Gas sensors with improved resistance to humidity interference

Abstract
Semiconductor gas-sensitive materials of the formula Cr2−xTixO3 where 0.05>x≧0.0001, and gas sensors formed therefrom.
Description


[0001] Foremost amongst the many technical challenges facing manufacturers of semiconductor sensors/detectors is the need to avoid false alarms. A common cause of false alarms is the presence in the vicinity of the detector of a gas (so-called interference gas) to which the detector responds in a way similar to that for the target gas. Another cause is a change in relative humidity. It is this unfortunate sensitivity of gas-sensitive semiconductors to the vapor pressure of water that has resulted in the sensor chips being run at temperatures of 150° C. or higher. Even then, problems associated with changes in relative humidity still pertain. With increasing demands placed on the performance of carbon monoxide sensors/detectors for domestic use, there is a need to reduce the sensitivity to water vapor still further.


[0002] Pure chromium oxide, Cr2O3, is itself gas-sensitive, as demonstrated in FIG. 1. However, at the low temperatures necessary to develop a signal to a gas of interest, the response and recovery are rather slow while the effect of variation in the water vapour concentration is unacceptably large (both on the sensor resistance and on the sensitivity to other gases). These effects preclude the use of pure Cr2O3 as a gas-resistive material, since sensors for practical use are required to have respectable response/recovery times and, as mentioned above, to be reasonably resistant to relative humidity changes.


[0003] However, the presence of minor oxide additions such as TiO2 have two distinct effects on Cr2O3: a significant increase in the electrical resistivity and the movement of the temperature for optimum sensitivity (for gases such as carbon monoxide) to much higher values—very desirable from a practical viewpoint. Accordingly, the system Cr—Ti—O has found use commercially as a sensor material in the detection of oxidisable organic and inorganic gases. For example, Capteur Sensors market a Carbon Monoxide sensor, NGL07, which incorporates a 90 micron thick layer of Cr—Ti—O heated to circa. 400° C. For the compositional range, Cr2−xTixO3where 0.05≦x≦0.45, gas sensitivities are high and sensitivity to moisture is respectably low.


[0004] In this document, we will demonstrate the surprising and advantageous effects of a much lower titanium substitution in Cr2−xTixO3. We have found that gas sensors based on the Cr—Ti—O system within the compositional window 0.05>r≧0.0001 combine the benefits of improved resistance to relative humidity changes an a respectable gas sensitivities.


[0005] The teaching in the literature with regard to the chromium oxide rich region of the Cr—Ti—O system is confusing and somewhat contradictory. FIG. 91-025 in “Phase diagrams for Ceramists” suggests a solid solubility limit of x˜0.06 for TiO2 in Cr2O3. Sonnja et al (Journal of Solid state Chemistry (1978), 25, pages 273-284) report a 2-phase mixture of Cr2O3 and E-phase (Cr2Ti2O7) from ˜47 wt % Cr2O3 to pure Cr2O3. Both of these studies were for reaction temperatures above 1300° C. Dyama et al (Nippon Kagaka (1993), No. 7, pages 825-830) reported the preparation of Cr2−xTixO3 by a vapour-phase explosive reaction. A solid solution extending up to x=0.5 was reported. Jayaraman et al (Sensors and Actuators B55 (1999), pages 175-179) fired mixtures of Cr2O3 and TiO2 to 1000° C. and reported a solid solution with 0.1<x<0.4. The presence of CrTiO3 as a minor phase was also reported. Henshaw et al (Journal of Materials Chemistry (1995), 5, pages 1791-1800) also reported a solid solution with x≦0.4 following firing at 1000° C.


[0006] It is well known to those skilled in the art that in the firing of ceramics, sintering competes with grain coarsening. From the viewpoint of sensitivity to gases, gain coarsening is undesirable as a reduction in surface area, and therefore catalytic activity, results. In the literature, titanium oxide is reported as a sintering aid for Cr2O3. Sintering aids promote development of the neck between grains and greater neck development should result in a reduced resistance. For pure Cr2O3, grain coarsening will dominate but as the level of TiO2 addition increases, particle coarsening will become suppressed and sintering will start to dominate. We have found that at very low levels of TiO2 additions before TiO2 “kicks in” as a sintering aid, it is remarkably surface active and that this surface activity contributes to an increase in gas sensitivity. Coincident with this incres in gas sensitivity is an increase in the degree of interference from humidity changes. Accordingly, a compositional window exists which provides an optimum balance between gas sensitivity and reduced humidity effects. The lower bound of this range is determined by the minimum amount of titanium required to obtain a sensor signal, which we have determined to be x˜0.001. The upper bound is defined by the error in CO prediction caused by changes in reative humidity effects, which is x<0.05 (giving an error≦100 ppm for a 400 ppm CO gas).


