FRANGIBLE GUY WIRE OF AN AIRPORT MAST

Information

  • Patent Application
  • 20150345169
  • Publication Number
    20150345169
  • Date Filed
    May 22, 2015
    9 years ago
  • Date Published
    December 03, 2015
    9 years ago
Abstract
A frangible guy wire of an airport mast, which breaks on impact without presenting a hazard or causing critical damage to the object impacting with it. The main part of the length of the guy wire consists of a tube or tubular profile made of composite material, the proportions of the dimensions and materials of which have been selected in such a way that in the event of impact, the tube (4) or tubular profile will break by fracturing, that is, by breaking into pieces. The wall thickness of the tube or tubular profile is selected to be so thin that the desired fracturing is achieved.
Description

The object of the invention is a frangible guy wire of an airport mast, which breaks on impact without presenting a hazard or causing critical damage to the object impacting with it.


It is known that airport masts are manufactured of composite tubes, wherein fibreglass is used as the reinforcement. The aim is to produce a light-weight mast, which is easily frangible on impact, in order to prevent the mast from presenting a hazard or causing critical damage in the event of impact with an aircraft. The ICAO Design Manual, Part 6, specifies that the failure mode of the support structure should be fracture, windowing or bending. Fracturing guy wires, that is, breaking into pieces, is new invention as currently used known guyed mast's breaking mechanism is based on windowing. Steel or other guy wires are typically used, when the breaking mechanism of the guy is based on the specific break away points of the guy wire in the middle and in the base.


The aim of the invention is to provide an improved guy structure of composite material, based on fracture breaking mechanism, which means that the guy can be used, for example, for demanding applications requiring ICAO or FAA certification.


This aim is achieved on the basis of the characteristics disclosed in the accompanying claim 1. The dependent claims disclose preferred embodiments of the invention.


The guy wire according to the invention is, therefore, a tube or tubular profile made of composite material, which upon impact fragments into several components, and the mass of these components should be as low as possible, and their manner of release should not cause a secondary hazard the aircraft (e.g. to enter through the wind screen, fuselage, tail surfaces etc.), and not to present the kind of hazard, that guy wires made of steel or aluminium materials do.





The invention is illustrated in the following with reference to the accompanying drawings, in which:



FIG. 1 shows a perspective view of a guyed tubular mast, which can be used, for example, as an approach light mast or a weather mast for aircrafts,



FIGS. 1A to 1D show detailed enlargements of sections A to D of FIG. 1.



FIG. 2 shows, on a larger scale, the tubular part of the guy according to the invention, as seen from the side, and



FIG. 3 shows a section of FIG. 2 along line AA.





In FIG. 1, a tubular airport mast 1 is braced with guys 2 and 3. The guys consist of six composite tubes 4, the colouring of which alternates between red and white. According to ICAO regulations, the colouring of support structures having a length exceeding 2 m must be alternately red and white, divided into seven parts. In the embodiment shown, the colour of the seventh part is determined by the top of the mast, which is painted in one colour at the guy attachment point. Guys 2 and 3 also comprise a short wire 5 close to the base of the guy. The top ends of the guys are fixed to the mast 1 by means of a guy flange 6, to which the top ends of the guys attach with shackles 7. Between the composite tubes 4 are shackles 7, and the bottom end of the lower composite tube 4 is connected to the wire 5 by means of a shackle 7. The wires 5 are, in turn, connected to an anchor bolt 11 by means of guy tighteners 10. The anchor bolt is fixed to a guy anchor 8.



FIGS. 2 and 3 show in greater detail the composite tube 4 used in guys 2 and 3. The length of the composite tube 4 may vary according to need. However, the main part of the length of the guy consists of tubes 4 made of composite materials. A tubular profile (e.g. C-profile) may alternatively also be used. What is essential is that the materials and the proportions of the dimensions of the tube, or tubular profile, are selected in such a way that, on impact, it will break by shattering, that is, by breaking into pieces. In this case, secondary fragments are formed, the size and mass of which are sufficiently small not to cause critical damage to an aircraft in the event of impact. The shackle 7 and the fastening eye 12 are fixed to the ends of the composite tube 4 by means of end inserts 13, which do not have to become detached on impact, since the tube material itself fractures (breaks into pieces). The shackles 7 and the fastening eyes 12 may be replaced with other types of attachment means with which the composite tubes 4 can be connected in succession to form a continuous guy which withstands pulling.


The wall thickness of the tube or tubular profile must be sufficiently thin to bring about fracturing. The wall thickness is typically within the range 1-3 mm, preferably within the range 1.5-2.5 mm. The diameter of the tube 4 is typically within the range 20-40 mm, preferably within the range 20-30 mm. The composite materials may be a fibreglass reinforcement and a thermosetting resin. The amount of reinforcement in the composite material may be greater than 35% of the weight. Typically, the amount of reinforcement is within the range 35-80% of the weight, preferably within the range 60-80% of the weight. The tube or tube profile used for the guy can be manufactured by means of the pulltrusion, pullwinding, co-winding, filament winding or prepreg method.


The breaking mechanism of the guy tube is based on both profile geometry and material behaviour. By means of the guideline values and tests disclosed above, a person skilled in the art will be able to find the required proportions of the dimensions and ratios of material components to provide the desired fracturing.


As a thermosetting matrix may be used, for example, polyester, vinyl ester, polyurethane, epoxy, acrylic or phenol. The fibre reinforcement may be comprised of continuous or short fibres.


The airport mast 1 is also made of composite material by means of the pultrusion or pullwinding method. It has a tubular shape and the proportions of the dimensions and materials of the tube have been selected in such a way that, in the event of impact, the mast will also break by fracturing. Especially the wall thickness should be thin with respect to the diameter. Such dimensioning is possible when the mast is sufficiently braced with guy wires.

Claims
  • 1. A frangible guy of an airport mast, which breaks on impact without presenting a hazard or causing critical damage to the object impacting with it, characterised in that the main part of the length of the guy (2, 3) consists of a tube (4) or tubular profile made of composite material, the proportions of the dimensions and materials of which have been selected in such a way that in the event of impact, the tube (4) or tubular profile will break by fracturing, that is, by breaking into pieces.
  • 2. A guy wire as claimed in claim 1, characterised in that the wall thickness of the tube (4) or tubular profile is selected to be so thin that the desired fracturing is achieved.
  • 3. A guy wire as claimed in claim 1, characterised in that the composite materials are a fibreglass reinforcement and a thermoplastic matrix, and that the amount of fibreglass reinforcement is 35-80% by weight.
  • 4. A guy wire as claimed in claim 1, characterised in that each guy wire (2, 3) is comprised of at least six composite tubes (4) connected in succession by means of shackles (7) and fastening eyes (12) or similar attachment means.
  • 5. A guy wire as claimed in claim 1, characterised in that the tube (4) or tubular profile is manufactured by one of the following methods: the pultrusion, pullwinding, co-winding, filament winding or prepreg method.
  • 6. An airport mast made of composite material, characterised in that the mast (1) is supported by guy wires (2, 3) as claimed in claim 1, and that the tubular mast (1) is made of composite material and the proportions of the dimensions and materials of the tube are selected in such a way that, on impact, the mast will break by fracturing.