Patent Grant
7745540
1. Field of the Invention
The present invention is concerned with new anti-reflective compositions and via fill compositions for use in the manufacture of microelectronic devices. These compositions include a dendritic polymer dispersed or dissolved in a solvent system.
2. Description of the Prior Art
1. Anti-reflective Coatings
Integrated circuit manufacturers are consistently seeking to maximize substrate wafer sizes and minimize device feature dimensions in order to improve yield, reduce unit case, and increase on-chip computing power. Device feature sizes on silicon or other chips are now submicron in size with the advent of advanced deep ultraviolet (DUV) microlithographic processes.
However, a frequent problem encountered by photoresists during the manufacturing of semiconductor devices is that activating radiation is reflected back into the photoresist by the substrate on which it is supported. Such reflectivity tends to cause blurred patterns which degrade the resolution of the photoresist. Degradation of the image in the processed photoresist is particularly problematic when the substrate is non-planar and/or highly reflective. One approach to address this problem is the use of an anti-reflective coating applied to the substrate beneath the photoresist layer.
In the semiconductor industry, two broad types of bottom anti-reflective coatings have been used: organic and inorganic. Inorganic bottom anti-reflective coatings like SiON and TiN are deposited by plasma-enhanced, chemical vapor deposition techniques (PEVCD). These inorganic films are conformal and difficult to remove after the photolithography step. On the other hand, organic bottom anti-reflective coatings are planarizing, are deposited by a cost-effective spin-coating process, and can be easily removed by dry etching or stripping using wet chemicals.
Organic bottom anti-reflective coatings are formulated based on linear chain polymers which have crosslinkable sites. Light attenuating chromophores are grafted to these linear polymers to absorb light at the exposure wavelengths. For example, linear chain acrylate polymers have been used as the basic structure to formulate bottom anti-reflective coatings. Aliphatic polyester polymers have also been used. One major drawback of linear chain polymers, however, is that they undergo chain entanglements, leading to poor flow properties, particularly when used as fill compositions as discussed below.
2. Fill Compositions
The damascene process, or the process of forming inlaid metal patterning in preformed grooves, is generally a preferred method of fabricating interconnections for integrated circuits. In its simplest form, the dual damascene process starts with an insulating layer which is first formed on a substrate and then planarized. Horizontal trenches and vertical holes (i.e., the contact and via holes) are then etched into the insulating layer corresponding to the required metal line pattern and hole locations that will descend down through the insulating layer to the device regions (if through the first insulating layer, i.e., a contact hole) or to the next metal layer down (if through an upper insulating layer in the substrate structure, i.e., a via hole). Metal is next deposited over the substrate, thereby filling the trenches and the holes and forming the metal lines and interconnect holes simultaneously, As a final step, the resulting surface is planarized (e.g., by the known chemical-mechanical polish (CMP) technique) and readied to accept another damascene structure.
During the dual damascene process, the contact and via holes are typically etched to completion prior to the trench etching. Thus, the step of trench etching exposes the bottom and sidewalls (which are formed of the insulating or dielectric layer) of the contact or via holes to over-etch which can deteriorate contact with the base layer. An organic material is typically used to partially or completely fill the via or contact holes and to protect the bottom and sidewalls from further etch attack. These organic fill materials can also serve as a bottom anti-reflective coating (as discussed above) to reduce or eliminate pattern degradation and linewidth variation in the patterning of the trench layer, provided the fill material covers the surface of the dielectric layer.
Fill materials which have high optical density at the typical exposure wavelengths have been used for the past several years. However, most prior art materials have limited fill properties. For example, when the prior art compositions are applied to the via or contact holes formed within the substrate, the films formed by the compositions tend to be quite thin on the substrate surface immediately adjacent the holes, thus leading to undesirable light reflection during subsequent exposure steps. Also, the flow properties of the composition tend to be lacking in that the composition does not completely flow into via and contact holes, resulting in inadequate protection of those holes.
There is a need in the art for contact or via hole fill materials which provide complete coverage at the top of via and contact holes. Furthermore, this material should properly flow into the via and contact holes to protect the base during etching and prevent degradation of the barrier layer and damage to the underlying metal conductors.
The present invention is broadly concerned with new anti-reflective or fill compositions and methods of using those compositions to protect substrates, and particularly contact and via holes formed therein, during circuit manufacturing.
