Patent Grant
10377661
This application is a National Stage application of International patent application PCT/EP2015/060765 filed on May 15, 2015, which claims priority to European patent application No. 14168719.4 filed on May 16, 2014, the disclosures of which are incorporated herein by reference in their entirety.
The invention relates to a glass ceramic having SiO2 as main crystal phase which is suitable in particular for use in dentistry and preferably for the preparation of dental restorations, as well as to precursors to the preparation of the glass ceramic.
Glass ceramics with quartz-like crystals are already known from the state of the art. They are usually glass ceramics with so-called high quartz solid solution crystals. These crystals contain different additional ions in the SiO2 framework silicate, which allow this particular type of crystal to have a metastable existence even at room temperature. If these ions were not contained in the glass ceramic, the high quartz formed at high temperatures in the glass ceramic would change into low quartz at 573° C. Holand and Beall describe that glass ceramics with crystals in the high quartz structure have the particular property of low thermal expansion or even of zero expansion within a large temperature range (“Glass-Ceramic Technology” 2nd edition, Wiley, 2012, 272-273). For such glass ceramics, linear coefficients of thermal expansion (CTE) of less than 1.5·10−6 K−1 (within the temperature range of 20-700° C.) are usually measured. Even glass ceramics with a negative coefficient of expansion can be provided with the aid of the high quartz structure.
Further, lithium disilicate glass ceramics are known from EP 916 625, which contain lithium disilicate as main crystal phase and, because of their high translucence and very good mechanical properties, are used particularly in the dental field and primarily for the preparation of crowns and bridges.
The object of the invention is to provide a glass ceramic which, in addition to a high strength and very good optical properties, is also characterized by a high coefficient of thermal expansion. The glass ceramic should further be easy to process, in particular by machining, to form dental restorations and thus be suitable in an excellent manner as restorative dental material. It would be desirable if the glass ceramic could also be given the desired shape by means of hot pressing.
These objects are achieved by the glass ceramic according to claims 1 to 15 and 17. Likewise a subject of the invention are the starting glass according to claim 16, the method according to claims 18 to 20 and 23 as well as the use according to claims 21 and 22.
The glass ceramic according to the invention is characterized in that it comprises the following components
and comprises SiO2 as main crystal phase.
This glass ceramic surprisingly displays an advantageous combination of mechanical and optical properties desirable for a restorative dental material, and it can also be given the desired shape in a manner desirable for a dental material.
The glass ceramic according to the invention contains in particular 60.0 to 90.0, preferably 70.0 to 83.0 wt.-% and particularly preferably 73.0 to 81.0 wt.-% SiO2.
It is further preferred that the glass ceramic contains 2.8 to 9.0, in particular 5.0 to 9.0 and particularly preferably 5.0 to 7.8 wt.-% Li2O. Li2O serves to improve the meltability of the starting glasses. Further, it also promotes the mobility of the ions in the glass matrix, and it is assumed that this has a positive effect on the crystallization of some crystal phases, e.g. of low quartz and lithium silicate.
It is also preferred that the glass ceramic, in addition to Li2O, contains further alkali metal oxide MeI2O in an amount of from 0 to 13.0, in particular 1.0 to 13.0 and particularly preferably 2.0 to 13.0 wt.-%. The term “further alkali metal oxide MeI2O” refers to alkali metal oxide with the exception of Li2O, wherein this MeI2O is selected in particular from Na2O, K2O, Rb2O and/or Cs2O. The glass ceramic particularly preferably contains at least one and in particular all of the following further alkali metal oxides MeI2O in the amounts specified:
In a particularly preferred embodiment, the glass ceramic according to the invention contains 1.0 to 4.0 wt.-% K2O.
In addition, it is preferred that the glass ceramic contains 0 to 11.0 and in particular 1.0 to 7.0 wt.-% oxide of divalent elements MeIIO, wherein this oxide MeIIO is selected in particular from MgO, CaO, SrO and/or ZnO. The glass ceramic particularly preferably contains at least one and in particular all of the following oxides of divalent elements MeIIO in the quantities specified:
In a particularly preferred embodiment, the glass ceramic according to the invention contains 1.0 to 7.0, and in particular 1.0 to 2.0 wt.-% MgO.
