1. Field of the Invention
Embodiments of the present invention relate generally to fuel cells which utilize a current collector and/or a separator for the purpose of providing an electronic flow path for current generated by the fuel cell, to support the electrodes and electrolyte holding member, and to form the flow field for gas access to electrodes.
2. Description of Related Art
Conventional planar fuel cell stacks typically are comprised of a plurality of fuel cell sub-assemblies arranged in an electrical series relationship. Each fuel cell sub-assembly may be comprised of an anode electrode, a separator plate, and a cathode electrode. Each electrolyte holding member is located between adjacent fuel cell sub-assemblies so as to be in contact with the anode and the cathode of adjoining fuel cell sub-assemblies. Another approach is to provide a plurality of membrane-electrode assemblies, or MEA's, with the separators located between adjacent MEA's. At assembly, the fuel cell stack is compressed axially to afford good intimate contact at each interface of the fuel cell stack to establish the electronic flow path for the electrons liberated by the electrochemical fuel cell reaction.
The separator plate, being disposed between adjacent anodes and cathodes, is required to be constructed from a conductive material. Typically, the basis for selection of material to construct the separator is a function of the operating characteristics of the fuel cell type. Each of the various fuel cell types has its particular electrolyte and operating temperature and provides various degrees of operating efficiencies. Typically, fuel cells which operate at low temperatures (˜<400 C.) may utilize a polymer separated carbon graphite for the separator material. Fuel cells which operate at temperatures greater than ˜400 C. utilize stainless steels and ceramics as the separator material.
The separator plate of a conventional high temperature fuel cell stack serves multiple purposes.
In many cases the separator is comprised of multiple components to achieve these purposes. Typically, three to four separate components, or sheets of material, are needed depending upon the flow configuration of the fuel cell stack. It is frequently seen that one sheet of material is used to provide the separation of anode/cathode gasses while two additional sheets are used to provide the flow field and current collection duties for the anode and the cathode sides of the separator. Another example of prior art is to use one sheet of ribbed or dimpled material to create the anode/cathode separation as well as the flow fields. Additional sheets of perforated material are used for current collection and, in some instances, to enhance the flow field cross sectional area.
There are three fundamental flow patterns of the reactant gasses which may be applied to the separator to achieve varying objectives. The three patterns consist of co-flow, counter-flow, and cross-flow. Each of the three flow patterns introduces varying degrees of complexity to the design and construction of the separator and current collectors. Low temperature fuel cells, employing carbon graphite as the separator material, often will utilize a combination of the three fundamental flow patterns resulting in sinusoidal flow paths or “Z” patterns.
U.S. Pat. No. 4,548,876 teaches the application of a “corrugated metallic electron collector” which “includes a plurality of corrugations therein”. A preferred embodiment described in this patent utilizes particles within the metallic electron collector to “provide support for a respective catalyst (i.e. electrode) immediately adjacent to and in contact with the metallic electron collector”. These collectors are adjacent to flat “separators”.
This approach has been further advanced through the application of an additional sheet metal component comprised of a perforated sheet positioned between the “corrugated metallic electron collector” and the respective electrode. These approaches have proved to be technically feasible, however, the material content of such structures is economically prohibitive, consisting of three to five sheet metal components of rather significant complexity.
U.S. Pat. Nos. 4,654,195 and 5,531,956 among others teaches the application of “ribs” to the anode electrode of the fuel cell. This approach is intended to apply the flow field directly to the electrode. While technically effective, typically the material cost of the anode is greater than that of sheet metal used to otherwise form an anode flow field with the current collector and separator. Additionally, depth of the ribs formed on the anodes is insufficient for large area fuel cells requiring large cross-sectional flow area. Furthermore, excessive mechanical creep of ribbed anodes can result in poor performance of the fuel cell.
U.S. Pat. No. 4,983,472 teaches the application of a “plurality of arches” to the current collector in a somewhat similar fashion as the above mentioned U.S. Pat. No. 4,548,876. However, the plurality of arches are distributed much more densely and create a finer degree of support to the electrodes thus eliminating the requirement for supporting particles or an additional perforated sheet metal component. This approach has proven to be technically successful but yet again has not reduced the component count of the separator plate below three sheets of material, two current collectors and one separator sheet.
