Patent Application
20210187496
This application claims benefit under 35 USC § 119 of European Application 19219010.6 filed Dec. 20, 2019, the entire contents of which are incorporated herein by reference.
The present invention relates to a glass container and to a plurality of glass containers, wherein the glass container or each glass container contained in the plurality of glass containers is characterized by an advantageous contour of the outer surface of the circular glass bottom. The present invention also relates to a process for the determination of a physical property of a material that is contained in such a glass container and to the use of a glass container or of a plurality of glass containers for determining a physical property of a material contained in the glass container.
Glass bottles that are used for pharmaceutical purposes (also known as so-called “vials”) are usually prepared from borosilicate glass by hot-forming a borosilicate glass tube. In such a process in a first step the orifice of the vial is formed from the open tube end, wherein this orifice often has the form of a rolled-rim. Thereafter the vial bottom is formed and simultaneously the vial is separated from the residual of the glass tube. For the formation of the vial bottom the glass tube is, for example, secured in a vertical position by means of upper and lower clamping chucks and is then rotated around its longitudinal axis. The rotating glass tube in a certain region is heated by one or two separating gas burners until the heated mass of glass becomes deformable. As soon as this temperature is reached, the tube—under continuing rotation and heating by means of the burner—is extended in axial direction by means of a linear downwards movement of the lower chuck. Thereby the tube in the heated region extends under simultaneous tapering of its diameter, so that a constriction region in the form of a glass thread is formed. After the downward movement the constriction region is further heated. In this way the glass tube at the constriction region further contracts by means of the flow pressure of the burner gases so that the glass walls in the heated region melt together and finally the connection between the upper and the lower tube region pulls off. Thus, two tube regions (or sections) with closed ends are generated, wherein the lower tube region is the final vial, and the upper tube region is the residual glass tube from which further vials can be formed.
During the above-described thermal separation of the lower and the upper tube region, a mem-brane-like bottom is created. In order to provide a bottom thickness that roughly corresponds to the tube wall thickness, the glass in the bottom region has to be kept liquefied under the most massive supply of heat. However, the centrifugal force prevents the glass from penetrating to the centre of the bottom, i. e. to the centre of rotation. A large part gets stuck at about ⅔ of the bottom radius and forms a typical “ring bead”.
Furthermore, when the upper and lower tube regions are drawn apart from each other in the process described above and when in the course of that process a progressive, rotationally symmetrical constriction of the tube occurs until only one thread remains, this tread finally breaks off near its upper end where the gas separation burner are located. The thread essentially falls downwards onto the membrane-like floor in the middle, where it forms an accumulation of glass mass called “the knot”. The minimum bottom thickness is usually found between the ring bead and the knot, the thickest part is usually the knot itself.
In addition to the formation of structures such as the “ring bead” and the “knot”, further irregular structures such as ultrafine fissures can also be observed on the outside of the glass bottom. Such structures are often the result of bringing the outer surface of the glass bottom of the glass container into contact with molding tools which in a conventional process for producing glass tubes are used to finally shape the circular glass bottom while still being in a molten state. The roughness of the surface of the molding tools also effects the structure on the outer surface of the glass bottom.
It has been observed that state of the art glass containers, particularly the state of art pharmaceutical vials that have been prepared by means of the conventional process as described above can often only be inspected optically through the glass bottom to an insufficient extent in an optical inspection machine. The reason for this limited inspection capability is—in addition to the lens effect of the glass bottom caused by the bottom indentation—a non-uniform structure of the outer surface of the glass bottom, which leads to undesired light refracting effects. As a consequence of these light refracting effects a large number of results cannot be interpreted by these inspection machines and the corresponding glass containers are therefore ejected from the automated process.
In general, it is an object of the present invention to at least partly overcome a disadvantage arising from the prior art. It is a particular object of the present invention to provide a glass container, preferably a pharmaceutical vial, that shows an improved inspection capability through the glass bottom, compared to glass containers known from the prior art. Moreover, the glass containers, preferably a pharmaceutical vial, should be characterized in that they can be inspected in an optical inspection machine with a reduced number of glass containers that are ejected because the result obtained by optical inspection of that glass container cannot be interpreted.
A contribution to solving at least one of the objects according to the invention is made by an embodiment 1 of a glass container comprising as container parts: a glass tube with a first end, a further end, an outer diameter d1, an inner diameter d2 and a glass thickness s1, the glass tube being characterized by a longitudinal axis Ltube that passes through the centre of the first and the further end; a circular glass bottom, wherein the circular glass bottom closes the glass tube at the first end, wherein the circular glass bottom comprises an inner surface directed to the inside of the glass container, an outer surface directed to the outside of the glass container and a centre; a curved glass heel extending from an outer end of the circular glass bottom to the first end of the glass tube; wherein at least one, preferably both of the following conditions (α) and (β) is/are fulfilled:
(α) if h(x,y) is the two-dimensional distance between a contact plane representing the ground on which the glass container rests with the circular glass bottom being at least partially in contact with the ground, and the outer surface of the circular glass bottom at a given position x,y, with x=0 and y=0 in the centre of the circular glass bottom, the two-dimensional distance being measured in a direction that is parallel to the longitudinal axis Ltube, wherein
√{square root over ((dh/dx)2+(dh/dy)2)}
is the slope magnitude of the outer surface of the circular glass bottom at the given position x,y, the 75% quantile of the values that have been determined for the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta
for all given positions x,y within a circular area having a radius of 0.4×d2/2 and a centre that corresponds to the centre of the glass bottom, is less than 4100 μm/mm, preferably less than 3900 μm/mm, more preferably less than 3700 μm/mm, even more preferably less than 3500 μm/mm, even more preferably less than 3300 μm/mm, even more preferably less than 3100 μm/mm, even more preferably less than 2900 μm/mm, even more preferably less than 2500 μm/mm and even more preferably less than 2000 μm/mm, wherein adjacent positions x,y increase stepwise by 200 μm and wherein h(x,y)delta=h (x,y)max−h(x,y)min, h(x,y)max being the maximum value for h(x,y) and h(x,y)min being the minimum value for h(x,y) being determined in that circular area;
(β) for the wavefront distortion W(,φ) of a laser light with a wave length of 520 nm, a beam width of at least 0.6×d2 and less than 0.85×d2, that passes through the circular glass bottom in a direction from the outer surface to the inner surface, that is aligned collinear with Ltube and that has been corrected for piston, tilt and defocus, the peak to valley difference
(W(,φ)corrected)max−(W(
, φ)corrected)min
is less than 100 waves, preferably less than 80 waves, more preferably less than 60 waves, even more preferably less than 40 waves, even more preferably less than 30 waves, even more preferably less than 20 waves and even more preferably less than 10 waves.
