The instant invention relates to a free radical initiator system, and a high pressure, free radical polymerization process for producing a low density polyethylene polymer.
The use of peroxide initiators in high pressure free radical polymerization of ethylene and optionally at least one comonomer is generally known. As a general rule, peroxide initiators need to be stored at relatively low temperatures of less than 30° C. to −20° C. in order to prevent premature decomposition. For metering into the polymerization reactor by means of piston pumps and other injection equipment, the peroxide initiators are typically dissolved or diluted in a hydrocarbon solvent. However, the solubility of peroxide initiators are affected by pressure conditions and/or composition conditions experienced in the peroxide storage, and injection and metering systems. As a result, a phase separation, e.g. liquid-liquid phase separation or solid-liquid phase separation, may occur. The phase separation of peroxide/solvent mixture may interrupt its injection into the polymerization reactor or it may cause a non-uniform peroxide concentration. A stable initiator/solvent mixture having a uniform initiator concentration is an important requirement to achieve a stable high pressure free radical polymerization process and to avoid ethylene decomposition in high pressure low density polyethylene reactors.
U.S. Pat. No. 3,642,747 discloses the production of ethylene homopolymers or copolymers by polymerization of ethylene or of mixtures of major amounts of ethylene and minor amounts of other monomers at super-atmospheric pressure and elevated temperature using a polymerization initiator. It is characteristic of the process according to the invention that a 2-hydro-peroxy-2-isopropylphenylpropane is used as polymerization initiator.
U.S. Pat. No. 3,714,135 discloses the production of homopolymers or copolymers of ethylene by homopolymerization of ethylene or copolymerization of mixtures of ethylene and other monomers at super-atmospheric pressure and elevated temperature under the influence of a free radical generating polymerization initiator with or without a polymerization regulator. The initiator used is a mixture of (a) an initiator having a half-life of ten to 30 hours at 50° C., and (b) an initiator having a half-life of 0.2 to 10 hours at 50° C., the half-life at 50° C. of initiator (a) being at least twice as long as that of initiator (b).
U.S. Pat. No. 4,581,429 discloses a processes for free radical polymerization, in which it is possible to control the growth steps of the polymerization to produce relatively short chain length homopolymers and copolymers, including block and graft copolymers.
U.S. Pat. No. 4,777,230 discloses a process for the free radical polymerization of monomers derived from substituted or unsubstituted acrylic acid/methacrylic acid and esters thereof for the production of a polymer having a narrow molecular weight distribution and an average molecular weight of less than 4000. These polymers are produced by the solution polymerizing of said monomers wherein 20 to 40 percent by weight of the monomer composition is hydroxyalkyl acrylate or methacrylate in the presence of a solvent system suitable for high solids coating applications and in the presence of an initiating amount of a tertiary alkyl hydroperoxide and/or its derivatives having at least 5 carbons wherein the initiator and monomers, alone or in combination, are added continuously at a programmed rate wherein the rate of addition corresponds approximately to the rate of decomposition of said monomer and initiator.
U.S. Pat. No. 5,100,978 discloses polyethylene and copolymers of predominant amounts of ethylene and minor amounts of comonomers that are polymerizable with ethylene, obtainable by free radical polymerization of the monomers under from 1,500 to 5,000 bar and at from 40° C. to 250° C. by means of an initiator with virtually complete exclusion of oxygen in not less than n=3 polymerization stages.
U.S. Pat. No. 5,322,912 discloses a free radical polymerization process for the preparation of a thermoplastic resin or resins comprising heating a mixture of a free radical initiator, a stable free radical agent, and at least one polymerizable monomer compound to form a thermoplastic resin or resins with a high monomer to polymer conversion; cooling the mixture; optionally isolating the thermoplastic resin or resins; and optionally washing and drying thermoplastic resin or resins.
