The present invention relates to a forming mold employed in yielding a molded product.
Typically, molded products such as urethane molded products are produced by means of a forming mold through the following sequential steps. Firstly, a precursor of a molded product (e.g., a slurry) is poured into a space for forming a material (hereinafter referred to as a forming space) defined by a surface provided for forming an object material (hereinafter referred to as a forming surface) of the forming mold. Then, the slurry or the like is solidified (and dried), to thereby provide a molded product in the forming space. The forming mold is removed from the molded product (i.e., the molded product is released from the forming mold), to thereby separate the molded product.
During mold releasing, in some cases, a molded product adheres on the forming surface of the forming mold. In order to prevent adhesion of a molded product (i.e., to enhance mold-releasability), a fluororesin layer is provided on the forming surface of a forming mold. This technique is widely known in the art (see, for example, Japanese Patent Application Laid-Open (kokai) No. 2006-264225).
For example, the above Patent Document discloses that an Ni-containing under-plating layer is formed on the forming surface of a forming mold, and the under-plating layer is coated with a fluororesin layer. The Patent Document also discloses that the hardness of the forming surface of the forming mold is ensured by means of the under-plating layer formed through the treatment, and the fluororesin layer provides excellent mold-releasability.
However, in the case where a fluororesin layer is formed through a coating process as described in the above document, relatively large depressions (cavities) having, for example, a depth of 0.01 mm or more may be problematically formed in the surface portion of the fluororesin layer (i.e., the surface in direct contact with a slurry or the like (actual forming surface)). The large depressions are easily formed when the fluororesin layer is relatively thick. The large depressions are thought to be formed by, for example, removal of foam remaining in the fluororesin layer formed through a coating process.
Meanwhile, when the fluororesin layer is relatively thin, such large depressions are difficult to form. However, in the case where a slurry containing hard powder, in particular a ceramic slurry, is used, mold-releasability may be impaired due to surface wearing of the fluororesin layer, even though the mold is subjected to molding processes several times (e.g., about 10 times), which is problematic.
The present invention has been conceived in order to solve the problem. Thus, an object of the present invention is to provide a forming mold which is free from large depressions in the surface portion of the resin layer serving as an actual forming surface and which has high durability.
Accordingly, the forming mold of the present invention comprises a base member, a resin layer which is bonded to the base member and which serves as a forming surface, and a bonding layer which intervenes between the base member and the resin layer and which bonds the base member to the resin layer. Furthermore, the base member has a rigidity higher than that of the resin layer. In one embodiment of the present invention, the resin layer is formed of a fluororesin, and the base member is formed of a metal. As used herein, the term “rigidity” refers to a product (EI) of Young's modulus of material E [N/m2] and second moment of area I along the depth direction [m4].
The forming mold may be produced through, for example, bonding the resin layer onto the base member by use of an adhesive, and working the surface of the thus-bonded resin layer, to thereby realize the forming surface. Alternatively, the forming mold may be produced through, for example, providing a forming surface in the surface portion of a resin layer, and bonding the thus-formed resin layer onto the base member by use of an adhesive. The adhesive may be formed from a material (i.e., a material for forming the bonding layer) containing no metallic element. Examples of such a material include an adhesive for bonding members formed of different materials.
Thus, according to the forming mold of the invention, the surface of the resin layer (i.e., the surface in direct contact with a slurry or the like (actual forming surface)) may be produced through working and molding or a similar process. Therefore, differing from the forming mold disclosed in the above document (i.e., a forming mold in which the fluororesin layer has been formed through a coating process), no large depressions are formed in the surface portion of the resin layer serving as an actual forming surface. Specifically, the maximum depth of the depressions unaviodably remaining in the surface portion (surface, flat portion) of the forming surface of the resin layer is preferably 0.007 mm or less.
In addition to the forming mold of the invention, the resin layer is bonded to the base member having a rigidity higher that of the resin layer. Therefore, as compared with a forming mold formed of only a resin layer, deformation of the resin layer is prevented, wherein dimensional precision of the resin layer serving as an actual forming surface can be further enhanced. Specifically, the flatness of the flat portion of the forming surface of the resin layer may be adjusted to 0.030 mm or less (described in detail hereinbelow).
In the forming mold of the present invention, the material forming the forming surface of the resin layer preferably contains no additive or primer. Generally, when the material forming the forming surface contains an additive or a primer, the resin content of the resin layer decreases, resulting in reduction in mold-releasability. That is, satisfactory mold-releasability can be attained on the basis of the above characteristic feature. Notably, the inside of the resin layer (a portion not forming the forming surface) may contain an additive or a primer.
In the forming mold of the present invention, the forming surface of the resin layer preferably has a contact angle with respect to water of 60° or more. More preferably, the forming surface of the resin layer has a contact angle with respect to water of 85° or more. Through controlling the contact angle, satisfactory mold-releasability can be attained.
