The present invention relates to a rotor coil for a revolving armature and the manufacturing method thereof.
In the rotor coil of a variable speed generator motor used in a pumped storage system, the strand coils extending from each of a plurality of core slots (Roebel-transposed (coil braided) coil conductors) are welded to the solid coils that form the coil end. A plurality of solid coils, provided at the coil end around the axis of the rotor, is supported and secured by tightly fastening with the binding wires that are wound around the solid coils (for example, see Japanese Patent No. 2529953).
In such a rotor coil, to prevent the coil end from being displaced in the centrifuge direction by the centrifugal force generated during the operation of a power generator, the coil end is made of solid coils of high mechanical strength and is supported and secured strongly by binding wires. On the other hand, Roebel-transposed strand coils are used in a core slot to reduce a circulating current loss. The rotor coil having this configuration therefore increases durability.
Welding between the solid coils and the strand coils in a conventional rotor coil is performed by means of Tungsten Inert Gas (TIG) welding (for example, Japanese Patent No. 2529953). More specifically, the butt joint between the solid coils and the strand coils is formed by multi-pass welding while measuring the interlayer temperature. The problem with such TIG welding is that it depends largely on the worker's professional skill and there is a variation in quality with the result that the yield rate is low. In addition, multi-pass layer welding requires more work time. Another problem is that, because there are great many TIG welding points in a conventional rotor coil, the work to weld the solid coils and the strand coils is extremely complicated.
When a variable speed generator motor, in which the solid coils are supported and secured by binding wires, is started and stopped repeatedly, stress is generated in the welded joint between the solid coils and the strand coils due to thermal expansion and contraction. Therefore, considering that there is an increasing need today for a large-capacity, high-voltage variable speed generator motor, more reliability is desired for the welded joint between the solid coils and the strand coils than before.
In view of the foregoing, it is an object of the present invention to provide a rotor coil for a revolving armature and a manufacturing method thereof for forming a more reliable welded joint between the solid coils and the strand coils in a simpler manner than before.
To solve the problems described above, a rotor coil for a revolving armature according to an embodiment of the present invention is characterized in that the end of the solid coils at the coil end and the end of the strand coils extending from within the core slots are welded by friction stir welding.
A manufacturing method of a rotor coil for a revolving armature according to an embodiment of the present invention, which solves the problems described above, is a manufacturing method of a rotor coil for a revolving armature in which the end of a solid coil at the coil end and the end of a strand coil extending from the core slot are welded. The method includes the step of forming the end of the solid coil and the end of the strand coil in such a way that the butt joint between the end of the solid coil and the end of the strand coil is tilted to a width direction of the solid coil; and the step of performing friction stir welding for the butt joint where the end of the solid coil and the end of the strand coil are butted against each other.
The manufacturing method of a rotor coil for a revolving armature according to the embodiment of the present invention further includes the step, before the step of performing friction stir welding for the butt joint, of soldering the end of the strand coil to integrate element wires into one unit.
The present invention can provide a rotor coil for a revolving armature and a manufacturing method thereof for forming a more reliable welded joint between solid coils and strand coils in a simpler manner than before.
Other objects, features and advantages of the invention will become apparent from the following description of the embodiments of the invention taken in conjunction with the accompanying drawings.
A rotor coil for a revolving armature (hereinafter simply called “rotor coil”) according to an embodiment of the present invention is described in detail below with reference to the drawings as necessary.
As will be described later, the rotor coil of the present invention is characterized in that the end of solid coils and the end of strand coils are welded by friction stir welding. The following first describes the general configuration of a variable speed generator motor used, for example, in a pumped storage system. After that, a rotor coil according to this embodiment, which is applied to the variable speed generator motor, is described.
As shown in
The rotor 1 includes an almost cylindrical rotor core 11 configured by laminating a plurality of almost circular plates in the extending direction of the axis of rotation 3.
