1. Field of the Invention
The present invention relates to full-type rolling bearings and roller cam followers for engines that have no cage, such as bearings for rocker arms, cam followers and roller follower bearings.
2. Description of the Background Art
Of recent rolling bearings, full-type roller bearings without cage like bearings for rocker arms to be used for high-speed heavy-load applications are increasing in number. In the full-type roller bearing without cage, it inevitably occurs that rollers interfere with each other. Therefore, at high speeds, the rollers are not properly controlled in terms of their positions so that skew is likely to occur. Resultant heat generation due to sliding as well as a local increase in surface pressure are likely to cause surface damages (peeling, smearing, surface-initiated peeling) and inside-initiated peeling, while the full-type roller bearing should have a high load capacity according to calculation.
More specifically, in such full-type roller bearings as roller follower, cam follower and rocker arm, the interference between rollers and poor supply of lubricant into the bearings could cause peelings initiated from the surfaces of rollers and raceways. Moreover, influences of an assembly error and a biasing load could cause skew of rollers, resulting in surface-initiated peelings due to sliding and inside-initiated peelings due to a local increase in surface pressure. The full-type roller bearing herein refers to a bearing without cage as described above and may sometimes be abbreviated as full roller bearing.
For a roller cam follower of an engine that has an outer ring with its circumference being in rolling contact with a cam, most improvements of the roller cam follower have been for the purpose of improving the circumference of the outer ring. For example, compression residual stress induced by such a process as shot peening and increased hardness induced by high-concentration carbonitriding (process-induced effects) have been used for prolonging the lifetime, chiefly for improving the circumference of the outer ring that is in rolling contact with the cam.
Although improvements with the aim of prolonging the rolling life of a roller shaft serving as an inner ring, rollers and the entire bearing have been relatively few, some improvements have still been made in terms of materials for providing heat resistance and microstructure stability as well as increased hardness that are obtained through carbonitriding, and thereby prolonging the lifetime of the bearing. There have been known techniques regarding prolonging of the lifetime of the roller cam follower for the engine:
(d1) For a cam follower bearing of an engine valve mechanism, a calculated life of the bearing, at a rated engine rpm, of 1000 hours or longer is achieved (Japanese Patent Laying-Open No. 2000-38907).
(d2) In order to achieve a bearing shaft of a cam follower with the properties of: a carbide ratio=10–25%; ratio of decomposed austenite content to initial retained austenite content=1/10–3/10; end hardness=HV 830–960; and average wavelength of surface roughness=25 μm or less, a bearing steel is carbonitrided and hard shot peened (Japanese Patent Laying-Open No. 10-47334).
(d3) A solid lubricant film of high polymer for example is formed on a cam follower shaft for improving wear resistance of the shaft (Japanese Patent Laying-Qpen No. 10-103339).
(d4) A cam follower shaft is made of a tool steel for example and is ion-nitrided or ion-plated at a temperature lower than a tempering temperature so as to have a high hardness (Japanese Patent Laying-Open No. 10-110720).
(d5) A cam follower bearing for an engine valve mechanism that has its shaft for which a bending stress is 150 MPa or less (Japanese Patent Laying-Open No. 2000-38906).
(d6) A cam follower for an engine valve mechanism that has a phosphate film which is excellent in lubricating-oil retention and provided on a rolling surface of a bearing component (Japanese Patent Laying-Open No. 2002-31212).
(d7) A cam follower for an engine valve mechanism that has a crowning in a region of a shaft where rollers roll (Japanese Utility-Model Laying-Open No. 63-185917).
(d8) A carburized shaft has a rolling surface layer which is high-concentration carburized or carbonitrided with a carbon concentration of 1.2%–1.7% and has an internal hardness of HV 300 (Japanese Patent Laying-Open No. 2002-194438).
There is another problem regarding the rocker arm as described below. In such a case that both ends of a roller shaft are caulked to be fixed to a roller supporting member, although a rolling surface of the roller shaft should have high hardness, the ends thereof should be soft enough to be caulked. Further, after the shaft ends are caulked to be fixed, the strength (hardness) should be high for preventing loosening in use. The following document discloses caulking of both ends of a roller shaft of a roller rocker.
(d9) The outer surface of a roller shaft is uniformly high-frequency induction-hardened and then tempered, and thereafter only the ends of the shaft are high-frequency annealed and accordingly softened (Japanese Patent Laying-Open No. 5-179350).
It is assumed that, the full-type roller bearings like the rocker arm, roller follower and cam follower will, similar to normal caged bearings, increase in speed and load in use, and the viscosity of a lubricating oil therefor will decrease. In order to extend the rolling life of the full-type roller bearings under such conditions in use, (a1) any measure should be taken, as usually done, for the rolling fatigue life dependent on the load and (a2) any measure should further be taken for the surface damage life due to metal contact caused by sliding and loss of an oil film. However, there has been no technique for remarkably extending both of the rolling fatigue life dependent on the load and the surface damage life due to the metal contact. Moreover, in addition to these two measures for prolonging the life, (a3) any measure should be taken for the issue of shortening of the life due to the interference of rollers with each other as well as the skew thereof that are peculiar to the full-type roller bearings.
The above-described known techniques improve the rolling life by increasing the hardness and the compression residual stress, or improve the rolling surface where a bearing component is in rolling contact with a counterpart component. In actually evaluating these techniques, it is found that they are effective for extending the life in such an application where bending is applied as in the case of the outer ring, while such improvements are not necessarily effective by themselves for extending the life of the inner ring and rollers of the full roller bearing.
An object of the present invention is, in consideration of the increased speed and load in use and the decreased viscosity of the lubricating oil, to provide a full-type rolling bearing and particularly a roller cam follower of an engine that exhibit a long life under severe lubrication, sliding and load conditions,
A full-type rolling bearing according to the present invention is formed of an outer ring, an inner ring and rollers that are made of steel, at least one of the outer ring, inner ring and rollers has a carbonitrided layer in its surface layer, and the austenite crystal grain size number of the surface layer is greater than 10.
