Patent Grant
11167343
The invention is directed to a novel material for use as a dissolvable structure in oil drilling. Specifically, the invention is directed to a ball or other structure in a well drilling or completion operation, such as a structure that is seated in a hydraulic operation, that can be dissolved away after use so that that no drilling or removal of the structure is necessary. Primarily, dissolution is measured as the time the ball removes itself from the seat or can become free floating in the system. Secondarily, dissolution is measured in the time the ball is substantially or fully dissolved into submicron particles. Furthermore, the novel material of the present invention can be used in other well structures that also desire the function of dissolving after a period of time. The material is machinable and can be used in place of existing metallic or plastic structures in oil and gas drilling rigs including, but not limited to, water injection and hydraulic fracturing.
The ability to control the dissolution of a downhole well component in a variety of solutions is important to the utilization of non-drillable completion tools, such as sleeves, frac balls, hydraulic actuating tooling, and the like. Reactive materials for this application, which dissolve or or corrode when exposed to acid, salt, and/or other wellbore conditions, have been proposed for some time. Generally, these components consist of materials that are engineered to dissolve or corrode.
While the prior art well drill components have enjoyed modest success in reducing well completion costs, their consistency and ability to specifically control dissolution rates in specific solutions, as well as other drawbacks such as limited strength and poor reliability, have impacted their widespread adoption. Ideally, these components would be manufactured by a process that is low cost, scalable, and produces a controlled corrosion rate having similar or increased strength as compared to traditional engineering alloys such as aluminum, magnesium, and iron. Ideally, traditional heat treatments, deformation processing, and machining techniques could be used on the components without impacting the dissolution rate and reliability of such components.
Prior art articles regarding calcium use in magnesium are set for in Koltygin et al., “Effect of calcium on the process of production and structure of magnesium melted by flux-free method” Magnesium and Its Alloys (2013): 540-544; Koltygin et al., “Development of a magnesium alloy with good casting characteristics on the basis of Mg—Al—Ca—Mn system, having Mg—Al2Ca structure.” Journal of Magnesium and Alloys 1 (2013): 224-229; Li et al., “Development of non-flammable high strength AZ91+Ca alloys via liquid forging and extrusion.” Materials and Design (2016): 37-43; Cheng et al. “Effect of Ca and Y additions on oxidation behavior of AZ91 alloy at elevated temperatures.” Transactions of Nonferrous Metals Society of China (2009): 299-304; and Qudong et al., “Effects of Ca addition on the microstructure and mechanical properties of AZ91 magnesium alloy.” Journal of Materials Science (2001): 3035-3040.
The present invention is directed to a novel magnesium composite for use as a dissolvable component in oil drilling and will be described with particular reference to such application. As can be appreciated, the novel magnesium composite of the present invention can be used in other applications (e.g., non-oil wells, etc.). In one non-limiting embodiment, the present invention is directed to a ball or other tool component in a well drilling or completion operation such as, but not limited to, a component that is seated in a hydraulic operation that can be dissolved away after use so that no drilling or removal of the component is necessary. Tubes, valves, valve components, plugs, frac balls, sleeve, hydraulic actuating tooling, mandrels, slips, grips, balls, darts, carriers, valve components, other downhole well components and other shapes of components can also be formed of the novel magnesium composite of the present invention. For purposes of this invention, primary dissolution is measured for valve components and plugs as the time the part removes itself from the seat of a valve or plug arrangement or can become free floating in the system. For example, when the part is a plug in a plug system, primary dissolution occurs when the plug has degraded or dissolved to a point that it can no long function as a plug and thereby allows fluid to flow about the plug. For purposes of this invention, secondary dissolution is measured in the time the part is fully dissolved into submicron particles. As can be appreciated, the novel magnesium composite of the present invention can be used in other well components that also desire the function of dissolving after a period of time. In one non-limiting aspect of the present invention, a galvanically-active phase is precipitated from the novel magnesium composite composition and is used to control the dissolution rate of the component; however, this is not required. The novel magnesium composite is generally castable and/or machinable and can be used in place of existing metallic or plastic components in oil and gas drilling rigs including, but not limited to, water injection and hydraulic fracturing. The novel magnesium composite can be heat treated as well as extruded and/or forged.
In one non-limiting aspect of the present invention, the novel magnesium composite is used to form a castable, moldable, or extrudable component. Non-limiting magnesium composites in accordance with the present invention include at least 50 wt. % magnesium. One or more additives are added to a magnesium or magnesium alloy to form the novel magnesium composite of the present invention. The one or more additives can be selected and used in quantities so that galvanically-active intermetallic or insoluble precipitates form in the magnesium or magnesium alloy while the magnesium or magnesium alloy is in a molten state and/or during the cooling of the melt; however, this is not required. The one or more additives can be in the form of a pure or nearly nearly pure additive element (e.g., at least 98% pure), or can be added as an alloy of two or more additive elements or an alloy of magnesium and one or more additive elements. The one or more additives typically are added in a weight percent that is less than a weight percent of said magnesium or magnesium alloy. Typically, the magnesium or magnesium alloy constitutes about 50.1-99.9 wt. % of the magnesium composite and all values and ranges therebetween. In one non-limiting aspect of the invention, the magnesium or magnesium alloy constitutes about 60-95 wt. % of the magnesium composite, and typically the magnesium or magnesium alloy constitutes about 70-90 wt. % of the magnesium composite. The one or more additives can be added to the molten magnesium or magnesium alloy at a temperature that is less than the melting point of the one or more additives; however, this is not required. The one or more additives generally have an average particle diameter size of at least about 0.1 microns, typically no more than about 500 microns (e.g., 0.1 microns, 0.1001 microns, 0.1002 microns . . . 499.9998 microns, 499.9999 microns, 500 microns) and include any value or range therebetween, more typically about 0.1-400 microns, and still more typically about 10-50 microns. In one non-limiting configuration, the particles can be less than 1 micron. During the process of mixing the one or more additives in the molten magnesium or magnesium alloy, the one or more additives do not typically fully melt in the molten magnesium or magnesium alloy; however, the one or more additives can form a single-phase liquid with the magnesium while the mixture is in the molten state. As can be appreciated, the one or more additives can be added to the molten magnesium or magnesium alloy at a temperature that is greater than the melting point of the one or more additives. The one or more additives can be added individually as pure or substantially pure additive elements or can be added as an alloy that is formed of a plurality of additive elements and/or an alloy that includes one or more additive elements and magnesium. When one or more additive elements are added as an alloy, the melting point of the alloy may be less than the melting point of one or more of the additive elements that are used to form the alloy; however, this is not required. As such, the addition of an alloy of the one or more additive elements could be caused to melt when added to the molten magnesium at a certain temperature, whereas if the same additive elements were individually added to the molten magnesium at the same temperature, such individual additive elements would not fully melt in the molten magnesium.
The one or more additives are selected such that as the molten magnesium cools, newly formed metallic alloys and/or additives begin to precipitate out of the molten metal and form the in situ phase to the matrix phase in the cooled and solid magnesium composite. After the mixing process is completed, the molten magnesium or magnesium alloy and the one or more additives that are mixed in the molten magnesium or magnesium alloy are cooled to form a solid component. In one non-limiting embodiment, the temperature of the molten magnesium or magnesium alloy is at least about 10° C. less than the melting point of the additive that is added to the molten magnesium or magnesium alloy during the addition and mixing process, typically at least about 100° C. less than the melting point of the additive that is added to the molten magnesium or magnesium alloy during the addition and mixing process, more typically about 100-1000° C. (and any value or range therebetween) less than the melting point of the additive that is added to the molten magnesium or magnesium alloy during the addition and mixing process; however, this is not required. As can be appreciated, one or more additives in the form of an alloy or a pure or substantially pure additive element can be added to the magnesium that have a melting point that is less than the melting point of magnesium, but still at least partially precipitate out of the magnesium as the magnesium cools from its molten state to a solid state. Generally, such one or more additives and/or one or more components of the additives form an alloy with the magnesium and/or one or more other additives in the molten magnesium. The formed alloy has a melting point that is greater than a melting point of magnesium, thereby results in the precipitation of such formed alloy during the cooling of the magnesium from the molten state to the solid state. The never melted additive(s) and/or the newly formed alloys that include one or more additives are referred to as in situ particle formation in the molten magnesium composite. Such a process can be used to achieve a specific galvanic corrosion rate in the entire magnesium composite and/or along the grain boundaries of the magnesium composite.
The invention adopts a feature that is usually a negative in traditional casting practices wherein a particle is formed during the melt processing that corrodes the alloy when exposed to conductive fluids and is imbedded in eutectic phases, the grain boundaries, and/or even within grains with precipitation hardening. This feature results in the ability to control where the galvanically-active phases are located in the final casting, as well as the surface area ratio of the in situ phase to the matrix phase, which enables the use of lower cathode phase loadings as compared to a powder metallurgical or alloyed composite to achieve the same dissolution rates. The in situ formed galvanic additives can be used to enhance mechanical properties of the magnesium composite such as ductility, tensile strength, and/or shear strength. The final magnesium composite can also be enhanced by heat treatment as well as deformation processing (such as extrusion, forging, or rolling) to further improve the strength of the final composite over the as-cast material; however, this is not required. The deformation processing can be used to achieve strengthening of the magnesium composite by reducing the grain size of the magnesium composite. Further enhancements, such as traditional alloy heat treatments (such as solutionizing, aging and/or cold working) can be used to enable control of dissolution rates through precipitation of more or less galvanically-active phases within the alloy microstructure while improving mechanical properties; however, this is not required. Because galvanic corrosion is driven by both the electro potential between the anode and cathode phase, as well as the exposed surface area of the two phases, the rate of corrosion can also be controlled through adjustment of the in situ formed particle size, while not increasing or decreasing the volume or weight fraction of the addition, and/or by changing the volume/weight fraction without changing the particle size. Achievement of in situ particle size control can be achieved by mechanical agitation of the melt, ultrasonic processing of the melt, controlling cooling rates, and/or by performing heat treatments. In situ particle size can also or alternatively be modified by secondary processing such as rolling, forging, extrusion and/or other deformation techniques.
In another non-limiting aspect of the invention, a cast structure can be made into almost any shape. During formation, the active galvanically-active in situ phases can be uniformly dispersed throughout the component and the grain or the grain boundary composition can be modified to achieve the desired dissolution rate. The galvanic corrosion can be engineered to affect only the grain boundaries and/or can affect the grains as well (based on composition); however, this is not required. This feature can be used to enable fast dissolutions of high-strength lightweight alloy composites with significantly less active (cathode) in situ phases as compared to other processes.
In still another and/or alternative non-limiting aspect of the invention, ultrasonic processing can be used to control the size of the in situ formed galvanically-active phases; however, this is not required. Ultrasonic energy is used to degass and grain refine alloys, particularly when applied in the solidification region. Ultrasonic and stirring can be used to refine the grain size in the alloy, thereby creating a high strength alloy and also reducing dispersoid size and creating more equiaxed (uniform) grains. Finer grains in the alloy have been found to reduce the degradation rate with equal amounts of additives.
In yet another and/or alternative non-limiting aspect of the invention, the in situ formed particles can act as matrix strengtheners to further increase the tensile strength of the material compared to the base alloy without the one or more additives; however, this is not required. For example, tin can be added to form a nanoscale precipitate (can be heat treated, e.g., solutionized and then precipitated to form precipitates inside the primary magnesium grains). The particles can be used to increase the strength of the alloy by at least 10%, and as much as greater than 100%, depending on other strengthening mechanisms (second phase, grain refinement, solid solution) strengthening present.
In still yet another and/or alternative non-limiting aspect of the invention, there is provided a method of controlling the dissolution properties of a metal selected from the class of magnesium and/or magnesium alloy comprising of the steps of a) melting the magnesium or magnesium alloy to a point above its solidus, b) introducing one or more additives to the magnesium or magnesium alloy in order to achieve in situ precipitation of galvanically-active intermetallic phases, and c) cooling the melt to a solid form. The one or more additives are generally added to the magnesium or magnesium alloy when the magnesium or magnesium alloy is in a molten state and at a temperature that is less than the melting point of one or more additive materials. As can be appreciated, one or more additives can be added to the molten magnesium or magnesium alloy at a temperature that is greater than the melting point of the one or more additives. The one or more additives can be added as individual additive elements to the magnesium or magnesium alloy, or be added in alloy form as an alloy of two or more additives, or an alloy of one or more additives and magnesium or magnesium alloy. The galvanically-active intermetallic phases can be used to enhance the yield strength of the alloy; however, this is not required. The size of the in situ precipitated intermetallic phase can be controlled by a melt mixing technique and/or cooling rate; however, this is not required. It has been found that the addition of the one or more additives (SM) to the molten magnesium or magnesium alloy can result in the formation of MgSMx, MgxSM, and LPSO and other phases with two, three, or even four components that include one or more galvanically-active additives that result in the controlled degradation of the formed magnesium composite when exposed to certain environments (e.g., salt water, brine, fracking liquids, etc.). The method can include the additional step of subjecting the magnesium composite to intermetallic precipitates to solutionizing of at least about 300° C. to improve tensile strength and/or improve ductility; however, this is not required. The solutionizing temperature is less than the melting point of the magnesium composite. Generally, the solutionizing temperature is less than 50-200° C. of the melting point of the magnesium composite and the time period of solutionizing is at least 0.1 hours. In one non-limiting aspect of the invention, the magnesium composite can be subjected to a solutionizing temperature for about 0.5-50 hours (and all values and ranges therebetween) (e.g., 1-15 hours, etc.) at a temperature of 300-620° C. (and all values and ranges therebetween) (e.g., 300-500° C., etc.). The method can include the additional step of subjecting the magnesium composite to intermetallic precipitates and to artificially age the magnesium composite at a temperature at least about 90° C. to improve the tensile strength; however, this is not required. The artificial aging process temperature is typically less than the solutionizing temperature and the time period of the artificial aging process temperature is typically at least 0.1 hours. Generally, the artificial aging process at is less than 50-400° C. (the solutionizing temperature). In one non-limiting aspect of the invention, the magnesium composite can be subjected to the artificial aging process for about 0.5-50 hours (and all values and ranges therebetween) (e.g., 1-16 hours, etc.) at a temperature of 90-300° C. (and all values and ranges therebetween) (e.g., 100-200° C.).
In still yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is over 50 wt. % magnesium and about 0.5-49.5 wt. % of additive (SM) (e.g., aluminum, zinc, tin, beryllium, boron carbide, copper, nickel, bismuth, cobalt, titanium, manganese, potassium, sodium, antimony, indium, strontium, barium, silicon, lithium, silver, gold, cesium, gallium, calcium, iron, lead, mercury, arsenic, rare earth metals (e.g., yttrium, lanthanum, samarium, europium, gadolinium, terbium, dysprosium, holmium, ytterbium, etc.) and zirconium) (and all values and ranges therebetween) is added to the magnesium or magnesium alloy to form a galvanically-active intermetallic particle. The one or more additives can be added to the magnesium or magnesium alloy while the temperature of the molten magnesium or magnesium alloy is less than or greater than the melting point of the one or more additives. In one non-limiting embodiment, throughout the mixing process, the temperature of the molten magnesium or magnesium alloy can be less than the melting point of the one or more additives. In another non-limiting embodiment, throughout the mixing process, the temperature of the molten magnesium or magnesium alloy can be greater than the melting point of the one or more additives. In another non-limiting embodiment, throughout the mixing process, the temperature of the molten magnesium or magnesium alloy can be greater than the melting point of the one or more additives and less than the melting point of one or more other additives. In another non-limiting embodiment, throughout the mixing process, the temperature of the molten magnesium or magnesium alloy can be greater than the melting point of the alloy that includes one or more additives. In another non-limiting embodiment, throughout the mixing process, the temperature of the molten magnesium or magnesium alloy can be less than the melting point of the alloy that includes one or more additives. During the mixing process, solid particles of SMMgx, SMxMg can be formed. Once the mixing process is complete, the mixture of molten magnesium or magnesium alloy, SMMgx, SMxMg, and/or any unalloyed additive is cooled and an in situ precipitate is formed in the solid magnesium composite.
In another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is over 50 wt. % magnesium and about 0.05-49.5 wt. % nickel (and all values or ranges therebetween) is added to the magnesium or magnesium alloy to form intermetallic Mg2Ni as a galvanically-active in situ precipitate. In one non-limiting arrangement, the magnesium composite includes about 0.05-23.5 wt. % nickel, 0.01-5 wt. % nickel, 3-7 wt. % nickel, 7-10 wt. % nickel, or 10-24.5 wt. % nickel. The nickel is added to the magnesium or magnesium alloy while the temperature of the molten magnesium or magnesium alloy is less than the melting point of the nickel; however, this is not required. In one non-limiting embodiment, throughout the mixing process, the temperature of the molten magnesium or magnesium alloy is less than the melting point of the nickel. During the mixing process, solid particles of Mg2Ni can be formed; but is not required. Once the mixing process is complete, the mixture of molten magnesium or magnesium alloy, any solid particles of Mg2Ni, and any unalloyed nickel particles are cooled and an in situ precipitate of any solid particles of Mg2Ni and any unalloyed nickel particles is formed in the solid magnesium composite. Generally, the temperature of the molten magnesium or magnesium alloy is at least about 200° C. less than the melting point of the nickel added to the molten magnesium or magnesium alloy during the addition and mixing process; however, this is not required.
In still another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is over 50 wt. % magnesium and about 0.05-49.5 wt. % copper (and all values or ranges therebetween) is added to the magnesium or magnesium alloy to form galvanically-active in situ precipitate that includes copper and/or copper alloy. In one non-limiting arrangement, the magnesium composite includes about 0.01-5 wt. % copper, about 0.5-15 wt. % copper, about 15-35 wt. % copper, or about 0.01-20 wt. % copper. The copper is added to the magnesium or magnesium alloy while the temperature of the molten magnesium or magnesium alloy is less than the melting point of the copper; however, this is not required. In one non-limiting embodiment, throughout the mixing process, the temperature of the molten magnesium or magnesium alloy is less than the melting point of the copper; however, this is not required. During the mixing process, solid particles of CuMg2 can be formed; but is not required. Once the mixing process is complete, the mixture of molten magnesium or magnesium alloy, any solid particles of CuMg2, and any unalloyed copper particles are cooled and an in situ precipitate of any solid particles of CuMg2 and any unalloyed copper particles is formed in the solid magnesium composite. Generally, the temperature of the molten magnesium or magnesium alloy is at least about 200° C. less than the melting point of the copper added to the molten magnesium or magnesium alloy; however, this is not required.
In yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is over 50 wt. % magnesium and about 0.05-49.5% by weight cobalt (and all values and ranges therebetween) is added to the magnesium or magnesium alloy to form galvanically active in situ precipitate that includes cobalt and/or cobalt alloy. In one non-limiting arrangement, the magnesium composite includes about 0.01-5 wt. %© cobalt, about 0.5-15 wt. % cobalt, about 15-35 wt. % cobalt, or about 0.01-20 wt. % cobalt. The cobalt is added to the magnesium or magnesium alloy while the temperature of the molten magnesium or magnesium alloy is less than the melting point of the cobalt; however, this is not required. In one non-limiting embodiment, throughout the mixing process, the temperature of the molten magnesium or magnesium alloy is less than the melting point of the cobalt; however, this is not required. During the mixing process, solid particles of CoMg2 and/or MgxCo can be formed; but is not required. Once the mixing process is complete, the mixture of molten magnesium or magnesium alloy, any solid particles of CoMg2, MgxCo, any solid particles of any unalloyed cobalt particles are cooled and an in situ precipitate of any solid particles of CoMg2, MgxCo, any solid particles of unalloyed cobalt particles is formed in the solid magnesium composite. Generally, the temperature of the molten magnesium or magnesium alloy is at least about 200° C. less than the melting point of the cobalt added to the molten magnesium or magnesium alloy; however, this is not required.
In another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is over 50 wt. % magnesium and up to about 49.5% by weight bismuth (and all values and ranges therebetween) is added to the magnesium or magnesium alloy to form galvanically-active in situ precipitate that includes bismuth and/or bismuth alloy. Bismuth intermetallics are formed above roughly 0.1 wt. % bismuth, and bismuth is typically useful up to its eutectic point of roughly 11 wt. % bismuth. Beyond the eutectic point, a bismuth intermetallic is formed in the melt. This is typical of additions, in that the magnesium-rich side of the eutectic forms flowable, castable materials with active precipitates or intermetallics formed at the solidus (in the eutectic mixture), rather than being the primary, or initial, phase solidified. In desirable alloy formulations, alpha magnesium (may be in solid solution with alloying elements) should be the initial/primary phase formed upon initial cooling. In one non-limiting embodiment, bismuth is added to the magnesium composite at an amount of greater than 11 wt. %, and typically about 11.1-30 wt. % (and all values and ranges therebetween).
In another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is over 50 wt. % magnesium and up to about 49.5% by weight tin (and all values and ranges therebetween) is added to the magnesium or magnesium alloy to form galvanically-active in situ precipitate that includes tin and/or tin alloy. Tin additions have a significant solubility in solid magnesium at elevated temperatures, forming both a eutectic (at grain boundaries), as well as in the primary magnesium (dispersed). Dispersed precipitates, which can be controlled by heat treatment, lead to large strengthening, while eutectic phases are particularly effective at initiating accelerated corrosion rates. In one non-limiting embodiment, tin is added to the magnesium composite at an amount of at least 0.5 wt. %, typically about 1-30 wt. % (and all values and ranges therebetween), and more typically about 1-10 wt. %.
In another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is over 50 wt. % magnesium and up to about 49.5% by weight gallium (and all values and ranges therebetween) is added to the magnesium or magnesium alloy to form galvanically active in situ precipitate that includes gallium and/or gallium alloy. Gallium additions are particularly effective at initiating accelerated corrosion, in concentrations that form up to 3-5 wt. % Mg5Ga2. Gallium alloys are heat treatable forming corrodible high strength alloys. Gallium is fairly unique, in that it has high solubility in solid magnesium, and forms highly corrosive particles during solidification which are located inside the primary magnesium (when below the solid solubility limit), such that both grain boundary and primary (strengthening precipitates) are formed in the magnesium-gallium systems and also in magnesium-indium systems. At gallium concentrations of less than about 3 wt. %, additional superheat (higher melt temperatures) is typically used to form the precipitate in the magnesium alloy. To place Mg5Ga2 particles at the grain boundaries, gallium concentrations above the solid solubility limit at the pouring temperature are used such that Mg5Ga2 phase is formed from the eutectic liquid. In one non-limiting embodiment, gallium is added to the magnesium composite at an amount of at least 1 wt. %, and typically about 1-10 wt. % (and all values and ranges therebetween), typically 2-8 wt. %, and more typically 3.01-5 wt. %.
In another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is over 50 wt. % magnesium and up to about 49.5% by weight indium (and all values and ranges therebetween) is added to the magnesium or magnesium alloy to form galvanically-active in situ precipitate that includes indium and/or indium alloy. Indium additions have also been found effective at initiating corrosion. In one non-limiting embodiment, indium is added to the magnesium composite at an amount of at least 1 wt. %, and typically about 1-30 wt. % (and all values and ranges therebetween).
In general, precipitates having an electronegativity greater than 1.4-1.5 act as corrosion acceleration points, and are more effective if formed from the eutectic liquid during solidification, than precipitation from a solid solution. Alloying additions added below their solid solubility limit which precipitate in the primary magnesium phase during solidification (as opposed to along grain boundaries), and which can be solutionized are more effective in creating higher strength, particularly in as-cast alloys.
