Patent Application
20090202644
The present invention provides carbon nanotubes (CNTs) filled with a suspension or colloidal solution of functional nanoparticles. The present invention also provides methods for production of CNTs loaded with functional nanoparticles. In one embodiment, CNTs filled with magnetic nanoparticles and methods for their production are provided. In other embodiments CNTs filled with gold colloidal nanoparticles and nanodiamonds are described.
The unique physico-chemical properties of carbon nanotubes (CNTs) has initiated extensive research into their possible applications in various areas of engineering (Baughman et al. Science 2002 297, 787-792; Rossi et al. Nano Letters 2004 4, 989-993; Tolles, W. M. and Rath, B. B. Current Science 2003 85, 1746-1759; Gogotsi, Y. Materials Research Innovations 2003 7, 192-194; Lin et al. Journal of Materials Chemistry 2004 14, 527-541).
The unique conductive properties of CNTs have attracted engineers to investigate methods to make CNTs magnetic as well (Gao et al. Carbon 2004 42:47-52; Coey, J. M. D. and Sanvito, S. Physics World 2004). To the best of the inventors' knowledge, previous attempts have had limited success.
For example, nanotubes with magnetic particles imbedded into CNTs during synthesis do not have useful magnetic properties. Further, the amount and location of the magnetic material inside the tube is difficult to control.
Techniques disclosed thus far for producing magnetic needles, are expensive, time-consuming (Singh et al. Journal of Nanoscience and Nanotechnology 2003 3:165-170), and have a relatively low yield. When increasing magnetization of magnetic needles, it is also important to prevent nanoneedles from agglomeration when magnetic field is not applied. Thus, encapsulating paramagnetic particles into CNT is desirable as it makes magnetic needles stable.
The phenomenon of spontaneous penetration of fluids into wettable capillaries has been taken as a guiding idea to load nanotubes with magnetic nanoparticles. As known from everyday experience, when a capillary is set in contact with a wetting fluid, the fluid spontaneously penetrates inside. This method of filling of nanotubes with molten metals has been suggested (Ajayan, P. M. and Iijima, S. Nature 1993 361:333-334; Dujardin et al. Science 1994 265:1850-1852; Ugarte et al. Science 1996 Science 274:1897-1899). Drawbacks of using the melts in this manner, however, include time consumption in that such methods are quite tedious and include the unpredictable step of nanotube opening. Further, the filling efficiency is too low to consider this method for large scale production. In addition, ferrous metals, which are of interest for magnetic applications, have high melting points (1565° C.) and can react with carbon.
U.S. Pat. No. 5,457,343 discloses nanometer sized carbon tubules enclosing a foreign material. The foreign material is introduced into the nanotube by forming an opening at the top portion of the carbon tubule either by contacting the foreign material with the top portion of the carbon tubule together with a heat treatment or by evaporation of the foreign material on the top portion of the carbon tubule together with heat treatment.
U.S. Pat. No. 5,543,378 discloses a carbon nanostructure having a palladium crystallite encapsulated therein.
U.S. Pat. No. 6,090,363 discloses a method for making carbon nanotubes open on at least one end by treating capped nanotubes with an oxidizing acid such as nitric acid. This patent also discloses methods for depositing materials into the carbon nanotubes once opened.
U.S. Pat. No. 6,129,901 discloses a method for producing uniform sized and uniformly aligned nanotubes and filling these nanotubes with metals using, for example electroless deposition.
Chemical vapor deposition (CVD) CNTs produced by template synthesis can be filled with water (Rossi et al. Nano Letters 2004 4:989-993; Naguib et al. Abstracts of Papers of the American Chemical Society Annual Meeting 2003 226:U535), ethylene glycol, hydrocarbons, and other liquids. Further, recent demonstration on a coulter-counter (Henriquez et al. Analyst 2004 129:478-482) shows that particulate flow inside nanotubes is possible.