For the full-type rolling bearing of the present invention, a material with fine crystal grains and heat resistance can be used to extend the surface damage (surface-initiated exfoliation like peeling and smearing) life as well as the inside-initiated peeling life. Specifically, processing of such a material as bearing steel or heat treatment pattern is improved to produce a carbonitrided structure ensuring an austenite crystal grain size number greater than 10 defined by JIS. The resultant structure can remarkably enhance the resistance to occurrence and development of cracks. Accordingly, heat generation of the surface layer due to sliding and occurrence of surface cracks due to tangential force can be prevented. Moreover, against cracks resulting from inside-initiated peelings, the life can remarkably be extended.
The above-described microstructure is further processed and heat-treated and a compression residual stress is imposed on the surface layer to increase the hardness, so that the life can further be extended. The processing and heat treatment may be any one of, or a combination of: (b1) shot peening, (b2) barrel finishing, (b3) rolling, (b4) varnishing, (b5) carburizing and carbonitriding, (b6) carbonitriding and sub-zero treatment, and (b7) carbonitriding and secondary quenching and sub-zero treatment.
Here, the austenite crystal grain size number greater than 10 means that austenite crystal grains are fine enough to have the number greater than 10 or 11 or more which is determined according to a method of testing the austenite crystal grain size defined under JIS G 0551. When a structure is quenched from a temperature in the austenite temperature range, austenite grain boundaries remain in the quenched structure and accordingly the content of remaining austenite grains is measured, which is sometimes referred to as prior austenite grain boundaries.
At least one of the outer ring, inner ring and rollers may be carbonitrided at a carbonitriding temperature equal to or higher than the Al transformation temperature, cooled to a temperature lower than the Al transformation temperature and heated to a quenching temperature lower than the carbonitriding temperature and thereby quenched.
Such a microstructure is once cooled to a temperature lower than the carbonitriding temperature and then quenched from the resultant quenching temperature so that considerably fine austenite crystal grains can be obtained. This process of quenching by heating to a temperature lower than the carbonitriding temperature is sometimes called, in terms of the order of the process, secondary quenching or final quenching.
The quenching temperature may be in a temperature range at which carbide and/or nitride and an austenite phase coexist in the carbonitrided surface layer of the steel.
The quenching temperature is lower than the carbonitriding temperature, and thus the amount of un-dissolved carbide and/or nitride in the surface layer, which is influenced by the carbonitriding process, increases as compared with that in the carbonitriding process. Then, when the quenching temperature is in the temperature range where those components coexist, the ratio of un-dissolved carbide/nitride increases while the ratio of austenite decreases at the quenching temperature as compared with those ratios in the carbonitriding process. In addition, it is seen from the Fe—C binary phase diagram that, in the range where carbide (cementite) and austenite coexist, the concentration of carbon dissolved in austenite decreases as the quenching temperature decreases. As the steel for the bearing has low contents of other alloy elements like Si and Mn, the temperature region and the generated layer can be discussed with sufficient precision with reference to the Fe—C binary phase diagram. In addition, nitrogen, like carbon, is an interstitial element dissolved in iron and produces nitride with iron similar to cementite in a predetermined temperature region, and the nitrogen can be regarded approximately as the same as carbon.
When the temperature is increased to the quenching temperature, austenite grains are made fine since there remain a large amount of un-dissolved carbide and/or nitride that prevent growth of austenite grains. Moreover, the structure transformed from austenite to martensite through quenching has a somewhat low carbon concentration when the above-described heat treatment is applied, so that the structure has somewhat high toughness as compared with the structure quenched from the carbonitriding temperature. In other words, the quenched structure has (c1) a greater amount of un-dissolved carbide/nitride as compared with the structure produced through the conventional process, and (c2) a lower carbon concentration than the conventional one.
The above-discussed quenching temperature may be 790° C.–830° C. This temperature is applicable to most of steel materials to facilitate management of the sintering temperature.
Further, at least one of the outer ring, inner ring and rollers may be cold-worked before being carbonitrided.
The cold-working can be applied to increase the nucleation density of austenite grains in the heat treatment and thereby produce a fine-grain structure.
The austenite may have the grain size number of at least 11. With the defined austenite grain size, austenite grains that are extremely and unthinkably fine austenite grains contribute to achievement of stably long rolling fatigue life and surface damage life. Moreover, the issue of the decreased viscosity of the lubricating oil can satisfactory be addressed.
In at least one of the outer ring, inner ring and rollers, a compression residual stress of at least 500 MPa may be generated.
As discussed above, the microstructure can further be processed and heat-treated and a compression residual stress can be formed in the surface layer so as to further extend the life.
A roller cam follower of an engine according to the present invention includes an outer ring being in rolling contact with a cam shaft of the engine, a roller shaft located inside the outer ring and fixed to a cam follower body, and bearing elements placed between the outer ring and the roller shaft. At least one of the outer ring, roller shaft and bearing elements has a carbonitrided layer, and austenite crystal grains in at least a surface layer are made fine to have a grain size number greater than 10.
The austenite grains in the component are made fine enough to have the grain size number greater than 10, and accordingly the rolling fatigue life can considerably be improved. With the austenite grain size number of 10 or less, any remarkable improvement of the rolling fatigue life is impossible and thus the grain size number is greater than 10, and preferably 11 or greater. Although further finer austenite grains are desirable, the grain size number exceeding 13 is usually difficult to achieve. It is noted here that, the above-mentioned bearing elements located between the outer ring and the roller shaft refer to bearings including rollers or rolling elements, however, the bearing elements may be, in a narrow sense, rollers or rolling elements.
The austenite grain size number may be determined by the usual method defined by JIS, or determined according to the intercept method for example with the average grain size corresponding to the above grain size number. A smaller austenite grain size is desirable and an austenite grain size number of 11 or greater is further desirable. Alternatively, the average grain size may be 6 μm or less. The austenite grain size number may be achieved in the carbonitrided layer. In general, however, the condition of the fineness of austenite is satisfied in the body of steel located inside the carbonitrided layer.
Here, the austenite grains refer to crystal grains of austenite which is phase-transformed during the heating process, and the traces of grains remain after the austenite is transformed into martensite through cooling.
For another roller cam follower of an engine according to the present invention, at least one of an outer ring, a roller shaft and bearing elements has a carbonitrided layer and has a fracture stress of at least 2650 MPa.
