Patent Application
20230067445
The present invention relates to fuse-coated trim components for ball valves, such as balls and seats.
Ball valves used in severe service applications, such as pressure acid leaching of ores, are subject to high temperatures, high pressures, abrasive solids, and acid corrosion. Trim components of ball valves, such as balls and seats, are often thermally spray coated to improve their reliability and resistance to degradation or wear, such as abrasion, erosion and corrosion. For example, balls and seats made of titanium are thermally sprayed coated with coatings, such as chrome carbide.
Conventional thermally spray coated balls and seats suffer from several drawbacks. In use, the thermal spray coatings unpredictably delaminate and spall from the trim components which reduces the sealing efficiency of the ball valve. This delamination and spalling provide increased access of abrasive solids and corrosive acid to the underlying metal substrate that sets off a cycle of exacerbated deterioration, wear and corrosion. In addition, the delaminated or spalled coating poses contamination and damage hazards to plant and process equipment downstream of the ball valve.
In view of this background, a need exists for improved coated balls and seats for severe-service ball valves that have increased resistance against wear and corrosion, but decreased delamination and spalling (or increased adherence).
According to the present invention, there is provided a ball for a ball valve, wherein the ball comprises a substrate of metal having surface modified portions to act as seating surfaces for a seat of the ball valve.
The substrate and surface modified portions may each comprise titanium or titanium alloy.
The surface modified portions may be formed by nitriding.
The surface modified portions may be formed by nitriding surface portions of the substrate to form a hard titanium nitride phase, and alloying the nitrided surface portions with a beta stabiliser to form a tough beta titanium phase which surrounds the hard titanium phase.
The surface modified portions may be densified to fill any cracks or voids.
The surface modified portions may comprise raised annular bands.
The raised annular bands may be metallurgically fused to the substrate by fusion welding.
The present invention also provides a seat ring for a ball valve, wherein the seat ring comprises a substrate of metal having a surface modified portion to act as a seating surface for a ball of the ball valve.
The substrate and surface modified portion may each comprise titanium or titanium alloy.
The surface modified portion may be formed by nitriding.
The surface modified portion may be formed by nitriding a surface portion of the substrate to form a hard titanium nitride phase, and alloying the nitrided surface portion with a beta stabiliser to form a tough beta titanium phase which surrounds the hard titanium phase.
The surface modified portion may be densified to fill any cracks or voids.
The surface modified portion may comprise a raised annular band.
The raised annular band may be metallurgically fused to the substrate by fusion welding.
The surface modified portion may comprise two axially spaced raised annular bands.
The seat ring may further comprise a band of low friction material between the two axially spaced raised annular bands.
The present invention further provides a kit of parts for a ball valve comprising the ball and two of the seat rings described above.
Embodiments of the invention will now be described by way of example only with reference to the accompanying drawings, in which:
Referring to
The 12 ball may comprise a substrate of metal having surface modified portions 16 to act as seating surfaces for the seat rings 14 of the ball valve 10. The substrate and surface modified portions may each comprise titanium or titanium alloy, for example, Titanium Grade 12.
The surface modified portions 16 may be formed by nitriding. The nitriding may be performed alone, or in combination with additional surface modification techniques, for example, those described in WO/2020/212883 by Callidus Welding Solutions Pty Ltd, which is hereby incorporated by reference in its entirety. Among other things, WO/2020/212883 describes forming surface modified portions by nitriding surface portions of a substrate to form a hard titanium nitride phase, and alloying the nitrided surface portions of the substrate with a beta stabiliser to form a tough beta titanium phase which surrounds the hard titanium phase.
The surface modified portions 16 may be densified to fill any cracks or voids, for example, using a thermal spray coating of one or more metal oxides, or one or more metal carbides. Further or alternatively, the surface modified portions 16 may be densified using a suitable sealant or filler, such as “XP 61” ceramic coatings produced by Fireside Coatings. The densified surface modified portions may then be machined to remove any excess densifying material from the seating surfaces.
Referring to
Referring to
In some embodiments, each seat ring 14 may comprise two or more axially spaced raised annular bands 16 to act as two or more spaced seating surfaces for the ball 12. Each seat ring 14 may further comprise a band of low friction material 18, such as polytetrafluoroethylene (PTFE) or polyetheretherketone (PEEK), between each pair of adjacent axially spaced raised annular bands 16.
The ball 12 may be matched lapped to the two seat rings 14, and the finished fused-coated trim components may be supplied to end users as a kit of parts for a ball valve.
The following example is intended to illustrate the invention. It is not intended to limit the scope of the invention.
Examples of a fuse-coated ball and two seat rings of a titanium alloy for a 10″ Class 600 ball valve were prepared and coated in the manner described above. The surface-modified raised annular bands on the ball and seat rings were densified using a thermal spray coating of TiOxCrOx to leave a metallurgically fused coating having a finished thickness of around 1.5 mm. In comparison, conventional thermally spray coated balls have a coating thickness of around 0.5 mm.
The fuse-coated ball of this example was installed in-line at a high pressure acid leaching (HPAL) nickel plant as isolation trim in autoclave trains in parallel with conventional thermally spray coated titanium balls. The respective balls were then subjected to similar conditions, such as temperature, pressure and acidic slurry.
The fuse-coated ball of this example was checked at the 12-month mark and returned directly back to service due to the trim’s exceptional condition. It was only removed at the 29-month mark for research and development purposes, but otherwise was deemed in satisfactory condition for repair and reuse.
In addition to the above in-line testing, the fuse-coated trim of this example was subjected to accelerated in-house testing. Before the accelerated testing, the fuse-coated trim was test against standardised pipeline valve specification, API 6D. The leakage rate was 0 ml/min versus the allowable factory acceptance test of 1.5 ml/min. The fuse-coated trim of this example was then subject to accelerated testing under simulated HPAL conditions of 255° C., 4,500 kPa and using client-supplied acidic slurry, the valve was stroked 200+ times at pressure with 20+ strokes at full differential pressure, simulating 4 years of severe service. The valve operated within acceptable torque demand range and isolation performance throughout testing. No seizure occurred throughout the entire testing duration. As shown in
In view of the above, it is believed that the fuse-coated trim of this example may be capable of significantly extending trim life, particularly during severe conditions such as flashing during opening and closing phases.
Embodiments of the present invention provide fuse-coated trim components for ball valves, such as balls and seats, that are both specifically and generally useful in severe-service ball valves, such as those used in pressure leaching service applications.
Although embodiments of the present invention have been described above by way of example only in the context of trim components for severe-service, metal-seated ball valves, it will be nevertheless appreciated that embodiments may be alternatively implemented to metallurgically fuse coat any and all metal components used in any and all industrial processes that require increased resistance against wear and corrosion, but decreased delamination and spalling (or increased adherence) compared to conventional thermal spray coatings.
For the purpose of this specification, the word “comprising” means “including but not limited to,” and the word “comprises” has a corresponding meaning.
The above embodiments have been described by way of example only and modifications are possible within the scope of the claims that follow.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2020900303 | Feb 2020 | AU | national |