In another and/or alternative non-limiting aspect of the invention, the molten magnesium or magnesium alloy that includes the one or more additives can be controllably cooled to form the in situ precipitate in the solid magnesium composite. In one non-limiting embodiment, the molten magnesium or magnesium alloy that includes the one or more additives is cooled at a rate of greater than 1° C. per minute. In one non-limiting embodiment, the molten magnesium or magnesium alloy that includes the one or more additives is cooled at a rate of less than 1° C. per minute. In one non-limiting embodiment, the molten magnesium or magnesium alloy that includes the one or more additives is cooled at a rate of greater than 0.01° C. per min and slower than 1° C. per minute. In one non-limiting embodiment, the molten magnesium or magnesium alloy that includes the one or more additives is cooled at a rate of greater than 10° C. per minute and less than 100° C. per minute. In one non-limiting embodiment, the molten magnesium or magnesium alloy that includes the one or more additives is cooled at a rate of less than 10° C. per minute. In another non-limiting embodiment, the molten magnesium or magnesium alloy that includes the one or more additives is cooled at a rate 10-100° C./min (and all values and ranges therebetween) through the solidus temperature of the alloy to form fine grains in the alloy.
In another and/or alternative non-limiting aspect of the invention, there is provided a magnesium alloy that includes over 50 wt. % magnesium (e.g., 50.01-99.99 wt. % and all values and ranges therebetween) and includes at least one metal selected from the group consisting of aluminum, boron, bismuth, zinc, zirconium, and manganese. As can be appreciated, the magnesium alloy can include one or more additional metals. In one non-limiting embodiment, the magnesium alloy includes over 50 wt. % magnesium and includes at least one metal selected from the group consisting of aluminum in an amount of about 0.05-10 wt. % (and all values and ranges therebetween), zinc in amount of about 0.05-6 wt. % (and all values and ranges therebetween), zirconium in an amount of about 0.01-3 wt. % (and all values and ranges therebetween), and/or manganese in an amount of about 0.015-2 wt. % (and all values and ranges therebetween). In another non-limiting formulation, the magnesium alloy includes over 50 wt. % magnesium and includes at least one metal selected from the group consisting of zinc in amount of about 0.05-6 wt. %, zirconium in an amount of about 0.05-3 wt. %©, manganese in an amount of about 0.05-0.25 wt. %, boron (optionally) in an amount of about 0.0002-0.04 wt. %, and bismuth (optionally) in an amount of about 0.4-0.7 wt. %. In still another and/or alternative non-limiting aspect of the invention, there is provided a magnesium alloy that is over 50 wt. % magnesium and at least one metal selected from the group consisting of aluminum in an amount of about 0.05-10 wt. % (and all values and ranges therebetween), zinc in an amount of about 0.05-6 wt. % (and all values and ranges therebetween), calcium in an amount of about 0.5-8 wt. %% (and all values and ranges therebetween), zirconium in amount of about 0.05-3 wt. % (and all values and ranges therebetween), manganese in an amount of about 0.05-0.25 wt. % (and all values and ranges therebetween), boron in an amount of about 0.0002-0.04 wt. % (and all values and ranges therebetween), and/or bismuth in an amount of about 0.04-0.7 wt. % (and all values and ranges therebetween).
In still another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is over 50 wt. % magnesium and includes one or more additives in the form of a first additive that has an electronegativity that is greater than 1.5, and typically greater than 1.8. The electronegativity of magnesium is 1.31. As such, the first additive has a higher electronegativity than magnesium. The first additive can include one or more metals selected from the group consisting of nickel (1.91), cobalt (1.88), copper (1.90), bismuth (2.02), lead (1.87), tin (1.96), antimony (2.05), indium (1.78), silver (1.93), gold (2.54), and gallium (1.81). It has been found that by adding one or more first additives to a molten magnesium or molten magnesium alloy, galvanically-active phases can be formed in the solid magnesium composite having desired dissolution rates in salt water, fracking liquid or brine environments. The one or more first additives are added to the molten magnesium or molten magnesium alloy such that the final magnesium composite includes 0.05-49.55% by weight of the one or more first additives (and all values and ranges therebetween), and typically 0.5-35% by weight of the one or more first additives. The one or more first additives having an electronegativity that is greater than 1.5 have been found to form galvanically-active phases in the solid magnesium composite to enhance the dissolution rate of the magnesium composite in salt water, fracking liquid or brine environments.
In yet another and/or alternative non-limiting aspect of the invention, it has been found that in addition to the adding of one or more first additives having an electronegativity that is greater than 1.5 to the molten magnesium or molten magnesium alloy to enhance the dissolution rates of the magnesium composite in salt water, fracking liquid or brine environments, one or more second additives that have an electronegativity of 1.25 or less can also be added to the molten magnesium or molten magnesium alloy to further enhance the dissolution rates of the solid magnesium composite. The one or more second additives can optionally be added to the molten magnesium or molten magnesium alloy such that the final magnesium composite includes 0.05-35% by weight of the one or more second additives (and all values and ranges therebetween), and typically 0.5-30% by weight of the one or more second additives. The second additive can include one or more metals selected from the group consisting of calcium (1.0), strontium (0.95), barium (0.89), potassium (0.82), sodium (0.93), lithium (0.98), cesium (0.79), and the rare earth metals such as yttrium (1.22), lanthanum (1.1), samarium (1.17), europium (1.2), gadolinium (1.2), terbium (1.1), dysprosium (1.22), holmium (1.23), and ytterbium (1.1).
Secondary additives are usually added at 0.5-10 wt. %, and generally 0.1-3 wt. %. In one non-limiting embodiment, the amount of secondary additive is less than the primary additive; however, this is not required. For example, calcium can be added up to 10 wt. %, but is added normally at 0.5-3 wt. %. In most cases, the strengthening alloying additions or modifying materials are added in concentrations which can be greater than the high electronegativity corrosive phase forming element. The secondary additions are generally designed to have high solubility, and are added below their solid solubility limit in magnesium at the melting point, but above their solid solubility limit at some lower temperature. These form precipitates that strengthen the magnesium, and may or may not be galvanically active. They may form a precipitate by reacting preferentially with the high electronegativity addition (e.g., binary, ternary, or even quaternary intermetallics), with magnesium, or with other alloying additions.
The one or more secondary additives that have an electronegativity that is 1.25 or less have been found to form galvanically-active phases in the solid magnesium composite to enhance the dissolution rate of the magnesium composite in salt water, fracking liquid or brine environments are. The inclusion of the one or more second additives with the one or more first additives in the molten magnesium or magnesium alloy has been found to enhance the dissolution rate of the magnesium composite by 1) alloying with inhibiting aluminum, zinc, magnesium, alloying additions and increasing the EMF driving force with the gavanically-active phase, and/or 2) reducing the electronegativity of the magnesium (e.g., α-magnesium) phase when placed in solid solution or magnesium-EPE (electropositive element) intermetallics. The addition of materials with an electronegativity that is less than magnesium, such as rare earths, group 1, and group II, and group III elements on the periodic table, can enhance the degradability of the alloy when a high electronegativity addition is also present by reducing the electronegativity (increasing the driving force) in solid solution in magnesium, and/or by forming lower electronegativity precipitates that interact with the higher electronegativity precipitates. This technique/additions is particularly effective at reducing the sensitivity of the corrosion rates to temperature or salt content of the corroding or downhole fluid.
The addition of both electropositive (1.5 or greater) first additives and electronegative (1.25 or less) second additives to the molten magnesium or magnesium alloy can result in higher melting phases being formed in the magnesium composite. These higher melting phases can create high melt viscosities and can dramatically increase the temperature (and therefore the energy input) required to form the low viscosity melts suitable for casting. By dramatically increasing the casting temperature to above 700-780° C., or utilizing pressure to drive mold filling (e.g., squeeze casting), such processes can be used to produce a high quality, low-inclusion and low-porosity magnesium composite casting.
In yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is subjected to heat treatments such as solutionizing, aging and/or cold working to be used to control dissolution rates through precipitation of more or less galvanically-active phases within the alloy microstructure while improving mechanical properties. The artificial aging process (when used) can be for at least about 1 hour, for about 1-50 hours (and all values and ranges therebetween), for about 1-20 hours, or for about 8-20 hours. The solutionizing (when used) can be for at least about 1 hour, for about 1-50 hours (and all values and ranges therebetween), for about 1-20 hours, or for about 8-20 hours. When an alloy with a galvanically-active phase (higher and/or lower electronegativity than Mg) with significant solid solubility is solutionized, substantial differences in corrosion/degradation rates can be achieved through mechanisms of oswald ripening or grain growth (coarsening of the active phases), which increases corrosion rates by 10-100% (and all values and ranges therebewteen). When the solutionizing removes active phase and places it in solid solution, or creates finer precipitates (refined grain sizes), corrosion rates are decreased by 10-50%, up to about 75%.
In still yet another and/or alternative non-limiting aspect of the invention, there is provided a method for controlling the dissolution rate of the magnesium composite wherein the magnesium content is at least about 75% and at least about 0.05 wt. % nickel is added to form in situ precipitation in the magnesium or magnesium alloy and solutionizing the resultant metal at a temperature within a range of 100-500° C. (and all values and ranges therebetween) for a period of 0.25-50 hours (and all values and ranges therebetween), the magnesium composite being characterized by higher dissolution rates than metal without nickel additions subjected to the said artificial aging process.
In another and/or alternative non-limiting aspect of the invention, there is provided a method for improving the physical properties of the magnesium composite wherein the magnesium content is at least about 85% and at least about 0.05 wt. % nickel is added to form in situ precipitation in the magnesium or magnesium alloy and solutionizing the resultant metal at a temperature at about 100-500° C. (and all values and ranges therebetween) for a period of 0.25-50 hours, the magnesium composite being characterized by higher tensile and yield strengths than magnesium base alloys of the same composition, not including the amount of nickel.
In still another and/or alternative non-limiting aspect of the invention, there is provided a method for controlling the dissolution rate of the magnesium composite wherein the magnesium content in the alloy is at least about 75% and at least about 0.05 wt. % copper is added to form in situ precipitation in the magnesium or magnesium alloy and solutionizing the resultant metal at a temperature within a range of 100-500° C. for a period of 0.25-50 hours, the magnesium composite being characterized by higher dissolution rates than metal without copper additions subjected to the said artificial aging process.
In still yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that includes the addition of calcium to galvanically-active magnesium-aluminum-(X) alloys with X being a galvanically-active intermetallic forming phase such as, but not limited to, nickel, copper, or cobalt to further control the degradation rate of the alloys, further increase the use and extrusion temperature of the magnesium composite, and/or reduce the potential for flammability during formation of the magnesium composite, thereby increasing safety. Calcium has a higher standard electrode potential than magnesium at −2.87V as compared to −2.37V for magnesium relative to standard hydrogen electrode (SHE). This electrode potential of calcium makes the galvanic potential between other metallic ions significantly higher, such as nickel (−0.25V), copper (+0.52V) and iron (−0.44V). The difference in galvanic potential also depends on other alloying elements with respect to microstructural location. In alloys where only magnesium and calcium are present, the difference in galvanic potential can change the degradation behavior of the alloy by leading to a greater rate of degradation in the alloy. However, the mechanism for dissolution speed change in the galvanically-active alloys created by intermetallic phases such as magnesium-nickel, magnesium-copper, and magnesium-cobalt is actually different. In the case of the magnesium-aluminum-calcium-(X) with X being a galvanically-active intermetallic forming phase such as nickel, copper, or cobalt with aluminum in the alloy, the calcium typically bonds with the aluminum (−1.66V), and this phase precipitates next to the magnesium matrix. The Mg17Al12 phase that is normally precipitated in a magnesium-aluminum-(X) with X being a galvanically-active intermetallic forming phase such as nickel, copper, or cobalt alloy is the primary contributor to a reduced and controlled degradation of the alloy.
By introducing calcium into the alloy, the amount of Mg17Al12 is reduced in the alloy, thus increasing the ratio of magnesium-(X) phase to the pure magnesium alloy and thereby reducing the galvanic corrosion resistance of the Mg17Al12 phase, which result in the further increase of the degradation rate of the magnesium-aluminum-calcium-(X) alloy as compared to magnesium-aluminum-(X) alloys. This feature of the alloy is new and unexpected because it is not just the addition of a higher standard electrode potential that is causing the degradation, but is also the reduction of a corrosion inhibitor by causing the formation of a different phase in the alloy. The calcium addition within the magnesium alloy forms an alternative phase with aluminum alloying elements. The calcium bonds with aluminum within the alloy to form lamellar Al2Ca precipitates along the grain boundary of the magnesium matrix. These precipitates act as nucleation sites during cooling (due to their low energy barrier for nucleation) leading to decreased grain size and thereby higher strength for the magnesium alloy. However, the lamellar precipitates on a microscopic level tend to shear or cut into the alloy matrix and lead to crack propagation and can offset the beneficial strengthening of the grain refinement if an excessive amount of the Al2Ca phase is formed. The offsetting grain structure effects typically lead to a minimal improvement on tensile strength of the magnesium-aluminum-calcium alloy, if any. This seems to lead to no significant reduction in tensile strength of the alloy. The significant advantage for the addition of calcium in a magnesium-aluminum alloy is in the improved incipient melting temperature when the Al2Ca phase is formed as opposed to Mg17Al12. Al2Ca has a melting temperature of approximately 1080° C. as opposed to 460° C. for the magnesium-aluminum phase, which means a higher incipient melting point for the alloy. This solution leads to a larger hot deformation processing window or, more specifically, greater speeds during extrusion or rolling. These greater speeds can lead to lower cost production and a safer overall product. Another benefit of the calcium addition into the alloy is reduced oxidation of the melt. This feature is a result of the CaO layer which forms on the surface of the melt. In melt protection, the thickness and density of the calcium layer benefits the melt through formation of a reinforced CaO—MgO oxide layer when no other elements are present. This layer reduces the potential for “burning” in the foundry, thus allows for higher casting temperatures, reduced cover gas, reduced flux use and improved safety and throughput. The oxide layer also significantly increases the ignition temperature by eliminating the magnesium oxide layer typically found on the surface and replacing it with the much more stable CaO. The calcium addition in the magnesium alloy is generally at least 0.05 wt. % and generally up to about 30 wt. % (and all values and ranges therebetween), and typically 0.1-15 wt. %.
The developed alloys can be degraded in solutions with salt contents as low as 0.01% at a rate of 1-100 mg/cm2-hr. (and all values and ranges therebetween) at a temperature of 20-100° C. (and all values and ranges therebetween). The calcium additions work to enhance degradation in this alloy system, not by traditional means of adding a higher standard electrode potential material as would be common practice, but by actually reducing the corrosion inhibiting phase of Mg17Al12 by the precipitation of Al2Ca phases that are mechanically just as strong, but do not inhibit the corrosion. As such, alloys can be created with higher corrosion rates just as alloys can be created by reducing aluminum content, but without strength degradation and the added benefit of higher use temperature, higher incipient melting temperatures and/or lower flammability. The alloy is a candidate for use in all degradation applications such as downhole tools, temporary structures, etc. where strength and high use temperature are a necessity and it is desirable to have a greater rate of dissolving or degradation rates in low-salt concentration solutions.
In yet another and/or alternative non-limiting aspect of the invention, there is provided a method for improving the physical properties of the magnesium composite wherein the total content of magnesium in the magnesium or magnesium alloy is at least about 85 wt. % and copper is added to form in situ precipitation in the magnesium or magnesium composite and solutionizing the resultant metal at a temperature of about 100-500° C. for a period of 0.25-50 hours. The magnesium composite is characterized by higher tensile and yield strengths than magnesium-based alloys of the same composition, but not including the amount of copper.
In still yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite for use as a dissolvable ball or frac ball in hydraulic fracturing and well drilling.
In another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite for use as a dissolvable tool for use in well drilling and hydraulic control as well as hydraulic fracturing.
In another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that has controlled dissolution or degradation for use in temporarily isolating a wellbore.
In another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that can be used to partially or full form a mandrel, slip, grip, ball, frac ball, dart, sleeve, carrier, or other downhole well component.
In another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that can be used for controlling fluid flow or mechanical activation of a downhole device.
In still another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that includes secondary in situ formed reinforcements that are not galvanically active to the magnesium or magnesium alloy matrix to increase the mechanical properties of the magnesium composite. The secondary in situ formed reinforcements can optionally include a Mg2Si phase as the in situ formed reinforcement.
In yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is subjected to a greater rate of cooling from the liquidus to the solidus point to create smaller in situ formed particles.
In still yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is subjected to a slower rate of cooling from the liquidus to the solidus point to create larger in situ formed particles.
In yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is subjected to heat treatments such as solutionizing, aging and/or cold working to be used to control dissolution rates though precipitation of more or less galvanically-active phases within the alloy microstructure while improving mechanical properties. The artificial aging process (when used) can be for at least about 1 hour, for about 1-50 hours, for about 1-20 hours, or for about 8-20 hours. The solutionizing (when used) can be for at least about 1 hour, for about 1-50 hours, for about 1-20 hours, or for about 8-20 hours.
In still yet another and/or alternative non-limiting aspect of the invention, there is provided a method for controlling the dissolution rate of the magnesium composite wherein the magnesium content is at least about 75 wt. % and at least 0.05 wt. % nickel is added to form in situ precipitation in the magnesium or magnesium alloy and solutionizing the resultant metal at a temperature within a range of 100-500° C. for a period of 0.25-50 hours, the magnesium composite being characterized by higher dissolution rates than metal without nickel additions subjected to the said artificial aging process.
In another and/or alternative non-limiting aspect of the invention, there is provided a method for improving the physical properties of the magnesium composite wherein the magnesium content is at least about 85 wt. % and at least 0.05 wt. % nickel is added to form in situ precipitation in the magnesium or magnesium alloy and solutionizing the resultant metal at a temperature at about 100-500° C. for a period of 0.25-50 hours, the magnesium composite being characterized by higher tensile and yield strengths than magnesium base alloys of the same composition, but not including the amount of nickel.
In still another and/or alternative non-limiting aspect of the invention, there is provided a method for controlling the dissolution rate of the magnesium composite wherein the magnesium content in the alloy is at least about 75 wt. % and at least 0.05 wt. % copper is added to form in situ precipitation in the magnesium or magnesium alloy and solutionizing the resultant metal at a temperature within a range of 100-500° C. for a period of 0.25-50 hours, the magnesium composite being characterized by higher dissolution rates than metal without copper additions subjected to the said artificial aging process.
In yet another and/or alternative non-limiting aspect of the invention, there is provided a method for improving the physical properties of the magnesium composite wherein the total content of magnesium in the magnesium or magnesium alloy is at least about 85 wt. % and at least 0.05 wt. % copper is added to form in situ precipitation in the magnesium or magnesium composite and solutionizing the resultant metal at a temperature of about 100-500° C. for a period of 0.25-50 hours, the magnesium composite being characterized by higher tensile and yield strengths than magnesium base alloys of the same composition, but not including the amount of copper.
In still another and/or alternative non-limiting aspect of the invention, the additive generally has a solubility in the molten magnesium or magnesium alloy of less than about 10% (e.g., 0.01-9.99% and all values and ranges therebetween), typically less than about 5%, more typically less than about 1%, and even more typically less than about 0.5%.
In still another and/or alternative non-limiting aspect of the invention, the additive can optionally have a surface area of 0.001-200 m2/g (and all values and ranges therebetween). The additive in the magnesium composite can optionally be less than about 1 μm in size (e.g., 0.001-0.999 μm and all values and ranges therebetween), typically less than about 0.5 μm, more typically less than about 0.1 μm, and more typically less than about 0.05 μm. The additive can optionally be dispersed throughout the molten magnesium or magnesium alloy using ultrasonic means, electrowetting of the insoluble particles, and/or mechanical agitation. In one non-limiting embodiment, the molten magnesium or magnesium alloy is subjected to ultrasonic vibration and/or waves to facilitate in the dispersion of the additive in the molten magnesium or magnesium alloy.
In still yet another and/or alternative non-limiting aspect of the invention, a plurality of additives in the magnesium composite are located in grain boundary layers of the magnesium composite.
In still yet another and/or alternative non-limiting aspect of the invention, there is provided a method for forming a magnesium composite that includes a) providing magnesium or a magnesium alloy, b) providing one or more additives that have a low solubility when added to magnesium or a magnesium alloy when in a molten state; c) mixing the magnesium or a magnesium alloy and the one or more additives to form a mixture and to cause the one or more additives to disperse in the mixture; and d) cooling the mixture to form the magnesium composite. The step of mixing optionally includes mixing using one or more processes selected from the group consisting of thixomolding, stir casting, mechanical agitation, electrowetting and ultrasonic dispersion. The method optionally includes the step of heat treating the magnesium composite to improve the tensile strength, elongation, or combinations thereof of the magnesium composite without significantly affecting a dissolution rate of the magnesium composite. The method optionally includes the step of extruding or deforming the magnesium composite to improve the tensile strength, elongation, or combinations thereof of the magnesium composite without significantly affecting a dissolution rate of the magnesium composite. The method optionally includes the step of forming the magnesium composite into a device that a) facilitates in separating hydraulic fracturing systems and zones for oil and gas drilling, b) provides structural support or component isolation in oil and gas drilling and completion systems, or c) is in the form of a frac ball, valve, or degradable component of a well composition tool or other tool. Other types of structures that the magnesium composite can be partially or fully formed into include, but are not limited to, sleeves, valves, hydraulic actuating tooling and the like. Such non-limiting structures or additional non-limiting structure are illustrated in U.S. Pat. Nos. 8,905,147; 8,717,268; 8,663,401; 8,631,876; 8,573,295; 8,528,633; 8,485,265; 8,403,037; 8,413,727; 8,211,331; 7,647,964; US Publication Nos. 2013/0199800; 2013/0032357; 2013/0029886; 2007/0181224; and WO 2013/122712, all of which are incorporated herein by reference.
In still yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite for use as a dissolvable ball or frac ball in hydraulic fracturing and well drilling.
In another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite for use as a dissolvable tool for use in well drilling and hydraulic control as well as hydraulic fracturing.
In still another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that includes secondary in situ formed reinforcements that are not galvanically active to the magnesium or magnesium alloy matrix to increase the mechanical properties of the magnesium composite. The secondary in situ formed reinforcements include a Mg2Si phase or silicon particle phase as the in situ formed reinforcement.
In yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is subjected to a greater rate of cooling from the liquidus to the solidus point to create smaller in situ formed particles.
In still yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is subjected to a slower cooling rate from the liquidus to the solidus point to create larger in situ formed particles.
In yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is subjected to heat treatments such as solutionizing, aging and/or cold working to be used to control dissolution rates through precipitation of more or less galvanically-active phases within the alloy microstructure while improving mechanical properties. The artificial aging process (when used) can be for at least about 1 hour, for about 1-50 hours (and all values and ranges therebetween), for about 1-20 hours, or for about 8-20 hours. Solutionizing (when used) can be for at least about 1 hour, for about 1-50 hours (and all values and ranges therebetween), for about 1-20 hours, or for about 8-20 hours.
In another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is subjected to mechanical agitation during the cooling rate from the liquidus to the solidus point to create smaller in situ formed particles.
In still another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is subjected to chemical agitation during the cooling rate from the liquidus to the solidus point to create smaller in situ formed particles.
In yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is subjected to ultrasonic agitation during the cooling rate from the liquidus to the solidus point to create smaller in situ formed particles.
In still yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that is subjected to deformation or extrusion to further improve dispersion of the in situ formed particles.
In still yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that has a dissolve rate or dissolution rate of at least about 30 mg/cm2-hr in 3% KCl solution at 90° C., and typically 30-500 mg/cm2-hr in 3% KCl solution at 90° C. (and all values and ranges therebetween).