U.S. Pat. No. 6,407,191 discloses a free radical initiation polymerization process for the preparation of medium density ethylene polymers or copolymers, comprising reacting ethylene and optionally one or more comonomers at a high pressure, conveniently between 1600 and 4000 kg/cm2, and at temperatures of about 150-330° C. in a reactor system consisting of at least one autoclave reactor or of a combination of autoclave and tubular reactors, in the presence of free radical initiators and a carbonyl group containing compound.
U.S. Pat. No. 6,569,962 discloses a method for producing ethylene homopolymerizates and ethylene copolymerizates in tubular reactors in the presence of radical-forming initiators, oxygen thereunder and chain transfer agents, of which at least one comprises an aldehydic structure.
U.S. Pat. No. 6,727,326 discloses a method for the continuous production of ethylene homo-polymers and ethylene co-polymers in the presence of radical polymerization initiators and, optionally, molecular weight regulators in a tubular reactor with a hot water jacket and one or several reaction zones at pressures of 1000 to 4000 bar and temperatures of 120° C. to 350° C.
European Patent No. EP 0221610 discloses a storageable and/or transportable composition containing a peroxydicarbonate.
European Patent No. EP 0879224 discloses poly(monoperoxycarbonate) compounds and their use as free-radical initiators for polymerizing ethylenically unsaturated monomers, such as styrene, at faster production rates while retaining polymer molecular weight and polymer physical properties.
International Publication No. WO 02/051802 discloses a method to safely produce, handle and transport packaged organic peroxide formulations comprising a reactive phlegmatiser and to the use of such packaged material in polymerization and polymer modification processes, particularly the high-pressure (co)polymerization process of ethylene and/or the suspension (co)polymerization process of styrene.
International Publication No. WO 2004/052877 discloses a cyclic ketone peroxide formulation comprising one or more crystallizing cyclic ketone peroxides, one or more co-crystallizing compounds which solidify in said cyclic ketone peroxide formulation at a temperature above the crystallization temperature of the crystallizing cyclic ketone peroxide, and, optionally, one or more conventional phlegmatisers.
International Publication No. WO 2005/092966 discloses the use of a composition consisting of a crosslinking agent and an efflorescence-inhibiting agent, wherein said crosslinking agent is selected from a group formed by (a) an aromatic peroxide and (b) the combination of at least of one type aromatic peroxide and at least one type of aliphatic peroxide and said efflorescence-inhibiting agent being an alcohol. The efflorescence-inhibiting agent is embodied in the form of a sorbitol, mannitol, glycerol and a polyglycerol or the derivatives thereof.
Despite the research efforts in developing free radical initiator systems for high pressure (co)polymerization process, there is still a need for a stable initiator/solvent mixture having a uniform initiator concentration thereby facilitating a stable high pressure free radical (co)polymerization process and avoiding ethylene decomposition in such high pressure low density polyethylene reactors.
The instant invention is a free radical initiator system, and a high pressure, free radical polymerization process for producing a low density polyethylene polymer. The free radical initiator system according to instant invention includes at least one peroxide initiator, at least one hydrocarbon solvent, and at least one polar co-solvent. The high pressure, free radical polymerization process for producing a low density polyethylene polymer includes the steps of polymerizing ethylene and optionally at least one comonomer under high pressure conditions using a free radical initiator system comprising at least one peroxide initiator, at least one hydrocarbon solvent, and at least polar co-solvent.
For the purpose of illustrating the invention, there is shown in the drawings a form that is exemplary; it being understood, however, that this invention is not limited to the precise arrangements and instrumentalities shown.
The free radical initiator system according to instant invention includes at least one peroxide initiator, at least one hydrocarbon solvent, and at least one polar co-solvent.
The free radical initiator system includes at least one peroxide initiator. The peroxide initiator may, for example, be an organic peroxide. Exemplary organic peroxides include, but are not limited to, cyclic peroxides, diacyl peroxides, dialkyl peroxides, hydroperoxides, peroxycarbonates, peroxydicarbonates, peroxyesters, and peroxyketals.
Exemplary cyclic peroxides include, but are not limited to, 3,6,9-triethyl-3,6,9-trimethyl-1,4,7-triperoxonane. Such cyclic peroxides, for example, are commercially available under the tradename TRIGONOX 301, from Akzo Nobel, Arnhem, The Netherlands.
