Patent Application
20110059845
The present invention relates generally to sorbent materials and methods for selective capture and retention of target species. More particularly, the invention relates to a porous sorbent and process for chemical separations and retention of preselected gases.
Selective capture and retention of unwanted gases, e.g., in flue gas streams, are of high interest. Various methods are known for sorption of gases including, e.g., use of liquids such as monoethanol amine (MEA). However, liquid amines can have volatile emissions, corrode infrastructure, quickly reach saturation, suffer from slow capture kinetics, and can degrade over time, losing capacity. Fluid methods thus have serious limitations for long-term chemical sorption and retention of unwanted gases. Accordingly, new solid phase sorption materials and methods are needed that are stable, exhibit fast sorption kinetics, provide long-term retention of unwanted gases, and are capable of being regenerated, providing for long service lifetimes. Additional advantages and novel features of the present invention will be set forth as follows and will be readily apparent from the descriptions and demonstrations set forth herein. Accordingly, the following descriptions of the present invention should be seen as illustrative of the invention and not as limiting in any way.
The invention in one aspect is a sequentially functionalized, solid-state sorbent for chemical sorption that provides for capture and retention of preselected target analytes. The sorbent includes: a porous support (substrate) of a preselected porous material that includes pores of a preselected size, pore volume, and surface area. The porous support is composed of a preselected material including, but not limited to, e.g., metals, transition metals, main group metalloids, metal oxides, ceramic oxides, oxide coated materials, metal silicates, including combinations of these porous materials. Metals include, e.g., aluminum (Al), and tin (Sn). Transition metals include, but are not limited to, e.g., titanium (Ti), zirconium (Zr), zinc (Zn), iron (Fe), nickel (Ni), copper (Cu), including combinations of these metals. Main group metalloids include, but are not limited to, e.g., Si, Ge, As, Sb, Bi, including combinations of these metalloids. Metal oxides include, but are not limited to, e.g., Al2O3, Ga2O3, GeO2, SnO2, and combinations of these oxides. Ceramic oxides include, but are not limited to, e.g., SiO2 and TiO2. The porous support includes pores with a pore size of from about 30 Å to about 500 Å. The porous support further includes a pore volume that is greater than or equal to about 0.5 cc/g. More particularly, the pore volume is in the range from about 1 cc/g to about 3 cc/g, but is not limited thereto. Porous support includes a specific pore surface area greater than or equal to about 150 m2/g. More particularly, specific pore surface area is in the range from 200 m2/g to about 1500 m2/g. Pores' of the porous support are functionalized with a preselected quantity of short-length (e.g., 5-20 Å) amino silanes that are chemically attached to surfaces (e.g., walls) of the pores, and substantially evenly distributed within the pores. In various embodiments, the short-length amino silanes include a terminal amine group. In one embodiment, the terminal amine group includes diethylenetriamine (DETA). In one embodiment, the short-length organic amino silane is 3-diethylenetriamine (DETA)-propyltrimethoxysilane. Short-length organic amino silanes preferably have a molecular weight of less than about 300 g/mol. Pores of the porous support further include a preselected quantity of organic polyfunctional oligomeric amino silanes (e.g., 25-45 Å) that are chemically attached to surfaces within the pores and interspersed between previously attached short-length amino silanes. The polyfunctional oligomeric amino silanes are substantially evenly dispersed across the pore surface within the pore. In one embodiment, the terminal group of the polyfunctional oligomeric amino silanes includes polyethyleneimine (PEI). In various embodiments, the polyfunctional oligomeric amino silanes have a molecular weight of from about 200 g/mol to about 1000 g/mol, but molecular weight is not limited thereto. Pores of the support further include a quantity of other short-length (e.g., 5-20 Å) amino silanes of like or different kind that are interspersed and chemically attached between previously attached short-length amino silanes and previously attached polyfunctional oligomeric