In still yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that has a dissolve rate or dissolution rate of at least about 0.2 mg/cm2-min in a 3% KCl solution at 90° C., and typically 0.2-150 mg/cm2-min in a 3% KCl solution at 90° C. (and all values and ranges therebetween).
In still yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that has a dissolve rate or dissolution rate of at least about 0.1 mg/cm2-hr in a 3% KCl solution at 21° C., and typically 0.1-5 mg/cm2-hr in a 3% KCl solution at 21° C. (and all values and ranges therebetween).
In still yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that has a dissolve rate or dissolution rate of at least about 0.2 mg/cm in a 3% KCl solution at 20° C.
In still yet another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that has a dissolve rate or dissolution rate of at least about 0.1 mg/cm2-hr in 3% KCl solution at 20° C., typically 0.1-5 mg/cm2-hr in a 3% KCl solution at 20° C. (and all values and ranges therebetween).
In another and/or alternative non-limiting aspect of the invention, there is provided a method for forming a novel magnesium composite including the steps of a) selecting an AZ91D magnesium alloy having 9 wt. % aluminum, 1 wt. % zinc and 90 wt. % magnesium, b) melting the AZ91 D magnesium alloy to a temperature above 800° C., c) adding up to about 7 wt. % nickel to the melted AZ91D magnesium alloy at a temperature that is less than the melting point of nickel, d) mixing the nickel with the melted AZ91D magnesium alloy and dispersing the nickel in the melted alloy using chemical mixing agents while maintaining the temperature below the melting point of nickel, and e) cooling and casting the melted mixture in a steel mold. The cast material has a tensile strength of about 14 ksi, and an elongation of about 3% and a shear strength of 11 ksi. The cast material has a dissolve rate of about 75 mg/cm2-min in a 3% KCl solution at 90° C. The cast material dissolves at a rate of 1 mg/cm2-hr in a 3% KCl solution at 21° C. The cast material dissolves at a rate of 325 mg/cm2-hr. in a 3% KCl solution at 90° C. The cast material can be subjected to extrusion with an 11:1 reduction area. The extruded cast material exhibits a tensile strength of 40 ksi, and an elongation to failure of 12%. The extruded cast material dissolves at a rate of 0.8 mg/cm2-min in a 3% KCl solution at 20° C. The extruded cast material dissolves at a rate of 100 mg/cm2-hr. in a 3% KCl solution at 90° C. The extruded cast material can be subjected to an artificial T5 age treatment of 16 hours between 100-200° C. The aged and extruded cast material exhibits a tensile strength of 48 ksi, an elongation to failure of 5%, and a shear strength of 25 ksi. The aged extruded cast material dissolves at a rate of 110 mg/cm2-hr in 3% KCl solution at 90° C. and 1 mg/cm2-hr in 3% KCl solution at 20° C. The cast material can be subjected to a solutionizing treatment T4 for about 18 hours between 400-500° C. and then subjected to an artificial T6 age treatment for about 16 hours between 100-200° C. The aged and solutionized cast material exhibits a tensile strength of about 34 ksi, an elongation to failure of about 11%, and a shear strength of about 18 ksi. The aged and solutionized cast material dissolves at a rate of about 84 mg/cm2-hr in 3% KCl solution at 90° C., and about 0.8 mg/cm2-hr in 3% KCl solution at 20° C.
In another and/or alternative non-limiting aspect of the invention, there is provided a method for forming a novel magnesium composite including the steps of a) selecting an AZ91D magnesium alloy having 9 wt. % aluminum, 1 wt. % zinc and 90 wt. % magnesium, b) melting the AZ91D magnesium alloy to a temperature above 800° C., c) adding up to about 1 wt. % nickel to the melted AZ91D magnesium alloy at a temperature that is less than the melting point of nickel, d) mixing the nickel with the melted AZ91ID magnesium alloy and dispersing the nickel in the melted alloy using chemical mixing agents while maintaining the temperature below the melting point of nickel, and e) cooling and casting the melted mixture in a steel mold. The cast material has a tensile strength of about 18 ksi, and an elongation of about 5% and a shear strength of 17 ksi. The cast material has a dissolve rate of about 45 mg/cm2-min in a 3% KCl solution at 90° C. The cast material dissolves at a rate of 0.5 mg/cm2-hr. in a 3% KCl solution at 21° C. The cast material dissolves at a rate of 325 mg/cm2-hr. in a 3% KCl solution at 90° C. The cast material is subjected to extrusion with a 20:1 reduction area. The extruded cast material exhibits a tensile yield strength of 35 ksi, and an elongation to failure of 12%. The extruded cast material dissolves at a rate of 0.8 mg/cm2-min in a 3% KCl solution at 20° C. The extruded cast material dissolves at a rate of 50 mg/cm2-hr in a 3% KCl solution at 90° C. The extruded cast material can be subjected to an artificial T5 age treatment of 16 hours between 100-200° C. The aged and extruded cast material exhibits a tensile strength of 48 ksi, an elongation to failure of 5%, and a shear strength of 25 ksi.
In still another and/or alternative non-limiting aspect of the invention, there is provided a method for forming a novel magnesium composite including the steps of a) selecting an AZ9ID magnesium alloy having about 9 wt. % aluminum, 1 wt. % zinc and 90 wt. % magnesium, b) melting the AZ9ID magnesium alloy to a temperature above 800° C., c) adding about 10 wt. % copper to the melted AZ9ID magnesium alloy at a temperature that is less than the melting point of copper, d) dispersing the copper in the melted AZ9ID magnesium alloy using chemical mixing agents at a temperature that is less than the melting point of copper, and e) cooling casting the melted mixture in a steel mold. The cast material exhibits a tensile strength of about 14 ksi, an elongation of about 3%, and shear strength of 11 ksi. The cast material dissolves at a rate of about 50 mg/cm2-hr. in a 3% KCl solution at 90° C. The cast material dissolves at a rate of 0.6 mg/cm2-hr. in a 3% KCl solution at 21° C. The cast material can be subjected to an artificial T5 age treatment for about 16 hours at a temperature of 100-200° C. The aged cast material exhibits a tensile strength of 50 ksi, an elongation to failure of 5%, and a shear strength of 25 ksi. The aged cast material dissolved at a rate of 40 mg/cm2-hr in 3% KCl solution at 90° C. and 0.5 mg/cm2-hr in 3% KCl solution at 20° C.
In still another and/or alternative non-limiting aspect of the invention, there is provided a method for forming a novel magnesium composite including the steps of a) providing magnesium having a purity of at least 99.9%, b) providing antimony having a purity of at least 99.8%, c) adding the magnesium and antimony in the crucible (e.g., carbon steel crucible), d) optionally adding a flux to the top of the metals in the crucible, e) optionally heating the metals in the crucible to 250° C. for about 2-60 minutes, heating the metals in the crucible to 650-720° C. to cause the magnesium to melt, and g) cooling the molten magnesium to form a magnesium composite that includes about 7 wt. % antimony. The density of the magnesium composite is 1.69 g/cm3, the hardness is 6.8 Rockwell Hardness B, and the dissolution rate in 3% solution of KCl at 90° C. is 20.09 mg/cm2-hr.
In still another and/or alternative non-limiting aspect of the invention, there is provided a method for forming a novel magnesium composite including the steps of a) providing magnesium having a purity of at least 99.9%, b) providing gallium having a purity of at least 99.9%, c) adding the magnesium and gallium in the crucible (e.g., carbon steel crucible), d) optionally adding a flux to the top of the metals in the crucible, e) optionally heating the metals in the crucible to 250° C. for about 2-60 minutes, f) heating the metals in the crucible to 650-720° C. to cause the magnesium to melt, and g) cooling the molten magnesium to form a magnesium composite that includes about 5 wt. % gallium. The density of the magnesium composite is 1.80 g/cm3, the hardness is 67.8 Rockwell Hardness B, and the dissolution rate in 3% solution of KCl at 90° C. is 0.93 mg/cm2-hr.
In still another and/or alternative non-limiting aspect of the invention, there is provided a method for forming a novel magnesium composite including the steps of a) providing magnesium having a purity of at least 99.9%, b) providing tin having a purity of at least 99.9%, c) adding the magnesium and tin in the crucible (e.g., carbon steel crucible), d) optionally adding a flux to the top of the metals in the crucible, e) optionally heating the metals in the crucible to 250° C. for about 2-60 minutes, heating the metals in the crucible to 650-720° C. to cause the magnesium to melt, and g) cooling the molten magnesium to form a magnesium composite that includes about 13 wt. % tin. The density of the magnesium composite is 1.94 g/cm3, the hardness is 75.6 Rockwell Hardness B, and the dissolution rate in 3% solution of KCl at 90° C. is 0.02 mg/cm2-hr.
In still another and/or alternative non-limiting aspect of the invention, there is provided a method for forming a novel magnesium composite including the steps of a) providing magnesium having a purity of at least 99.9%, b) providing bismuth having a purity of at least 99.9%, c) adding the magnesium and bismuth in the crucible (e.g., carbon steel crucible), d) optionally adding a flux to the top of the metals in the crucible, e) optionally heating the metals in the crucible to 250° C. for about 2-60 minutes, f) heating the metals in the crucible to 650-720° C. to cause the magnesium to melt, and g) cooling the molten magnesium to form a magnesium composite that includes about 10 wt. % bismuth. The density of the magnesium composite is 1.86 g/cm3, the hardness is 16.9 Rockwell Hardness B, and the dissolution rate in 3% solution of KCl at 90° C. is 26.51 mg/cm2-hr.
In still another and/or alternative non-limiting aspect of the invention, there is provided a method for controlling the dissolution properties of a magnesium or a magnesium alloy comprising of the steps of: a) heating the magnesium or a magnesium alloy to a point above its solidus temperature; b) adding an additive to said magnesium or magnesium alloy while said magnesium or magnesium alloy is above said solidus temperature of magnesium or magnesium alloy to form a mixture, said additive including one or more first additives having an electronegativity of greater than 1.5, said additive constituting about 0.05-45 wt. % of said mixture; c) dispersing said additive in said mixture while said magnesium or magnesium alloy is above said solidus temperature of magnesium or magnesium alloy; and, d) cooling said mixture to form a magnesium composite, said magnesium composite including in situ precipitation of galvanically-active intermetallic phases. The first additive can optionally have an electronegativity of greater than 1.8. The step of controlling a size of said in situ precipitated intermetallic phase can optionally be by controlled selection of a mixing technique during said dispersion step, controlling a cooling rate of said mixture, or combinations thereof. The magnesium or magnesium alloy can optionally be heated to a temperature that is less than said melting point temperature of at least one of said additives. The magnesium or magnesium alloy can be heated to a temperature that is greater than said melting point temperature of at least one of said additives. The additive can optionally include one or more metals selected from the group consisting of calcium, copper, nickel, cobalt, bismuth, silver, gold, lead, tin, antimony, indium, arsenic, mercury, and gallium. The additive can optionally include one or more metals selected from the group consisting of calcium, copper, nickel, cobalt, bismuth, tin, antimony, indium, and gallium. The additive can optionally include one or more second additives that have an electronegativity of less than 1.25. The second additive can optionally include one or more metals selected from the group consisting of strontium, barium, potassium, sodium, lithium, cesium, and the rare earth metals such as yttrium, lanthanum, samarium, europium, gadolinium, terbium, dysprosium, holmium, and ytterbium. The additive can optionally be formed of a single composition, and has an average particle diameter size of about 0.1-500 microns. At least a portion of said additive can optionally remain at least partially in solution in an α-magnesium phase of said magnesium composite. The magnesium alloy can optionally include over 50 wt. % magnesium and one or more metals selected from the group consisting of aluminum, boron, bismuth, zinc, zirconium, and manganese. The magnesium alloy can optionally include over 50 wt. % magnesium and one or more metals selected from the group consisting of aluminum in an amount of about 0.5-10 wt. %, zinc in amount of about 0.1-6 wt. %, zirconium in an amount of about 0.01-3 wt. %, manganese in an amount of about 0.15-2 wt. %; boron in amount of about 0.0002-0.04 wt. %, and bismuth in amount of about 0.4-0.7 wt. %. The magnesium alloy can optionally include over 50 wt. % magnesium and one or more metals selected from the group consisting of aluminum in an amount of about 0.5-10 wt. %, zinc in amount of about 0.1-3 wt. %, zirconium in an amount of about 0.01-1 wt. %, manganese in an amount of about 0.15-2 wt. %; boron in amount of about 0.0002-0.04 wt. %, and bismuth in amount of about 0.4-0.7 wt %. The step of solutionizing said magnesium composite can optionally occur at a temperature above 300° C. and below a melting temperature of said magnesium composite to improve tensile strength, ductility, or combinations thereof of said magnesium composite. The step of forming said magnesium composite into a final shape or near net shape can optionally be by a) sand casting, permanent mold casting, investment casting, shell molding, or other pressureless casting technique at a temperature above 730° C., 2) using either pressure addition or elevated pouring temperatures above 710° C., or 3) subjecting the magnesium composite to pressures of 2000-20,000 psi through the use of squeeze casting, thixomolding, or high pressure die casting techniques. The step of aging said magnesium composite can optionally be at a temperature of above 100° C. and below 300° C. to improve tensile strength of said magnesium composite. The magnesium composite can optionally have a hardness above 14 Rockwell Harness B. The magnesium composite can optionally have a dissolution rate of at least 5 mg/cm2-hr. in 3% KCl at 90° C. The additive metal can optionally include about 0.05-35 wt. % nickel. The additive can optionally include about 0.05-35 wt. % copper. The additive can optionally include about 0.05-35 wt. % antimony. The additive can optionally include about 0.05-35 wt. % gallium. The additive can optionally include about 0.05-35 wt. % tin. The additive can optionally include about 0.05-35 wt. % bismuth. The additive can optionally include about 0.05-35 wt. % calcium. The method can optionally further include the step of rapidly solidifying said magnesium composite by atomizing the molten mixture and then subjecting the atomized molten mixture to ribbon casting, gas and water atomization, pouring into a liquid, high speed machining, saw cutting, or grinding into chips, followed by powder or chip consolidation below its liquidus temperature.
In still another and/or alternative non-limiting aspect of the invention, there is provided a magnesium composite that includes in situ precipitation of galvanically-active intermetallic phases comprising a magnesium or a magnesium alloy and an additive constituting about 0.05-45 wt. % of said magnesium composite, said magnesium having a content in said magnesium composite that is greater than 50 wt. %, said additive forming metal composite particles or precipitant in said magnesium composite, said metal composite particles or precipitant forming said in situ precipitation of said galvanically-active intermetallic phases, said additive including one or more first additives having an electronegativity of greater than 1.5. The magnesium composite can optionally further include one or more second additives having an electronegativity of less than 1.25. The first additive can optionally have an electronegativity of greater than 1.8. The first additive can optionally include one or more metals selected from the group consisting of copper, nickel, cobalt, bismuth, silver, gold, lead, tin, antimony, indium, arsenic, mercury, and gallium. The first additive can optionally include one or more metals selected from the group consisting of copper, nickel, cobalt, bismuth, tin, antimony, indium, and gallium. The second additive can optionally include one or more metals selected from the group consisting of calcium, strontium, barium, potassium, sodium, lithium, cesium, and the rare earth metals such as yttrium, lanthanum, samarium, europium, gadolinium, terbium, dysprosium, holmium, and ytterbium. The magnesium alloy can optionally include over 50 wt. % magnesium and one or more metals selected from the group consisting of aluminum, boron, bismuth, zinc, zirconium, and manganese. The magnesium alloy can optionally include over 50 wt. % magnesium and one or more metals selected from the group consisting of aluminum in an amount of about 0.5-10 wt. %, zinc in amount of about 0.1-3 wt. %, zirconium in an amount of about 0.01-1 wt. %, manganese in an amount of about 0.15-2 wt. %, boron in amount of about 0.0002-0.04 wt. %, and bismuth in amount of about 0.4-0.7 wt. %. The additive can optionally include about 0.05-45 wt. % nickel. The first additive can optionally include about 0.05-45 wt. % copper. The first additive can optionally include about 0.05-45 wt. % cobalt. The first additive can optionally include about 0.05-45 wt. % antimony. The first additive can optionally include about 0.05-45 wt. % gallium. The first additive can optionally include about 0.05-45 wt. % tin. The first additive can optionally include about 0.05-45 wt. % bismuth. The second additive can optionally include 0.05-35 wt. % calcium. The magnesium composite can optionally have a hardness above 14 Rockwell Harness B. The magnesium composite can optionally have a dissolution rate of at least 5 mg/cm2-hr. in 3% KCl at 90° C. The magnesium composite can optionally have a dissolution rate of about 5-300 mg/cm2-hr in 3 wt. % KCl water mixture at 90° C. The magnesium composite can optionally be subjected to a surface treatment to improve a surface hardness of said magnesium composite, said surface treatment including peening, heat treatment, aluminizing, or combinations thereof. A dissolution rate of said magnesium composite can optionally be controlled by an amount and size of said in situ formed galvanically-active particles whereby smaller average sized particles of said in situ formed galvanically-active particles, a greater weight percent of said in situ formed galvanically-active particles in said magnesium composite, or combinations thereof increases said dissolution rate of said magnesium composite.
In still another and/or alternative non-limiting aspect of the invention, there is provided a dissolvable component for use in downhole operations that is fully or partially formed of a magnesium composite, said dissolvable component including a component selected from the group consisting of sleeve, frac ball, hydraulic actuating tooling, mandrel, slip, grip, ball, dart, carrier, tube, valve, valve component, plug, or other downhole well component, said magnesium composite includes in situ precipitation of galvanically-active intermetallic phases comprising a magnesium or a magnesium alloy and an additive constituting about 0.05-45 wt. % of said magnesium composite, said magnesium having a content in said magnesium composite that is greater than 50 wt. %, said additive forming metal composite particles or precipitant in said magnesium composite, said metal composite particles or precipitant forming said in situ precipitation of said galvanically-active intermetallic phases, said additive including one or more first additives having an electronegativity of greater than 1.5. The dissolvable component can optionally further include one or more second additives having an electronegativity of less than 1.25. The first additive can optionally have an electronegativity of greater than 1.8. The first additive can optionally include one or more metals selected from the group consisting of copper, nickel, cobalt, bismuth, silver, gold, lead, tin, antimony, indium, arsenic, mercury, and gallium. The first additive can optionally include one or more metals selected from the group consisting of copper, nickel, cobalt, bismuth, tin, antimony, indium, and gallium. The second additive can optionally include one or more metals selected from the group consisting of calcium, strontium, barium, potassium, sodium, lithium, cesium, and the rare earth metals such as yttrium, lanthanum, samarium, europium, gadolinium, terbium, dysprosium, holmium, and ytterbium. The second additive can optionally include 0.05-35 wt. % calcium. The magnesium alloy can optionally include over 50 wt. % magnesium and one or more metals selected from the group consisting of aluminum, boron, bismuth, zinc, zirconium, and manganese. The magnesium composite can optionally have a hardness above 14 Rockwell Harness B. The magnesium composite can optionally have a dissolution rate of at least 5 mg/cm2-hr. in 3% KCl at 90° C. The magnesium composite can optionally have a dissolution rate of at least 10 mg/cm2-hr in a 3% KCl solution at 90° C. The magnesium composite can optionally have a dissolution rate of at least 20 mg/cm2-hr in a 3% KCl solution at 65° C. The magnesium composite can optionally have a dissolution rate of at least 1 mg/cm2-hr in a 3% KCl solution at 65° C. The magnesium composite can optionally have a dissolution rate of at least 100 mg/cm2-hr in a 3% KCl solution at 90° C. The magnesium composite can optionally have a dissolution rate of at least 45 mg/cm2/hr. in 3 wt. % KCl water mixture at 90° C. and up to 325 mg/cm2/hr. in 3 wt. % KCl water mixture at 90° C. The magnesium composite can optionally have a dissolution rate of up to 1 mg/cm2/hr. in 3 wt. % KCl water mixture at 21° C. The magnesium composite can optionally have a dissolution rate of at least 90 mg/cm2-hr. in 3% KCl solution at 90° C. The magnesium composite can optionally have a dissolution rate of at least a rate of 0.1 mg/cm2-hr. in 0.1% KCl solution at 90° C. The magnesium composite can optionally have a dissolution rate of a rate of <0.1 mg/cm2-hr. in 0.1% KCl solution at 75° C. The magnesium composite can optionally have a dissolution rate of, a rate of <0.1 mg/cm2-hr. in 0.1% KCl solution at 60° C. The magnesium composite can optionally have a dissolution rate of <0.1 mg/cm2-hr. in 0.1% KCl solution at 45° C. The magnesium composite can optionally have a dissolution rate of at least 30 mg/cm2-hr. in 0.1% KCl solution at 90° C. The magnesium composite can optionally have a dissolution rate of at least 20 mg/cm2-hr. in 0.1% KCl solution at 75° C. The magnesium composite can optionally have a dissolution rate of at least 10 mg/cm2-hr. in 0.1% KCl solution at 60° C. The magnesium composite can optionally have a dissolution rate of at least 2 mg/cm2-hr. in 0.1% KCl solution at 45° C. The metal composite particles or precipitant in said magnesium composite can optionally have a solubility in said magnesium of less than 5%. The magnesium alloy can optionally include over 50 wt. % magnesium and one or more metals selected from the group consisting of aluminum, boron, bismuth, zinc, zirconium, and manganese. The magnesium alloy can optionally include over 50 wt. % magnesium and one or more metals selected from the group consisting of aluminum in an amount of about 0.5-10 wt. %, zinc in an amount of about 0.1-6 wt. %, zirconium in an amount of about 0.01-3 wt. %, manganese in an amount of about 0.15-2 wt. %, boron in an amount of about 0.0002-0.04 wt. %, and bismuth in amount of about 0.4-0.7 wt. %. The magnesium alloy can optionally include over 50 wt. % magnesium and one or more metals selected from the group consisting of aluminum in an amount of about 0.5-10 wt. %, zinc in an amount of about 0.1-3 wt. %, zirconium in an amount of about 0.01-1 wt. %, manganese in an amount of about 0.15-2 wt. %, boron in an amount of about 0.0002-0.04 wt. %, and bismuth in an amount of about 0.4-0.7 wt. %. The magnesium alloy can optionally include at least 85 wt. % magnesium and one or more metals selected from the group consisting of 0.5-10 wt. % aluminum, 0.05-6 wt. % zinc, 0.01-3 wt. % zirconium, and 0.15-2 wt. % manganese. The magnesium alloy can optionally include 60-95 wt. % magnesium and 0.01-1 wt. % zirconium. The magnesium alloy can optionally include 60-95 wt. % magnesium, 0.5-10 wt. % aluminum, 0.05-6 wt. % zinc, and 0.15-2 wt. % manganese. The magnesium alloy can optionally include 60-95 wt. % magnesium, 0.05-6 wt. % zinc, and 0.01-1 wt. % zirconium. The magnesium alloy can optionally include over 50 wt. % magnesium and one or more metals selected from the group consisting of 0.5-10 wt. % aluminum, 0.1-2 wt. % zinc, 0.01-1 wt. % zirconium, and 0.15-2 wt. % manganese. The magnesium alloy can optionally include over 50 wt. % magnesium and one or more metals selected from the group consisting of 0.1-3 wt. % zinc, 0.01-1 wt. % zirconium, 0.05-1 wt. % manganese, 0.0002-0.04 wt. % boron, and 0.4-0.7 wt. % bismuth.