Further, a glass ceramic is preferred which contains 0 to 10.0 and in particular 2.0 to 9.0 wt.-% oxide of trivalent elements MeIII2O3, wherein this MeIII2O3 is selected in particular from Al2O3, B2O3, Y2O3, La2O3, Ga2O3 and/or In2O3. The glass ceramic particularly preferably contains at least one and in particular all of the following oxides of trivalent elements MeIII2O3 in the amounts specified:
In a particularly preferred embodiment, the glass ceramic according to the invention contains 2.0 to 8.0 wt.-% Al2O3.
Furthermore, a glass ceramic is preferred which contains further oxide of tetravalent elements MeIVO2 in an amount of from 0 to 21.0 wt.-%. The term “further oxide of tetravalent elements MeIVO2” refers to tetravalent oxides with the exception of SiO2, wherein this MeIVO2 is selected in particular from ZrO2, GeO2, CeO2, TiO2 and/or SnO2. The glass ceramic particularly preferably contains at least one and in particular all of the following further oxides of tetravalent elements MeIVO2 in the amounts specified:
In a further preferred embodiment, the glass ceramic contains 0 to 7.0, in particular 0 to 6.5, particularly preferably 1.0 to 6.5 and quite particularly preferably 2.0 to 6.5 wt.-% P2O5.
P2O5 can act as nucleating agent. However, the presence of a nucleating agent is not absolutely necessary for the formation of SiO2 as main crystal phase.
Moreover, a glass ceramic is preferred which contains further oxide of pentavalent elements MeV2O5 in an amount of from 0 to 6.0 and in particular 0 to 5.0 wt.-%. The term “further oxide of pentavalent elements MeV2O5” refers to pentavalent oxides with the exception of P2O5, wherein this MeV2O5 is selected in particular from V2O5, Ta2O5 and/or Nb2O5. The glass ceramic particularly preferably contains at least one and in particular all of the following further oxides of pentavalent elements MeV2O5 in the amounts specified:
A glass ceramic is also preferred which contains 0 to 6.0 wt.-% oxide of hexavalent elements MeVI2O3, wherein this MeVI2O3 is selected in particular from WO3 and/or MoO3. The glass ceramic particularly preferably contains at least one and in particular all of the following oxides MeVIO3 in the amounts specified:
In addition, a glass ceramic is preferred which contains 0 to 5.0 and in particular 0 to 1.0 wt.-% fluorine.
A glass ceramic is particularly preferred which contains at least one and preferably all of the following components in the amounts specified:
wherein MeI2O, MeIIO, MeIII2O3, MeIVO2, MeV2O5 and MeVIO3 have the above-specified meaning.
In a further particularly preferred embodiment, the glass ceramic contains at least one and preferably all of the following components:
Some of the above-mentioned components can serve as colorants and/or fluorescent agents. The glass ceramic according to the invention can in addition also contain further colorants and/or fluorescent agents, which can be selected in particular from inorganic pigments and/or oxides of d- and f-elements, such as the oxides of Sc, Mn, Fe, Co, Pr, Nd, Tb, Er, Dy, Gd, Eu and Yb. Metal colloids, e.g. of Ag, Au and Pd, which can in addition also act as nucleating agents, can also be used as further colorants. These metal colloids can be formed e.g. by reduction of corresponding oxides, chlorides or nitrates during the melting and crystallization processes.
The properties of the glass ceramic are substantially influenced by the main crystal phase. The glass ceramic according to the invention contains SiO2 as main crystal phase. In a preferred embodiment, the glass ceramic according to the invention contains low quartz, cristobalite or a mixture thereof, preferably low quartz or cristobalite and particularly preferably low quartz, as main crystal phase.