The inventors of the present invention have found that, the heat treatment method (low-temperature secondary quenching method) herein described later can be used to increase the fracture stress of a steel having a carbonitrided layer to 2650 MPa or more which has not been achieved by any conventional method. In this way, a high-strength rolling bearing can be obtained to achieve excellent durability under a load condition of the roller cam follower.
For still another roller cam follower of an engine according to the present invention, at least one of an outer ring, a roller shaft and bearing elements has a carbonitrided layer and has a hydrogen content of at most 0.5 ppm,
The above-described heat treatment (low-temperature secondary quenching) can be used to lower the hydrogen content in any of components before being assembled into a cam follower. Then, it is possible to shorten the time required for hydrogen entering the steel to increase and attain a critical point at which cracks occur. For this reason, together with any reasons which have not been clarified, the durability can be enhanced.
A lower hydrogen content is desirable. However, reduction of the hydrogen content to the one less than 0.3 ppm requires long-term heat treatment, resulting in increase in size of austenite grains and thus deterioration in toughness. Then, a hydrogen content is desirably in a range from 0.3 to 0.5 ppm and more desirably in a range from 0.35 to 0.45 ppm.
In measuring the above hydrogen content, diffusible hydrogen is not measured and only the non-diffusible hydrogen released from the steel at a predetermined temperature or higher is measured. Diffusible hydrogen in a sample of small size is released from the sample to be scattered even at room temperature, and therefore the diffusible hydrogen is not measured. Non-diffusible hydrogen is trapped in any defect in the steel and only released from the sample at a predetermined heating temperature or higher. Even if only the non-diffusible hydrogen is measured, the hydrogen content considerably varies depending on the method of measurement. The above mentioned range of hydrogen content is determined by thermal conductimetry. In addition, as detailed later, the measurement may be taken by means of a LECO DH-103 hydrogen determinator or like measuring device.
(c1) The cam follower body may be pivotably attached to a rotational shaft located between one and the other end of itself, an open/close valve of the engine may abut on the one end, the other end may have a bifurcated roller supporting portion, and the roller shaft may be fixed to the bifurcated roller supporting portion.
(c2) The cam follower body may be mounted between one end and the other end of itself, having the roller shaft fixed in a roller hole extending between two sidewalls, an end of an open/close valve of the engine may abut on one end, and a pivot may abut on the other end.
(c3) The cam follower body may be pivotably attached to a rotational shaft located between one end and the other end of itself, one end of an open/close valve of the engine may abut on one end, the other end may abut on one end of an interlocking rod transmitting a stress from the cam shaft, the cam follower body is mounted on the other end of the interlocking rod, the one end and the other end of the interlocking rod being located respectively on the rocker arm and the cam, and the roller shaft may be attached to the cam follower body and abuts on the cam.
The cam follower bodies of (c1), (c2) and (c3) are common in that they transmit a driving force from the cam to the engine valve while they are different in structure to be applicable to different engine types.
Regarding the roller cam follower of the engine discussed above, the bearing elements may be full-type needle bearing. The roller shaft may have its end with a lower hardness than that of its central portion. The central portion of the roller shaft thus has a hardness necessary for serving as a rolling contact surface while the end is made soft. Accordingly, with durability like the rolling fatigue life ensured, caulking for example can be done. All of the rolling bearings described above may have an end of a roller shaft which is caulked.
Further, the cam follower body may be press-formed to improve production efficiency.
The foregoing and other objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings.
Embodiments of the present invention are hereinafter described in connection with the drawings.
An adjust screw 7 is screwed into one end 1b of this rocker arm 1. Adjust screw 7 is fixed by a lock nut 8 having its lower end abutting on the upper end of an intake valve or discharge valve of an internal-combustion engine. Valve 9 is biased by elasticity of a spring 10.
Rocker arm 1 has the other end 1a provided with a body of the cam follower (cam follower body) 50, and cam follower body 50 has a bifurcated roller supporting portion 14 which is formed integrally with the body. In bifurcated roller supporting portion 14, both ends of roller shaft 2 which corresponds to an inner ring is press-fit or fixed by means of a snap ring. On a central part of the outer surface of roller shaft 2, an outer ring 4 is supported rotatably via rollers 3. Rollers 3 are placed between roller shaft 2 and outer ring 4 to serve as bearing elements. In other words, bearing elements located between roller shaft 2 and outer ring 4 are rollers. The axial direction of rollers 3 is in parallel with the axial direction of the roller shaft. The outer surface of outer ring 4 is brought into contact with the surface of cam 6 by the biasing force of spring 10. It is noted that terms “one” and “the other” herein used have no specified meaning, merely used in the order of reference in this description.
Cam follower body 50 is one specific example of full-type rolling bearings. Specifically, a rolling bearing including an inner ring formed of roller shaft 2, rolling elements formed of rollers 3 and outer ring 4 is employed as a full roller bearing for a rocker arm. In general, a bearing without cage is called full roller bearing. The above-mentioned full roller bearing for the rocker arm rotates while contacting cam 6 so that pressing force and impact force of cam 6 are exerted on outer ring 4. The roller cam follower of an engine in this embodiment is thus a member which includes the full roller bearing for the rocker arm and the cam follower body.
As the rocker arm bearing rotates while contacting cam 6, the pressing force and impact force of cam 6 are exerted on outer ring 4, possibly resulting in indentations and cracks due to repeated bending stress. In particular, with the increased engine output, the engine rpm accordingly increases so that those forces become greater resulting in a higher risk of occurrence of cracks and indentations and thus shortening of the rolling life and surface damage life.
Indentations due to exertion of a great force on the bearing are likely to be formed on the inner ring since the surface pressure between the inner ring and the rolling elements (rollers) is usually higher than the surface pressure between the outer ring and the rolling elements (rollers). For the cam follower, however, the bending stress is exerted on the outer ring while the high surface-pressure load is also exerted on the outer ring, and thus indentations are likely to be formed between the outer ring and the rolling elements. The inventors of the present invention have found that the surface damage life and the rolling life can be prolonged by forming a carbonitrided layer in a surface layer of at least one of the above-discussed components, with the austenite grain size number of the surface layer being greater than 10 for example or at least 11 in a predetermined case. In addition, the inventors have found that the extent to which the life is prolonged is increased by adding a compression residual stress to the surface layer.