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable magnesium alloy including 1-15 wt. % aluminum and a dissolution enhancing intermetallic phase between magnesium and cobalt, nickel, and/or copper with the alloy composition containing 0.05-25 wt. % cobalt, nickel, and/or copper, and 0.1-15 wt. % calcium.
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable magnesium alloy including 1-15 wt. % aluminum and a dissolution enhancing intermetallic phase between magnesium and cobalt, nickel, and/or copper with the alloy composition containing 0.05-25 wt. % cobalt, nickel, and/or copper, and 0.1-15 wt. % of calcium, strontium, barium and/or scandium.
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable magnesium alloy wherein the alloy composition includes 0.5-8 wt. % calcium, 0.05-20 wt. % nickel, 3-11 wt. % aluminum, and 50-95 wt. % magnesium and the alloy degrades at a rate that is greater than 5 mg/cm2-hr. at temperatures below 90° C. in fresh water (water with less than 1000 ppm salt content).
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable magnesium alloy wherein the alloy composition includes 0-2 wt. % zinc, 0.5-8 wt. % calcium, 0.05-20 wt. % nickel, 5-11 wt. % aluminum, and 50-95 wt. % magnesium and the alloy degrades at a rate that is greater than 1 mg/cm2-hr. at temperatures below 45° C. in fresh water (water with less than 1000 ppm salt content).
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable alloy can optionally include calcium, strontium and/or barium addition that forms an aluminum-calcium phase, an aluminum-strontium phase and/or an aluminum-barium phase that leads to an alloy with a higher incipient melting point and increased corrosion rate.
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable alloy can optionally include calcium that creates an aluminum-calcium (e.g., AlCa2 phase) as opposed to a magnesium-aluminum phase (e.g., Mg17Al12 phase) to thereby enhance the speed of degradation of the alloy when exposed to a conductive fluid vs. the common practice of enhancing the speed of degradation of an aluminum-containing alloy by reducing the aluminum content to reduce the amount of Mg17Al12 in the alloy.
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable alloy can optionally include calcium addition that forms an aluminum-calcium phase that increases the ratio of dissolution of intermetallic phase to the base magnesium, and thus increases the dissolution rate of the alloy.
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable alloy can optionally include calcium addition that forms an aluminum-calcium phase reduces the salinity required for the same dissolution rate by over 2× at 90° C. in a saline solution.
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable alloy can optionally include calcium addition that increases the incipient melting temperature of the degradable alloy, thus the alloy can be extruded at higher speeds and thinner walled tubes can be formed as compared to a degradable alloy without calcium additions.
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable alloy wherein the mechanical properties of tensile yield and ultimate strength are optionally not lowered by more than 10% or are enhanced as compared to an alloy without calcium addition.
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable alloy wherein the elevated mechanical properties of yield strength and ultimate strength of the alloy at temperatures above 100° C. are optionally increased by more than 5% due to the calcium addition.
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable alloy wherein the galvanically active phase is optionally present in the form of an LPSO (Long Period Stacking Fault) phase such as Mg12Zn1-xNix RE (where RE is a rare earth element) and that phase is 0.05-5 wt. % of the final alloy composition.
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable alloy wherein the mechanical properties at 150° C. are optionally at least 24 ksi tensile yield strength, and are not less than 20% lower than the mechanical properties at room temperature (77° F.).
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable alloy wherein the dissolution rate at 150° C. in 3% KCl brine is optionally 10-150 mg/cm2/hr.
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable alloy that optionally can include 2-4 wt. % yttrium, 2-5 wt. % gadolinium, 03-4 wt. % nickel, and 0.05-4 wt. % zinc.
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable alloy that can optionally include 0.1-0.8 wt. % manganese and/or zirconium.
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable alloy that can optionally be use in downhole applications such as pressure segmentation, or zonal control.
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable alloy can optionally be used for zonal or pressure isolation in a downhole component or tool.
In still another and/or alternative non-limiting aspect of the invention, there is provided a method for forming a degradable alloy wherein a base dissolution of enhanced magnesium alloy is optionally melted and calcium is added as metallic calcium above the liquids of the magnesium-aluminum phase and the aluminum preferentially forms AlCa2 vs. Mg17Al12 during solidification of the alloy.
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable alloy can optionally be formed by adding calcium is in the form of an oxide or salt that is reduced by the molten melt vs. adding the calcium as a metallic element.
In still another and/or alternative non-limiting aspect of the invention, there is provided a degradable alloy can optionally be formed at double the speed or higher as compared to an alloy that does not include calcium due to the rise in incipient melting temperature.
One non-limiting objective of the present invention is the provision of a castable, moldable, or extrudable magnesium composite formed of magnesium or magnesium alloy and one or more additives dispersed in the magnesium or magnesium alloy.
Another and/or alternative non-limiting objective of the present invention is the provision of selecting the type and quantity of one or more additives so that the grain boundaries of the magnesium composite have a desired composition and/or morphology to achieve a specific galvanic corrosion rate in the entire magnesium composite and/or along the grain boundaries of the magnesium composite.
Still yet another and/or alternative non-limiting objective of the present invention is the provision of forming a magnesium composite wherein the one or more additives can be used to enhance mechanical properties of the magnesium composite, such as ductility and/or tensile strength.
Another and/or alternative non-limiting objective of the present invention is the provision of forming a magnesium composite that can be enhanced by heat treatment as well as deformation processing, such as extrusion, forging, or rolling, to further improve the strength of the final magnesium composite.
Yet another and/or alternative non-limiting objective of the present invention is the provision of forming a magnesium composite that can be can be made into almost any shape.
Another and/or alternative non-limiting objective of the present invention is the provision of dispersing the one or more additives in the molten magnesium or magnesium alloy is at least partially by thixomolding, stir casting, mechanical agitation, electrowetting, ultrasonic dispersion and/or combinations of these processes.
Another and/or alternative non-limiting objective of the present invention is the provision of producing a magnesium composite with at least one insoluble phase that is at least partially formed by the additive or additive material, and wherein the one or more additives have a different galvanic potential from the magnesium or magnesium alloy.
Still yet another and/or alternative non-limiting objective of the present invention is the provision of producing a magnesium composite wherein the rate of corrosion in the magnesium composite can be controlled by the surface area via the particle size and morphology of the one or more additions.
Yet another and/or alternative non-limiting objective of the present invention is the provision of producing a magnesium composite that includes one or more additives that have a solubility in the molten magnesium or magnesium alloy of less than about 10%.
Still yet another and/or alternative non-limiting objective of the present invention, there is provided a magnesium composite that can be used as a dissolvable, degradable and/or reactive structure in oil drilling.
These and other objects, features and advantages of the present invention will become apparent in light of the following detailed description of preferred embodiments thereof, as illustrated in the accompanying drawings.
Referring now to the figures wherein the showings illustrate non-limiting embodiments of the present invention, the present invention is directed to a magnesium composite that includes one or more additives dispersed in the magnesium composite. The magnesium composite of the present invention can be used as a dissolvable, degradable and/or reactive structure in oil drilling. For example, the magnesium composite can be used to form a frac ball or other structure (e.g., sleeves, valves, hydraulic actuating tooling and the like, etc.) in a well drilling or completion operation. Although the magnesium composite has advantageous applications in the drilling or completion operation field of use, it will be appreciated that the magnesium composite can be used in any other field of use wherein it is desirable to form a structure that is controllably dissolvable, degradable and/or reactive.
The present invention is directed to a novel magnesium composite that can be used to form a castable, moldable, or extrudable component. The magnesium composite includes at least 50 wt. % magnesium. Generally, the magnesium composite includes over 50 wt. % magnesium and less than about 99.5 wt. % magnesium and all values and ranges therebetween. One or more additives are added to a magnesium or magnesium alloy to form the novel magnesium composite of the present invention. The one or more additives can be selected and used in quantities so that galvanically-active intermetallic or insoluble precipitates form in the magnesium or magnesium alloy while the magnesium or magnesium alloy is in a molten state and/or during the cooling of the melt; however, this is not required. The one or more additives are added to the molten magnesium or magnesium alloy at a temperature that is typically less than the melting point of the one or more additives; however, this is not required. During the process of mixing the one or more additives in the molten magnesium or magnesium alloy, the one or more additives are not caused to fully melt in the molten magnesium or magnesium alloy; however, this is not required. For additives that partially or fully melt in the molten magnesium or molten magnesium alloy, these additives form alloys with magnesium and/or other additives in the melt, thereby resulting in the precipitation of such formed alloys during the cooling of the molten magnesium or molten magnesium alloy to form the galvanically-active phases in the magnesium composite. After the mixing process is completed, the molten magnesium or magnesium alloy and the one or more additives that are mixed in the molten magnesium or magnesium alloy are cooled to form a solid magnesium component that includes particles in the magnesium composite. Such a formation of particles in the melt is called in situ particle formation as illustrated in
In accordance with the present invention, a novel magnesium composite is produced by casting a magnesium metal or magnesium alloy with at least one component to form a galvanically-active phase with another component in the chemistry that forms a discrete phase that is insoluble at the use temperature of the dissolvable component. The in situ formed particles and phases have a different galvanic potential from the remaining magnesium metal or magnesium alloy. The in situ formed particles or phases are uniformly dispersed through the matrix metal or metal alloy using techniques such as thixomolding, stir casting, mechanical agitation, chemical agitation, electrowetting, ultrasonic dispersion, and/or combinations of these methods. Due to the particles being formed in situ to the melt, such particles generally have excellent wetting to the matrix phase and can be found at grain boundaries or as continuous dendritic phases throughout the component depending on alloy composition and the phase diagram. Because the alloys form galvanic intermetallic particles where the intermetallic phase is insoluble to the matrix at use temperatures, once the material is below the solidus temperature, no further dispersing or size control is necessary in the component. This feature also allows for further grain refinement of the final alloy through traditional deformation processing to increase tensile strength, elongation to failure, and other properties in the alloy system that are not achievable without the use of insoluble particle additions. Because the ratio of in situ formed phases in the material is generally constant and the grain boundary to grain surface area is typically consistent even after deformation processing and heat treatment of the composite, the corrosion rate of such composites remains very similar after mechanical processing.
An AZ91D magnesium alloy having 9 wt. % aluminum, 1 wt. % zinc and 90 wt. % magnesium was melted to above 800° C. and at least 200° C. below the melting point of nickel. About 7 wt. % of nickel was added to the melt and dispersed. The melt was cast into a steel mold. The cast material exhibited a tensile strength of about 14 ksi, an elongation of about 3%, and shear strength of 11 ksi. The cast material dissolved at a rate of about 75 mg/cm2-min in a 3% KCl solution at 90° C. The material dissolved at a rate of 1 mg/cm2-hr in a 3% KCl solution at 21° C. The material dissolved at a rate of 325 mg/cm2-hr. in a 3% KCl solution at 90° C.
The composite in Example 1 was subjected to extrusion with an 11:1 reduction area. The material exhibited a tensile yield strength of 45 ksi, an Ultimate tensile strength of 50 ksi and an elongation to failure of 8%. The material has a dissolve rate of 0.8 mg/cm2-min. in a 3% KCl solution at 20° C. The material dissolved at a rate of 100 mg/cm2-hr. in a 3% KCl solution at 90° C.
The alloy in Example 2 was subjected to an artificial T5 age treatment of 16 hours from 100-200° C. The alloy exhibited a tensile strength of 48 ksi and elongation to failure of 5% and a shear strength of 25 ksi. The material dissolved at a rate of 110 mg/cm2-hr. in 3% KCl solution at 90° C. and 1 mg/cm2-hr. in 3% KCl solution at 20° C.
The alloy in Example 1 was subjected to a solutionizing treatment T4 of 18 hours from 400° C.-500° C. and then an artificial T6 aging process of 16 hours from 100-200 C. The alloy exhibited a tensile strength of 34 ksi and elongation to failure of 11% and a shear strength of 18 Ksi. The material dissolved at a rate of 84 mg/cm2-hr. in 3% KCl solution at 90° C. and 0.8 mg/cm2-hr. in 3% KCl solution at 20° C.
An AZ91D magnesium alloy having 9 wt. % aluminum, 1 wt. % zinc, and 90 wt. % magnesium was melted to above 800° C. and at least 200° C. below the melting point of copper. About 10 wt. % of copper alloyed to the melt and dispersed. The melt was cast into a steel mold. The cast material exhibited a tensile yield strength of about 14 ksi, an elongation of about 3%, and shear strength of 11 ksi. The cast material dissolved at a rate of about 50 mg/cm2-hr. in a 3% KCl solution at 90° C. The material dissolved at a rate of 0.6 mg/cm2-hr. in a 3% KCl solution at 21° C.
The alloy in Example 5 was subjected to an artificial T5 aging process of 16 hours from 100-200° C. The alloy exhibited a tensile strength of 50 ksi and elongation to failure of 5% and a shear strength of 25 ksi. The material dissolved at a rate of 40 mg/cm′-hr. in 3% KCl solution at 90° C. and 0.5 mg/cm2-hr. in 3% KCl solution at 20° C.
An AZ91D magnesium alloy having 9 wt. % aluminum, 1 wt. % zinc, and 90 wt. % magnesium was melted to above 700° C. About 16 wt. % of 75 μm iron particles were added to the melt and dispersed. The melt was cast into a steel mold. The cast material exhibited a tensile strength of about 26 ksi, and an elongation of about 3%. The cast material dissolved at a rate of about 2.5 mg/cm2-min in a 3% KCl solution at 20° C. The material dissolved at a rate of 60 mg/cm2-hr in a 3% KCl solution at 65° C. The material dissolved at a rate of 325 mg/cm2-hr. in a 3% KCl solution at 90° C.
An AZ91D magnesium alloy having 9 wt. % aluminum, 1 wt. % zinc, and 90 wt. % magnesium was melted to above 700° C. About 2 wt. % 75 μm iron particles were added to the melt and dispersed. The melt was cast into steel molds. The material exhibited a tensile strength of 26 ksi, and an elongation of 4%. The material dissolved at a rate of 0.2 mg/cm2-min in a 3% KCl solution at 20° C. The material dissolved at a rate of 1 mg/cm2-hr in a 3% KCl solution at 65° C. The material dissolved at a rate of 10 mg/cm2-hr in a 3% KCl solution at 90° C.
An AZ91D magnesium alloy having 9 wt. % aluminum, 1 wt. % zinc, and 90 wt. % magnesium was melted to above 700° C. About 2 wt. % nano iron particles and about 2 wt. % nano graphite particles were added to the composite using ultrasonic mixing. The melt was cast into steel molds. The material dissolved at a rate of 2 mg/cm2-min in a 3% KCl solution at 20° C. The material dissolved at a rate of 20 mg/cm2-hr in a 3% KCl solution at 65° C. The material dissolved at a rate of 100 mg/cm2-hr in a 3%© KCl solution at 90° C.
The composite in Example 7 was subjected to extrusion with an 11:1 reduction area. The extruded metal cast structure exhibited a tensile strength of 38 ksi, and an elongation to failure of 12%. The extruded metal cast structure dissolved at a rate of 2 mg/cm2-min in a 3%© KCl solution at 20° C. The extruded metal cast structure dissolved at a rate of 301 mg/cm2-min in a 3% KCl solution at 90° C. The extruded metal cast structure exhibited an improvement of 58% tensile strength and an improvement of 166% elongation with less than 10% change in dissolution rate as compared to the non-extruded metal cast structure.
Pure magnesium was melted to above 650° C. and below 750° C. About 7 wt. % of antimony was dispersed in the molten magnesium. The melt was cast into a steel mold. The cast material dissolved at a rate of about 20.09 mg/cm2-hr in a 3% KCl solution at 90° C.
Pure magnesium was melted to above 650° C. and below 750° C. About 5 wt % of gallium was dispersed in the molten magnesium. The melt was cast into a steel mold. The cast material dissolved at a rate of about 0.93 mg/cm2-hr in a 3% KCl solution at 90° C.
Pure magnesium was melted to above 650° C. and below 750° C. About 13 wt. % of tin was dispersed in the molten magnesium. The melt was cast into a steel mold. The cast material dissolved at a rate of about 0.02 mg/cm2-hr in a 3% KCl solution at 90° C.
A magnesium alloy that included 9 wt. % aluminum, 0.7 wt. % zinc, 0.3 wt. % nickel, 0.2 wt. % manganese, and the balance magnesium was heated to 157° C. (315° F.) under an SF6—CO2 cover gas blend to provide a protective dry atmosphere for the magnesium alloy. The magnesium alloy was then heated to 730° C. to melt the magnesium alloy and calcium was then added into the molten magnesium alloy in an amount that the calcium constituted 2 wt. % of the mixture. The mixture of molten magnesium alloy and calcium was agitated to adequately disperse the calcium within the molten magnesium alloy. The mixture was then poured into a preheated and protective gas-filled steel mold and naturally cooled to form a cast part that was a 9″×32″ billet. The billet was subsequently preheated to ˜350° C. and extruded into a solid and tubular extrusion profile. The extrusions were run at 12 and 7 inches/minute respectively, which is 2×-3× faster than the maximum speed the same alloy achieved without calcium alloying. It was determined that once the molten mixture was cast into a steel mold, the molten surface of the mixture in the mold did not require an additional cover gas or flux protection during solidification. This can be compared to the same magnesium-aluminum alloy without calcium that requires either an additional cover gas or flux during solidification to prevent burning.
The effect of the calcium on the corrosion rate of a magnesium-aluminum-nickel alloy was determined. Since magnesium already has a high galvanic potential with nickel, the magnesium alloy corrodes rapidly in an electrolytic solution such as a potassium chloride brine. The KCl brine was a 3% solution heated to 90° C. (194° F.). The corrosion rate was compared by submerging 1″×0.6″ samples of the magnesium alloy with and without calcium additions in the solution for 6 hours and the weight loss of the alloy was calculated relative to initial exposed surface area. The magnesium alloy that did not include calcium dissolved at a rate of 48 mg/cm2-hr. in the 3% KCl solution at 90° C. The magnesium alloy that included calcium dissolved at a rate of 91 mg/cm2-hr. in the 3% KCl solution at 90° C. The corrosion rates were also tested in fresh water. The fresh water is water that has up to or less than 1000 ppm salt content. A KCl brine solution was used to compare the corrosion rated of the magnesium alloy with and without calcium additions. 1″×0.6″ samples of the magnesium alloy with and without calcium additions were submerged in the 0.1% KCL brine solution for 6 hours and the weight loss of the alloys were calculated relative to initial exposed surface area. The magnesium alloy that did not include calcium dissolved at a rate of 0.1 mg/cm2-hr. in the 0.1% KCl solution at 90° C., a rate of <0.1 mg/cm2-hr. in the 0.1% KCl solution at 75° C., a rate of <0.1 mg/cm2-hr. in the 0.1% KCl solution at 60° C., and a rate of <0.1 mg/cm2-hr. in the 0.1% KCl solution at 45° C. The magnesium alloy that did include calcium dissolved at a rate of 34 mg/cm2-hr. in the 0.1% KCl solution at 90° C., a rate of 26 mg/cm2-hr. in the 0.1% KCl solution at 75° C., a rate of 14 mg/cm2-hr. in the 0.1% KCl solution at 60° C., and a rate of 5 mg/cm2-hr. in the 0.1% KCl solution at 45° C.
The effect of calcium on magnesium alloy revealed that the microscopic “cutting” effect of the lamellar aluminum-calcium phase slightly decreases the tensile strength at room temperature, but increased tensile strength at elevated temperatures due to the grain refinement effect of Al2Ca. The comparative tensile strength and elongation to failure are shown in Table A.
The effect of varying calcium concentration in a magnesium-aluminum-nickel alloy was tested. The effect on ignition temperature and maximum extrusion speed was also tested. For mechanical properties, the effect of 0-2 wt. % calcium additions to the magnesium alloy on ultimate tensile strength (UTS) and elongation to failure (Ef) is illustrated in Table B.
0%
The effect of calcium additions in the magnesium-aluminum-nickel alloy on ignition temperature was tested and found to be similar to a logarithmic function, with the ignition temperature tapering off. The ignition temperature trend is shown in Table C.
The incipient melting temperature effect on maximum extrusion speeds was also found to trend similarly to the ignition temperature since the melting temperature of the magnesium matrix is limiting. The extrusion speed for a 4″ solid round extrusion from at 9″ round billet trends as shown in Table D.
Pure magnesium is heated to a temperature of 680-720° C. to form a melt under a protective atmosphere of SF6+CO2+air. 1.5-2 wt. % zinc and 1.5-2 wt. % nickel were added using zinc lump and pelletized nickel to form a molten solution. From 3-6 wt. % gadolinium, as well as about 3-6 wt. % yttrium was added as lumps of pure metal, and 0.5-0.8% zirconium was added as a Mg-25% zirconium master alloy to the molten magnesium, which is then stirred to distribute the added metals in the molten magnesium. The melt was then cooled to 680° C., and degassed using HCN and then poured in to a permanent A36 steel mold and solidified. After solidification of the mixture, the billet was solution treated at 500° C. for 4-8 hours and air cooled. The billet was reheated to 360° C. and aged for 12 hours, followed by extrusion at a 5:1 reduction ratio to form a rod.
It is known that LPSO phases in magnesium can add high temperature mechanical properties as well as significantly increase the tensile properties of magnesium alloys at all temperatures. The Mg12Zn1-xNix RE1 LPSO (long period stacking order) phase enables the magnesium alloy to be both high strength and high temperature capable, as well as to be able to be controllably dissolved using the phase as an in situ galvanic phase for use in activities where enhanced and controllable use of degradation is desired. Such activities include use in oil and gas wells as temporary pressure diverters, balls, and other tools that utilize dissolvable metals.
The magnesium alloy was solution treated at 500° C. for 12 hours and air-cooled to allow precipitation of the 14H LPSO phase incorporating both zinc and nickel as the transition metal in the layered structure. The solution-treated alloy was then preheated at 350-400° C. for over 12 hours prior to extrusion at which point the material was extruded using a 5:1 extrusion ratio (ER) with an extrusion speed of 20 ipm (inch per minute).
At the nano-layers present between the nickel and the magnesium layers or magnesium matrix, the galvanic reaction took place. The dissolution rate in 3% KCl brine solution at 90° C. as well as the tensile properties at 150° C. of the galvanically reactive alloy are shown in Table E.
It will thus be seen that the objects set forth above, among those made apparent from the preceding description, are efficiently attained, and since certain changes may be made in the constructions set forth without departing from the spirit and scope of the invention, it is intended that all matter contained in the above description and shown in the accompanying drawings shall be interpreted as illustrative and not in a limiting sense. The invention has been described with reference to preferred and alternate embodiments. Modifications and alterations will become apparent to those skilled in the art upon reading and understanding the detailed discussion of the invention provided herein. This invention is intended to include all such modifications and alterations insofar as they come within the scope of the present invention. It is also to be understood that the following claims are intended to cover all of the generic and specific features of the invention herein described and all statements of the scope of the invention, which, as a matter of language, might be said to fall there between. The invention has been described with reference to the preferred embodiments. These and other modifications of the preferred embodiments as well as other embodiments of the invention will be obvious from the disclosure herein, whereby the foregoing descriptive matter is to be interpreted merely as illustrative of the invention and not as a limitation. It is intended to include all such modifications and alterations insofar as they come within the scope of the appended claims.