In more detail, the compositions comprise a dendritic polymer dispersed or dissolved in a solvent system. Preferred dendritic polymers include both dendrimers and hyperbranched polymers. It is particularly preferred that the dendritic polymer have a viscosity of less than about 150×103 cP, and more preferably from about 7×103 to about 110×103 cP. The average molecular weight (as determined by Gel Permeation Chromatograplly/Size Exclusion Chromatography) of the dendrtic polymer is preferably less than about 15,000 g/mole, more preferably from about 800-5,200 g/mole, and more preferably from about 1,500-5,200 g/mole.
In one embodiment, the dendritic polymer should have a hydroxyl number (as determined by ASTM E-222) of at least about 100 mg KOH/g of dendritic polymer, preferably from about 300-600 mg KOH/g of dendritic polymer, and more preferably from about 500-600 ing KOH/g of dendritic polymer.
Particularly preferred dendritic polymers include those selected from the group consisting of dendritic polyesters, dendritic polyols, dendritic polyethers, dendritic polyamines, dendritic carboxylic acids, and mixtures thereof.
The inventive compositions generally have an overall solids content of from about 0.5-10% and can be prepared by simply dissolving or dispersing the dendritic polymer in a suitable solvent system. The solvent system should have a boiling point of from about 100-200° C., and preferably from about 120-170° C. The amount of dendritic polymer dissolved in the solvent system is from about 0.2-10% by weight dendritic polymer, preferably from about 2-7% by weight dendritic polymer, and more preferably from about 3-6% by weight dendritic polymer, based upon the total weight of the composition taken as 100% by weight.
The solvent system should be utilized at a level of from about 90-99% by weight, preferably from about 93-98% by weight, and more preferably from about 94-97% by weight, based upon the total weight of the composition taken as 100% by weight. Preferred solvent systems include a solvent selected from the group consisting of propylene glycol monomethyl ether (PGME), propylene glycol monomethyl ether acetate (PGMEA), ethyl lactate, propylene glycol n-propyl ether (PnP), cyclohexanone, tetrahydrofuran (THF), dimethyl formamide (DMF), γ-butyrolactone, 2-heptanone, N-methylpyrollidinone, and mixtures thereof.
Preferably, the inventive compositions further comprise a compound selected from the group consisting of crosslinking agents, catalysts, light attenuating compounds, and mixtures thereof. Preferred crosslinking agents include those selected from the group consisting of melamines and glycourils (e.g., POWDERLINK® 1174, Cymel® products), multifunctional epoxy resins (e.g., MY720, CY179MA, DENACOL), anhydrides, and mixtures thereof. The crosslinking agent should be present in the composition at a level of from about 0.2-5% by weight, and preferably from about 0.5-3% by weight, based upon the total weight of the composition taken as 100% by weight. Thus, the compositions of the invention should crosslink at a temperature of from about 100-250° C., and more preferably from about 150-205° C.
Preferred catalysts include sulfonic acids (e.g., p-toluenesulfonic acid, styrene sulfonic acid), thermal acid generators (e.g., pyridinium tosylate), carboxylic acids (e.g., trichloroacetic acid, benzene tetracarboxylic acid), sulfonates (e.g., pyridinium trifluoromethanesulfonate, pyridinium 3-nitrobenzenesulfonate), and mixtures thereof. The catalyst should be present in the composition at a level of from about 0.2-1% by weight, and preferably from about 0.3-0.6% by weight, based upon the total weight of the composition taken as 100% by weight.
Preferred light attenuating compounds include those selected from the group consisting of anthracenes (e.g., 9-anthracene carboxylic acid, 9-hydroxy methyl anthracene), naphthalenes (e.g., 3-hydroxy-2-naphthoic acid, 1,4-dihydroxy-2-naphthoic acid), phenyls (e.g. 4-hydroxybenzoic acid, 3,4-hydroxy benzoic acid), and mixtures thereof. The light attenuating compound should be present in the composition at a level of from about 0.5-4% by weight, and preferably from about 1-2% by weight, based upon the total weight of the composition taken as 100% by weight.
The method of applying the anti-reflective or fill compositions to a substrate having a contact or via hole simply comprises applying a quantity of a composition hereof to the substrate surfaces forming the hole by any conventional application method (including spincoating). Advantageously the inventive compositions will have low viscosities (e.g., less than about 10 cP, more preferably from about 2-7 cP, and ever more preferably from about 3-5 cP) at this stage, thus providing superior coverage.