A contribution to solving at least one of the objects according to the invention is also made by an embodiment 1 of a plurality of glass containers, each glass container comprising as contain-er parts a glass tube with a first end, a further end, an outer diameter d1, and an inner diameter d2 and a glass thickness s1, the glass tube being characterized by a longitudinal axis Ltube that passes through the centre of the first and the further end; a circular glass bottom, wherein the circular glass bottom closes the glass tube at the first end, wherein the circular glass bottom comprises an inner surface directed to the inside of the glass container, an outer surface directed to the outside of the glass container and a centre; a curved glass heel extending from an outer end of the circular glass bottom to the first end of the glass tube; wherein at least one, preferably both of the following conditions (α) and (β) is/are fulfilled:
(α) if h(x,y) is the two-dimensional distance between a contact plane representing the ground on which the glass container rests with the circular glass bottom being at least partially in contact with the ground, and the outer surface of the circular glass bottom at a given position x,y, with x=0 and y=0 in the centre of the circular glass bottom, the two-dimensional distance being measured in a direction that is parallel to the longitudinal axis Ltube, wherein
√{square root over ((dh/dx)2+(dh/dy)2)}.
is the slope magnitude of the outer surface of the circular glass bottom at the given position x,y, for at least 90%, more preferably for at least 95%, even more preferred for at least 99% and most preferably for 100% of the glass containers in the plurality of glass containers the 75% quantile of the values that have been determined for the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta
for all given positions x,y within a circular area having a radius of 0.4×d2/2 and a centre that corresponds to the centre of the glass bottom is less than 4100 μm/mm, preferably less than 3900 μm/mm, more preferably less than 3700 μm/mm, even more preferably less than 3500 μm/mm, even more preferably less than 3300 μm/mm, even more preferably less than 3100 μm/mm, even more preferably less than 2900 μm/mm, even more preferably less than 2500 μm/mm and even more preferably less than 2000 μm/mm, wherein adjacent positions x,y increase stepwise by 200 μm and wherein h(x,y)delta=h(x,y)max−h(x,y)min, h(x,y)max being the maximum value for h(x,y) and h(x,y)min being the minimum value for h(x,y) being determined in that circular area;
(β) for the wavefront distortion W(,φ) of a laser light with a wave length of 520 nm, a beam width of at least 0.6×d2 and less than 0.85×d2, that passes through the circular glass bottom in a direction from the outer surface to the inner surface, that is aligned collinear with Ltube and that has been corrected for piston, tilt and defocus, for at least 90%, more preferably for at least 95%, even more preferred for at least 99% and most preferably for 100% the peak to valley difference
(W(, φ)corrected)max−(W(
,φ)corrected)min
is less than 100 waves, preferably less than 80 waves, more preferably less than 60 waves, even more preferably less than 40 waves, even more preferably less than 30 waves, even more preferably less than 20 waves and even more preferably less than 10 waves.
As used herein, the phrase “plurality of glass containers” in the sense of the present invention preferably comprises at least 10 glass containers, preferably at least 25 glass containers, more preferably at least 50 glass containers, even more preferably at least 75 glass containers and most preferably at least 100 glass containers. Preferably, the plurality of glass containers comprises at most 1000 glass container, more preferably at most 500 glass containers. Furthermore, the plurality of glass containers preferably has been collected arbitrarily and particularly has not been selected with regard to any property. For example, the plurality of glass containers may be the group of containers which are packed together in a typical transport tray.
According to a first particular embodiment of the glass container according to the present invention condition or the plurality of glass containers according to the present invention (α) is fulfilled. According to a second particular embodiment of the glass container according to the present invention or the plurality of glass containers according to the present invention condition (β) is fulfilled. According to a third particular embodiment of the glass container according to the present invention or the plurality of glass containers according to the present invention conditions (α) and (β) are fulfilled.
If the circular glass bottom of a glass container, particularly the circular glass bottom of a vial, is characterized by an outer surface the contour of which is characterized in that the 75% quantile of the values that have been determined for the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta
for all given positions x,y within a circular area having a radius of 0.4×d2/2 and a centre that corresponds to the centre of the glass bottom is less than 4100 μm/mm, it has surprisingly been discovered that the inspection capability through the glass bottom can be significantly increased compared to circular glass bottoms of glass containers known from the prior art.
In an embodiment 2 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to its embodiment 1, wherein the 75% quantile of the values that have been determined for the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta
within a circle having a radius of 0.6×d2/2 and a centre that corresponds to the centre of the glass bottom is less than 4100 μm/mm, preferably less than 3900 μm/mm, more preferably less than 3700 μm/mm, even more preferably less than 3500 μm/mm, even more preferably less than 3300 μm/mm, even more preferably less than 3100 μm/mm, even more preferably less than 2900 μm/mm, even more preferably less than 2500 μm/mm and even more preferably less than 2000 μm/mm.
In an embodiment 3 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to its embodiment 1 or 2, wherein the 75% quantile of the values that have been determined for the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta
within a circle having a radius of 0.8×d2/2 and a centre that corresponds to the centre of the glass bottom is less than 4100 μm/mm, preferably less than 3900 μm/mm, more preferably less than 3700 μm/mm, even more preferably less than 3500 μm/mm, even more preferably less than 3300 μm/mm, even more preferably less than 3100 μm/mm, even more preferably less than 2900 μm/mm, even more preferably less than 2500 μm/mm and even more preferably less than 2000 μm/mm.
In an embodiment 4 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 3, wherein h(x,y)delta is at least 30 μm, preferably at least 50 μm, more preferably at least 75 μm and even more preferably at least 100 μm.
In an embodiment 5 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 4, wherein for the wavefront distortion W(,φ) of a laser light with a wave length of 520 nm, a beam width of at least 0.6×d2 and less than 0.85×d2, that passes through the circular glass bottom in a direction from the outer surface to the inner surface, that is aligned collinear with Ltube and that has been corrected for piston, tilt and defocus, the peak to valley difference
(W(,φ)corrected)max−(W(
,φ)corrected)min
is less than 100 waves, preferably less than 80 waves, more preferably less than 60 waves, even more preferably less than 40 waves, even more preferably less than 30 waves, even more preferably less than 20 waves and even more preferably less than 10 waves.
In an embodiment 6 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiment 1 to 5, wherein for the wavefront distortion W(,φ) of a laser light with a wave length of 520 nm, a beam width of at least 0.6×d2 and less than 0.85×d2, that passes through the circular glass bottom in a direction from the outer surface to the inner surface, that is aligned collinear with Ltube and that has been corrected for piston and tilt, the corrected wavefront distortion is point symmetric and wherein for a fixed set of radii
0=¼,
0=½ and
0=1, the azimuthal peak to valley difference
(W(,φ)corrected)max−(W(
,φ)corrected)min
is less than 100 waves, preferably less than 80 waves, more preferably less than 60 waves, even more preferably less than 40 waves, even more preferably less than 30 waves, even more preferably less than 20 waves and even more preferably less than 10 waves.
In an embodiment 7 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 6, wherein at least within the range from x=−0.4×d2/2 to x=+0.4×d2/2 the maximum value for ĥ(x) that the fitted curvature function takes on in that range is ĥ(x)max, ĥ(x)max being in the range from 0.01 to 0.25 mm when d1 is in the range from 6 to 14 mm, ĥ(x)max being in the range from 0.3 to 0.5 mm when d1 is in the range from 16 to 24 mm and ĥ(x)max being in the range from 1 to 2 mm when d1 is in the range from 30 to 50 mm. ĥ(x) usually reaches its maximum value ĥ(x)max at the centre of the circular glass bottom (x=0). According to a particular embodiment of the glass container or the plurality of glass containers according to the present invention value ĥ(x)max represents the bottom indentation t.
In an embodiment 8 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 7, wherein the topography of the outer surface of the circular glass bottom is defined by a function ĥ(x), wherein ĥ(x) is the azimuthal average of the distance h between a contact plane representing the ground on which the glass container rests with at least a part of the circular glass bottom being in contact with the ground, and the outer surface of the circular glass bottom at any given position that is located on a circle having the centre and the radius |x|, wherein individual values ĥ are determined for a plurality of circles the radius of which increases stepwise by 500 μm, starting with a circle around the centre having a radius of 500 μm, and wherein the individual values ĥ are determined in the range from x=−0.4×d2/2 to x=+0.4×d2/2, d2 having a size such that at least 4 values ĥ, more preferably at least 5 values ĥ, even more preferably at least 6 valuesĥ and most preferably at least 10 values ĥ are determined, wherein the thus obtained individual values ĥ can be fitted in a least square fit with a curvature function (I)
wherein c and h0 being free fitting parameters, and
wherein Δc is the standard deviation error for constant c when fitting the individual values ĥ(x) with curvature function (I) and wherein the relative standard deviation error Δc/c is less than 0.1.
