GARNET-TYPE LITHIUM-ION SOLID-STATE CONDUCTOR

Abstract

Disclosed is a solid state electrolyte comprising a compound of Formula 1

Description

BACKGROUND

1. Field

Disclosed is a garnet-type lithium-ion solid-state conductor, methods of synthesis thereof, an electrode and a battery including the solid-state conductor, and methods of manufacture thereof.

2. Description of the Related Art

Lithium batteries are of interest because they can potentially offer improved specific energy and energy density, improved safety, and in some configurations improved power density. However, currently available materials are not sufficiently stable to lithium metal. Desired is a material that would permit the use of high-voltage positive electrode materials and low-voltage negative electrode materials such as lithium metal, and provide high power density. The lithium conductivity of available solid-state materials is significantly less than liquid alternatives. Thus there remains a need for an improved lithium-ion conducting solid-state material, and an electrochemical cell including the same.

SUMMARY

Disclosed is a solid state electrolyte comprising a compound of Formula 1

Li_{7-a*α-(b−4)*β−x}M^a_αLa₃Hf_2−βM^b_βO_12−x−δX_x   (1)

wherein

• • M^a is a cationic element having a valence of a+;
  • M^b is a cationic element having a valence of b+; and
  • X is an anion having a valence of -1,
  • wherein, when M^a includes H, 0≤α≤5, otherwise 0≤α≤0.75, and wherein 0≤β≤1.5, 0≤x≤1.5, and (a*α+(b−4)β+x)>0, 0≤δ1.

Also disclosed is a particle including: the solid state electrolyte of claim 1; and a liquid electrolyte within a pore of the particle.

Also disclosed is a solid state electrolyte including: a core including a first solid state electrolyte; and a shell including the compound of Formula 1 on the core, wherein the first solid state electrolyte and the compound of Formula 1 are different.

Also disclosed is a porous separator for a battery, the separator including: a porous substrate, and the compound of Formula 1 on the substrate.

Also disclosed is a protected negative electrode, the electrode comprising lithium metal and the solid state electrolyte directly on the lithium metal.

Also disclosed is a positive active material for a lithium battery, the positive active material including: a lithium transition metal oxide; and the solid state electrolyte on the lithium transition metal oxide.

Also disclosed is a battery including: a positive electrode; a negative electrode; and the solid state electrolyte between the positive electrode and the negative electrode.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other advantages and features of this disclosure will become more apparent by describing in further detail exemplary embodiments thereof with reference to the accompanying drawings, in which:

FIG. 1 is a graph of diffusivity (square centimeters per second) versus inverse temperature (1/Kelvin) illustrating the activation energy and conductivity of the composition Li_6.25La₃Hf₂Al_0.25O₁₂;

FIG. 2 is a graph of diffusivity (square centimeters per second) versus inverse temperature (1/Kelvin) illustrating the activation energy and conductivity of the composition Li_6.75La₃Hf₂O_11.75F_0.25;

FIG. 3 is a graph of diffusivity (square centimeters per second) versus inverse temperature (1/Kelvin) illustrating the activation energy and conductivity of the composition Li_6.5La₃Hf₂O_11.5F_0.5;

FIG. 4 is a graph of lithium uptake or loss per formula unit versus voltage (Volts versus Li/Li⁺) illustrating the stability of Li_6.75La₃Hf₂O_11.75F0.25 between 0 and 3.2 volts versus Li/Li⁺;

FIG. 5 is a graph of lithium uptake or loss per formula unit versus voltage (Volts versus Li/Li⁺) illustrating the stability of Li_6.5La₃Hf₂O_11.75F0.5 between 0 and 3.2 volts versus Li/Li⁺; and

FIG. 6 is a graph of intensity (relative counts) versus diffraction angle (degrees 2-theta) for the Li_6.55La₃Hf_1.55Tao.45O₁₂ product of Example 4; and

FIG. 7 is a graph of intensity (arbitrary units) versus diffraction angle (degrees 2-theta) for the Li_6.25La₃Hf₂Mg_0.375O₁₂ product of Example 5 and the Li_6.25Hf₂La₃O_11.25F_0.75 product of Example 6;

FIGS. 8A and 8B are each a graph of imaginary resistance (Z₂, ohms-square centimeters, Ωcm²) versus real resistance (Z₁, ohms-square centimeters, Ωcm²) which shows the results of impedance analysis of the Li_6.25La₃Hf₂Mg_0.375O₁₂ product of Example 5 and the Li_6.25Hf₂La₃O_11.25F_0.75 product of Example 6, respectively; and

FIG. 9 is a schematic illustration of an aspect of a battery.

DETAILED DESCRIPTION

Disclosed is a solid-state lithium-ion conducting material having improved stability and improved ionic conductivity. The material may be used to provide a solid-state separator, e.g., to electrically separate a positive electrode and a negative electrode of a lithium-ion or a lithium metal battery. In an aspect, the material may be used as protection layer on lithium metal to provide a protected lithium-metal negative electrode having improved stability. In an aspect, the material is an Hf-containing garnet-type oxide material and provides an improved combination of conductivity and stability against lithium metal. Disclosed is a solid state electrolyte comprising a compound of Formula 1

Li_{7-a*α-(b−4)*β−x}M^a_αLa₃Hf_2−βM^b_βO_12−x−δX_x   (1)

wherein M^a is a cationic element having a valence of a+; M^b is a cationic element having a valence of b+; and X is an anion having a valence of -1, wherein, when M^a comprises H, 0≤α≤5, otherwise 0≤α≤0.75, and wherein 0≤β≤1.5, 0≤x≤1.5, and a*α+(b−4)β+x>0, 0≤δ1.

