Friction material containing BT resin dust

Abstract

A friction material containing dust having bismaleimidetriazine as a major ingredient. The dust is effective when contained in amount of 1 to 20 wt. % in the friction material. Compared with conventional friction material containing cashew dust, the generation rate of noise is reduced drastically, while the frictional performance is equivalent or higher.

Description

BACKGROUND OF THE INVENTION

The present invention relates to a friction material for use in brakes and etc. of cars and others, wherein, in particular, the noises generating on braking are prevented.

The conventional mechanical brake rubs solid members one another by contacting them, thus the noises generate inevitably due to the vibrations of them. Today, it is difficult to completely prevent such noises, and we are coping to decrease the noises by such methods that a material absorbing the vibration is formulated in one of opposing brake pads, that an elastomer with good viscoelastic characteristics is allowed to intervene on the way of vibration transfer system, and the like. However, it cannot still be said to be sufficient.

Here, the inventors have investigated the solution thereof and, paying an attention to the dust contained in the friction material of brake for following purposes, the investigations have been made further.

Namely, the main functions of organic dust are 1 improved brake feeling, 2 increased efficacy, 3 prevention of noises, and others. Types of dust include now rubber dust, cashew dust and modified articles thereof as shown in U.S. Pat. Nos. 4,310,452 and 4,886,107. The dusts are formed of particles of material of regulated size, after having vulcanized or cured the material of the dusts. The dusts are incorporated in an amount of 2-10 wt. % into the material from which disk brake pads are formed which include fiber reinforcing materials, inorganic fillers and thermosetting resin binder.

On the other hand, with respect to the environment surrounding the brake, the loading exerted on the brake pad is in a tendency to become increasingly severe, resulting from that the rigidity tends to decrease structurally from lightening in weight of car body accompanying with large-sized cars and that the brake system is also progressing toward miniaturization and lightening as well.

Hence, the requirement for the heat resistance of brake pad is increasing, but, with said rubber dust, the purpose is attained by no means and, with cashew dust, it has been difficult to effect the stabilized function over a long period of time, though the heat resistance thereof is higher than that of rubber dust. Namely, the noises generating with pad containing cashew dust have a strong tendency to generate more frequently as the braking is repeated. This is because of that, with increasing heat history due to the repetition of braking, the temperature of brake pad increases gradually and ends up to become over the heat decomposition temperature (about 290.degree. C.) of cashew dust at last, thus exceeding the heat-resistant limit of cashew dust.

As a result of further investigations in view of the points aforementioned, a friction material with excellent heat resistance having prevented the generation of noises has been developed according to the invention.

SUMMARY OF THE INVENTION

The invention is characterized by containing dust having bismaleimidetriazine resin as a major ingredient, the content of said dust being only necessary to be 1 to 20 wt. %.

BRIEF DESCRIPTION OF THE DRAWING

FIG. 1 is a column diagram showing the result of brake noise test.

DETAILED DESCRIPTION OF THE INVENTION

The heat resistance and the residual carbon rate after the heat decomposition due to braking were compared between the bismaleimidetriazine (hereinafter referred to as BT resin) and conventional cashew dust as shown in Table 1.

TABLE 1______________________________________ Heat resist- Residual carbonDust ance (.degree.C.) rate (%)______________________________________BT resin ca. 390 70-75Cashew dust ca. 290 50______________________________________

As shown, since the heat decomposition point (heat resistance) of BT resin is as higher as about 100.degree. C. over cashew dust, the available temperature range is broader, thus providing a characteristic of broader application range as a friction material. Moreover, since the residual amount of carbon after heat decomposition is also higher, that is, since the existing amount of thermally stable carbon is higher, the BT resin has an advantage that the change in the frictional characteristics including noise property decreases.

Furthermore, the content of dust having said BT resin as a major ingredient in the friction material is effective in amount of 1 to 20 wt. %, but, more preferably, 3 to 8 wt. % are better.

