Gasket with corrosion inhibitor

Information

  • Patent Grant
  • 6194074
  • Patent Number
    6,194,074
  • Date Filed
    Wednesday, March 3, 1999
    25 years ago
  • Date Issued
    Tuesday, February 27, 2001
    23 years ago
Abstract
The functioning of an aircraft is dependent on numerous mechanical, hydraulic and electronic systems. Access to these systems, for example for maintenance purposes, can often only be made from the outside or inside of the aircraft by removing panels. In order to protect the systems from environmental influences such as water ingress, a reliable panel sealant is required. A sealant material has been developed which before use consists essentially of a) 30-90% by weight porous base material and b) 10-70% by weight corrosion inhibitor having the requirements that it is compatible with saud porous material and has a group which is polar in nature. Preferably the porous base material is expanded polytetrafluorethylene. Further disclosed is a method for manufacturing sealantg material with anti-corrosion properties comprising the following steps: a) a first step of manufacturing a porous base sealant material (90), b) a second step of preparing a fluid (70) of a corrosion inhibitor, c) a third step of applying said fluid to said base sealant material (90) and d) a fourth step of drying the base sealant material to form the sealant material with anti-corrosion properties.
Description




The functioning of an aircraft is dependent on numerous mechanical, hydraulic and electronic systems. Access to these systems, for example for maintenance purposes, can often only be made from the outside or inside of the aircraft by removing panels. In order to protect the systems from environmental influences such as water ingress, a reliable panel sealant is required.




In the past two-component sealants have been mixed and applied to the aircraft structure with a gun or a spatula. Controlled ambient conditions, a limited pot life as well as long curing times (usually 24 hours but can be longer depending on air humidity and temperature) are characteristic of this method. Polysulphide is an example of such a sealant material. Furthermore, the sealants are difficult to remove when they have to be replaced. The replaced sealants have to be disposed after use with special waste techniques for poisonous waste.




W. L. Gore & Associates have developed a range of sealant tapes sold under the name of SKYFLEX® which overcome these problems. They have none of the above limitations and do not require the use of protective measures during installation. The sealant tapes are described in more detail in the German Patent Application DE-A-37 26 853 (Forrest et. al.).




The SKYFLEX® sealant tapes are manufactured from expanded polytetrafluoroethylene (ePTFE). This material is chemically inert and not affected by any common chemical. It functions over a wide temperature range (−240° C. to +260° C.), does not age and is weather and UV resistant. The ePTFE used in SKYFLEX® sealant is manufactured by the GORE® expansion process. The result is a material which combines the above advantages with high pressure resistance. In addition the material conforms perfectly to irregularities in sealed surfaces.




As well as in aircraft the sealant tapes are currently finding application in other systems such as cars and trains in which reliable panel sealants are required. All of these systems also suffer from corrosion problems around the panels.

FIGS. 1 and 2

illustrate these problems.

FIG. 1

shows a top view two metal parts


10




a,




10




b


made in this example of aluminium alloy between which is placed a sealant


20


. At the boundary between the metal parts


10


and the sealant


20


, joins


30




a


and


30




b


are formed. The joins


30




a


and


30




b


behave like a crevice


30


(such as illustrated in

FIG. 2

) on the metal surface but in macroscopic dimensions.




In

FIG. 2

a side view of the metal crevice


30


is depicted. Within the join


30


oxygen diffusion is hindered. The hindered diffusion of oxygen leads to a depletion of oxygen within a lower or inner part


40


of the join


30


. As a result the inner part


40


of the join


30


shows a reduced electrochemical potential compared with an upper or outer region


50


of the join


30


which is fully covered with aluminium oxide. This difference in electrochemical potential initiates an electrochemical reaction. In the inner part


40


of the join


30


, aluminium ions will be generated. In a second reaction, these ions will be hydrolysed which causes the generation of acid. The existence of acid within the join


30


accelerates the metal dissolution which in turn further accelerates the corrosion.




Corrosion is reduced in two component sealants by adding corrosion-inhibiting substances such as chromates or phosphates to the two component sealant. These corrosion-inhibiting substances are, however, mostly very toxic and have the disadvantage that they need to be dispersed within the sealant mass. They are only effective in a limited area and experiments have shown that with time they tend to lose their activity and dissipate out of the sealant mass and thus the anti-corrosion properties of the sealant diminish. The corrosion-inhibiting substances work by increasing the electrochemical potential of the metal surface and thus leading to a temporary passivation of the surface.