In an embodiment 9 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to its embodiment 8, wherein for the individual values ĥ that have been determined in the range from x=−0.6×d2/2 to x=+0.6×d2/2 the relative standard deviation error Δc/c is less than 0.1.
In an embodiment 10 of the glass container or the plurality of glass containers according to the invention the glass container or in the plurality of glass containers is designed according to its embodiment 8 or 9, wherein for the individual values ĥ that have been determined in the range from x=−0.8×d2/2 to x=+0.8×d2/2 the relative standard deviation error Δc/c is less than 0.1.
In an embodiment 11 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 8 to 10, wherein for the individual values ĥ that have been determined in the range from x=−0.4×d2/2 to x=+0.4×d2/2 the relative standard deviation error Δc/c is less than 0.09.
In an embodiment 12 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 8 to 11, wherein for the individual values ĥ that have been determined in the range from x=−0.6×d2/2 to x=+0.6×d2/2 the relative standard deviation error Δc/c is less than 0.09.
In an embodiment 13 of the glass container or the plurality of glass containers according to the invention the glass container or in the plurality of glass containers is designed according to anyone of its embodiments 8 to 12, wherein for the individual values ĥ that have been determined in the range from x=−0.8×d2/2 to x=+0.8×d2/2 the relative standard deviation error Δc/c is less than 0.09.
In an embodiment 14 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 8 to 13, wherein the relative standard deviation error Δc/c is less than 0.08, preferably less than 0.07, more preferably less than 0.06, even more preferably less than 0.05, even more preferably less than 0.04 and even more preferably less than 0.03.
In an embodiment 15 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 14, wherein for any cut surface of the circular glass bottom that is obtainable by cutting the circular glass bottom in a plane that includes the longitudinal axis Ltube the following condition is fulfilled: s2max/s1×(s2max/s2min−1)≤1.1; preferably s2max/s1×(s2max/s2min−1)≤1.0; more preferably s2max/s1×(s2max/s2min−1)≤0.9; even more preferably s2max/s1×(s2max/s2min−1)≤0.8; even more preferably s2max/s1×(s2max/s2min−1)≤0.7; even more preferably s2max/s1×(s2max/s2min−1)≤0.6; even more preferably s2max/s1×(s2max/s2min−1)≤0.5; even more preferably s2max/s1×(s2max/s2min−1)≤0.4; even more preferably s2max/s1×(s2max/s2min−1)≤0.3; even more preferably s2max/s1×(s2max/s2min−1)≤0.2; most preferably s2max/s1×(s2max/s2min−1)≤0.1; wherein s2max corresponds to the maximum glass thickness of the circular glass bottom and s2min to the minimum glass thickness of the circular glass bottom as determined within a given cut surface at least within the range from x=−0.4×d2/2 to x=+0.4×d2/2, the centre of the circular glass bottom being at position x=0, wherein s2min and s2max are both measured in a direction that is parallel to the longitudinal axis Ltube.
In an embodiment 16 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to its embodiment 15, wherein s2max and s2min are determined within a given cut surface at least within the range from x=−0.6×d2/2 to x=+0.6×d2/2.
In an embodiment 17 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to its embodiment 15 or 16, wherein s2max and s2min are determined at least within a given cut surface within the range from x=−0.8×d2/2 to x=+0.8×d2/2.
In an embodiment 18 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 17, wherein the glass container comprises a top region in which the inner diameter is d4 and a body region in which the inner diameter of the glass tube is d2, wherein d2>d4 and wherein the glass container comprises a shoulder that connects the body region with the top region. Preferably, the shoulder is characterized by a shoulder angle α, wherein α is in the range from 10 to 70°, preferably in the range from 15 to 60°, more preferably in the range from 20 to 50°, even more preferably in the range from 25 to 40° and most preferably in the range from 27° to 33°.
In an embodiment 19 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to its embodiment 18, wherein the glass container in the container part from the glass bottom up to the shoulder is rotation-symmetric around the longitudinal axis Ltube that goes perpendicular through the centre of the glass bottom.
In an embodiment 20 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to its embodiment 18 or 19, wherein d4 is in the range from 5 to 20 mm, preferably in the range from 7 to 14 mm and more preferably in the range from 6 to 8 mm.
In an embodiment 21 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 18 to 20, wherein throughout the body region the glass thickness s1 of the glass tube is in a range from ±0.2 mm, preferably ±0.1 mm, more preferably ±0.08 mm and most preferably ±0.05 mm, in each case based on a mean value of this glass thickness in the body region.
In an embodiment 22 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 21, wherein d2 is in the range from 10 to 60 mm, preferably in the range from 12 to 50 mm, more preferably in the range from 12 to 30 mm, even more preferably in the range from 12 to 25 mm and most preferably in the range from 12 to 17 mm.
In an embodiment 23 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 22, wherein s1 is in the range from 0.5 to 3.0 mm, preferably in the range from 0.7 to 1.8 mm, more preferably in the range from 0.8 to 1.2 mm, even more preferably in the range from 0.9 to 1.1 mm and most preferably in the range from 0.95 to 1.05 mm.
In an embodiment 24 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 23, wherein the glass container has a mass of glass mg and an interior volume Vi and wherein the following condition is fulfilled: mg/Vi0.75<2.0, preferably mg/Vi0.75<1.75.
In an embodiment 25 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 24, wherein the glass container has an interior volume Vi in a range from 2 to 150 ml, preferably from 3 to 100 ml, more preferably from 3 to 50 ml, even more preferably from 3 to 15 ml, most preferably from 3 to 7 ml.
In an embodiment 26 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 25, wherein the glass container has a height h1 in the range from 15 to 100 mm, preferably in the range from 20 to 60 mm, more preferably in the range from 25 to 55 mm, even more preferably in the range from 30 to 50 mm and most preferably in the range from 34 to 46 mm.
In an embodiment 27 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 26, wherein d1 is in the range from 13 to 65 mm, preferably in the range from 15 to 55 mm, more preferably in the range from 15 to 35 mm, even more preferably in the range from 15 to 30 mm and most preferably in the range from 15 to 20 mm.
In an embodiment 28 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 27, wherein at least one of the properties of the glass container selected from the group consisting of s1, d1, h1 and t is within the requirements defined in DIN EN ISO 8362-1:2016-06.
In an embodiment 29 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 28, wherein the glass container is a packaging container for a medical or a pharmaceutical packaging good or both. A preferred pharmaceutical packaging good is a pharmaceutical composition. Preferably, the glass container 1 is suitable for packaging parenteralia in accordance with section 3.2.1 of the European Pharmacopoeia, 7th edition from 2011.
In an embodiment 30 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 29, wherein the glass container is a vial.
In an embodiment 31 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 30, wherein the glass is of a type selected from the group consisting of a borosilicate glass, an aluminosilicate glass, soda lime glass and fused silica. As used herein the term “Soda lime glass” according to the invention is an alkaline/alkaline earth/silicate glass according to table 1 of ISO 12775 (1st edition 1997-10-15).
In an embodiment 32 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 31, wherein the glass container comprises a pharmaceutical composition.
In an embodiment 33 of the glass container or the plurality of glass containers according to the invention the glass container or the plurality of glass containers is designed according to anyone of its embodiments 1 to 32, wherein the glass container comprises a closure at the top of the glass container, preferably a lid.
A contribution to solving at least one of the objects according to the invention is also made by a process for the determination of a physical property of a material that is contained in a glass container comprising as process step:
providing a glass container or a plurality of glass containers according to anyone of embodiments 1 to 33, wherein the glass container or each glass container in the plurality of glass containers contains the material;
determining the physical property of the material by a radiation that passes through the bottom of the glass container.