M^a may be a monovalent element, a divalent element, a trivalent element, or a tetravalent element. In an aspect, a is 1 and M^a is monovalent and is H, Na, K, Rb, or a combination thereof, thus M^a may comprise H⁺, Na+, K+, Rb+, or a combination thereof. In an aspect, a is 2 and M^a is divalent and is Be, Mg, Ca, Sr, Ba, or a combination thereof. Thus M^a may comprise Be²⁺, Mg²⁺, Ca²⁺, Sr²⁺, Ba²⁺, or a combination thereof. In an aspect, a is 3, and M^a is trivalent and comprises B, Al, Ga, In, Sc, Y, La, Ce, Pr, Nd, or a combination thereof. Thus M^a may comprise B³⁺, Al³⁺, Ga³⁺, In³⁺, Sc³⁺, Y³⁺, La³⁺, Ce³⁺, Pr³⁺, Nd³⁺, or a combination thereof. In an aspect, a is 4, and M^a is tetravalent and is Zr, Ti, Sn, Si, Ge, Pb, or a combination thereof. Thus M^a may be Zr⁴⁺, Ti⁴⁺, Sn⁴⁺, Si⁴⁺, Ge⁴⁺, Pb⁴⁺, or a combination thereof.

A content α of M^a in Formula 1 may be 0≤α≤5, 0≤α≤5, 0.1≤α≤4, or 0.2≤α≤3 when M^a comprises H. Otherwise, e.g., when M^a is other than H, i.e., a divalent element, a trivalent element, or a tetravalent, a content a of M^a in Formula 1 may be 0≤α≤0.75, 0≤α≤0.75, 0.1≤α≤0.7, 0.2≤α≤0.6, or 0.3≤α≤0. 5.

While not wanting to be bound by theory, it is understood that in the structure of the compound of Formula 1, M^a resides on a lithium crystallographic site. It is observed that when the compound adopts a structure in which M^a resides on a lithium crystallographic site, the lithium-ion conductivity and stability are improved.

In an aspect, M^b in Formula 1 is a divalent element, a trivalent element, a tetravalent element, or a pentavalent element. In an aspect, b is 2 and M^b is divalent and is Be, Mg, Ca, Sr, Ba, or a combination thereof. Thus M^b may comprise Be²⁺, Mg²⁺, Ca²⁺, Sr²⁺, Ba²⁺, or a combination thereof. In an aspect, b is 3 and M^b is trivalent and is B, Al, Ga, In, Sc, Y, La, Ce, Pr, Nd, or a combination thereof. Thus M^b may comprise B³⁺, Al³⁺, Ga³⁺, In³⁺, Sc³⁺, Y³⁺, La³⁺, Ce³⁺, Pr³⁺, Nd³⁺, or a combination thereof. In an aspect, b is 4 and M^b is tetravalent and is Zr, Ti, Sn, Si, Ge, Pb, or a combination thererof. Thus M^b may comprise Zr⁴⁺, Ti⁴⁺, Sn⁴⁺, Si⁴⁺, Ge⁴⁺, Pb⁴⁺, or, a combination thereof. In an aspect, b is 5 and M^b is pentavalent and is V, Ta, Nb, or a combination thereof. Thus M^b may comprise V⁵⁺, Ta⁵⁺, Nb⁵⁺, or a combination thereof. In an aspect, b is 6 and M^b is hexavalent and is Cr, Mo, W, or a combination thereof. Thus M^b may comprise Cr⁶⁺, Mo⁶⁺, W⁶⁺, or a combination thereof.

A content β of M^b in Formula 1 may be 0≤β≤1.5, 0≤β≤1.5, 0.1≤β≤1.4, 0.2≤β≤1.3, 0.3≤β≤1.2. Also, M^a and M^b may be different.

While not wanting to be bound by theory, it is understood that in the structure of the compound of Formula 1, M^b resides on a hafnium crystallographic site. It is observed that when the compound adopts a structure in which M^b resides on a hafnium crystallographic site, the lithium-ion conductivity and stability are improved.

In an aspect X in Formula (1) is F, Cl, Br, I, or a combination thereof. Use of fluorine, F⁻, i.e., having a valence of −1, is mentioned. A content x of the anion X in the compound of Formula 1 may be 2≤x≤1.5, 0<x<1.5, 0.19≤x≤1.4, or 0.2≤x≤1.3.

Also, the compound of Formula 1 may comprise an oxygen defect. An oxygen defect content δ in Formula 1 may be 0≤δ≤1, 0<δ<1, 0.1≤δ≤0.9, or 0.2≤δ≤0.8. While not wanting to be bound by theory, it is understood that including an oxygen defect in the compound of Formula 1 provides improved ionic conductivity.

In the compound of Formula 1, (a*α+(b−4)βαx)>0. For example, 0≤(a*α+(b−4)β+x)<1, 0.1<(a*α+(b−4)β+x)<0.8, or 0.2<(a*α+(b−4)β+x)<0.6.

The compound of Formula 1 may be in the form of a particle. The particle can have, for example, a spherical form, an oval-spherical form, or the like. The particle diameter is not particularly limited, and a mean particle diameter ranging, for example, from 0.01 to 50 μm, for example, 0.1 to 25 μm, or 0.2 μm to 10 μm is mentioned. A mean particle diameter refers to a number average diameter (D50) of the particle size distribution of particles obtained by scattering, or the like. The particle can be processed, for example, by mechanical milling, to provide a suitable particle size.

The particle comprising the compound of Formula 1 may comprise a gradient of M^b, wherein the gradient is in a direction from a center of the particle to a surface of the particle. A content of M^b, if present, may vary such that a content of M^b is decreases in a direction from a center of the particle towards a surface of the particle. For example, a ratio of a concentration of Hf to M^b on a surface of the particle is greater than a ratio of a concentration of Hf to M^b in a center of the particle. In an aspect, wherein M^b is Zr, a ratio of a concentration of Hf to Zr on a surface of the particle is greater than a ratio of a concentration of Hf to Zr in a center of the particle. Also, a concentration of Hf may increase in a direction from a center of the particle to a surface of the particle. In an aspect, a content of Hf in a center of the particle is zero, and increases in a direction to a surface of the particle.