[0007] The following Examples support and illustrate the invention:






EXAMPLE 1

[0008] Gas-sensing Properties of Pure Cr2O3


[0009] Ultrafine chromia powder was produced from the decomposing ammonia dichromate by heating to 400° C. Pellets of 1 cm diameter and 3 mm thick were made from the powder by means of a manual press (1 tonne weight applied over surface of pellet), and fired to 1000° C. for 4 hours in air. The fired pellets were placed between two gold electrode disks in a specially constructed jig. Electrical contact between pellet and electrode was achieved by applying pressure via a spring-loaded arrangment Gold wires spot-welded to the gold disks were fed to an ohmeter. This jig assembly was placed inside a tube-furnace and fired to 800° C. to consolidate the gold/pellet contacts and cooled to 200° C. in steps of 50° C. At each temperature interval, CO-air mixture were introduced with the CO concentration varying from 30 ppm to 400 ppm. A measurable response to low concentrations of carbon monoxide is observable but only for rather low operation temperatures (≦250° C). For temperatures greater than approx. 300° C., the signal is small or non-existent.



EXAMPLE 2

[0010] Surface Segregation of Titanium


[0011] Mixtures of Cr2O3 and TiO2 powders were weighed out to give compositions in the range 0<x<45 and homogenised by ball-milling in propanol for 24 hours. The Cr2O3 was produced as described in Example 1. Pellets were prepared according to the method of Example 1. Compositional analysis of the surface of the various pellets was carried out in an ESCA VG instrument. The results are shown in FIG. 2 where the surface composition of titanium is plotted as a function of x in the starting composition. Noteworthy is that the surface segregation is most marked when values of x are very low. As x increases, the ratio (Ti/(Ti+Cr))surface/(Ti/(Ti+Cr))bulk approaches 2, i.e. the surface composition approaches Cr2Ti2O7 or CrTiO3.



EXAMPLE 3

[0012] CO Response as a Function of x Where 0.01<x<0.2.


[0013] In this example, sensor devices were constructed in accordance with the construction described in Capteur Sensors data sheet for NGL07. However, the filter cap was not used and the production Cr—Ti—O layer was replaced with various Cr2—xTixO3 layers Starting materials of pigment-grade Cr2O3 (surface area=7 m2/g) and ultrafine TiO2 (surface area=55 m/g) were weighed out to give compositions in the range 0.8≦x≦0.01. The mixtures were homogenised by wet-milling in propanol, sieved through a 38 micron mesh followed by calcining at 1000° C. for 4 hours. The calcined mixtures were made into a screen-printing ink by mixing with a proprietary vehicle system supplied by ESL (Reading, UK) in the ratio 55 wt % solids:45 wt % vehicle. The ink was printed onto an alumina tile over an interdigitated gold electrode pattern so as to give an unfired thickness of 90 microns. The underside of the tile contained a platinum serpentine track heater. The resulting structure was fired to 800° C. prior to assembling into the standard build. The sensors were powered up to approx. 400° C. in 50% RH lean air. Following stabilisation for a period of 20 minutes, the sensors were exposed to wet air (20 minutes), dry air (20 minutes), wet air (20 minutes) followed by exposure to a 400 ppm CO—clean air gas mixture at 50 %RH for 20 minutes. The ratio of sensor resistance to 400 ppm CO (Rgwet):sensor resistance in wet air (Rowet) as a function of x is shown plotted in FIG. 3.



EXAMPLE 4

[0014] Humidity Response as a Function of x Where 0.01<x<0.2


[0015] As for Example 3, where the function 100%×(Rowet−Rodry)/Rowet)) with Rowet is the sensor resistance in wet air (50% RH) and Rodry is the sensor resistance in dry air, respectively, is shown plotted as a function of x in FIG. 4.



EXAMPLE 5

[0016] Error in CO Predictability as a Function of x Where 0.01<x<0.2


[0017] As for Example 3, where the error in CO predictability for 40 ppm CO in dry conditions (for sensors calibrated in wet conditions) is shown plotted as a function of x in FIG. 5. The error is calculated from the following equation:


Error=400−400×D2/W2


[0018] Where D=(Rgdry/Rodry−1)2 and W=(Rgwet/Rowet−1)2 and Rgdry is the sensor resistance in 400 ppm CO in dry conditions.



EXAMPLE 6

[0019] Baseline Resistance as a Function of x Where 0.01<x<0.2


[0020] As for Example 3, where the sensor resistance in wet air (50% RH) is plotted as a function of x in FIG. 6.


Claims
  • 1. A semiconductor gas-sensitive material of the formula:
  • 2. A material according to claim 1 when in a single phase.
  • 3. A material according to claim 1 when in more than one phase.
  • 4. A material according to any of claims 1 to 3 which additionally contains one or more oxides or metals which do not degrade the sensitivity of the material.
  • 5. A gas sensor comprising a sensor as claimed in any of claims 1 to 4 for detecting reducing inorganic or organic gases.
  • 6. The use of a sensor as claimed in claim 5 for sensing or detecting a reducing gas.
  • 7. The use according to claim 6 wherein the gas is CO.
Priority Claims (1)
Number Date Country Kind
0011704.4 May 2000 GB
PCT Information
Filing Document Filing Date Country Kind
PCT/GB01/02046 5/9/2001 WO