Gas storage using transition metal dichalcogenides

Abstract

Hydrogen and gaseous hydrocarbons are stored by introducing the gases into a transition metal dichalcogenide having the formula MX.sub.2. M is selected from the group consisting of Mo, W and Ti and X is selected from the group consisting of S and Se. The MX.sub.2 is in the form of platelets affixed to basal planes of adjacent platelets. The basal planes of adjacent platelets are separated by voids. The composition is prepared by intercalating MX.sub.2 powder with lithium, adding water to separate the MX.sub.2 into single layers and then adding acid to adjust the pH to a range where edges and basal planes of the single layers have opposite charges. Preferably a catalyst is added to the MX.sub.2, the catalyst being selected from the group of metals consisting of Pt, Pd, Ni, Co, Fe, Mg, Zr, Cr, Al, Zn, Mn or combinations thereof. The gas can be recovered from the composition by heating to a temperature of 250.degree. C. when the catalyst is used.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to compositions of transition metal dichalcogenides for storing hydrogen and gaseous hydrocarbons and methods for preparation thereof.

2. Description of Related Art

There has been intense interest and considerable research activity directed to ways for storing hydrogen gas other than the conventional manner as a highly compressed gas. The cylinders used to store the compressed gas are heavy, costly and potentially dangerous because of the high pressure of flammable gas they contain. One reason for the great activity in pursuing a better storage system is the potential use of hydrogen as an ecologically sound substitute for gasoline as a vehicle fuel. Prototype vehicles burning hydrogen fuel have already been produced, but one of the factors delaying production is the lack of an acceptable storage means. Preferably, the storage means should also be suitable for gaseous hydrocarbons as well.

Materials have been developed which aid in storing such gases at relatively low pressures. Desirable characteristics of suitable materials include (a) the ability to adsorb or absorb large quantities of the gas in a minimum volume, (b) provision for easy access of the gases to the adsorption or absorption sites, and (c) easy reversibility so that the gas can be reclaimed from the storage material easily and conveniently.

One approach has been to use materials which form hydrides which are easily decomposed. See, for example, U.S. Pat. No. 4,948,423 and 5,002,730 to Fetcenko as well as U.S. Pat. No. 4,946,646, 4,923,770, 4,915,898 and 5,006,328. Examples of such materials are LaNi.sub.5, CaNi.sub.5, FeTi, Mg.sub.2.4.Ni and CoNi.sub.5. These materials absorb hydrogen, allowing large quantities of the gas to be stored. Each of the above compositions covers a certain range of pressure and temperature. For example, LaNi.sub.5 performs well between 1-2 atm at 20.degree. C., forming the hydride of LaNi.sub.5 H.sub.6. CaNi.sub.5 is a low pressure hydride, below 0.5 atm. FeTi operates at 10 atmospheres and Mg.sub.24.Ni works at high pressures of 10 atm and at high temperatures--more than 300.degree. C. The gas is reclaimed by heating the cylinder or other container.

Many of such materials do not provide satisfactory storage and release of the gas. There is simply no way in which the gas has access to the interior of such materials to react therewith. In order to provide pores through which the gas can move to and from the absorption sites, the absorbent is typically supported by a material, such as alumina particles, that have no role in the absorption process as such, and take up valuable space as well as adding weight. The alumina particles are typically pelletized into small pellets of approximately 1 cm.sup.3, to permit gas movement. The gas can move between the pellets freely, and with the small pellets can enter the pores of the pressed alumina and reach the absorbent.

The production of single molecular thickness layers of MoS.sub.2 and other transition metal dichalcogenides is disclosed in U.S. Pat. No. 4,822,590 to S. Roy Morrison et al. The MoS.sub.2 is exfoliated into monolayers by intercalation with lithium followed by reaction with water. The reaction between the water and the lithium forces the layers of MoS.sub.2 apart into one-molecule-thick platelets. Flocculation occurred rapidly when the pH was reduced to a value of 3 or less.

U.S. Pat. No. 4,996,108 to Divigalpitya et al. carries this process further by forming a suspension of a transition metal dichalcogenide in water and adding to the suspension a liquid which is immiscible with water. The mixture is agitated, then allowed to rest. A sheet-like composition of about 500 .ANG. to 750 .ANG. forms at the interface of the water and the immiscible liquid.

In U.S. Pat. No. 4,853,359 to Morrison et al., a novel flocculated, supporting single-layered transition metal dichalcogenide catalyst is disclosed. The patent discloses that if the pH is maintained at a value about 3, the suspension of MoS.sub.2 will not flocculate, but will stay four days or more suspended in water. The next step in producing the catalyst according to the patent is to add a catalytic promoter to the suspension. A solid is formed by adding this promoter or support substance to the water. The flocculated solid is then separated from the liquid.