The U.S. Pat. No. 4,028,324 (Tuschner et al.), assigned to United Technologies Corporation, illustrates a method for improving the chemical resistance of a sealant for a phosphoric fuel cell. The sealant used is an extruded seal material, the composition of which consists essentially of ePTFE, a halogenated oil, 0-5% by weight of a halogenated solvent and a filler stable in phosphoric acid and compatible with PTFE. This sealant is manufactured by mixing PTFE, fluorocarbon oil, solvent and filler in a mixer. After the components are mixed, it is allowed to dry and the solvent evaporates. The compound is afterwards extruded into the form of tape by means of a ram extruder.




Because of environmental concerns, the teachings of this patent are, however, nowadays of limited relevance. The use of CFCs is increasingly being avoided due to their known detrimental effects on the ozone layer in the atmosphere.




The taught manufacturing method also has a number of disadvantages as the addition of PFPE to PTFE prior to the extrusion of PTFE is only possible in a limited way. Firstly, the PFPE must completely saturate the PTFE which requires a low surface energy and viscosity of PFPE (i.e. less than 24 mN/m). Secondly the proportion of PFPE in relation to PTFE can only be chosen in a limited range. If the proportion is too low, for example under 30%, then the material can no longer be extruded as the extrusion pressure required is too high. If the share of PFPE is too high, then the extrusion pressure falls. However, the extruded material is then not adequately stable to allow its use as sealants. A further disadvantage is that Tuschner mentions that the material needs only to be stable to 240° C. (400° F.). However, expanded PTFE requires sintering at temperatures of above 250° C. Thus the teachings of Tuschner cannot be applied to the manufacture of expanded PTFE with PFPE.




In WO-A-92/21715 (Chung) assigned to the Donaldson Company Inc. the use of ePTFE which has been treated with a non-functionalised perfluoropotyether (PFPE) fluid prior to or after expansion as a mechanical seal is described. The inventor of this patent application recognised that the system described in this application offered improved radiation resistance properties. However, there is no hint in the patent application that sealant material made from this material could furthermore be resistant to corrosion.




Similarly JP-A-61-163944 (Omori) assigned to Daikin Industry Ltd. teaches the incorporation of a non-functionalised PFPE compound into ePTFE for use as a diaphragm in a sensor. This patent application also does not teach the anti-corrosion properties of the PFPE/PTFE system.




The incorporation of both functionalised and non-functionalised PFPE into ePTFE is also taught in DE-A-43 08 369 (Bürger) assigned to W. L. Gore & Associates. This patent application teaches that the system possesses improved oleophobic properties. However, the disclosure fails to teach that this system also shows anti-corrosion properties.




The object of the invention is therefore to provide a sealant with improved anti-corrosion properties.




A further object of the invention is to provide an improved manufacturing method for a sealant with improved anti-corrosion properties.




A further object of the invention is to provide a sealant made of microporous material which incorporates corrosion inhibitors within the body of the microporous material.




This object is achieved by providing a sealant material which before use consists essentially of a) 30-90% by weight porous base material and b) 10-70% by weight corrosion inhibitor having the requirements that it is compatible with said porous material. The words “by weight” as used in the current patent refer to a weight of the sealant or of the corrosion inhibitor as a proportion of the total weight of the sealant plus corrosion inhibitor. This combination of materials is non-toxic and is easy to apply between two metal parts, requiring no special tools and no setting time. Furthermore the sealant material is easy and cheap to manufacture requiring no special mixing steps prior to the expansion of the polytetrafluoroethylene.




The corrosion inhibitor used in the invention has preferably at least a group which is polar in nature. This aids the building of a film on the surface of the metal parts to protect the metal parts from attack by corrosive materials.




The corrosion inhibitor in the sealant material is selected from the group consisting of perfluoropolyether, polysiloxane, polybutadiene, butadiene-acrylonitrile co-polymers, ethylene-propylene co-polymers, ethylene-propylene-diene co-polymers, ethylene-butylene co-polymers, fluoroalkyl surfactant polymers, and polyesters. It has been found that a particularly suitable corrosion inhibitor is perfluoropolyether or a functionalised derivative thereof. This corrosion inhibitor is easy to obtain and prevents corrosion on aluminium plates reliably.




The corrosion inhibitors are preferably functionalised by the addition of a polar group selected from the group consisting of carboxylic acids, carboxylates, alcohols, mono-, di- and triesters of phosphoric acid, salts of phosphoric acids and carboxylic acids, silane, amines, ethers, isocyanates, urethanes, thiols, dithiols, esters, amides, maleic anhydride or acetates as well as fluorinated derivatives thereof.