The present invention claims priority on U.S. Provisional Application Ser. No. 62/569,004 filed Oct. 6, 2017, which is incorporated herein by reference The present invention is a continuation-in-part of U.S. application Ser. No. 15/294,957 filed Oct. 17, 2016, which is a divisional of U.S. application Ser. No. 14/627,236 filed Feb. 20, 2015 (now U.S. Pat. No. 9,757,796 issued Sep. 12, 2017), which in turn claims priority on U.S. Provisional Application Ser. No. 61/942,879 filed Feb. 21, 2014, which are incorporated herein by reference. The present invention is also a continuation-in-part of U.S. application Ser. No. 15/641,439 filed Jul. 5, 2017, which is a divisional of U.S. patent application Ser. No. 14/689,295 filed Apr. 17, 2015 (now U.S. Pat. No. 9,903,010 issued Feb. 27, 2018), which in turn claims priority on U.S. Provisional Patent Application Ser. No. 61/981,425 filed Apr. 18, 2014, which are incorporated herein by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 1468905 | Herman | Jul 1923 | A |
| 1558066 | Veazey et al. | Oct 1925 | A |
| 1880614 | Wetherill et al. | Oct 1932 | A |
| 2352993 | Albertson | Jul 1933 | A |
| 2011613 | Brown et al. | Aug 1935 | A |
| 2094578 | Blumenthal et al. | Oct 1937 | A |
| 2189697 | Baker | Feb 1940 | A |
| 2222233 | Mize | Nov 1940 | A |
| 2225143 | Baker et al. | Dec 1940 | A |
| 2238895 | Gage | Apr 1941 | A |
| 2261292 | Salnikov | Nov 1941 | A |
| 2294648 | Ansel et al. | Sep 1942 | A |
| 2301624 | Holt | Nov 1942 | A |
| 2394843 | Cook et al. | Feb 1946 | A |
| 2672199 | McKenna | Mar 1954 | A |
| 2753941 | Hebard et al. | Jul 1956 | A |
| 2754910 | Derrick et al. | Jul 1956 | A |
| 2933136 | Ayers et al. | Apr 1960 | A |
| 2983634 | Budininkas et al. | May 1961 | A |
| 3057405 | Mallinger | Oct 1962 | A |
| 3066391 | Vordahl et al. | Dec 1962 | A |
| 3106959 | Huitt et al. | Oct 1963 | A |
| 3142338 | Brown | Jul 1964 | A |
| 3152009 | DeLong | Oct 1964 | A |
| 3180728 | Pryor et al. | Apr 1965 | A |
| 3180778 | Rinderspacher et al. | Apr 1965 | A |
| 3196949 | Thomas | Jul 1965 | A |
| 3226314 | Wellington et al. | Dec 1965 | A |
| 3242988 | McGuire, Jr. et al. | Mar 1966 | A |
| 3295935 | Pflumm et al. | Jan 1967 | A |
| 3298440 | Current | Jan 1967 | A |
| 3316748 | Lang et al. | May 1967 | A |
| 3326291 | Zandemer | Jun 1967 | A |
| 3347714 | Broverman et al. | Oct 1967 | A |
| 3385696 | Hitchcock et al. | May 1968 | A |
| 3390724 | Caldwell | Jul 1968 | A |
| 3395758 | Kelly et al. | Aug 1968 | A |
| 3406101 | Kilpatrick | Oct 1968 | A |
| 3416918 | Roberts | Dec 1968 | A |
| 3434539 | Merritt | Mar 1969 | A |
| 3445148 | Harris et al. | May 1969 | A |
| 3445731 | Saeki et al. | May 1969 | A |
| 3465181 | Colby et al. | Sep 1969 | A |
| 3489218 | Means | Jan 1970 | A |
| 3513230 | Rhees et al. | May 1970 | A |
| 3600163 | Badia et al. | Aug 1971 | A |
| 3602305 | Kisling | Aug 1971 | A |
| 3637446 | Elliott et al. | Jan 1972 | A |
| 3645331 | Maurer et al. | Feb 1972 | A |
| 3660049 | Benjamin | May 1972 | A |
| 3765484 | Hamby, Jr. et al. | Oct 1973 | A |
| 3768563 | Blount | Oct 1973 | A |
| 3775823 | Adolph et al. | Dec 1973 | A |
| 3816080 | Bomford et al. | Jun 1974 | A |
| 3823045 | Hielema | Jul 1974 | A |
| 3878889 | Seaboume | Apr 1975 | A |
| 3894850 | Kovalchuk et al. | Jul 1975 | A |
| 3924677 | Prenner et al. | Dec 1975 | A |
| 3957483 | Suzuki | May 1976 | A |
| 4010583 | Highberg | Mar 1977 | A |
| 4039717 | Titus | Aug 1977 | A |
| 4050529 | Tagirov et al. | Sep 1977 | A |
| 4157732 | Fonner | Jun 1979 | A |
| 4248307 | Silberman et al. | Feb 1981 | A |
| 4264362 | Serveg et al. | Apr 1981 | A |
| 4284137 | Taylor | Aug 1981 | A |
| 4292377 | Petersen et al. | Sep 1981 | A |
| 4368788 | Drake | Jan 1983 | A |
| 4372384 | Kinney | Feb 1983 | A |
| 4373584 | Silberman et al. | Feb 1983 | A |
| 4373952 | Parent | Feb 1983 | A |
| 4374543 | Richardson | Feb 1983 | A |
| 4384616 | Dellinger | May 1983 | A |
| 4395440 | Abe et al. | Jul 1983 | A |
| 4399871 | Adkins et al. | Aug 1983 | A |
| 4407368 | Erbstoesser | Oct 1983 | A |
| 4422508 | Rutledge, Jr. et al. | Dec 1983 | A |
| 4450136 | Dudek et al. | May 1984 | A |
| 4452311 | Speegle et al. | Jun 1984 | A |
| 4475729 | Costigan | Oct 1984 | A |
| 4498543 | Pye et al. | Feb 1985 | A |
| 4499048 | Hanejko | Feb 1985 | A |
| 4499049 | Hanejko | Feb 1985 | A |
| 4524825 | Fore | Jun 1985 | A |
| 4526840 | Jerabek | Jul 1985 | A |
| 4534414 | Pringle | Aug 1985 | A |
| 4539175 | Lichti et al. | Sep 1985 | A |
| 4554986 | Jones | Nov 1985 | A |
| 4619699 | Petkovic-Luton et al. | Oct 1986 | A |
| 4640354 | Boisson | Feb 1987 | A |
| 4648901 | Murray et al. | Mar 1987 | A |
| 4655852 | Rallis | Apr 1987 | A |
| 4664962 | DesMarais, Jr. | May 1987 | A |
| 4668470 | Gilman et al. | May 1987 | A |
| 4673549 | Ecer | Jun 1987 | A |
| 4674572 | Gallus | Jun 1987 | A |
| 4678037 | Smith | Jul 1987 | A |
| 4681133 | Weston | Jul 1987 | A |
| 4688641 | Knieriemen | Aug 1987 | A |
| 4690796 | Paliwal | Sep 1987 | A |
| 4693863 | Del Corso et al. | Sep 1987 | A |
| 4703807 | Weston | Nov 1987 | A |
| 4706753 | Ohkochi et al. | Nov 1987 | A |
| 4708202 | Sukup et al. | Nov 1987 | A |
| 4708208 | Halbardier | Nov 1987 | A |
| 4709761 | Setterberg, Jr. | Dec 1987 | A |
| 4714116 | Brunner | Dec 1987 | A |
| 4716964 | Erbstoesser et al. | Jan 1988 | A |
| 4719971 | Owens | Jan 1988 | A |
| 4721159 | Ohkochi et al. | Jan 1988 | A |
| 4738599 | Shilling | Apr 1988 | A |
| 4741973 | Condit et al. | May 1988 | A |
| 4768588 | Kupsa | Sep 1988 | A |
| 4775598 | Jaeckel | Oct 1988 | A |
| 4784226 | Wyatt | Nov 1988 | A |
| 4805699 | Halbardier | Feb 1989 | A |
| 4817725 | Jenkins | Apr 1989 | A |
| 4834184 | Streich et al. | May 1989 | A |
| H635 | Johnson et al. | Jun 1989 | H |
| 4853056 | Hoffman | Aug 1989 | A |
| 4869324 | Holder | Sep 1989 | A |
| 4869325 | Halbardier | Sep 1989 | A |
| 4875948 | Verneker | Oct 1989 | A |
| 4880059 | Branded et al. | Nov 1989 | A |
| 4889187 | Terrell et al. | Dec 1989 | A |
| 4890675 | Dew | Jan 1990 | A |
| 4901794 | Baugh et al. | Feb 1990 | A |
| 4909320 | Hebert et al. | Mar 1990 | A |
| 4917966 | Wilde et al. | Apr 1990 | A |
| 4921664 | Couper | May 1990 | A |
| 4929415 | Okazaki | May 1990 | A |
| 4932474 | Schroeder, Jr. et al. | Jun 1990 | A |
| 4934459 | Baugh et al. | Jun 1990 | A |
| 4938309 | Emdy | Jul 1990 | A |
| 4938809 | Das et al. | Jul 1990 | A |
| 4944351 | Eriksen et al. | Jul 1990 | A |
| 4949788 | Szarka et al. | Aug 1990 | A |
| 4952902 | Kawaguchi et al. | Aug 1990 | A |
| 4975412 | Okazaki et al. | Dec 1990 | A |
| 4977958 | Miller | Dec 1990 | A |
| 4981177 | Carmody et al. | Jan 1991 | A |
| 4986361 | Muuller et al. | Jan 1991 | A |
| 4997622 | Regazzoni et al. | Mar 1991 | A |
| 5006044 | Walker, Sr. et al. | Apr 1991 | A |
| 5010955 | Springer | Apr 1991 | A |
| 5036921 | Pittard et al. | Aug 1991 | A |
| 5048611 | Cochran | Sep 1991 | A |
| 5049165 | Tselesin | Sep 1991 | A |
| 5061323 | DeLuccia | Oct 1991 | A |
| 5063775 | Walker, Sr. et al. | Nov 1991 | A |
| 5073207 | Faure et al. | Dec 1991 | A |
| 5074361 | Brisco et al. | Dec 1991 | A |
| 5076869 | Bourell et al. | Dec 1991 | A |
| 5084088 | Okazaki | Jan 1992 | A |
| 5087304 | Chang et al. | Feb 1992 | A |
| 5090480 | Pittard et al. | Feb 1992 | A |
| 5095988 | Bode | Mar 1992 | A |
| 5103911 | Heijnen | Apr 1992 | A |
| 5106702 | Walker et al. | Apr 1992 | A |
| 5117915 | Mueller et al. | Jun 1992 | A |
| 5161614 | Wu et al. | Nov 1992 | A |
| 5171734 | Sanjurjo et al. | Dec 1992 | A |
| 5178216 | Giroux et al. | Jan 1993 | A |
| 5181571 | Mueller et al. | Jan 1993 | A |
| 5183631 | Kugimiya et al. | Feb 1993 | A |
| 5188182 | Echols, III et al. | Feb 1993 | A |
| 5188183 | Hopmann et al. | Feb 1993 | A |
| 5204055 | Sachs et al. | Apr 1993 | A |
| 5222867 | Walker, Sr. et al. | Jun 1993 | A |
| 5226483 | Williamson, Jr. | Jul 1993 | A |
| 5228518 | Wilson et al. | Jul 1993 | A |
| 5234055 | Cornette | Aug 1993 | A |
| 5238646 | Farcy et al. | Aug 1993 | A |
| 5240495 | Dieckmann et al. | Aug 1993 | A |
| 5240742 | Johnson et al. | Aug 1993 | A |
| 5252365 | White | Oct 1993 | A |
| 5253714 | Davis et al. | Oct 1993 | A |
| 5271468 | Streich et al. | Dec 1993 | A |
| 5273569 | Gilman et al. | Dec 1993 | A |
| 5282509 | Schurr, III | Feb 1994 | A |
| 5285798 | Banerjee et al. | Feb 1994 | A |
| 5292478 | Scorey | Mar 1994 | A |
| 5293940 | Hromas et al. | Mar 1994 | A |
| 5304260 | Aikawa et al. | Apr 1994 | A |
| 5304588 | Boysen et al. | Apr 1994 | A |
| 5309874 | Willermet et al. | May 1994 | A |
| 5310000 | Arterbury et al. | May 1994 | A |
| 5316598 | Chang et al. | May 1994 | A |
| 5318746 | Lashmore et al. | Jun 1994 | A |
| 5336466 | Iba | Aug 1994 | A |
| 5342576 | Whitehead | Aug 1994 | A |
| 5352522 | Kugimiya et al. | Oct 1994 | A |
| 5380473 | Bogue et al. | Jan 1995 | A |
| 5387380 | Cima et al. | Feb 1995 | A |
| 5392860 | Ross | Feb 1995 | A |
| 5394236 | Murnick | Feb 1995 | A |
| 5394941 | Venditto et al. | Mar 1995 | A |
| 5398754 | Dinhoble | Mar 1995 | A |
| 5407011 | Layton | Apr 1995 | A |
| 5409555 | Fujita et al. | Apr 1995 | A |
| 5411082 | Kennedy | May 1995 | A |
| 5417285 | Van Buskirk et al. | May 1995 | A |
| 5425424 | Reinhardt et al. | Jun 1995 | A |
| 5427177 | Jordan, Jr. et al. | Jun 1995 | A |
| 5435392 | Kennedy | Jul 1995 | A |
| 5439051 | Kennedy et al. | Aug 1995 | A |
| 5454430 | Kennedy et al. | Oct 1995 | A |
| 5456317 | Hood, III et al. | Oct 1995 | A |
| 5456327 | Denton et al. | Oct 1995 | A |
| 5464062 | Blizzard, Jr. | Nov 1995 | A |
| 5472048 | Kennedy | Dec 1995 | A |
| 5474131 | Jordan, Jr. et al. | Dec 1995 | A |
| 5476632 | Shivanath et al. | Dec 1995 | A |
| 5477923 | Jordan, Jr. et al. | Dec 1995 | A |
| 5479986 | Gano et al. | Jan 1996 | A |
| 5494538 | Kirillov et al. | Feb 1996 | A |
| 5506055 | Dorfman et al. | Apr 1996 | A |
| 5507439 | Story | Apr 1996 | A |
| 5511620 | Baugh et al. | Apr 1996 | A |
| 5524699 | Cook | Jun 1996 | A |
| 5526880 | Jordan, Jr. et al. | Jun 1996 | A |
| 5526881 | Martin et al. | Jun 1996 | A |
| 5529746 | Knoss et al. | Jun 1996 | A |
| 5531735 | Thompson | Jul 1996 | A |
| 5533573 | Jordan, Jr. et al. | Jul 1996 | A |
| 5536485 | Kume et al. | Jul 1996 | A |
| 5552110 | Iba | Sep 1996 | A |
| 5558153 | Holcombe et al. | Sep 1996 | A |
| 5601924 | Beane et al. | Feb 1997 | A |
| 5607017 | Owens et al. | Mar 1997 | A |
| 5623993 | Van Buskirk et al. | Apr 1997 | A |
| 5623994 | Robinson | Apr 1997 | A |
| 5641023 | Ross et al. | Jun 1997 | A |
| 5636691 | Hendrickson et al. | Jul 1997 | A |
| 5647444 | Williams | Jul 1997 | A |
| 5665289 | Chung et al. | Sep 1997 | A |
| 5677372 | Yamamoto et al. | Oct 1997 | A |
| 5685372 | Gano | Nov 1997 | A |
| 5701576 | Fujita et al. | Dec 1997 | A |
| 5707214 | Schmidt | Jan 1998 | A |
| 5709269 | Head | Jan 1998 | A |
| 5720344 | Newman | Feb 1998 | A |
| 5722033 | Carden | Feb 1998 | A |
| 5728195 | Eastman et al. | Mar 1998 | A |
| 5765639 | Muth | Jun 1998 | A |
| 5767562 | Yamashita | Jun 1998 | A |
| 5772735 | Sehgal et al. | Jun 1998 | A |
| 5782305 | Hicks | Jul 1998 | A |
| 5797454 | Hipp | Aug 1998 | A |
| 5820608 | Luzio et al. | Oct 1998 | A |
| 5826652 | Tapp | Oct 1998 | A |
| 5826661 | Parker et al. | Oct 1998 | A |
| 5829520 | Johnson | Nov 1998 | A |
| 5836396 | Norman | Nov 1998 | A |
| 5857521 | Ross et al. | Jan 1999 | A |
| 5881816 | Wright | Mar 1999 | A |
| 5896819 | Turila et al. | Apr 1999 | A |
| 5902424 | Fujita et al. | May 1999 | A |
| 5934372 | Muth | Aug 1999 | A |
| 5941309 | Appleton | Aug 1999 | A |
| 5960881 | Allamon et al. | Oct 1999 | A |
| 5964965 | Schulz et al. | Oct 1999 | A |
| 5894007 | Yuan et al. | Nov 1999 | A |
| 5980602 | Carden | Nov 1999 | A |
| 5985466 | Atarashi et al. | Nov 1999 | A |
| 5988287 | Jordan, Jr. et al. | Nov 1999 | A |
| 5990051 | Ischy et al. | Nov 1999 | A |
| 5992452 | Nelson, II | Nov 1999 | A |
| 5992520 | Schultz et al. | Nov 1999 | A |
| 6007314 | Nelson, II | Dec 1999 | A |
| 6024915 | Kume et al. | Feb 2000 | A |
| 6030637 | Whitehead | Feb 2000 | A |
| 6032735 | Echols | Mar 2000 | A |
| 6033622 | Maruyama | Mar 2000 | A |
| 6036777 | Sachs | Mar 2000 | A |
| 6036792 | Chu et al. | Mar 2000 | A |
| 6040087 | Kawakami | Mar 2000 | A |
| 6047773 | Zeltmann et al. | Apr 2000 | A |
| 6050340 | Scott | Apr 2000 | A |
| 6069313 | Kay | May 2000 | A |
| 6076600 | Vick, Jr. et al. | Jun 2000 | A |
| 6079496 | Hirth | Jun 2000 | A |
| 6085837 | Massinon et al. | Jul 2000 | A |
| 6095247 | Streich et al. | Aug 2000 | A |
| 6119783 | Parker et al. | Sep 2000 | A |
| 6126898 | Butler | Oct 2000 | A |
| 6142237 | Christmas et al. | Nov 2000 | A |
| 6161622 | Robb et al. | Dec 2000 | A |
| 6167970 | Stout et al. | Jan 2001 | B1 |
| 6170583 | Boyce | Jan 2001 | B1 |
| 6171359 | Levinski et al. | Jan 2001 | B1 |
| 6173779 | Smith | Jan 2001 | B1 |
| 6176323 | Weirich et al. | Jan 2001 | B1 |
| 6189616 | Gano et al. | Feb 2001 | B1 |
| 6189618 | Beeman et al. | Feb 2001 | B1 |
| 6213202 | Read, Jr. | Apr 2001 | B1 |
| 6220349 | Vargus et al. | Apr 2001 | B1 |
| 6220350 | Brothers et al. | Apr 2001 | B1 |
| 6220357 | Carmichael et al. | Apr 2001 | B1 |
| 6228904 | Yadav et al. | May 2001 | B1 |
| 6230799 | Slaughter et al. | May 2001 | B1 |
| 6237688 | Burleson et al. | May 2001 | B1 |
| 6238280 | Ritt et al. | May 2001 | B1 |
| 6241021 | Bowling | Jun 2001 | B1 |
| 6248399 | Hehmann | Jun 2001 | B1 |
| 6250392 | Muth | Jun 2001 | B1 |
| 6261432 | Huber et al. | Jul 2001 | B1 |
| 6265205 | Hitchens et al. | Jul 2001 | B1 |
| 6273187 | Voisin, Jr. et al. | Aug 2001 | B1 |
| 6276452 | Davis et al. | Aug 2001 | B1 |
| 6276457 | Moffatt et al. | Aug 2001 | B1 |
| 6279656 | Sinclair et al. | Aug 2001 | B1 |
| 6287332 | Bolz et al. | Sep 2001 | B1 |
| 6287445 | Lashmore et al. | Sep 2001 | B1 |
| 6302205 | Ryll | Oct 2001 | B1 |
| 6315041 | Carlisle et al. | Nov 2001 | B1 |
| 6315050 | Vaylnshteyn et al. | Nov 2001 | B2 |
| 6325148 | Trahan et al. | Dec 2001 | B1 |
| 6328110 | Joubert | Dec 2001 | B1 |
| 6341653 | Fermaniuk et al. | Jan 2002 | B1 |
| 6341747 | Schmidt et al. | Jan 2002 | B1 |
| 6349766 | Bussear et al. | Feb 2002 | B1 |
| 6354372 | Carisell et al. | Mar 2002 | B1 |
| 6354379 | Miszewski et al. | Mar 2002 | B2 |
| 6371206 | Mills | Apr 2002 | B1 |
| 6372346 | Toth | Apr 2002 | B1 |
| 6382244 | Vann | May 2002 | B2 |
| 6390195 | Nguyen et al. | May 2002 | B1 |
| 6390200 | Allamon et al. | May 2002 | B1 |
| 6394180 | Berscheidt et al. | May 2002 | B1 |
| 6394185 | Constien | May 2002 | B1 |
| 6395402 | Lambert et al. | May 2002 | B1 |
| 6397950 | Streich et al. | Jun 2002 | B1 |
| 6401547 | Hatfield et al. | Jun 2002 | B1 |
| 6403210 | Stuivinga et al. | Jun 2002 | B1 |
| 6408946 | Marshall et al. | Jun 2002 | B1 |
| 6419023 | George et al. | Jul 2002 | B1 |
| 6422314 | Todd et al. | Jul 2002 | B1 |
| 6439313 | Thomeer et al. | Aug 2002 | B1 |
| 6444316 | Reddy et al. | Sep 2002 | B1 |
| 6446717 | White et al. | Sep 2002 | B1 |
| 6457525 | Scott | Oct 2002 | B1 |
| 6467546 | Allamon et al. | Oct 2002 | B2 |
| 6470965 | Winzer | Oct 2002 | B1 |
| 6491097 | Oneal et al. | Dec 2002 | B1 |
| 6491116 | Berscheidt et al. | Dec 2002 | B2 |
| 6513598 | Moore et al. | Feb 2003 | B2 |
| 6513600 | Ross | Feb 2003 | B2 |
| 6527051 | Reddy et al. | Mar 2003 | B1 |
| 6540033 | Sullivan et al. | Apr 2003 | B1 |
| 6543543 | Muth | Apr 2003 | B2 |
| 6554071 | Reddy et al. | Apr 2003 | B1 |
| 6561275 | Glass et al. | May 2003 | B2 |
| 6581681 | Zimmerman et al. | Jun 2003 | B1 |
| 6588507 | Dusterhoft et al. | Jul 2003 | B2 |
| 6591915 | Burris et al. | Jul 2003 | B2 |
| 6601648 | Ebinger | Aug 2003 | B2 |
| 6601650 | Sundararajan | Aug 2003 | B2 |
| 6609569 | Howlett et al. | Aug 2003 | B2 |
| 6612826 | Bauer et al. | Sep 2003 | B1 |
| 6613383 | George et al. | Sep 2003 | B1 |
| 6619400 | Brunet | Sep 2003 | B2 |
| 6630008 | Meeks, III et al. | Oct 2003 | B1 |
| 6634428 | Krauss et al. | Oct 2003 | B2 |
| 6662886 | Russell | Dec 2003 | B2 |
| 6675889 | Mullins et al. | Jan 2004 | B1 |
| 6699305 | Myrick | Mar 2004 | B2 |
| 6712153 | Turley et al. | Mar 2004 | B2 |
| 6712797 | Southern, Jr. | Mar 2004 | B1 |
| 6713177 | George et al. | Mar 2004 | B2 |
| 6715541 | Pedersen et al. | Apr 2004 | B2 |
| 6737385 | Todd et al. | May 2004 | B2 |
| 6779599 | Mullins et al. | Aug 2004 | B2 |
| 6799638 | Butterfield, Jr. | Oct 2004 | B2 |
| 6810960 | Pia | Nov 2004 | B2 |
| 6817414 | Lee | Nov 2004 | B2 |
| 6831044 | Constien | Dec 2004 | B2 |
| 6883611 | Smith et al. | Apr 2005 | B2 |
| 6887297 | Winter et al. | May 2005 | B2 |
| 6896049 | Moyes | May 2005 | B2 |
| 6896061 | Hriscu et al. | May 2005 | B2 |
| 6899777 | Vaidyanathan et al. | May 2005 | B2 |
