Patent Application
20090025431
This application claims the benefit of Japanese Patent Application No. 2007-191694, filed Jul. 24, 2007, which is hereby incorporated by reference herein in its entirety.
1. Field of the Invention
The invention relates to a furnace used for heating a preform in a sintering process to transparently vitrify a porous glass preform, a drawing process to reduce the diameter of a glass preform and a process for making an optical fiber from a glass preform.
2. Description of the Related Art
An optical fiber is fabricated through several processes. First, a process of depositing glass particles onto a core rod, as a starting material, is conducted to produce a porous glass preform. Next, the porous glass perform is heated so as to sinter the perform and produce a transparently vitrified glass preform. Next, a heating and drawing of the glass perform to reduce its outer diameter is performed to produce a glass preform having an outer diameter suitable for drawing an optical fiber. Finally, a distal end of the glass preform is heated and melted so as to provide a pre-adjusted outer diameter and an optical fiber is drawn from the distal end in a furnace so as to produce an optical fiber.
An explanation of a conventional method of drawing an optical fiber will be given with reference to
The glass preform 1 is subject to radiation heat of the furnace core tube 4 so as to be heated, melted, and then drawn down as an optical fiber. A drawn optical fiber 6 is coated with a resin by a resin coating device 20, and then taken up to a bobbin by a winding device 30.
In addition, a clearance gap between a glass preform insertion opening 2a disposed at an upper end 2t of the furnace 2 and the glass preform 1 is sealed with an annular sealing disk 7 having a hole 7a with an inner diameter slightly greater than the outer diameter of the glass preform 1. On the other hand, a clearance gap between an insertion opening 2b for an optical fiber 6, disposed at a bottom end of the furnace 2, and the optical fiber 6 is sealed with an iris 8 with an adjustable inner diameter.
The outer diameter of the optical fiber 6, to be drawn, is generally controlled within 125±1 μm, so that the clearance gap between the optical fiber 6 and the iris 8 is substantially constant. While at the top end of the furnace 2, a clearance gap between the optical fiber 6 and the glass preform 1 can be significantly changed in size in response to a fluctuation of the outer diameter of the glass preform 1 when drawing the optical fiber 6. The fluctuation of the size of the clearance gap causes a change of the flow of the inert gas so that it becomes difficult to control the outer diameter of the optical fiber 6. Further, when the clearance gap becomes bigger in size than a predetermined value, outside air flows into the inside of the furnace 2 and a carbon part at a high temperature, such as the furnace core tube 4, is eroded by oxidization. As a result, dust from an eroded portion adheres to a melted portion of the glass preform 1. The adhered dust causes a localized fluctuation of the outer diameter and localized embrittlement of the optical fiber 5, as well as a decrease in the life of the carbon part in the furnace 2.
To prevent this problem from occurring, a fine adjustment of the outer diameter of the glass preform 1 to make it uniform in the longitudinal direction is required. However, in fabrication methods of optical fiber glass preforms by a sintering process, such as a Vapor-phase Axial Deposition (VAD) process or an Outside Vapor Deposition (OVD) process, a fluctuation of an outer diameter of a porous glass preform usually occurs because of a lack of balance between a shrinking force caused by sintering and a gravitational force due to its own mass in the longitudinal direction of the porous glass preform.
To avoid that problem, Japanese Patent Laid-open No. 2005-8452 (corresponding to International Publication Number WO2004/110941) discloses a method of transparently vitrifying a porous glass preform which comprises monitoring the amount of expansion and contraction of a porous glass preform to control a sintering condition during sintering of the porous glass preform.
However, in this method, a core rod as a core of the porous glass preform is required in which the outer diameter is pre-adjusted in the longitudinal direction based on a pre-consideration of an expansion and contraction of the porous glass preform. Additionally, when depositing soot onto a periphery, an adjustment of the amount of soot to deposit onto the core rod is required in response to the diameter of the core rod along the entire longitudinal direction. As a result, in fabricating a glass preform by this method, numerous processes are needed.
Further, if a glass preform is drawn with a smaller diameter and has a fluctuation in the outer diameter in the longitudinal direction, especially near the beginning and ending of drawing of the glass preform, a finished outer diameter of the glass preform might have large fluctations. The portion(s) where the outer diameter of the glass preform significantly fluctuates is not available for drawing an optical fiber, so that it is unavoidable to cut off and remove the portions.
To reduce such a waste of a glass preform and enable use of even a glass preform having a relatively large fluctuation in the longitudinal direction, a method capable of effectively sealing a clearance gap between a furnace and a glass preform has been proposed.
For example, Japanese Patent Laid-open No. 2006-342030 (corresponding to US 2006/290578A1) discloses a sealing method which comprises pushing a sealing ring, formed of a combination of an inner ring and an outer ring respectively configured with a plurality of mutually connected seal ring fragments, onto a surface of glass preform with elastic springs arranged on a periphery of the outer ring.