amino silanes that serve to backfill open locations across the surface of the pores, forming the fully functionalized sorbent. The short-length organic amino silanes and organic polyfunctional oligomeric amino silanes in combination define a three-dimensional structure of active binding sites that are oriented substantially orthogonal to surfaces of the pores of the support. Crosslinking of silane groups between the short length organic amino silanes and the organic polyfunctional oligomeric amino silanes at the surface serves to maintain the 3-dimensional structure of amino silanes within the pores and further provides thermal stability of the solid-state sorbent. Amine functional groups present on the backbone of the highly functionalized silanes of the sorbent define active binding sites that provide the sorbent with a preselected functional density, selectivity, and capacity for retention of preselected target analytes. Functional density of the sorbent is defined by at least 3 or more amine functional groups per square nanometer of sorbent surface area. The density of active binding sites provide a preselected selectivity and capacity to selectively sorb, bind, capture, and retain preselected target analytes on the porous support of the sequentially functionalized sorbent when contacted by the analytes, including, e.g., gaseous analytes. Gaseous analytes include, but are not limited to, e.g., HCl, SO2, SO3, CO2, and combinations of these gases. In various embodiments, the binding sites of the sorbent can be further modified to include various functional groups including, but not limited to, e.g., thiols, carboxylates, sulfonates, phosphonates, phosphines, heteroaromatic ligands, ammonium salts, phosphonium salts, and combinations of these functional groups to provide selective binding for various target analytes. Heteroaromatic ligands include, but are not limited to, e.g., pyridines; 1,10-phenanthroline; 2,2′-bipyridine; and combinations of these ligands. The sorbent can be functionalized in various organic solvents, in supercritical fluids, or in the vapor phase. The sorbent can be used as a component of a sorption system or device, e.g., for trapping unwanted gases in a flue gas stream. The sorbent can also be used as a component of, e.g., analysis devices and applications, assay devices and applications, chemical separations devices and applications, including, e.g., biomedical devices and applications. No limitations are intended.
In another aspect, the invention includes a method for making a sequentially functionalized sorbent that provides for capture and retention of preselected analytes. In one functionalization step, pores of the support are pretreated and functionalized with a sub-monolayer quantity of a short-length (e.g., 5-20 Å) organic amino silane that is chemically attached to surfaces (e.g., walls) of the pores, and substantially evenly distributed within the pores. The pretreatment with short-length amino silane passivates the surface to allow passage and diffusion of other molecules larger than the short-length amino silanes into the pores of the porous support. In various embodiments, the short-length organic amino silane is an aminoalkylsilane selected from the group consisting of: aminopropylsilanes; and 3-(2-aminoethyl)aminopropylsilanes; 3-(diethylenetriamine)-propylsilanes, including combinations of these silanes. In a preferred embodiment, the short-length amino silane is a diethylenetriamine (DETA) amino silane. In another embodiment, the short-length organic amino silane is 3-diethylenetriamine (DETA) propyltrimethoxysilane. In a preferred embodiment, the sequentially functionalized sorbent includes short-length organic amino silanes with a molecular weight less than about 300 g/mole. The step of pretreating includes chemically dispersing short aminoalkylslane molecules throughout the porous support in a sub-monolayer quantity, and then subjecting them to hydrolysis/condensation chemistry to chemically attach them to surfaces within the pores. This pretreatment step enables functionalization in subsequent functionalization steps to include larger aminosilane molecules to percolate easily throughout the porous support by saturating hydroxyl groups located at the surface of the pores through an acid/base interaction with the amine backbones of the aminosilanes introduced the pores. The step of pretreating includes heating the porous support at a temperature of from about 50° C. to about 150° C. In one embodiment, the step of pretreating includes use of