The base sealant is typically selected from the group consisting of polytetrafluoroethylene and expanded polytetrafluoroethylene which have been shown to be non-toxic and highly effective sealants. However, it would be possible to use other sealant materials in this invention as long as they are porous. Examples of such materials are those produced by phase separation processes such as polycarbonates, polyvinylidene fluoride, polypropylene, polysulfone, nylon, cellulose acetates and thermoplastic polyurethanes and foams suchas polyurethane or polysiloxane.




Furthermore, sealants can also be made from blends and composites of ePTFE with glass, ceramics, carbon black and thermoplastics. Blends of ePTFE with thermoplastics such as PEEK (Poly-(Ether-Ether-Ketone)) and UHMW-PE (Polyethylene with high molecular weight) are known from the co-pending German Patent Application DE-A-196 38 416.8.




Experiments have shown that the good anti-corrosion results are obtained when the sealant material before use consists of a) 30-90% by weight expanded polytetrafluoroethylene and b) 10-70% by weight corrosion inhibitor. Preferably a sealant material is used which before use consists of 40-60% by weight expanded polytetrafluoroethylene and 40-60% by weight corrosion inhibitor.




The method for manufacturing sealant material with anti-corrosion properties comprises the following steps:




a) a first step of manufacturing a porous base sealant material,




b) a second step of preparing a fluid comprising at least a corrosion inhibitor,




c) a third step of applying said base sealant material to said fluid for a specified period of time and




d) a fourth step of drying to base sealant material to form the sealant material with anti-corrosion properties.




Compared to the prior art methods, this provides a very cheap and easy method of introducing anti-corrosion properties into a sealant.




In a preferred embodiment of the invention, the porous base sealant material is dipped into a fluid which is a mixture of a corrosion inhibitor and a further fluid. This has been found to be the most practical method of ensuring that the corrosion inhibitor is absorbed into the body of the porous base sealant. However, it would also be possible to spray, roll or brush the corrosion inhibitor onto the surface of the base sealant material




Experiments have also shown that it is possible to spray the pure additive in liquid form onto the surface of the porous base sealant material.




The mixture into which the base sealant material is dipped is a solution, dispersion or suspension of corrosion inhibitor in another fluid. In one advantageous embodiment, the mixture is a solution in which the solute is the corrosion inhibitor having the requirements that it is compatible with polytetrafluoroethylene and has a group which is polar in nature. The solvent is typically selected from the group consisting of alcohols, ketones, alkanes, water or perfluoropolyethers or mixtures thereof. In one advantageous embodiment of the invention, the solvent is an alcohol and the corrosion inhibitor is perfluoropolyether. This combination allows the manufacture of effective sealants with anti-corrosion properties. The perfluoropolyether has the major advantage compared to prior art corrosion inhibitors in that it is non-toxic and not detrimental to health. Furthermore, it is known that this material does not damage the ozone layer which is of great importance for sealants incorporated into aircraft flying high in the atmosphere.




Good results for manufacturing sealant material with anti-corrosion properties have been obtained wherein said mixture consists of a) 50-80% by weight corrosion inhibitor and b) 20-50% by weight solvent. The drying step (fourth step) in one embodiment of the invention comprises




a) a step of drying for a specified period of time at room temperature and atmospheric pressure and




b) a step of drying for a specified period of time in vacuum.




It would also be possible to heat the sealant material in order to speed up the drying process.




The manufactured sealant can be used in a system of two metal plates


10




a,




10




b


which are separated by the sealant


20


. This system typically finds an application in transportation vehicles, such as an aircraft, in which corrosion is a serious problem. The manufactured sealant can furthermore be used as a sealant between disimilar material such as metal and plastic.












FIG. 1

shows a top view of a sealant between two metal parts.





FIG. 2

shows a side view of a crevice.





FIG. 3

shows a simplified overview of the apparatus used for manufacturing the sealant according to the invention.





FIG. 4

shows the design of a sealant.





FIG. 5

shows an overview of the experimental apparatus used for determining the extent of corrosion on aluminium alloy plates separated by a band sealant manufactured according to this method.





FIG. 6

shows photographs of corrosion problems.





FIG. 7

shows a graph of weight increase of the sealant against concentration of an inhibitor in solution.











The apparatus used for the manufacture of the sealant according to the invention is depicted in FIG.


3


. It consist of a vat


60


in which a solution


70


of a corrosion inhibitor and a solvent is to be found. A sealant


90


is dipped into the solution


70


by means of a holder


80


.




