Claims
- 1. A powdered phosphor material comprising a member of the group consisting of GaP, GaxAl1-xP, GaxIn1-xN, GaAs, GaAlAs, GaN, GaxAl1-xN, and GaxIn1-xN wherein X is in the range of about 0.25 to about 1.
- 2. The phosphor material according to claim 1, wherein said powdered phosphor material additionally comprises an activator.
- 3. The powdered phosphor material according to claim 2, wherein said activator is selected from the group consisting of europium, terbium, thulium, manganese, copper, silver, praseodymium, cerium, dysprosium, holmium, ytterbium, samarium, gadolinium, chlorine, bismuth, titanium, aluminum, sodium, lithium, potassium, indium, zinc, magnesium, silicon, germanium and combinations thereof.
- 4. The phosphor material according to claim 1, wherein said powdered phosphor material additionally comprises a fluxing compound.
- 5. The phosphor material according to claim 4, wherein said fluxing compound is selected from the group consisting of sodium chloride, lithium chloride, potassium chloride, lithium fluoride, lithium silicate, chlorides of magnesium, strontium, and barium, magnesium fluoride, barium fluoride and combinations thereof.
- 6. The phosphor material according to claim 1, wherein the average particle size of said powder is in the range of about 1 micron to about 500 microns.
- 7. The phosphor material according to claim 1, wherein the average particle size of said powder is in the range of about 2 microns to about 10 microns.
- 8. A method of producing a powdered gallium phosphor material comprising:
i) heating a gallium metal to a temperature above the melting point of the metal to produce a molten gallium metal; ii) directing said molten gallium metal into an evacuated chamber; and, iii) impinging said molten gallium metal in said evacuated chamber with a nitrogen bearing gas to form a powdered gallium phosphor material.
- 9. The method of claim 8, wherein said gallium metal is semiconductor grade gallium.
- 10. The method of claim 8, wherein said gallium metal is a gallium alloy.
- 11. The method of claim 8, wherein said evacuated chamber is backfilled with a nitrogen-containing gas.
- 12. The method of claim 11, wherein said nitrogen-containing gas is selected from the group consisting of nitrogen, ammonia and mixtures thereof.
- 13. The method of claim 11, wherein said nitrogen-containing gas is buffered with a sulfur-bearing gas selected from the group consisting of SO2, SO3 and H2S gas.
- 14. The method of claim 8, comprising the additional step of:
firing said powdered gallium phosphor material under a gas comprising nitrogen, hydrogen, oxygen and hydrogen.
- 15. The method of claim 14, wherein said firing step further comprises adding an activator element selected from the group consisting of europium, terbium, thulium, manganese, copper, silver, praseodymium, cerium, dysprosium, holmium, ytterbium, samarium, gadolinium, chlorine, bismuth, titanium, aluminum, sodium, lithium, potassium, indium, zinc, magnesium, silicon, germanium and combinations thereof.
- 16. The method of claim 14, wherein said firing step further comprises adding a fluxing compound selected from the group consisting of sodium chloride, lithium chloride, potassium chloride, lithium fluoride, lithium silicate, chlorides of magnesium, strontium, and barium, magnesium fluoride, barium fluoride and combinations thereof.
- 17. A method of producing a powdered gallium phosphor material comprising the steps of:
i) supplying a gallium material selected from the group consisting of gallium metal and gallium oxide; ii) placing said gallium material into a fused silica retort; iii) flushing said retort with a nitrogen, hydrogen, sulfur and oxygen bearing gas; iv) heating said retort to a temperature between about 1000K and about 2000K for about 5 to about 50 hours; v) cooling said retort to less than about 400K; and, vi) exposing the gallium material within said retort to air to produce a powdered gallium phosphor material.
- 18. The method of claim 17, wherein the nitrogen, hydrogen, sulfur and oxygen bearing gas in said flushing step comprises ammonia.
- 19. The method of claim 17, wherein the nitrogen and hydrogen bearing gas comprises between about 99% nitrogen gas with about 1% hydrogen gas and about 5% nitrogen gas with about 95% hydrogen gas.