| 6908516 | Hehmann et al. | Jun 2005 | B2 |
| 6913827 | Georget et al. | Jul 2005 | B2 |
| 6926086 | Patterson et al. | Aug 2005 | B2 |
| 6932159 | Hovem | Aug 2005 | B2 |
| 6939388 | Angeliu | Sep 2005 | B2 |
| 6945331 | Patel | Sep 2005 | B2 |
| 6951331 | Haughom et al. | Oct 2005 | B2 |
| 6959759 | Doane et al. | Nov 2005 | B2 |
| 6973970 | Johnston et al. | Dec 2005 | B2 |
| 6973973 | Howard et al. | Dec 2005 | B2 |
| 6983796 | Bayne et al. | Jan 2006 | B2 |
| 6986390 | Doane et al. | Jan 2006 | B2 |
| 7013989 | Hammond et al. | Mar 2006 | B2 |
| 7013998 | Ray et al. | Mar 2006 | B2 |
| 7017664 | Walker et al. | Mar 2006 | B2 |
| 7017677 | Keshavan et al. | Mar 2006 | B2 |
| 7021389 | Bishop et al. | Apr 2006 | B2 |
| 7025146 | King et al. | Apr 2006 | B2 |
| 7028778 | Krywitsky | Apr 2006 | B2 |
| 7044230 | Starr et al. | May 2006 | B2 |
| 7048812 | Bettles et al. | May 2006 | B2 |
| 7049272 | Sinclair et al. | May 2006 | B2 |
| 7051805 | Doane et al. | May 2006 | B2 |
| 7059410 | Bousche et al. | Jun 2006 | B2 |
| 7063748 | Talton | Jun 2006 | B2 |
| 7090027 | Williams | Aug 2006 | B1 |
| 7093664 | Todd et al. | Aug 2006 | B2 |
| 7096945 | Richards et al. | Aug 2006 | B2 |
| 7096946 | Jasser et al. | Aug 2006 | B2 |
| 7097807 | Meeks, III et al. | Aug 2006 | B1 |
| 7097906 | Gardner | Aug 2006 | B2 |
| 7108080 | Tessari et al. | Sep 2006 | B2 |
| 7111682 | Blaisdell | Sep 2006 | B2 |
| 7128145 | Mickey | Oct 2006 | B2 |
| 7141207 | Jandeska, Jr. et al. | Nov 2006 | B2 |
| 7150326 | Bishop et al. | Dec 2006 | B2 |
| 7163066 | Lehr | Jan 2007 | B2 |
| 7165622 | Hirth et al. | Jan 2007 | B2 |
| 7168494 | Starr et al. | Jan 2007 | B2 |
| 7174963 | Bertelsen | Feb 2007 | B2 |
| 7182135 | Szarka | Feb 2007 | B2 |
| 7188559 | Vecchio | Mar 2007 | B1 |
| 7210527 | Walker et al. | May 2007 | B2 |
| 7210533 | Starr et al. | May 2007 | B2 |
| 7217311 | Hong et al. | May 2007 | B2 |
| 7234530 | Gass | Jun 2007 | B2 |
| 7250188 | Dodelet et al. | Jul 2007 | B2 |
| 7252162 | Akinlade et al. | Aug 2007 | B2 |
| 7255172 | Johnson | Aug 2007 | B2 |
| 7255178 | Slup et al. | Aug 2007 | B2 |
| 7264060 | Wills | Sep 2007 | B2 |
| 7267172 | Hofman | Sep 2007 | B2 |
| 7267178 | Krywitsky | Sep 2007 | B2 |
| 7270186 | Johnson | Sep 2007 | B2 |
| 7287592 | Surjaatmadja et al. | Oct 2007 | B2 |
| 7311152 | Howard et al. | Dec 2007 | B2 |
| 7316274 | Xu et al. | Jan 2008 | B2 |
| 7320365 | Pia | Jan 2008 | B2 |
| 7322412 | Badalamenti et al. | Jan 2008 | B2 |
| 7322417 | Rytlewski et al. | Jan 2008 | B2 |
| 7325617 | Murray | Feb 2008 | B2 |
| 7328750 | Swor et al. | Feb 2008 | B2 |
| 7331388 | Vilela et al. | Feb 2008 | B2 |
| 7337854 | Horn et al. | Mar 2008 | B2 |
| 7346456 | Le Bemadjiel | Mar 2008 | B2 |
| 7350582 | McKeachnie et al. | Apr 2008 | B2 |
| 7353867 | Carter et al. | Apr 2008 | B2 |
| 7353879 | Todd et al. | Apr 2008 | B2 |
| 7360593 | Constien | Apr 2008 | B2 |
| 7360597 | Blaisdell | Apr 2008 | B2 |
| 7363970 | Corre et al. | Apr 2008 | B2 |
| 7373978 | Barry et al. | May 2008 | B2 |
| 7380600 | Willberg et al. | Jun 2008 | B2 |
| 7384443 | Mirchandani | Jun 2008 | B2 |
| 7387158 | Murray et al. | Jun 2008 | B2 |
| 7387165 | Lopez de Cardenas et al. | Jun 2008 | B2 |
| 7392841 | Murray et al. | Jul 2008 | B2 |
| 7401648 | Richard | Jul 2008 | B2 |
| 7416029 | Telfer et al. | Aug 2008 | B2 |
| 7422058 | O'Malley | Sep 2008 | B2 |
| 7426964 | Lynde et al. | Sep 2008 | B2 |
| 7441596 | Wood et al. | Oct 2008 | B2 |
| 7445049 | Howard et al. | Nov 2008 | B2 |
| 7451815 | Hailey, Jr. | Nov 2008 | B2 |
| 7451817 | Reddy et al. | Nov 2008 | B2 |
| 7461699 | Richard et al. | Dec 2008 | B2 |
| 7464752 | Dale et al. | Dec 2008 | B2 |
| 7464764 | Xu | Dec 2008 | B2 |
| 7472750 | Walker et al. | Jan 2009 | B2 |
| 7478676 | East, Jr. et al. | Jan 2009 | B2 |
| 7503390 | Gomez | Mar 2009 | B2 |
| 7503392 | King et al. | Mar 2009 | B2 |
| 7503399 | Badalamenti et al. | Mar 2009 | B2 |
| 7509993 | Turng et al. | Mar 2009 | B1 |
| 7510018 | Williamson et al. | Mar 2009 | B2 |
| 7513311 | Gramstad et al. | Apr 2009 | B2 |
| 7516791 | Bryant et al. | Apr 2009 | B2 |
| 7527103 | Huang et al. | May 2009 | B2 |
| 7531020 | Woodfield et al. | May 2009 | B2 |
| 7537825 | Wardle et al. | May 2009 | B1 |
| 7552777 | Murray et al. | Jun 2009 | B2 |
| 7552779 | Murray | Jun 2009 | B2 |
| 7559357 | Clem | Jul 2009 | B2 |
| 7575062 | East, Jr. | Aug 2009 | B2 |
| 7579087 | Maloney et al. | Aug 2009 | B2 |
| 7591318 | Tilghman | Sep 2009 | B2 |
| 7600572 | Slup et al. | Oct 2009 | B2 |
| 7604049 | Vaidya et al. | Oct 2009 | B2 |
| 7604055 | Richard et al. | Oct 2009 | B2 |
| 7607476 | Tom et al. | Oct 2009 | B2 |
| 7617871 | Surjaatmadja et al. | Nov 2009 | B2 |
| 7635023 | Goldberg et al. | Dec 2009 | B2 |
| 7640988 | Phi et al. | Jan 2010 | B2 |
| 7647964 | Akbar et al. | Jan 2010 | B2 |
| 7661480 | Al-Anazi | Feb 2010 | B2 |
| 7661481 | Todd et al. | Feb 2010 | B2 |
| 7665537 | Patel et al. | Feb 2010 | B2 |
| 7686082 | Marsh | Mar 2010 | B2 |
| 7690436 | Turley et al. | Apr 2010 | B2 |
| 7699101 | Fripp et al. | Apr 2010 | B2 |
| 7703511 | Buyers et al. | Apr 2010 | B2 |
| 7708078 | Stoesz | May 2010 | B2 |
| 7709421 | Jones et al. | May 2010 | B2 |
| 7712541 | Loretz et al. | May 2010 | B2 |
| 7723272 | Crews et al. | May 2010 | B2 |
| 7726406 | Xu | Jun 2010 | B2 |
| 7735578 | Loehr et al. | Jun 2010 | B2 |
| 7743836 | Cook et al. | Jun 2010 | B2 |
| 7752971 | Loehr | Jul 2010 | B2 |
| 7757773 | Rytlewski | Jul 2010 | B2 |
| 7762342 | Richard et al. | Jul 2010 | B2 |
| 7770652 | Bamett | Aug 2010 | B2 |
| 7771289 | Palumbo et al. | Aug 2010 | B2 |
| 7771547 | Bieler et al. | Aug 2010 | B2 |
| 7775284 | Richard et al. | Aug 2010 | B2 |
| 7775285 | Surjaatmadja et al. | Aug 2010 | B2 |
| 7775286 | Duphorne | Aug 2010 | B2 |
| 7784543 | Johnson | Aug 2010 | B2 |
| 7793714 | Johnson | Sep 2010 | B2 |
| 7793820 | Hirano et al. | Sep 2010 | B2 |
| 7794520 | Murty et al. | Sep 2010 | B2 |
| 7798225 | Giroux et al. | Sep 2010 | B2 |
| 7798226 | Themig | Sep 2010 | B2 |
| 7798236 | McKeachnie et al. | Sep 2010 | B2 |
| 7806189 | Frazier | Oct 2010 | B2 |
| 7806192 | Foster et al. | Oct 2010 | B2 |
| 7810553 | Cruickshank et al. | Oct 2010 | B2 |
| 7810567 | Daniels et al. | Oct 2010 | B2 |
| 7819198 | Birckhead et al. | Oct 2010 | B2 |
| 7828055 | Willauer et al. | Nov 2010 | B2 |
| 7833944 | Munoz et al. | Nov 2010 | B2 |
| 7849927 | Herrera | Dec 2010 | B2 |
| 7851016 | Arbab et al. | Dec 2010 | B2 |
| 7855168 | Fuller et al. | Dec 2010 | B2 |
| 7861779 | Vestavik | Jan 2011 | B2 |
| 7861781 | D'Arcy | Jan 2011 | B2 |
| 7874365 | East, Jr. et al. | Jan 2011 | B2 |
| 7878253 | Stowe et al. | Feb 2011 | B2 |
| 7879162 | Pandey | Feb 2011 | B2 |
| 7879367 | Heublein et al. | Feb 2011 | B2 |
| 7896091 | Williamson et al. | Mar 2011 | B2 |
| 7897063 | Perry et al. | Mar 2011 | B1 |
| 7900696 | Nish et al. | Mar 2011 | B1 |
| 7900703 | Clark et al. | Mar 2011 | B2 |
| 7909096 | Clarke et al. | Mar 2011 | B2 |
| 7909104 | Bjorgum | Mar 2011 | B2 |
| 7909110 | Sharma et al. | Mar 2011 | B2 |
| 7909115 | Grove et al. | Mar 2011 | B2 |
| 7913765 | Crow et al. | Mar 2011 | B2 |
| 7918275 | Clem | Apr 2011 | B2 |
| 7931093 | Foster et al. | Apr 2011 | B2 |
| 7938191 | Vaidya | May 2011 | B2 |
| 7946335 | Bewlay et al. | May 2011 | B2 |
| 7946340 | Surjattmadja et al. | May 2011 | B2 |
| 7958940 | Jameson | Jun 2011 | B2 |
| 7963331 | Surjattmadja et al. | Jun 2011 | B2 |
| 7963340 | Gramstad et al. | Jun 2011 | B2 |
| 7963342 | George | Jun 2011 | B2 |
| 7980300 | Roberts et al. | Jul 2011 | B2 |
| 7987906 | Troy | Aug 2011 | B1 |
| 7992763 | Vecchio et al. | Aug 2011 | B2 |
| 7999987 | Dellinger et al. | Aug 2011 | B2 |
| 8002821 | Stinson | Aug 2011 | B2 |
| 8020619 | Robertson et al. | Sep 2011 | B1 |
| 8020620 | Daniels et al. | Sep 2011 | B2 |
| 8025104 | Cooke, Jr. | Sep 2011 | B2 |
| 8028767 | Radford et al. | Oct 2011 | B2 |
| 8033331 | Themig | Oct 2011 | B2 |
| 8034152 | Westin et al. | Oct 2011 | B2 |
| 8039422 | Al-Zahrani | Oct 2011 | B1 |
| 8056628 | Whitsitt et al. | Nov 2011 | B2 |
| 8056638 | Clayton et al. | Nov 2011 | B2 |
| 8109340 | Doane et al. | Feb 2012 | B2 |
| 8114148 | Atanasoska et al. | Feb 2012 | B2 |
| 8127856 | Nish et al. | Mar 2012 | B1 |
| 8153052 | Jackson et al. | Apr 2012 | B2 |
| 8163060 | Imanishi et al. | Apr 2012 | B2 |
| 8211247 | Marya et al. | Jul 2012 | B2 |
| 8211248 | Marya | Jul 2012 | B2 |
| 8211331 | Jorgensen et al. | Jul 2012 | B2 |
| 8220554 | Jordan et al. | Jul 2012 | B2 |
| 8226740 | Chaumonnot et al. | Jul 2012 | B2 |
| 8230731 | Dyer et al. | Jul 2012 | B2 |
| 8231947 | Vaidya et al. | Jul 2012 | B2 |
| 8263178 | Boulos et al. | Sep 2012 | B2 |
| 8267177 | Vogel et al. | Sep 2012 | B1 |
| 8276670 | Patel | Oct 2012 | B2 |
| 8277974 | Kumar et al. | Oct 2012 | B2 |
| 8297364 | Agrawal et al. | Oct 2012 | B2 |
| 8327931 | Agrawal et al. | Dec 2012 | B2 |
| 8403037 | Agrawal et al. | Mar 2013 | B2 |
| 8413727 | Holmes | Apr 2013 | B2 |
| 8425651 | Xu et al. | Apr 2013 | B2 |
| 8459347 | Stout | Jun 2013 | B2 |
| RE44385 | Johnson | Jul 2013 | E |
| 8485265 | Marya et al. | Jul 2013 | B2 |
| 8486329 | Shikai et al. | Jul 2013 | B2 |
| 8490674 | Stevens et al. | Jul 2013 | B2 |
| 8490689 | McClinton et al. | Jul 2013 | B1 |
| 8506733 | Enami et al. | Aug 2013 | B2 |
| 8528633 | Agrawal et al. | Sep 2013 | B2 |
| 8535604 | Baker et al. | Sep 2013 | B1 |
| 8573295 | Johnson et al. | Nov 2013 | B2 |
| 8579023 | Nish et al. | Nov 2013 | B1 |
| 8613789 | Han et al. | Dec 2013 | B2 |
| 8631876 | Xu et al. | Jan 2014 | B2 |
| 8663401 | Marya et al. | Mar 2014 | B2 |
| 8668762 | Kim et al. | Mar 2014 | B2 |
| 8695684 | Chen et al. | Apr 2014 | B2 |
| 8695714 | Xu | Apr 2014 | B2 |
| 8714268 | Agrawal et al. | May 2014 | B2 |
| 8715339 | Atanasoska et al. | May 2014 | B2 |
| 8723564 | Kim et al. | May 2014 | B2 |
| 8734602 | Li et al. | May 2014 | B2 |
| 8746342 | Nish et al. | Jun 2014 | B1 |
| 8770261 | Marya | Jul 2014 | B2 |
| 8776884 | Xu | Jul 2014 | B2 |
| 8789610 | Oxford | Jul 2014 | B2 |
| 8808423 | Kim et al. | Aug 2014 | B2 |
| 8852363 | Numano et al. | Oct 2014 | B2 |
| 8905147 | Fripp et al. | Dec 2014 | B2 |
| 8950504 | Xu et al. | Feb 2015 | B2 |
| 8956660 | Launag et al. | Feb 2015 | B2 |
| 8967275 | Crews | Mar 2015 | B2 |
| 8978734 | Stevens | Mar 2015 | B2 |
| 8998978 | Wang | Apr 2015 | B2 |
| 9010416 | Xu et al. | Apr 2015 | B2 |
| 9016363 | Xu et al. | Apr 2015 | B2 |
| 9016384 | Xu | Apr 2015 | B2 |
| 9022107 | Agrawal et al. | May 2015 | B2 |
| 9027655 | Xu | May 2015 | B2 |
| 9033041 | Baihly et al. | May 2015 | B2 |
| 9033060 | Xu et al. | May 2015 | B2 |
| 9044397 | Choi et al. | Jun 2015 | B2 |
| 9057117 | Harrison et al. | Jun 2015 | B2 |
| 9057242 | Mazyar et al. | Jun 2015 | B2 |
| 9068428 | Mazyar et al. | Jun 2015 | B2 |
| 9010424 | Xu | Jul 2015 | B2 |
| 9079246 | Xu et al. | Jul 2015 | B2 |
| 9080098 | Xu et al. | Jul 2015 | B2 |
| 9080403 | Xu et al. | Jul 2015 | B2 |
| 9080439 | O'Malley | Jul 2015 | B2 |
| 9089408 | Xu | Jul 2015 | B2 |
| 9090955 | Xu et al. | Jul 2015 | B2 |
| 9090956 | Xu | Jul 2015 | B2 |
| 9101978 | Xu | Aug 2015 | B2 |
| 9109429 | Xu et al. | Aug 2015 | B2 |
| 9119906 | Tomantschager et al. | Sep 2015 | B2 |
| 9127515 | Xu et al. | Sep 2015 | B2 |
| 9163467 | Gaudette et al. | Oct 2015 | B2 |
| 9181088 | Sibuet et al. | Nov 2015 | B2 |
| 9187686 | Crews | Nov 2015 | B2 |
| 9211586 | Lavernia et al. | Dec 2015 | B1 |
| 9217319 | Frazier et al. | Dec 2015 | B2 |
| 9227243 | Xu et al. | Jan 2016 | B2 |
| 9243475 | Xu | Jan 2016 | B2 |
| 9260935 | Murphree et al. | Feb 2016 | B2 |
| 9284803 | Stone et al. | Mar 2016 | B2 |
| 9309733 | Xu et al. | Apr 2016 | B2 |
| 9309744 | Frazier | Apr 2016 | B2 |
| 9366106 | Xu et al. | Jun 2016 | B2 |
| 9447482 | Kim et al. | Sep 2016 | B2 |
| 9458692 | Fripp et al. | Oct 2016 | B2 |
| 9528343 | Jordan et al. | Dec 2016 | B2 |
| 9587156 | Crews | Mar 2017 | B2 |
| 9605508 | Xu | Mar 2017 | B2 |
| 9643250 | Mazyar et al. | May 2017 | B2 |
| 9682425 | Xu et al. | Jun 2017 | B2 |
| 9689227 | Fripp et al. | Jun 2017 | B2 |
| 9689231 | Fripp et al. | Jun 2017 | B2 |
| 9789663 | Zhang et al. | Oct 2017 | B2 |
| 9790763 | Fripp et al. | Oct 2017 | B2 |
| 9802250 | Xu | Oct 2017 | B2 |
| 9803439 | Xu et al. | Oct 2017 | B2 |
| 9833838 | Mazyar et al. | Dec 2017 | B2 |
| 9835016 | Zhang et al. | Dec 2017 | B2 |
| 9863201 | Fripp et al. | Jan 2018 | B2 |
| 9925589 | Xu | Mar 2018 | B2 |
| 9926763 | Mazyar et al. | Mar 2018 | B2 |
| 9938451 | Crews | Apr 2018 | B2 |
| 9970249 | Zhang et al. | May 2018 | B2 |
| 10016810 | Salinas et al. | Jul 2018 | B2 |
| 10059092 | Welch et al. | Aug 2018 | B2 |
| 10059867 | Crews | Aug 2018 | B2 |
| 10081853 | Wilks et al. | Sep 2018 | B2 |
| 10082008 | Robey et al. | Sep 2018 | B2 |
| 10092953 | Mazyar et al. | Oct 2018 | B2 |
| 10119358 | Walton et al. | Nov 2018 | B2 |
| 10125565 | Fripp et al. | Nov 2018 | B2 |
| 10167691 | Zhang et al. | Jan 2019 | B2 |
| 10174578 | Walton et al. | Jan 2019 | B2 |
| 10202820 | Xu et al. | Feb 2019 | B2 |
| 10221637 | Xu et al. | Mar 2019 | B2 |
| 10221641 | Zhang et al. | Mar 2019 | B2 |
| 10221642 | Zhang et al. | Mar 2019 | B2 |
| 10221643 | Zhang et al. | Mar 2019 | B2 |
| 10227841 | Fripp et al. | Mar 2019 | B2 |
| 10253590 | Xu et al. | Apr 2019 | B2 |
| 10266923 | Wilks et al. | Apr 2019 | B2 |
| 10316601 | Walton et al. | Jun 2019 | B2 |
| 10329643 | Wilks et al. | Jun 2019 | B2 |
| 10335855 | Welch et al. | Jul 2019 | B2 |
| 10337086 | Wilks et al. | Jul 2019 | B2 |
| 10344568 | Murphree et al. | Jul 2019 | B2 |
| 10364630 | Xu et al. | Jul 2019 | B2 |
| 10364631 | Xu et al. | Jul 2019 | B2 |
| 10364632 | Xu et al. | Jul 2019 | B2 |
| 10450840 | Xu | Oct 2019 | B2 |
| 10472909 | Xu et al. | Nov 2019 | B2 |
| 10533392 | Walton et al. | Jan 2020 | B2 |
| 10544652 | Fripp et al. | Jan 2020 | B2 |
| 10597965 | Allen | Mar 2020 | B2 |
| 10612659 | Xu et al. | Apr 2020 | B2 |
| 10619438 | Fripp et al. | Apr 2020 | B2 |
| 10619445 | Murphree et al. | Apr 2020 | B2 |
| 10626695 | Fripp et al. | Apr 2020 | B2 |
| 10633947 | Fripp et al. | Apr 2020 | B2 |
| 10655411 | Fripp et al. | May 2020 | B2 |
| 10669797 | Johnson et al. | Jun 2020 | B2 |
| 10724321 | Leonard et al. | Jul 2020 | B2 |
| 10737321 | Xu | Aug 2020 | B2 |
| 10781658 | Kumar et al. | Sep 2020 | B1 |
| 10807355 | Welch et al. | Oct 2020 | B2 |
| 20020020527 | Kilaas et al. | Feb 2002 | A1 |
| 20020047058 | Verhoff et al. | Apr 2002 | A1 |
| 20020092654 | Coronado et al. | Jul 2002 | A1 |
| 20020104616 | De et al. | Aug 2002 | A1 |
| 20020108756 | Harrall et al. | Aug 2002 | A1 |
| 20020121081 | Cesaroni et al. | Sep 2002 | A1 |
| 20020139541 | Sheffield et al. | Oct 2002 | A1 |
| 20020197181 | Osawa et al. | Dec 2002 | A1 |
| 20030019639 | Mackay | Jan 2003 | A1 |
| 20030060374 | Cooke, Jr. | Mar 2003 | A1 |
| 20030104147 | Bretschneider et al. | Jun 2003 | A1 |
| 20030111728 | Thai et al. | Jun 2003 | A1 |
| 20030127013 | Zavitsanos et al. | Jul 2003 | A1 |
| 20030141060 | Hailey, Jr. et al. | Jul 2003 | A1 |
| 20030150614 | Brown et al. | Aug 2003 | A1 |
| 20030155114 | Pedersen et al. | Aug 2003 | A1 |
| 20031073005 | Higashi | Sep 2003 | |
| 20040005483 | Lin | Jan 2004 | A1 |
| 20040055758 | Brezinski et al. | Mar 2004 | A1 |
| 20040069502 | Luke | Apr 2004 | A1 |
| 20040089449 | Walton et al. | May 2004 | A1 |
| 20040094297 | Malone et al. | May 2004 | A1 |
| 20040154806 | Bode et al. | Aug 2004 | A1 |
| 20040159446 | Haugen et al. | Aug 2004 | A1 |
| 20040216868 | Owens, Sr. | Nov 2004 | A1 |
| 20040231845 | Cooke, Jr. | Nov 2004 | A1 |
| 20040244968 | Cook et al. | Dec 2004 | A1 |
| 20040256109 | Johnson | Dec 2004 | A1 |
| 20040261993 | Nguyen | Dec 2004 | A1 |
| 20040261994 | Nguyen et al. | Dec 2004 | A1 |
| 20050064247 | Sane et al. | Mar 2005 | A1 |
| 20050074612 | Eklund et al. | Apr 2005 | A1 |
| 20050098313 | Atkins et al. | May 2005 | A1 |
| 20050102255 | Bultman | May 2005 | A1 |
| 20050106316 | Rigney et al. | May 2005 | A1 |
| 20050161212 | Leismer et al. | Jul 2005 | A1 |
| 20050165149 | Chanak et al. | Jul 2005 | A1 |
| 20050194141 | Sinclair et al. | Sep 2005 | A1 |
| 20050235757 | De Jonge et al. | Oct 2005 | A1 |
| 20050241824 | Burris, II et al. | Nov 2005 | A1 |
| 20050241825 | Burris, II et al. | Nov 2005 | A1 |
| 20050268746 | Abkowitz et al. | Dec 2005 | A1 |
| 20050269097 | Towler | Dec 2005 | A1 |
| 20050275143 | Toth | Dec 2005 | A1 |
| 20050279427 | Park et al. | Dec 2005 | A1 |
| 20050279501 | Surjaatmadja et al. | Dec 2005 | A1 |
| 20060012087 | Matsuda et al. | Jan 2006 | A1 |
| 20060013350 | Akers | Jan 2006 | A1 |
| 20060057479 | Niimi et al. | Mar 2006 | A1 |