An object of the present invention is to provide a method for producing carbon nanotubes loaded with functional nanoparticles which comprises synthesizing open carbon nanotubes and filling the open carbon nanotubes with a suspension of functional nanoparticles or a colloidal solution of functional nanoparticles. In one embodiment, the carbon nanotubes are synthesized by chemical vapor deposition of the carbon nanotubes onto an internal wall of a template. Carbon nanotubes are filled with the suspension of functional nanoparticles or colloidal solution of functional nanoparticle either before or after separation of the carbon nanotubes from the template.
Another object of the present invention is to provide a carbon nanotube loaded with functional nanoparticles. In one embodiment a magnetic carbon nanotube is provided comprising a hollow carbon nanotube filled with a suspension of magnetic nanoparticles. In this embodiment, the carbon nanotube is preferably filled with a ferrofluid. In other embodiments the hollow carbon nanotubes are filled with functional nanoparticles such as, but not limited to, colloidal gold nanoparticles and non-metallic diamond nanoparticles.
a) and (b) are transmission electron microscope (TEM) images of CNTs filled with organic-based ferrofluid EMG 911.
a) and (b) show the process of filling of individual nanotubes.
a), (b) and (c) show manipulation of magnetic nanotubes by magnetic field.
a) and 8(b) are TEM images of CNTs filled with nanodiamond particles.
The present invention relates to methods for producing carbon nanotubes (CNTs) loaded with functional nanoparticles. In these methods, open CNTs are synthesized. Any method for synthesis of open CNTs can be used. An exemplary method is synthesis via chemical vapor deposition onto a template such as an alumina membrane. The open CNTs are then filled with a suspension of functional nanoparticles or a colloidal solution of functional nanoparticles. Because dragging of nanoparticles into nanotubes is mostly affected by the process of initial enforcement of the fluid body as a whole continuum (Kornev K. G. and Neimark, A. V. Journal of Colloid Interface Science 2003 262:253-262), it is expected that inertia-dominated flow will provide a useful means for filling the open CNTs. Once filled, the CNTs are sealed using various known methodologies. In one embodiment, the CNT tips are selectively sealed with polypirrol using bipolar electrochemistry (Bradley et al. Chemistry Preprint Archive 2003 3:245-250). Effects of functional nanoparticle separation in the filled nanotubes are expected to occur only at the late stage of penetration when quasi-stationary menisci have already formed (Karnis A. and Mason, S. G. Journal of Colloid and Interface Science 1967 23:120).
The methodologies described herein were used to produce CNTs loaded with functional magnetic nanoparticles. The resulting magnetic structures, also referred to herein as magnetic needles, are useful in numerous applications including but not limited to nanotechnology, memory devices and medicine.
As shown herein, the methodologies of the present invention provide a simple and versatile technique to produce magnetic tubes by filling CNTs with paramagnetic, iron oxide particles (approximately 10 nm in diameter). In this exemplary embodiment, commercial fluids were used to fill chemically vapor deposited CNTs with average outer diameter 300 nm. Examination of the filled nanotubes by transmission electron microscope (TEM) showed a high density of particles inside the CNT. Experiments using an external magnetic field demonstrated that almost 100% of the nanotubes became magnetic and could be easily manipulated in a magnetic field. These filled nanotubes can be used as nanosubmarines externally driven through blood vessels of a mammal by magnetic field and transporting nanoscale amounts of a drug or drugs from one point to the other. Also, these filled CNTs can be used in the form of nanowebs or films for magnetic recording or optical transducers for wearable electronics.
For these experiments, CNTs produced in accordance with methodologies set forth in Example 1 were used.