Exemplary diacyl peroxides include, but are not limited to, di(3,5,5-trimethylhexanoyl) peroxide. Such diacyl peroxides, for example, are commercially available under the tradename TRIGONOX 36, from Akzo Nobel, Arnhem, The Netherlands.
Exemplary dialkyl peroxides include, but are not limited to, 2,5-dimethyl-2,5-di(tert-butylperoxy)hexane; 2,5-dimethyl-2,5-di(tert-butylperoxy)hexyne-3; di-tert-amyl peroxide; di-tert-butyl peroxide; and tert-butyl cumyl peroxide. Such dialkyl peroxides, for example, are commercially available under the tradenames TRIGONOX 101, TRIGONOX 145, TRIGONOX 201, TRIGONOX B, and TRIGONOX T from Akzo Nobel, Arnhem, The Netherlands.
Exemplary hydroperoxides include, but are not limited to, tert-Amyl hydroperoxide; and 1,1,3,3-tetramethylbutyl hydroperoxide. Such hydroperoxides, for example, are commercially available under the tradenames TRIGONOX TAHP, and TRIGONOX TMBH, from Akzo Nobel, Arnhem, The Netherlands.
Exemplary peroxycarbonates include, but are not limited to, tert-butylperoxy 2-ethylhexyl carbonate; tert-amylperoxy 2-ethylhexyl carbonate; and tert-butylperoxy isopropyl carbonate. Such peroxycarbonates, for example, are commercially available under the tradenames TRIGONOX 117, TRIGONOX 131, and TRIGONOX BPIC, from Akzo Nobel, Arnhem, The Netherlands.
Exemplary peroxydicarbonates include, but are not limited to, di(2-ethylhexyl) peroxydicarbonates; and di-sec-butyl peroxydicarbonates. Such peroxydicarbonates, for example, are commercially available under the tradename TRIGONOX EHP, and TRIGONOX SBP, from Akzo Nobel, Arnhem, The Netherlands.
Exemplary peroxyesters include, but are not limited to, tert-amyl peroxy-2-ethylhexanoate; tert-amyl peroxyneodecanoate; tert-amyl peroxypivalate; tert-amyl peroxybenzoate; tert-amyl peroxyacetate; 2,5-dimethyl-2,5-di(2-ethylhexanoylperoxy)hexane; tert-butyl peroxy-2-ethylhexanoate; tert-butyl peroxyneodecanoate; tert-butyl peroxyneoheptanoate; tert-butyl peroxypivalate; tert-butyl peroxydiethylacetate; tert-butyl peroxyisobutyrate; 1,1,3,3-tetramethylbutyl peroxy-2-ethylhexanoate; 1,1,3,3-tetramethylbutyl peroxyneodecanoate; 1,1,3,3-tetramethylbutyl peroxypivalate; tert-butyl peroxy-3,5,5-trimethylhexanoate; cumyl peroxyneodecanoate; tert-butyl peroxybenzoate; and tert-butyl peroxyacetate. Such peroxyesters solvents, for example, are commercially available under the tradenames TRIGONOX 121; TRIGONOX 123; TRIGONOX 125; TRIGONOX 127; TRIGONOX 133; TRIGONOX 141; TRIGONOX 21; TRIGONOX 23; TRIGONOX 257; TRIGONOX 25; TRIGONOX 27; TRIGONOX 41; TRIGONOX 421; TRIGONOX 423; TRIGONOX 425;TRIGONOX 42; TRIGONOX 99; TRIGONOX C; and TRIGONOX F, from Akzo Nobel, Arnhem, The Netherlands.
Exemplary peroxyketals include, but are not limited to, 1,1-di(tert-amylperoxy)cyclohexane; 1,1-di(tert-butylperoxy)cyclohexane; 1,1-di(tert-butylperoxy)-3,3,5-trimethylcyclohexane; and 2,2-di(tert-butylperoxy)butane. Such peroxyketals, for example, are commercially available under the tradenames TRIGONOX 122, TRIGONOX 22, TRIGONOX 29, and TRIGONOX D, from Akzo Nobel, Arnhem, The Netherlands.