A cam follower body 50 is provided to a hollow bearing attachment 16a located on the lower end of interlocking rod 16, and a full roller bearing for the rocker arm is attached by an attachment member 17. A cam 6 abutting on an outer ring 4 transmits a driving force to the interlocking rod.
Of the components of the full roller bearing of the roller cam follower for the engine, at least one of rollers 3, roller shaft 2 and outer ring 4 is heat-treated through low-temperature secondary quenching so as to make austenite grains fine.
A carbonitrided layer in which austenite crystal grains are made fine is preferably produced by a method for example described below, however, any method except for this may be used.
Compared with ordinary or normal quenching by which carbonitriding is done and immediately thereafter quenching is done once, the above-discussed heat treatment can improve the crack strength and prolong both of the surface damage life and the rolling fatigue life while carbonitriding the surface layer. Moreover, the issue of the decreased viscosity of the lubricating oil can be addressed. This heat treatment can also produce a microstructure having austenite crystal grains of a grain size which is smaller than the conventional one by one half or more. A bearing component undergoing this heat treatment has a long rolling fatigue life and a long surface damage life and can address the issue of decreased viscosity. The bearing component can also have an improved crack strength and a decreased rate of secular dimensional change.
Bearings of respective materials shown in Table 1 were prepared. These bearings were full-type needle bearings included in a roller cam follower of an engine. An inner ring (roller shaft) was 14.64 mm (outer diameter)×17.3 mm (width) in size and an outer ring was 18.64 mm (inner diameter)×24 mm (outer diameter)×6.9 mm (width) in size. 26 rollers each having a size of 2 mm (outer diameter)×6.8 mm (length) were used. The bearings were full-type bearings without cage. The bearings had a basic load rating of 8.6 kN and a basic static load rating of 12.9 kN. Here, basically the bearings were each a combination of the same materials, while some were each a combination of different materials and some were produced by being additionally processed. Table 1 shows a list of the prepared bearings.
Samples shown in Table 1 are as follows.
No. 1: A bearing steel was subjected to heavy cold working in advance, heat-treated with crystal grains thereafter being made fine, and then carbonitrided.
No. 2: A bearing steel was carbonitrided and then secondary-quenched at a temperature lower than the carbonitriding temperature.
No. 3: A carburizing steel was carburized, carbonitrided and then secondary-quenched at a lower temperature. In other words, the low-temperature quenching was performed after the carburizing process.
The crystal grain size of austenite of samples Nos. 1–3 was at least No. 11. These materials were used as base samples. The following samples were prepared by additionally processing the base samples for producing a compression residual stress in the surface layer.
No. 4: The inner and outer rings of sample No. 1 were shot-peened and rollers were barrel-finished.
No. 5: The inner and outer rings of sample No. 2 were shot-peened and rollers were barrel-finished.
No. 6: The inner and outer rings of sample No. 3 were shot-peened and rollers were barrel-finished.
Samples with their surface hardness increased are as follows.
No. 7: The inner and outer rings of sample No. 1 were additionally sub-zero treated (−196° C.).
No. 8: The inner and outer rings of sample No. 1 were additionally sub-zero treated (−196° C.) and then shot-peened, and rollers were barrel-finished.
For the following samples, the above-described methods were applied to the inner and outer rings and rollers each, especially the inner ring and rollers for which the rolling life was significant.
No. 9: The inner ring and rollers were carbonitrided and then secondary-quenched at a temperature lower than the carbonitriding temperature, and the outer ring was subjected to a normal heat treatment.
No. 10: For inner and outer rings, a carburizing steel was carburized, carbonitrided, cooled, and then secondary-quenched at a lower temperature, and, for rollers, a bearing steel was carbonitrided.
As comparative examples, five samples No. 11–15 were prepared as shown in the lower part of Table 1.
No. 11: Inner and outer rings and rollers were made of a bearing steel which was normally heat-treated (normal sample).
No. 12: Inner and outer rings and rollers were made of a bearing steel which was carbonitrided.
No. 13: Inner and outer rings were made of a carburizing steel which was carburized and rollers were made of a bearing steel which was normally heat-treated.
No. 14: This sample was made of a carburizing steel which was secondary-quenched.
No. 15: Inner and outer rings of sample No. 11 were shot-peened and rollers thereof were barrel-finished.
For these samples, crystal grain size, hardness and hardness after 500° C.-tempering (index of heat resistance) were measured, resultant measurements being shown in Table 1.
Tests for evaluating rolling life and surface damage strength are detailed below.
Evaluation of rolling life:
An outer ring (18.64 mm (inner diameter)×24 mm (outer diameter)×6.9 mm (width)), 26 rollers (2 mm (outer diameter)×6.8 mm (length)) and a roller shaft (14.64 mm (outer diameter)×17.3 mm (length)) were assembled and then subjected to a rolling fatigue test under a load of 2.58 kN. A test machine is shown in
Regarding the samples with the test results shown in Table 3, the peeling was mainly occurred on the rollers or the inner ring while the peeling was also occurred partially on the outer ring of sample No. 9. It is seen from Table 3 that the samples of the present invention exhibit a longer life as compared with the comparative examples and any samples of the present invention exhibit a lifetime which is approximately three times as long as that of the normally processed sample and approximately 1.5 times as long as the carbonitrided sample.
Peeling Test:
Table 4 shows a list of samples subjected to tests including a peeling test as well as results of the test, and Table 5 shows peeling-test conditions. Samples Nos. 1–3 of the present invention and samples of the present invention that were shot-peened or sub-zero treated ones of those samples were prepared. The samples of the present invention were 8 in total (No. 1–8) and five samples (No. 11–15) were prepared as comparative examples, and thus the number of samples was 13 in total that were subjected to the peeling test.