a quantity of the short-length amino silane that is between about 10% and 50% of the monolayer quantity. In another embodiment, the step of pretreating includes use of a quantity of the short-length amino silane between about 5% and 50% by weight of the monolayer quantity. In another (sequential) functionalization step, pores of the support are functionalized with a preselected quantity of an organic polyfunctional oligomeric amino silane (e.g., 25-45 Å) that is deposited, and chemically attached, to surfaces within the pores and interspersed between previously attached short length amino silanes such that they are substantially evenly dispersed across the pore surface within the pore. In various embodiments, polyfunctional oligomeric amino silanes include an aminated terminal group including, e.g., polyethylene imines; aminodendrimers; aminated polymers; aminated chitosans; aminoethylcelluloses; aminomethylpolystyrenes; and combinations of these amines. In a preferred embodiment, the polyfunctional oligomeric amino silane is a polyethyleneimine (PEI) silane. In one embodiment, the polyfunctional oligomeric amine silane includes polyethylene imine (PEI) that has been chemically modified to include a propyltrimethoxysilane anchor. In another embodiment, the step of depositing includes use of a polyethyleneimine (PEI) silane that is deposited using a method of incipient wetness (i.e., uses concentration solution) to occupy about 90% of the total pore volume of the porous support sample. In another functionalization step, pores of the support are backfilled with a preselected quantity of another short-length amine of like or different kind that chemically attach to the surface within the pores, backfilling the pores. Backfilling orients both short-length amines and polyfunctional oligomeric amines substantially orthogonal- to the surface forming a three-dimensional structure of active binding sites defined by amine groups on the silanes attached at the surface that provide the sorbent with a preselected functional density, selectivity, and capacity for capture and retention of target analytes. In various embodiments, the step of backfilling includes use of a short-length amino silane selected from: aminopropylsilanes; 3-(2-aminoethyl)aminopropylsilanes; 3-(diethylenetriamine)-propylsilanes; including combinations of these silanes. The step of backfilling includes crosslinking between adjacent siloxane groups located on the various short-length amino silanes and organic polyfunctional oligomeric amino silanes chemically attached at the surface that serves to maintain the 3-dimensional structure of active binding sites within the pores of the sorbent. The sorbent has a demonstrated sorption capacity for CO2 that yields a residual concentration of CO2 in air of below 0.01% in a time of less than one second. The deposition of polyfunctional oligomeric amine silane polymers is accomplished by chemically modifying the amine with an organosilane coupling agent. In various embodiments, the organosilane coupling agent includes, but is not limited to, e.g., 3-isocyanatopropyltrialkoxysilanes; 3-chloropropyltrialkoxysilanes;3-bromopropyltrialkoxysilanes; 3-iodopropyltrialkoxysilanes; 2-isocyanatoethyltrialkoxysilanes; 2-chloroethyltrialkoxysilanes; 2-bromoethyltrialkoxysilanes; 2-iodoethyltrialkoxysilanes; 4-(chloromethylphenyl)trialkoxysilanes; including combinations of these coupling agents. The step of back-filling is accomplished by a subsequent treatment of the pretreated support with a short-length aminoalkylsilane that fills in defects left over from the polymer deposition. The net result of these 3 sequential treatment steps is a higher overall functional loading than is possible with standard coating methods using typical amine terminated silanes. In one embodiment, the polyfunctional oligomeric amine is PEI and the polyfunctional oligomeric aminosilane is PEI silane. The sequentially functionalized sorbent provides a sorption capacity for target analytes that is from 2× to 3× greater than possible with sorbents made using standard coating methods using typical amine terminated silanes. The sequentially functionalized sorbent of the invention has a sorption capacity that can deplete concentrations of gas-phase target analytes. In one embodiment, the sequentially functionalized sorbent removes CO2 to below 0.01% in less than one second. Time to capture a gas phase analyte is dependent on the selected analyte specific gas, and the molecular weight of the gas. Thus, no limitations are intended.