In an embodiment 2 of the process according to the invention the process is designed according to its embodiment 1, wherein the material is a pharmaceutical composition, preferably a liquid or solid pharmaceutical composition, more preferably a freeze-dried product or a liquid comprising at least one drug dissolved or dispersed therein.
In an embodiment 3 of the process according to the invention the process is designed according to its embodiment 1 or 2, wherein the physical property of the material is determined by radiation in an optical inspection machine, preferably in an automated optical inspection machine.
In an embodiment 4 of the process according to the invention the process is designed according to anyone of its embodiment 1 to 3, wherein the physical property is selected from the group consisting of the transmission, the colour, the refractive index and the absorption at a given wavelength of electromagnetic radiation.
A contribution to solving at least one of the objects according to the invention is also made by the use of a glass container or a plurality of glass containers according to anyone of embodiments 1 to 33 for determining a physical property of a material contained in the glass container.
The glass container according to the present invention or the glass containers contained in the plurality of glass containers according to the present invention is preferably produced by means of an embodiment 1 of a process for the preparation of a glass container from a glass tube in a glass processing machine, wherein the glass tube comprises a first portion with a first end, a second portion with a second end and a longitudinal axis Ltube that passes through the centre of the first and the second end, wherein the glass processing machine comprises a plurality of processing stations and pairs of first and second clamping chucks which are adapted and arranged to hold the glass tube while rotating the glass tube around its longitudinal axis Ltube and to transport the rotating glass tube from one glass container processing station to the next one, wherein the first clamping chucks hold the glass tube at first portion and the second clamping chucks hold the glass tube at the second portion, wherein the process comprises the steps of heating the glass tube at a defined position between the first portion and the second portion by means of at least one separation gas burner to a temperature above the glass transition temperature, preferably above its softening temperature, while the glass tube is rotating around its longitudinal axis Ltube; pulling apart the first portion and the second portion of the heated glass tube, while the heated glass tube is still rotating around its longitudinal axis Ltube, in a direction that is substantially parallel to the longitudinal axis Ltube by moving the first and the second clamping chucks away from each other, thereby forming a glass thread and separating the first portion from the second portion by pulling apart the glass thread, the part of the mass of the glass thread that remains at a portion of the glass tube forming a circular bottom at one end of that portion; characterized in that, while moving away the first and the second clamping chucks in process step III), at least one separation gas burner follows at least one portion of the glass tube selected from the first portion and the second portion in a direction that is substantially parallel to the direction in which the first and the second clamping chucks are moved away from each other, the at least one separation gas burner thereby following the one end of at least one portion of the glass tube selected from the first portion and the second portion.
Surprisingly, it has been discovered that—if at least one separation gas burner follows at least one portion of the glass tube in the separation process—an advantageous bottom geometry of the glass container can be obtained, compared to the bottom geometry obtained in a prior art process in which the separation gas burners remain in a fixed position. The present invention thus simplifies the production of vials by creating the required bottom geometry during the separation process and thereby enables a new, unprecedented quality of the bottom geometry that is ideal for automated inspection processes, both unfilled and filled.
As used herein, the term “softening temperature” of the glass is the temperature at which the glass has a viscosity (determined according to ISO 7884-6:1987) of 107.6 dPa×sec.
In an embodiment 2 of the process for the preparation of a glass container, the process is designed according to its embodiment 1, wherein in process step II) two diametrically opposed separation gas burners are used which are arranged such that the glass tube rotates centrally between the two flames generated by these two separation gas burners.
In an embodiment 3 of the process for the preparation of a glass container, the process is designed according to its embodiment 1 or 2, wherein the first and second clamping chucks are adapted and arranged to hold the glass tube in a vertical position; wherein the first portion of the glass tube corresponds to the lower portion of the glass tube having a lower end and the second portion of the glass tube corresponds to the upper portion of the glass tube having an upper end; wherein the first clamping chucks are arranged as upper clamping chucks holding the upper portion of the glass tube and the second clamping chucks are arranged as lower clamping chucks holding the lower part of the glass tube; wherein in process step III) the lower portion of the glass tube is pulled downwards by moving downwards the lower clamping chucks and wherein, while pulling downwards the lower portion, the at least one separation gas burner is moved downwards in a direction that is substantially parallel to the direction in which the lower clamping chucks are moved downwards, the at least one separation gas burner thereby following the upper end of the lower portion.
In an embodiment 4 of the process for the preparation of a glass container, the process is designed according to its embodiment 3, wherein in process step III) the lower clamping chucks are moved downwards at a point of time t and the at least one separation gas burner is moved downwards at a point of time t′=t+Δt.
In an embodiment 5 of the process for the preparation of a glass container, the process is designed according to its embodiment 4, wherein Δt=0 sec. In this particular embodiment of the process the at least one separation gas burner and the lower clamping chucks (and thus also the lower portion of the glass tube) are moved downwards simultaneously.
In an embodiment 6 of the process for the preparation of a glass container, the process is designed according to its embodiment 4, wherein Δt is in the range from 0.01 to 1.0 sec, preferably in the range from 0.03 to 0.8 sec, more preferably in the range from 0.05 to 0.4 sec and even more preferably in the range from 0.1 to 0.2 sec.
In an embodiment 7 of the process for the preparation of a glass container, the process is designed according to anyone of its embodiments 2 to 6, wherein in process step III) the at least one separation gas burner is moved downwards starting from a position Y′0 to a stop position Y′stop and the lower clamping chucks is moved downwards starting from a position Y0 and, preferably after the at least one separation gas burner has stopped at position Y′stop, to stop at a position Ystop.
In an embodiment 8 of the process for the preparation of a glass container, the process is designed according to its embodiment 7, wherein |Y′stop−Y′0|<|Ystop−Y0|. According to this embodiment it is thus preferred that the distance with which the at least one separation gas burner is moved downwards is smaller than the distance with which the lower clamping chucks are moved downward.
In an embodiment 9 of the process for the preparation of a glass container, the process is designed according to its embodiment 8, wherein (|Y′stop−Y′0|/|Ystop−Y0|) (i. e. the ratio of the distance with which the burner has been moved downwards to the distance with which the lower clamping chucks have been moved downwards) is in the range from 0.1 to 1, preferably in the range from 0.2 to 0.95, more preferably in the range from 0.3 to 0.9, even more preferably in the range from 0.4 to 0.85, even more preferably in the range from 0.5 to 0.8 and most preferably in the range from 0.6 to 0.75.
In an embodiment 10 of the process for the preparation of a glass container, the process is designed according to anyone of its embodiments 2 to 9, wherein the downward movements of the at least one separation gas burner and the lower clamping chucks are independent from each other. In this context it is particularly preferred that the downward movements of the at least one separation gas burner and the lower clamping chucks are accomplished through independent servo drives.
In an embodiment 11 of the process for the preparation of a glass container, the process is designed according to anyone of its embodiments 2 to 10, wherein the downward movements of the at least one separation gas burner and the lower clamping chucks are both linear synchronous with each other.
In an embodiment 12 of the process for the preparation of a glass container, the process is designed according to anyone of its embodiments 2 to 11, wherein the distance between the at least one separation gas burner and the upper end of the lower portion is kept constant when the at least one separation gas burner follows the upper end of the lower portion.
In an embodiment 13 of the process for the preparation of a glass container, the process is designed according to anyone of its embodiments 2 to 12, wherein the outer surface of the upper end of the lower portion does not come into contact with any part of the glass processing machine while the final shape of the circular glass bottom is formed.
In an embodiment 14 of the process for the preparation of a glass container, the process is designed according to anyone of its embodiments 2 to 13, wherein after process step III) in a further process step IV) the thickness of the glass in the circular glass bottom is equalized by heating the circular glass bottom, while still having a temperature above the glass transition temperature and while still rotating the lower portion of the glass tube around its longitudinal axis Ltube, with at least one bottom shaping gas burner, thereby forming the final shape of the circular glass bottom.