Test pieces (mirror-finished) having a diameter of 40 mm of respective 13 test samples were brought into rolling contact with a rough-surfaced counterpart test piece under constant conditions, and the ratio of an area where peelings (a collection of fine peelings) were observed on the (mirror-finished) test piece of a sample to the entire area was measured after a certain time. The reciprocal of the determined ratio of the area is herein defined as peeling strength, and the peeling strength of comparative example No. 1 which is the normal sample is indicated by 1 as a reference.
Test results are shown in Table 4. Any of the test pieces of the present invention has a peeling strength which is at least 1.5 times as high as that of comparative examples. It is observed that fine austenite grains with the grain size number greater than 10 enhance the toughness and thereby increase resistances against occurrence and subsequent growth of cracks. Moreover, samples (No. 4–8) with a compression residual stress provided through the sub-zero treatment and any processing are improved in terms of strength. This is because the high hardness and the compression residual stress effectively contribute to prevention of occurrence and growth of peeling cracks.
Smearing Test:
The same test pieces as those for the peeling test were used (see Table 4) to examine smearing strength. Test conditions are shown in Table 6. A test piece to be tested and a counterpart test piece were each made of a combination of the same materials.
Results are shown in Table 4. Here, the smearing strength was evaluated on the basis of the rotational speed of the counterpart test piece when smearing occurred, and the results are shown as a ratio with respect to the result of the normal sample (comparative example No. 11) which was used as a reference. With regard to smearing, it is also observed that the smearing strength (rotational speed before the smearing occurs) of the examples of the present invention is at least 1.5 times as high as that of the normal sample of the comparative example and is somewhat higher than the smearing strength of other comparative examples. The balance established between the fineness of the crystal grains with the grain size number of at least No. 11, an appropriate amount of retained austenite and the presence of fine carbide prevents plastic flow of the surface layer and accordingly improves the anti-seizure property. Samples that were additionally processed exhibit a slight improvement in strength compared with samples without being additionally processed.
Static Crack Strength Test:
For test samples shown in Table 4, crack strength was measured by imposing a load by an Amsler's testing machine on only an outer ring (18.64 mm (inner diameter)×24 mm (outer diameter)×6.9 mm (width)) in the shape as shown in
It is considered that a reason for the deterioration of the strength of comparative example No. 12 is an increased crystal grain size of austenite and an increased amount of retained austenite resulting from a long-term heating in the diffusion process of the carbonitriding so that a structure having a low tensile strength is locally formed. Comparative example No. 13 also deteriorates in strength for the same reason.
Crack Fatigue Strength Test:
Crack fatigue strength was determined by repeatedly imposing a load under conditions shown in Table 7 on an outer ring of the test samples shown in
Results are shown in Table 4. The results of the crack fatigue strength test are represented as a ratio of the strength to the strength of the normal heat-treated sample of the comparative example. It is seen that all examples of the present invention are remarkably improved in crack fatigue strength as compared with comparative examples. Regarding the crack fatigue strength, example No. 3 of the present invention having the carburizing steel as the base component and example No. 6 of the present invention with the carburizing steel as the base component to which the compression residual stress is added are superior in strength.
Softening of the Ends of the Roller Shaft:
The two end surfaces of the roller shaft are high-frequency annealed by bringing only one end of the roller shaft material, which has already been appropriately processed, close to an opening at the end of a high-frequency coil or maintaining the one end in a slightly inserted state in the opening, heating the end for a considerably short period of time by high-frequency induction current and then cooling in the air. Alternatively, after the high-frequency heating and the above-mentioned short-term cooling, rapid cooling may be done by pouring water onto the surface or putting the material into water. A resultant hardness distribution is shown in
As shown in
It can accordingly be confirmed from the above results that the durability is improved of the rolling bearing for the rocker arm that is likely to have a short life due to adverse sliding conditions, skew of rollers and interference of rollers with each other. The improvement of the durability is achieved by processing the material into the one having fine crystal grains and heat resistance and thereby simultaneously improving the surface damage (such surface-initiated exfoliation as peeling and smearing) life as well as the inside-initiated peeling life. Specifically, specific processing of the material or heat treatment pattern is employed to produce a carbonitrided structure which has at least a certain crystal grain size of austenite, which provides remarkably increased resistance against occurrence and growth of cracks. In this way, occurrence of surface cracks can be prevented that is caused by heat generation from the surface layer and tangential stress due to sliding, and a considerably long life can further be achieved against peeling initiated from the internal part. On the basis of this, processing and heat treatment are additionally done to provide a compression residual stress to the surface layer and increase the hardness, so as to further increase the life. These heat treatment and processing include shot peening, barrel finishing, rolling, varnishing, carburizing & carbonitriding, carbonitriding & sub-zero treatment, carbonitriding, secondary quenching & sub-zero treatment, for example.
In a case where caulking is done, for the roller shaft serving as the inner ring which is an element of the bearing, both of the outer surface on the end of the roller shaft as well as the outer region of the end surface are required to be soft enough to plastically deform in the caulking process. On the other hand, the ends of the roller shaft are required to have certain hardness or higher since the roller shaft which is caulked to be fixed to a roller supporting portion could loosen in long-term use of the cam follower, resulting in dropping off from the shaft hole. For the roller shaft having properties added by the above heat treatment and processing, heating and cooling conditions in the high-frequency annealing are adjusted for only the two ends of the roller shaft in order to adjust the hardness of the end surfaces. Then, the roller shaft which can be caulked and is excellent in durability is achieved. In other words, different from the conventional carbonitriding, the above-discussed heat treatment and processing do not deteriorate the crack strength and thus a high-strength and long-life full rolling bearing can be produced. Moreover, the high-frequency annealing is performed on both ends of the roller shaft which is an element of the bearing to adjust the hardness and thereby allow the ends to be caulked.
Accordingly, for a bearing of a rocker arm employed for opening/closing of an intake valve or exhaust valve of an auto engine, for example, a small full-type bearing having a width ranging from 5 mm to 12 mm, the durability of the bearing can be increased while caulking thereof can be done.
JIS-SUJ2 (1.0 wt % of C—0.25 wt % of Si—0.4 wt % of Mn—1.5 wt % of Cr) was used for Example 2 of the present invention. Samples shown in Table 9 were each produced through the procedure described below.