In an aspect, the particle comprising the compound of Formula 1 may be porous. The porous structure of the particle can refer to a particle having micro- and/or nanostructural features, e.g., microporosity and/or nanoporosity. For example, the porosity of the solid electrolyte comprising the compound of Formula 1 can be 10% to 90%, or 20% to 80%, or 30% to 70%. As used herein, “pores” can also refer to “voids.” Also, a pore size of the pores of particle comprising the compound of Formula 1 may be 0.1 μm to 50 μm, 2 μm to 40 μm, or 5 μm to 30 μm.

A liquid electrolyte may be disposed in a pore of the particle. In an aspect, the liquid electrolyte is disposed in a pore of the particle comprising the compound of Formula 1. The liquid electrolyte may comprise a polar aprotic solvent and a lithium salt. The polar aprotic solvent can be dimethylether, diethylether, dimethyl carbonate, diethyl carbonate, ethylmethyl carbonate, dipropyl carbonate, methylpropyl carbonate, ethylpropyl carbonate, ethylene carbonate, propylene carbonate, butylene carbonate, fluoroethylene carbonate, methyl acetate, ethyl acetate, n-propyl acetate, dimethylacetate, methyl propionate, ethyl propionate, γ-butyrolactone, decanolide, valerolactone, mevalonolactone, caprolactone, dibutyl ether, tetraglyme, diglyme, polyethylene glycol dimethylether, dimethoxy ethane, 2-methyl tetrahydrofuran, 2,2-dimethyl tetrahydrofuran, 2,5-dimethyl tetrahydrofuran, cyclohexanone, triethylamine, triphenylamine, triether phosphine oxide, acetonitrile, dimethyl formamide, 1,3-dioxolane, and sulfolane, but the organic solvent is not limited thereto and any suitable solvent can be used. In an embodiment, the solvent preferably comprises a carbonate ester, and more preferably comprises ethylene carbonate and propylene carbonate.

The lithium salt may comprise LiPF₆, LiBF₄, LiSbF₆, LiAsF₆, LiN(SO₃C₂F₅)₂, LiC₄F₉SO₃, LiClO₄, LiAlO₂, LiAlCl₄, LiN(C_xF_2x+1SO₂)(C_yF_2y+1SO₂) in which the x and y are natural numbers, e.g., an integer of 1 to 20, LiCl, LiI, LiB(C₂O₄)₂, lithium bis(fluorosulfonyl)imide, or a combination thereof. The concentration of the lithium salt may be 0.1 to 2 molar (M), e.g., 0.5 to 1.3 M in the aprotic solvent.

In an aspect, a solid state electrolyte comprises a core comprising a first solid state electrolyte; and a shell comprising the compound of Formula 1 on the core, wherein the first solid state electrolyte and the compound of Formula 1 are different. The first solid state electrolyte may comprise a sulfide solid electrolyte, or an additional solid electrolyte.

The sulfide solid electrolyte may comprise Li₂S—P2S₅, Li₂S—P₂S₅—LiX, wherein X is a halogen element, Li₂S—P₂S₅—Li₂O, Li₂S—P₂S₅—Li₂O—LiI, Li₂S—SiS₂, Li₂S —SiS₂—Lii, Li₂S —SiS₂—LiBr, Li₂S—SiS₂—LiC₁, Li₂S—SiS₂—B₂S₃—LiI, Li₂S—SiS₂—P₂S₅—LiI, Li₂S—B₂S₃, Li₂S—P₂S₅—Z_mS_n, wherein m and n are positive numbers, Z is one of Ge, Zn or Ga, Li₂S—GeS₂, Li₂S—SiS₂—Li₃PO₄, Li₂S—SiS₂-Li_pM¹O_q wherein p and q are positive numbers, M¹ is P, Si, Ge, B, Al, Ga, or In, Li_7-xPS_6-xCl_x wherein 0<x<2, Li_7,PS6,Brx wherein 0<x<2, or Li_7-xPS_6-xI_x wherein 0<x<2. Mentioned are Li₆PS₅Cl, Li₆PS₅Br, or Li₆PS₅I.

The additional oxide solid electrolyte may comprise Li_1+x+yAl_xTi_2−x,Si_yP_3−yO₁₂ wherein 0<x<2, 0<y<3, BaTiO₃, Pb(Zr_(1−x)Ti_x)O₃ wherein 0≤x≤1, Pb_1−xLa_xZr_1−yTi_yO₃ wherein 0≤x≤1, 0≤y<1, Pb(Mg_1/3Nb_2/3)O₃-PbTiO₃, HfO₂, SrTiO₃, SnO₂, CeO₂, Na₂O, MgO, NiO, CaO, BaO, ZnO, ZrO₂, Y₂O₃, Al₂O₃, TiO₂, SiO₂, SiC, Li₃PO₄, Li_xTi_y(PO₄)₃ wherein 0<x<2, 0<y<3), Li_xAl_yTi_z(PO₄)₃0<x<2, 0<y<1, 0<z<3), Li_1+x+Y(Al_(1−m)Ga_m)_x(Ti_(1−n) )_2−xSi_yP_3−yO₁₂ (0≤x≤1, 0≤y≤1, 0≤m≤1, and 0≤n≤1, Li_xLa_yTiO₃ wherein 0<x<2, 0<y<3, Li_xGe_yP_zS_w wherein 0<x<4, 0<y<1, 0<z<1, and 0<w<5, Li_xN_y wherein 0<x<4 and 0<y<2, SiS₂, Li_xSi_yS_z wherein 0<x<3, 0<y<2, 0<z<4, Li_XP_yS_z wherein 0<x<3, 0<y<3 and 0<z<7, Li₂O, LiF, LiOH, Li₂CO₃, LiAlO₂, a Li₂O—Al₂O₃—SiO₂—P₂O₅—TiO₂—GeO₂ ceramic, a garnet ceramic of the formula Li_3+xLa₃M¹₂O₁₂ wherein M¹ is Te, Nb or Zr and x is an integer of 1 to 10, or a combination thereof. Mentioned is (La_1−xLi_x)TiO₃ (LLTO) wherein 0<x<1.