In one embodiment, the CNTs were filled with magnetic particles via filling of the alumina membrane upon which the CNTs were deposited. Upon deposition of a droplet of ferrofluid onto the membrane, the fluid invaded the pores. A magnetic field was applied to control the magnetic anisotropy of prepared magnetic peapods. A permanent magnet H of approximately 4 kGauss was mounted underneath the membrane. Even without field the penetration happened almost instantaneously. Applied magnetic field increased the rate of penetration, because it created an additional force to direct magnetic nanoparticles towards the magnet, i.e. into the tubes. After evaporation of the carrying liquid at room temperature, the membrane was broken into tiny pieces and dispersed in isopropanol for TEM examination. During the processing, the magnetic grains deposited outside the nanotubes were washed out, while the grains deposited inside, were held by adhesion forces. In
In another embodiment, individual nanotubes were filled with magnetic nanoparticles. Using this technique, the alumina template after preparation of the CNTs by the CVD method was dissolved in 4.0 M NaOH. After sonication, the solution was vacuum filtered through the Polyester nucleopore membrane (Osmonic Corp.) with the pore size of 0.2 μm. Then the filtrate was dispersed in toluene. A few milliliters of this filtrate solution of CNTs dispersed in toluene were then filtered again using a similar Polyester membrane. After filtration, the residue was rinsed with alcohol and distilled water, and then dried. Typically, a gray area of concentrated nanotubes appeared on the substrate after drying. A drop of ferrofluid was deposited on that gray spot. Again, after complete evaporation of the solvent, the substrate was rinsed with the alcohol, immersed into a small vial and 5 ml of alcohol was added. The vial was put into a sonicator and the deposit was removed from the membrane. This solution was analyzed by TEM. TEM images are depicted in
As shown by the TEM images, filling of the nanotubes either via the alumina membrane or individually gives almost the same results with the nanotubes being filled with magnetic nanoparticles. The density of magnetic grains was so high that the grains can be probed by rough macroscopic technique. In particular, the alumina membranes filled with magnetic grains can be easily dragged by permanent magnet after drying. Suspended in liquids, magnetic nanotubes follow the change of the direction of applied magnetic field.
An analysis of magnetization of magnetic nanotubes within membranes is extremely difficult. This is because an incremental increase of the weight of membranes after filling is so small that available balances cannot resolve the distinction. Also, even after rinsing the membrane, some particles are left at the membrane surfaces. Estimates based on an experimental magnetization curve taken on membranes, however, show that magnetic particles on the membrane surface contribute significantly to the magnetization. Thus, rotation field experiments were used to estimate the magnetization parameters of individual CNTs. In rotating magnetic field, the CNTs filled with magnetic particles follow the field and rotate. However, the magnetic moment coupling with the field cannot be considered as a sum of each individual magnetic grain, because collected together within the nanotube, magnetic particles constitute a multidomain magnetic nanotube. Upon application of magnetic field, magnetic moments of each magnetic particle rotate to follow the local magnetic field. This local field is influenced by the neighbors in a complicated way. Unlike typical magnetic solids, in which motion of magnetic spins can be, in a first approximation, considered independently of the deformations of the atomic lattice, in filled nanotubes rotations of magnetic moments and particles both are interconnected. To the best of the inventors' knowledge, the problem of magnetization of granular materials such as these has never been considered in the literature. This makes an estimate of magnetic properties of CNTs challenging. However, an estimate of an effective magnetization associated with the magnetic moments oriented along the nanotube can be made.
With respect to the stationary reference frame, the angle between the direction of the external field H and the reference axis X changes with time as Ω=ωt. If the angle between the nanotube axis, which is supposed to be the axis of magnetization m, and the direction of the field is θ, the following equation of tube rotation (Landau, L. D. and Lifshitz, E. M. Electrodynamics of continuous media (Pergamon, Oxford 1960)) can be written:
γ(ω−θ′)=μmH sin θ (1)
where prime denotes the time derivative, and γ is the friction coefficient of the tube (Doi, M. and Edwards, S. F. The theory of polymer dynamics Oxford University Press, London 1986),
γ=πηL3/3 ln(L/d)−3A),A−0.8. (2)
Here L is the tube length, d is the tube external diameter, and η is the fluid viscosity. As seen from Eq. (1), there is a solution θ=constant, which disappears as the frequency of the field becomes:
ωcr=μ0mH/γ.