1)evaluation failed due to insufficient quenching
Samples A–D: Examples of the Present Invention
Carbonitriding was performed at 850° C. held for 150 minutes in an atmosphere of a mixture of RX gas and ammonia gas. Following the heat treatment pattern shown in
Samples E and F: Comparative Examples
These samples were carbonitrided through the same procedure as that of samples A–D of the present invention, and then secondary quenched at a temperature from 850° C. to 870° C. equal to or higher than the carbonitriding temperature of 850° C.
Conventional Carbonitrided Sample: Comparative Example
Carbonitriding was performed at 850° C. held for 150 minutes in an atmosphere of a mixture of RX gas and ammonia gas. Quenching was successively done from the carbonitriding temperature and no secondary quenching was done.
Normal Quenched Sample: Comparative Example
Without carbonitriding, quenching was done by increasing the temperature to 850° C. and no secondary quenching was done.
For the samples above, tests were conducted for (1) measuring the amount of hydrogen, (2) measuring crystal grain size, (3) Charpy impact test, (4) measuring fracture stress and (5) rolling fatigue test, by the methods described below.
I. Test Methods for Example 2
(1) Measurement of Hydrogen Amount
The amount of hydrogen was determined by means of a DH-103 hydrogen determinator manufactured by LECO Corporation to analyze the amount of non-diffusible hydrogen in a steel. The amount of diffusible hydrogen was not measured. Specifications of the LECO DH-103 hydrogen determinator are as follows.
Analysis range: 0.01–50.00 ppm
Analysis precision: 0.1 ppm or +3% H (higher one)
Analysis sensitivity: 0.01 ppm
Detection method: thermal conductimetry
Sample weight size: 10 mg–35 g (max: 12 mm (diameter)×100 mm (length))
Furnace temperature range: 50° C.–1100° C.
Reagent: anhydron Mg(ClO4)2, Ascarite and NaOH
Carrier gas: nitrogen gas
Dosing gas: hydrogen gas
(Both gases have a purity of at least 99.99% and a pressure of 40 PSI (2.8 kgf/cm2).)
The procedure of the analysis is roughly described here. A sample was taken by a dedicated sampler and the sample together with the sampler was put into the hydrogen determiner. Diffusible hydrogen therein was directed by the nitrogen carrier gas to a thermal conductimetry detector. The diffusible hydrogen was not measured in this example. Then, the sample was taken out of the sampler to be heated in a resistance heater and non-diffusible hydrogen was directed by the nitrogen carrier gas to the thermal conductimetry detector. The thermal conductivity was measured by the thermal conductimetry detector to determine the amount of non-diffusible hydrogen.
(2) Measurement of Crystal Grain Size
The crystal grain size was measured according to the method of testing the crystal grain size of austenite in a steel defined by JIS G 0551.
(3) Charpy Impact Test
A Charpy impact test was conducted according to the Charpy impact test method for a metal material defined by JIS Z 2242. A test piece used here was a U-notch test piece (JIS No. 3 test piece) defined by JIS Z 2202.
(4) Measurement of Fracture Stress
Suppose that a fiber stress on the convex surface of the test piece shown in
σ1=(N/A)+{M/(Aρo)}[1+e1/{κ(ρo+e1)}]
σ2=(N/A)+{M/(Aρo)}[1−e2/{κ(ρo−e2)}]
κ=—(1/A)∫A{η)}dA
(5) Rolling Fatigue Test
Test conditions for a rolling fatigue life test are shown in Table 10.
II. Results of Tests for Example 2
(1) Amount of Hydrogen
The conventional carbonitrided sample without being additionally processed has a considerably large hydrogen amount of 0.72 ppm. A reason therefor is considered that ammonia (NH3) contained in the atmosphere in the carbonitriding process is decomposed and then hydrogen enters the steel. On the other hand, the hydrogen amount of samples B–D is reduced to 0.37–0.40 ppm and thus almost a half of that of the conventional sample. This amount of hydrogen is substantially equal to that of the normal quenched sample.
The above-mentioned reduction of the hydrogen amount can lessen the degree of embrittlement of the steel that is due to hydrogen in the solid solution. In other words, by the reduction of the hydrogen amount, the Charpy impact value of samples B–D of the present invention is remarkably improved.
(2) Crystal Grain Size
Regarding the crystal grain size, samples that are secondary quenched at a temperature lower than the quenching temperature in the carbonitriding process (primary quenching), namely samples B–D have austenite grains which are remarkably made fine, i.e., crystal grain size number is 11–12. Samples E and F as well as the conventional carbonitrided sample and the normal quenched sample have austenite grains with the crystal grain size number of 10, which means that the crystal grain size of samples E and F is greater than that of samples B–D of the present invention.
(3) Charpy Impact Test
Table 9 shows that the Charpy impact value of the conventional carbonitrided sample is 5.33 J/cm2 while that of samples B–D of the present invention is higher, ranging from 6.30 to 6.65 J/cm2. It is also seen from this that a lower secondary quenching temperature leads to a higher Charpy impact value. The normal quenched sample has a high Charpy impact value of 6.70 J/Cm2.
(4) Measurement of Fracture Stress
The fracture stress corresponds to anti-crack strength. It is seen from Table 9 that the fracture stress of the conventional carbonitrided sample is 2330 MPa. On the other hand, the fracture stress of samples B–D is improved to 2650–2840 MPa. The normal quenched sample has a fracture stress of 2770 MPa which is in the range of the fracture stress of samples B–F. It is considered that the reduction in hydrogen content greatly contributes to the improved anti-crack strength of samples B–D as well as the reduction in size of austenite crystal grains.
(5) Rolling Fatigue Test
According to Table 9, the normal quenched sample has the shortest rolling fatigue life (L10) due to the absence of carbonitrided layer in the surface layer. In contrast, the rolling fatigue life of the conventional carbonitrided sample is 3.1 times as long as that of the normal quenched sample. The rolling fatigue life of samples B–D is remarkably improved as compared with the conventional carbonitrided sample. Samples E and F of the present invention have the rolling fatigue life almost equal to that of the conventional carbonitrided sample.