The purpose of the foregoing abstract is to enable the United States Patent and Trademark Office and the public generally, especially scientists, engineers, and practitioners in the art who are not familiar with patent or legal terms or phraseology, to determine quickly from a cursory inspection the nature and essence of the technical disclosure of the application. The abstract is neither intended to define the invention, which is measured by the claims, nor is it intended to be limiting as to the scope of the invention in any way. Various advantages and novel features of the present invention are described herein and will become readily apparent to those skilled in this art from the following detailed description. Only the preferred embodiment of the invention is shown and described to illustrate the best mode contemplated for carrying out the invention. As will be realized, the invention is capable of modification in various respects without departing from the invention. Accordingly, the drawings and description of the preferred embodiment set forth hereafter are to be regarded as illustrative in nature, not as restrictive.
a is a cross-sectional view of a porous support used in conjunction with the invention.
b-c present different cross-sectional views of a representative pore of the porous support.
a shows surfaces of a pore of the silica support following pretreatment with short-length amine silanes.
b shows surfaces of a pore of the silica support following deposition of polyfunctional oligomeric amine silanes.
c shows the 3-dimensional structure of active binding sites within a pore of the silica support after backfilling with additional short-length amine silanes.
A sequentially functionalized, porous solid-state sorbent is described that provides for the chemical sorption and retention of target analytes including, e.g., target gases, e.g., in flue gas streams. The sorbent has a substantially high surface area, is highly permeable, and has good physical and thermal stability. The porous sorbent includes pores of a preselected size, quantity, pore volume, and specific surface area that permit various amines and polymers with preselected sizes to enter and chemically attach to the surface within pores of the porous support. Amines and other basic molecules chemically interact with hydroxyl groups located on surfaces within pores of the selected porous support material (e.g., silica) via an acid/base interaction. The selected amines of polymer molecules are chemically modified to include a preselected alkoxysilane group that undergoes hydrolysis and condensation to covalently anchor selected molecules to surfaces (e.g., oxide surfaces) within the pores. The term “silanes” is used herein to describe general deposition precursors that are silicon-based analogues of alkanes that include Si—H and Si—C bonds. Silanes encompass compounds including, but not limited to, e.g., chlorosilanes, aminosilanes, alkylamine silanes, and like silanes. The term “siloxane” is used herein to denote terminal end-groups of alkylamine silanes of the form: —R—Si—O—, where R is a preselected hydrocarbon group. The siloxane end group is used to anchor the selected silane to the surface of the support. The term “siloxane” is thus used when drawing attention to the oxygen-silicon bond at the surface, for example, when discussing crosslinking between adjacent tethered silanes. These terminal end-groups can also be aminated. In a preferred embodiment described hereafter, a propyl-silyl anchor is used to bind alkylamine silanes to the surface through an oxygen-silicon (Si—O) bond.
The sequential attachment of short-length amino silanes on surfaces within the pores of the porous support in a first functionalization step saturates hydroxyl groups at the surface with the selected amino silanes, which pretreats the porous support allowing larger polyfunctional oligomeric amines and polymers to diffuse freely throughout the porous matrix in subsequent functionalization steps. Introduction and dissemination of larger polyfunctional oligomeric amines and polymers into the pores of the porous matrix in these subsequent functionalization steps does not occur absent the first functionalization step. In one embodiment described hereafter, the porous support is pre-treated with DETA silane that passivates hydroxyl groups on the acidic surface. Pretreatment of the surface facilitates introduction of PEI silane molecules that can further functionalize the surface within the pores. Absent pretreatment, PEI molecules do not diffuse readily through the porous matrix and are deposited predominantly at or near the mouth of the pores, which can plug the pores of the porous support. The inventive method of sequential attachment functionalizes the support sequentially, forming a unique 3-dimensional structure within the pores of the sorbent that provides a greater sorption capacity for capture and retention of various target analytes including, e.g., acid gases. The sorbent can be further functionalized with various functional groups including, but not limited to, e.g., carboxylates, sulfonates, phosphonates, and other groups that impart other types of chemical specificity to the sorbent, e.g., for sorption and retention of, e.g., transition metal cations, heavy metals, and/or radionuclides. The sorbent has extremely good sorption kinetics target analytes retained from the gas phase, as described further herein. The process of functionalization of active binding sites within pores of the sorbent can be carried out either in routine organic solvents or in supercritical fluids, and can involve various ligands, e.g., as detailed in U.S. Pat. No. 7,019,037; U.S. Pat. No. 6,846,554; U.S. Pat. No. 6,753,038; U.S. Pat. No. 6,733,835; U.S. Pat. No. 6,531,224; and U.S. Pat. No. 6,326,326, which patents are incorporated in their entirety, herein. Applications for the invention include, but are not limited to, e.g., uses in chemical catalysis; chemical separations; biomedical applications; capture of toxic heavy metals in the body or in the blood; controlled release of pharmaceuticals or pheromones; refining; chemical processing; and material recovery. Functionalized sorbents of the invention are easy-to-use, do not require complex chemical pre-treatment, transport of liquid samples, or large complicated instruments. Sorbents of the invention can further be used as components of, e.g., gas-capture and release devices. No limitations are intended. Sorbents of the invention provide rapid rates of sorption, e.g., as described further herein. The sorbents can also be relatively low cost to produce. Because the sorbents are solids, they also exhibit greater physical, chemical, and thermal stability compared to liquid sorbents.
