Patent Application
20160186506
1. Technical Field
The present invention relates to a fracturing liquid delivery hose for recovery of shale oil & gas, and manufacturing method and co-extrusion mold thereof, and falls within the field of fluid delivery equipment.
2. Related Art
The hydrofracturing technology is a method only available for commercial recovery of shale oil & gas at present, where after a high pressure liquid is filled in a bore well and causes a terrane to fracture, a propping agent in the high pressure liquid allows a crack to be hold up and to be a quick permeation channel for oil-gas steering drilling. The fracturing liquid used in the hydrofracturing method available for recovery of shale gas essentially includes water, sand and chemical additives (salts and some emulsifying agents), with the content of water and sand being 99% or more. An amount of the fracturing liquid used for exploitation of shale gas is very high, and the fracturing liquid of 4-5 million gallons (1 gallon corresponding to about 3.78 L) is required for each of the shale gas bore wells, to make shale rupture.
Presently, a metal pipe is commonly used for long distance delivery (about 10 miles) in recovery of shale oil & gas, having disadvantages of a high layout load, difficult layout on topographically complicated zones such as slope, ravine and pond, and more severely, soil pollution caused by water leakage from pipe couplings susceptible to cracking.
To solve the problems mentioned above, an objective of the present invention is to provide a fracturing liquid delivery hose for recovery of shale oil & gas and manufacturing method and co-extrusion mold thereof, where the hose of the present invention is more integral, anti-flexible, long in service life; but also has high resistance to high pressure, high delivering rate, convenient connection, desirable weather- and chemical-resistance, and is suitable for various topographies; in case of no service, it is flat, easily wound up and has low volume during storage and transportation.
The objective is achieved by the technical solutions as follows:
A method for manufacturing the fracturing liquid delivery hose for recovery of shale oil & gas, including the following steps:
(1) Extrusion of a cover layer bearing an adhesive layer: extruding the cover layer grains and adhesive grains by two extruders into a co-extrusion mold, and subjecting a coextruded laminate layer to cooling, pulling and squashing to give a flat tube i.e. the cover layer bearing the adhesive layer, where the adhesive layer has a thickness of 0.10-0.35 mm and the cover layer has a thickness of 0.5-4.0 mm;
(2) Extrusion of an inner lining bearing an adhesive layer: extruding the inner lining grains and adhesive grains by two extruders into a co-extrusion mold, and subjecting the coextruded laminate layer to cooling, pulling and squashing to give a flat tube i.e. the inner lining bearing the adhesive layer, where the adhesive layer has a thickness of 0.10-0.35 mm and the inner lining has a thickness of 0.5-4.0 mm;
(3) Separate treatment of the intermediates from Step (1) and Step (2) on the surface: immersing it into a solution for physical permeation prior to use, where the solution is formulated from a curing agent and solvent at a ratio of 10-30:70-90;
(4) Formation of an enhancement layer: weaving a tubular enhancement layer according to product design specifications;
(5) Bonding between the cover layer and the enhancement layer: pulling the surface-treated cover layer with the adhesive layer from Step (3) into the tubular enhancement layer, fixing at both ends, passing through a steam of 0.10-0.35 Mpa for 4-10 minutes, prior to cooling with air in place of steam while maintaining pressure to the desired temperature;
(6) Turnover: turning over the product from Step (5) to exchange its inner layer for the outer layer;
(7) Bonding between the inner lining and the enhancement layer: pulling the surface-treated inner lining with the adhesive layer from Step (3) into the product from
Step (6), fixing at both ends, passing through a steam of 0.10-0.35 Mpa for 4-10 minutes, prior to cooling with air in place of steam while maintaining pressure to the desired temperature.
In the method for manufacturing the fracturing liquid delivery hose for recovery of shale oil & gas, the TPU grains or TPU and PVC alloys are used in the cover layer described in Step (1), and the TPU grains or TPU/PVC alloys or PVC or PVC/butyronitrile are used in the inner lining described in Step (2), where in the TPU/PVC alloys, TPU:PVC=100:0-70; in the PVC/butyronitrile, PVC:butyronitrile=100:0-70; and in Step (1) and Step (2), the cover layer and inner lining grains are extruded at temperature of 150-210° C., and the adhesive grains are extruded at temperature of 140-175° C.
In the method for manufacturing the fracturing liquid delivery hose for recovery of shale oil & gas, a color concentrate is also added to the cover layer grains and the inner lining grains described in Step (1) and/or Step (2) at 100:(0.5-1.5) mass ratio of the cover layer grains or the inner lining grains to the color concentrate, and then stirred uniformly and dried.