In an Article, J. Appl. Phys. 69(9) 6373 (1991) by Miremadi et al., the deposition of thick oriented films of a transition metal dichalcogenide, with a thickness in the order of 0.1 to 10 microns, is disclosed.

In pending U.S. patent application No. 07/704,432, a novel transition metal dichalcogenide with a house-of-cards (HOC) structure is disclosed and method for production thereof. The method involves reducing the pH of a suspension of single molecular thickness platelets of MoS.sub.2, or other transition metal dichalcogenides, until they flocculate, and the pH is within a range between a first pH where basal planes of the platelets have a zero charge and a second pH where edges of the platelets have a zero charge.

SUMMARY OF THE INVENTION

It is an object of the invention to provide an improved hydrogen storage medium wherein the absorbent is effective by itself without the addition of large quantities of inert materials, such as alumina pellets.

It is also an object of the invention to provide a storage medium for hydrogen and other gases, wherein the gas can be recovered relatively easily, for example by heating the medium to a relatively low temperature.

It is a further object of the invention to provide a storage medium for hydrogen and other gases, which is capable of storing relatively large quantities of gas at a low pressure with a relatively small volume and weight of the storage medium.

In accordance with these objects, one aspect of the invention provides a method for storing a gas selected from the group consisting of hydrogen and gaseous hydrocarbons. The method comprises introducing the gas into a transition metal dichalcogenide having the formula MX.sub.2. M is selected from the group consisting of Mo, W and Ti and X is selected from the group consisting of S and Se. The MX.sub.2 is in the form of platelets which have edges affixed to basal planes of adjacent platelets, and wherein the basal planes of adjacent platelets are separated by voids. The gas may be recovered by heating the MX.sub.2 to about 250.degree. C.

Preferably, the MX.sub.2 is coated with a catalyst selected from the group consisting of Pt, Pd, Ni, Co, Fe, Mg, Zr, Cr, Al, Zn, Mn or combinations thereof.

Another aspect of the invention provides a composition having the formula Y-MX.sub.2, MX.sub.2 is in the form of platelets having edges affixed to basal planes of adjacent said platelets with basal planes of adjacent platelets being separated by voids. The M is selected from the group consisting of Mo, W and Ti. X is selected from the group consisting of S and Se. The MX.sub.2 is coated with Y which is selected from the group consisting of Pt, Pd, Ni, Co, Fe, Mg, Zr, Cr, Al, Zn, Mn or combinations thereof.

A further aspect of the invention provides a method for producing a hydrogen gas storage medium. MX.sub.2 is intercalated with lithium. M is selected from the group consisting of Mo, W and Ti. X is selected from the group consisting of S and Se. Water is added to the lithium intercalated MX.sub.2 to separate the MX.sub.2 into single layers. An acid is added to the single-layered MX.sub.2 to adjust the pH to a pH in the range where edges and basal planes of the single layers have opposite charges. A cataylst is added to the MX.sub.2 which is selected from the group consisting of Pt, Pd, Ni, Co, Fe, Mg, Zr, Cr, Al, Zn, Mn or combinations thereof. Preferably, the MX.sub.2 is heated in hydrogen to 400.degree. C. after the pH is adjusted.

BRIEF DESCRIPTION OF THE DRAWING

The drawing is a graph showing a plot of pressure-composition isotherms for hydrogen desorption for various materials.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The preferred basic material used for the storage of hydrogen or the other gases according to the invention is MoS.sub.2 which is prepared with the House of Cards (HOC) structure. Lithium is intercalated into powdered MoS.sub.2. The powder is immersed in water to generate hydrogen, separating the layered compound into single layers. Next, the pH is lowered in a controlled way to pH=2.0. This is the point of zero charge for MoS.sub.2 where the HOC structure is formed. The pH is 2 for MoS.sub.2. The applicable pH varies if other transition metal dichalcogenides are substituted.

The MoS.sub.2 is heated in hydrogen at 400.degree. C. to stabilize the HOC structure, presumably causing a reaction at the contacting points between the edges and basal planes of adjacent platelets. The open structure has all the desirable characteristics for storage of the hydrogen or other gases, assuming that the gases can be absorbed by the MoS.sub.2 in large quantities at low temperature and also removed at low temperature. These requirements have been established by the present invention.