| 20060102871 | Wang et al. | May 2006 | A1 |
| 20060108114 | Johnson | May 2006 | A1 |
| 20060110615 | Karim et al. | May 2006 | A1 |
| 20060113077 | Willberg et al. | Jun 2006 | A1 |
| 20060116696 | Odermatt et al. | Jun 2006 | A1 |
| 20060131031 | McKeachnie | Jun 2006 | A1 |
| 20060131081 | Mirchandani et al. | Jun 2006 | A1 |
| 20060144515 | Tada et al. | Jul 2006 | A1 |
| 20060150770 | Freim, III et al. | Jul 2006 | A1 |
| 20060153728 | Schoenung et al. | Jul 2006 | A1 |
| 20060169453 | Savery et al. | Aug 2006 | A1 |
| 20060175059 | Sinclair et al. | Aug 2006 | A1 |
| 20060186602 | Martin et al. | Aug 2006 | A1 |
| 20060207387 | Soran et al. | Sep 2006 | A1 |
| 20060269437 | Pandey | Nov 2006 | A1 |
| 20060278405 | Turley | Dec 2006 | A1 |
| 20060283592 | Sierra et al. | Dec 2006 | A1 |
| 20070017675 | Hammami et al. | Jan 2007 | A1 |
| 20070134496 | Katagiri et al. | Jan 2007 | A1 |
| 20070039161 | Garcia | Feb 2007 | A1 |
| 20070044958 | Rytlewski et al. | Mar 2007 | A1 |
| 20070044966 | Davies et al. | Mar 2007 | A1 |
| 20070051521 | Fike et al. | Mar 2007 | A1 |
| 20070053785 | Hetz et al. | Mar 2007 | A1 |
| 20070054101 | Sigalas et al. | Mar 2007 | A1 |
| 20070057415 | Katagiri et al. | Mar 2007 | A1 |
| 20070062644 | Nakamura et al. | Mar 2007 | A1 |
| 20070102199 | Smith et al. | May 2007 | A1 |
| 20070107899 | Werner et al. | May 2007 | A1 |
| 20070108060 | Park | May 2007 | A1 |
| 20070131912 | Simone et al. | Jun 2007 | A1 |
| 20070151009 | Conrad, III et al. | Jul 2007 | A1 |
| 20070151769 | Slutz et al. | Jul 2007 | A1 |
| 20070181224 | Marya et al. | Aug 2007 | A1 |
| 20070187095 | Walker et al. | Aug 2007 | A1 |
| 20070207182 | Weber et al. | Sep 2007 | A1 |
| 20070221373 | Murray | Sep 2007 | A1 |
| 20070227745 | Roberts et al. | Oct 2007 | A1 |
| 20070259994 | Tour et al. | Nov 2007 | A1 |
| 20070270942 | Thomas | Nov 2007 | A1 |
| 20070284112 | Magne et al. | Dec 2007 | A1 |
| 20070299510 | Venkatraman et al. | Dec 2007 | A1 |
| 20080011473 | Wood et al. | Jan 2008 | A1 |
| 20080020923 | Debe et al. | Jan 2008 | A1 |
| 20080041500 | Bronfin | Feb 2008 | A1 |
| 20080047707 | Boney et al. | Feb 2008 | A1 |
| 20080060810 | Nguyen et al. | Mar 2008 | A9 |
| 20080081866 | Gong et al. | Apr 2008 | A1 |
| 20080093073 | Bustos et al. | Apr 2008 | A1 |
| 20080121436 | Slay et al. | May 2008 | A1 |
| 20080127475 | Griffo | Jun 2008 | A1 |
| 20080149325 | Crawford | Jun 2008 | A1 |
| 20080149345 | Marya et al. | Jun 2008 | A1 |
| 20080149351 | Marya et al. | Jun 2008 | A1 |
| 20080169130 | Norman et al. | Jul 2008 | A1 |
| 20080175744 | Motegi | Jul 2008 | A1 |
| 20080179104 | Zhang et al. | Jul 2008 | A1 |
| 20080196801 | Zhao et al. | Aug 2008 | A1 |
| 20080202764 | Clayton et al. | Aug 2008 | A1 |
| 20080202814 | Lyons et al. | Aug 2008 | A1 |
| 20080210473 | Zhang et al. | Sep 2008 | A1 |
| 20080216383 | Pierick et al. | Sep 2008 | A1 |
| 20080220991 | Slay et al. | Sep 2008 | A1 |
| 20080223587 | Cherewyk | Sep 2008 | A1 |
| 20080236829 | Lynde | Oct 2008 | A1 |
| 20080236842 | Bhavsar et al. | Oct 2008 | A1 |
| 20080248205 | Blanchet et al. | Oct 2008 | A1 |
| 20080248413 | Ishii et al. | Oct 2008 | A1 |
| 20080264205 | Zeng et al. | Oct 2008 | A1 |
| 20080264594 | Lohmueller et al. | Oct 2008 | A1 |
| 20080277980 | Koda et al. | Nov 2008 | A1 |
| 20080282924 | Saenger et al. | Nov 2008 | A1 |
| 20080296024 | Huang et al. | Dec 2008 | A1 |
| 20080302538 | Hofman | Dec 2008 | A1 |
| 20080314581 | Brown | Dec 2008 | A1 |
| 20080314588 | Langlais et al. | Dec 2008 | A1 |
| 20090038858 | Griffo et al. | Feb 2009 | A1 |
| 20090044946 | Shasteen et al. | Feb 2009 | A1 |
| 20090044955 | King et al. | Feb 2009 | A1 |
| 20090050334 | Marya et al. | Feb 2009 | A1 |
| 20090056934 | Xu | Mar 2009 | A1 |
| 20090065216 | Frazier | Mar 2009 | A1 |
| 20090068051 | Gross | Mar 2009 | A1 |
| 20090074603 | Chan et al. | Mar 2009 | A1 |
| 20090084600 | Severance | Apr 2009 | A1 |
| 20090090440 | Kellett | Apr 2009 | A1 |
| 20090107684 | Cooke, Jr. | Apr 2009 | A1 |
| 20090114381 | Stroobants | May 2009 | A1 |
| 20090116992 | Lee | May 2009 | A1 |
| 20090126436 | Fly et al. | May 2009 | A1 |
| 20090151949 | Marya et al. | Jun 2009 | A1 |
| 20090152009 | Slay et al. | Jun 2009 | A1 |
| 20090155616 | Thamida | Jun 2009 | A1 |
| 20090159289 | Avant et al. | Jun 2009 | A1 |
| 20090194745 | Tanaka | Aug 2009 | A1 |
| 20090205841 | Kluge et al. | Aug 2009 | A1 |
| 20090211770 | Nutley et al. | Aug 2009 | A1 |
| 20090226340 | Marya | Sep 2009 | A1 |
| 20090226704 | Kauppinen et al. | Sep 2009 | A1 |
| 20090242202 | Rispler et al. | Oct 2009 | A1 |
| 20090242208 | Bolding | Oct 2009 | A1 |
| 20090255667 | Clem et al. | Oct 2009 | A1 |
| 20090255684 | Bolding | Oct 2009 | A1 |
| 20090255686 | Richard et al. | Oct 2009 | A1 |
| 20090260817 | Gambier et al. | Oct 2009 | A1 |
| 20090266548 | Olsen et al. | Oct 2009 | A1 |
| 20090272544 | Giroux et al. | Nov 2009 | A1 |
| 20090283270 | Langeslag | Nov 2009 | A1 |
| 20090293672 | Mirchandani et al. | Dec 2009 | A1 |
| 20090301730 | Gweily | Dec 2009 | A1 |
| 20090308588 | Howell et al. | Dec 2009 | A1 |
| 20090317556 | Macary | Dec 2009 | A1 |
| 20090317622 | Huang et al. | Dec 2009 | A1 |
| 20100003536 | Smith et al. | Jan 2010 | A1 |
| 20100012385 | Drivdahl et al. | Jan 2010 | A1 |
| 20100015002 | Barrera et al. | Jan 2010 | A1 |
| 20100015469 | Romanowski | Jan 2010 | A1 |
| 20100025255 | Su et al. | Feb 2010 | A1 |
| 20100038076 | Spray et al. | Feb 2010 | A1 |
| 20100038595 | Imholt et al. | Feb 2010 | A1 |
| 20100040180 | Kim et al. | Feb 2010 | A1 |
| 20100044041 | Smith et al. | Feb 2010 | A1 |
| 20100051278 | Mytopher et al. | Mar 2010 | A1 |
| 20100055492 | Baroum et al. | Mar 2010 | A1 |
| 20100089583 | Xu et al. | Apr 2010 | A1 |
| 20100116495 | Spray | May 2010 | A1 |
| 20100119405 | Okamoto et al. | May 2010 | A1 |
| 20100139930 | Patel et al. | Jun 2010 | A1 |
| 20100161031 | Papirov et al. | Jun 2010 | A1 |
| 20100200230 | East, Jr. et al. | Aug 2010 | A1 |
| 20100236793 | Bjorgum | Sep 2010 | A1 |
| 20100236794 | Duan et al. | Sep 2010 | A1 |
| 20100243254 | Murphy et al. | Sep 2010 | A1 |
| 20100252273 | Duphorne | Oct 2010 | A1 |
| 20100252280 | Swor et al. | Oct 2010 | A1 |
| 20100270031 | Patel | Oct 2010 | A1 |
| 20100276136 | Evans et al. | Nov 2010 | A1 |
| 20100276159 | Mailand et al. | Nov 2010 | A1 |
| 20100282338 | Gerrard et al. | Nov 2010 | A1 |
| 20100282469 | Richard et al. | Nov 2010 | A1 |
| 20100297432 | Sherman et al. | Nov 2010 | A1 |
| 20100304178 | Dirscherl | Dec 2010 | A1 |
| 20100304182 | Facchini et al. | Dec 2010 | A1 |
| 20100314105 | Rose | Dec 2010 | A1 |
| 20100314127 | Swor et al. | Dec 2010 | A1 |
| 20100319427 | Lohbeck et al. | Dec 2010 | A1 |
| 20100326650 | Tran et al. | Dec 2010 | A1 |
| 20110005773 | Dusterhoft et al. | Jan 2011 | A1 |
| 20110036592 | Fay | Feb 2011 | A1 |
| 20110048743 | Stafford et al. | Mar 2011 | A1 |
| 20110052805 | Bordere et al. | Mar 2011 | A1 |
| 20110067872 | Agrawal | Mar 2011 | A1 |
| 20110067889 | Marya et al. | Mar 2011 | A1 |
| 20110091660 | Dirscherl | Apr 2011 | A1 |
| 20110094406 | Marya et al. | Apr 2011 | A1 |
| 20110135530 | Xu et al. | Jun 2011 | A1 |
| 20110135805 | Doucet et al. | Jun 2011 | A1 |
| 20110139465 | Tibbles et al. | Jun 2011 | A1 |
| 20110147014 | Chen et al. | Jun 2011 | A1 |
| 20110186306 | Marya et al. | Aug 2011 | A1 |
| 20110192613 | Garcia et al. | Aug 2011 | A1 |
| 20110214881 | Newton et al. | Sep 2011 | A1 |
| 20110221137 | Obi et al. | Sep 2011 | A1 |
| 20110236249 | Kim et al. | Sep 2011 | A1 |
| 20110247833 | Todd et al. | Oct 2011 | A1 |
| 20110253387 | Ervin | Oct 2011 | A1 |
| 20110259610 | Shkurti et al. | Oct 2011 | A1 |
| 20110277987 | Frazier | Nov 2011 | A1 |
| 20110277989 | Frazier | Nov 2011 | A1 |
| 20110277996 | Cullick et al. | Nov 2011 | A1 |
| 20110284232 | Huang | Nov 2011 | A1 |
| 20110284240 | Chen et al. | Nov 2011 | A1 |
| 20110284243 | Frazier | Nov 2011 | A1 |
| 20110300403 | Vecchio et al. | Dec 2011 | A1 |
| 20110314881 | Hatcher et al. | Dec 2011 | A1 |
| 20120046732 | Sillekens et al. | Feb 2012 | A1 |
| 20120067426 | Soni et al. | Mar 2012 | A1 |
| 20120080189 | Marya et al. | Apr 2012 | A1 |
| 20120090839 | Rudic | Apr 2012 | A1 |
| 20120097384 | Valencia et al. | Apr 2012 | A1 |
| 20120103135 | Xu et al. | May 2012 | A1 |
| 20120125642 | Chenault | May 2012 | A1 |
| 20120130470 | Agnew et al. | May 2012 | A1 |
| 20120145378 | Frazier | Jun 2012 | A1 |
| 20120145389 | Fitzpatrick, Jr. | Jun 2012 | A1 |
| 20120156087 | Kawabata | Jun 2012 | A1 |
| 20120168152 | Casciaro | Jul 2012 | A1 |
| 20120177905 | Seals et al. | Jul 2012 | A1 |
| 20120190593 | Soane et al. | Jul 2012 | A1 |
| 20120205120 | Howell | Aug 2012 | A1 |
| 20120205872 | Reinhardt et al. | Aug 2012 | A1 |
| 20120211239 | Kritzler et al. | Aug 2012 | A1 |
| 20120234546 | Xu | Sep 2012 | A1 |
| 20120234547 | O'Malley et al. | Sep 2012 | A1 |
| 20120247765 | Agrawal et al. | Oct 2012 | A1 |
| 20120267101 | Cooke, Jr. | Oct 2012 | A1 |
| 20120269673 | Koo et al. | Oct 2012 | A1 |
| 20120273229 | Xu et al. | Nov 2012 | A1 |
| 20120318513 | Mazyar et al. | Dec 2012 | A1 |
| 20130000985 | Agrawal et al. | Jan 2013 | A1 |
| 20130008671 | Booth | Jan 2013 | A1 |
| 20130017610 | Roberts et al. | Jan 2013 | A1 |
| 20130022816 | Smith et al. | Jan 2013 | A1 |
| 20130029886 | Mazyar et al. | Jan 2013 | A1 |
| 20130032357 | Mazyar et al. | Feb 2013 | A1 |
| 20130043041 | McCoy et al. | Feb 2013 | A1 |
| 20130047785 | Xu | Feb 2013 | A1 |
| 20130052472 | Xu | Feb 2013 | A1 |
| 20130056215 | Crews | Mar 2013 | A1 |
| 20130068411 | Forde et al. | Mar 2013 | A1 |
| 20130068461 | Maerz et al. | Mar 2013 | A1 |
| 20130084643 | Commarieu et al. | Apr 2013 | A1 |
| 20130105159 | Alvarez et al. | May 2013 | A1 |
| 20130112429 | Crews | May 2013 | A1 |
| 20130126190 | Mazyar et al. | May 2013 | A1 |
| 20130133897 | Bailhly et al. | May 2013 | A1 |
| 20130144290 | Schiffl et al. | Jun 2013 | A1 |
| 20130146144 | Joseph et al. | Jun 2013 | A1 |
| 20130160992 | Agrawal et al. | Jun 2013 | A1 |
| 20130167502 | Wilson et al. | Jul 2013 | A1 |
| 20130168257 | Mazyar et al. | Jul 2013 | A1 |
| 20130186626 | Aitken et al. | Jul 2013 | A1 |
| 20130199800 | Kellner et al. | Aug 2013 | A1 |
| 20130209308 | Mazyar et al. | Aug 2013 | A1 |
| 20132200496 | Bang | Aug 2013 | |
| 20130240200 | Frazier | Sep 2013 | A1 |
| 20130240203 | Frazier | Sep 2013 | A1 |
| 20130261735 | Pacetti et al. | Oct 2013 | A1 |
| 20130277044 | King et al. | Oct 2013 | A1 |
| 20130310961 | Intriago Velez | Nov 2013 | A1 |
| 20130048289 | Mazyar | Dec 2013 | A1 |
| 20130319668 | Tschetter et al. | Dec 2013 | A1 |
| 20130327540 | Hamid et al. | Dec 2013 | A1 |
| 20140018489 | Johnson | Jan 2014 | A1 |
| 20140020712 | Benson | Jan 2014 | A1 |
| 20140027128 | Johnson | Jan 2014 | A1 |
| 20140060834 | Quintero | Mar 2014 | A1 |
| 20140093417 | Liu | Apr 2014 | A1 |
| 20140110112 | Jordan, Jr. | Apr 2014 | A1 |
| 20140116711 | Tang | May 2014 | A1 |
| 20140124216 | Fripp et al. | May 2014 | A1 |
| 20140154341 | Manuel et al. | Jun 2014 | A1 |
| 20140186207 | Bae et al. | Jul 2014 | A1 |
| 20140190705 | Fripp | Jul 2014 | A1 |
| 20140196889 | Jordan et al. | Jul 2014 | A1 |
| 20140202284 | Kim | Jul 2014 | A1 |
| 20140202708 | Jacob et al. | Jul 2014 | A1 |
| 20140219861 | Han | Aug 2014 | A1 |
| 20140224477 | Wiese et al. | Aug 2014 | A1 |
| 20140236284 | Stinson | Aug 2014 | A1 |
| 20140271333 | Kim et al. | Sep 2014 | A1 |
| 20140286810 | Marya | Sep 2014 | A1 |
| 20140305627 | Manke | Oct 2014 | A1 |
| 20140311731 | Smith | Oct 2014 | A1 |
| 20140311752 | Streich et al. | Oct 2014 | A1 |
| 20140360728 | Tashiro et al. | Dec 2014 | A1 |
| 20140374086 | Agrawal et al. | Dec 2014 | A1 |
| 20150060085 | Xu | Mar 2015 | A1 |
| 20150065401 | Xu et al. | Mar 2015 | A1 |
| 20150102179 | McHenry et al. | Apr 2015 | A1 |
| 20150184485 | Xu et al. | Jul 2015 | A1 |
| 20150240337 | Sherman et al. | Aug 2015 | A1 |
| 20150247376 | Tolman et al. | Sep 2015 | A1 |
| 20150299838 | Doud | Oct 2015 | A1 |
| 20150354311 | Okura et al. | Dec 2015 | A1 |
| 20160024619 | Wilkes et al. | Jan 2016 | A1 |
| 20160128849 | Yan et al. | May 2016 | A1 |
| 20160201425 | Walton | Jul 2016 | A1 |
| 20160201427 | Fripp | Jul 2016 | A1 |
| 20160201435 | Fripp et al. | Jul 2016 | A1 |
| 20160209391 | Zhang et al. | Jul 2016 | A1 |
| 20160230494 | Fripp et al. | Aug 2016 | A1 |
| 20160251934 | Walton et al. | Sep 2016 | A1 |
| 20160258242 | Hayter et al. | Sep 2016 | A1 |
| 20160265091 | Walton et al. | Sep 2016 | A1 |
| 20160272882 | Stray et al. | Sep 2016 | A1 |
| 20160279709 | Xu et al. | Sep 2016 | A1 |
| 20170050159 | Xu et al. | Feb 2017 | A1 |
| 20170266923 | Guest et al. | Sep 2017 | A1 |
| 20170356266 | Arackakudiyil et al. | Dec 2017 | A1 |
| 20180010217 | Wilks et al. | Jan 2018 | A1 |
| 20180023359 | Xu | Jan 2018 | A1 |
| 20180178289 | Xu et al. | Jun 2018 | A1 |
| 20180187510 | Xu et al. | Jul 2018 | A1 |
| 20180216431 | Walton et al. | Aug 2018 | A1 |
| 20180274317 | Hall | Sep 2018 | A1 |
| 20190054523 | Wolf et al. | Feb 2019 | A1 |
| 20190093450 | Walton et al. | Mar 2019 | A1 |
| 20190203563 | Gano et al. | Jul 2019 | A1 |
| 20190249510 | Deng et al. | Aug 2019 | A1 |
| Number | Date | Country |
|---|---|---|
| 2783241 | Jun 2011 | CA |
| 2783346 | Jun 2011 | CA |
| 2886988 | Oct 2015 | CA |
| 1076968 | Oct 1993 | CN |
| 1079234 | Dec 1993 | CN |
| 1255879 | Jun 2000 | CN |
| 1668545 | Sep 2005 | CN |
| 1882759 | Dec 2006 | CN |
| 101050417 | Oct 2007 | CN |
| 101351523 | Jan 2009 | CN |
| 101381829 | Mar 2009 | CN |
| 101392345 | Mar 2009 | CN |
| 101454074 | Jun 2009 | CN |
| 101457321 | Jun 2009 | CN |
| 101605963 | Dec 2009 | CN |
| 101720378 | Jun 2010 | CN |
| 102517489 | Jun 2012 | CN |
| 102796928 | Nov 2012 | CN |
| 103343271 | Oct 2013 | CN |
| 103343271 | Oct 2013 | CN |
| 103602865 | Feb 2014 | CN |
| 103898384 | Jul 2014 | CN |
| 104004950 | Aug 2014 | CN |
| 104152775 | Nov 2014 | CN |
| 104480354 | Apr 2015 | CN |
| 201532089 | Apr 2015 | CN |
| 104651691 | May 2015 | CN |
| 10577976 | Jul 2016 | CN |
| 106086559 | Nov 2016 | CN |
| 200600343 | Jun 2006 | EA |
| 200870227 | Feb 2009 | EA |
| 0033625 | Aug 1981 | EP |
| 0400574 | May 1990 | EP |
| 0470599 | Feb 1998 | EP |
| 1006258 | Jan 2000 | EP |
| 1174385 | Jan 2002 | EP |
| 1412175 | Apr 2004 | EP |
| 1493517 | Jan 2005 | EP |
| 1798301 | Jun 2007 | EP |
| 1857570 | Nov 2007 | EP |
| 2088217 | Aug 2009 | EP |
| 912956 | Dec 1962 | GB |
| 1046330 | Oct 1966 | GB |
| 1280833 | Jul 1972 | GB |
| 1357065 | Jun 1974 | GB |
| 2095288 | Sep 1982 | GB |
| 2529062 | Feb 2016 | GB |
| H10147830 | Jun 1998 | JP |
| 2000073152 | Mar 2000 | JP |
| 2000185725 | Jul 2000 | JP |
| 2002053902 | Feb 2002 | JP |
| 2004154837 | Jun 2004 | JP |
| 2004225084 | Aug 2004 | JP |
| 2004225765 | Aug 2004 | JP |
| 2005076052 | Mar 2005 | JP |
| 2008266734 | Nov 2008 | JP |
| 2008280565 | Nov 2008 | JP |
| 2009144207 | Jul 2009 | JP |
| 2010502840 | Jan 2010 | JP |
| 2012197491 | Oct 2012 | JP |
| 2013019030 | Jan 2013 | JP |
| 2014043601 | Mar 2014 | JP |
| 20130023707 | Mar 2013 | KR |
| 2373375 | Jul 2006 | RU |
| 9111587 | Aug 1881 | WO |
| 1990002655 | Mar 1990 | WO |
| 1992013978 | Aug 1992 | WO |
| 9857347 | Dec 1998 | WO |
| 9909227 | Feb 1999 | WO |
| 1999027146 | Jun 1999 | WO |
| 9947726 | Sep 1999 | WO |
| 2001001087 | Jan 2001 | WO |
| 2004001087 | Dec 2003 | WO |
| 2004073889 | Sep 2004 | WO |
| 2005065281 | Jul 2005 | WO |
| 2007044635 | Apr 2007 | WO |
| 2007095376 | Aug 2007 | WO |
| 2008017156 | Feb 2008 | WO |
| 2008034042 | Mar 2008 | WO |
| 2008057045 | May 2008 | WO |
| 2008079485 | Jul 2008 | WO |
| 2008079777 | Jul 2008 | WO |
| 2008142129 | Nov 2008 | WO |
| 2009055354 | Apr 2009 | WO |
| 2009079745 | Jul 2009 | WO |
| 2009093420 | Jul 2009 | WO |
| 2010012184 | Feb 2010 | WO |
| 2010038016 | Apr 2010 | WO |
| 2010083826 | Jul 2010 | WO |
| 2010110505 | Sep 2010 | WO |
| 2011071902 | Jun 2011 | WO |
| 2011071907 | Jun 2011 | WO |
| 2011071910 | Jun 2011 | WO |
| 2011130063 | Oct 2011 | WO |
| 2012015567 | Feb 2012 | WO |
| 2012071449 | May 2012 | WO |
| 2012091984 | Jul 2012 | WO |
| 2012149007 | Nov 2012 | WO |
| 2012164236 | Dec 2012 | WO |
| 2012174101 | Dec 2012 | WO |
| 2012175665 | Dec 2012 | WO |
| 2013019410 | Feb 2013 | WO |
| 2013019421 | Feb 2013 | WO |
| 2013053057 | Apr 2013 | WO |
| 2013078031 | May 2013 | WO |
| 2013109287 | Jul 2013 | WO |
| 2013122712 | Aug 2013 | WO |
| 201354634 | Oct 2013 | WO |
| 2014100141 | Jun 2014 | WO |
| 2014113058 | Jul 2014 | WO |
| 2014121384 | Aug 2014 | WO |
| 2014210283 | Dec 2014 | WO |
| 2015142862 | Sep 2015 | WO |
| 2015171126 | Nov 2015 | WO |