Because of the scatter in the tube length, different CNTs stop spinning at different frequencies. Experiments were performed with water-based suspension on CNTs in the field of 0.007 Tesla. The critical frequency varies between fcr=6-10 Hz. Taking these values, the magnetization is estimated through the formula
m=ω
crγ/μ0H=2π·fcrπηL3[(3 ln(L/d)−2.4)μ0H]−1
where L=10-15 μm, d=300 nm and μ0 H=0.007 Tesla. The experimental data give m=5×10−15-2×10−14 A·m2. If the saturation magnetization of magnetite is Ms=4.46×105 A/m (Rosensweig, R. E. Ferrodynamics (Cambridge University Press, Cambridge 1985), then the magnetic moment of individual magnetic grain is mg=πMsdg3/6=2×10−19 A·m2. Assuming the packing factor is 0.74, the number of magnetic grains in the tubes is estimated as N˜3×104-105.
The high magnetization of the loaded CNTs of the present invention, as well as the compatibility of CNTs to many polymeric materials, makes these magnetic nanotubes produced in accordance with the present invention highly attractive engineering materials for multiple uses. For example, functionally nanoparticle loaded CNTs can be used as nanosubmarines for drug delivery in desired locations in the body, as well as for diagnostics without surgical interference. Further, experiments shown in
As will be understood by the skilled artisan upon reading this disclosure, other particulate fluids, emulsions, and polymer solutions can be used to fill hollow CNTs in accordance with the present invention and transform them into multifunctional nanostructures. For example, the methods described herein where used to functionally fill hallow CNTs with gold colloidal nanoparticles (see
As shown herein, the present invention provides a relatively easy, inexpensive and fast method of filling CNTs with functional nanoparticles, and in particular magnetic nanograins, colloidal gold nanoparticles as well as nonmetallic nanodiamond particles. Based on the phenomenon of spontaneous penetration of wetting fluids into capillaries, this technique opens doors in engineering magnetic nanotubes. The magnetization of magnetic CNTs is controlled by the amount of encapsulated nanograins, thus making it very high. In these experiments, for example, the number of magnetic grains in the tubes varied between 104 and 105. Further, the yield of magnetic nanotubes after wet filling was sufficiently high, tending to be 100%. As evidence of this,
The following nonlimiting examples are provided to further illustrate the present invention.
All experiments were performed with carbon nanotubes produced by the chemical vapor deposition (CVD) technique. The nanotubes were formed in the straight cylindrical pores connecting both faces of a template comprising an alumina membrane. The alumina membrane template comprised an Anodisc of 13 mm in diameter purchased from WhatmanR. The pore diameter and thickness of the membrane determine the dimensions of the nanotubes. For experiments described herein, the pore size was 300 nm on average, and the membrane thickness was 60 μm. The synthesis of CNT by CVD is described in detail by Bradley et al. (Chemistry Preprint Archive 2002 237-242). The resulting CNTs have open ends from one or both sides, and their walls are highly disordered and hydrophilic to allow water to invade the tubes (Rossi et al. Nano Letters 2004 4:989-993; Naguib et al. Abstract of Papers of the American Chemical Society, Annual meeting 2003 226:U535; Ye et al. Nanotechnology 2004 15:232-236). This makes it possible to fill the nanotubes not only with organic based ferrofluids but with water-based ferrofluids as well. CNTs were filled with magnetic particles using the following commercially available ferrofluids: water based (EMG 508) and organic based (EMG 911) (Ferrotec Corporation) which carry the magnetite particles (Fe3O4) with the characteristic grain size of 10 nm. Samples were characterized by transmission electron microscopy (TEM) using a JEOL JEM-2010F (200 kV) with a point-to-point resolution of 0.23 nm. The TEM samples were prepared by dispersing the nanotubes in isopropanol and then placing them onto a copper grid coated with a lacy carbon film. Images of nanotubes in experiments with external magnetic field of strength 110-120 Gauss were taken on a Leca DM LFS microscope with a Leica HCX APO 63×/0.90 U-V-I water immersion lens and MagnaFire SP Model S99805 camera.
This patent application claims the benefit of priority to U.S. Provisional Application Ser. No. 60/668,636, filed Apr. 6, 2005, the teachings of which are herein incorporated by reference in their entirety.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/US06/13215 | 4/6/2006 | WO | 00 | 5/6/2008 |
| Number | Date | Country | |
|---|---|---|---|
| 60668636 | Apr 2005 | US |