However, in this method, to move equally each seal ring fragment in response to a fluctuation of the outer diameter of the glass preform in the longitudinal direction, a fine machining of the seal ring fragments is required.
Furthermore, when combining the inner ring and the outer ring, the height of a single sealing ring is too short to provide sufficient sealing efficiency. To improve the sealing efficiency, it is necessary to stack up a plurality of the sealing rings.
However, when stacking up a plurality of the sealing rings, the entire body of the sealing rings becomes considerably heavy. As a result, when drawing an optical fiber, movement of the glass preform in X and Y directions is required to adjust a position of an optical fiber in the center of an outer diameter measurement device. If the entire body of the sealing rings is too heavy, the sealing rings can not smoothly respond and it becomes difficult to control sliding the position of the glass preform.
Japanese Patent Laid-open No. 2007-70189 discloses a sealing method that uses a donut-like brush made of carbon fibers. According to this method there is no need for fine machining as described above, the donut-like brush can be relatively light, and an excellent sealing efficiency can be obtained.
However, the carbon fibers forming the brush might fall off and adhere onto the surface of the glass preform. As a result, the strength of the optical fiber might degrade.
The problem described above regarding the sealing of the clearance gap between the preform insertion opening and the preform to be processed at the top end of the furnace caused by the fluctuation of the outer diameter of the glass preform in the longitudinal direction is not only a peculiar problem when drawing an optical fiber from a glass preform but is also a problem when transparently vitrifying a porous preform by sintering and when adjusting an outer diameter of a glass preform by heating and drawing it.
It is an object of the present invention is to provide a furnace for heating an optical fiber preform, such as a porous glass preform and a transparently vitrified glass preform, which includes a sealing structure capable of effectively sealing a clearance gap between a preform insertion opening at a top end of the furnace and the optical fiber preform to be heated in the furnace.
The present invention provides a furnace for heating an optical fiber preform to be inserted from its insertion opening, the furnace includes an annular sealing body for sealing a clearance gap between the optical fiber preform and the insertion opening, the annular sealing body includes a plurality of annular disks mutually piled/stacked up, each of the plurality of annular disks has an insertion hole in its central area, a plurality of slits formed from an inner edge of the insertion hole toward its periphery and a plurality of flexible portions that are defined by the plurality of slits and bend by an interference with the optical fiber preform to be inserted into the insertion hole.
Further features of the present invention will become apparent from the following description of exemplary embodiments with reference to the attached drawings.
An embodiment of the present invention will be described below in detail with reference to the attached drawings. In addition, an optical fiber preform heated in the furnace includes a porous glass preform transparently vitrified by sintering, a glass preform to be heated and drawn for a preliminary adjustment of its outer diameter prior to being changed to an optical fiber, and a glass preform to be changed to an optical fiber by being heated and drawn.
An annular sealing body 9 is slidably disposed on a top end 2t of the furnace 2. The annular sealing body 9 seals a clearance gap between a glass preform insertion opening 2a and a glass preform 1.
The annular sealing body 9 is configured with a plurality of annular disks 10 having an insertion hole 10a in its central area. The plurality of annular disks 10 are mutually piled or stacked up on each other.
An annular disk 10 has a plurality of slits 10b which are formed to extend from a inner edge of the insertion hole 10a toward its periphery. Additionally, the annular disk 10 has a plurality of flexible portions 10c, which are defined by the plurality of slits 10b, so as to provided flexibility to the disk.
The slits in the annular disk 10, for example, are formed to extend from the inner edge of the insertion hole 10a in radial directions. The slits 10b, for example, are formed at regular angular intervals in the circumferential direction of the annular disk 10. However, the slits 10b are not limited to these examples.
The annular disk is formed from a heat-resistant material such as a carbon-carbon composite, a graphite sheet, and a heat-resistant metal.
When employing a graphite sheet as a material for forming the annular disk 10, it is preferable to use a highly oriented pyrolytic graphite sheet or an expanded graphite sheet. Further, as a heat-resistant metal for forming the annular disk 10, it is preferable to use a metal such as tantalum.
The annular disks 10 have respectively identical structures in the example shown in
The stacked annular disks 10 are integrated by fasten means such as clip fastener. It is not necessary to integrate the stacked annular disks about their entire circumference, also a structure can be employed so that several portions of the disks can be integrated in the circumference direction.
The insertion hole 10a of the annular disk 10 is formed so as to be smaller in diameter than the outer diameter of the glass preform 1. Therefore, when the glass preform 1 is inserted into the insertion hole 10a of each of the stacked annular disks 10, the respective flexible portions 10c bend due to an interference with the glass preform 1. In this situation, each of the flexible portions 10c responds to any fluctuation of the outer diameter of the glass preform 1, and the amount of deflection also fluctuates. As a result, a condition is established in which each of the flexible portions 10c is always in stable contacts with a surface of the glass preform 1, so that the annular clearance gap between the glass preform insertion opening 2a and the glass preform 1 is effectively sealed.