The free radical initiator system may, for example, include a mixture or combination of any of the above mentioned peroxide initiators.
The free radical initiator system may, for example, comprise less than 60 percent by weight of the peroxide initiator, based on the weight of the free radical initiator system. All individual values and subranges less than 60 weight percent are included herein and disclosed herein; for example, the free radical initiator system may comprise 1 to 40 percent by weight of the peroxide initiator, based on the weight of the free radical initiator system; or in the alternative, the free radical initiator system may comprise 4 to 40 percent by weight of the peroxide initiator, based on the weight of the free radical initiator system; or in the alternative, the free radical initiator system may comprise 4 to 30 percent by weight of the peroxide initiator, based on the weight of the free radical initiator system; or in the alternative, the free radical initiator system may comprise 10 to 40 percent by weight of the peroxide initiator, based on the weight of the free radical initiator system.
The free radical initiator system further includes at least one hydrocarbon solvent. The hydrocarbon solvent may, for example, be a C5 to C30 hydrocarbon solvent. Exemplary hydrocarbon solvents include, but are not limited to, mineral solvents, e.g. from mineral oils, normal paraffinic solvents, isoparaffinic solvents, cyclic solvents, and the like. The hydrocarbon solvents may, for example, be selected from the group consisting of n-octane, iso-octane (2,2,4-trimethylpentane), n-dodecane, iso-dodecane (2,2,4,6,6-pentamethylheptane), and other isoparaffinic solvents. Exemplary hydrocarbon solvents such as isoparaffinic solvents, for example, are commercially available under the tradenames ISOPAR C, ISPOAR E, and ISOPAR H, from ExxonMobil Company, USA. The free radical initiator system may, for example, comprise less than 99 percent by weight of the hydrocarbon solvent, based on the weight of the free radical initiator system. All individual values and subranges less than 99 weight percent are included herein and disclosed herein; for example, the free radical initiator system may comprise 5 to 95 percent by weight of the hydrocarbon solvent, based on the weight of the free radical initiator system; or in the alternative, the free radical initiator system may comprise 5 to 90 percent by weight of the hydrocarbon solvent, based on the weight of the free radical initiator system; or in the alternative, the free radical initiator system may comprise 10 to 90 percent by weight of the hydrocarbon solvent, based on the weight of the free radical initiator system.
The free radical initiator system further includes a polar a co-solvent. The polar co-solvent may be an alcohol co-solvent, for example, a C1 to C30 alcohol. Additionally, the alcohol functionality of the alcohol co-solvent may, for example, be mono-functional or multi-functional. Exemplary alcohols as a polar co-solvent include, but are not limited to, isopropanol (2-propanol), allylalcohol (1-pentanol), methanol, ethanol, propanol, butanol, 1,4-butanediol, combinations thereof, mixtures thereof, and the like. The free radical initiator system may, for example, comprise less than 80 percent by weight of the polar co-solvent, based on the weight of the free radical initiator system. All individual values and subranges less than 80 weight percent are included herein and disclosed herein; for example, the free radical initiator system may comprise 0.1 to 80 percent by weight of the polar co-solvent, based on the weight of the free radical initiator system; or in the alternative, the free radical initiator system may comprise 2 to 60 percent by weight of the polar co-solvent, based on the weight of the free radical initiator system; or in the alternative, the free radical initiator system may comprise 2 to 30 percent by weight of the polar co-solvent, based on the weight of the free radical initiator system; or in the alternative, the free radical initiator system may comprise 5 to 15 percent by weight of the polar co-solvent, based on the weight of the free radical initiator system.
In an alternative embodiment, the polar co-solvent may be an aldehyde. Such aldehydes are generally known to a person of skill in the art; for example, propionaldehyde may be use as a polar co-solvent. However, the reactivity potential of aldehydes as chain transfer agents should be taken into account when using such aldehydes polar co-solvents. Such reactivity potentials are generally known to a person of skill in the art.
