Patent Application
20230234121
The present invention relates to gear materials, and production methods and finishing methods therefor. More particularly, the present invention relates to a gear material that is for a differential ring gear (final gear) or the like, and that has spur gear teeth or helical gear teeth at an outer prephery thereof, a production method therefor, and a finishing method therefor using a hobbing machine.
Differential ring gears, which have a relatively large shape, i.e., an outer diameter of about 200 mm and a tooth width of about 40 mm, have conventionally been produced using, for example, the following methods (see Japanese Unexamined Patent Publication No. H07-275989).
In all of these methods, gear teeth are formed at an outer periphery (outer peripheral surface) of a material by gear cutting using a hobbing machine, followed by shaving, carburizing, and shot blasting. Thereafter, the gear teeth are finished by polishing or the like.
Method of forging a ring-shaped material using a 4000-ton press includes, as illustrated in
However, method (1) requires a large number of steps, disadvantageously leading to an increase in die cost.
Method of forging, rolling, and oscillatory rolling using Wagner (Germany)’s scheme includes, as illustrated in
However, method (2) requires many kinds of equipment and a large number of pieces of equipment, and the die for oscillatory rolling costs high. In addition to a large number of steps, rolling and oscillatory rolling are performed in two heating processes, and therefore, a double heating cost is required. As a whole, the material cost is disadvantageously high.
Method of rolling using two edge rolls and a receiving roll includes, as illustrated in
However, in the case of method (3), the final product shape (d) is a ring shape, and therefore, a large machining allowance is present for gear cutting with a hobbing machine, disadvantageously leading to a deterioration in machining yield and a decrease in tool life. In addition, the cutting rate is typically at most 200 m/min, disadvantageously leading to a time-consuming and high-cost machining step.
With the above problems with conventional differential ring gear production methods in mind, it is an object of the present invention to provide a gear material that is for a differential ring gear or the like, and that has a relatively large shape and has spur gear teeth or helical gear teeth at an outer periphery thereof, and with which the yield of a final product is improved, the operating cost of gear cutting by a hobbing machine is reduced, and the rate of cutting is dramatically increased to reduce a machining time, whereby the total manufacturing cost can be reduced; a production method therefor; and a finishing method therefor using a hobbing machine.
To achieve the object, a gear material according to the present invention is in the shape of a ring having an outer diameter of at least 170 mm (about 170 mm to about 230 mm) and an outer peripheral thickness of at least 30 mm (about 30 mm to about 50 mm), and having, at an outer peripheral surface thereof, spur gear teeth or helical gear teeth with a machining allowance of 0.2 mm to 2.0 mm on either side thereof.
In this case, the gear material can have a gear module of 1.5 to 3.5.
A method for producing a gear material according to the present invention is characterized in that the gear material is formed from a billet only by hot forging.
A method for finishing a gear material according to the present invention is characterized in that the gear material is finished using a hobbing machine at a cutting rate of 250 m/min to 500 m/min.
As used herein, the cutting rate is a numerical value that is set when a cutter made of a high-speed tool steel (high-speed steel) is used.
With a gear material according to the present invention and a production method therefor and a finishing method therefor using a hobbing machine, the yield of a final product of a gear material that is for a differential ring gear or the like, and that has a relatively large shape and has spur gear teeth or helical gear teeth at an outer periphery thereof is improved, the operating cost of gear cutting by a hobbing machine is reduced, and the rate of cutting is dramatically increased to reduce a machining time, whereby the total manufacturing cost can be reduced.
Embodiments of a gear material according to the present invention, a production method therefor, and a finishing method therefor using a hobbing machine will be described below with reference to the accompanying drawings.
In the method for producing a gear material, gear teeth are formed during a series of steps using a conventional production line for forging a ring gear without gear teeth.