U.S. Pat. No. 5,503,945 teaches the application of corrugations to the “main plate” of the separator and the use of perforated current collector for both the anode and cathode. This patent further teaches the integration of the current collector with its respective electrode. Additionally, this patent teaches the integration of the current collector of either the anode or the cathode with the peripheral sealing structure of the separator and claims a two piece separator with reduced material content and component count. However, the requirement for a current collector for the anode and for the cathode have not been eliminated. The active central area of the fuel cell typically constitutes the far greater portion of the area of the fuel cell relative to the peripheral sealing area. Therefore, while component count of the separator assembly has been reduced through integration of one of the current collectors with either the anode or with the cathode, the material content and component count of the separator as a whole has not appreciably been altered when viewing the total assembly. Furthermore, current collector/separator designs which utilize a ribbed separator and a nominally flat perforated current collector suffer from diminished cross-communication of the reactant gas from one rib to adjoining ribs.
U.S. Pat. No. 5,795,665 teaches the application of “a plurality of rows of dimples” to the separator plate and to the “current collector/active component subassembly”. Though resulting in modest reduction of material content the separator/current collector component count remains at three. This invention provides for cross-flow, co-flow, or counter-flow of reactant gasses utilizing three sheets of material.
U.S. Pat. No. 5,811,202 teaches the application of ribs to an “anode field plate” and to a “cathode field plate” separated by a “flat middle plate”. A perforated current collector is disposed between the cathode field plate and the cathode electrode throughout the central active area of the fuel cell. Again, as with the above mentioned U.S. Pat. No. 5,503,945, the active central area of the fuel cell typically constitutes the far greater portion of the area of the fuel cell relative to the peripheral sealing area. Therefore, while component count of the separator assembly has been stated as being three, the component count of the separator as a whole when viewing the total assembly is four.
Material content of the separator/current collector assembly tends to be a function of two factors: the size of the active area of the fuel cell and the efficient use of structural forming materials. Fuel cells with areas exceeding about one square foot and operating at or near atmospheric pressures require reactant flow fields (i.e. anode and cathode) with sufficient cross-sectional area to prevent excessive pressure build-up at the inlets. Excessive pressure at the inlets relative to the outlets can create undesirable pressure differentials that may contribute to leakage of the reactants. As such, as cell area, and consequently flow field length, is increased to provide ever greater quantities of power output the cross-sectional area of the reactant flow fields also must increase. As it is the material of construction of the separator which forms the flow fields, material content of the separator rises with the increase in cross-sectional flow area. Excessive material content can be controlled with efficient use of the structural forming materials and the limitation of flow field length.
Material thickness of the various current collector designs is governed by several factors which include corrosion rates of the various fuel cell environments as well as the mechanical constraints induced by the axial compressive load applied to the fuel cell stack and the unsupported spans of the flow field induced by the desire to maximize the cross-sectional flow area. As mentioned above, as cell area increases the cross-sectional flow area also is increased to accommodate the added reactant gas flow rate and associated back pressure. As a result fuel cells which seek large areas and/or operate at atmospheric pressures must provide relatively large cross-sectional flow area which tends to manifest in wide unsupported spans requiring robust current collector design.
In some instances it has been found necessary to electroplate a stainless steel alloy with nickel for corrosion protection in anode current collector applications. Nickel is very stable in the anode environment of the molten carbonate fuel cell but does not retain the same degree of strength at operating temperatures as certain stainless steel alloys. When the current collector is configured to provide high degrees of structure to the flow field, as with U.S. Pat. No. 4,983,472, a high strength alloy may be utilized to produce the anode current collector and typically is nickel plated following the forming process. Nickel plating adds significant expense to the manufactured cost of the current collector.
All of the above described prior art utilizes perforated sheet metal in one form or another to create the current collector of the fuel cell. These perforations are arranged in highly repetitive patterns to simplify manufacture as well as to maximize the access of the reactant gasses to the electrodes. The degree of reactant access to the electrode is often referred to as “percent open area” of the current collector. A reasonably large percent open area is needed to avoid choking the fuel cell electrochemical reaction which diminishes performance. However, large percentage of open area alone neglects the electrodes requirement for physical support against the stack axial compressive load. A compromise is made to limit percentage of open area while maintaining appropriately dispersed electrode support.
For example, molten carbonate fuel cell electrodes can sustain only modest widths of open and unsupported area of approximately 0.10 inches. Additionally, the performance of molten carbonate fuel cells is diminished if the width of the areas of the current collector supporting the electrode exceeds approximately 0.10 inches. As a result the typical MCFC current collector pattern of perforated openings has a pitch in at least one axis of approximately 0.20 inches. These factors become more restrictive as electrode thickness is reduced.