The larger the number of annular disk 10 for forming the annular sealing body 9, the higher the sealing efficiency of the annular sealing body 9.
As shown in
A spacer 11 for forming a space S1 to be filled with an inert gas is disposed between the two annular sealing bodies 9.
The spacer 11 is provided with a gas inlet for feeding an inert gas G.
A furnace core tube 4 is heated to over 2000 degrees C. Therefore, if the clearance gap between the glass preform 1 and the preform insertion opening 2a is relatively large, the annular sealing body 9 is subject to a radiation heat from the furnace 2 and will be heated to a higher temperature. As a result, the annular carbon disks forming the annular sealing body 9 are oxidized by an oxide gas included in outside air and will erode.
To avoid this problem, in the present embodiment, by piling up two annular sealing bodies and feeding the inert gas G, such as argon and helium, through the gas inlet 12 therebetween, an external air flow into the furnace can be effectively blocked. As a result, erosion of the annular disks 10 on the lower side of the sealing body 9 that is caused by an oxide gas from a carbon material can be suppressed. Further, the annular sealing body 9 on the upper side is subject to light shielding and heat shielding, so that radiation heat to which the upper side annular sealing body 9 is subject can be reduced. Accordingly, erosion of the upper side annular disks 10 can also be suppressed.
By piling/stacking up additional annular sealing bodies 9, erosion resistance and sealing efficiency of the annular sealing body 9 can be effectively improved.
Ten glass preforms 1 having an average outer diameter of 64 mm and a fluctuation of its outer diameter within plus or minus 2 mm and a length of 1000 mm were heated by using the furnace 2 shown in
At the preform insertion opening 2a of the furnace 2, the annular sealing bodies, which were made under the following condition, were piled up.
The annular disk 10 was made from a highly oriented pyrolytic graphite sheet with a thickness of 0.1 mm, of which the insertion hole 10a had a diameter of 60 mm. Twelve slits 10b with a length of 20 mm were formed in the annular disk 10 so as to extend from an inner edge of its insertion hole 10a in a radial direction at angular intervals of 30 degrees in the circumferential direction.
The annular sealing body 9 was made from eight annular disks 10 having a same structure were stacked, so that the annular disks lying next to each other were shifted by 15 degrees so as to prevent the slits 10b from being overlapped with each other.
An argon gas was fed from the inert gas inlet 12 into the space S1 between the annular sealing bodies 9 at a flow rate of 3 liters per minute.
After drawing an optical fiber, the thickness of the furnace core tube 4 at a topmost portion was measured. However, the measured thickness was not reduced, and a fluctuation of an outer diameter of the drawn optical fiber was within 125 μm plus or minus 0.5 μm i.e. precisely controlled. Further, the strength of the optical fiber was tested with a predetermined proof test. But, there was no breakage in the optical fiber. In the proof test, a predetermined load was applied to the optical fiber for a second so as to cause extension strain of 1.0% over the entire length of the optical fiber.
Ten glass preforms 1 having an average outer diameter of 64 mm and a fluctuation of its outer diameter within plus or minus 2 mm and a length of 1000 mm were heated by using the furnace 2 shown in
Donut disk-like brushes 13 were used for sealing the clearance gap between the top end 2t of the furnace 2 and the glass preform 1.
The donut disk-like brush 13 is configured with a ring part and hair materials with a length of 8 mm implanted around the inner circumferential surface of the ring part in the radial directions, and comprises an insertion opening with an inner diameter of 60 mm for the preform 1.
Argon gas was fed from the inert gas inlet 12 into a space between the donut disk-like brushes 13 at a flow rate of 3 liters per minute.
After drawing an optical fiber, the thickness of the furnace core tube 4 at a topmost portion was measured. However, the measured thickness was not reduced, and a fluctuation of the outer diameter of a drawn optical fiber was within 125 μm plus or minus 0.5 μm. However, the strength of the optical fiber was tested by the predetermined proof test. There was a break at an average frequency of once every 120 km of the optical fiber.
In the embodiment described above, an explanation was made in case in which slits were formed in the radial direction of the annular disk, however, the present invention is not limited to this configuration. For example, a configuration in which the slits are formed in a direction inclined relative to a radial direction at a predetermined angle can be employed. In this case, by alternately turning the annular disks upside down to pile them up, it is possible to prevent the slits from being overlapped without a mutual alignment of the disks.
In the embodiment described above, an explanation was made in the case where the plurality of annular disks have the same structures, however, the present invention is not limited to this configuration. For example, a configuration in which the locations of the slits and the direction of the slits to be formed in each of the disks are respectively different from each other can be employed.
Having described preferred embodiments of the invention with reference to the accompanying drawings, it is to be understood that the invention is not limited to the precise embodiments, and that various changes and modifications may be effected therein by those skilled in the art without departing from the scope or spirit of the invention as defined by appended claims.