Abstract
A magnetic head (32) includes a magnet core (30) of ferrite and a layer of a bonding material (28) consisting of glass in the gap-forming area of the magnet core (38). In order to ensure that the ferrite is not attacked by the glass during the bonding process and that the temperature adjustment during the bonding process is not too critical, double layer diffusion barriers are provided between the layer of bonding material (28) and the core parts (10), (10'), respectively. Each barrier is formed by a layer of silicon nitride (26) on the side of the bonding layer (28) and a layer of silicon oxide (24) on the side of the core.
Description
BACKGROUND OF THE INVENTION
The invention relates to a magnetic head which includes a magnetic core having a gap-forming area, and a layer of non-magnetizable bonding material in the gap-forming area of the magnetic core. The head also includes diffusion barriers provided between the core parts and the layer of non-magnetizable material. The invention also relates to a method of manufacturing such a magnetic head.
Magnetic heads serve to record, playback and/or erase magnetic information. They are used, for example, in tape recorders for recording and/or playing back audio information or video information. Particularly when a magnetic head is used in tape recorders for recording and/or playing back video information (so-called video recorders), it is usual to manufacture the core of the magnetic head from (monocrystalline) ferrite.
The gap of a magnetic head for a video recorder is formed by bonding two parts of (monocrystalline) ferrite to each other by means of a sputtered film of a low-melting-point glass. In order to prevent the glass from attacking the ferrite during bonding at approximately 700.degree. C., the ferrite is first coated with a layer which is impervious to glass and which is often termed a diffusion barrier. Although British Patent Specification No. 1,317,634 suggests as materials for the diffusion barrier: non-magnetizable metals, metal oxides, borides, nitrides, silicon oxide and ferrite which is non-magnetizable at room temperature, a sputtered SiO.sub.2 layer has so far been used in practice as the diffusion barrier. In the heating phase of the bonding process, the glass becomes less and less viscous. When the glass is heated to a sufficiently high temperature it may work as an adhesive. However, above a given temperature, the SiO.sub.2 -layer dissolves in the glass. As a result, the glass becomes more viscous so that its value as an adhesive decreases. In the manufacture of heads, heating to 700.+-.5.degree. C. has to be done quickly (in approximately 10 minutes) so as to obtain a good bonding. It has been found difficult to maintain this narrow tolerance of .+-.5.degree. C.
So the search is for a diffusion barrier which permits a freer temperature adjustment. It was expected that silicon nitride, which is known from I.C. technology to be impervious to glass in certain circumstances, might be suitable. A glass-bonded ferrite head with a silicon nitride barrier has been suggested in German Offenlegungsschrift No. 2,341,649.
It has been found, however, that thin Si.sub.3 N.sub.4 layers having ferrite as a substratum are damaged after termination of the temperature cycle of the bonding process. The glass penetrates through the chinks formed, flows below the Si.sub.3 N.sub.4 and attacks the ferrite.
The damage to the Si.sub.3 N.sub.4 layer is probably the result of the high elastic stress at the interface Si.sub.3 N.sub.4 -ferrite. This stress may substantially be ascribed to the comparatively low elasticity of Si.sub.3 N.sub.4.
SUMMARY OF THE INVENTION
It is the object of the present invention to provide a magnetic head of the kind described in the opening paragraph having a diffusion barrier in the gap-forming area which associates a comparatively free temperature adjustment during the bonding process with a sufficient insensitivity to the temperature occurring during the bonding process.
For that purpose, the magnetic head according to the invention is characterized in that each diffusion barrier includes a layer of silicon nitride adjoining the non-magnetizable bonding layer, and a layer of silicon oxide.
Interestingly, it was found that, in a ferrite head having in the gap-forming area a system of layers SiO.sub.2 -Si.sub.3 N.sub.4 -glass-Si.sub.3 N.sub.4 -SiO.sub.2, the system of layers remained totally undamaged after heating to 700.degree. C. and cooling to room temperature. Thus, the glass was not capable of reacting with the ferrite and the SiO.sub.2 was not capable of dissolving in the glass. Consequently, said system of layers satisfies the requirements imposed.
Because of the good action as a diffusion barrier of the silicon oxide-silicon nitride double layer, the temperature control upon bonding the core parts in the gap-forming area is less critical while, nevertheless, an accurately defined proportioning of the non-magnetic gap area is obtained. Therefore, the present invention significantly improves the efficiency of manufacturing glass-cemented ferrite heads.