a is a cross-sectional view of a porous support 10 used in conjunction with the sequentially functionalized sorbent of the invention. Porous support 10 is composed of a porous material including, but not limited to, e.g., silica (SiO2); germania (GeO2); alumina (Al2O3); metals, including transition metals (e.g., Ti; Zr); solid oxides (e.g., SnO2, ZnO2); as well as combinations of these materials. In a preferred embodiment, porous support 10 is composed of porous silica, but is not limited thereto. In the figure, porous support 10 includes pores 12. Pores 12 of the preferred porous silica support 10 have a preselected pore size and pore volume that retains the structure of the pores in the sorbent product. Pores are preferably of a size in the range from about 30 Å to about 150 Å, but size is not limited thereto. In one preferred size, pores 12 are about 50-60 Å, but again, size is not limited thereto. Pores 12 of porous support 10 include surfaces 14 that define the surface area and the pore volume of pores 12 of porous support 10. Specific surface area of porous support 10 is in the range from about 200 m2/g to about 1500 m2/g, and preferably in the range from about 500 m2/g to about 1000 m2/g. Pore volume is preferably in the range from about 1.0 cc/g to about 3.0 cc/g. The selected porosity enhances mass transport and kinetic properties in the fully functionalized product sorbent. In order to take full advantage of all of the surface area of the porous support, pores of the sorbent are functionalized in a manner that prevents plugging of the pores. Functionalization reagents must be dispersed uniformly throughout the porous matrix. The method of the invention, described further herein, sequentially functionalizes the sorbent that provides uniform dispersement of the functionalization reagents throughout the porous matrix. Those of skill in the ceramic processing and material arts will readily recognize that methods of the invention will be equally useful for silica particles derived from other particle and ceramic sources, e.g., precipitated silica, silica gels, chromatographic silica, and like sources. Thus, no limitations are intended by the description to the preferred embodiments described herein. All porous materials as will be contemplated or implemented by those of skill in the ceramic processing arts in view of the description of the invention are within the scope of the invention. No limitations are intended.
Mass transport properties of the porous support enhance both the sequential functionalization process for preparation of the sorbent, as well as the speed of sorption of analytes by the fully functionalized sorbent. In short, porosity of the silica template provides the sorbent with a suitable pore volume for functionalization and a suitable surface area for sorption of analytes that contact the sorbent, including, e.g., gas analytes. Other properties of the sorbent are described further herein.