In the forming mold of the present invention, the minimum thickness of the resin layer may be adjusted to 0.1 mm or more. Through the adjustment, the resin layer has a sufficient thickness. As a result, there can be prevented “impairment of mold-releasability due to surface wearing of the fluororesin layer” occurring when the resin layer is relatively thin. That is, durability of the forming mold can be enhanced. Such a characteristic feature cannot be attained by a forming mold disclosed in the above document (i.e., a forming mold in which the fluororesin layer has been formed through a coating process).
In a portion of the forming surface of the resin layer, the portion being present on a flat portion of the bonding surface of the base member, a step having a height of 0.1 mm or more may be formed. An edge of the step is formed at high precision to have any shape (e.g., rectangular edge, chamfered edge, R-shape edge). The step is formed in the aforementioned production method of the forming mold in which the resin layer is bonded to the base member, to form a resin-base integrated member, and the forming surface of the resin layer is produced through working and molding or a similar process. The above characteristic feature cannot be attained by the forming mold disclosed in the above document (Le., a forming mold in which the fluororesin layer has been formed through a coating process).
Preferably, the base member is formed of a metal; the resin layer is formed of “a resin material having a glass transition point of 130° C. or higher”; and the bonding layer is formed of “a material having a glass transition point of 80° C. or higher.” More preferably, the bonding layer is formed of “a material having a glass transition point of 100° C. or higher.” Conventionally, there has been widely known a technique of applying a mold-release agent to a forming surface of a forming mold made of metal in order to enhance mold-releasability of a target material from the forming mold. In this technique, a material having a glass transition point lower than 60° C. (e.g., fluorine-containing polymer) is used as a mold-releasing agent. Therefore, when the molded product produced by means of the forming mold is dried at 60° C. or higher, the mold-release agent is softened, thereby impairing mold-releasability, which is problematic. In contrast, by virtue of the above characteristic feature, even when the molded product produced by means of a forming mold is dried at high temperature, no softening occurs in the resin layer and the bonding layer, whereby mold-releasability does not decrease.
[
[
[
[
[
[
[
[
[
The forming mold according to the present invention may be employed as a forming mold for yielding a molded product through a process which includes preparing a slurry from slurry raw materials including a ceramic material powder, a dispersion medium, a gelling agent, and a dispersing agent; and casting the slurry into the mold. In the forming mold of the present invention, at least a portion of the mold has the characteristic features of the present invention, and preferably the entirety of the forming mold has the characteristic features of the present invention. In the case where the forming mold is composed of a plurality of members such as an upper half and a lower half, at least one member has the characteristic features of the present invention.
The base member 10 is formed of a metallic material such as aluminum alloy, stainless steel, titanium, or iron-based material. The base member 10 has a rigidity higher than that of the resin layer 20. In other words, the base member 10 can serve as a support base for preventing deformation of the resin layer 20.
The resin layer 20 is formed of a material which provides high mold-releasability, such as fluororesin (fluorine-containing compound), silicone resin (silicone compound), or PVA. Examples of the fluorine-containing compound include PTFE, PFA, ETFE, FEP, PVDF, PCTFE, and PFA. The material for forming the resin layer 20 preferably has a glass transition point of 130° C. or higher.
The surface of the resin layer 20 (the upper surface in
The material forming the “forming surface” preferably contains no additive or primer. Also, the “forming surface” preferably has a contact angle with respect to water of 60° or more (more preferably 85° or more). Through controlling the contact angle, excellent mold-releasability can be attained. The inside portion of the resin layer 20 (the portion not serving as the forming surface) may contain an additive or a primer.
The bonding layer 30 intervenes between the base member 10 and the resin layer 20, to thereby bond the resin layer 20 to the base member 10. Before carrying out bonding, the bonding surface of the base member 10 and that of the resin layer 20 may be subjected to a treatment for enhancing bonding strength between the two layers (e.g., surface roughening). The bonding layer 30 is formed from a material containing no metallic element. An example of the material is an adhesive for bonding members formed of different materials. Specific examples thereof include an epoxy-base adhesive. Examples of the epoxy-type adhesive include a 1:1 (by mass) mixture “EPDXY RESIN AV138” and “HARDNER HV998”(products of Nagase Chemtex Corporation). The bonding layer 30 has a thickness of, for example, 0.01 to 1 mm. The material for forming the bonding layer 30 preferably has a glass transition point of 80° C. or higher.
With reference to
In the first production method, a resin plate corresponding to the resin layer 20 having no “forming surface” is produced through a known technique. Then, as shown in
Subsequently, as shown in
With reference to
In the second production method, as shown in
Subsequently, as shown in
Subsequently, as shown in
According to the embodiments of the forming mold of the present invention, the surface of the resin layer 20; i.e., the “forming surface” is provided through working (in first production method) or molding (in second production method). Therefore, differing from the forming mold disclosed in the above document (in Description of the Related Art) (i.e., a forming mold in which the fluororesin layer has been formed through a coating process), no large depression is formed in the surface portion of the resin layer serving as an actual forming surface.
