listed in Table 1, foaming additives with lower acute toxicity in fish are obtained. In particular, the toxicity declines in proportion to the C12-C14 alcohol content.
The acute toxicity in fish of the additives called “Polyfoamer ECO 100” and “sample 4” was evaluated according to OECD 203. The data are expressed as:
The data demonstrate the lower ecotoxicological impact of sample 4. By wholly replacing the C12-C14 alcohol ethoxylate (2-3 moles of ethylene oxide) sodium sulphate with the surfactants listed in Table 4, a foaming additive characterised by much lower acute toxicity in fish was obtained.
The foaming additives called “Polyfoamer ECO 100” and “sample 7” were evaluated to establish their acute toxicity in fish (OECD 203).
The data are expressed as:
The data set out in Table 12 demonstrate the ecotoxicological impact of sample 7. By wholly replacing the C12-C14 alcohol ethoxylate (2-3 moles of ethylene oxide) sodium sulphate with the surfactants listed in Table 6, a foaming additive characterised by much lower acute toxicity in fish was obtained.
| Number | Date | Country | Kind |
|---|---|---|---|
| 102018000007438 | Jul 2018 | IT | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/IB2019/056273 | 7/23/2019 | WO | 00 |