The term “main crystal phase” refers to the crystal phase which has the highest proportion by mass out of all the crystal phases present in the glass ceramic. The masses of the crystal phases are in particular determined using the Rietveld method. A suitable method for the quantitative analysis of the crystal phases using the Rietveld method is described e.g. in M. Dittmer's doctoral thesis “Gläser and Glaskeramiken im System MgO—Al2O3—SiO2 mit ZrO2 als Keimbildner” [Glasses and glass ceramics in the MgO—Al2O3—SiO2 system with ZrO2 as nucleating agent], University of Jena 2011.
It is further preferred that the glass ceramic according to the invention contains 5.0 to 50.0 and in particular 10.0 to 30.0 wt.-% SiO2 as crystal phase, in particular in the form of low quartz, cristobalite or mixtures thereof.
The glass ceramic according to the invention can contain, in addition to SiO2 as main crystal phase, also further crystal phases, such as in particular lithium phosphate and/or lithium silicate. Still further nanoscale phases in amorphous or crystalline form can likewise also be present in the glass ceramic according to the invention.
It is preferred that the glass ceramic according to the invention comprises 5.0 to 30.0 and in particular 10.0 to 25.0 wt.-% lithium disilicate.
The type and quantity of crystal phases formed can be controlled in particular by the composition of the starting glass as well as the heat treatment which is used to prepare the glass ceramic from the starting glass. The examples illustrate this by varying the composition and the heat treatment applied.
The glass ceramic according to the invention has a coefficient of thermal expansion CTE (measured in the range of from 100 to 500° C.) of in particular at least 5.0·10−6 K−1, preferably 10.0 to 20.0·10−6 K−1 and particularly preferably 13.0 to 18.0·10−6 K−1. The CTE is determined according to ISO 6872 (2008).
The glass ceramic according to the invention is characterized by a very good chemical stability. To determine the chemical stability, the glass ceramic was tested according to ISO standard 6872 (2008) by determining the mass loss during storage in aqueous acetic acid. The glass ceramic according to the invention displayed a mass loss of preferably less than 30 μg/cm2.
Furthermore, the glass ceramic according to the invention is characterized in particular by mechanical properties which allow a particularly simple and quick machining to bring the glass ceramic e.g. into the shape of a dental restoration.
The glass ceramic has a biaxial breaking strength of preferably at least 200 MPa and particularly preferably 200 to 500 MPa. The biaxial breaking strength was determined according to ISO 6872 (2008) (piston-on-three-balls test).
The translucence of the glass ceramic was determined in the form of the contrast value (CR value) according to British Standard BS 5612 and it was preferably 35 to 80.
The invention likewise relates to precursors with a corresponding composition from which the glass ceramic according to the invention can be prepared by heat treatment. These precursors are a starting glass with corresponding composition and a starting glass with nuclei with corresponding composition. The term “corresponding composition” means that these precursors contain the same components in the same amounts as the glass ceramic, wherein the components with the exception of fluorine are calculated as oxides, as is customary for glasses and glass ceramics.
The invention therefore likewise relates to a starting glass which contains the components of the glass ceramic according to the invention.
The starting glass according to the invention therefore contains as components
Further, the starting glass can also contain other components, such as are specified above for the glass ceramic according to the invention. All those embodiments which are also specified as preferred for the components of the glass ceramic according to the invention are preferred for the components of the starting glass.
The invention likewise relates to a starting glass which contains nuclei for the crystallization of SiO2 and in particular of low quartz and/or cristobalite and preferably of low quartz.
By heat treatment of the starting glass, the starting glass with nuclei can be produced first, which can for its part be converted into the glass ceramic according to the invention having SiO2 as main crystal phase by further heat treatment.
The preparation of the starting glass is carried out in particular in such a way that a mixture of suitable starting materials, such as carbonates, oxides and phosphates, is melted at temperatures of in particular from 1500 to 1800° C. for 0.5 to 10 h. To achieve a particularly high homogeneity, the obtained glass melt is poured into water in order to form a glass granulate, and the obtained granulate is then melted again.
The melt can then be poured into moulds, e.g. steel or graphite moulds, in order to produce blanks of the starting glass, so-called solid glass blanks or monolithic blanks. These monolithic blanks are usually stress-relieved first, e.g. by keeping them at 450 to 600° C. for 5 to 120 min. This stress relief in the specified temperature range usually leads to the formation of nuclei for the crystallization of SiO2 crystal phase and in particular of low quartz crystal phase.