- 20. The method of claim 17, wherein the nitrogen and hydrogen bearing gas comprises between about 90% nitrogen gas with about 10% hydrogen gas and about 25% nitrogen gas with about 75% hydrogen gas.
- 21. The method of claim 17, comprising the additional step of:
grinding said powdered gallium phosphor material.
- 22. The method of claim 17, comprising the additional step of:
refiring said powdered gallium phosphor material under a gas comprising nitrogen, hydrogen, oxygen and hydrogen.
- 23. The method of claim 22, wherein said refiring step is conducted in the presence of an activator selected from the group consisting of europium, terbium, thulium, manganese, copper, silver, praseodymium, cerium, dysprosium, holmium, ytterbium, samarium, gadolinium, chlorine, bismuth, titanium, aluminum, sodium, lithium, potassium, indium, zinc, magnesium, silicon, germanium and combinations thereof.
- 24. The method of claim 22, wherein said refiring step is conducted in the presence of a fluxing compound selected from the group consisting of sodium chloride, lithium chloride, potassium chloride, lithium fluoride, lithium silicate, chlorides of magnesium, strontium, and barium, magnesium fluoride, barium fluoride and combinations thereof.
- 25. A method of producing a powdered gallium phosphor material comprising:
i) heating a gallium metal selected from the group consisting of semiconductor grade gallium and a gallium alloy to a temperature above the melting point of the metal to produce a molten gallium metal; ii) directing a stream of said molten gallium metal into a chamber that has been evacuated and backfilled with a gas selected from the group consisting of nitrogen, ammonia, a sulfoxide-buffered nitrogen-containing gas and mixtures thereof; iii) impinging said molten gallium metal in said evacuated chamber with a jet of nitrogen-bearing gas to form a powdered gallium phosphor material; and, iv) firing said powdered gallium phosphor material under a gas comprising nitrogen, hydrogen, oxygen and hydrogen in the presence of an activator selected from the group consisting of europium, terbium, thulium, manganese, copper, silver, praseodymium, cerium, dysprosium, holmium, ytterbium, samarium, gadolinium, chlorine, bismuth, titanium, aluminum, sodium, lithium, potassium, indium, zinc, magnesium, silicon, germanium and combinations thereof and in the presence of a fluxing compound selected from the group consisting of sodium chloride, lithium chloride, potassium chloride, lithium fluoride, lithium silicate, chlorides of magnesium, strontium, and barium, magnesium fluoride, barium fluoride and combinations thereof.
- 26. A method of producing a powdered gallium phosphor material comprising the steps of:
i) supplying a gallium material selected from the group consisting of gallium metal and gallium oxide; ii) placing said gallium material into a fused silica retort; iii) flushing said retort with a nitrogen, hydrogen, sulfur and oxygen bearing gas comprising between about 90% nitrogen gas with about 10% hydrogen gas and about 25% nitrogen gas with about 75% hydrogen gas; iv) heating said retort to a temperature between about 1000K and about 2000K for about 5 to about 50 hours; v) cooling said retort to less than about 400K; vi) exposing the gallium material within said retort to air to produce a powdered gallium phosphor material; and, vii) refiring said powdered gallium phosphor material under a gas comprising nitrogen, hydrogen, oxygen and hydrogen in the presence of an activator selected from the group consisting of europium, terbium, thulium, manganese, copper, silver, praseodymium, cerium, dysprosium, holmium, ytterbium, samarium, gadolinium, chlorine, bismuth, titanium, aluminum, sodium, lithium, potassium, indium, zinc, magnesium, silicon, germanium and combinations thereof and in the presence of a fluxing compound selected from the group consisting of sodium chloride, lithium chloride, potassium chloride, lithium fluoride, lithium silicate, chlorides of magnesium, strontium, and barium, magnesium fluoride, barium fluoride and combinations thereof.
Parent Case Info
[0001] This application claims the benefit of Provisional Patent Application Serial No. 60/270,501 filed in the U.S. Patent and Trademark Office on Feb. 21, 2001.
Provisional Applications (1)
|
Number |
Date |
Country |
|
60270501 |
Feb 2001 |
US |