Manufacture of the sealant according to the invention is carried out as follows. Firstly a sealant tape


90


is manufactured according to the known prior art methods. One example of such a sealant tape is the SKYFLEX® sealant tapes which are manufactured by W. L. Gore & Associates. These sealant tapes are made by extruding and then stretching PTFE.




The PTFE can be uniaxially stretched or biaxially stretched. An example of one such tape, sold under the part number GO-AS-0001, is shown in FIG.


4


. The geometry of the tape is chosen to make it suitable for the particular application and is not limiting of the invention. For example, the tapes might be completely flat or they could have ribs of different heights and in different locations. In this example, the ePTFE has re-densified to a density of 0.5 g/cm


3


. However, sealant tapes with other densities can be used if required by the application.




In a second step a corrosion inhibitor is mixed with a solvent in the vat


60


. In one embodiment of the invention the inhibitor used is polar PFPE (Perfluoropolyether) and the solvent used a fluorinated solvent. Suitable PFPEs for this purpose are supplied by Ausimont under the trade names FOMBLIN-Z® and FLUOROLINK™. A suitable fluorinated solvent is a PFPE of low molecular weight. These examples are only meant to illustrate suitable materials for the performance of the invention. Further examples of suitable materials will be given later. The PFPEs used are preferably functionalised with one or two polar head groups and have the following general structure:











where —OR is an alkoxygroup.




The sealant tape


90


is then dipped into the solution


70


in the vat


60


. The sealant tape


90


remains submerged for a period varying between 30 seconds and 5 minutes. The submergence time needs to be sufficiently long to ensure that the sealant tape


90


becomes saturated with the solution


70


. The exact length of time depends not only on the concentration of the solution but also on the geometry of the sealant tape


90


which is to be treated.




As is known, a material such as ePTFE has large voids within its structure. The solution


70


is absorbed within the voids. When these voids are completely filled, the sealant tape


90


can no longer absorb more solution


70


. It is at this point that the sealant tape can be removed from the solution. The length of time in which the sealant tape is kept in the solution can be shortened by stirring the solution


70


whilst the sealant tape


90


is in the vat


60


or by using ultrasound to promote mixing of the solution


70


and absorption by the sealant tape


90


.




The sealant tape


90


can alternately be sprayed, rolled or brushed with the corrosion inhibitor directly or with a solution


70


containing the corrosion inhibitor.




After removal from the solution


70


, the sealant tapes


90


are dried. The length of drying also depends on the geometry of the sealant tape


90


and the components of the solution


70


as well as on the atmosphere in which the drying occurs. The sealant tape


90


should be dried for a sufficient length of time in order to ensure that all the solvent is evaporated from the sealant tape


90


. A typical drying time at room temperature in the open air for the embodiment cited above would be four hours. Warming the sealant tape


90


or placing it in vacuum will shorten the necessary drying time. After evaporation of the solvent, the sealant tapes


90


can be weighed. It is found that they have an increase in weight typically between 10% and 130%. Good anti-corrosion properties have been obtained for those sealant tapes in which the weight increase has been above 20% as will be shown later.




The sealant tapes


90


are now ready for application. The sealant tapes


90


have been found to be suitable for sealing aircraft panels. They are furthermore suitable for sealed metal parts on other transportation vehicles which are susceptible to corrosion, such as those on cars and in trains. The sealant tapes could equally well be used on stationary objects such as battery fuel cells which are filled with aggresive compounds.




In order to demonstrate the anti-corrosion properties of the sealant tapes manufactured by the described method, an experimental apparatus as shown in

FIG. 5A

was constructed. Two aluminium plates


100




a


and


100




b


were pressed together by two PTFE blocks


120




a


,


120




b


. Between the aluminium plates


100




a


and


100




b


and the blocks


120




a


and


120




b


, sealants


110




a,




110




b


and


110




c


made according to the above method were introduced. One of the aluminium plates


100




a


or


100




b


was provided with one or more slits


113


within the gap to allow an electrolytic medium to attack the aluminium in the inner part of the gap.




Two experiments were used to test the sealants. In a first experiment shown in

FIG. 5B

, the aluminium alloy plates


100




a


,


100




b


were placed in a vat


130


with a brine solution. A constant potential was applied to the two plates by means of the electrode


140


and potential source


150


. A reference electrode


145


is introduced into the brine solution in order to measure and to adjust the potential of the aluminium alloy plates


110




a


and


110




b


. The surface structure of the aluminium plates


110




a


,


110




b


was characterised by observation. In the second experiment, no potential was applied. This experiment simulated free corrosion conditions.