It is likewise possible to put the melt into water again in order to prepare a frit, i.e. a granulate. This frit can be pressed, after grinding and, optionally, addition of further components, such as binders and/or colorants and fluorescent agents, to form a blank, a so-called powder compact.
Finally, the starting glass can also be processed to form a powder after the production of a glass frit.
The starting glass with nuclei can then be produced from the starting glass by heat treatment. This is also called nucleation process.
The invention is therefore likewise directed towards a method for the preparation of the starting glass with nuclei for the crystallization of SiO2, in particular of low quartz, in which the starting glass is subjected to a heat treatment at a temperature of from 450 to 600° C. and in particular 500 to 550° C. for a period of in particular from 5 to 120 min and preferably 10 to 40 min.
The glass ceramic according to the invention can then be formed from the starting glass with nuclei by heat treatment.
The invention is therefore likewise directed towards a method for the preparation of the glass ceramic according to the invention, in which the starting glass, in particular the starting glass with nuclei, is subjected to at least one heat treatment at a temperature of from 700 to 950° C. for a period of in particular from 5 to 40 min and preferably 10 to 30 min.
The starting glass or the starting glass with nuclei can be subjected to the at least one heat treatment e.g. in the form of a solid glass blank or a powder compact.
The at least one heat treatment carried out in the method according to the invention can also take place during a hot pressing, in particular of a solid glass blank, or during a sintering-on, in particular of a powder.
The invention in a preferred embodiment thus relates to a method for the preparation of the glass ceramic according to the invention, in which
In a further preferred embodiment the invention relates to a method for the preparation of the glass ceramic according to the invention, in which
In both preferred embodiments of the method according to the invention a further above-described nucleation can be carried out before the heat treatment in step (b) or (b′).
The glass ceramics according to the invention and the glasses according to the invention are present in particular in the form of powders, granulates or blanks in any form or size, e.g. monolithic blanks, such as platelets, cuboids or cylinders, or powder compacts, in unsintered, partly sintered or densely-sintered form. They can easily be further processed in these forms, e.g. to form dental restorations. They can, however, also be present in the form of dental restorations, such as inlays, onlays, crowns, veneers, facets or abutments.
Dental restorations, such as bridges, inlays, onlays, crowns, veneers, facets or abutments, can be prepared from the glass ceramics according to the invention and the glasses according to the invention. The invention therefore relates to their use as dental material and in particular to their use for the preparation of dental restorations. It is preferred that the glass ceramic or the glass is given the shape of the desired dental restoration by pressing or machining.
The pressing is usually carried out under increased pressure and at increased temperature. It is preferred that the pressing is carried out at a temperature of from 700 to 1200° C. It is further preferred to carry out the pressing at a pressure of from 10 to 30 bar. During pressing, the desired shape change is achieved by viscous flow of the material used. The starting glass according to the invention and the starting glass with nuclei according to the invention as well as preferably the glass ceramic according to the invention can be used for the pressing. The glasses and glass ceramics according to the invention can be used in particular in the form of blanks in any form or size, e.g. solid blanks or powder compacts, e.g. in unsintered, partly sintered or densely-sintered form.
The machining is usually carried out by material removal processes and in particular by milling and/or grinding. It is particularly preferred that the machining is carried out as part of a CAD/CAM method. The starting glass according to the invention, the starting glass with nuclei according to the invention as well as the glass ceramic according to the invention can be used for the machining. The glasses and glass ceramics according to the invention can be used in particular in the form of blanks, e.g. solid blanks or powder compacts, e.g. in unsintered, partly sintered or densely-sintered form. The glass ceramic according to the invention is preferably used for the machining. The glass ceramic according to the invention can also be used in a not yet fully crystallized form which was produced by heat treatment at a lower temperature. This has the advantage that an easier machining and thus the use of simpler equipment for the machining is possible. After the machining of such a partly-crystallized material, the latter is usually subjected to a further heat treatment in order to cause a further crystallization of SiO2 as crystal phase.