In another alternative, the polar co-solvent may be a ketone. Such ketones are generally known to a person of skill in the art; for example, acetone or tetrahydrofuran may be use as polar co-solvents. However, the reactivity potential of ketones as chain transfer agents should be taken into account when using such ketones polar co-solvents. Such reactivity potentials are generally known to a person of skill in the art.
The free radical initiator system according to instant invention may further include a chain transfer agent. Such chain transfer agents are generally known to a person of skill in the art, and they include, but are not limited to, propane, isobutane, acetone, propylene, isopropanol, butene-1, propionaldehyde, and methyl ethyl ketone (“MEK”). In the alternative, such chain transfer agent may be charged into the reactor via a separate inlet port. In another alternative, such chain transfer agents may be mixed with ethylene, pressurized, and then charged into the reactor.
In production, the peroxide initiator may initially be dissolved or diluted in a hydrocarbon solvent, and then the polar co-solvent may be added to the peroxide initiator/hydrocarbon solvent mixture prior to the metering of the free radical initiator system into the polymerization reactor. In the alternative, the peroxide initiator may initially be dissolved or diluted in a hydrocarbon solvent, and then the polar co-solvent may be added to the peroxide initiator/hydrocarbon solvent mixture immediately prior to the metering of the free radical initiator system into the polymerization reactor. In another alternative, the peroxide initiator may be dissolved in the hydrocarbon solvent in the presence of the polar co-solvent.
The high pressure, free radical (co)polymerization process for producing a low density polyethylene polymer includes the steps of polymerizing ethylene and optionally at least one comonomer under high pressure conditions using a free radical initiator system comprising at least one peroxide initiator, at least one hydrocarbon solvent, and at least one polar co-solvent. The term (co)polymerization, as used herein, refers to both polymerization and copolymerization of ethylene.
The high pressure (co)polymerization process is generally known in the art. Generally the (co)polymerization process involves the free radical polymerization of ethylene gas in the presence of a liquid hydrocarbon medium containing organic peroxide initiators. The (co)polymerization process is generally conducted at elevated temperatures and pressures. The (co)polymerization may be carried out in either a batch-wise process or continuous manner. The (co)polymerization reaction may be carried out in a tubular reactor, an autoclave reactor, or a combination of a tubular reactor and an autoclave reactor. Such reactors are generally known to a person of skill in the art. For example, a tubular reactor may have a diameter to the length ratio of 1:14,000. The tube is typically surrounded by a jacket-tube for reception of a heat transfer medium. The jacket-tube itself may be subdivided into multiple zones operable independently of one another. At the end of the reaction tube, there is a valve which serves to control the pressure in the polymerization chamber, and to discharge the reaction product. Following this valve, there are typically a conventional high pressure separator and a conventional low pressure separator for separating the polymer obtained from unpolymerized substances, i.e., mainly from the portion of the monomers which have not been involved in the (co)polymerization.
In a high pressure (co)polymerization process, ethylene may, for example, be pressurized in a primary compressor and a secondary compressor, and then fed into the reactor. A free radical initiator system comprising at least one peroxide initiator, at least one hydrocarbon solvent, and at least one polar co-solvent is also pressurized, and then fed into the reactor. The free radical initiator system may further include a chain transfer agent; or in the alternative, a chain transfer agent may individually be pressurized and fed into the reactor. The (co)polymerization reaction is conducted at elevated temperatures and pressures. When the (co)polymerization reaction is completed, or at a desired suitable percent conversion prior to completion, the (co)polymerization reaction may be quenched or terminated by reducing the reaction temperature. For example, the (co)polymerization reaction may be terminated by reducing the processing temperature to below about 100° C.; or in the alternative, the (co)polymerization reaction may be terminated by reducing the processing temperature to below about 40° C., although the exact temperature depends upon the specific reactants involved. Following completion or termination of the reaction, the resultant polymer can be optionally separated from the reaction mixture, washed and dried. Subsequent processing of the polyethylene homopolymer or copolymer can then be conducted.