The results of the experiments from potentiometric and optical detection are summarised in table 1. The first column of the table is merely the sample number. The second column shows the type of sealant tape used. The letters refer to part numbers of SKYFLEX® tape sealants available from W. L. Gore & Associates. The third column shows the proportion of “classical” inhibitors used. These traditional inhibitors, such as zinc-aluminium polyphosphate, are pre-blended with the PTFE prior to extrusion. The fourth column of the table shows the mass increase of the ePTFE after evaporation. The fifth column of the table shows whether and which type of inhibitor was included in the solution


70


. In the examples of the table, four types of PFPE were used. MF201 and MF407 are monofunctional PFPEs which are available from Montefluos. The PFPEs were either used alone or as a mixture. Additionally, as a control, the corrosion of aluminium which was sealed by sealant tapes incorporating no PFPE was investigated using the same experimental apparatus. These control investigations are indicated by the word “non” in the fifth column of the table.




















TABLE 1











Content







Potential










classical




Mass increase





Corrosion at constant




exposure




Free corrosion




Exposure






Sample No.




Sealing




inhibitor




PFPE (%)




PFPE




corrosion rating




time




rating




time











C




Go Ts 0008




0




0




none




O





XX







L1aC









0




12.5




MF 201




X




71 h




O




68 d






L1bC









0




34.9




MF 201




XXXX





XXX/OO






L1cC









0




57




MF 201




XXX





X






C




Go Ts 0008




0




0




none




O






L2aC









0




21.4




MF 407




XX





O






L2bC









0




60.6




MF 407




XX




72 h




O




68 d






L2cC









0




102




MF 407




XXX





O






C




Go Ts 0008




0




0




none




O





O






L1a2aC









0




11.4




MF 201 / MF 407




XX




152 h 




XXX




68 d






L1b2bC









0




39.7




MF 201 / MF 407




X





X






L1c2cC









0




68.3




MF 201 / MF 407




XX





OO/XX






B




Go As 0001




0




0




none






L6B









5




0











L6aB









15




0









XX




88 h




O




49 d






L6bB









10




0











L6B




Go As 0001




5




0




none




X





O






L6/1aB









5




6.8




MF 201




XX




71 h




O




49 d






L6/1bB









5




19.4




MF 201




XXX





X






L6/2aB









5




14.3




MF 407




XXX





O






L6/2bB









5




36.8




MF 407






O






L6/1c2cB









5




48.8




MF 201 / MF 407




XXX





O






C




Go Ts 0008




0




0




non






L7aC









0




126




Fluorolink C




XXX




72 h




XXXX




68 d






L8aC









0




106




Fluorolink D




XXX





XXXX














The results of corrosion at constant potential are shown in the sixth column of the table for the periods of time given in hours in the seventh column. A O in the table indicates that the metal plates were fully corroded, a single X indicates severe corrosion and XXXX represents little or no corrosion observable. Similarly the seventh column shows the results of free corrosion experiments for time periods shown in days in the eighth column.




As will be seen from the table, corrosion is severe when no inhibitor (in this example PFPE) is incorporated into the sealant tape. However, corrosion is reduced when the weight of the sealant tape is increased due to absorption of the PFPE. The more PFPE that is incorporated into the tapes, the better the results that are obtained.





FIG. 6

shows the results of optical observation of a slit within one of the aluminium plates


100




a


or


100




b


.

FIG. 6A

shows the results of corrosion after the aluminium plate


100




a


,


100




b


was placed in the brine solution


130


for 68 days and a constant potential applied. In this example, the sealant


110


used did not contain any corrosion inhibitor, In

FIG. 6B

the sealant


110


had a corrosion inhibitor added to it in accordance with the invention. It will be observed, that no corrosion is observable.




A further experiment was made to quantify the extent of protection against corrosion offered by the various corrosion inhibitors. The same experimental apparatus as depicted in

FIGS. 5A and 5B

was employed and the depth of damage at the top and bottom of the slit in plate


100




b


and also on the other side of the plate


100




b


was measured. The results are shown in Table 2.




In the table “whole area” means that damage were observed over the whole area of the aluminium plates


100




a


and


100




b


. “Some” means that some damage was observed either in a limited area of the aluminium plates


100




a


and


100




b


or homogeneously distributed over the aluminium plates


100




a


and


100




b.


















