Patent Application
20220018291
A gas turbine engine typically includes a fan section, a compressor section, a combustor section, and a turbine section. Air entering the compressor section is compressed and delivered into the combustor section where it is mixed with fuel and ignited to generate a high-speed exhaust gas flow. The high-speed exhaust gas flow expands through the turbine section to drive the compressor and the fan section. The compressor section typically includes low and high pressure compressors, and the turbine section includes low and high pressure turbines.
A gas turbine engine also includes bearings that support rotatable shafts. The bearings require lubricant. Various seal assemblies near the rotating shafts contain oil within bearing compartments. Specifically, during operation of the engine, non-rotating seal faces contact rotating seal plates to maintain bearing compartment pressures and keep lubricating oil inside the various bearing compartments.
A gas turbine engine according to an exemplary aspect of the present disclosure includes, among other things, a compressor section, a combustor section, a turbine section, and at least one rotatable shaft. The engine further includes a seal assembly including a seal plate mounted for rotation with the rotatable shaft and a face seal in contact with the seal plate at a contact area. The seal assembly further includes an abradable coating adjacent the contact area, and wherein the abradable coating includes magnetic particles.
In a further non-limiting embodiment of the foregoing gas turbine engine, the abradable coating includes particles of an alloy.
In a further non-limiting embodiment of any of the foregoing gas turbine engines, the alloy includes iron (Fe).
In a further non-limiting embodiment of any of the foregoing gas turbine engines, the alloy further includes nickel (Ni) and aluminum (Al).
In a further non-limiting embodiment of any of the foregoing gas turbine engines, the alloy further includes chrome (Cr), nickel (Ni), and carbon (C).
In a further non-limiting embodiment of any of the foregoing gas turbine engines, the particles are deposited on at least one of the face seal, the seal plate, and a seal carrier supporting the face seal using a thermal spray coating process.
In a further non-limiting embodiment of any of the foregoing gas turbine engines, the abradable coating includes a solid lubricant.
In a further non-limiting embodiment of any of the foregoing gas turbine engines, the lubricant is hexagonal boron nitride (h-BN) or molybdenum disulfide (MoS2).
In a further non-limiting embodiment of any of the foregoing gas turbine engines, the abradable coating is applied to one or both of a face seal and a seal carrier holding the face seal, the abradable coating is positioned such that, in normal operating conditions, the seal plate does not contact the abradable coating, and the abradable coating is positioned such that, in a worn seal condition, the seal plate contacts the abradable coating and releases at least some particles of the abradable coating.
In a further non-limiting embodiment of any of the foregoing gas turbine engines, the abradable coating is a sacrificial coating.
In a further non-limiting embodiment of any of the foregoing gas turbine engines, the abradable coating is positioned, in normal operating conditions, radially outward of the contact area.
In a further non-limiting embodiment of any of the foregoing gas turbine engines, a bearing assembly is mounted relative to the rotatable shaft, and the seal assembly is adjacent the bearing assembly.
In a further non-limiting embodiment of any of the foregoing gas turbine engines, the face seal is made of a carbon material.
A bearing compartment for a gas turbine engine according to an exemplary aspect of the present disclosure includes, among other things, a bearing assembly and a seal assembly including a seal plate and a face seal in contact with the seal plate at a contact area. The seal assembly includes an abradable coating adjacent the contact area. Further, the abradable coating includes magnetic particles.
In a further non-limiting embodiment of the foregoing bearing compartment, the abradable coating further includes particles of an alloy.
In a further non-limiting embodiment of any of the foregoing bearing compartments, the abradable coating is applied to one or both of a face seal and a seal carrier holding the face seal, the abradable coating is positioned such that, in normal operating conditions, the seal plate does not contact the abradable coating, and the abradable coating is positioned such that, in a worn seal condition, the seal plate contacts the abradable coating and frees at least some magnetic particles of the abradable coating.
The embodiments, examples and alternatives of the preceding paragraphs, the claims, or the following description and drawings, including any of their various aspects or respective individual features, may be taken independently or in any combination. Features described in connection with one embodiment are applicable to all embodiments, unless such features are incompatible.
The exemplary engine 20 generally includes a low speed spool 30 and a high speed spool 32 mounted for rotation about an engine central longitudinal axis A relative to an engine static structure 36 via several bearing systems 38. It should be understood that various bearing systems 38 at various locations may alternatively or additionally be provided, and the location of bearing systems 38 may be varied as appropriate to the application.