In summary, samples B–D of the present invention have the lower hydrogen content, finer austenite crystal grains with the crystal grain size number of at least 11, and improved Charpy impact value, anti-crack strength and rolling fatigue life.
Example 3 of the present invention is now described. On the following samples A, B and C, a series of tests was conducted. A material to be heat-treated that was employed commonly to samples A–C was JIS-SUJ2 (1.0 wt % of C-0.25 wt % of Si-0.4 wt % of Mn-1.5 wt % of Cr). Samples A–C were each processed through the following procedure.
Sample A—comparative example: normal quenching only (without carbonitriding)
Sample B—comparative example: quenching directly after carbonitriding (conventional carbonitriding and quenching) Carbonitriding was conducted at 845° C. held for 150 minutes. The atmosphere in the carbonitriding process was a mixture of RX gas and ammonia gas.
Sample C—example of the present invention: A bearing material was processed following the heat treatment pattern shown in
(1) Rolling Fatigue Life
Test conditions and the test device for the rolling fatigue life test are as shown in Table 10 and
According to Table 11, sample B which is a comparative example has a rolling fatigue life (L10 life: one out of ten test pieces being damaged) that is 3.1 times as long as that of sample A which is also a comparative example and undergoes normal quenching only, and thus it is seen that the effect of extending the life is obtained through the carbonitriding process. In contrast, sample C of the present invention has a longer life which is 1.74 times as long as that of sample B and 5.4 times as long as that of sample A. It is considered that this improvement is obtained mainly from the fine microstructure.
(2) Charpy Impact Test
A Charpy impact test was conducted by using a U-notch test piece defined by JIS Z 2242 mentioned above. Test results are shown in Table 12.
Sample B (comparative example) having undergone carbonitriding has a Charpy impact value which is not larger than that of sample A (comparative example) having undergone normal quenching, while sample C has a Charpy impact value equivalent to that of sample A.
(3) Static Fracture Toughness Test
KIc=(PL√a/BW2){5.8−9.2(a/W)+43.6(a/W)2−75.3(a/W)3+77.5(a/W)4}. . . (I)
m)
As the pre-crack has a depth greater than the depth of the carbonitrided layer and thus the same results are obtained for samples A and B (comparative examples), while the result for sample C (example of the present invention) is approximately 1.2 times as high as that of the comparative examples.
(4) Static-Pressure Fracture-Strength Test (Measurement of Fracture Stress)
A static-pressure fracture-strength test piece as shown in
Sample B having been carbonitrided has a strength somewhat smaller than that of sample A having undergone normal quenching, while sample C of the present invention has an improved static-pressure fracture-strength compared with sample B and is thus equivalent to that of sample A.
(5) Rate of Secular Dimensional Change
Table 15 shows the rate of secular dimensional change measured under the conditions of 130° C. (holding temperature) and 500 hours (holding time), together with the surface hardness and the amount of retained austenite (0.1 mm depth).
As compared with the rate of dimensional change of sample B having a large amount of retained austenite, sample C of the present invention has the smaller rate of dimensional change due to the lower amount of retained austenite which is one-half or less.
(6) Life Test Under Contaminated Lubricant Condition
Ball bearing 6206 was used to evaluate the rolling fatigue life under a contaminated lubricant condition having a predetermined amount of normal contaminants mixed therein. Test conditions are shown in Table 16 and test results are shown in Table 17.
Sample B having undergone conventional carbonitriding has a lifetime which is approximately 2.5 times as long as that of sample A, and sample C of the present invention has a lifetime which is approximately 2.3 times as long as that of sample A. While sample C of the present invention has a smaller amount of retained austenite than that of sample B of the comparative example, sample C has a long lifetime substantially equivalent to that of sample B because of influences of entering nitrogen and the fine microstructure.
It is accordingly seen from the above-discussed results that, sample C of the present invention, namely a bearing component produced by the heat treatment method of the present invention can simultaneously achieve three goals: extension of the rolling fatigue life that has been difficult to achieve by the conventional carbonitriding, improvement in crack strength and reduction of the rate of secular dimensional change.
Although the present invention has been described and illustrated in detail, it is clearly understood that the same is by way of illustration and example only and is not to be taken by way of limitation, the spirit and scope of the present invention being limited only by the terms of the appended claims.
Number | Date | Country | Kind |
---|---|---|---|
2002-303036 | Oct 2002 | JP | national |