In addition, the resin layer 20 is bonded to the base member 10 having a rigidity higher than that of the resin layer 20. Therefore, as compared with a forming mold formed of only a resin layer, deformation of the resin layer is prevented, wherein dimensional precision of the resin layer serving as an actual forming surface can be further enhanced.
Furthermore, since the resin layer 20 is integrated into the base member 10 via bonding, the thickness of the resin layer 20 can be adjusted as desired. Thus, the minimum thickness of the resin layer 20 can be adjusted to 0.1 mm or more. When the resin layer 20 is sufficiently thick, the aforementioned “impairment of mold-releasability due to surface wearing of the fluororesin layer” can be prevented. Although the bonding surface of the base member 10 serving as a supporting substrate for the resin layer 20 has no step (i.e., is flat), the depth (height) of the recess (step) 21 of the resin layer 20 can be adjusted to 0.1 mm or more. This cannot be attained by the forming mold disclosed in the above document (i.e., a forming mold in which the fluororesin layer has been formed through a coating process).
In one preferred embodiment, the base member 10 is formed of a metal; the resin layer 20 is formed of a “resin material having a glass transition point of 130° C. or higher; and the bonding layer 30 is formed of a “material having a glass transition point of 80° C. or higher. Therefore, even when the molded product produced by means of the forming mold is dried at a high temperature as high as about 80° C., the resin layer 20 and the bonding layer 30 do not melt, whereby impairment in mold-releasability is prevented.
Next will be described an experiment of measuring the flatness of the flat portion of the resin layer 20 serving as an actual “forming surface” of a forming mold according to an embodiment of the present invention. In this experiment, as shown in
In the above embodiment, the plane shape (shape of the surface P2 as viewed from the top) is a square (300×300 mm). The molded product of the embodiment has been produced through the “first production method.” That is, the flat-plate-like resin layer 20 having no “forming surface” was bonded to the flat-plate-like base member 10 by the mediation of the bonding layer 30, and the “forming surface” of the resin layer 20 was produced through surface grinding, to thereby realize the flat surface P2.
In the experiment, the embodiment was compared with reference molded products having the same general shape. Comparative Example 1 was a forming mold that is formed of resin, and Comparative Example 2 was a forming mold in which the surface of a metal mold was coated with a fluororesin. The plane shape (shape of the surface as viewed from the top) of each of the molded products of Comparative Examples 1 and 2 is the same as that of the present embodiment; i.e., a square (300×300 mm). In Comparative Example 1, similar to the present embodiment, the flat surface serving as the “forming surface” was produced through surface grinding. In Comparative Example 2, the flat surface serving as the “forming surface” is produced through coating the flat portion of the metal mold with fluororesin (the (flat) surface of the coating film not being further worked).
Table 1 shows the results. In Table 1, level 1 corresponds to the present embodiment, levels 2 and 3 correspond to the Comparative Example 1, and level 4 corresponds to the Comparative Example 2. The thickness of the base member and that of the resin layer and other properties are also shown in Table 1. Three samples were prepared at each level. The flatness of the “forming surface” of each sample was measured. The measurement was performed by means of a known 3-dimensional measuring apparatus according to the method described in JIS B0621.
As is clear from Table 1, the forming surface of the present embodiment has a flatness of 0.030 mm or less, whereas the flatness of Comparative Example 1 or 2 is greater than 0.030 mm. Conceivable reasons why the flatness of Comparative Example 1 is somewhat great are that a high-rigidity base level is not present during surface grinding of the “forming surface” and that deformation of the grinded surface is difficult to prevent. Conceivable reasons why the flatness of Comparative Example 2 is somewhat great are that the thickness of the coating film unaviodably varies and that the surface of the coating film (i.e., “forming surface”) is readily deformed due to deformation of the metal mold at a high coating process temperature.
In contrast, conceivable reasons why the flatness of the embodiment is as small as 0.030 mm or less are that the resin layer 20 is difficult to deform by virtue of bonding thereof to the high-rigidity metal mold (base member 10) and that surface grinding is performed with the high-rigidity metal mold (base member 10) as a base level.
Notably, no particular limitation is imposed on the present invention. Other than the aforementioned embodiment, various modifications may be employed, within the scope of the present invention. For example, in the above embodiment, the bonding surface of the base member 10 and that of the resin layer 20 are flat. However, the bonding surfaces may be curved. In the above embodiment, the “forming surface” of the resin layer 20 has a flat portion P1. However, the flat portion may be absence. Furthermore, the recess (step) 21 may be omitted.