The invention relates to a gasket having at least one metallic layer, in which at least one gasket opening and at least one bead are formed, and in and/or adjacent to such a bead a coating is applied as a deformation limiter (stopper), the coating comprising at least one filler and one bonding agent, as well as to a method of producing such a gasket. Such a gasket can be used by preference as a cylinder head gasket for internal combustion engines.
In gaskets which are formed from one or even more metallic layers disposed the one above the other, it is usual to form beads by deformation, in order to improve the sealing effect, especially in the critical regions in which apertures are arranged for the cylinder bores but also other apertures through which bolts, lubricant or coolant are led. In order to prevent too strong a compression or displacement of such beads as a result of the clamping forces acting during assembly, it is usual to form or arrange at or on individual metallic layers of such a gasket deformation limiters, also called spring limiters or stoppers.
To form such a deformation limiter, besides the bending over of a metallic layer in a region in the proximity of such a bead, in EP 0 797 029 A1 reference is made to another possible way of forming such a deformation limiter. There it is proposed that the deformation limiter be configured in the form of a raised portion, and for this purpose a sufficiently temperature-stable thermosetting material is used as the transport medium and bonding agent with the addition of at least one mineral filler, with a low thermal expansion coefficient. These components are intended to form a heavy-duty and resilient framework, with which it is possible to counteract any undesired excessive deformation in the bead region. It is proposed here that the bonding agent and such a filler (quartz powder, rutile, dolomite or wollastonite) should be used in equal proportions, more favourably however in the ratio 1:3 filler to bonding agent.
This means that the bonding agent has to be so selected that it not only withstands increased temperatures but also has sufficient strength to be able to withstand the pressures and compressive forces and the oscillations which occur for example in internal combustion engines, since the proportion of filler is correspondingly limited. This aspect becomes more and more important since modern combustion engines are operated at higher combustion pressures and correspondingly also higher temperatures and with higher demands of a gasket.
Since organic binders, as also the mineral fillers, have relatively poor heat conductivity, the deformation limiters so produced hinder heat transfer and this can lead to undesired temperature gradients on such a gasket.
This disadvantage can, however, also not be easily overcome by using metal powders as the filler, as is proposed in U.S. Pat. No. 5,582,415, if the known bonding agent:filler proportions are maintained. Such a metal powder as the filler is moistened during a corresponding application all over by the organic bonding agent, the fissured surface structuring of such metal powders also having a disadvantageous effect and the largest number of the individual metal powder particles being thermally insulated from one another by the organic bonding agent.
The object of the invention, therefore, is to provide a gasket having at least one metallic layer, in which at least one gasket opening and at least one bead are formed, with deformation limiters, the strength of which is increased and the temperature properties of which are improved.
According to the invention, this object is achieved with the features of a gasket and the method of producing such a gasket. Advantageous embodiments and developments of the invention arise with the features mentioned in the subordinate claims.
In the invention, deformation limiters are also formed by the application of a coating which contains at least one filler and one bonding agent. However here an increased proportion of filler is used, the mass proportion of which is greater than the proportion of bonding agent. Furthermore a filler in particle form is used, the individual particles of which have a small surface in relation to the volume of the particle, such that in the finished coating tight packing of the individual particles of the filler can be achieved and a relatively large number of these particles adjoin one another directly, such that they support one another directly and the bonding agent used must substantially ensure the connecting function for the filler and the applied coating, whereas the pressures and compressive forces are substantially borne by the filler in particle form.
The spherical filler particles used should, in contrast to conventional powder-form materials, have a smoothed surface, the edges of which at least are rounded. It is certainly most propitious to use spherical particles since they are known to be able to achieve the smallest surface:volume ratio. When such a filler is used, good processability is provided, especially during application.
As already mentioned, the proportion of filler should be greater than the proportion of bonding agent, improved properties being easily achieved from ratios of 2:1, i.e. ⅓ bonding agent and ⅔ filler, upwards. The proportion of filler should advantageously be further increased and filling amounts of above 90% by mass of such a filler can be achieved, the desired properties being able to be further improved with the increased proportion of filler.
The individual particles of the filler used should have average grain sizes in the range between 5 and 100 μm, it being necessary for at least 80% of the particles to be in this grain size range.
To improve the properties of the finished coating, it can moreover be propitious to use particles of differing grain size so that tighter packing of the individual particles and correspondingly higher degrees of filling can be achieved, since smaller particles can fill the spaces between larger particles.