The rotor core 11 has a plurality of equally-spaced, groove-like core slots 12 formed along its periphery. Each of these core slots 12 is formed in the extending direction of the axis of rotation 3 in the shape of a long groove. In the core slot 12, an outer circumference strand coil 13a and an inner circumference strand coil 13b are extended along the longitudinal direction. The outer circumference strand coil 13a and the inner circumference strand coil 13b are Roebel-transposed, or coil-braided, to reduce losses. The inner circumference strand coil 13b is arranged nearer to the axis of rotation 3 in the core slot 12, and the outer circumference strand coil 13a is arranged in the upper side (outer side in the radial direction of the rotor 1) of the inner circumference strand coil 13b.
The outer circumference strand coil 13a and the inner circumference strand coil 13b, as well as an outer circumference solid coil 14a and an inner circumference solid coil 14b that will be described later, constitute a rotor coil 10 in this embodiment.
In
As shown in
Each of the outer circumference strand coil 13a and the inner circumference strand coil 13b, extending from within the core slot 12 of the rotor core 11, forms an end near the exit of the core slot 12 on the top face of the rotor core 11 (or on the bottom face of the rotor core 11 at the lower coil end not shown). The ends of the outer circumference strand coil 13a and the inner circumference strand coil 13b are welded, respectively, to the ends of the outer circumference solid coil 14a and the inner circumference solid coil 14b by friction stir welding. Friction stir welding will be described in detail later.
As described above, a plurality of inner circumference solid coils 14b is arranged so that they each correspond to the inner circumference strand coils 13b. At the same time, the inner circumference solid coils 14b are arranged on the outer circumference face of the solid coil holding unit 152 of the clamping ring 15 via a cushioning material 16b as shown in
As shown in
As described above, a plurality of outer circumference solid coils 14a is arranged so that they each correspond to the outer circumference strand coils 13a. At the same time, the inner circumference solid coils 14b are arranged on the upper side (radially outer side of the rotor) of the binding wires 18b, which are wound around the inner circumference solid coils 14b, via an insulating layer 17a as shown in
As shown in
Next, the following describes the welded joint between the outer circumference strand coil 13a and the outer circumference solid coil 14a and the welded joint between the inner circumference strand coil 13b and the inner circumference solid coil 14b. In
Referring to
As shown in
The strand coil 13 in this embodiment is configured by braiding a plurality of rectangular cross-section wires of oxygen free high conductivity copper as shown in
It is desirable that the butt joint between the end of the solid coil 14 and the end of the strand coil 13 in this embodiment be formed in such a manner that the butt joint is tilted at a predetermined angle of θ1 to the width direction W1 of the solid coil 14. The end of the solid coil 14 and the end of the strand coil 13 are welded by friction stir welding described below.
Next, with reference to
In
Next,
As shown in
As described above, when welding the butt joint 19 (see
A tool 120 shown in
First, in the manufacturing method of the rotor coil 10 in this embodiment, it is desirable that, as described above, the butt joint 19 (see
Next, in the manufacturing method of the rotor coil 10 in this embodiment, friction stir welding is performed for the butt joint 19 using the tool 20 (see
The strand coil 13 and the solid coil 14, which have their ends butted against each other, are fixed by tightly holding them between the upper pressing plate 21a and the lower pressing plate 21b, provided at the both end edges in the longitudinal direction, and by pressing their end edges.
After that, in the manufacturing method of the rotor coil 10 in this embodiment, friction stir welding is performed in such a manner that the tool 20 enters the butt joint 19 from the side, where the strand coil 13 arranged in the advancing side (AS) is at an acute angle of θ2 at the end, as shown in
At this time, the tool 20, which is pushed against a predetermined position on the upper pressing plate 21a on an extension of the butt joint 19, enters the butt joint 19 from the side of the upper pressing plate 21a. After the butt joint 19 is welded, the tool 20 advances to the lower pressing plate 21b and then leaves the lower pressing plate 21b. This welding method prevents a mark (hole) of removal of the tool 20 from being formed in the welded joint between the strand coil 13 and the solid coil 14.