Initially, a billet (cylindrical material) 1 is heated to a predetermined temperature in an induction heating furnace, and then upset-forged into a disc-shaped blank 2 by an upset forging step including a plurality of steps. A blank 3 having a thicker outer peripheral portion is formed by volume distribution in a rough step. In a finishing step, produced is a gear material 4 that is in the shape of a ring having an outer diameter of at least 170 mm (about 170 mm to about 230 mm) and an outer peripheral thickness of at least 30 mm (about 30 mm to about 50 mm), and has, at an outer peripheral surface thereof, spur gear teeth or helical gear teeth having a module of 1.5 to 3.5 (helix angle: at most about 35°) with a machine allowance of 0.2 mm to 2.0 mm (preferably 0.2 mm to 1.5 mm, more preferably 0.2 mm to 1.0 mm) on either side thereof, using a forging die (forging die having, in an inner peripheral surface thereof, a shape corresponding to spur gear teeth or helical gear teeth to be formed). By piercing the gear material 4 in a piercing step as a final step, a gear material 5 is obtained.
Here, the temperature of a gear tooth portion is likely to decrease because of its small volume, and therefore, needs to be maintained. In this process, the formation of the gear material 5 from the the billet 1 only by hot forging is completed quickly by a series of forming steps in a pressing machine, and therefore, can be carried out with the temperature maintained sufficiently high. Thus, it is not necessary to heat again. More specifically, the cycle time it takes to carry out each step of forming the gear material 5 from the billet 1 is set to at most 10 seconds, e.g., about 4 seconds to about 6 seconds. As a result, it is easy to manage temperature, and the amount of oxide scale generated can be reduced.
After hot forging, the gear material 5 is subjected to a finishing process, i.e., a material thermal treatment (forging isothermal annealing, normalizing, or without a thermal treatment) and then shot blasting, followed by lathe/piercing, hobbing (gear cutting in an outer peripheral surface using a hobbing machine), and a thermal treatment (carburizing, highfrequency quenching/tempering, or the like), and optionally, tooth surface polishing or the like, to obtain a final product.
Here, the spur gear teeth or helical gear teeth of the gear material 5 formed using a forging die can be hobbed using a conventional hobbing machine for machining a ring-shaped material, with the threads of the hobbing machine mating with the gear teeth (the gear teeth at the outer peripheral surface are finished using the hobbing machine).
As illustrated in
It should be note that a typical cutter made of high-speed tool steel (high-speed steel) has a cutting rate of about 200 m/min.
Specifications (example) of a final product thus produced (the gear material 5) are described below.
Specifications of a final product (the gear material 5)
As a result, the yield of a final product of a gear material that is for a differential ring gear or the like, and that has a relatively large shape and has spur gear teeth or helical gear teeth at an outer periphery thereof is improved, the operating cost of gear cutting by a hobbing machine is reduced (a reduction in the cost of a tool due to an improvement in tool life is included), and the rate of cutting is dramatically increased to reduce a machining time, whereby the total manufacturing cost can be reduced.
Specifically, as illustrated in
In addition, the cutting rate can be increased to 250 m/min to 500 m/min. In addition to the reduction of the amount of a material to be cut, the net machining time can be reduced from about 42 seconds (conventional examples (ring gears without gear teeth)) to about 14 seconds (examples), result in a reduction in cycle time (reduction by at least 40%).
The cutting load due to hobbing is small, and therefore, the increase in the temperature of a workpiece (the gear material 5) is reduced, whereby the adjustment of temperature is not required during hobbing.
For the spur gear teeth or helical gear teeth formed at the outer peripheral surface of the gear material 5 using a forging die, metal flow is not interrupted, and therefore, the gear teeth can have a high strength.
In the foregoing, a gear material according to the present invention, and a production method and finishing method therefor, have been described by way of example. The present invention is not limited to the configurations described in the above examples. Various changes and modification can be made to the examples, as appropriate, without departing the spirit and scope of the present invention.
With a gear material according to the present invention and a production method and finishing method therefor, the yield of a final product is improved, the operating cost of gear cutting by a hobbing machine is reduced, and the rate of cutting is dramatically increased to reduce a machining time, whereby the total manufacturing cost can be reduced. Therefore, the present invention is widely useful for a gear material that is for a differential ring gear or the like, and that has a relatively large shape and has spur gear teeth or helical gear teeth at an outer periphery thereof, and a production method and finishing method therefor.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2021-190739 | Nov 2021 | JP | national |