GAS DIFFUSION LAYER

Abstract

A carbon-fiber-based gas diffusion layer (GDL) for use in polymer electrolyte membrane (PEM) fuel cells (FC) having structured hydrophilic properties, wherein materials with hydrophilic properties and selected from the group of metal oxides in an average domain size of 0.5 to 80 μm are present as hydrophilic wicks in the gas diffusion layer.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a carbon-fiber-based gas diffusion layer (GDL) having structured hydrophilic properties, which is used in polymer electrolyte membrane (PEM) fuel cells (FC).

2. Description of the Related Art

Fuel cells are highly efficient sources of energy in which fuel (typically gasses rich in hydrogen) and an oxidation agent (typically atmospheric oxygen) are electrochemically converted to water in catalyst layers on the two primary sides of a PEM. The electromechanical reaction generates electrical energy and causes the reactants to react, producing water. In this process, the PEM handles proton transport between the half cells, where the electrons are used via the electrodes and an external circuit to perform electrical work. The main problem of this type of fuel is cells balancing between the necessary moisture retention of the membrane and the bordering catalyst layer as well as conducting away the water produced, which otherwise fills the pores of the GDL, thereby impeding gas transport and reducing power output. The moisture level can be influenced and controlled by a series of factors. Moistening the anodic and cathodic reaction gas is often used as a means for setting the necessary moisture level. The working conditions (cell temperature, gas pressure and gas stoichiometry) are additional influencing parameters that influence the water content of the membrane and the GDL. Finally, the power range in which the fuel cell works also has a significant influence in balancing the water volume in the cell. Operating at high current densities causes a large volume of water to be produced, which must be controlled and guided so that optimal reliability and trouble-free operation is achieved.

A gas diffusion electrode with a layer for controlling the cross-diffusion of water is known from document DE 102 60 501 A 1. In this example, a water cross-diffusion layer made of hydrophilic fibers, in particular hydrophilic carbon fibers, is provided between the microporous GDL and the macroporous GDL of the gas diffusion electrode.

A heat and water management device for PEM fuel cells is known from the document WO 2007/139940 A2. The device comprises a thermal and electrically conductive, hydrophilic heat and water transport element, which extends from the interior to the exterior of the cell and is arranged between the GDL and the current collector. The transport element is made of boron nitride, aluminum nitride, copper-, aluminum-, nickel-alloys, graphite, expanded graphite, graphite fabric, graphite paper, aluminum foam, stainless steel foam, nickel foam, polyvinyl alcohol foam, glass microfiber, wool fabric, cotton paper, cotton fabric, polyurethane foam, cellulose acetate, polyvinyl pyrrolidone or polyacrylamide.

What is needed in the art is a GDL configured to ensure effective water management and with which fuel cells can be controlled and operated in a simple manner even at continuous high power output.

SUMMARY OF THE INVENTION

The present invention provides a carbon fiber-based gas diffusion layer having structured hydrophilic properties ensuring effective water management and structured such that fuel cells can be effectively controlled and operated even at continuous high power output. The present invention further provides a method for manufacturing the GDL according to the present invention.

According to the present invention, laterally predetermined paths are introduced into a GDL at which liquid water should collect to facilitate transport along these paths. The areas at the hydrophilic wicks should systematically draw away liquid water to ensure that the immediately neighboring pores remain free for gas transport.

These paths can be introduced, for example, by:

• • incorporating hydrophilic fibers into the microporous layer (MPL);
  • incorporating hydrophilic fibers into the interface MPL/catalyst;
  • incorporating fibers into the interface substrate/MPL; and/or
  • incorporating printed patterns with micro-/nanoscale, hydrophilic substances.

Inorganic fibers such as aluminum oxide or mixed Al₂O₃-SiO₂ (“aluminum silicate”) fibers are used as hydrophilic fibers. These fibers are cut or are available as An advantage of the present invention is ground fibers. Other possible hydrophilic substances are micro- or nanoscale SiO₂- (pyrogenic silicic acids, fumed silica), TiO₂-, Al₂O₃- or B₂O₃-based particles.

The lateral and vertical orientation of the hydrophilic wicks is important. In low and moderate load range, the ranges above the bars of the flow field, for example, contribute to the performance of the PEM fuel cell. There, the reaction products are, for example, formed as liquid water. Liquid water, which is formed above the bar, must be conducted to the canal at a right angle to the bar and an extensive flooding of the GDL must be avoided. Wick orientation must, therefore, ideally correspond to the flow field geometry. To achieve the most universal design possible, a honeycomb structure is proposed with a comb width having the same scale of the flow field structures. Similar simple polygonal structures are also suitable as an alternative option. This feature makes it easier for liquid water to flow from the reaction zone, while at the same time creating free space for the necessary transport of gas to the reaction site.

The transport paths for liquid water are varied in shape and form and are required in the three spatial directions. There is evidence that fluid water collects at the interface between the catalyst and MPL. This liquid water passes through the MPL as steam and then collects as liquid in the substrate. This crossing of the MPL as steam (vaporization and re-condensation) involves additional processes that reduce efficiency and kinetic energy. Transporting liquid water through the MPL along hydrophilic domains (in the Z direction) promises advantages in performance.