Preparation of the sorbent includes a sequence of functionalization steps: 1) Passivation/pre-treatment with short-length or low-molecular weight amino silanes; 2) Deposition of polyfunctional oligomeric amines or polymers; and 3) Backfilling with another short-length or low-molecular weight amino silane. Each functionalization step is described further hereafter.
a shows a cross-sectional view of pore 12 of porous support 10 immediately following a first functionalization step, {Step 102}, that passivates/pretreats surface 14 of pores 12. Plugging or clogging of pores 12 can result when constituents including amines (or other functional-group constituents) that are basic come in contact with acidic moieties such as hydroxyl groups found, e.g., on oxide (e.g., silica) surfaces, e.g., at pore openings. Any plugging that occurs significantly reduces the quantity of amines that can enter into, and be distributed within, the pores during steps that functionalize the support and ultimately form the fully functionalized sorbent. Thus, preventing clogging of pores of the porous silica support maximizes the functionalization density of the functionalized pores of the functionalized sorbent, and thus the ultimate sorption capacity of the sorbent. To minimize potential for plugging of pores, in a first sequential functionalization step {Step 102}, acidic hydroxyl groups 16 along the surface of pores 12 are passivated. Porous support 10 is pretreated with a low molecular weight or short-length alkyl amino silane 30 that serves to passivate acidic hydroxyl groups 16 located along surfaces 14 of pores 12. In the pretreatment step, porous silica 10 is mixed as a slurry with a short-length amino silane 30 dissolved in a preselected solvent (e.g., toluene). The term “short length” means a molecular weight less than about 300 g/mole. The low molecular weight alkyl amino silane 30 is readily and evenly distributed within pores 12 throughout porous support 10. Alkyl amino silanes 30 include a branched or unbranched aminated alkane bearing a siloxane (i.e., —R—Si—O—) linking group 22 that is capable of covalently attaching to a surface 14 (e.g., an oxide surface) of pore 12. Once attached, amine functional groups 20 that define active binding sites 20 of low molecular weight alkyl amino silane 30 then chemically associate with other hydroxyl groups 16, aligning in a first dimension (e.g., horizontally) along surface 14 of pore 12, which anchors amine groups 20 to surface 14 of pores 12, which passivates (inactivates) hydroxyl groups 16 to which they anchor, making them no longer available to interact with other basic molecules. Passivation in the pretreatment step allows, and provides, for passage and diffusion of larger organic amino silanes and polymers into, and throughout, pores 12 of porous support 10 in subsequent functionalization steps described hereafter. Quantity of short-length amino silanes 30 used to pretreat and passivate surfaces 14 of pores 12 is a preselected fraction of the total available surface area of porous support 10. The selected quantity is less than is required to cover surfaces 14 with an ordered monolayer film of short-length amino silanes, i.e., a submonolayer of coverage. The term “monolayer” means the quantity of amino silanes required to completely cover the entire surface area of the pores with an ordered monolayer film. The specific surface area of the support is determined and then a quantity of the selected amino siloxane that will cover a preselected fraction (e.g., 50%) of the available surface area is added. Percentage of surface area covered is not limited. In particular, the preferred quantity of short-length amino siloxane used is between about 5% and 50% by weight of the calculated monolayer quantity. More particularly, the quantity of short-length amino silanes used is about 25% by weight of the monolayer quantity. In practice, because the quantity used represents a sub-monolayer of coverage (i.e., less than needed for a monolayer), some fraction of hydroxyl groups 16 remain along surface 14 of pores 12 between low-molecular weight amino silanps 30 attached at the surface. Short length amino silanes 30 initially introduced to pores 12 are generally uniformly distributed within pores 12 and tend to align along surface 14 of pores 12 due to their short length. {Step 102} ends with the formation of a pretreated support 75. Pretreated support 75 is air-dried at ambient temperature to remove residual solvent, but temperature is not limited thereto.
In another functionalization step {Step 104}, illustrated in
In another sequential functionalization step {Step 106}, illustrated in
The sequentially functionalized solid-state sorbent 100 described herein comprised of a silica support 10, a sub-monolayer of short-length amino silanes 30, polyfunctional oligomers/polymers 40, and backfilled amino silanes 30 provides a high density of active binding sites 20 that are chemically anchored to surfaces 14 within pores 12 of the sequentially functionalized sorbent 100. Sorbent 100 demonstrates good thermal stability at ambient temperatures at which the sorbent is used and/or regenerated. Sorbent 100 is expected to exhibit excellent stability at temperatures up to about 175° C. in air and over 200° C. in inert atmospheres. Temperatures will depend on the selected target analyte. For example, for CO2 capture, regeneration temperatures are generally in the temperature range from about 110° C. to about 115° C. No limitations are intended.
