The present invention relates to the display technical field, in particular to a functional material and a method for preparing the same, as well as a three-dimensional display raster and a display device.
Naked eye three-dimensional display is a type of three-dimensional display (3D display), and refers to a technology in which users can obtain three-dimensional display effects without the need to wear polarized glasses.
As shown in
Nonetheless, the display panel of a three-dimensional display device will inevitably produce some electromagnetic radiation pollution during use, which will affect human health.
Regarding the problem that current three-dimensional display devices will produce pollution, the present invention provides an environmentally friendly functional material which can play a role in heath care and a method for preparing the same, as well as a three-dimensional display raster and a display device.
One technical solution employed to address a technical problem of the present invention is a functional material comprising an inorganic mixed powder whose surface has a modified layer, the inorganic mixed powder comprising a primary ingredient and a secondary ingredient;
the primary ingredient consisting of boron oxide, sodium oxide, lithium oxide, and zirconium oxide;
the secondary ingredient including any one or more of aluminum oxide, zinc oxide, titanium dioxide, silicon dioxide, calcium oxide, silver complexes, silver phosphate, silver nitrate, tourmaline, silver thiosulfate, carbon nanotubes, aluminum sulfate, manganese, manganese oxide, iron, iron oxide, cobalt, cobalt oxide, nickel, nickel oxide, chromium, chromium oxide, copper, copper oxide, magnesium oxide, boron carbide, silicon carbide, titanium carbide, zirconium carbide, tantalum carbide, molybdenum carbide, boron nitride, chromium nitride, titanium nitride, zirconium nitride, aluminum nitride, chromium boride, Cr3B4, titanium boride, zirconium boride, tungsten disilicide, and titanium disilicide; and the modified layer being generated by a reaction of a dianhydride and a diamine.
For example, the molar ratio of the dianhydride to the diamine for generating the modified layer is between 0.85:1 and 1.05:1.
More preferably, the molar ratio of the dianhydride to the diamine for generating the modified layer is between 0.92:1 and 1.05:1.
For example, the dianhydride for generating the modified layer comprises at least one phenyl group, and the diamine for generating the modified layer comprises at least one phenyl ring or at least one non-phenyl six-membered carbocyclic ring.
More preferably, the dianhydride for generating the modified layer is selected from any one of pyromellitic dianhydride, trimellitic anhydride, benzophenone dianhydride, biphenyl dianhydride, diphenyl ether dianhydride, and 4,4′-(hexafluoroisopropylidene) diphthalic anhydride; the diamine for generating the modified layer is selected from any one of 3-amino-benzylamine, 2,2′-difluoro-4,4′-(9-fluorenylidene) dianiline, 2,2-bis(3-amino-4-hydroxyphenyl) hexafluoropropane, hexahydro-m-xylylene diamine, 1,4-bis(aminomethyl)cyclohexane, 2,2-bis[4-(4-aminophenoxy)phenyl] hexafluoropropane, 2,2-bis(3-amino-4-methylphenyl) hexafluoropropane, 2,2-bis(3-aminophenyl) hexafluoropropane, 2,2-bis(4-aminophenyl) hexafluoropropane, 2,7-diamino-fluorene, m-xylylene diamine, and 4,4′-methylene bis(2-ethyl-6-methylaniline).
For example, the inorganic mixed powder has a particle diameter of 1 to 5000 nm.
One technical solution employed to solve a technical problem of the present invention is a method for preparing the above functional material, comprising: mixing the inorganic mixed powder, the dianhydride, and the diamine with an initiator and a solvent uniformly; and
reacting the dianhydride with the diamine by heating to form the modified layer on the surface of the inorganic mixed powder.
For example, the mass ratio of the inorganic mixed powder to the substance generated by the reaction of the dianhydride and the diamine is between 20:1 and 1:1.
More preferably, the initiator is any one of azo bisisobutyronitrile, 2,2′-azo-bis-(2,4-dimethylvaleronitrile), dimethyl azobisisobutyrate and azo bisisovaleronitrile.
For example, the heating comprises two steps: heating at a temperature of 35 to 70° C. for 20 to 40 min; and heating at a temperature of 70 to 100° C. for 20 to 40 min.
One technical solution employed to solve a technical problem of the present invention is a three-dimensional display raster comprising a raster body comprising a shade strip and a transparent strip which are alternately arranged, wherein the surface and/or interior of the raster body comprise(s) the above functional material.
For example, the interior of the raster body comprises the functional material in an amount of 0.1 to 30% by mass; and/or, the surface of the raster body has a surface film layer with a thickness of 50 to 1000 nm which comprises the functional material in an amount of 0.1 to 10% by mass.