As filler materials, metals, metal alloys, glass but also ceramics and mixtures thereof can be used, silicon nitride or silicon carbide being advantageously used as ceramics taking into account their heat conductivity.
A suitable filler is a copper/tin alloy.
As a suitable bonding agent can be used a thermosetting material, for example an epoxy resin, a silicon resin or a polyamide resin, especially an epoxy resin based on bisphenol A; on account of the lowered strength requirements, a bonding agent can also be selected which can be optimised in the direction of temperature resistance and increased bonding agent function.
In the initial material for the coating to be applied, at least one thermoplastic addition can also be contained which, for example, improves the processability of a prepared mixture. Such an addition can be for example a PTFE, polyethylene, polypropylene or a polyamide.
For the processability, especially during the application of the coating, it is propitious to use a bonding agent which already has plastic deformability at room temperature. For this purpose some of the possible thermosetting materials already mentioned are very suitable. Another criterion for the selection of such a plastics material is the glass-transition temperature. It should advantageously be above 150° C. in order to make allowance for the temperature conditions occurring at an internal combustion engine.
Since the brittleness of the initial materials selected for the coating is low, these can be easily applied even before the stamping process for forming the beads.
The coating forming the deformation limiter can be applied as lines in the form of a closed line but also in the form of an interrupted line. The lines can be varied in width, height and/or shape, according to requirement. The coating can be arranged adjacent to a bead, but also directly in a bead or respectively in a multi-layer gasket on a layer in the region of a bead which is formed in the adjacent layer.
If the coating is arranged in the bead, this bead can be crimped again on the outside, so that a bulge extends into the bead.
The coating, as the deformation limiter can however also be applied on opposite sides of a layer of a gasket, or respectively a bead, in order to ensure the deformation-limiting effect.
Especially when the coating has been applied in a bead, it can be advantageous so to configure the coating that the surface of the coating pointing to the outside comprises substantially bonding agent and/or a thermoplastic addition so that such a surface is configured more even and ensures more favourable sliding properties. For this purpose, however, a thin sealing layer can also be formed in addition.
During the production of a gasket according to the invention, the deformation limiter or limiters can be formed by the application of a mixture, containing the components mentioned already, to a metallic layer, this being followed generally by a hardening process in which the hardening is carried out by means of an energy input, e.g. during heat treatment.
The prepared mixture can be applied for example by means of a printing method, such as matrix printing or screen printing, the width and thickness of the coating during screen printing being able to be especially easily set by corresponding configuration and dimensioning of the screen used.
The invention is described below by way of example. The figures show:
In
The thickness of such a coating 2 can be in the range between 20 and 300 μm.
If a coating 2 is applied inside a bead 3 on a metallic layer 1, as is illustrated in
In the example shown in
In the example represented in
Number | Date | Country | Kind |
---|---|---|---|
199 28 580 | Jun 1999 | DE | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/DE00/01972 | 6/15/2000 | WO | 00 | 3/4/2002 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO00/79156 | 12/28/2000 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
4180211 | Olcott et al. | Dec 1979 | A |
4203608 | Nicholson | May 1980 | A |
4290616 | Nicholson | Sep 1981 | A |
4721315 | Ueta | Jan 1988 | A |
5582415 | Yochida et al. | Dec 1996 | A |
5688860 | Croft | Nov 1997 | A |
5702111 | Smith | Dec 1997 | A |
6062572 | Hasegawa et al. | May 2000 | A |
6105971 | Hasegawa | Aug 2000 | A |
6113110 | Hasegawa | Sep 2000 | A |
6180167 | Majewski et al. | Jan 2001 | B1 |
6211458 | Mitchell et al. | Apr 2001 | B1 |
20010048202 | Zerfab et al. | Dec 2001 | A1 |
Number | Date | Country |
---|---|---|
3543839 | Dec 1985 | DE |
3611285 | Apr 1986 | DE |
195 28 031 | Feb 1997 | DE |
197 11 562 | Sep 1998 | DE |
0 757 195 | Feb 1997 | EP |
0797029 | Mar 1997 | EP |
0853204 | Jan 1998 | EP |
0982517 | Aug 1998 | EP |
09229196 | Sep 1997 | JP |
409287663 | Nov 1997 | JP |
10036764 | Feb 1998 | JP |
2000145968 | May 2000 | JP |