| 2015171585 | Nov 2015 | WO |
| 2016024974 | Feb 2016 | WO |
| 2016032490 | Mar 2016 | WO |
| 2016032493 | Mar 2016 | WO |
| 2016032620 | Mar 2016 | WO |
| 2016032621 | Mar 2016 | WO |
| 2016032758 | Mar 2016 | WO |
| 2016032761 | Mar 2016 | WO |
| 2016036371 | Mar 2016 | WO |
| 2016085798 | Jun 2016 | WO |
| 2016165041 | Oct 2016 | WO |
| 2020018110 | Jan 2020 | WO |
| 2020109770 | Jun 2020 | WO |
| Entry |
|---|
| The Declaration of Dana J. Medlin, Ph.D., P.E., FASM Under 37 C.F.R. § 1.68 In Support of Petition for Inter Partes Review of U.S. Pat. No. 9,903,010; Dated Sep. 11, 2020. (Year: 2020). |
| Saravanan et al., “Fabrication and characterization of pure magnesium-30 vol. SiCP particle composite”, Material Science and Eng., vol. 276, pp. 108-116 (2000). |
| Song et al., Texture evolution and mechanical properties of AZ31B magnesium alloy sheets processed by repeated unidirectional bending, Journal of Alloys and Compounds, vol. 489, pp. 475-481 (2010). |
| Blawert et al., “Magnesium secondary alloys: Alloy design for magnesium alloys with improved tolerance limits against impurities”, Corrosion Science, vol. 52, No. 7, pp. 2452-2468 (Jul. 1, 2010). |
| Wang et al., “Effect of Ni on microstructures and mechanical properties of AZ1 02 magnesium alloys” Zhuzao Foundry, Shenyang Zhuzao Yanjiusuo, vol. 62, No. 1, pp. 315-318 (Jan. 1, 2013). |
| Kim et al., “Effect of aluminum on the corrosions characteristics of Mg—4Ni—xAl alloys”, Corrosion, vol. 59, No. 3, pp. 228-237 (Jan. 1, 2003). |
| Unsworth et al., “A new magnesium alloy system”, Light Metal Age, vol. 37, No. 7-8., pp. 29-32 (Jan. 1, 1979). |
| Geng et al., “Enhanced age-hardening response of Mg—Zn alloys via Co additions”, Scripta Materialia, vol. 64, No. 6, pp. 506-509 (Mar. 1, 2011). |
| Zhu et al., “Microstructure and mechanical properties of Mg6ZnCuO.6Zr (wt.%) alloys”, Journal of Alloys and Compounds, vol. 509, No. 8, pp. 3526-3531 (Dec. 22, 2010). |
| International Search Authority, International Search Report and Written Opinion for PCT/GB2015/052169 (dated Feb. 17, 2016). |
| Search and Examination Report for GB 1413327.6 (dated Jan. 21, 2015). |
| Magnesium Elektron Test Report (Mar. 8, 2005). |
| New England Fishery Management Counsel, “Fishery Management Plan for American Lobster Amendment 3” (Jul. 1989). |
| Emly, E.F., “Principles of Magnesium Technology” Pergamon Press, Oxford (1966). |
| Shaw, “Corrosion Resistance of Magnesium Alloys”, ASM Handbook, vol. 13A, pp. 692-696 (2003). |
| Hanawalt et al., “Corrosion studies of magnesium and its alloys”, Metals Technology, Technical Paper 1353 (1941). |
| The American Foundry Society, Magnesium alloys, casting source directory 8208, available at www.afsinc.org/files/magnes.pdf. |
| Rokhlin, “Magnesium alloys containing rare earth metals structure and properties”, Advances in Metallic Alloys, vol. 3, Taylor & Francis (2003). |
| Ghali, “Corrosion Resistance of Aluminum and Magnesium Alloys” pp. 382-389, Wiley Publishing (2010). |
| Kim et al., “High Mechanical Strengths of Mg—Ni—Y and MG—Cu Amorphous Alloys with Significant Supercooled Liquid Region”, Materials Transactions, vol. 31, No. 11, pp. 929-934 (1990). |
| Tekumalla et al., “Mehcanical Properties of Magnesium-Rare Earth Alloy Systems”, Metals, vol. 5, pp. 1-39 (2014). |
| Corrected (Non-Truncated) Machine Translation of CN103898384 (originally submitted in Information Disclosure Statement filed Aug. 19, 2020). |
| Corrected (Non-Truncated) Machine Translation of KR 20130023707 (originally cited in Information Disclosure Statement filed Aug. 19, 2020). |
| Corrected (Non-Truncated) Machine Translation of CN 103602865 (originally cited in Information Disclosure Statement filed Aug. 19, 2020). |
| Corrected (Non-Truncated) Machine Translation of CN101381829 (originally cited in Information Disclosure Statement filed Aug. 19, 2020). |
| Corrected (Non-Truncated) Machine Translation of CN102518489 (originally cited in Information Disclosure Statement filed Aug. 19, 2020). |
| Corrected (Non-Truncated) Machine Translation of CN 103343271 (originally cited in Information Disclosure Statement filed Aug. 19, 2020). |
| Corrected (Non-Truncated) Machine Translation of CN 102796928 (originally cited in Information Disclosure Statement filed Aug. 19, 2020). |
| Corrected (Non-Truncated) Machine Translation of JP2008266734 (originally cited in Information Disclosure Statement filed Aug. 19, 2020 ). |
| Corrected (Non-Truncated) Machine Translation of JP2012197491 (originally cited in Information Disclosure Statement filed Aug. 19, 2020). |
| Corrected (Non-Truncated) Machine Translation of JP2013019030 (originally cited in Information Disclosure Statement filed Aug. 19, 2020). |
| Corrected (Non-Truncated) Machine Translation of JP2014043601 (originally cited in Information Disclosure Statement filed Aug. 19, 2020). |
| Corrected (Non-Truncated) Machine Translation of CN104004950 (originally cited in Information Disclosure Statement filed Aug. 19, 2020). |
| Corrected (Non-Truncated) Machine Translation of CN104651691 (originally cited in Information Disclosure Statement filed Aug. 19, 2020). |
| Ye et al., “Review of recent studies in magnesium matrix composites”, Journal of Material Science, vol. 39, pp. 6153-6171 (2004). |
| Hassan et al., “Development of a novel magnesium-copper based composite with improved mechanical properties”, Materials Research Bulletin, vol. 37, pp. 377-389 (2002). |
| Ye et al., “Microstructure and tensile properties of Ti6A14V/AM60B magnesium matrix composite”, Journal of Alloys and Composites, vol. 402, pp. 162-169 (2005). |
| Kumar et al., “Mechanical and Tribological Behavior of Particulate Reinforced Aluminum metal Matrix Composite”, Journal of Minerals & Materials Characterization and Engineering, vol. 10, pp. 59-91 (2011). |
| Majumdar, “Micromechanics of Discontinuously Reinforced MMCs”, Engineering Mechanics and Analysis of Metal-Matrix Composites, vol. 21, pp. 395-406. |
| Machine Translation of CN103898384 (originally cited in Information Disclosure Statement filed Jun. 24, 2020). |
| Machine Translation of KR 20130023707 (originally cited in Information Disclosure Statement filed Jun. 24, 2020). |
| Machine Translation of CN103602865 (originally cited in Information Disclosure Statement filed Jun. 24, 2020). |
| Machine Translation of CN101381829 (originally cited in Information Disclosure Statement filed Jun. 23, 2020). |
| Machine Translation of CN102518489 (originally cited in Information Disclosure Statement filed Jun. 23, 2020). |
| Machine Translation of CN 103343271 (originally cited in Information Disclosure Statement filed Jun. 23, 2020). |
| Machine Translation of CN102796928 (originally cited in Information Disclosure Statement filed Jun. 23, 2020). |
| Machine Translation of JP2008266734 (originally cited in Information Disclosure Statement filed Jun. 23, 2020). |
| Machine Translation of JP2012197491 (originally cited in Information Disclosure Statement filed Jun. 23, 2020). |
| Machine Translation of JP2013019030 (originally cited in Information Disclosure Statement filed Jun. 23, 2020). |
| Machine Translation of JP2014043601 (originally cited in Information Disclosure Statement filed Jun. 23, 2020). |
| Machine Translation of CN10465191. |
| Machine Translation of CN 104004950. |
| Hassan et al., “Development of high strength magnesium based composites using elemental nickel particulates as reinforcement”, Journal of Materials Science, vol. 37, pp. 2467-2474 (2002). |
| Metals Handbook, Desk Edition, edited by J.R. Davis, published by ASM International, pp. 559-574 (1998). |
| Sigworth et al. “Grain Refinement of Aluminum Castings Alloys” American Foundry Society; Paper 07-67; pp. 5-7 (2007). |
| Momentive, “Titanium Diborid Powder” condensed product brochure; retrieved from https:/www.momentive.com/WorkArea/DownloadAsset.aspx?id+27489.; p. 1 (2012). |
| Durbin, “Modeling Dissolution in Aluminum Alloys” Dissertation for Georgia Institute of Technology; retrieved from https://smartech;gatech/edu/bitstream/handle/1853/6873/durbin_tracie_L_20- 0505_phd.pdf> (2005). |
| Pegeut et al.., “Influence of cold working on the pitting corrosion resistance of stainless steel” Corrosion Science, vol. 49, pp. 1933-1948 (2007). |
| Elemental Charts from chemicalelements.com; retrieved Jul. 27, 2017. |
| Song et al., “Corrosion Mechanisms of Magnesium Alloys” Advanced Engg Materials, vol. 1, No. 1 (1999). |
| Zhou et al., “Tensile Mechanical Properties and Strengthening Mechanism of Hybrid Carbon Nanotubes . . . ” Journal of Nanomaterials, 2012; 2012:851862 (doi: 10.1155/2012/851862) Figs. 6 and 7. |
| Trojanova et al., “Mechanical and Acoustic Properties of Magnesium Alloys . . . ” Light Metal Alloys Application, Chapter 8, Published Jun. 11, 2014 (doi: 10.5772/57454) p. 163, para. [0008], [0014-0015]; [0041-0043]. |
| AZoNano “Silicon Carbide Nanoparticles-Properties, Applications” http://www.amazon.com/articles.aspx?ArticleD=3396) p. 2, Physical Properties, Thermal Properties (May 9, 2013). |
| AZoM “Magnesium AZ91D-F Alloy” http://www.amazon.com/articles.aspx?ArticleD=8670) p. 1, Chemical Composition; p. 2 Physical Properties (Jul. 31, 2013. |
| Elasser et al., “Silicon Carbide Benefits and Advantages . . . ” Proceedings of the IEEE, 2002; 906(6):969-986 (doi: 10.1109/JPROC.2002.1021562) p. 970, Table 1. |
| Lan et al., “Microstructure and Microhardness of SiC Nanoparticles . . . ” Materials Science and Engineering A; 386:284-290 (2004). |
| Casati et al., “Metal Matrix Composites Reinforced by Nanoparticles”, vol. 4:65-83 (2014). |
| Scharf et al., “Corrosion of AX 91 Secondary Magnesiunm Alloy”, Advanced Engineering Materials, vol. 7, No. 12, pp. 1134-1142 (2005). |
| Hillis et al., “High Purity Magnesium AM60 Alloy: The Critical Contaminant Limits and the Salt Water Corrosion Performance”, SAE Technical Paper Series (1986). |
| Pawar, S.G , “Influence of Microstructure on the Corrosion Behaviour of Magnesium Alloys”, PhD Dissertation, University of Manchester (2011). |
| Czerwinski, “Magnesium Injection Molding”; Technology & Engineering; Springer Science + Media, LLC, pp. 107-108, (Dec. 2007). |
| National Physical Laboratory, “Bimetallic Corrosion” Crown (C) p. 1-14 (2000). |
| Shimizu et al., “Multi-walled carbon nanotube-reinforced magnesium alloy composites”, Scripta Materialia, vol. 58, pp. 267-270 (2008). |
| Zhan et al., “Single-wall carbon nanotubes as attractive toughening agents in alumina-based nanocomposites”, Mature Materials, vol. 2, pp. 38-42 (Jan. 2003). |
| Curtin et al., “CNT-reinforced ceramics and metals”, Materials Today, vol. 7, pp. 44-49 (2004). |
| Pardo et al., “Corrosion behavior of magnesium/aluminum alloys in 3.5 wt.% NaCl”, Corrosion Science, vol. 50, pp. 823-834 (2008). |
| Song et L., “Influence of microstructure on the corrosion of diecast AZ91D”, Corrosion Science, vol. 41, pp. 249-273 (1999). |
| Watarai, “Trend of Research and Development for Magnesium Alloys—Reducing the Weight of Structural Materials in Motor Vehicles”, Science & Technology Trends, Quarterly Review, No. 18, pp. 84-97 (Jan. 2006). |
| Saravanan et al., “Mechanically Alloyed Carbon Nanotubes (CNT) Reinforced Nanocrystalline AA 4032: Synthesis and Characterization”, Journal of Minerals & Materials Characterization & Engineering, vol. 9, No. 11, pp. 1027-1035 (2010). |
| Tsipas et al., “Effect of high energy ball milling on titanium-hydroxyapatite powders”, Powder Metallurgy, vol. 46, No. 1 pp. 73-77 (2003). |
| Xie et al., “TEM Observation of Interfaces between Particles in Al—Mg Powder Compacts Prepared by Pulse Electric Current Sintering”, Materials Transactions, vol. 43, No. 9, pp. 2177-2180 (2002). |
| Elsayed et al., “Effect of Consolidation and Extrusion Temperatures on Tensile Properties of Hot Extruded ZK61 Magnesium Alloy Gas Atomized Powders via Spark Plasma Sintering”, Tranasctions of JWRI, vol. 38, No. 2, p. 31. |
| Shigematsu et al., “Surface treatment of AZ91D magnesium alloy by aluminum diffusion coating”, Journal of Materials Science Letters, vol. 19, pp. 473-475 (2000). |
| Spencer et al., “Fluidized Bed Polymer Particle ALD Process for Producing HDPE/Alumina Nanocomposites”, 12th International Conference on Fluidization, vol. RP4 (2007). |
| Maisano, “Cryomilling of Aluminum-Based and Magnesium-Based Metal Powders”, Thesis, Virginia Tech (Jan. 2006). |
| Walters et al., “A Study of Jets from Unsintered-Powder Metal Lined Nonprecision Small-Caliber Shaped Charges”, Army Research Laboratory, Aberdeen Proving Group, MC 21005-5066 (Feb. 2001). |
| Ashby, “Teach Yourself Phase Diagrams and Phase Transformations”, Cambridge, 5th Edition, pp: unknown (Mar. 2009). |
| Callister, Materials Science and Engineering An Introduction:, 6th Edition, New York, pp: unknown (2003). |
| Hanson et al. Constitution of Binary Alloys:, McGraw-Hill Book Co. Inc., pp: unknown (1958). |
| MSE 2090: Introduction to Materials Science, Chapter 9, pp: unknown (date unknown). |
| Metals Handbook, “Metallography, Structures and Phase Diagrams”, Aluminum-Magnesium, American Society For Metals, 8th Edition, vol. 8, pp: unknown (1973). |
| Metals Handbook, “Metallography, Structures and Phase Diagrams”, Magnesium-Nickel, American Society For Metals, 8th Edition, vol. 8, pp: unknown (1973). |
| Principles and Prevention of Corrosion, “Volts versus saturated calomel reference electrobe”, D.A. Jones, p. 170 (1996). |
| Medlin, “Mass Balance”, handwritten notes (Nov. 2020). |
| Metals Handbook, “Metallography, Structures and Phase Diagrams”, Aluminum-Iron, American Society For Metals, 8th Edition, vol. 8, p. 260 (1973). |
| Metals Handbook, “Metallography, Structures and Phase Diagrams”, Aluminum-Nickel, American Society For Metals, 8th Edition, vol. 8, p. 261 (1973). |
| Metals Handbook, “Metallography, Structures and Phase Diagrams”, Aluminum-Copper, American Society For Metals, 8th Edition, vol. 8, p. 259 (1973). |
| Metals Handbook, “Metallography, Structures and Phase Diagrams”, Silver-Aluminum, American Society For Metals, 8th Edition, vol. 8, p. 252 (1973). |
| Medlin, Declaration of Dona J. Medlin Ph.D., P.E., FASM Under 37 CFR Section 1.68 in Support of Petition For Inter Partes Review of U.S. Pat. No. 9,903,010 (Sep. 2020). |
| Li, Qiang, “Translation Declaration and Translation of China Patent Publication No. 103343271” (Jun. 2020). |
| Ho et al., The mechanical behavior of magnesium alloy AZ91 reinforced with fine copper particulates:, Materials Science and Engineering A369, pp. 302-308 (2004). |
| Trojanova et al., “Mechanical and fracture properties of an AZ91 Magnesium alloy reinforced by Si and SiC particles”, Composites Science and Technology, vol. 69, pp. 2256-2264 (2009). |
| Lin et al., “Formation of Magnesium Metal Matrix Composites Al2O3p/AZ91D and Their Mechanical Properties After Heat Treatment” Acta Metallurgica Slovaca, vol. 16, pp. 237-245 (2010). |
| United States District Court/Northern District of Ohio/Eastern Division, Supplemental Declaration of Dana J. Medlin, Ph.D. in Support of Opposition to Terves LLC'S Motion for Preliminary Injunction in related Case 1:19-CV-1611 (filedOct. 15, 2020). |
| United States District Court/Northern District of Ohio/Eastern Division, Declaration of Andrew Sherman in Support of Terves' Preliminary Injunction Motion in related Case 1:19-CV-1611 (filed May 1, 2020). |
| Hemanth, “Fracture Behavior of Cryogenically solidifed aluminum-alloy reinforced with Nano-ZrO2 Metal Matrix Composites (CNMMCs)”, Journal of Chemical Engineering and Materials Science, vol. 2(8), pp. 110-121 (Aug. 2011). |
| United States District Court/Northern District of Ohio/Eastern Division, Memorandum Opinion and Order in related Case 1:19-CV-1611 (issued Mar. 29, 2021). |
| United States District Court/Northern District of Ohio/Eastern Division, Second Rebuttal Rule 26 Report of Lee A. Swanger, Ph D., P.E. in related Case 1:19-CV-1611 (filed Nov. 24, 2020). |
| U.S. Patent and Trademark Office, Declaration of Dana J. Medlin in Support of Request for Ex Parte Reexamination of U.S. Appl. No. 10/329,653 (filed Jul. 6, 2021). |
| Number | Date | Country | |
|---|---|---|---|
| 20190054523 A1 | Feb 2019 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61981425 | Apr 2014 | US | |
| 62569004 | Oct 2017 | US | |
| 61942879 | Feb 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14627236 | Feb 2015 | US |
| Child | 15294957 | US | |
| Parent | 16149637 | US | |
| Child | 15294957 | US | |
| Parent | 14689295 | Apr 2015 | US |
| Child | 15641439 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15294957 | Oct 2016 | US |
| Child | 16149637 | US | |
| Parent | 15641439 | Jul 2017 | US |
| Child | 16149637 | US |