More preferably, the interior of the raster body comprises the functional material in an amount of 3 to 20% by mass; and/or, the surface film layer comprises the functional material in an amount of 0.5 to 5% by mass.
One technical solution employed to solve a technical problem of the present invention is a three-dimensional display device comprising a display panel and the above three-dimensional display raster.
Functional materials of the present invention can emit far-infrared light and negative ions. Far-infrared light, after being absorbed by a human body, can allow water molecules in the body to resonate and be activated, which enhances the intermolecular bonding force, thereby activating proteins and other biological macromolecules and bringing the organism cells to the highest vibration level. Furthermore, far-infrared heat can be transferred to a subcutaneous deeper part, thus increasing the temperature of the subcutaneous deeper part, expanding the capillaries, promoting the blood circulation, strengthening the metabolism among tissues, promoting a tissue regeneration capacity, enhancing the organism immunity, and bringing the vivacity. On the other hand, negative ions can decompose and oxidize bacteria and organic substances, and may serve the function of disinfection and sterilization and produce the effect of improving air quality. Therefore, the functional material may play a role in health care and is environmentally friendly.
The surface of the inorganic mixed powder in the functional material according to the present invention has a modified layer, which can allow the inorganic mixed powder to bond well with the raster body and can further improve the inorganic mixed powder's capacity to emit far-infrared light and negative ions, so that the functional material is well incorporated into the three-dimensional display raster to increase its environmental friendliness without affecting the performance of the three-dimensional display raster itself.
wherein the reference signs are:
To enable those skilled in the art to better understand the technical solution of the present invention, further detailed descriptions are made for the present invention with reference to the drawings and embodiments.
The present embodiment provides a functional material and a method for preparing the same.
The functional material comprises an inorganic mixed powder having a modified layer on its surface, the inorganic mixed powder comprising a primary ingredient and a secondary ingredient;
the primary ingredient consisting of boron oxide, sodium oxide, lithium oxide, and zirconium oxide;
the secondary ingredient including any one or more of aluminum oxide, zinc oxide, titanium oxide, silicon dioxide, calcium oxide, silver complexes, silver phosphate, silver nitrate, tourmaline, silver thiosulfate, carbon nanotubes, aluminum sulfate, manganese, manganese oxide, iron, iron oxide, cobalt, cobalt oxide, nickel, nickel oxide, chromium, chromium oxide, copper, copper oxide, magnesium oxide, boron carbide, silicon carbide, titanium carbide, zirconium carbide, tantalum carbide, molybdenum carbide, boron nitride, chromium nitride, titanium nitride, zirconium nitride, aluminum nitride, chromium boride, Cr3B4, titanium boride, zirconium boride, tungsten disilicide, and titanium disilicide; and
the modified layer being generated by reaction of a dianhydride and a diamine.
The particle diameter of the inorganic mixed powder is from nanometers to micrometers, specifically, for example, from 1 to 5000 nm, preferably from 10 to 500 nm. The particle diameter can be measured, for example, by a Malvern laser particle size analyzer.
Dianhydride refers to a substance containing at least two anhydride groups in the molecular structure; while diamine refers to a substance containing at least two amine groups (or amino groups) in the molecular structure.
The dianhydride, for example, contains at least one phenyl group, and is preferably any one of pyromellitic dianhydride, trimellitic anhydride, benzophenone dianhydride, biphenyl dianhydride, diphenyl ether dianhydride, and 4,4′-(Hexafluoroisopropylidene)diphthalic anhydride.
The diamine, for example, contains at least one phenyl ring or at least one non-phenyl six-membered carbocyclic ring (e.g. cyclohexane), preferably any one of 3-amino-benzylamine, 2,2′-difluoro-4,4′-(9-fluorenyl idene) dianiline, 2,2-bis(3-amino-4-hydroxyphenyl) hexafluoropropane, hexahydro-m-xylylene diamine, 1,4-bis(aminomethyl) cyclohexane, 2,2-bis[4-(4-aminophenoxy)phenyl] hexafluoropropane, 2,2-bis(3-amino-4-methylphenyl) hexafluoropropane, 2,2-bis(3-aminophenyl) hexafluoropropane, 2,2-bis(4-aminophenyl) hexafluoropropane, 2,7-diamino-fluorene, m-xylylene diamine, and 4,4′-methylene bis(2-ethyl-6-methylaniline).
The molar ratio of the dianhydride to the diamine is from 0.85:1 to 1.05:1, preferably from 0.92:1 to 1.05:1.