The additional oxide solid electrolyte may comprise an oxide of the formula Li_5+xE₃(Me²_zMe²_(2−z))O_d wherein E is a trivalent cation; Me^l and Me² are each independently one of a trivalent, tetravalent, pentavalent, and a hexavalent cation; 0<x≤3, 0≤z<2, and 0<d≤12; and O can be partially or totally substituted with a pentavalent anion, a hexavalent anion, a heptavalent anion, or a combination thereof. For example, E can be partially substituted with a monovalent or divalent cation. In another embodiment, for example, in the solid ion conductor, when 0<x≤2.5, E may be La and Me² can be Zr. In an aspect, the oxide can be of the formula Li_5+x+2y(D_yE_3-7) (Me¹_zMe²_2−z)O_d wherein D is a monovalent or divalent cation; E is a trivalent cation; Me^l and Me² are each independently a trivalent, tetravalent, pentavalent, or a hexavalent cation; 0<x+2y≤3, 0<y≤0.5, 0≤z<2, and 0<d≤12; and O can be partially or totally substituted with a pentavalent anion, a hexavalent anion, a heptavalent anion, or a combination thereof. The preferred number of moles of lithium per formula unit (Li-pfu) in the above formula is 6<(5+x+2y) <7.2, 6.2 <(5+x+2y)<7, 6.4<(5+x+2y)<6.8. In the garnet-type oxides of the above formulas, D can comprise potassium (K), rubidium (Rb), cesium (Cs), calcium (Ca), barium (Ba), or strontium (Sr). In an embodiment, D is calcium (Ca), barium (Ba), or strontium (Sr). In the above formulas, Me can be a transition metal. For example, Me can be tantalum (Ta), niobium (Nb), yttrium (Y), scandium (Sc), tungsten (W), molybdenum (Mo), antimony (Sb), bismuth (Bi), hafnium (Hf), vanadium (V), germanium (Ge), silicon (Si), aluminum (Al), gallium (Ga), titanium (Ti), cobalt (Co), indium (In), zinc (Zn), or chromium (Cr). Mentioned is Li_6.5La₃Zr_1.5Ta_0.5O₁₂.

Disclosed is a separator, e.g., for a battery, or other electrochemical device. The separator may comprise a layer comprising the compound of Formula 1 between a positive electrode and a negative electrode. In an aspect the separator is porous.

A porous separator may comprise a porous substrate, and the compound of Formula 1 on the substrate. The porous separator may be a microporous polyolefin. The separator may comprise a glass fiber, polyester, polyethylene, polypropylene, polytetrafluoroethylene (PTFE), or a combination thereof. The separator may comprise a microporous polymeric film, such as a microporous polyethylene or microporous polypropylene film. The separator may comprise the solid-state electrolyte and a porous olefin film such as polyethylene and polypropylene. A diameter of a pore of the porous olefin film can be 0.01 to 10 micrometers (μm), and a thickness of the separator can be in a range of 5 to 300 μm.

Also disclosed is a protected negative electrode comprising the compound of Formula 1 on the negative electrode active material. In an aspect, the negative electrode active material comprises lithium metal, a lithium alloy, or a combination thereof. Mentioned is a negative electrode comprising lithium metal having a protection layer comprising compound of Formula 1 directly thereon.

Also disclosed is a protected positive active material comprising the compound of Formula 1 on the positive active material. In an aspect, the positive active material comprises a lithium transition metal oxide. Mentioned is a positive active material comprising a particle of the transition metal oxide having a protection layer comprising compound of Formula 1 directly thereon. While not wanting to be bound by theory, it is understood that the compound of Formula 1 is effective to protect the positive electrode active material, e.g., to prevent or suppress reaction with the electrolyte.

The positive active material can comprise a lithium transition metal oxide, a transition metal sulfide, or the like. For example, the positive active material can include a composite oxide of lithium and a metal selected from cobalt, manganese, and nickel. For example, the positive active material can be a compound represented by any of the Formulas: Li_pM¹_1−qM²_qD₂ wherein 0.90≤p≤1.8 and 0≤q≤0.5; Li_pE_1−qM²_qO_2−qD_x wherein 0.90≤p≤1.8, 0≤q≤0.5, and 0≤x≤0.05; LiE_2−qM²_qO_4−xD_x wherein 0≤q≤0.5 and 0≤x≤0.05; Li_pNi_1−q−rCo_qM²_rD_x wherein 0.90≤p≤1.8, 0≤q≤0.5, 0≤r≤0.05, and 0<x≤2; Li_pNi_1−q−rCo_pM²_rO_2−xX_x wherein 0.90≤p≤1.8, 0≤q≤0.5, 0≤r≤0.05, and 0≤x≤2; Li_pNi_{1-31 q−r}Co_pM²_rO_{2-31 x}X_x wherein0.90≤p≤1.8, 0≤q≤0.5, 0≤r≤0.05, and 0≤x≤2; Li_pNi_1−q−rMn_qM²_rD_x wherein 0.90≤p≤1.8, 0≤q≤0.5, 0≤r≤0.05, and 0<x≤2; Li_pNi_1−q−rMn_qM²_rO_2−pX_x wherein 0.90≤p≤1.8, 0≤q≤0.5, 0≤r≤0.05, and 0<x<2; Li_pNi_1−q−rMn_qM²_rO_2−xX_x wherein 0.90≤p≤1.8, 0≤q≤0.5, 0≤r≤0.05, and 0<x<2; Li_pNi_qE_rG_dO₂ wherein 0.90≤p≤1.8, 0≤q≤0.9, 0≤r≤0.5, and 0.001≤d≤0.1; Li_pNi_qCo_rMn_dGeO₂ wherein 0.90≤p≤1.8, 0≤q≤0.9, 0≤r≤0.5, 0≤d≤0.5, and 0.001≤d≤0.1; Li_pNiG_qO₂ wherein 0.90≤p≤1.8 and 0.001≤q≤0.1; Li_pCoG_qO₂ wherein 0.90≤p≤1.8 and 0.001≤q≤0.1; Li_pMnG_qO₂ where 0.90≤p≤1.8 and 0.001≤q≤0.1; Li_pMn2G_qO₄ wherein 0.90≤p≤1.8 and 0.001≤q≤0.1; QO₂; QS₂; LiQS₂; V₂O₅; LiV₂O₂; LiRO₂; LiNiVO₄; Li_(3−f)J₂(PO₄)₃ (0≤f≤2); Li_(3−f)Fe₂(PO₄)₃ wherein 0≤f≤2; and LiFePO4, in which in the foregoing positive active materials M¹ is Ni, Co, or Mn; M² is Al, Ni, Co, Mn, Cr, Fe, Mg, Sr, V, or a rare-earth element; D is O, F, S, or P; E is Co or Mn; X is F, S, or P; G is Al, Cr, Mn, Fe, Mg, La, Ce, Sr, or V; Q is Ti, Mo or Mn; R is Cr, V, Fe, Sc, or Y; and J is V, Cr, Mn, Co, Ni, or Cu. Examples of the positive active material include LiC0O₂, LiMn_xO_2x where x=1 or 2, LiNi_1−xMn_xO₂x where 0<x<1, LiNi_1−x−yCo_xMn_yO₂ where 0≤x≤0.5 and 0≤y≤0.5, LiFePO₄, TiS₂, FeS₂, TiS₃, and FeS₃.