TABLE 2











Depth of damage









Depth of damage




on surface of plate




Depth of damage






Corrosion inhibitor




on Opposite side




between slits




in Slit (lower part)




Distribution of






used in ePTFE




(mm)




(mm)




(mm)




damage











No corrosion inhibitor




0.25




0.015




0.055




whole area






MF 201




0.15




0.01




0.04




whole area






FLUOROLINK C




0.01




0.005




0.003




some (limited area)






FLUOROLINK D




0.003




0.003




0.003




whole area






DA 306




0.11




0.04




0.05




whole area






Fomblin FE 20C




0.04




0.003




0.025




whole area






Fomblin Vac 25/6




0.085




0.065




0.115




whole area






MF 201 / Vac 25/6




0.12




0.005




0.035




whole area






Nuva LE




0.12




0.015




0.03




whole area






Hoe T 4334




0.05




0.01




0.035




some (homogeneous










distribution)














The results obtained show that functionalised PFPE liquids with a phosphate group (MF 201) and a silane group (MF 407) show a low or medium anti-corrosion activity. Functionalised PFPE liquids with a carboxylic group (FLUOROLINK C) or hydroxyl group (FLUOROLINK D) show much better anti-corrosion activity probably due to the good adhesion of the PFPE liquid on the surface of the metal.




It has been found that the mass or weight increase of the sealant material manufactured by this invention can be controlled by altering the concentration of the inhibitor in the solution


70


. This is illustrated in FIG.


7


.




In this example, a GORE SKYFLEX® GO-TS-0008/4 sealant tape was placed in one of three types of solutions for three minutes and the solution stirred. The sealant tape was then dried for 12 hours at room temperature and pressure followed by two hours in an oil vacuum pump. The results from the three solutions can be summarised in Table 3.


















TABLE 3













Weight of




Weight of









Weight of





SKYFLEX ®




SKYFLEX ®




% wt







Weight of




isopropanol-




% wt PFPE




before




after




increase






Solution




PFPE MF201




alcohol




in




absorption




absorption




of






Number




(g)




(g)




solution




(g)




(g)




SKYFLEX ®











1




15




55




21.4




6  




 7.8




30.0






2




20




37




35.1




7.7




11.8




53.2






3




25




30




45.5




7.2




13.1




81.9














As can be seen from the graph in

FIG. 7

, the weight increase of the sealant material is linearly proportional to the concentration of the inhibitor in solution


70


.




The addition of inhibitors to the sealant material has been shown to have further advantages. In particular, when the weight increase of the sealant material is greater than 70%, the sealant material has better sealant properties.




In the above examples, the inhibitor used to fill the sealant material was PFPE. However, the invention is not limited to the use of this type of inhibitor. Investigations have shown that the invention works by allowing the inhibitors in use to seep out of the sealant material and form a film on the surface of the metal parts


10


which have to be sealed. This film then protects the metal parts


10


from corrosion. Thus other suitable materials for use as corosion inhibitors must have the following properties: they must be compatible with the sealant material


20


to be used (in this case ePTFE) and thus be capable of being substantially uniformly distributed throughout the base sealant material; they must be capable of forming a waterproof film on the surface of the metal; therefore they should be hydrophobic. The corosion inhibitors can also be advantageously oleophobic.




Experiments have furthermore shown that inhibitors most advantageously used have a so-called anchor group which is polar or substantially polar in nature. These anchor groups are then attracted by the potential on the surface of the metal parts


10


to be sealed. For example, the carboxyl group —COOH is polar and is known to adhere well to the surface of aluminium oxide which is formed naturally on the surface of aluminium metal plates. Carboxylic acid salts are also polar and adhere well to the surface of steel.




The kinetics of the formation of thin layers of organic films on metal parts is described in the book “An introduction to Ultrathin Organic Film, From Langmuir-Blodget to Self Assembly” by Abraham Ulman, San Diego: Academic Press, 1991.




Taking these requirements into consideration, the materials given in table 4 were tested.














TABLE 4









Trade Name




Composition




Manufacturer











MF 201




PFPE, terminal one phosphate group




Ausimont






MF 407




PFPE, terminal one silane group




Ausimont






FLUOROLINK C




PFPE, terminal two carboxylic acid groups




Ausimont






FLUOROLINK D




PFPE, terminal two hydroxyl groups




Ausimont






DA 306




PFPE, ammonium salt functionalised




Ausimont






Fomblin FE 20C




PFPE, ammonium salt functionalised




Ausimont






Fomblin Vac 25/6




PFPE, not functionalised




Ausimont






Hoe T 4334




Fluorosilicone urethane functionalised




Hoechst AG






NUVA LE




Fluorosilicone




Hoechst AG






Trilene M-101




Ethylene-propylene copolymer, epoxy




Uniroyal







functionalised




Chemical






Trilene M-301




Ethylene-propylene copolymer,




Uniroyal







maleic.anhydr. functionalised




Chemical






Kraton Liquid L-1203




Ethylene-butylene copolymer, hydroxyl




Shell Chemicals







functionalised






EL Vernetzer W




Hydrogen functionalised polysiloxane




Wacker Chemie














The functionalised fluorosilicones have the following general structure:











The functionalised polysiloxane has the following general structure:











and a functionalised olefin copolymers (ethylene-butylene copolymer) has the general structure:











where the head groups can be the same as those given above for PFPE.