The low speed spool 30 generally includes an inner shaft 40 that interconnects, a first (or low) pressure compressor 44 and a first (or low) pressure turbine 46. The inner shaft 40 is connected to the fan 42 through a speed change mechanism, which in exemplary gas turbine engine 20 is illustrated as a geared architecture 48 to drive a fan 42 at a lower speed than the low speed spool 30. The high speed spool 32 includes an outer shaft 50 that interconnects a second (or high) pressure compressor 52 and a second (or high) pressure turbine 54. A combustor 56 is arranged in exemplary gas turbine 20 between the high pressure compressor 52 and the high pressure turbine 54. A mid-turbine frame 57 of the engine static structure 36 may be arranged generally between the high pressure turbine 54 and the low pressure turbine 46. The mid-turbine frame 57 further supports bearing systems 38 in the turbine section 28. The inner shaft 40 and the outer shaft 50 are concentric and rotate via bearing systems 38 about the engine central longitudinal axis A which is collinear with their longitudinal axes.
The core airflow is compressed by the low pressure compressor 44 then the high pressure compressor 52, mixed and burned with fuel in the combustor 56, then expanded over the high pressure turbine 54 and low pressure turbine 46. The mid-turbine frame 57 includes airfoils 59 which are in the core airflow path C. The turbines 46, 54 rotationally drive the respective low speed spool 30 and high speed spool 32 in response to the expansion. It will be appreciated that each of the positions of the fan section 22, compressor section 24, combustor section 26, turbine section 28, and fan drive gear system 48 may be varied. For example, gear system 48 may be located aft of the low pressure compressor, or aft of the combustor section 26 or even aft of turbine section 28, and fan 42 may be positioned forward or aft of the location of gear system 48.
The engine 20 in one example is a high-bypass geared aircraft engine. In a further example, the engine 20 bypass ratio is greater than about six (6), with an example embodiment being greater than about ten (10), the geared architecture 48 is an epicyclic gear train, such as a planetary gear system or other gear system, with a gear reduction ratio of greater than about 2.3 and the low pressure turbine 46 has a pressure ratio that is greater than about five. In one disclosed embodiment, the engine 20 bypass ratio is greater than about ten (10:1), the fan diameter is significantly larger than that of the low pressure compressor 44, and the low pressure turbine 46 has a pressure ratio that is greater than about five 5:1. Low pressure turbine 46 pressure ratio is pressure measured prior to inlet of low pressure turbine 46 as related to the pressure at the outlet of the low pressure turbine 46 prior to an exhaust nozzle. The geared architecture 48 may be an epicycle gear train, such as a planetary gear system or other gear system, with a gear reduction ratio of greater than about 2.3:1 and less than about 5:1. It should be understood, however, that the above parameters are only exemplary of one embodiment of a geared architecture engine and that the present invention is applicable to other gas turbine engines including direct drive turbofans, low bypass engines, and multi-stage fan engines.
The bearing compartment 60 is representative of any bearing compartment within the engine 20. Further, the shaft 72 is representative of any shaft within the engine 20, such as the inner shaft 40 or the outer shaft 50. This disclosure is not limited to bearing compartments at any particular engine location. Further, this disclosure applies outside the context of bearing compartments.
The seal assembly 64 includes a face seal 74 and a seal plate 76. In this example, the face seal 74 is mounted to a static structure, namely a seal carrier 78, and therefore does not rotate during operation of the engine 20. The face seal 74 may be made of a carbon (C) material, however other materials come within the scope of this disclosure.
The face seal 74 is biased against, and in direct contact with, the seal plate 76. In particular, either the seal carrier 78 itself is configured to bias the face seal 74 axially toward the seal plate 76, or another structure biases the seal carrier 78, and in turn the face seal 74, axially toward the seal plate 76.
The seal plate 76 is configured to rotate about the engine central longitudinal axis A with the shaft 72. The contact area, namely the region where the face seal 74 directly contacts the seal plate 76, between the face seal 74 and the seal plate 76 ensures that cooling fluid, namely lubricant such as oil, remains within the bearing compartment 60 during operation of the gas turbine engine 20. Over time, the face seal 74 and/or the seal plate 76 may wear. This disclosure relates to detection of such wear. In particular, this disclosure relates to an abradable coating that permits detection of undue wear at the interface between the face seal 74 and/or the seal plate 76.