Mentioned is an aspect in which the positive active material is a NCA material represented by Li_xNi_yE_zG_dO₂ (wherein 0.90≤x≤1.8, 0≤y≤0.9, 0≤z≤0.5, 0.001≤d≤0.1, E is Co, Mn, or a combination thereof, and G is Al, Cr, Mn, Fe, Mg, La, Ce, Sr, V, or a combination thereof). In an implementation, the positive active material may include, e.g., lithium cobalt oxide, lithium nickel cobalt manganese oxide, lithium nickel cobalt aluminum oxide, or a combination thereof.

A positive electrode may comprise a layer comprising the positive active material and may further include a conductive agent and a binder. Any suitable conductive agent and binder may be used. A binder can facilitate adherence between components of the electrode, such as the positive active material and the conductor, and adherence of the electrode to a current collector. Examples of the binder can include polyacrylic acid (PAA), polyvinylidene fluoride, polyvinyl alcohol, carboxymethyl cellulose (CMC), starch, hydroxypropyl cellulose, regenerated cellulose, polyvinylpyrrolidone, tetrafluoroethylene, polyethylene, polypropylene, ethylene-propylene-diene monomer (EPDM), sulfonated EPDM, styrene-butadiene-rubber, fluorinated rubber, a copolymer thereof, or a combination thereof. The amount of the binder can be in a range of about 1 part by weight to about 10 parts by weight, for example, in a range of about 2 parts by weight to about 7 parts by weight, based on a total weight of the positive active material. When the amount of the binder is in the range above, e.g., about 1 part by weight to about 10 parts by weight, the adherence of the electrode to the current collector may be suitably strong.

The conductive agent can include, for example, carbon black, carbon fiber, graphite, carbon nanotubes, graphene, or a combination thereof. The carbon black can be, for example, acetylene black, Ketjen black, Super P carbon, channel black, furnace black, lamp black, thermal black, or a combination thereof. The graphite can be a natural graphite or an artificial graphite. A combination comprising at least one of the foregoing conductive agents can be used. The positive electrode can additionally include an additional conductor other than the carbonaceous conductor described above. The additional conductor can be an electrically conductive fiber, such as a metal fiber; a metal powder such as a fluorinated carbon powder, an aluminum powder, or a nickel powder; a conductive whisker such as a zinc oxide or a potassium titanate; or a polyphenylene derivative. A combination comprising at least one of the foregoing additional conductors can be used.

The negative active material, e.g., lithium metal, may be disposed on a current collector, such as a copper current collector to form a negative electrode.

A positive electrode can be produced from a positive active material composition including a positive active material, and optionally, the conductive agent, and the binder. In an embodiment the positive active material composition is disposed on a current collector, such as an aluminum current collector to form a positive electrode. Screen printing, slurry casting, or powder compression may be used, the details of which may be determined by one of skill in the art without undue experimentation and are not further elaborated upon herein for clarity.

A battery may be manufactured by providing a negative electrode; providing a positive electrode; and disposing an electrolyte between the positive electrode and the negative electrode. In an aspect, the electrolyte may be a solid state electrolyte comprising the compound of Formula 1. In an aspect, a separator comprises the compound of Formula 1. In an aspect the negative active material, e.g., lithium metal, or the positive active material are protected by a layer comprising the compound of Formula 1. An aspect of the lithium battery is shown in FIG. 9, which illustrates schematically a battery 900 comprising a negative electrode 910, a solid electrolyte 920, an optional separator 930 and a positive electrode 940. The electrode assembly may be disposed in a can 950 having a header 960.

The compound of Formula 1 may be synthesized by combining, for example, Li₂CO₃, La(OH)₃, HfO₂, a compound comprising M^a if M^a is present, a compound comprising Mb if Mb is present, and a lithium salt comprising a halogen if a halogen is present, in suitable stoichiometric amount. For example, if M^a or Mb is Mg, magnesium carbonate or magnesium oxide may be used. If M^a or Mb is Al, Al₂(CO₃)₃ may be used. Also, if X is F, LiF may be used, or if X is Cl, LiCl may be used. The mixture can be heat treated in a suitable container, such as a crucible, at temperature between 700° C. and 1000° C. for two to 10 hours in air. The resulting material can ground into a fine powder using a ball-mill for 30 minutes. If desired, a wet process, such as wet-milling in methanol may be used. The dried powder can again be treated at an appropriate temperature between 700° C. and 1000° C. for 2 to 24 hours to provide the desired phase. The product may be reground, e.g., by ball-milling if desired, to provide a suitable form. The particle size of the ball-milled powder can be smaller than 1 μm, or smaller than 5 μm. The ball-milled powder can be mixed with a suitable amount of a 3 weight percent (wt %) polyvinylalcohol (PVA) solution if desired, or pressed into a pellet without the PVA at a pressure between 1 and 10 tons. The pellet can be sintered for 2 to 4 hours in air at a temperature ranging from 1000° C. to 1300° C.