In an embodiment 15 of the process for the preparation of a glass container, the process is designed according to anyone of its embodiments 2 to 13, wherein after process step III) in a further process step IV) the thickness of the glass in the circular glass bottom is equalized by bringing the outer surface of the circular glass bottom, while still having a temperature above the glass transition temperature and while still rotating the lower portion of the glass tube around its longitudinal axis Ltube, into contact with a molding tool, thereby forming the final shape of the circular glass bottom.
In an embodiment 16 of the process for the preparation of a glass container, the process is designed according to anyone of its embodiments 2 to 13, wherein after process step III) in a further process step IV) the thickness of the glass in the circular glass bottom is equalized by heating the circular glass bottom, while still having a temperature above the glass transition temperature and while still rotating the lower portion of the glass tube around its longitudinal axis Ltube, with at least one bottom shaping gas burner, followed by a process step of bringing the outer surface of the circular glass bottom, while still having a temperature above the glass transition temperature and while still rotating the lower portion of the glass tube around its longitudinal axis Ltube, into contact with a molding tool, thereby forming the final shape of the circular glass bottom.
In an embodiment 17 of the process for the preparation of a glass container, the process is designed according to anyone of its embodiments 14 to 16, wherein the process comprises the further process step of heating the lower portion of the glass tube at the lower end by means of at least one further gas burner to a temperature above its glass transition temperature while rotating the glass tube around its longitudinal axis Ltube and forming an orifice, preferably an orifice in the form of a flange or a rolled rim, at the lower end of the glass tube, wherein the processing stations of the glass processing machine are arranged along at least one circle, wherein the glass tube is passed along this circle from one processing station to the next one while rotating around its longitudinal axis Ltube, and wherein process steps I) to IV) are all carried out at processing stations which are arranged within the same circle.
The glass container according to the invention or the glass container contained in the plurality of glass containers according to the invention may have any size or shape which the skilled person deems appropriate in the context of the invention. Preferably, the top region of the glass container comprises an opening, which allows for inserting a pharmaceutical composition into the interior volume of the glass container. A preferred glass container is a pharmaceutical glass container, more preferably one selected from the group consisting of a vial, an ampoule or a combination thereof, wherein a vial is particularly preferred.
For the use in this document, the interior volume Vi represents the full volume of the interior of the glass container. This volume may be determined by filling the interior of the glass container with water up to the brim and measuring the volume of the amount of water which the interior can take up to the brim. Hence, the interior volume as used herein is not a nominal volume as it is often referred to in the technical field of pharmacy. This nominal volume may for example be less than the interior volume by a factor of about 0.5.
The following are particularly preferred embodiments of the glass container according to the present invention (or of the glass container contained in the plurality of glass containers according to the present invention). When reference is made to the relative standard deviation error Δc/c, the values for Δc and c are preferably determined by fitting the individual values ĥ (x) that have been obtained within the range from x=−0.8×d2/2 to x=+0.8×d2/2 with curvature function (I). When reference is made to the 75% quantile of the values that have been determined for the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta,
this term has been determined for all given positions x,y within a circular area having a radius of 0.8×d2/2. When reference is made to the parameters s2max/s1×(s2max/s2min−1), the corresponding value is also preferably determined within the range from x=−0.8×d2/2 to x=+0.8×d2/2.
According to a first preferred embodiment of the glass container according to the present invention (or of the glass container contained in the plurality of glass containers according to the present invention) the glass container is a vial with an overflow capacity equal to or larger than 1 ml up to maximal 5 ml, preferably a vial with a size designation “2R” according to DIN EN ISO 8362-1:2016-06, wherein it is furthermore preferred that at least one, preferably all of the following conditions is/are fulfilled: s1 is in the range from 0.4 to 2 mm, preferably in the range from 0.8 to 1.3 mm and more preferably in the range from 0.9 to 1.15 mm; d1 is in the range from 13 to 19 mm, preferably in the range from 14 to 18 mm and more preferably in the range from 15 to 17 mm; Δc/c is less than less than 0.1, preferably less than 0.09, more preferably less than 0.08, even more preferably less than 0.07, even more preferably less than 0.06, even more preferably less than 0.05, even more preferably less than 0.04 and even more preferably less than 0.03; ĥ(x)max is in the range from 0.01 to 0.75 mm, preferably in the range from 0.05 to 0.5 mm and even more preferably in the range from 0.08 to 0.12 mm; the 75% quantile of the values that have been determined the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta
is less than 4100 μm/mm, preferably less than 3900 μm/mm, more preferably less than 3700 μm/mm, even more preferably less than 3500 μm/mm, even more preferably less than 3300 μm/mm, even more preferably less than 3100 μm/mm, even more preferably less than 2900 μm/mm, even more preferably less than 2500 μm/mm and even more preferably less than 2000 μm/mm; s2max/s1×(s2max/s2min−1) is less than 1.1, preferably less than 0.8 and even more preferably less than 0.5.
According to a second preferred embodiment of the glass container according to the present invention the glass container is a vial with an overflow capacity of larger than 4 ml up to maximal 8 ml, preferably a vial with a size designation “4R” according to DIN EN ISO 8362-1:2016-06, wherein it is furthermore preferred that at least one, preferably all of the following conditions is/are fulfilled: s1 is preferably in the range from 0.9 to 1.15 mm; d1 is in the range from 13 to 19 mm, preferably in the range from 14 to 18 mm and even more preferably in the range from 15 to 17 mm; Δc/c less than less than 0.1, preferably less than 0.09, more preferably less than 0.08, even more preferably less than 0.07, even more preferably less than 0.06, even more preferably less than 0.05, even more preferably less than 0.04 and even more preferably less than 0.03; ĥ(x)max is in the range from 0.01 to 0.75 mm, preferably in the range from 0.05 to 0.5 mm and even more preferably in the range from 0.08 to 0.12 mm; the 75% quantile of the values that have been determined the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta
is less than 4100 μm/mm, preferably less than 3900 μm/mm, more preferably less than 3700 μm/mm, even more preferably less than 3500 μm/mm, even more preferably less than 3300 μm/mm, even more preferably less than 3100 μm/mm, even more preferably less than 2900 μm/mm, even more preferably less than 2500 μm/mm and even more preferably less than 2000 μm/mm; s2max/s1×(s2max/s2min−1) is less than 1.1, preferably less than 0.8 and even more preferably less than 0.5.
According to a third preferred embodiment of the glass container according to the present invention the glass container is a vial with an overflow capacity of larger than 8 ml up to maximal 10.75 ml, preferably a vial with a size designation “6R” according to DIN EN ISO 8362-1:2016-06, wherein it is furthermore preferred that at least one, preferably all of the following conditions is/are fulfilled: s1 is preferably in the range from 0.9 to 1.15 mm; d1 is in the range from 19 to 25 mm, preferably in the range from 20 to 24 mm and even more preferably in the range from 21 to 23 mm; Δc/c is less than less than 0.1, preferably less than 0.09, more preferably less than 0.08, even more preferably less than 0.07, even more preferably less than 0.06, even more preferably less than 0.05, even more preferably less than 0.04 and even more preferably less than 0.03; ĥ(x)max is in the range from 0.01 to 0.75 mm, preferably in the range from 0.05 to 0.5 mm and even more preferably in the range from 0.08 to 0.12 mm; the 75% quantile of the values that have been determined the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta
is less than 4100 μm/mm, preferably less than 3900 μm/mm, more preferably less than 3700 μm/mm, even more preferably less than 3500 μm/mm, even more preferably less than 3300 μm/mm, even more preferably less than 3100 μm/mm, even more preferably less than 2900 μm/mm, even more preferably less than 2500 μm/mm and even more preferably less than 2000 μm/mm; s2max/s1×(s2max/s2min−1) is less than 1.1, preferably less than 0.8 and even more preferably less than 0.5.