The sequentially functionalized sorbent was further tested with analytes of interest to determine sorption capacity for various analytes. Analytes were shown to readily diffuse into the pore structure of the sorbent and be retained by the sorbent, e.g., in conjunction with the pendant surface chemistry described herein. Analytes, including target analyte gases, diffuse easily into pores 12 of the solid-state sorbent 100 due to the selected porosity (e.g., 50 Å to about 150 Å). The high density of active binding sites 20 provides a high sorption capacity, e.g., 5-6 wt % for CO2. Thus, the sorbent is effective for capture and retention of, e.g., unwanted gases, e.g., in flue gas streams or other gas-based fluid processes.
The following examples will further assist in the understanding of the invention.
5.0 g mesoporous silica (surface area: ˜585 m2/g; pore size: ˜60 Å; pore volume: 2.45 cc/g) as a support material was suspended in 150 mL of toluene. 1.0 mL of 3-(diethylenetriamine)propyltrimethoxysilane (“DETA silane”), was added to the suspension, representing ˜25% of the amount of silane needed to produce a full monolayer of coverage in the support material. The mixture was stirred and heated to a reflux temperature of 110° C. Reflux was maintained for 2 hours to pretreat the support. The pretreated support was collected by vacuum filtration, washed with isopropyl alcohol to remove reaction by-products, and air-dried. Mass of the pretreated product showed the desired sub-monolayer coverage by DETA silane was achieved.
A solution containing 18.0 mL of polyethyleneimine (PEI) (423 g/mole; 1.07 g/mL; 45.5 mmole) in 100 mL of diglyme was prepared. 11.4 mL of 3-isocyanatopropyltrimethoxysilane was added to the solution and stirred overnight at ambient temperature to form PEI silane. The pretreated support product obtained in Example 1 was mixed with 10 mL of PEI silane solution, representing a solution volume less than the total pore volume of the pretreated silica support sample. The pretreated silica support sample was mixed thoroughly by rotating and stirring the mixture to obtain a uniform distribution of PEI silane in the pores of the porous silica. Sample was placed in a thick-walled thermolysis tube sealed with a threaded teflon stopper and heated in an oven at ˜80° C. for 18 hours to deposit and attach PEI silane at surfaces of pores of the silica support. Product was cooled to ambient temperature, washed with isopropyl alcohol to remove reaction by-products, and air-dried. The polymer deposition step can be repeated if additional polymer loading is desired. Mass of the product showed incorporation of PEI silane. BET surface area analysis revealed that the product still maintained high surface area and an open pore structure.
The DETA/PEI-coated silica product from Example 2 was suspended in 150 mL of toluene and treated with 4 mL of DETA silane, representing an excess quantity (above monolayer coverage) of DETA silane. DETA silane was added to the suspension and the mixture was heated at a (solvent) reflux temperature of 110° C. for 4 hours to produce the fully functionalized sorbent product. Sorbent product was collected by vacuum filtration, washed copiously with isopropyl alcohol and air-dried. Mass of the sorbent product showed that additional DETA coverage had been achieved in the product. Brunauer, Emmett, and Teller (BET) surface area analysis revealed that the sorbent product retains a high surface area and open pore structure.
The sequentially functionalized sorbent was prepared in a 3-stage synthesis that included: 1) pretreatment with a 12.5% DETA pre-fill; 2) a one-time deposition with PEI, which number is not limited; and 3) backfilling with DETA silane. Sorption data were characterized using a gas stream containing 0.5% CO2 in air. Baseline concentration of CO2 prior to contact with the sorbent is shown in
This invention was made with Government support under Contract DE-AC05-76RLO1830 awarded by the U.S. Department of Energy. The Government has certain rights in the invention.