In the manufacturing method of the rotor coil 10 in this embodiment, the tool 20 (see
The welded joint between the strand coil 13 the solid coil 14, welded by friction stir welding as described above, is arranged as shown in
The production method of the rotor coil 10 in this embodiment described above achieves the following effect.
The problem with a conventional rotor coil (for example, see Japanese Patent No. 2529953) is a decrease in mechanical strength in a heal-affected portion formed by TIG welding and an effect of a defect within a welded joint. More specifically, a solid coil supported and secured by binding wires in a conventional rotor coil. Therefore, when a variable speed generator motor is started and stopped repeatedly, thermal stress is generated in a welded joint with the result that the durability (reliability) of a welded joint becomes insufficient.
In contrast, a welded joint between the solid coil 14 and the strand coil 13 is formed by friction stir welding in this embodiment, meaning that a defect within a welded joint and a range of a thermal affected portion are significantly smaller than those formed by TIG welding. This embodiment significantly increases durability (reliability) of a welded joint. More specifically, this embodiment significantly increases tensile strength in a welded joint.
According to this embodiment, a butt joint between the end of the solid coil 14 and the end of the strand coil 13 is tilted and, at the same time, friction stir welding is performed for this butt joint. This configuration further increases mechanical strength in a welded joint. Next,
When the butt joint 19b between the strand coil 13 and the solid coil 14 is formed in a way in which the butt joint 19b runs along the width (W1) direction of the solid coil 14 (vertical to the end edge of the solid coil 14) as shown in
In contrast, when the butt joint 19a is formed in such a manner that the butt joint 19a is tilted with respect to the width W1 direction of the solid coil 14 as shown in
Note that the method described below can prevent the tensile strength of the welded joint from being decreased even when friction stir welding is performed for the butt joint 19b such as the one shown in
Conventional welding (for example, TIG welding) involves large quality-variations and high defect-generation rates. On the other hand, the method in this embodiment, which does not depend largely on the worker's professional skill, features small quality-variations and low defect-generation rate.
This embodiment ensures a reduction in the defect generation rate by performing friction stir welding for the butt joint 19 with the strand coil 13 arranged in the advancing side (AS) and with the solid coil 14 arranged in the retreating side (RS). Next,
As shown in
In addition, as compared to a conventional method in which multi-layer welding is performed while measuring each interlayer temperature, the welded joint between the solid coil 14 and the strand coil 13 can be formed very easily in this embodiment using one-pass welding for each of both sides. “One-pass welding” refers to the friction stir welding process for one of the sides of a butt joint. Welding is completed when the friction stir welding processing is performed for both the front side and the reverse side.
Welding deformation is not generated easily in this embodiment as in conventional welding (for example, TIG welding). Therefore, high-accuracy mold casting is possible when an insulator is formed in a coil such as the strand coil 13.
As compared to conventional welding (for example, TIG welding), this embodiment ensures an improved working environment and a reduced running cost when a welded joint is formed.
While the embodiment of the present invention has been described, the present invention is not limited to the embodiment described above but may be implemented in various forms.
In the embodiment described above, the rotor coil 10 has been described on the assumption that the rotor coil 10 is used in a variable speed generator motor used in a reversible pumped system. However, the present invention is not limited to this type of coil but may be applied widely to a rotor coil for a revolving armature that has the welded joint 22 between the supported and secured solid coil 14a, 14b and the strand coil 13a, 13b.
In the embodiment described above, though the rotor coil 10 is described that has the welded joint 22 between the solid coil 14a, 14b, supported and secured by the binding wires 18a, 18b, and the strand coil 13a, 13b, the present invention is applicable widely to a rotor coil that has the welded joint 22 between the solid coil 14a, 14b, supported and secured by other joining means such as a bolt, and the strand coil 13a, 13b.