The invention also relates to a method of manufacturing a magnetic head having the above-mentioned structure. The method comprises the following steps: forming a first core part and a second core part of magnetic material; working a face of each of said core parts in such manner that said faces may serve as gap-forming faces; providing a layer of anti-diffusion material on each of the gap-forming faces; providing a layer of bonding material on at least one of the layers of anti-diffusion material; placing the two core parts against each other with the provided layers in between; and forming a permanent bond by means of a thermal treatment, and is characterized in that the layer of anti-diffusion material is provided by sputtering, from a first target, a layer of SiO.sub.2 having a desired thickness and by subsequently sputtering a layer of Si.sub.3 N.sub.4 having a desired thickness. The layer of Si.sub.3 N.sub.4 may be sputtered from an Si.sub.3 N.sub.4 target or, which is easier, may be sputtered in a nitrogen-containing gas atmosphere from a silicon target. In the latter case, the silicon target may be also be used to sputter the layer of SiO.sub.2. For that purpose, sputtering should be carried out in an oxygen-containing atmosphere. By gradually replacing the oxygen of the gas atmosphere during sputtering by nitrogen after a layer of SiO.sub.2 having a desired thickness has been provided, it is achieved that the silicon oxide layer turns gradually into the silicon nitride layer.
BRIEF DESCRIPTION OF THE DRAWINGS
An embodiment of the invention will be described in greater detail with reference to the accompanying drawing, in which:
FIG. 1 is a perspective view which shows a block of starting material;
FIG. 2 is a perspective view which shows a worked core part;
FIGS. 3a and 3b are perspective views which show two core parts provided with layers for forming a diffusion barrier;
FIGS. 4a and 4b are perspective views which show the core parts of FIGS. 3a and 3b after providing bonding layers;
FIG. 5 is a perspective view which shows an assembly of the two core parts bonded together under pressure;
FIG. 6 is a perspective view which shows the assembly of FIG. 5 after a tape contact face has been provided; and
FIGS. 7a and 7b show an ultimate magnetic head and an enlarged view of the gap-forming area, respectively.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
A block of material 10 which may be manufactured from polycrystalline (sintered) or, in particular, monocrystalline ferrite (FIG. 1) is given the shape shown in FIG. 2 by means of the usual techniques. As is shown in FIG. 2, two grooves 14, 16 are provided in the block 10 and the surfaces 18, 20 and 22 are polished so that they may serve as gap-bounding faces.
By using known deposition methods, first layers 24 are provided on the surfaces 18, 20, 22 of core parts 10, 10' (FIGS. 3a, 3b). The first layers 24 consist of a non-magnetizable material which does not react, or at most reacts very slightly. For example, the non-magnetizable material may be silicon oxide. Silicon oxide (e.g. SiO.sub.2) can easily be provided by means of a sputtering method and, because of its compatively high elasticity, after providing shows a comparatively low elastic stress at the interface with the ferrite.
An alternative method of providing a thin layer of SiO.sub.2 is the so-called reactive vapour deposition method. In this method, a mixture of SiH.sub.2 and O.sub.2 is applied to a furnace which is kept at a temperature of approximately 400.degree. C. and in which the pole pieces are present. It has been found that a homogeneous layer of SiO.sub.2 is the formed on the core parts.
Second layers 26 are provided on the first layers 24. Said second layers 26 consist of Si.sub.3 N.sub.4. A thickness of between 100 and 1000 .ANG. is preferable for each of the layers 24, 26. 200 .ANG. is a particularly preferable thickness. In order to achieve a gradual change of the chemical composition of the SiO.sub.2 layer into a Si.sub.3 N.sub.4 layer, the SiO.sub.2 may be sputtered from an Si-target (in oxygen) instead of from an SiO.sub.2 -target and the atmosphere during sputtering may then be replaced gradually by nitrogen as a result of which the last sputtered material becomes Si.sub.3 N.sub.4.
Bonding layers 28 are provided on the second layers 26 which, together with the layers 24, form a diffusion barrier (FIGS. 4a, 4b). The third layers 28 may consist of a glass which comprises 12-20% by weight of Al.sub.2 O.sub.3, 40-48% by weight of B.sub.2 O.sub.3, and furthermore a share of one or more of the oxides BaO, CaO or SrO. A suitable glass comprises, for example, 15 mol % Al.sub.2 O.sub.3, 60 mol % B.sub.2 O.sub.3 and 25 mol % BaO or SrO. This glass can be provided by means of sputtering with the composition remaining constant and can be provided in the same sputtering device as the layers 24, 26 from a glass target.
The sum of the thicknesses of the layers 24, 26 and 28 determines the ultimate gap length of the magnetic head.
The core parts 10, 10' are then placed against each other with the glass layers (FIG. 5) and heated in a furnace at a temperature which is sufficiently high to soften the layer of glass (for example, approximately 650.degree. C.), the core parts 10, 10' being pressed against each other at a pressure of 20-70 kg/cm.sup.2. After cooling, the core parts 10, 10' are rigidly connected together and may then be further processed to obtain a magnetic head of the desired shape. For example, the assembly may be processed and polished so that, with simultaneous adjustment of the gap height h, the construction shown in FIG. 6 is formed which has a tape contact face 29. As shown in FIG. 7a, this construction may again be divided into individual magnet core segments 30 which, after providing an electric winding 31, form a magnetic head 32.