After the desired coverage is achieved, the resulting fill composition layer should be heated to at least about the crosslinking temperature (e.g., from about 100-250° C.) of the composition so as to cure the layer. Because of the superior coverage and flow properties of the present inventive composition, the thickness of the cured fill material layer on the surface of the substrate adjacent the edge of the contact or via hole will be at least about 50%, preferably at least about 55%, and more preferably at least about 65% of the thickness of the film on the substrate surface a distance away from the edge of the contact or via hole approximately equal to the diameter of the hole, even with hole diameters as small as about 0.1-0.2 μm in diameter and/or about 0.5-0.8 μm in depth.
Cured compositions according to the invention exhibit particularly good properties at wavelengths of less than about 400 nm. For example, they have high etch rates. The cured compositions have an etch selectivity to resist (i.e., the anti-reflective coating layer etch rate divided by the photoresist etch rate) of at least about 1.1, and preferably at least about 1.2, when CF4 is used as the etchant. Additionally, at 193 nm and 248 nm exposure wavelengths, the cured compositions can form layers having a k value (i.e., the imaginary component of the complex index of refraction) of at least about 0.3, and preferably at least about 0.4, and an n value (i.e., the real component of the complex index of refraction) of at least about 1.0, and preferably at least about 1.5 at film thicknesses of from about 150-190 μm.
Furthermore, the cured coatings according to the invention will be substantially insoluble in typical photoresist solvents. Thus, when subjected to a stripping test, the inventive anti-reflective coating layers will have a percent stripping of less than about 5%, preferably less than about 1%, and even more preferably about 0%. The stripping test involves first determining the thickness (by taking the average of measurements at five different locations) of a cured film. This is the average initial film thickness. Next, a solvent (e.g., ethyl lactate) is puddled onto the cured film for about 10 seconds, followed by spin drying at about 2,000-3,500 rpm for about 20-30 seconds to remove the solvent. The film thickness is measured again at five different points on the wafer using ellipsometry, and the average of these measurements is determined. This is the average final film thickness.
The amount of stripping is the difference between the initial and final average film thicknesses. The percent stripping is:
A photoresist can be applied to the cured material, followed by drying (soft bake), exposing, post-exposure baking, and developing the photoresist. Following the methods of the invention will yield precursor structures for dual damascene and other microlithographic processes which have the foregoing desirable properties.
Polymeric architectures can be divided into different types. One type of polymeric architecture is the dendritic macromolecules. Dendritic molecules can be divided into two subtypes—dendrimers and hyperbranched polymers. Dendrimers are symmetrical and globular structures (i.e., they're monodisperse, tree-like structures) which have well-defined branches radiating from a central core. The structure becomes more branched and crowded at the outer periphery thereof.
Hyperbranched polymers also have a fractal pattern of chemical bonds, but the branches of hyperbranched polymers don't radiate from a central core (i.e., they're polydisperse). Furthermore, hyperbranched polymers have a degree of branching that is less than <1.
Dendritic polymers are different from linear polymers in that they don't have entangled chains, and they have numerous side chains which can be functionalized. The advantages of dendritic polymers include their low hydrodynamic volumes and the compactness of the high generations of these macromolecules.
The following examples set forth preferred methods in accordance with the invention. It is to be understood, however, that these examples are provided by way of illustration and nothing therein should be taken as a limitation upon the overall scope of the invention.
In this example, a gap fill material was prepared by mixing 5.65% by weight of BOLTORN H40 (a hyperbranched polymer having a molecular weight of 5100 g/mole and available from Perstorp Specialty Chemicals AB, Sweden), 0.05% by weight of CYMEL 303LF (a crosslinking agent available from Cytec Industries), 1.31% by weight of POWDERLINK 1174 (a crosslinking agent available from Cytec Industries), 0.018% by weight of p-toluenesulfonic acid (pTSA), 0.32% by weight of Bisphenol-A, 91.652% by weight of propylene glycol monomethyl ether (PGME), and 1.0% by weight of propylene glycol monomethyl ether acetate (PGMEA). The solution was coated onto a silicon wafer at 1500 rpm for 60 seconds and then baked at 205° C. for 60 seconds. The film thickness was 190 nm measured on an ellipsometer. The refractive index, n, was 1.60 at a wavelength of 248 nm and 1.71 at a wavelength of 193 nm. The extinction coefficient, k, was 0.00 at a wavelength of 248 nm and 0.05 at a wavelength of 193 nm.