The HOC MoS.sub.2 itself has been found to be effective for storing hydrogen and other gases. This is due to the structure which is characterised by single layers of MoS.sub.2 stacked in a particularly open structure. The layers are about 6 .ANG. thick and about 1000 .ANG. in diameter. It was found that by cycling the temperature, hydrogen adsorbs on the HOC MoS.sub.2 in an amount equivalent to a high pressure storage tank at 1000 psi. In other words, a tank filled with HOC MoS.sub.2 would hold the same amount of gas at atmospheric pressure as the same tank would hold at 1000 psi without the MoS.sub.2. The gas was removed from the MoS.sub.2 by heating the adsorbent to 250.degree. C.

However, further efforts were made to produce an improved adsorbent which would not require such a high temperature cycle. Various metals, including nobel metals are known to catalyze the dissociation of the hydrogen or gaseous organic. Thus, a catalyst was introduced into the HOC MoS.sub.2 to help dissociate the H.sub.2 at room temperature. The catalyst may be Pt, Pd, Ni, Co, Fe, Mg, Zr, Cr, Al, Zn, Mn or combinations thereof.

With MoS.sub.2 untreated with a catalyst, the adsorption at room temperature corresponded to the gas stored in a pressure tank at 20 psi. However, with 0.1 atomic % Pt to Mo in HOC MoS.sub.2, the amount stored corresponded to the gas stored at a pressure of 40 psi. It was found that the gas can be added or removed in about ten minutes.

The HOC MoS.sub.2 may also be used as a support for the standard "hydrideforming" materials used for storage, including LaNi.sub.5, CdNi.sub.5,CaNi.sub.5 FeTi, CoNi.sub.5 and Mg.sub.2.4.Ni. The use of HOC MoS.sub.2 as a support is preferred over alumina, because the support itself is highly active in helping to store the gas and is of the open structure needed for rapid gas adsorption and removal without requiring pellets or the like.

The materials, HOC MoS.sub.2 -H, HOC MoS.sub.2 -Pt.sub.0.1 -H and HOC MoS.sub.2 -Pd.sub.0.2 -H all perform at room temperature and 1.5 atm as one-hydrogen hydrides. In other words, the Pd and the Pt have no effect except to catalyze the dissociation of the hydrogen. Approximately one hydrogen per molecule of MoS.sub.2 is absorbed. At elevated temperature however, specifically 200.degree. C., higher hydrides are formed as in Table 1:

TABLE 1______________________________________Formula Material H Absorbed per Molecule______________________________________A HOC MoS.sub.2 H.sub.2B HOC MoS.sub.2 -- Pt.sub.0.1 H.sub.4C HOC MoS.sub.2 -- Pd.sub.0.2 H.sub.6______________________________________

FIG. 1 shows a plot of pressure-composition isotherms for hydrogen desorption. The number of hydrogen atoms is represented by x. For example for formulas A, B, and C at room temperature and 1.5 atm, x=1. At 200.degree. C. and 1 atmosphere, x=4 for B, and at 200.degree. C. and at 1 atm, x=6 for C, as indicated in Table 1. For comparison the pressure/composition isotherm for LaNi.sub.5 is also presented. This is a high purity material specifically prepared for hydrogen storage material obtained from Alpha products, Johnson Mathers Inc. It is observed for this material that x=6 at room temperature and 1.3 atm. The plot of data for Formula A is not shown in the graph. At 200.degree. C. and 1 atm., x=2 for this material.

To compare the materials described in this invention with those currently available, it should be noted that the adsorption/desorption process is much easier with materials according to the invention than, for example, with LaNi.sub.5, CaNi.sub.5 or FeTi. With the HOC materials, hydrogen adsorbed at 20.degree. C. shows a desorption peak at 70.degree. C., while hydrogen adsorbed at 200.degree. C. shows a desorption peak at 270.degree. C. By comparison, for LaNi.sub.5, CaNi.sub.5 or FeTi, all desorption peaks are above 300.degree. C., even when the adsorption is done at room temperature.

EXAMPLE 1

MoS.sub.2 obtained from MRC Inc., was immersed in n-butyllithium dissolved in hexane. The suspension was stored in a dry box for more than 24 hours to intercalate the MoS.sub.2 with lithium. The lithiated powder was washed with hexane and dried in a dry box. The powder was immersed in water for the Li/H.sub.2 O reaction and hydrogen was seen to evolve. The single layers formed were in a suspension in a LiOH solution. The single layers were washed to remove the excess lithium and introduced slowly into a pH 2.0 solution of HNO.sub.3. The material flocculated in a form recognizable as the HOC structure by the absence of a (002) x-ray diffraction line, indicating no contact between the basal planes.