According to a fourth preferred embodiment of the glass container according to the present invention the glass container is a vial with an overflow capacity of larger than 10.75 ml up to maximal 12.5 ml, preferably a vial with a size designation “8R” according to DIN EN ISO 8362-1:2016-06, wherein it is furthermore preferred that at least one, preferably all of the following conditions is/are fulfilled: s1 is preferably in the range from 0.9 to 1.15 mm; d1 is in the range from 19 to 25 mm, preferably in the range from 20 to 24 mm and even more preferably in the range from 21 to 23 mm; Δc/c is less than less than 0.1, preferably less than 0.09, more preferably less than 0.08, even more preferably less than 0.07, even more preferably less than 0.06, even more preferably less than 0.05, even more preferably less than 0.04 and even more preferably less than 0.03; ĥ(x)max is in the range from 0.01 to 0.75 mm, preferably in the range from 0.05 to 0.5 mm and even more preferably in the range from 0.08 to 0.12 mm; the 75% quantile of the values that have been determined the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta
is less than 4100 μm/mm, preferably less than 3900 μm/mm, more preferably less than 3700 μm/mm, even more preferably less than 3500 μm/mm, even more preferably less than 3300 μm/mm, even more preferably less than 3100 μm/mm, even more preferably less than 2900 μm/mm, even more preferably less than 2500 μm/mm and even more preferably less than 2000 μm/mm; s2max/s1×(s2max/s2min−1) is less than 1.1, preferably less than 0.8 and even more preferably less than 0.5.
According to a fifth preferred embodiment of the glass container according to the present invention the glass container is a vial with an overflow capacity of larger than 12.5 ml up to maximal 16.25 ml, preferably a vial with a size designation “10R” according to DIN EN ISO 8362-1:2016-06, wherein it is furthermore preferred that at least one, preferably all of the following conditions is/are fulfilled: s1 is preferably in the range from 0.9 to 1.15 mm; d1 is in the range from 21 to 27 mm, preferably in the range from 22 to 26 mm and even more preferably in the range from 23 to 25 mm; Δc/c is less than less than 0.1, preferably less than 0.09, more preferably less than 0.08, even more preferably less than 0.07, even more preferably less than 0.06, even more preferably less than 0.05, even more preferably less than 0.04 and even more preferably less than 0.03; ĥ(x)max is in the range from 0.01 to 0.75 mm, preferably in the range from 0.05 to 0.5 mm and even more preferably in the range from 0.08 to 0.12 mm; the 75% quantile of the values that have been determined the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta
is less than 4100 μm/mm, preferably less than 3900 μm/mm, more preferably less than 3700 μm/mm, even more preferably less than 3500 μm/mm, even more preferably less than 3300 μm/mm, even more preferably less than 3100 μm/mm, even more preferably less than 2900 μm/mm, even more preferably less than 2500 μm/mm and even more preferably less than 2000 μm/mm; s2max/s1×(s2max/s2min−1) is less than 1.1, preferably less than 0.8 and even more preferably less than 0.5.
According to a sixth preferred embodiment of the glass container according to the present invention the glass container is a vial with an overflow capacity of larger than 16.25 ml up to maximal 22.5 ml, preferably a vial with a size designation “15R” according to DIN EN ISO 8362-1:2016-06, wherein it is furthermore preferred that at least one, preferably all of the following conditions is/are fulfilled: s1 is in the range from 0.4 to 2 mm and preferably in the range from 0.9 to 1.15 mm; d1 is in the range from 21 to 27 mm, preferably in the range from 22 to 26 mm and even more preferably in the range from 23 to 25 mm; Δc/c is less than less than 0.1, preferably less than 0.09, more preferably less than 0.08, even more preferably less than 0.07, even more preferably less than 0.06, even more preferably less than 0.05, even more preferably less than 0.04 and even more preferably less than 0.03; ĥ(x)max is in the range from 0.01 to 0.75 mm, preferably in the range from 0.05 to 0.5 mm and even more preferably in the range from 0.08 to 0.12 mm; the 75% quantile of the values that have been determined the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta
is less than 4100 μm/mm, preferably less than 3900 μm/mm, more preferably less than 3700 μm/mm, even more preferably less than 3500 μm/mm, even more preferably less than 3300 μm/mm, even more preferably less than 3100 μm/mm, even more preferably less than 2900 μm/mm, even more preferably less than 2500 μm/mm and even more preferably less than 2000 μm/mm; s2max/s1×(s2max/s2min−1) is less than 1.1, preferably less than 0.8 and even more preferably less than 0.5.
According to a seventh preferred embodiment of the glass container according to the present invention the glass container is a vial with an overflow capacity of larger than 22.5 ml up to maximal 29.25 ml, preferably a vial with a size designation “20R” according to DIN EN ISO 8362-1:2016-06, wherein it is furthermore preferred that at least one, preferably all of the following conditions is/are fulfilled: s1 is in the range from 0.5 to 2.5 mm, preferably in the range from 0.9 to 1.6 mm and even more preferably in the range from 1.15 to 1.25 mm; d1 is in the range from 27 to 33 mm, preferably in the range from 28 to 32 mm and even more preferably in the range from 29 to 31 mm; Δc/c is less than less than 0.1, preferably less than 0.09, more preferably less than 0.08, even more preferably less than 0.07, even more preferably less than 0.06, even more preferably less than 0.05, even more preferably less than 0.04 and even more preferably less than 0.03; ĥ(x)max is in the range from 0.05 to 0.75 mm, preferably in the range from 0.1 to 0.5 mm and even more preferably in the range from 0.15 to 0.25 mm; the 75% quantile of the values that have been determined the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta
is less than 4100 μm/mm, preferably less than 3900 μm/mm, more preferably less than 3700 μm/mm, even more preferably less than 3500 μm/mm, even more preferably less than 3300 μm/mm, even more preferably less than 3100 μm/mm, even more preferably less than 2900 μm/mm, even more preferably less than 2500 μm/mm and even more preferably less than 2000 μm/mm; s2max/s1×(s2max/s2min−1) is less than 1.1, preferably less than 0.8 and even more preferably less than 0.5.
According to an eighth preferred embodiment of the glass container according to the present invention the glass container is a vial with an overflow capacity of larger than 29.25 ml up to maximal 35 ml, preferably a vial with a size designation “25R” according to DIN EN ISO 8362-1:2016-06, wherein it is furthermore preferred that at least one, preferably all of the following conditions is/are fulfilled: s1 is in the range from 0.5 to 2.5 mm, preferably in the range from 0.9 to 1.6 mm and even more preferably in the range from 1.15 to 1.25 mm; d1 is in the range from 27 to 33 mm, preferably in the range from 28 to 32 mm and even more preferably in the range from 29 to 31 mm; Δc/c is less than less than 0.1, preferably less than 0.09, more preferably less than 0.08, even more preferably less than 0.07, even more preferably less than 0.06, even more preferably less than 0.05, even more preferably less than 0.04 and even more preferably less than 0.03; ĥ(x)max is in the range from 0.05 to 0.75 mm, preferably in the range from 0.1 to 0.5 mm and even more preferably in the range from 0.15 to 0.25 mm; the 75% quantile of the values that have been determined the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta
is less than 4100 μm/mm, preferably less than 3900 μm/mm, more preferably less than 3700 μm/mm, even more preferably less than 3500 μm/mm, even more preferably less than 3300 μm/mm, even more preferably less than 3100 μm/mm, even more preferably less than 2900 μm/mm, even more preferably less than 2500 μm/mm and even more preferably less than 2000 μm/mm; s2max/s1×(s2max/s2min−1) is less than 1.1, preferably less than 0.8 and even more preferably less than 0.5.