Our studies have revealed that the modified layer generated by reaction of the above dianhydride and diamine can desirably improve the properties of the inorganic mixed powder.
Functional materials of the present embodiment can emit far-infrared light and negative ions. Far-infrared light, after being absorbed by a human body, can allow water molecules in the body to resonate and be activated, which enhances the intermolecular bonding force, thereby activating proteins and other biological macromolecules and bringing the organism cells to the highest vibration level. Furthermore, far-infrared heat can be transferred to a subcutaneous deeper part, thus increasing the temperature of the subcutaneous deeper part, expanding the capillaries, promoting the blood circulation, strengthening the metabolism among tissues, promoting a tissue regeneration capacity, enhancing the organism immunity, and bringing the vivacity. On the other hand, negative ions can decompose and oxidize bacteria and organic substances, and may serve the function of disinfection and sterilization and produce the effect of improving air quality. Therefore, the functional material may play a role in health care and is environmentally friendly.
The method for preparing the above functional material comprises: mixing the inorganic mixed powder, the dianhydride, and the diamine with an initiator and a solvent uniformly; and reacting the dianhydride with the diamine by heating to form the modified layer on the surface of the inorganic mixed powder.
To be specific, as shown in
S01, in the case of using a dispersant, pulverizing the raw materials respectively into powder and mixing the same uniformly in proportion, or mixing the raw materials in proportion uniformly and then pulverizing the same, to yield an inorganic mixed powder;
wherein the dispersant may be chosen from conventional dispersants such as BYK 161 manufactured by BYK Additives & Instruments and Solsperse 32500 and Solsperse 22000 manufactured by The Lubrizol Corporation; pulverization may be carried out using conventional methods such as ball milling, grinding, and the like; as the inorganic mixed powder may be prepared by existing methods, no further details will be provided herein.
S02, dissolving from a fourth to a third of an initiator and from a fourth to a third of a diamine in a solvent for later use.
The mass ratio of the inorganic mixed powder to the substance generated by the reaction of the dianhydride and the diamine is from 20:1 to 1:1.
That is to say, the amounts of the dianhydride and the diamine are determined as follows: assuming a complete reaction between the dianhydride and the diamine to yield a resultant (which is actually a modified layer), if the mass of the resultant is 1, then the mass of the inorganic mixed powder is between 1 and 20; such an amount can ensure that a modifier layer with a suitable thickness can be obtained on the inorganic mixed powder.
An initiator is used to initiate the reaction, which, for example, is a nitrogen-based initiator, preferably any one of azo bisisobutyronitrile, 2,2′-azo bis(2,4-dimethylvaleronitrile), dimethyl azo bisisobutyrate, and azo bisisovaleronitrile.
The solvent can be selected from fatty alcohols, glycol ethers, ethyl acetate, methyl ethyl ketone, methyl isobutyl ketone, ethylene glycol monomethyl ether, γ-butyrolactone, ethyl 3-ethoxypropionate, butyl carbitol, butyl carbitol acetate, propylene glycol monomethyl ether, propylene glycol monomethyl ether acetate, cyclohexane, xylene, isopropanol, and other conventional organic solvents. Since the choice of the solvent has no significant effect on the performance of the final product, propylene glycol monomethyl ether acetate is used in all the Examples as the solvent.
S03, adding the inorganic mixed powder to a reaction vessel (e.g., a four-neck flask) which is then subjected to stirring, shocking, shaking and the like; afterwards, adding the dianhydride and the solvent as well as the remaining initiator and diamine and allowing them to be dissolved uniformly.
S04, heating to carry out the reaction for example in two steps, specifically comprising: heating at a temperature of 35 to 70° C. for 20 to 40 min; and then continuing heating at a temperature of 70 to 100° C. for 20 to 40 min.
During the above heating process, the dianhydride and the diamine are allowed to react, thereby generating a modified layer on the surface of the inorganic mixed powder; wherein heating is carried out in two steps so as to prevent the reaction from being too severe.
During the reaction process, the above solution prepared by dissolving an initiator and a diamine is gradually added dropwise to a four-neck flask so as to prevent the reaction from being too severe.
The reaction in this step may be carried out, for example, under the protection of nitrogen, and for example under constant stirring.
The solvent in each step is in an amount sufficient to disperse and dissolve the substances therein uniformly, while the initiator is in an amount sufficient to initiate the reaction, which can be adjusted by those skilled in the art based on the actual conditions, and thus no further detail is given herein. However, the mass ratio (all referring to the total amount) of the inorganic mixed powder, the initiator and the solvent is generally 1:(from 0.25 to 0.4):(from 1 to 1.5). To achieve consistency in the process of preparing the functional material in the various Examples, the mass ratio of the inorganic powder, the initiator and the solvent is 1:0.3:1.4.