In the method for manufacturing the fracturing liquid delivery hose for recovery of shale oil & gas, the enhancement layer described in Step (4) is woven from the Terylene filaments or Nylon filaments or aramid fibers or the blends of Terylene and nylon filaments or aramid fibers.
The method for manufacturing the fracturing liquid delivery hose for recovery of shale oil & gas further includes rolling pass on the surface after turnover.
The fracturing liquid delivery hose for recovery of shale oil & gas, manufactured in the method, is characterized in that it includes, from outer to inner: the cover layer, the enhancement layer and the inner lining, where bonding between the cover layer and the enhancement layer and between the enhancement layer and the inner lining are achieved by the adhesive layer respectively.
In the fracturing liquid delivery hose for recovery of shale oil & gas, the thickness is 0.5-4.0 mm for the cover layer, 1.5-5.0 mm for the enhancement layer, 0.5-4.0 mm for the inner lining and 0.10-0.35 mm for the adhesive layer.
In the fracturing liquid delivery hose for recovery of shale oil & gas, the enhancement layer woven from ends and picks is tubular.
In the fracturing liquid delivery hose for recovery of shale oil & gas, the copper wire is woven uniformly in axial direction on the enhancement layer for antistatic effect.
A co-extrusion mold, including: a housing equipped with a shaft therein; a distributor block, provided below the shaft, in the form of frustum for its lower part, where there is a gap between the shaft and the distributor block, the distributor block is fixedly connected to the housing having a first feed inlet connected to the cover layer or inner lining grain extruder, the first feed inlet penetrates through the housing and is connected fluidly to the gap between the shaft and the distributor block; a mold case provided outside the distributor block, where there is a gap between the mold case and the distributor block, the mold case is fixedly connected to the housing, the mold case has a second feed inlet connected to the adhesive extruder, the second feed inlet penetrates through the mold case and is connected fluidly to the gap between the mold case and the distributor block; and a clamping ring provided between the distributor block and the housing.
1. The fracturing liquid delivery hose for recovery of shale oil & gas according to the present invention includes from outer to inner: the cover layer, the enhancement layer and the inner lining, where the adhesive layer is used for bonding between the cover layer and enhancement layer and between the enhancement layer and the inner lining respectively, the cover layer and the inner lining may be designed for different materials, with the inner lining used with the materials having resistance to corrosion of the chemical media and oils and the cover layer used with the materials having resistance to weather, ozone, wear and piercing, thus allowing the advantages of various materials to maximize. As an embodiment of the present invention, TPU is used in both the cover layer and the inner lining which are bound to the enhancement layer by the adhesive agent by physical and chemical cross-linking, and the hose with peel strength up to 8 KN/M is more integral, remains strong bonding after long time service, significantly improving the flexibility and service life of the product. The process according the present invention is simple in operation, high in efficiency, high in productive capacity and low in investment.
2. The hose produced in the method of the present invention is light in weight, desirable in ductility, wear-resistant, corrosion-resistant, weather-resistant, but also may be connected by various standard fasteners, easily wound up, and easily assembled and disassembled. The turnover process is used for the hose according to the present invention, with length of more than 200 meters and inner diameters of 200 mm (8″), 250 mm (10″), 300 mm (12″), 400 mm (16″), 600 mm (24″) for various specifications.
3. In the present invention, the adhesive layer enables firm bonding between the cover layer and the enhancement layer and between the inner lining and the enhancement layer, leading to improved peel strength, more integrity of the hose and improved service life. In the present invention, the turnover process is carried out by laminating the cover layer and the adhesive layer by mechanical co-extrusion, immersing into the curing agent solution, pulling into the enhancement layer, bonding, turning over, rolling pass; and laminating the inner lining and the adhesive layer by co-extrusion, immersing the curing agent solution, pulling into the cover layer/enhancement layer and bonding at elevated temperature and pressure. The process is advantageous in that the cover layer and inner lining are designed by functions respectively and used with different materials, and the operation is easy, with high efficiency.
4. In the present invention, a special co-extrusion mold is designed with easy operation and high efficiency.
where, 1: housing, 2: shaft, 3: clamping ring, 4: distributor block, 5: mold case, 6: first feed inlet, 7: second feed inlet.
The fracturing liquid delivery hose for recovery of shale oil & gas includes from outer to inner: the cover layer, the enhancement layer and the inner lining, where bonding between the cover layer and the enhancement layer and between the enhancement layer and the inner lining were achieved by the adhesive layer respectively.
The thickness was 0.5 mm for the cover layer, 5.0 mm for the enhancement layer, 4.0 mm for the inner lining, and 0.35 mm for the adhesive layer.