2003-053505 | Feb 2003 | JP | national |
Number | Name | Date | Kind |
---|---|---|---|
3954517 | Jatczak et al. | May 1976 | A |
4162419 | DeAngelis | Jul 1979 | A |
4930909 | Murakami et al. | Jun 1990 | A |
4971634 | Shibata et al. | Nov 1990 | A |
5085733 | Mitamura | Feb 1992 | A |
5129966 | Rao | Jul 1992 | A |
5137375 | Murakami et al. | Aug 1992 | A |
5180450 | Rao | Jan 1993 | A |
5338377 | Mitamura et al. | Aug 1994 | A |
5352303 | Murakami et al. | Oct 1994 | A |
5375323 | Sata | Dec 1994 | A |
5413643 | Murakami et al. | May 1995 | A |
5427457 | Furumura et al. | Jun 1995 | A |
5427600 | Itoh et al. | Jun 1995 | A |
5456136 | Yamashita et al. | Oct 1995 | A |
5456766 | Beswick et al. | Oct 1995 | A |
5595610 | Maeda et al. | Jan 1997 | A |
5611250 | Narai et al. | Mar 1997 | A |
5658082 | Tsushima et al. | Aug 1997 | A |
5772956 | Hasegawa et al. | Jun 1998 | A |
5775280 | Schmidt et al. | Jul 1998 | A |
5803993 | Yoshida et al. | Sep 1998 | A |
5848846 | Sugiyama et al. | Dec 1998 | A |
5853249 | Maeda et al. | Dec 1998 | A |
5944916 | Chung | Aug 1999 | A |
5972130 | Underys et al. | Oct 1999 | A |
5979383 | Faville et al. | Nov 1999 | A |
6012851 | Hirakawa et al. | Jan 2000 | A |
6086686 | Tanaka et al. | Jul 2000 | A |
6095692 | Takemura | Aug 2000 | A |
6149734 | Isogai et al. | Nov 2000 | A |
6158263 | Maeda et al. | Dec 2000 | A |
6165289 | Matsumoto et al. | Dec 2000 | A |
6224688 | Takemura et al. | May 2001 | B1 |
6251198 | Koo et al. | Jun 2001 | B1 |
6258179 | Takayama et al. | Jul 2001 | B1 |
6290398 | Fujiwara et al. | Sep 2001 | B1 |
6306227 | Okayama et al. | Oct 2001 | B2 |
6328009 | Brothers | Dec 2001 | B1 |
6342109 | Takemura et al. | Jan 2002 | B1 |
6423158 | Maeda et al. | Jul 2002 | B1 |
6440232 | Takemura et al. | Aug 2002 | B1 |
6447619 | Takayama et al. | Sep 2002 | B1 |
6488789 | Tajima et al. | Dec 2002 | B2 |
6532920 | Sweetnam et al. | Mar 2003 | B1 |
6582532 | Kurebayashi et al. | Jun 2003 | B1 |
6602358 | Ochi et al. | Aug 2003 | B1 |
6641680 | Nishimori et al. | Nov 2003 | B2 |
6699335 | Murakami et al. | Mar 2004 | B2 |
6855217 | Suzuki | Feb 2005 | B2 |
7147382 | Suzuki et al. | Dec 2006 | B2 |
20020082133 | Yoshikawa et al. | Jun 2002 | A1 |
20020088511 | Nakamura et al. | Jul 2002 | A1 |
20030037635 | Tsuchiyama et al. | Feb 2003 | A1 |
20030040401 | Okita et al. | Feb 2003 | A1 |
20030075244 | Kurebayashi et al. | Apr 2003 | A1 |
20030123769 | Ohkl | Jul 2003 | A1 |
20040170348 | Okugami et al. | Sep 2004 | A1 |
20040170761 | Li et al. | Sep 2004 | A1 |
20040179761 | Ohki et al. | Sep 2004 | A1 |
20040228561 | Okugami et al. | Nov 2004 | A1 |
20050045247 | Ohki | Mar 2005 | A1 |
20050109308 | Suzuki et al. | May 2005 | A1 |
20050205163 | Ohki et al. | Sep 2005 | A1 |
20070034301 | Hasegawa et al. | Feb 2007 | A1 |
20070169850 | Ohki et al. | Jul 2007 | A1 |
Number | Date | Country |
---|---|---|
1421541 | Jun 2003 | CN |
42 04 982 | Aug 1993 | DE |
1 996 0803 | Jun 2000 | DE |
1 025 4635 | Jun 2003 | DE |
0 458 646 | Nov 1991 | EP |
0 600 421 | Jun 1994 | EP |
0 626 468 | Nov 1994 | EP |
0 723 034 | Jul 1995 | EP |
0 811 789 | Dec 1997 | EP |
0 811 789 | Dec 1997 | EP |
0 950 723 | Oct 1999 | EP |
0 950 723 | Oct 1999 | EP |
1 070 760 | Jan 2001 | EP |
1 158 064 | Nov 2001 | EP |
1 273 672 | Jan 2003 | EP |
1 411 142 | Apr 2004 | EP |
2 841 907 | Jan 2004 | FR |
2 258 274 | Feb 1993 | GB |
2 258 274 | Feb 1993 | GB |
48-028308 | Apr 1973 | JP |
63-185917 | Nov 1988 | JP |
02-125841 | May 1990 | JP |
2-190615 | Jul 1990 | JP |
03-116706 | Dec 1991 | JP |
4-254574 | Sep 1992 | JP |
05-009584 | Jan 1993 | JP |
5-163563 | Jun 1993 | JP |
5-179350 | Jul 1993 | JP |
5-263091 | Oct 1993 | JP |
6-101424 | Apr 1994 | JP |
06-117438 | Apr 1994 | JP |
6-247253 | Sep 1994 | JP |
6-286577 | Oct 1994 | JP |
6-341441 | Dec 1994 | JP |
07-027139 | Jan 1995 | JP |
08004774 | Jan 1996 | JP |
8-49057 | Feb 1996 | JP |
08-233070 | Sep 1996 | JP |
09-053148 | Feb 1997 | JP |
9-176740 | Jul 1997 | JP |
9-316601 | Dec 1997 | JP |
9-329139 | Dec 1997 | JP |
10-030150 | Feb 1998 | JP |
10-47334 | Feb 1998 | JP |
10-68419 | Mar 1998 | JP |
10-103339 | Apr 1998 | JP |
10-110720 | Apr 1998 | JP |
10-168515 | Jun 1998 | JP |
10-184701 | Jul 1998 | JP |
10-204612 | Aug 1998 | JP |
11-80897 | Mar 1999 | JP |
11101247 | Apr 1999 | JP |
11-140543 | May 1999 | JP |
11-303874 | Nov 1999 | JP |
2000-038906 | Feb 2000 | JP |
2000-38907 | Feb 2000 | JP |
2000-54810 | Feb 2000 | JP |
2000-129347 | May 2000 | JP |
2000-205284 | Jul 2000 | JP |
2000-212721 | Aug 2000 | JP |
2001-123244 | May 2001 | JP |
2001-200314 | Jul 2001 | JP |
2002-31212 | Jan 2002 | JP |
2002-070872 | Mar 2002 | JP |
2002-120508 | Apr 2002 | JP |
2002-180203 | Jun 2002 | JP |
2002-194438 | Jul 2002 | JP |
2002-256336 | Sep 2002 | JP |
2002-339054 | Nov 2002 | JP |
2003-56315 | Feb 2003 | JP |
2003-083337 | Mar 2003 | JP |
2003-083339 | Mar 2003 | JP |
2003-156050 | May 2003 | JP |
2003-226918 | Aug 2003 | JP |
2003-226919 | Aug 2003 | JP |
2003-287035 | Oct 2003 | JP |
2003-294034 | Oct 2003 | JP |
WO 9100929 | Jan 1991 | WO |
WO 0240730 | May 2002 | WO |
Number | Date | Country | |
---|---|---|---|
20040079310 A1 | Apr 2004 | US |