In the embodiment described above, though the rotor coil 10 is described that has the welded joint 22 between the end of the solid coil 14a, 14b, which is the coil end, and the strand coil 13a, 13b extending from within the core slot 12, that is, a rotor coil whose welded joint 22 is formed outside the core slot 12, the present invention is applicable also to a rotor coil in which the welded joint 22 is formed near to the coil end and within the core slot 12.
The present invention is applicable not only to an embodiment in which the welded joint 22 (butt joint 19) between the solid coil 14 and the strand coil 13 is tilted. The present invention of course includes an embodiment in which friction stir welding is performed without tilting the welded joint 22 (butt joint 19).
It should be further understood by those skilled in the art that although the foregoing description has been made on embodiments of the invention, the invention is not limited thereto and various changes and modifications may be made without departing from the spirit of the invention and the scope of the appended claims.
Number | Date | Country | Kind |
---|---|---|---|
2012-033012 | Feb 2012 | JP | national |
Number | Name | Date | Kind |
---|---|---|---|
1775633 | Apple | Sep 1930 | A |
2714675 | Heidbreder | Sep 1955 | A |
4863091 | Dubois | Sep 1989 | A |
5191911 | Dubois | Mar 1993 | A |
5456405 | Stagg | Oct 1995 | A |
5515707 | Smith | May 1996 | A |
5813592 | Midling et al. | Sep 1998 | A |
6352193 | Bellino | Mar 2002 | B1 |
6538203 | Nolle et al. | Mar 2003 | B1 |
7097091 | Okamura | Aug 2006 | B2 |
20030098336 | Yamashita | May 2003 | A1 |
20100018768 | Takahashi et al. | Jan 2010 | A1 |
20130167555 | Schwarz | Jul 2013 | A1 |
20140144015 | Mayer et al. | May 2014 | A1 |
20140367452 | Dinda | Dec 2014 | A1 |
Number | Date | Country |
---|---|---|
1144499 | Mar 1997 | CN |
1212194 | Mar 1999 | CN |
1421294 | Jun 2003 | CN |
10 2008 054 449 | Jun 2009 | DE |
0 893 190 | Jan 1999 | EP |
1 825 946 | Aug 2007 | EP |
63-124738 | May 1988 | JP |
63124738 | May 1988 | JP |
02055673 | Feb 1990 | JP |
2529953 | Jun 1996 | JP |
2008-182848 | Aug 2008 | JP |
2008-194732 | Aug 2008 | JP |
2008182848 | Aug 2008 | JP |
2009-195008 | Aug 2009 | JP |
2010-125495 | Jun 2010 | JP |
2011-235335 | Nov 2011 | JP |
2011235335 | Nov 2011 | JP |
Entry |
---|
Cavaliere et al., “Effect of welding parameters on mechanical and microstructural properties of dissimilar AA6082-AA2024 joints produced by friction stir welding” Materials and Design 30, (2009), 609-616. |
Chinese Office Actions received in corresponding Chinese Application No. 201310050909.3 dated Jan. 30, 2015. |
Chinese Office Actions received in corresponding Chinese Application No. 201310050909.3 dated Nov. 2, 2015. |
Zhanhui, H., “Application Prospect of Friction Stir Welding in Manufacturing Electric Motor”, Hongdu Science and Technology, 2002, pp. 15-17. |
Japanese Office Action received in corresponding Japanese Application No. 2013-019054 dated Apr. 26, 2016. |
Chinese Office Actions received in corresponding Chinese Application No. 201310050909.3 dated Nov. 3, 2016. |
Extended European Search Report received in corresponding European Application No. 13155132.7 dated Jul. 7, 2017. |
Number | Date | Country | |
---|---|---|---|
20170133917 A1 | May 2017 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 13765169 | Feb 2013 | US |
Child | 15405652 | US |