The enhancement layer woven from ends and picks was tubular.
This embodiment was different from Embodiment 1 in that, the thickness was 4.0 mm for the cover layer, 1.0 mm for the enhancement layer, 4.0 mm for the inner lining, and 0.10 mm for the adhesive layer. The ends and picks were used with Nylon.
This embodiment was different from Embodiment 1 in that, the thickness was 2.5 mm for the cover layer, 3.5 mm for the enhancement layer, 2.5 mm for the inner lining and 0.25 mm for the adhesive layer. Moreover, two copper wires were uniformly distributed in axial direction in the enhancement layer. Addition of copper wires enabled antistatic effect.
This embodiment was different from the preceding embodiments in that, 8 copper wires were uniformly distributed in axial direction in the enhancement layer. It was also possible for 3 or 4 or 5 or 6 or 7 copper wires.
The method for manufacturing the fracturing liquid delivery hose for recovery of shale oil & gas includes the following steps:
(1) Extrusion of a cover layer bearing an adhesive layer: extruding the cover layer grains and adhesive grains by two extruders into a co-extrusion mold, and subjecting a coextruded laminate layer to cooling, pulling and squashing to give a flat tube i.e. the cover layer bearing the adhesive layer, where the adhesive layer had a thickness of 0.10-0.35 mm and the cover layer had a thickness of 0.5-4.0 mm;
(2) Extrusion of an inner lining bearing an adhesive layer: extruding the inner lining grains and adhesive grains by two extruders into a co-extrusion mold, and subjecting the coextruded laminate layer to cooling, pulling and squashing to give a flat tube i.e. the inner lining bearing the adhesive layer, where the adhesive layer had a thickness of 0.10-0.35 mm and the inner lining had a thickness of 0.5-4.0 mm;
(3) Separate treatment of the intermediates from Step (1) and Step (2) on the surface: immersing it into a solution for physical permeation prior to use, where the solution was formulated from a curing agent and ethyl acetate at a ratio of 10-30:70-90. In this embodiment, the adhesive grains used were TPU hot melt adhesive, with UB410B from Lubrizol Corp. used in this embodiment, and the curing agent was a material named diphenylmethane diisocyanate (MDI), with BASF M20S used in this embodiment. The curing agent (including an active NCO) may be bound firmly to the Terylene filaments also including hydroxy, by physical permeation and chemical reaction, at a certain temperature and pressure. Nylon includes aminoisocyanate as active site, which readily reacts with hydroxy and amino to give carbamate and urea structure, which would also firmly bond together by physical permeation and chemical reaction, at a certain temperature and pressure. The treated aramid fiber may include amino and isocyanate, which may also firmly bond by physicochemical reaction with the curing agent at a certain temperature and pressure.
(4) Formation of an enhancement layer: weaving the tubular enhancement layer according to product design specification:
(5) Bonding between the cover layer and the enhancement layer: pulling the surface-treated cover layer with the adhesive layer from Step (3) into the tubular enhancement layer, fixing at both ends, passing through a steam of 0.10-0.35 Mpa for 4-10 minutes, prior to cooling with air in place of steam while maintaining pressure to the desired temperature;
(6) Turnover: turning over the product from Step (5) to exchange its inner layer for the outer layer;
(7) Rolling pass on the product from Step (6).
(8) Bonding between the inner lining and the enhancement layer: pulling the surface-treated inner lining with the adhesive layer from Step (3) into the product from Step (7), fixing at both ends, passing through a steam of 0.10-0.35 Mpa for 4-10 minutes, prior to cooling with air in place of steam while maintaining pressure to a desired temperature.
In this embodiment, the cover layer and the inner lining were used with TPU (polyether type, R185A from Lubrizol Corp.).
This embodiment was different from Embodiment 5 in that, the cover layer was used with TPU of polyether type (R185A from Lubrizol Corp.), the inner lining was used with liner PVC (medical grade PVC from Shanghai Chloro-Alkali Chemical Co., Ltd.) or PVC/butyronitrile (medical grade PVC from Shanghai Chloro-Alkali Chemical Co., Ltd., LG830 from LG chemical as powdered PNBR, the mass ratio of PVC to powdered butyronitrile=100:0-70).
This embodiment was different from Embodiment 6 in that, the enhancement layer described in Step (4) was woven from Terylene filaments or Nylon or aramid fibers.
A co-extrusion mold, as shown in
In the co-extrusion mold described in Embodiment 8, the clamping ring 3 was provided between the distributor block and the housing.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2013104895374 | Oct 2013 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2013/086105 | 10/29/2013 | WO | 00 |