In an aspect, a film comprising the compound of Formula 1 can be provided on a release layer, the film disposed on at least one of the negative electrode and the positive electrode, the release layer removed, and then the negative electrode disposed on the positive electrode to manufacture the battery.

Various embodiments are shown in the accompanying drawings. This invention may, however, be embodied in many different forms, and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art. Like reference numerals refer to like elements throughout.

It will be understood that when an element is referred to as being “on” another element, it can be directly on the other element or intervening elements may be present therebetween. In contrast, when an element is referred to as being “directly on” another element, there are no intervening elements present.

It will be understood that, although the terms “first,” “second,” “third,” etc. may be used herein to describe various elements, components, regions, layers, and/or sections, these elements, components, regions, layers, and/or sections should not be limited by these terms. These terms are only used to distinguish one element, component, region, layer, or section from another element, component, region, layer or section. Thus, “a first element,” “component,” “region,” “layer,” or “section” discussed below could be termed a second element, component, region, layer or section without departing from the teachings herein.

The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting. As used herein, the singular forms “a,” “an,” and “the” are intended to include the plural forms, including “at least one,” unless the content clearly indicates otherwise. “At least one” is not to be construed as limiting “a” or “an.” “Or” means “and/or.” As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items. It will be further understood that the terms “comprises” and/or “comprising,” or “includes” and/or “including” when used in this specification, specify the presence of stated features, regions, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, regions, integers, steps, operations, elements, components, and/or groups thereof.

Spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. It will be understood that the spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. For example, if the device in the figures is turned over, elements described as “below” or “beneath” other elements or features would then be oriented “above” the other elements or features. Thus, the exemplary term “below” can encompass both an orientation of above and below. The device may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein interpreted accordingly.

Unless otherwise defined, all terms (including technical and scientific terms) used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure belongs. It will be further understood that terms, such as those defined in commonly used dictionaries, should be interpreted as having a meaning that is consistent with their meaning in the context of the relevant art and the present disclosure, and will not be interpreted in an idealized or overly formal sense unless expressly so defined herein.

Exemplary embodiments are described herein with reference to cross section illustrations that are schematic illustrations of idealized embodiments. As such, variations from the shapes of the illustrations as a result, for example, of manufacturing techniques and/or tolerances, are to be expected. Thus, embodiments described herein should not be construed as limited to the particular shapes of regions as illustrated herein but are to include deviations in shapes that result, for example, from manufacturing. For example, a region illustrated or described as flat may, typically, have rough and/or nonlinear features. Moreover, sharp angles that are illustrated may be rounded. Thus, the regions illustrated in the figures are schematic in nature and their shapes are not intended to illustrate the precise shape of a region and are not intended to limit the scope of the present claims.

EXAMPLES

Example 1. Phase Stability

The stability of the compounds listed in Table 1 was evaluated by determining their energy above hull. Compounds having an energy above hull of less than 50 millielectron volts (meV) per atom at a temperature between 450° C. to 1200° C. are observed to be stable and included in Table 1. The energy above hull is a measure of the energy penalty paid to dope the structure.