EXAMPLE 1

Carbon fiber paper of the type Sigracet® GDL 25 BA (SGL Technologies GmbH, Meitingen) is layered on a laboratory spreading knife with a coating paste (layer thickness of approximately 30-50 μm) and then sintered at approximately 350° C. for about 10 minutes. Various quantities of pre-ground aluminum oxide fibers (dispersed in water) are added to the coating paste (consisting of approximately 77% acetylene soot, 23% polytetrafluroethylene (PTFE) and organic binding substance).

SAMPLE A: approximately 0.16% aluminum oxide fibers in relation to the solid matter content of the paste

SAMPLE B: approximately 0.29% aluminum oxide fibers in relation to the solid matter content of the paste

SAMPLE C: approximately 0.67% aluminum oxide fibers in relation to the solid matter content of the paste

Just a small quantity of inorganic fibers in the coating will cause a significant hydrophilization of the surface (the surface without fibers is clearly hydrophobic owing to the PTFE portion in the layer). However, electrical resistance rises as the portion of fibers increases.

	Continuity
	resistance z	Water absorption	Angle of declination
	[mΩ cm2]	[g m−2 min−1]	[°]
SAMPLE A	9.1	~1	7-10
SAMPLE B	10.7	2-3	18-27
SAMPLE C	15.1	5-6	60-75

EXAMPLE 2

An aqueous dispersion of aluminum oxide fibers (approximately 0.01 to 0.05%, added binder/dispersant) is dehydrated in a vacuum via an uncoated GDL substrate located on a screen (e.g., sheet former/paper machine). Fiber deposits oriented along the x-y axes thereby form on the GDL. After drying, the GDL is provided with a microporous layer.

While this invention has been described with respect to at least one embodiment, the present invention can be further modified within the spirit and scope of this disclosure. This application is therefore intended to cover any variations, uses, or adaptations of the invention using its general principles. Further, this application is intended to cover such departures from the present disclosure as come within known or customary practice in the art to which this invention pertains and which fall within the limits of the appended claims.

Claims

1. A carbon-fiber-based gas diffusion layer for a fuel cell with a polymer electrolyte membrane (PEM) having structured hydrophilic properties, the gas diffusion layer comprising: a plurality of hydrophilic wicks including a plurality of materials having hydrophilic properties, said materials selected from a group of metal oxides and in an average domain size of approximately 0.5 to 80 μm.

2. The gas diffusion layer according to claim 1, wherein said metal oxides are at least one of silicon, aluminum, titanium, boron, tin, and zirconium.

3. The gas diffusion layer according to claim 1, wherein said domains are hydrophilic domains and are separated from one another by hydrophobic domains.

4. The gas diffusion layer according to claim 3, wherein said hydrophobic domains include one of a polymer containing fluorine and a hydrophobic sol-gel.

5. The gas diffusion layer according to claim 4, wherein said hydrophobic domains include one of polytetrafluroethylene (PTFE) and polyvinlidene fluoride (PVDF).

6. The gas diffusion layer according to claim 3, wherein a spacing between said hydrophilic domains ranges between approximately 10 μm and 3 mm.

7. The gas diffusion layer according to claim 6, wherein said hydrophilic domains are arranged in a pattern-like formation.

8. The gas diffusion layer according to claim 7, wherein said hydrophilic domains are arranged in a linear formation.

9. The gas diffusion layer according to claim 8, wherein said hydrophilic domains are arranged in a polygonal formation.

10. The gas diffusion layer according to claim 9, wherein said hydrophilic domains are arranged in one of a rhomboidal and a hexagonal formation.

11. The gas diffusion layer according to claim 10, wherein a surface area ratio of said hydrophilic domains to said hydrophobic domains ranges between approximately 10% and 90%.

12. The gas diffusion layer according to claim 11, wherein said surface area ratio of said hydrophilic domains to said hydrophobic domains ranges between approximately 40% and 60%.

13. The gas diffusion layer according to claim 12, wherein said hydrophilic domains are formed from one of particles and fibers.

14. The gas diffusion layer according to claim 13, wherein the gas diffusion layer is in one of a membrane electrode unit, a PEM fuel cell, an electrochemical sensor and an electrolyte cell.

15. A method for manufacturing a gas diffusion layer for a fuel cell with a polymer electrolyte membrane (PEM) having structured hydrophilic properties, the method comprising the steps of: selecting one of finely dispersive hydrophilic materials and precursors of said hydrophilic materials, said materials and said precursors being selected from a group including sol-gels, metal oxide precursors and volatile metal compounds and having an average particle size of approximately 0.1 μm to 10 μm; andintroducing one of said finely dispersive hydrophilic materials and said precursors of said finely dispersive hydrophilic materials in the gas diffusion layer.

16. The method according to claim 15, wherein said introduction is by one of screen printing and gravure printing.

17. The method according to claim 15, wherein said introduction step is performed with a plurality of masks through one of spray coating, laser and radiation treatment, plasma deposition, chemical deposition and physical gas phase deposition.

18. The method according to claim 15, wherein said introduction step is performed at least one of: following completion of the gas diffusion layer;during creation of the gas diffusion layer by admixing a plurality of hydrophilic fibers;prior to applying at least one of hydrophobic and pore-size-regulating substances; andsimultaneously with an application of said at least one of hydrophobic and said pore-size-regulating substances.