According to a ninth preferred embodiment of the glass container according to the present invention the glass container is a vial with an overflow capacity of larger than 35 ml up to maximal 49.75 ml, preferably a vial with a size designation “30R” according to DIN EN ISO 8362-1:2016-06, wherein it is furthermore preferred that at least one, preferably all of the following conditions is/are fulfilled: s1 is in the range from 0.5 to 2.5 mm, preferably in the range from 0.9 to 1.6 mm and even more preferably in the range from 1.15 to 1.25 mm; d1 is in the range from 27 to 33 mm, preferably in the range from 28 to 32 mm and even more preferably in the range from 29 to 31 mm; Δc/c is less than less than 0.1, preferably less than 0.09, more preferably less than 0.08, even more preferably less than 0.07, even more preferably less than 0.06, even more preferably less than 0.05, even more preferably less than 0.04 and even more preferably less than 0.03; ĥ(x)max is in the range from 0.05 to 0.75 mm, preferably in the range from 0.1 to 0.5 mm and even more preferably in the range from 0.15 to 0.25 mm; the 75% quantile of the values that have been determined the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta
is less than 4100 μm/mm, preferably less than 3900 μm/mm, more preferably less than 3700 μm/mm, even more preferably less than 3500 μm/mm, even more preferably less than 3300 μm/mm, even more preferably less than 3100 μm/mm, even more preferably less than 2900 μm/mm, even more preferably less than 2500 μm/mm and even more preferably less than 2000 μm/mm; s2max/s1×(s2max/s2min−1) is less than 1.1, preferably less than 0.8 and even more preferably less than 0.5.
According to a tenth preferred embodiment of the glass container according to the present invention the glass container is a vial with an overflow capacity of larger than 49.75 ml up to maximal 92.5m1, preferably a vial with a size designation “50R” according to DIN EN ISO 8362-1:2016-06, wherein it is furthermore preferred that at least one, preferably all of the following conditions is/are fulfilled: s1 is in the range from 0.4 to 2.5 mm, preferably in the range from 1.3 to 1.8 mm and even more preferably in the range from 1.45 to 1.55 mm; d1 is in the range from 37 to 43 mm, preferably in the range from 38 to 42mm and even more preferably in the range from 39 to 41 mm; Δc/c is less than less than 0.1, preferably less than 0.09, more preferably less than 0.08, even more preferably less than 0.07, even more preferably less than 0.06, even more preferably less than 0.05, even more preferably less than 0.04 and even more preferably less than 0.03; ĥ(x)max is in the range from 0.075 to 1.2 mm, preferably in the range from 0.1 to 0.75 mm and even more preferably in the range from 0.15 to 0.25 mm; the 75% quantile of the values that have been determined the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta
is less than 4100 μm/mm, preferably less than 3900 μm/mm, more preferably less than 3700 μm/mm, even more preferably less than 3500 μm/mm, even more preferably less than 3300 μm/mm, even more preferably less than 3100 μm/mm, even more preferably less than 2900 μm/mm, even more preferably less than 2500 μm/mm and even more preferably less than 2000 μm/mm; s2max/s1×(s2max/s2min−1) is less than 1.1, preferably less than 0.8 and even more preferably less than 0.5.
According to an eleventh preferred embodiment of the glass container according to the present invention the glass container is a vial with an overflow capacity of larger than 92.5 ml up to maximal 150 ml, preferably a vial with a size designation “100R” according to DIN EN ISO 8362-1:2016-06, wherein it is furthermore preferred that at least one, preferably all of the following conditions is/are fulfilled: s1 is in the range from 0.4 to 2.5 mm, preferably in the range from 1.3 to 1.8 mm and even more preferably in the range from 1.65 to 1.75 mm; d1 is in the range from 44 to 50 mm, preferably in the range from 45 to 49 mm and even more preferably in the range from 46 to 48 mm; Δc/c is less than less than 0.1, preferably less than 0.09, more preferably less than 0.08, even more preferably less than 0.07, even more preferably less than 0.06, even more preferably less than 0.05, even more preferably less than 0.04 and even more preferably less than 0.03; ĥ(x)max is in the range from 0.075 to 1.2 mm, preferably in the range from 0.1 to 0.75 mm and even more preferably in the range from 0.15 to 0.25 mm; the 75% quantile of the values that have been determined the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta
is less than 4100 μm/mm, preferably less than 3900 μm/mm, more preferably less than 3700 μm/mm, even more preferably less than 3500 μm/mm, even more preferably less than 3300 μm/mm, even more preferably less than 3100 μm/mm, even more preferably less than 2900 μm/mm, even more preferably less than 2500 μm/mm and even more preferably less than 2000 μm/mm; s2max/s1×(s2max/s2min−1) is less than 1.1, preferably less than 0.8 and even more preferably less than 0.5.
The glass of the container may be any type of glass and may consist of any material or combination of materials which the skilled person deems suitable in the context of the invention. Preferably, the glass is suitable for pharmaceutical packaging. Particularly preferable, the glass is of type I, more preferably type I b, in accordance with the definitions of glass types in section 3.2.1 of the European Pharmacopoeia, 7th edition from 2011. Additionally, or alternatively preferable to the preceding, the glass is selected from the group consisting of a borosilicate glass, an aluminosilicate glass, soda lime glass and fused silica; or a combination of at least two thereof. For the use in this document, an aluminosilicate glass is a glass which has a content of Al2O3 of more than 8 wt.-%, preferably more than 9 wt.-%, particularly preferable in a range from 9 to 20 wt.-%, in each case based on the total weight of the glass. A preferred aluminosilicate glass has a content of B2O3 of less than 8 wt.-%, preferably at maximum 7 wt.-%, particularly preferably in a range from 0 to 7 wt.-%, in each case based on the total weight of the glass. For the use in this document, a borosilicate glass is a glass which has a content of B2O3 of at least 1 wt.-%, preferably at least 2 wt.-%, more preferably at least 3 wt.-%, more preferably at least 4 wt.-%, even more preferably at least 5 wt.-%, particularly preferable in a range from 5 to 15 wt.-%, in each case based on the total weight of the glass. A preferred borosilicate glass has a content of Al2O3 of less than 7.5 wt.-%, preferably less than 6.5 wt.-%, particularly preferably in a range from 0 to 5.5 wt.-%, in each case based on the total weight of the glass. In a further aspect, the borosilicate glass has a content of Al2O3 in a range from 3 to 7.5 wt.-%, preferably in a range from 4 to 6 wt.-%, in each case based on the total weight of the glass.
A glass which is further preferred according to the invention is essentially free from B. Therein, the phrase “essentially free from B” refers to glasses which are free from B which has been added to the glass composition by purpose. This means that B may still be present as an impurity, but preferably at a proportion of not more than 0.1 wt.-%, more preferably not more than 0.05 wt.-%, in each case based on the weight of the glass.
The following measurement methods are to be used in the context of the invention. Unless otherwise specified, the measurements have to be carried out at an ambient temperature of 23° C., an ambient air pressure of 100 kPa (0.986 atm) and a relative atmospheric humidity of 50%.
The distance between the outer surface of the circular glass bottom and the ground is determined by means of non-contact profilometer (cyberSCAN CT 300; cyberTECHNOLOGIES, Eching-Dietersheim, Germany) and a chromatic sensor (Precitec CHRocodile S 3000) using the ASCAN software. As shown in
Fitting the curvature function ĥ (x) with the individual ĥ-values
In order to characterize the mean curvature of the glass bottom, the height function (I)
is fitted to at least four nodes Hi(xi) of the radial height profile using a common least square fitting, implemented in standard mathematical software packages, e.g. the “curve_fit” function of the open source scipy.optimize package:
https://docs.scipy.org/doc/scipy/reference/generated/scipy.optimize.curve_fit.html
For the fit the variable parameters are c and h0 are used. These variables are varied to obtain the minimum of
wherein standard deviation error (or fitting error) for constant c is referred to as “Δc”. The standard deviation error is defined as Δc=√{square root over (σ2)} (σ2 being the variance).