The (co)polymerization pressure is typically in the range of about 500 to about 5000 bars. All individual values and subranges in the range of about 500 to about 5000 bars are included herein and disclosed herein; for example, (co)polymerization pressure is in the range of about 1200 to about 4000 bars; or in the alternative, (co)polymerization pressure is in the range of about 1500 to about 3500 bars. The (co)polymerization temperature is typically in the range of about 70° C. to about 380° C. All individual values and subranges in the range of about 70° C. to about 370° C. are included herein and disclosed herein; for example, (co)polymerization temperature is in the range of about 100° C. to about 365° C.; or in the alternative, (co)polymerization temperature is in the range of about 120° C. to about 360° C.
Ethylene homopolymers or copolymers may be produced via a high pressure polymerization process. The method of the present invention can be used for both the homopolymerization of ethylene and the copolymerization of ethylene with one or more other monomers, provided that these monomers are copolymerizable with ethylene under free-radical conditions under high pressure. Examples of suitable copolymerizable monomers are α, β-unsaturated C3-C8-carboxylic acids, in particular maleic acid, fumaric acid, itaconic acid, acrylic acid, methacrylic acid and crotonic acid derivates of the α, β-unsaturated C3-C8-carboxylic acids, e.g. unsaturated C3-C15-carboxylic acid esters, in particular ester of C1-C6-alkanols, or anhydrides, in particular methyl methacrylate, ethyl methacrylate, n-butyl methacrylate, ter-butyl methacrylate, methyl acrylate, ethyl acrylate n-butyl acrylate, 2-ethylhexyl acrylate, tert-butyl acrylate, methacrylic anhydride, maleic anhydride or itaconic anhydride, and α-olefins such as propene, 1-butene, 1-pentene, 1-hexene, 1-octene, or 1-decene. Vinyl carboxylates, for example vinyl acetate, can also be used as comonomers. Exemplary comonomers include, but are not limited to, n-butyl acrylate, acrylic acid and methacrylic acid. The proportion of comonomer or comonomers in the reaction mixture may be from 1 to 45 percent by weight, based on the weight of ethylene. All individual values and subranges in the range 1 to 45 weight percent are included herein and disclosed herein; for example, the proportion of comonomer or comonomers in the reaction mixture may be from 1 to 30 percent by weight, based on the weight of ethylene; or in the alternative, the proportion of comonomer or comonomers in the reaction mixture may be from 1 to 20 percent by weight, based on the weight of ethylene. In the case of copolymerization, the further comonomers are preferably fed in at a plurality of points along the reactor.
The (co)polymerization process according to instant invention may be employed to produce a low density polyethylene polymer. Such polymers may be fabricated into a variety of articles e.g. films and molded articles. Different methods may be employed to make such films and molded articles. For example, a film according to the instant invention may be formed via blown film process or cast film process. A molded article according to instant invention may be formed via injection molding process or extrusion coating process. Such methods are generally known in the art.
The present invention may be embodied in other forms without departing from the spirit and the essential attributes thereof, and, accordingly, reference should be made to the appended claims, rather than to the foregoing specification, as indicating the scope of the invention.
The following examples illustrate the present invention but are not intended to limit the scope of the invention. The examples of the instant invention demonstrate that the free radical initiator system of the instant invention provides improved phase separation properties.
The high pressure solubility tests were carried out in a high pressure optical cell, as shown in
The cell was filled with the mixture of components and pressurized from 0 to 3500 bar at a constant temperature. The sample was agitated with a magnetic stirred while both pressure and temperature were recorded online. The phase separation behavior of the liquid was recorded in real time using a video camera.
(1) n-octane; (2) iso-octane (2,2,4-trimethylpentane); (3) n-dodecane; (4) iso-dodecane (2,2,4,6,6-pentamethylheptane); and (5) Isopar® E.