In this example, a gap fill material was prepared by mixing 5.65% by weight of BOLTORN H20 (a hyperbranched polymer having a molecular weight of 5100 g/mole and available from Perstorp Specialty Chemicals AB, Sweden), 0.05% by weight of CYMEL 303LF, 1.31% by weight of POWDERLINK 1174, 0.018% by weight of pTSA, 0.32% by weight of Bisphenol-A, 91.652% by weight of PGME, and 1.0% by weight of PGMEA. The solution was coated onto a silicon wafer at 1500 rpm for 60 seconds and then baked at 205° C. for 60 seconds. The film thickness was 183 nm measured on an ellipsometer. The refractive index, n, was 1.60 at a wavelength of 248 nm and 1.70 at a wavelength of 193 nm. The extinction coefficient, k, was 0.00 at a wavelength of 248 nm and 0.05 at a wavelength of 193 nm.
In this example, a gap fill material was prepared by mixing 5.65% by weight of BOLTORN H30 (a hyperbranched polymer having a molecular weight of 5100 g/mole and available from Perstorp Specialty Chemicals AB, Sweden), 0.05% by weight of CYMEL 303LF, 1.31% by weight of POWDERLINK 1174, 0.018% by weight of pTSA, 0.32% by weight of Bisphenol-A, 91.652% by weight of PGME, and 1.0% by weight of PGMEA. The solution was coated onto a silicon wafer at 1500 rpm for 60 seconds and then baked at 205° C. for 60 seconds. The film thickness was 186 nm measured on an ellipsometer. The refractive index, n, was 1.60 at a wavelength of 248 nm and 1.70 at a wavelength of 193 nm. The extinction coefficient, k, was 0.01 at a wavelength of 248 nm and 0.05 at a wavelength of 193 nm.
In this example, a bottom anti-reflective coating was prepared by mixing 2.8% by weight of BOLTORN H40, 1.4% by weight of 9-anthracene carboxylic acid (9-ACA, a cliromophore), 1.7% by weight of CYMEL 303LF, 0.2% by weight of pyridinium p-toluenesulfonate (PPTS), 46.8% by weight of PGME, and 47.1% by weight ethyl lactate (EL). The solution was coated onto a silicon wafer at 1500 rpm for 60 seconds and then baked at 160° C. for 60 seconds. The film thickness was 157 nm measured on an ellipsometer. The refractive index, n, was 1.60 at a wavelength of 248 nm. The extinction coefficient, k, was 0.40 at a wavelength of 248 μm.
In this example, a bottom anti-reflective coating was prepared by mixing 2.8% by weight of BOLTORN H40, 1.4% by weight of 3-hydroxy-2-naphthoic acid (a chromophore), 1.7% by weight of CYMEL 303LF, 0.2% by weight of PPTS, 46.8% by weight of PGME, and 47.1% by weight EL. The solution was coated onto a silicon wafer at 1500 rpm for 60 seconds, and then baked at 160° C. for 60 seconds. The film thickness was 153 nm measured on an ellipsometer. The refractive index, n, was 1.79 at a wavelength of 248 nm. The extinction coefficient, k, is 0.27 at a wavelength of 248 nm.
In this example, a bottom anti-reflective coating was prepared by mixing 2.6% by weight of BOLTORN H40, 1.8% by weight of 4-hydroxybenzoic acid (a cliromophore), 1.6% by weight of CYMEL 303LF, 0.3% by weight of PPTS, 49.6% by weight of PGME, and 44.0% by weight EL. The solution was coated onto a silicon wafer at 1500 rpm for 60 seconds, and then baked at 160° C. for 60 seconds. The film thickness was 142 nm measured on an ellipsometer. The refractive index, n, was 1.57 at a wavelength of 193 nm. The extinction coefficient, k, was 0.17 at a wavelength of 193 nm.