S05, cooling the reactant with a refrigerated solvent to room temperature (at about 10 to 30° C.) after the reaction is complete.
S06, evaporating the remaining solvent or separating the powder therefrom, to yield an inorganic mixed powder with a modified layer, i.e., a functional material.
Of course, it should be appreciated that the preparation method described above may undergo a number of variations, e.g., the dianhydride, the diamine, and the initiator can be dissolved once in the solvent; for another example, heating can be carried out in one step. After all, any variation is allowed as long as the dianhydride and the diamine can react to form a modified layer on the surface of the inorganic mixed powder.
The infrared emissivity of the functional material is measured according to the GB/T 7287-2008 standard test, and the amount of anions generated by the functional material is measured using an air anion analyzer (for example, Japan KEC Corporation's KEC-900 type).
Various functional materials were prepared according to the method described above, where the materials, amounts, parameters and product properties are shown in the following tables.
As can be seen from the above, all the functional materials of the Examples have a high infrared emissivity and a high anion concentration, which indicates that they actually can produce far-infrared light and anions, thereby improving the environment.
As shown in
The above functional material 3 is provided in the interior of the raster body 21 and/or on the surface of the raster body 21.
In another word, the above functional material 3 is applied to the interior and/or surface of the raster body 21 so as to improve the environmental friendliness of the three-dimensional display raster 2.
For example, the mass percentage of the functional material 3 in the interior of the raster body 21 is 3 to 20%; and/or, the surface of the raster body 21 has a surface film layer 22 with a thickness of 50 to 1000 nm which contains the functional material 3, wherein the mass percentage of the functional material 3 in the surface film layer 22 is 0.1 to 10%.
In other words, the functional material 3 can be directly incorporated into the raster body 21. Specifically, the functional material 3 can be added to the materials (e.g., polyethylene terephthalate particles, polyvinyl alcohol particles) for preparing the raster body 21. As such, in the process of heating and melting these materials to form the raster body 21, the functional material 3 will naturally be formed inside the raster body 21 directly and its mass percentage (based on the total mass 100% of the raster body 21 and the functional material 3) is, for example, 0.1 to 30%, preferably 3 to 20%.
Alternatively, the functional material 3 is distributed in a surface film layer 22 provided on the surface of the raster body 21. Specifically, the functional material 3 can be dispersed in a solvent to form a suspension, which is then applied to the surface of the raster body 21 by means of coating, spraying and the like. After curing, a surface film layer 22 having a thickness of 50 to 1000 nm is formed on the surface of the raster body 21, wherein the mass percentage (based on the total mass 100% of the surface film layer 22 and the functional material 3) of the functional material 3 is, for example, 0.1 to 10%, preferably 0.5 to 5%.
Apparently, while the functional material 3 is environmentally beneficial, if an excessive amount thereof is used, then the properties of the raster 2 itself will be affected. Our study reveals that the functional material 3 within the above content range is environmentally beneficial without notably affecting the properties of the three-dimensional display raster 2 itself, and therefore is preferable.
By observing the three-dimensional display raster 2 of the present embodiment, it was found out that the functional material 3 therein did not involve any phenomenon such as agglomeration, shedding, etc., which suggests that the functional material 3 could be well bonded to the three-dimensional display raster 2.
The surface of the inorganic mixed powder in the functional material 3 of the present embodiment has a modified layer which can allow the inorganic mixed powder to bond well to a raster body 21 and can improve the inorganic mixed powder's capacity to emit far-infrared light and negative ions, so that the functional material 3 can be well incorporated into the three-dimensional display raster 2 to increase its environmental friendliness without affecting the performance of the three-dimensional display raster 2 itself.
The three-dimensional display device of the present embodiment comprises a display panel 1 and the above three-dimensional display raster 2 provided outside the light-exiting surface of the display panel 1.
It should be appreciated that the above embodiments are merely exemplary embodiments to illustrate the principles of the present invention, but the present invention is not limited thereto. Those of ordinary skill in the art, without departing from the spirit and essence of the present invention, may make various changes and improvements. Such changes and improvements are deemed within the scope of the invention.
The present application claims the priority of the Chinese Patent Application No. 201410367829.5 filed on Jul. 29, 2014, which is incorporated herein by reference as part of the present application.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201410367829.5 | Jul 2014 | CN | national |