FIG. 7b shows, with reference to an enlargement of the gap-forming area of the magnetic head 32 of FIG. 7a, the resulting layer structure of the gap-forming area between the (ferrite) core parts 10, 10'. A layer 24 of silicon oxide and a layer 26 of silicon nitride are provided on each of the core parts 10, 10'. The assembly is cemented together via a glass layer 28.
Claims
- 1. A magnetic head, comprising:
- a magnetic core including two magnetic core parts having gap-bounding faces forming a transducing gap therebetween;
- a non-magnetizable bonding material disposed in the transducing gap; and
- a diffusion barrier provided between each gap-bounding face and the non-magnetizable bonding material;
- characterized in that each diffusion barrier includes a first layer consisting essentially of silicon oxide provided on the respective gap-bounding face, and a second layer consisting essentially of silicon nitride provided on the first layer.
- 2. A magnetic head as claimed in claim 1, characterized in that each core part consists essentially of a ferrite material.
- 3. A magnetic head as claimed in claim 2, characterized in that the silicon oxide is SiO.sub.2.
- 4. A magnetic head as claimed in claim 3, characterized in that the ferrite material is polycrystalline.
- 5. A magnetic head as claimed in claim 3, characterized in that the ferrite material is monocrystalline.
- 6. A magnetic head as claimed in claim 1, characterized in that each of the first and the second layers has a thickness in a range of between 100 and 1,000 angstroms.
- 7. A magnetic head as claimed in claim 6, characterized in that the non-magnetizable bonding material is a glass.
- 8. A magnetic head as claimed in claim 7, characterized in that the glass consists essentially of 15 mol.% Al.sub.2 O.sub.3, 60 mol.% B.sub.2 O.sub.3 and 25 mol.% BaO.
- 9. A magnetic head as claimed in claim 7, characterized in that the glass consists essentially of 15 mol.% Al.sub.2 O.sub.3, 60 mol.% B.sub.2 O.sub.3 and 25 mol.% SrO.
- 10. A magnetic head as claimed in claim 1, characterized in that each of the first and the second layers has a thickness of approximately 200 angstroms.
- 11. A magnetic head, comprising:
- two magnetic core parts having gap-bounding faces forming a transducer gap therebetween;
- a non-magnetizable material disposed in the transducing gap; and
- a diffusion barrier provided between each gap-bounding face and the non-magnetizable material;
- characterized in that each diffusion barrier includes a first layer consisting essentially of SiO.sub.2 provided on the respective gap-bounding face, and a second layer consisting essentially of Si.sub.3 N.sub.4 adjoining the non-magnetizable material.
- 12. A magnetic head as claimed in claim 11, characterized in that each diffusion barrier further includes an intermediate structure in which the first layer turns gradually into the second layer.
- 13. A magnetic head as claimed in claim 11, characterized in that each of the magnetic core parts consists essentially of a monocrystalline ferrite material.
- 14. A magnetic head as claimed in claim 13, characterized in that each of the first and the second layers has a thickness of approximately 200 angstroms.
- 15. A magnetic head as claimed in claim 11, characterized in that each of the magnetic core parts consists essentially of a polycrystalline ferrite material.
- 16. A magnetic head comprising a magnetic core having a gap-forming area in which a system of layers is provided, characterized in that the system of layers includes successively:
- a first layer consisting essentially of SiO.sub.2 ;
- a second layer consisting essentially of Si.sub.3 N.sub.4 provided on the first layer;
- a third layer consisting essentially of a non-magnetizable material provided on the second layer;
- a fourth layer consisting essentially of Si.sub.3 N.sub.4 provided on the third layer; and
- a fifth layer consisting essentially of SiO.sub.2 provided on the fourth layer.
- 17. A magnetic head as claimed in claim 16, characterized in that the magnetic core consists essentially of a ferrite material, and the first and the fifth layers are provided on the ferrite material of the magnetic core.
- 18. A magnetic head as claimed in claim 17, characterized in that each of the second and the fourth layers has a respective thickness in a range of between 100 and 1,000 angstroms.
- 19. A magnetic head as claimed in claim 18, characterized in that the non-magnetizable material is a glass.
- 20. A magnetic head as claimed in claim 19, characterized in that the ferrite material is polycrystalline.
- 21. A magnetic head as claimed in claim 19, characterized in that the ferrite material is monocrystalline.
- 22. A core part for a magnetic head, comprising:
- a ferrite part having a substantially planar surface;
- a first layer consisting essentially of silicon dioxide provided on the planar surface;
- a second layer consisting essentially of silicon nitride provided on the first layer; and
- a third layer including a non-magnetizable material provided on the second layer.
- 23. A core part as claimed in claim 22, wherein the non-magnetizable material is a glass, and wherein each of the first and the second layers has a thickness in a range of between 100 and 1000 angstroms.
Priority Claims (1)
Number |
Date |
Country |
Kind |
8202059 |
May 1982 |
NLX |
|
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
3886025 |
Riseman |
May 1975 |
|
4392167 |
Joormann |
Jul 1983 |
|
Foreign Referenced Citations (1)
Number |
Date |
Country |
50-24097 |
Aug 1975 |
JPX |