However, it has been observed that the electrodes are able to sustain considerable lengths of narrow unsupported areas. For example, the pattern described in the above mentioned U.S. Pat. No. 4,983,472 patent where, although the width of the typical opening is held at 0.06″, the length of the opening is 0.190″. Another example is the description in the above mentioned U.S. Pat. No. 5,811,202 patent which implies that the anode is supported only by a ribbed flow field implying significant lengths of narrow unsupported area.
In some instances, as with the current collector described in patent U.S. Pat. No. 4,983,472, the perforations are partial and the otherwise scrap metal is utilized to form the structure of the cross-sectional flow area. As such, the manufacture of these various current collector designs typically requires specialized tooling operated in press machines of varying degrees of complexity. In current collector patterns where the perforation is total and a through hole is produced a large quantity of scrap metal is generated during the manufacturing process, up to 35-40%. The complexity of the tooling and the generation of large quantity of scrap conspire to render the various designs as uneconomical at high production volume anticipated for commercial fuel cell applications.
As mentioned, the typical highly repetitive patterns are intended to maximize gas access to electrodes for optimum fuel cell performance. However, the various flow patterns of the separator and the vagaries of the electrochemical fuel cell process often result in undesirable concentrations of electrochemical reactions. This tends to create hot spots and cold spots, or thermal gradients, in the fuel cell which can contribute to premature failure of the fuel cell. It is well established in the art that counter-flow of reactant gasses in general provides the optimum distribution of the electrochemical fuel cell process and results in good current density distribution and reduced thermal gradients. In such a counter-flow approach the fuel stream in each cell is initially directed to a region of the anode layer witch coincides with the region of the adjoining cathode layer in which the oxidant stream has the lowest concentration of oxygen. As the fuel stream progresses through the fuel cell and approaches the exit it has been depleted of fuel and now coincides with the region of the cathode in which the oxidant stream has the highest concentration of oxygen. It is further well established in the art that co-flow and cross-flow of reactant gasses provide for a less optimum current density distribution and thermal gradients. It is additionally well established in the art that the current collector of a fuel cell is capable of diminishing the performance of the fuel cell if the current collector shields excessive areas of the electrodes from the reactant gases.
It is an object of this invention to provide a plurality of flat wires to act as the current collector for a fuel cell which utilizes a ribbed separator to form the flow fields.
It is a further object of the present invention to provide a current collector for a fuel cell with long lengths of areas of alternately narrowly supported and narrowly unsupported electrodes.
It is a further object of the present invention to provide a current collector for a fuel cell with lateral conduits for fluid communication between adjoining flow ribs of the separator.
It is a further object of this invention to provide a current collector for a fuel cell which is simple to manufacture with little or no scrap material generated during the manufacturing process.
It is a further object of the present invention to provide a current collector that does not require electroplating of corrosion resistant coatings.
It is yet a further object of the present invention to provide a current collector for a fuel cell such that the manufacturing tools may be easily modified or adjusted to alter the current collector pattern to selectively concentrate or disperse the fuel cell electro-chemical reaction to desirable locations to optimize fuel cell performance.
The preferred embodiment of the invention utilizes a plurality of parallel flat wires slit continuously from sheet metal and bonded to the face of an electrode on the side facing the respective flow field of the separator. The separator is formed with ribs. The fiat wires, or strips, are preferably narrow and are preferably spaced at sufficient frequency, or pitch, as to provide optimum access of the reactant gasses to the electrodes as well as to provide optimum mechanical support to the electrodes. The flat wires are preferably thin as to minimize material content and ease manufacturing constraints yet retain sufficient strength to react against the compressive sealing forces applied to the fuel cell stack at assembly.
The flat wire current collectors are preferably continuously and simultaneously slit from sheet metal using a powered rotary slitting device and spread apart to the desired spacing through a combing device prior to an adhesive bonding to a preferably continuously tape cast electrode. The current collector/electrode assembly may then be cut to desired length for installation to the ribbed separator.
The flat wires will span the peaks of the ribs of the separator and may be arranged at any significant angle, other than parallel, to the ribs of the separator that effectively supports the flat wire. Consequently, a secondary lateral conduit is created in the spaces between the flat wires which provides lateral fluid communication of the primary flow field conduit of the flow ribs for improved balancing of pressures and compositions of the reactant gasses.
Upon viewing the figures and reading the detailed description it will be apparent to those skilled in the art that the current collector herein described will be of low material content, produced with little or no scrap, provide ease of manufacture, will not require corrosion resistant coatings, and may be easily manipulated to selectively concentrate or disperse the fuel cell electrochemical reaction to desirable locations for optimized fuel cell performance.