As the binders, thermosetting resins such as phenol resin and polyimide resin can be used and they are preferable to be contained in a proportion of 5 to 20 wt. % in overall components of friction material. As the reinforcing materials, one kind or not less than two kinds of metal fibers such as steel and copper, organic fibers such as Aramid and acrylic and inorganic fibers such as glass and carbon can be used in combination. The optimal proportion thereof is 10 to 40 wt. % in overall components of friction material.

Moreover, as the inorganic fillers, those having a grinding effect such as zircon sand, alumina, silica and magnesia, those having a lubricating effect such as graphite and molybdenum disulfide those having a noise-reducing effect such as vermiculite and mica and those having an extending effect such as barium sulfate, calcium carbonate and calcium silicate can be used in combination. They may be contained in a proportion of 40 to 75 wt. % in overall components of friction material.

In following, explanation will be made about the examples of the invention.

EXAMPLE

The inventive friction materials and the comparative friction material comprising formulation compositions shown in Table 2 were produced. The physical properties of these friction materials are shown in Table 3.

TABLE 2__________________________________________________________________________ Friction material no. Inventive Inventive Inventive Inventive ComparativeFormulating friction friction friction friction frictionMaterial material 1 material 2 material 3 material 4 material 5__________________________________________________________________________Binder 8 8 8 8 8Phenol resinDustCashew dust -- -- -- -- 5Rubber dustBT resin dust 2 5 10 15 --Inorganic fillerBarium sulfate 15 15 15 15 15Zircon sand 10 10 10 10 10Graphite 12 12 12 12 12Vermiculite 23 20 15 10 20Reinforcing materialCopper fibers 25 25 25 25 25Aramid fibers 5 5 5 5 5__________________________________________________________________________ *ALL VALUES ARE EXPRESSED BY WEIGHT TABLE 3__________________________________________________________________________ Inventive Inventive Inventive Inventive ComparativePhysical friction friction friction friction frictionproperty material 1 material 2 material 3 material 4 material 5__________________________________________________________________________Hardness (HRS) 100 95 90 80 95Specific gravity (g/cm.sup.3) 3.2 3.1 3.0 2.9 3.1Porosity (%) 8 10 11 12 10__________________________________________________________________________

The friction materials as above were applied to brake pad. Table 4 shows the results of friction performance test carried out according to JASO 1201 and further FIG. 1 shows the results of noise test.

TABLE 4______________________________________Change in friction coefficient Second efficacy Amount State ofFriction Rub- (km/h) of wear frictionmaterial bing 50 100 125 Fade (mm) surface______________________________________Inventive 0.48 0.47 0.44 0.44 0.39 0.52 Normalfrictionmaterial 1Inventive 0.50 0.48 0.45 0.45 0.38 0.40 Normalfrictionmaterial 2Inventive 0.53 0.48 0.45 0.44 0.34 0.48 Normalfrictionmaterial 3Inventive 0.55 0.50 0.45 0.45 0.30 0.60 Normalfrictionmaterial 4Compar- 0.50 0.48 0.45 0.45 0.28 0.70 Normalativefrictionmaterial 5______________________________________

From Table 4, it can be seen that the brake pads using the inventive friction materials have equivalent or higher frictional performance over the pad using conventional comparative friction material. Moreover, according to FIG. 1, it is seen that the generation rate of noises of brakes using the inventive friction materials is obviously decreased compared with that of conventional brake.

As described, in accordance with the invention, conspicuous effects are exerted in that it is possible to drastically suppress the generation of noises on braking over the past without decreasing the frictional performance of friction material, and the like.

Claims

1. A friction material having heat-resistant properties, comprising:

from 10-40 wt. % of reinforcing fiber, from 40-75 wt. % of inorganic filler, from 1-20 wt. % of BT resin dust which modifies the frictional properties of the friction material, and from 5-20 wt. % of a thermosetting phenolic resin binder which binds the components of the friction material.

2. The friction material of claim 1, which contains from 3 to 8 wt. % of said dust.