The HOC MoS.sub.2 was dried at room temperature, then the HOC MoS.sub.2 was inserted into a pumpable system and hydrogen was admitted at a pressure of 1 atmosphere. The temperature was cycled to 225.degree. C. and then back to room temperature. The excess hydrogen was pumped off, and the sample was heated to evolve the remaining adsorbed hydrogen. The hydrogen was then desorbed by a temperature-program desorption (TPD) cycle, reaching a temperature of 250.degree. C. It was found that the amount adsorbed was 6.5.times.10.sup.-3 moles/g. By calculation, it may be shown that this corresponds to 2000 psi equivalent.

EXAMPLE 2

A 100 mg sample of the HOC MoS.sub.2 powder as described in Example 1 was placed in a test tube. 0.1 g of PtCl.sub.4 in HCl, having a volume of about 0.15 cc, was introduced into the test tube to prepare a slurry, which was stirred for uniformity. The slurry was dried in air at room temperature. The sample was heated to 400.degree. C. in a vacuum for 60 minutes and then cooled to room temperature. The sample, as described Example 1 was exposed to one atm of hydrogen at 20.degree. C. The system was pumped out quickly, the pump closed off, and the gas adsorbed was measured by TPD. With hydrogen adsorption at room temperature, the hydrogen release peaked at 125.degree. C. with the total released hydrogen being measured at 3.1.times.10.sup.-3 moles/g or 3 moles H/Kg MoS.sub.2 or 6.2 g H/6.25.times.FW (MoS.sub.2 =160). Therefore 1H atom per FW (Formula Weight) MoS.sub.2 is desorbed, viz. MoS.sub.2 -H.

EXAMPLE 3

A 100 mg sample of HOC MoS.sub.2 powder was prepared as described in Example 1. The powder was inserted into a pumpable container and the gases evacuated. The container was sealed and immersed in a solution containing the additive of interest, Pd in this example. The seal was opened and the solution impregnated the evacuated pores of the MoS.sub.2. The process yielded a much more even distribution of metal in the pores of the HOC MoS.sub.2.

Claims

1. A method for storing and recovering a gas selected from the group consisting of hydrogen and gaseous hydrocarbons, the method comprising:

adsorbing or absorbing the gas with a transition metal dichalcogenide having the formula:

MX.sub.2

wherein M is selected from the group consisting of Mo, W and Ti and X is selected from the group consisting of S and Se, the MX.sub.2 being in the form of platelets which have edges affixed to basal planes of adjacent platelets and wherein the basal planes of adjacent platelets are separated by voids, the MX.sub.2 contacting a catalyst selected from the group consisting of Pt, Pd, Ni, Co, Fe, Mg, Zr, Cr, Al, Zn, Mn and mixtures and salts thereof; and

recovering the gas by heating the MX.sub.2 to 125.degree. C., the catalyst catalyzing the recovery of the gas.

2. A method as claimed in claim 1, wherein the platelets have a single molecule thickness.

3. A method as claimed in claim 1, wherein the platelets are 6 .ANG. thick.

4. A method as claimed in claim 1, wherein the catalyst is in the form of a salt.

5. A method as claimed in claim 1, wherein the MX.sub.2 is coated with a hydrogen absorbent selected from the group consisting of La, Ni, Fe, Ti, Mg, Co, and compounds thereof apart from said MX.sub.2.

6. A method as claimed in claim 1, wherein the MX.sub.2 is treated with a hydrogen absorbent selected from the group consisting of LaNi.sub.5, CaNi.sub.5, FeTi, Mg.sub.24.Ni and CoNi.sub.5.

7. A method as claimed in claim 1, wherein the MX.sub.2 is a powder.

8. A method for storing and recovering a gas selected from the group consisting of hydrogen and gaseous hydrocarbons, the method comprising:

adsorbing or absorbing the gas with a transition metal dichalcogenide having the formula:

MX.sub.2

wherein

M is selected from the group consisting of Mo, W and Ti and X is selected from the group consisting of S and Se, the MX.sub.2 being in the form of platelets which have edges affixed to basal planes of adjacent platelets and wherein the basal planes of adjacent platelets are separated by voids; and

recovering the gas by heating the MX.sub.2 to 250.degree. C.

9. A method as claimed in claim 8, wherein the MX.sub.2 is coated with a hydrogen absorbent selected from the group consisting of La, Ni, Fe, Ti, Mg, Co, and compounds thereof apart from said MX.sub.2.

10. A method as claimed in claim 8, wherein the MX.sub.2 is coated with a hydrogen absorbent selected from the group consisting of LaNi.sub.5, CaNi.sub.5, FeTi, Mg.sub.2.4 .Ni and CoNi.sub.5.