(1) isopropanol (2-propanol); and (2) allylalcohol (1-pentanol)
Samples solution 1-16 were prepared according to the formulations listed on Table I, and then tested for high pressure solubility according to the above-described Experimental Setup and Experimental Protocol in Experiments 1-6. The results are shown below and in
Sample solutions 1 (comparative) and 2 (inventive), according to the formulations listed in Table I, were prepared and tested for high pressure solubility according to the above-described Experimental Setup and Experimental Protocol. The liquid-liquid phase separation is shown as a function of temperature and pressure for comparative sample solution 1(containing 20 weight percent Luperox JWEB50 and 80 weight percent iso-octane), and inventive sample solution 2 (containing 20 weight percent Luperox JWEB50 and 10 weight percent isopropanol and 70 weight percent iso-octane) in
Sample solutions 3-7, according to formulations listed in Table I, were prepared and tested for high pressure solubility according to the above-described Experimental Setup and Experimental Protocol. The liquid-liquid phase separation is shown as a function of temperature and pressure for comparative sample solution 3 (containing 40 weight percent Luperox JWEB50 and 60 weight percent n-octane), inventive sample solution 4 (containing 40 weight percent Luperox JWEB50 and 5 weight percent isopropanol and 55 weight percent n-octane), and inventive sample solution 5 (containing 40 weight percent Luperox JWEB50 and 10 weight percent isopropanol and 50 weight percent n-octane) in
Sample solutions 8-9, according to formulations listed in Table I, were prepared and tested for high pressure solubility according to the above-described Experimental Setup and Experimental Protocol. The liquid-liquid phase separation is shown as a function of temperature and pressure for comparative sample solution 8 (containing 40 weight percent Luperox JWEB50 and 60 weight percent Isopar E), and inventive sample solution 9 (containing 40 weight percent Luperox JWEB50 and 5 weight percent isopropanol and 55 weight percent Isopar E) in
Sample solutions 8-9, according to formulations listed in Table I, were prepared and tested for high pressure solubility according to the above-described Experimental Setup and Experimental Protocol. The liquid-liquid phase separation is shown as a function of temperature and pressure for comparative sample solution 6 (containing 100 weight percent n-octane), comparative sample solution 8 (containing 40 weight percent Luperox JWEB50 and 60 weight percent Isopar-E), inventive sample solution 10 (containing 40 weight percent Luperox JWEB50 and 10 weight percent 1-pentanol and 50 weight percent n-octane) in
Sample solutions 11-12, according to formulations listed in Table I, were prepared and tested for high pressure solubility according to the above-described Experimental Setup and Experimental Protocol. The liquid-liquid phase separation is shown as a function of temperature and pressure for comparative sample solution 11 (containing 20 weight percent TBPA and 80 weight percent iso-dodecane), and inventive sample solution 12 (containing 20 weight percent TBPA and 10 weight percent isopropanol and 70 weight percent iso-dodecane) in
Sample solutions 11-12, according to formulations listed in Table I, were prepared and tested for high pressure solubility according to the above-described Experimental Setup and Experimental Protocol. The liquid-liquid phase separation is shown as a function of temperature and pressure for comparative sample solutions 11, 13 and 14 (containing 20 weight percent, 35 weight percent, and 50 weight percent TBPA in iso-dodecane, respectively), and for inventive sample solutions 12, 15 and 16 (containing 20 weight percent, 35 weight percent, and 45 weight percent TBPA with 10 weight percent isopropanol in iso-dodecane, respectively) in
Referring to
This application is a non-provisional application claiming priority from the U.S. Provisional Patent Application No. 60/905,999, filed on Mar. 9, 2007 entitled “FREE RADICAL INITIATOR SYSTEM AND A HIGH PRESSURE, FREE RADICAL POLYMERIZATION PROCESS FOR PRODUCING A LOW DENSITY POLYETHYLENE POLYMER” the teachings of which are incorporated by reference herein as if reproduced in full hereinbelow.
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/US2008/053677 | 2/12/2008 | WO | 00 | 9/3/2009 |
Number | Date | Country | |
---|---|---|---|
60905999 | Mar 2007 | US |