TABLE 1
		Energy above hull	Possible impurity phases
Dopant	Composition	(meV/atom)	during synthesis
None	La7La3Hf2O12	9.8
Al	Li6.625La3Hf2Al0.125O12	16.6	Li5AlO4; Li6Hf2O7; La2O3
	Li6.25La3Hf2Al0.25O12	21.0	LiAlO2; Li6Hf2O7; La2O3
	Li5.875La3Hf2Al0.375O12	18.9	LiAlO2; La2Hf2O7; Li6Hf2O7; La2O3
	Li5.5La3Hf2Al0.5O12	20.8	LiAlO2; La2Hf2O7; Li6Hf2O7; La2O3
Ga	Li6.625La3Hf2Ga0.125O12	16.9	Li5GaO4; Li6Hf2O7; La2O3
	Li6.25La3Hf2Ga0.25O12	21.3	LiGaO2; Li6Hf2O7; La2O3
	Li5.875La3Hf2Ga0.375O12	19.1	LiGaO2; Li6Hf2O7; La2Hf2O7; La2O3
	Li5.5La3Hf2Ga0.5O12	21.3	LiGaO2; La2Hf2O7; Li6Hf2O7; La2O3
Ta	Li6.875La3Hf1.875Ta0.125O12	13.3	Li5TaO5; Li6Hf2O7; Li2O La2O3
	Li6.75La3Hf1.75Ta0.25O12	16.2	Li5TaO5; Li6Hf2O7; Li2O La2O3
	Li6.625La3Hf1.625Ta0.375O12	16.5	Li5TaO5; Li6Hf2O7; Li3TaO4; La2O3
	Li6.5La3Hf1.5Ta0.5O12	15.0	Li5TaO5; Li6Hf2O7; Li3TaO4; La2O3
	Li6.375La3Hf1.375Ta0.625O12	17.0	Li5TaO5; Li6Hf2O7; Li3TaO4; La2O3
	Li6.25La3Hf1.25Ta0.75O12	18.8	Li5TaO5; Li6Hf2O7; Li3TaO4; La2O3
Nb	Li6.875La3Hf1.875Nb0.125O12	12.5	Li8Nb2O9; Li6Hf2O7; Li2O; La2O3
	Li6.75La3Hf1.75Nb0.25O12	16.5	Li8Nb2O9; Li6Hf2O7; Li2O; La2O3
	Li6.625La3Hf1.625Nb0.375O12	16.3	Li8Nb2O9; Li6Hf2O7; La2O3
	Li6.5La3Hf1.5Nb0.5O12	17.5	Li8Nb2O9; Li6Hf2O7; La2O3
	Li6.375La3Hf1.375Nb0.625O12	20.1	Li8Nb2O9; Li6Hf2O7; Li3NbO4; La2O3
	Li6.25La3Hf1.25Nb0.75O12	22.1	Li8Nb2O9; Li6Hf2O7; Li3NbO4; La2O3
W	Li6.75La3Hf1.875W0.125O12	14.2	Li6Hf2O7; Li2O; Li4WO5; La2O3
	Li6.5La3Hf1.75W0.25O12	19.0	Li6Hf2O7; Li2O; Li4WO5; La2O3
	Li6.25La3Hf1.625W0.375O12	20.7	Li6Hf2O7; Li6Hf2O7; Li4WO5; La2O3
	Li6La3Hf1.5W0.5O12	27.0	Li6Hf2O7; Li6Hf2O7; Li4WO5; La2O3
F	Li6.875La3Hf2O11.875F0.125	15.1	Li6Hf2O7; La2O3; Li2O LiF
	Li6.75La3Hf2O11.75F0.25	20.0	Li6Hf2O7; La2O3; Li2O LiF
	Li6.625La3Hf2O11.625F0.375	23.8	Li6Hf2O7; La2O3; Li2O LiF
	Li6.5La3Hf2O11.5F0.5	27.6	Li6Hf2O7; La2O3; LiF
	Li6.375La3Hf2O11.375F0.625	32.3	Li6Hf2O7; La2O3; LiF; Li6Hf2O7
	Li6.25La3Hf2O11.25F0.75	36.7	Li6Hf2O7; La2O3; LiF; La6Hf2O7
	Li6.125La3Hf2O11.125F0.875	40.8	Li6Hf2O7; La2O3; LiF; La6Hf2O7
	Li6La3Hf2O11F	44.8	Li6Hf2O7; La2O3; LiF; La6Hf2O7
Al and Zr	Li6.625La3HfZrAl0.125O12	14.9	Li5AlO4; Li6Zr2O7; La2O3; Li6Hf2O7
	Li6.25La3HfZrAl0.25O12	19.2	LiAlO2; Li6Zr2O7; La2O3; Li6Hf2O7
	Li5.875La3HfZrAl0.375O12	19.4	LiAlO2; Li6Zr2O7; La2O3; La2Zr2O7; Li6Hf2O7
	Li5.5La3HfZrAl0.5O12	19.2	LiAlO2; Li6Zr2O7; La2O3; La2Zr2O7; Li6Hf2O7
Ta and Zr	Li6.75La3Hf0.875Zr0.875Ta0.25O12	13.8	Li5TaO5; Li6Hf2O7; Li6Hf2O7; Li2O; La2O3
	Li6.5La3Hf0.75Zr0.75Ta0.5O12	13.4	Li5TaO5; Li6Zr2O7; Li6Hf2O7; Li3TaO4; La2O3
	Li6.25La3Hf0.625Zr0.625Ta0.75O12	17.4	Li5TaO5; Li6Zr2O7; Li6Hf2O7; Li3TaO4; La2O3

Example 2. Activation Energy and Ionic Conductivity

The activation energy and ionic conductivity was determined for selected compositions by ab-initio molecular dynamics. FIG. 1 is graph of diffusivity versus the inverse of temperature for Li_6.25La₃Hf₂Al_0.25O₁₂. As shown in FIG. 1, the activation energy is 0.22 electron-volts (eV) and the conductivity at 300K is 1.63 milliSiemens per centimeter (mS/cm).

FIG. 2 is a graph of diffusivity versus the inverse of temperature for Li_6.75La₃Hf₂O_11.75F_0.25. As shown in FIG. 2, the activation energy is 0.24 eV and the conductivity at 300K is 1.58 mS/cm.

FIG. 3 is a graph of diffusivity versus the inverse of temperature for Li_6.5La₃Hf₂O_11.5F_0.5. As shown in FIG. 3, the activation energy is 0.25 eV and the conductivity at 300K is 1.75 mS/cm.

Example 3. Electrochemical Stability

The electrochemical stability of selected compositions was determined through analysis using the lithium grand potential phase diagram for the compositions Li_6.75La₃Hf₂O_11.75F_0.25 and Li_6.5La₃Hf₂O_11.5F_0.5. The grand potential phase diagram gives the stability of the solid electrolyte materials in contact with a lithium sink (charged cathode) or source (anode), each of which contains lithium at a given chemical potential. Shown in FIG. 4 is a graph of lithium uptake or loss per formula unit versus voltage for Li_6.75La₃Hf₂O_11.75F_0.25. FIG. 5 is a graph of lithium uptake or loss per formula unit versus voltage for Li_6.5La₃Hf₂O_11.5F_0.5. As shown in FIGS. 5 and 6, both Li_6.75La₃Hf₂O_11.75F_0.25 and Li_6.5La₃Hf₂O_11.5F_0.5 are intrinsically stable to lithium metal at 0 volts versus Li/Li⁺. Also, Li_6.75La₃Hf₂O_11.75F_0.25 is intrinsically stable to 3.0 V versus Li/Li⁺, and Li_6.5La₃Hf₂O_11.75F_0.25 is intrinsically stable to 3.2 V versus Li/Li⁺.

Example 4. Synthesis of Li_6.55La₃Hf_1.55Ta_0.45O₁₂

Li₂CO₃, La(OH)₃, HfO₂, and Ta₂O₅ are used as received. A mixture of stoichiometric amounts of the Li₂CO₃, La(OH)₃, HfO₂, and Ta₂O₅ for Li₆₅₅La₃Hfi_1.55Ta_0.45O₁₂ are dry-ball milled for 30 minutes at 1725 rpm with 12 mm YSZ balls. The resulting material is calcined at 950° C. for 12 hours in air. The calcined product is ground, and then uniaxially pressed into a pellet, covered with a mother powder and sintered at 1100° C. for 4 hour in air. The “mother powder” refers to a powder having the same composition but is not repeatedly used (i.e., it is not used for more than one experiment) to prevent loss of lithium.