However, the glass ceramics according to the invention and the glasses according to the invention are also suitable as coating material of e.g. ceramics, glass ceramics and metals. The invention is therefore likewise directed towards the use of the glasses according to the invention or the glass ceramics according to the invention for coating of in particular ceramics, glass ceramics and metals.
The invention also relates to a method for coating of ceramics, glass ceramics and metals, in which glass ceramic according to the invention or glass according to the invention is applied to the ceramic, the glass ceramic or the metal and exposed to a temperature of at least 600° C.
This can take place in particular by sintering-on and preferably by pressing-on. With sintering-on, the glass ceramic or the glass is applied to the material to be coated, such as ceramic, glass ceramic or metal, in the usual way, e.g. as powder, and then sintered. With the preferred pressing-on, glass ceramic according to the invention or glass according to the invention is pressed on, e.g. in the form of powder compacts or monolithic blanks, at an increased temperature of e.g. from 700 to 1200° C., accompanied by the application of pressure, e.g. 10 to 30 bar.
The methods described in EP 231 773 and the press furnace disclosed there can be used in particular for this. Suitable commercial furnaces are the furnaces of the Programat type from Ivoclar Vivadent AG, Liechtenstein.
Because of the above-described properties of the glass ceramics according to the invention and the glasses according to the invention, these are suitable in particular for use in dentistry. A subject of the invention is therefore also the use of the glass ceramics according to the invention or the glasses according to the invention as dental material and in particular for the preparation of dental restorations or as coating material for dental restorations, such as crowns, bridges and abutments.
The invention therefore also relates to a method for the preparation of a dental restoration, in particular bridge, inlay, onlay, veneer, abutment, partial crown, crown or facet, in which the glass ceramic according to the invention or the starting glass according to the invention is given the shape of the desired dental restoration by pressing, sintering or machining, in particular as part of a CAD/CAM method.
The invention is described in more detail below with reference to non-limiting examples.
A total of 35 glasses and glass ceramics having the composition given in Table I were prepared by melting corresponding starting glasses, optionally nucleation or stress relief, and then heat treatment for the crystallization.
The following meanings apply in Table 1:
In Examples 1 to 35 the starting glasses were first melted on a scale of 100 to 200 g from usual raw materials at the temperature Ts for a period ts. Glass frits were prepared by pouring the melted starting glasses into water. For the further processing of the glass frits, the three method variants A), B) and C) specified below were used:
In examples for which Tc and tc are specified in Table 1 (Examples 3-5, 7-12, 14, 16-24 and 26-35), the glass ceramics were prepared from solid glass blocks. For this, the obtained glass frits were melted again at the temperature Ts for a period ts. The obtained melts of the starting glass were then poured into a graphite mould in order to produce solid glass blocks. These glass monoliths were then usually stress-relieved at the temperature TKb for a period tKb, whereby nucleation could take place. The nucleated starting glasses were then heated to a temperature TC for a period tc. Glass ceramics according to the invention comprising SiO2 as main crystal phase were thereby formed, as could be established by X-ray diffraction tests at room temperature.
It is assumed that in this method variant a volume crystallization of the SiO2 crystal phase has taken place.
In examples for which TSinter and tSinter are specified in Table 1 (1, 2, 6, 15 and 25), the glass ceramics were prepared from powder compacts. For this, the obtained glass frits were ground in a zirconium oxide mill to a particle size of <90 μm. About g of these powders were then pressed to form cylindrical blanks and sintered in a sinter furnace (Programat® from Ivoclar Vivadent AG) at a temperature TSinter and a holding time of tSinter to form dense glass ceramic bodies. Glass ceramics according to the invention comprising SiO2 as main crystal phase were formed by the sintering, as could be established by X-ray diffraction tests at room temperature.
It is assumed that in this method variant a surface crystallization of the SiO2 crystal phase has taken place.
In Example 13, for which Tpress and tPress are specified, the glass ceramic was prepared by hot pressing of solid glass blocks.