An abradable coating 90 is applied to an axial end face 92 of the seal carrier 78, in this example. The axial end face 92 faces toward the seal plate 76. In this example, the abradable coating 90 projects axially from the axial end face 92 in a direction toward the seal plate 76. The abradable coating 90 is arranged on the seal carrier 78 radially outward of the projection 86 such that the seal plate 76 does not contact the abradable coating 90 during normal operating conditions. In other words, the contact area 80 is radially spaced-apart from, and in particular radially inward of, the abradable coating 90.
While in
In
The abradable coating 90, in this disclosure, includes a binder that holds the coating together, magnetic particles, and lubricants. The abradable coating 90 may also include a polyester material which is removed to create a porosity. These aspects of the abradable coating 90 will now be described in more detail.
In one example, the abradable coating 90 includes magnetic particles within a binder of particles of a metal alloy. Alternatively, the binder may be ceramic. The particles forming the abradable coating 90 are deposited on the seal carrier 78, in this example, using a process such as air plasma spraying (APS) or flame spraying (FS), or by another type of thermal spraying technique such as a high velocity oxygen fuel (HVOF) coating process or another similar process. In an example, the magnetic particles may include iron (Fe), iron oxides (Ferric oxide Fe2O3 and magnetite Fe3O4), actinide ferromagnets, Alnico alloy (an iron alloy with aluminum, nickel and cobalt), Yttrium iron garnet (Y3Fe2(FeO4)3 or Y3Fe5O12). Further, the alloy may include iron (Fe). In a further example, the alloy further includes nickel (Ni) and aluminum (Al). In that example, the alloy includes, by atomic weight, 35% nickel (Ni), 6% aluminum (Al), and a balance of iron (Fe). Another example alloy includes, in addition to iron (Fe), chrome (Cr), nickel (Ni), and carbon (C). Specifically, that alloy includes, by atomic weight, 18% chrome (Cr), 2% nickel (Ni), 0.2% carbon (C), and a balance of iron (Fe).
In another aspect of this disclosure, in order to increase the ease of releasing the particles 94, the abradable coating 90 may be formed such that it is porous. In this example, the alloy is initially deposited with a polyester material. The deposited alloy-polyester mixture is then heated to remove all or substantially all of the polyester material. In this respect, the polyester material is not intended to hold the alloy particles together or to adhere the alloy particles to the seal carrier 78, for example. Rather, the function of the polyester particles is to provide the abradable coating with a porous cross-section.
In yet another aspect of this disclosure, in order to increase the ease of releasing the particles 94, the abradable coating 90 may include a lubricant, such as a solid lubricant. Examples of such lubricants include hexagonal boron nitride (h-BN), molybdenum disulfide (MoS2), or graphite. The addition of lubricant may assist the seal plate 76 in breaking down the abradable coating 90.
The abradable coating 90 of the present disclosure is configured to maintain its structural integrity at relatively high operating temperatures as compared to polymer-based abradable coatings, without it being unduly difficult for the seal plate 76, for example, to liberate particles of the abradable coating 90 in a worn seal condition.
It should be understood that terms such as “axial” and “radial” are used above with reference to the normal operational attitude of the engine 20. Further, these terms have been used herein for purposes of explanation, and should not be considered otherwise limiting. Terms such as “generally,” “substantially,” and “about” are not intended to be boundaryless terms, and should be interpreted consistent with the way one skilled in the art would interpret those terms. Additionally, while many components of the engine 20 are shown in cross-section in the figures, it should be understood that certain of these components extend circumferentially around the engine central longitudinal axis A.
Although the different examples have the specific components shown in the illustrations, embodiments of this disclosure are not limited to those particular combinations. It is possible to use some of the components or features from one of the examples in combination with features or components from another one of the examples. In addition, the various figures accompanying this disclosure are not necessarily to scale, and some features may be exaggerated or minimized to show certain details of a particular component or arrangement.
One of ordinary skill in this art would understand that the above-described embodiments are exemplary and non-limiting. That is, modifications of this disclosure would come within the scope of the claims. Accordingly, the following claims should be studied to determine their true scope and content.