In this example, a bottom anti-reflective coating was prepared by mixing 2.6% by weight of BOLTORN H40, 1.8% by weight of 3,4-dihydroxybenzoic acid (a chromophore), 1.6% by weight of CYMEL 303LF, 0.3% by weight of PPTS, 49.6% by weight of PGME, and 44.0% by weight EL. The solution was coated onto a silicon wafer at 1500 rpm for 60 seconds, and then baked at 160° C. for 60 seconds. The film thickness was 156 nm measured on an ellipsometer. The refractive index, n, was 1.53 at a wavelength of 193 nm. The extinction coefficient, k, was 0.16 at a wavelength of 193 nm.
h this example, a bottom anti-reflective coating was prepared by mixing 1.8% by weight of BOLTORN H40, 0.9% by weight of Phenol Novolac PSM 4324 (a chromophore, available from Gun Ei Chemical, Industry CO. LTD), 0.5% by weight of CYMEL 303LF, 0.04% by weight of PPTS, 48.58% by weight of PGME, aid 48.17% by weight EL. The solution was coated onto a silicon wafer at 1500 rpm for 60 seconds and then baked at 205° C. for 60 sec. The film thickness was 84 nm measured on an ellipsometer. The refractive index, n, was 1.54 at a wavelength of 193 nm. The extinction coefficient, k, was 0.29 at a wavelength of 193 nm.
1. Ethyl Lactate Stripping Test
An ethyl lactate stripping test was carried out to determine the extent of the crosslinking reaction after baking. In this test, the particular formulation was spin-coated onto a 4-inch silicon wafer and then baked at 150° C. to 205° C. for 60 seconds. The initial film thickness was then measured using ellipsometry. After recording the thickness, the wafer was sprayed with ethyl lactate. The resulting puddle was left to stand for 10 seconds, and the wafer was spun at 2000-3500 rpm for 20-30 seconds. The wafer was then re-measured to determine the final film thickness. This final film thickness was subtracted from the initial film thickness to yield the amount of film stripping. Each of the formulations described in Examples 1-4 exhibited no stripping, thus indicating a very effective crosslinking reaction.
2. Etch Rate
The etch rate is an indicator of how fast the film will etch in a plasma. The etchant gas used was CF4, and the flow rate was 40 sccm. The power applied was 100W. The formulation of Example 1 was spin-coated onto a 4-inch silicon wafer and baked at 205° C. The initial film thickness was measured using ellipsometry. The wafer was placed in an etch chamber (a Reactive Ion Etcher manufactured by TRION Corp.) and subjected to CF4 etching for a predetermined time. The film thickness was measured after the etch process. A graph of film thickness as a function of etch time was plotted, and the etch rate was determined from the slope of the curve.
Thus, compositions according to the invention can be utilized with substrates having a wide variation of iso and/or dense patterns. An Iso pattern is a pattern in which the distance between the center of a first hole and the center of an adjacent hole is at least about three times the diameter of the first hole. A Dense pattern is a pattern in which the distance between the center of a first hole and the center of an adjacent hole is about equal to or less than the diameter of the first hole.
The degree of leveling of the cured inventive composition in contact or via holes should be at least about 90%, preferably at least about 92%, and more preferably at least about 95%. The degree of leveling of the anti-reflective coating is determined by observing (under a scanning electron microscope) the cross-sectional surface of a coated silicon wafer substrate. This can be better understood by referring to
wherein “M” and “H” are measurements taken from the cured material as shown in
The inventive compositions can achieve such high degrees of leveling because they are highly and smoothly flowable, thus allowing a large number of holes to be filled smoothly, resulting in a substantially constant film thickness.
This application is a divisional application of U.S. patent application Ser. No. 11/032,930, filed Jan. 11, 2005, pending and incorporated by reference herein.
This invention was made with Government support under contract MDA Phase III Contract # DASG60-01-C-0047. The Goverment has certain rights in the invention.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4631337 | Tomalia et al. | Dec 1986 | A |
| 5041516 | Frechet et al. | Aug 1991 | A |
| 5418301 | Hult et al. | May 1995 | A |
| 5705602 | Kawashima et al. | Jan 1998 | A |
| 6211329 | Rehnberg et al. | Apr 2001 | B1 |
| 6391472 | Lamb, III et al. | May 2002 | B1 |
| 6444320 | Takai et al. | Sep 2002 | B1 |
| 6569956 | Ramesh | May 2003 | B1 |
| 6617418 | Magnusson et al. | Sep 2003 | B1 |
| 6630520 | Bruza et al. | Oct 2003 | B1 |
| 20010011109 | Tomalia et al. | Aug 2001 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20080213544 A1 | Sep 2008 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 11032930 | Jan 2005 | US |
| Child | 11852137 | US |