For this, the obtained glass frit was melted again at the temperature Ts for a period ts. The obtained melt of the starting glass was then poured into a pre-heated steel mould in order to produce rods. These monolithic glass rods were then stress-relieved at a temperature TKb for a period tKb, whereby nucleation could take place. The rods were then sawn into blocks with a mass of about 4 to 6 g. These solid glass blocks were then pressed to form a shaped body in a hot-pressing furnace at the temperature Tpress and for a holding time of tpress. Glass ceramic according to the invention comprising SiO2 as main crystal phase was formed by the hot pressing, as could be established by X-ray diffraction tests of the formed shaped body at room temperature.
The glass ceramic blocks produced according to Examples 1 to 12 and 14 to 35 were machined in a CAD/CAM unit to form desired test pieces according to dental standard and to form dental restorations, such as crowns. For this, the crystallized blocks were provided with a suitable holder and then given the desired shape in an inLab MC XL grinding unit from Sirona Dental GmbH, Austria.
For the glass ceramic according to Example 1, the colour values (L, a, b) were additionally determined according to DIN5033 and DIN6174 as follows:
The examination of the chemical stability according to ISO 6872 (2008) of the glass ceramic according to Example 1 yielded an acid solubility of only 5 μg/cm2.
Further, glass ceramic blocks obtained according to Example 1 were provided with appropriate holders, and test pieces for determining the biaxial strength were ground out of them with an inLab grinding unit from Sirona Dental GmbH. The test pieces were polished to 15 μm and then the biaxial strength was determined without further thermal treatment. The average strength of the thus-prepared test pieces was 247 MPa.
| Number | Date | Country | Kind |
|---|---|---|---|
| 14168719 | May 2014 | EP | regional |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2015/060765 | 5/15/2015 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2015/173394 | 11/19/2015 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3445252 | MacDowell | May 1969 | A |
| 3804608 | Gaskell et al. | Apr 1974 | A |
| 4011091 | McCollister | Mar 1977 | A |
| 4050946 | Li | Sep 1977 | A |
| 4239521 | Beall | Dec 1980 | A |
| 4755488 | Nagashima | Jul 1988 | A |
| 5057018 | Bowen | Oct 1991 | A |
| 5173453 | Beall | Dec 1992 | A |
| 5446008 | Krolla | Aug 1995 | A |
| 5507981 | Petticrew | Apr 1996 | A |
| 5866489 | Yamaguchi | Feb 1999 | A |
| 6174827 | Goto et al. | Jan 2001 | B1 |
| 6372319 | Abe | Apr 2002 | B1 |
| 6410466 | Goto | Jun 2002 | B1 |
| 6426311 | Goto | Jul 2002 | B1 |
| 7601446 | Ikenishi | Oct 2009 | B2 |
| 8043706 | Goto | Oct 2011 | B2 |
| 20020137618 | Goto | Sep 2002 | A1 |
| 20110030423 | Johannes | Feb 2011 | A1 |
| 20120283086 | Schneider et al. | Nov 2012 | A1 |
| 20130149433 | Ehrt et al. | Jun 2013 | A1 |
| Number | Date | Country |
|---|---|---|
| 2252660 | May 1999 | CA |
| 0231773 | Aug 1987 | EP |
| H10338540 | Dec 1998 | JP |
| 2001288027 | Oct 2001 | JP |
| Entry |
|---|
| International Preliminary Report on Patentability of PCT/EP2015/060765, dated Nov. 22, 2016, 7 pages. |
| Höland et al., “Properties of β-Spodumere Solid Solution Glass-Ceramic Neoceram™ N-11 and the β-Quartz Solid-Solution Glass-Ceramics Neoceram™ N—O, Ceran®, and Robax®,” Glass Ceramic Technology, 2nd Edition, Wiley, 2012, pp. 272-273. |
| Dittmer, Marc, “Glasses and glass-ceramics in the system of MgO—Al2O3—SiO2 with ZrO2 as nucleating agent,” Dissertation, 2011, University of Jena. |
| Number | Date | Country | |
|---|---|---|---|
| 20170088456 A1 | Mar 2017 | US |