The above and other aspects of the invention will become more apparent upon reading the following detailed description in conjunction with the accompanying drawings, in which:
In
In
In all cases it is understood that the above-described arrangements are merely illustrative of the many possible specific embodiments which represent applications of the present invention. Numerous and varied other arrangements can be readily devised in accordance with the principles of the present invention without departing from the spirit and scope of the invention.
This is a continuation of U.S. patent application Ser. No. 09/413,169, filed on Oct. 7, 1999 now U.S. Pat. No. 6,383,677.
Number | Name | Date | Kind |
---|---|---|---|
4169917 | Baker et al. | Oct 1979 | A |
4175165 | Adlhart | Nov 1979 | A |
4476197 | Herceg | Oct 1984 | A |
4510212 | Fraioli | Apr 1985 | A |
4548876 | Bregoli | Oct 1985 | A |
4604331 | Louis | Aug 1986 | A |
4631239 | Spurrier et al. | Dec 1986 | A |
4702973 | Marianowski | Oct 1987 | A |
4753857 | Hosaka | Jun 1988 | A |
4781996 | Toriya et al. | Nov 1988 | A |
4853301 | Granata, Jr. et al. | Aug 1989 | A |
4855193 | McElroy | Aug 1989 | A |
4857420 | Maricle et al. | Aug 1989 | A |
4977041 | Shiozawa et al. | Dec 1990 | A |
4978589 | Shiozawa et al. | Dec 1990 | A |
4983472 | Katz et al. | Jan 1991 | A |
5084364 | Quaadvliet | Jan 1992 | A |
5227256 | Marianowski et al. | Jul 1993 | A |
5298342 | Laurens et al. | Mar 1994 | A |
5362578 | Petri et al. | Nov 1994 | A |
5424144 | Woods, Jr. | Jun 1995 | A |
5460897 | Gibson et al. | Oct 1995 | A |
5482792 | Faita et al. | Jan 1996 | A |
5503945 | Petri et al. | Apr 1996 | A |
5527363 | Wilkinson et al. | Jun 1996 | A |
5558955 | Breault et al. | Sep 1996 | A |
5707755 | Grot | Jan 1998 | A |
5726105 | Grasso et al. | Mar 1998 | A |
5733682 | Quadakkers et al. | Mar 1998 | A |
5770327 | Barnett et al. | Jun 1998 | A |
5773160 | Wilkinson et al. | Jun 1998 | A |
5773161 | Farooque et al. | Jun 1998 | A |
5776624 | Neutzler | Jul 1998 | A |
5795665 | Allen | Aug 1998 | A |
5798187 | Wilson et al. | Aug 1998 | A |
5798188 | Mukohyama et al. | Aug 1998 | A |
5811202 | Petraglia | Sep 1998 | A |
5833822 | Hsu | Nov 1998 | A |
5846668 | Watanabe | Dec 1998 | A |
5922485 | Enami | Jul 1999 | A |
5942349 | Badwal et al. | Aug 1999 | A |
6033794 | George et al. | Mar 2000 | A |
6037073 | Besmann et al. | Mar 2000 | A |
6040073 | Okamoto | Mar 2000 | A |
6040075 | Adcock et al. | Mar 2000 | A |
6040076 | Reeder | Mar 2000 | A |
6045934 | Enami | Apr 2000 | A |
6045935 | Ketcham et al. | Apr 2000 | A |
6048633 | Fujii et al. | Apr 2000 | A |
6048634 | Kaufman et al. | Apr 2000 | A |
6048636 | Naoumidis et al. | Apr 2000 | A |
6050331 | Breault et al. | Apr 2000 | A |
6051330 | Fasano et al. | Apr 2000 | A |
6051331 | Spear, Jr. et al. | Apr 2000 | A |
6054228 | Cisar et al. | Apr 2000 | A |
6054231 | Virkar et al. | Apr 2000 | A |
6071635 | Carlstrom, Jr. | Jun 2000 | A |
6071636 | Mosdale | Jun 2000 | A |
6074692 | Hulett | Jun 2000 | A |
6080502 | Nölscher et al. | Jun 2000 | A |
6096450 | Walsh | Aug 2000 | A |
6099984 | Rock | Aug 2000 | A |
6103415 | Kurita et al. | Aug 2000 | A |
6117580 | Nitschke et al. | Sep 2000 | A |
Number | Date | Country |
---|---|---|
07022038 | Jan 1995 | JP |
WO 9913522 | Mar 1999 | WO |
Number | Date | Country | |
---|---|---|---|
20020114989 A1 | Aug 2002 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 09413169 | Oct 1999 | US |
Child | 10067431 | US |