The curvature c directly affects imaging through the glass bottom. The offset height h0 depends on the reference system. In the case of referencing to the standing area, the offset height h0≈t (but only in rare cases equal).
Determination of the slope at position x,y and of the h(x,y)max- and h(x,y)min value
The two-dimensional distance between the outer surface of the circular glass bottom and the ground is again determined by means of a non-contact profilometer (cyberSCAN CT 300; cyberTECHNOLOGIES, Eching-Dietersheim, Germany) and a chromatic sensor (Precitec CHRocodile S 3000). For the determination of the h(x,y)-values, the glass bottom is divided into an array of square parts 112 having an edge length of 200 μm as shown in
From the thus obtained h(x,y)-values the slope-values are calculated using an appropriate mathematical software, for example the “Slope Analysis” function of the Mx software version 8.0.0.3 (Zygo, part of AMETEK, Inc.). The slope magnitude can be calculated as slope magnitude=√{square root over ((dh/dx)2+(dh/dy)2)}.
For this calculation with the Mx software a slope lateral resolution as well as integration length of the edge length of the square parts 112 can be used, here 200 μm. The h(x,y)max-value corresponds to the highest h(x,y)-value and the h(x,y)min-value corresponds to the lowest h(x,y)-value that have been determined within the circle having a radius of 0.4×d2/2 (or a radius of 0.6×d2/2 or 0.8×d2/2).
A polar coordinate system is used to fit a continuous wavefront W(, φ) to the measured nodes Wi. The wavefront is defined on the unit circle, thus ρ=1 corresponds to
With 2W<A<(2W+2 mm) and A being the measurement diameter of the Shack-Hartmann sensor. This continuous wavefront can again be expressed in Zernike terms by a superposition of Zernike polynomials (described by Thibos et al.: “Standards for Reporting the Optical Aberrations of Eyes”; Journal of Refractive Surgery; Vol. 18 (2002); pages S652-S660) as W(,φ)=ΣaiZi.
Here the coefficients a have been computed with the inner product
ai=∫∫ZiW(,φ)d
dφ,
where has been integrated from 0 to 1 and φ from 0 to 2 p. We define the corrected wavefront distortion W(
,φ)corrected
W(,φ)corrected=W(
,φ)−a0Z0−a1Z1−a2Z2−a4Z4
as the wavefront with piston (Z0), tilt (Z1, Z2) and defocus (Z4) subtracted. The OSA/ANSI indexing conventions as described in Thibos et al. are used. A setup to measure the wavefront distortion W(,φ) is shown in
Determination of s2max and s2min
The measurement of the thickness of the circular glass bottom was performed using a CHRocodile M4 high resolution measuring head (Precitec GmbH & Co. KG, Lemgo, Germany) with a measuring range of 200-3000 μm and a resolution of 0.1 μm. A step width of 0.1 mm was selected laterally.
The wall thickness s1 of the glass container at a given position as well as the outer diameter (d1) of the glass container at a given position are determined in accordance with DIN ISO 8362-1:2016-06. The inner diameter (d2) can be calculated from s1 and d1.
A glass tube (Fiolax® clear, Schott AG, Germany) having an outer diameter d1 of 30 mm and a wall thickness s1 of 1.1 mm is loaded into the head of a rotary machine. While rotating around its major axis the glass tube is heated to its softening point with two separation gas burners as shown in
Furthermore, the burner was moved downwards with a time offset (Δt) of 0.085 sec. In a Comparative Example representing the prior-art process the burner remains at a fixed position when the lower clamping chucks are moved downwards. The glass containers prepared as described above are characterized by a volume of 20 ml.
, φ)corrected)max − (W(
, φ)corrected)min
As can be seen, adjusting the outer contour of the circular glass bottom in order to ensure that the 75% quantile of the values for the term
√{square root over ((dh/dx)2+(dh/dy)2)}×d1/h(x,y)delta
for all given positions x,y within a circular area having a radius of 0.4×d2/2 is less than 4100 μm/mm significantly improves the optical inspection capability of the glass container.
From the thus obtained values for h the azimuthal average corresponds to the individual value ĥ that has been determined for any given circle 111.
in which c and h0 serve as individual fitting parameters. The above function is the curvature function of a sphere having the radius R with c=1/R. Values for c (and also for the standard deviation error (Δc) indicating how exactly the determined individual values of ĥ can be reproduced using the curvature function given above) are determined using an appropriate mathematical software (ASCAN-Software) as described in the “Test method”-section above.
√{square root over ((dh/dx)2+(dh/dy)2)}
of the outer surface 106 of the glass bottom 104 at a given position x,y. The distance h(x,y) between the outer surface 106 of the circular glass bottom 104 and the ground at a given position x,y is determined by means of a non-contact profilometer. For the determination of the individual values of the two-dimensional distance h(x,y), the glass bottom 104 is divided into an array of square parts 112 having an edge length of 200 μm. At the centre of each of these square parts 112 the distance between the outer surface 106 of the glass bottom 104 and the ground is determined at measurement point 135 as shown in
From the thus obtained h(x,y)-values the slope magnitude representing the slope of between measurement points for different x and y, preferably between neighboring measurement points, is calculated using an appropriate mathematical software, for example the “Slope Analysis” function of the Mx software.
The h(x,y)max-value corresponds to the highest h(x,y)-value and the h(x,y)min-value corresponds to the lowest h(x,y)-value that have been determined within the circular area 136 having a radius of 0.4×d2/2 (or within the circular area 137 having a radius of 0.6×d2/2 or within the circular area 138 having a radius of 0.8×d2/2).
The Shack-Hartmann sensor 123 contains an array micro-lenses 133 that images a characteristic dot pattern onto a CCD. For a planar wavefront 129, the dot pattern has the same spacing as the spacing of the micro-lens array. However, if the wavefront is aberrated when passing through the glass bottom to obtain the aberrated wavefront 125, any aberrations locally displace the dot laterally in the direction of the distortion (as shown in
100 glass container
101 glass tube
102 first end of the glass tube 101
103 second end of the glass tube 101
104 circular glass bottom
105 inner surface of the circular glass bottom 104
106 outer surface of the circular glass bottom 104
107 curved glass heel
108 outer end of the circular glass bottom
109 contact plane representing the ground
110 centre of the glass bottom 104 or the circle 111
111 Circle
112 square in the centre of which h(x,y) is determined
113 cut surface
114 first or lower portion of the glass tube 101
115 first or lower end of the first or lower portion 114
116 second or upper portion of the glass tube 101
117 second or upper end of the second or upper portion 116
118 first or upper clamping chucks
119 second or lower clamping chucks
120 separation gas burner
121 glass thread
122 upper end of portion 114,116, preferably of lower portion 114
123 Shark-Hartmann-sensor
124 aperture for measuring range of the Shark-Hartmann-sensor 123
125 wavefront aberrated by the circular glass bottom 104
126 cutting plane if top region has to be removed for measurement
127 H2O (filling height: 10 mm)
128 transparent support
129 undisturbed wavefront
130 collimated laser beam (width: 1/e2 at 2W)
131 laser source (520 nm)
132 plane of object
133 lens (NA 0.5)
134 plane of image
135 measurement point
136 circular area having a radius of 0.4×d2/2
137 circular area having a radius of 0.6×d2/2
138 circular area having a radius of 0.8×d2/2