The product was analyzed by X-ray powder diffraction. Shown in FIG. 6 is a graph of intensity versus diffraction angle for the sintered product.

Example 5. Synthesis of Li_6.25Hf₂La₃Mg_0.375O₁₂

Li₂CO₃, La(OH)₃, HfO₂, and MgO are used as received. A mixture of stoichiometric amounts of the Li₂CO₃, La(OH)₃, HfO₂, and MgO for Li_6.25Hf₂La₃Mg_0.375O₁₂ are dry-ball milled for 30 minutes at 1725 rpm with 12 mm YSZ balls. The resulting material is calcined at 950° C. for 12 hours in air. The calcined product is ground, and then uniaxially pressed into a pellet, covered with a mother powder and sintered at 1100° C. for 4 hours in air.

The product was analyzed by X-ray powder diffraction. Shown in FIG. 7 is a graph if intensity versus diffraction angle for the sintered product.

Bulk conductivity was determined by impedance spectroscopy. The product was found to have a bulk conductivity (σ_bulk)of 0.60 mS/cm at 30° C., as shown in FIG. 8A.

Example 6. Synthesis of Li_6.25Hf₂La₃O_11.25F_0.75

Li₂CO₃, La(OH)₃, HfO₂, and LiF are used as received. A mixture of stoichiometric amounts of the Li₂CO₃, La(OH)₃, HfO₂, and LiF for Li_6.25Hf₂La₃O_11.75F_0.75 are dry-ball milled for 30 minutes at 1725 rpm with 12 mm YSZ balls. The resulting material is calcined at 950° C. for 12 hours in air. The calcined product is ground, and then uniaxially pressed into a pellet, covered with a mother powder and sintered at 1100° C. for 4 hours in air.

The product was analyzed by X-ray powder diffraction. Shown in FIG. 7 is a graph if intensity versus diffraction angle for the sintered product.

Bulk conductivity was determined by impedance spectroscopy. The product was found to have a bulk conductivity (σ_bulk) of 0.23 mS/cm at 30° C., as shown in FIG. 8B.

Claims

1. A solid state electrolyte comprising a compound of Formula 1 Li7-a*α-(b−4)*β−xMaαLa3Hf2−βMbβO12−x−δXx   (1)

2. The solid state electrolyte of claim 1, wherein a Li crystallographic site comprises Ma disposed thereon.

3. The solid state electrolyte of claim 1, wherein Ma is a monovalent element, a divalent element, a trivalent element, or a tetravalent element.

4. The solid state electrolyte of claim 2, wherein a is 1 and Ma is monovalent and is H, Na, K, Rb, or a combination thereof.

5. The solid state electrolyte of claim 2, wherein a is 2 and Ma is divalent and is Be, Mg, Ca, Sr, Ba, or a combination thereof.

6. The solid state electrolyte of claim 2, wherein a is 3, and Ma is trivalent and is B, Al, Ga, In, Sc, Y, La, Ce, Pr, Nd, or a combination thereof.

7. The solid state electrolyte of claim 2, wherein a is 4, and Ma is tetravalent and is Zr, Ti, Sn, Si, Ge, Pb, or a combination thereof.

8. The solid state electrolyte of claim 1, wherein a Hf crystallographic site comprises Mb disposed thereon.

9. The solid state electrolyte of claim 1, wherein Mb is a divalent element, a trivalent element, a tetravalent element, or a pentavalent element.

10. The solid state electrolyte of claim 9, wherein b is 2 and Mb is divalent and is Be, Mg, Ca, Sr, Ba, or a combination thereof.

11. The solid state electrolyte of claim 9, wherein b is 3 and Mb is trivalent and is B, Al, Ga, In, Sc, Y, La, Ce, Pr, Nd, or a combination thereof.

12. The solid state electrolyte of claim 9, wherein b is 4 and Mb is tetravalent and is Zr, Ti, Sn, Si, Ge, Pb, or a combination thereof.

13. The solid state electrolyte of claim 9, wherein b is 5 and Mb is pentavalent and is V, Ta, Nb, or a combination thereof.

14. The solid state electrolyte of claim 9, wherein b is 6 and Mb is hexavalent and is Cr, Mo, W, or a combination thereof.

15. The solid state electrolyte of claim 1, wherein Ma and Mb are different.

16. The solid state electrolyte of claim 1, wherein X is F, Cl, Br, I, or a combination thereof.

17. The solid state electrolyte of claim 1, wherein Mb is Zr, and wherein the solid state electrolyte is in the form of a particle wherein a ratio of a concentration of Hf to Zr on a surface of the particle is greater than a ratio of a concentration of Hf to Zr in a center of the particle.

18. The solid state electrolyte of claim 1, wherein Mb is Zr, and wherein the solid state electrolyte is in the form of a particle wherein a concentration of Hf increases in a direction from a center of the particle to a surface of the particle.

19. A particle comprising: the solid state electrolyte of claim 1; anda liquid electrolyte within a pore of the particle.

20. A solid state electrolyte comprising: a core comprising a first solid state electrolyte; anda shell comprising the compound of Formula 1 on the core, wherein the first solid state electrolyte and the compound of Formula 1 are different.

21. A porous separator for a battery, the separator comprising: a porous substrate, andthe compound of Formula 1 on the substrate.

22. A protected negative electrode, the electrode comprising lithium metal and the solid state electrolyte of claim 1 directly on the lithium metal.

23. A positive active material for a lithium battery, the positive active material comprising: a lithium transition metal oxide; andthe solid state electrolyte of claim 1 on the lithium transition metal oxide.

24. A battery comprising: a positive electrode;a negative electrode; andthe solid state electrolyte of claim 1 between the positive electrode and the negative electrode.