To summarise, it is thought that the following materials suitable for use as inhibitors incorporated into PTFE.




PFPE or functionalised PFPE. In particular PFPE which has been functionalised by the addition of a polar group such as carboxylic acids, carboxylate, alcohol, mono-, di- and triesters of phosphoric acid, salts of phosphoric and carboxylic acids, silane, amine, amides, esters, ethers, isocyanates, urethanes, thiol and dithiol. Such compounds are manufactured by Ausimont and sold under the trade names GALDEN, FORMBLIN and FLUOROLINK.




Polysiloxane, functionalised polysiloxane or fluorinated polysiloxane. The same functional groups as listed above can be used. Polysiloxane is available from Wacker Chemie. Functionalised polysiloxanes are available from Wacker Chemie or Dow Chemicals. Fluorinated polysiloxanes are available from Hoechst under the trade name NUVA.,




Polybutadiene available from Hüls AG under the trade name Polyöl. Functionalised polybutadiene with similar functional groups to those listed above. These are available from Goodrich Chemical under the trade name Hycar. Butadiene-acrylonitrile co-polymers and functionalised butadiene-acrylonitrile co-polymers. These are also available from Goodrich Chemical.




Polyolefine copolymers such as ethylene-propylene co-polymers (so-called EPM polymers manufactured by Uniroyal), ethylene-Propylene-Diene polymers (termed EPDM co-polymers), functionalised EPM and EPDM co-polymers with the functional groups listed above and terpolymers on the basis of EPM and EPDM co-polymers as well as their functionalised derivatives. Additionally ethylene-butylene co-polymers such as Kraton L-1203 manufactured by Shell Chemicals are thought suitable for use.




Fluoroalkyl surfactant polymers (termed FSP) which are described in U.S. Pat. No. 4,929,666 (Schmidt et al.) assigned to The Dow Chemical Company and obtainable from 3M Corp.




Polyesters and polyethers as well as co-polymers or block co-polymers made from polyester, oligoester, polyether, oligoether, fluoroalkyls, siloxane or olefin units.




Fluid or wax-like inhibitors of low molecular weight such as silane, carboxylic acids and derivatives thereof (e.g. esters, salts and amides), alkane, thiol and dithiol compounds.




The additives are not restricted to the depicted linear molecules. The effectiveness of the additives as a corrosion inhibiting material is ensured by the presence of oleophobic polymer chains with a low content of polar groups. Thus additives with a nonlinear chain structure, for example a comb-like, star-like, cyclic or dendritic structure are contemplated to be also effective as additives.




It should be furthermore noted that the polar groups can be either attached at the end of the polymer chain or they can be incorporated in the main chain or side chains of the polymer.




The following can be used as solvents for the above listed inhibitors:




Alcohols (e.g. isopropanol IPA)




Ketones, e.g. methylethylketone, methylbutylketone




Chlorinated hydrocarbons e.g. methylene chloride, chloroform




Alkanes




PFPE of low molecular weight




Water




Mixtures of the above solvents




In the description it has been assumed that the fluid used is a solution of a solvent and an inhibitor. However, it would also be possible to use a dispersion or a suspension of the inhibitor in an aqueous or alcohol base. The sealant material could also be placed into a fluid which consisted solely of the corrosion inhibitor in liquid form without the presence of a solvent.




Furthermore it is possible to use other methods for applying the corrosion inhibitor to the sealant material. For example, the corrosion inhibitor could be sprayed, rolled or painted onto the surface of the sealant material from where it would be absorbed by the sealant material into the pores.




Furthermore, it has been assumed in this description that the base sealant material used is expanded polytetrafluoroethylene. However, other materials could be used as long as they have the characteristics that they are good sealant materials and are also sufficiently porous to allow absorption of the inhibitor within the pores of the material. Examples of such materials are materials produced by phase separation processes, such as polycarbonate, polyvinylidene fluoride, polypropylene, polysulfone, nylon, cellulose acetates, and foams such as polyurethane or polysiloxane.



Claims
  • 1. A combination system of at least one metal plate and a further plate which are separated at a joint by a sealant material which before use consists essentially ofa) 30-90% by weight porous base material and b) 10-70% by weight functionalized fluorosilicone distributed within said porous base material, whereby said functionalized fluorosilicone has been functionalized by the addition of one or more polar groups.
  • 2. The system according to claim 1 whereinsaid porous base material is selected from the group consisting of polytetrafluoroethylene, expanded polytetrafluoroethylene, blends of polytetrafluoroethylene with fluoropolymers, materials made from phase separation processes or polymer foams.
  • 3. The system according to claim 1 whereinsaid porous base material is expanded polytetrafluoroethylene.
  • 4. The system according to claim 1 whereinsaid functionalized fluorosilicone has been functionalized by the addition of one or more polar groups selected from the group consisting of carboxylic acid, carboxylates, alcohols, mono-, di- and triesters of phosphoric acid, salts of phosphoric or carboxylic acids, silane, amines, amides, esters, ethers, isocyanates, urethanes, thiol, dithiol and maleic anhydrides.
  • 5. The system according to claim 4 whereinsaid functionalized fluorosilicone is functionalized by the addition of at least one urethane group.
  • 6. The system according to claim 1 wherein the sealant material before use consists ofa) 40-90% by weight expanded polytetrafluoroethylene b) 10-60% by weight functionalized fluorosilicone.
  • 7. The system according to claim 6 wherein the sealant material before use consists ofa) 30-60% by weight expanded polytetrafluoroethylene b) 40-70% by weight functionalized fluorosilicone.
  • 8. A method of preventing corrosion between a metal plate and a further plate placed together at a joint comprising:applying to the joint a sealant material which consists essentially of a) 30-90% by weight porous base material and b) 10-70% by weight functionalized fluorosilicone distributed within said porous base material whereby said functionalized fluorosilicone has been functionalized by the addition of one or more polar groups.
  • 9. The method according to claim 8 whereinsaid porous base material is selected from group consisting of polytetrafluoroethylene, expanded polytetrafluoroethylene, blends of polytetrafluoroethylene with fluoropolymers, materials made from phase separation processes or polymer foams.
  • 10. The method according to claim 8 whereinsaid porous base material is expanded polytetrafluoroethylene.
  • 11. The method according to claim 8 whereinsaid functionalized fluorosilicone has been functionalized by the addition of one or more polar groups selected from the group consisting of carboxylic acid, carboxylates, alcohols, mono-, di- and triesters of phosphoric acid, salts of phosphoric or carboxylic acids, silane, amines, amides, esters, ethers, isocyanates, urethanes, thiol, dithiol and maleic anhydrides.
  • 12. The method according to claim 11 whereinsaid functionalized fluorosilicone is functionalized by the addition of at least one urethane group.
  • 13. The method according to claim 10 wherein the sealant material consists ofa) 40-90% by weight expanded polytetrafluoroethylene b) 10-60% by weight functionalized fluorosilicone.
  • 14. The method according to claim 13 wherein the sealant material before use consists ofa) 30-60% by weight expanded polytetrafluoroethylene b) 40-70% by weight functionalized fluorosilicone.
Priority Claims (1)
Number Date Country Kind
96 103 932 Mar 1996 EP
PCT Information
Filing Document Filing Date Country Kind 102e Date 371c Date
PCT/EP97/00848 WO 00 3/3/1999 3/3/1999
Publishing Document Publishing Date Country Kind
WO97/33949 9/18/1997 WO A
US Referenced Citations (3)
Number Name Date Kind
4028324 Tuschner et al. Jun 1977
5192310 Herweck et al. Mar 1993
5869156 Chung et al. Feb 1999
Foreign Referenced Citations (19)
Number Date Country
44 23 043 Jan 1996 DE
0 303 102 Feb 1989 EP
0 615 779 Sep 1994 EP
0 730 017 Sep 1996 EP
51-050963 May 1976 JP
59-232163 Jun 1983 JP
61-163 944 Jul 1986 JP
62-027485 Feb 1987 JP
62-074998 Apr 1987 JP
63-224728 Sep 1988 JP
64-014291 Jan 1989 JP
3-017562 Mar 1991 JP
4081489 Mar 1992 JP
6 247 473 Sep 1994 JP
7-501347 Feb 1995 JP
8 209114 Dec 1996 JP
872 874 Oct 1981 SU
9221715 Dec 1992 WO
9426960 Nov 1994 WO