Glass fiber-based sound absorbing sheet having adjustable permeability and air porosity

Information

  • Patent Grant
  • 9190046
  • Patent Number
    9,190,046
  • Date Filed
    Monday, August 13, 2012
    11 years ago
  • Date Issued
    Tuesday, November 17, 2015
    8 years ago
Abstract
The present invention relates to a sound absorbing sheet having excellent sound absorbing performance and surface decorative effects. The sound absorbing sheet of the present invention is characterized by comprising a base and having an average sound absorption of 0.4 or higher in a frequency range of 200 to 2000 Hz. The permeability and air porosity of a base layer of the sound absorbing sheet of the present invention may be adjusted, thereby achieving significantly superior effects of sound absorbing performance despite the thinness of the sound absorbing sheet.
Description
TECHNICAL FIELD

The present invention relates to glass fiber-based sound absorbing sheets including glass fibers and cellulose fibers as main components, and more particularly, to a glass fiber-based sound absorbing sheet having excellent sound absorption performance through adjustment of air permeability and porosity of a base material.


BACKGROUND ART

Conventionally, various kinds of sound absorbing sheets have been fabricated using polyester air-permeable polymer, glass wool, and the like. Further, Korean Patent Laid-open Publication No. 10-2002-0044600 discloses a technique of fabricating a layer paper for impregnation into a composite floor sheet including cellulose, polyester and PVA as main components. However, these products enhance absorption performance using mechanical properties and air-permeability of materials, thereby causing a complicated fabrication process and limited functions as sound absorbing sheets. Further, when sound absorbing sheets are made thicker in order to resolve these problems, another problem arises in that thick sheets occupy more space and require substantial manufacturing costs.


Therefore, there is a need for a new technique of fabricating sound absorbing sheets having excellent absorption performance through adjustment of mechanical properties.


DISCLOSURE
Technical Problem

An aspect of the present invention is to provide a sound absorbing sheet composed of glass fibers and cellulose fibers and providing excellent sound absorption performance.


Technical Solution

In accordance with an aspect of the present invention, there is provided a sound absorbing sheet including a base material and having a noise reduction coefficient of 0.4 or higher in a frequency range from 200 Hz to 2000 Hz.


Advantageous Effects

The sound absorbing sheet according to the present invention has excellent absorption performance. Further, the sound absorbing sheet is applicable to a base material for sound shielding and absorption materials and systems.





DESCRIPTION OF DRAWINGS


FIGS. 1 to 3 show test results of sound absorption coefficients of sound absorbing sheets fabricated according to conditions of Examples 1 to 3, wherein testing was performed to measure the sound absorption coefficients of the absorbing sheets subjected to normal incidence of sound using a pipe method.



FIGS. 4 to 7 show test results of sound absorption coefficients of sound absorbing sheets fabricated according to conditions of Comparative Examples 1 to 4, wherein testing was performed to measure the sound absorption coefficients of the absorbing sheets subjected to normal incidence of sound using a pipe method.





BEST MODE

The above and other aspects, features, and advantages of the present invention will become apparent from the detailed description of the following embodiments. It should be understood that the present invention is not limited to the following embodiments and may be embodied in different ways, and that the embodiments are provided for complete disclosure and thorough understanding of the present invention by those skilled in the art. The scope of the present invention is defined only by the claims. Like components will be denoted by like reference numerals throughout the specification.


Hereinafter, exemplary embodiments of the present invention will be described in detail.


The present invention provides a sound absorbing sheet which includes a base material and has a noise reduction coefficient of 0.4 or higher in a frequency range from 200 Hz to 2000 Hz. The sound absorption coefficient ranges from 0 to 1. Absorption performance is generally evaluated good as the sound absorption coefficient approaches 1. Since a conventional sound absorption material has a sound absorption coefficient of about 0.3, the sound absorption coefficient of 0.4 or higher is evaluated to have excellent absorption performance. The average sound absorption coefficient is generally defined by averaging sound absorption coefficients based on multiple frequencies. Since the sound absorbing sheet has a noise reduction coefficient of 0.4 or higher, it can be seen that the sound absorbing sheet has excellent absorption performance.


The base material may be composed of glass fibers and cellulose fibers. The glass fiber is fabricated by melting glass mainly containing SiO2, and processing the molten glass into fiber form. Glass fibers are divided into filaments and staples according to fabrication methods and use thereof. The fibers have excellent tensile strength and thermal conductivity as the diameter of the fibers decreases. Generally, glass fibers having a diameter ranging from 5 μm to 20 μm are used for heat retention and sound absorption applications, and glass fibers having a diameter ranging from 40 μm to 150 μm are used for filtering application.


Cellulose fibers generally refer to natural fibers and other fibers using the natural fibers as a fiber source, and include wood fibers, cotton fibers, hemp fibers, Rayon, and the like. The cellulose fibers are generally present in types of fabrics or knits. In addition, the cellulose fibers may also be used together with other synthetic fibers. The synthetic fibers may include polyester or the like. Cellulose fiber-containing textile products formed by mixing synthetic fibers with cellulose fibers are present as mixed yams, mixed fabrics, mixture fabrics, or mixed knits. The base material may contain 30% by weight (wt %) to 60 wt % of glass fibers and 40 wt % to 70 wt % of cellulose fibers. In the present invention, this composition of the glass fibers and the cellulose fibers is preferable in terms of sound absorption performance. Sound absorption performance can be degraded out of the above range.


Specifically, if the content of the glass fibers is less than 30 wt %, non-woven fabrics can be deteriorated in mechanical properties, such as tensile strength, tearing strength, and the like, and if the content of the glass fibers is more than 60 wt %, air permeability can be significantly increased, causing deterioration in absorption performance. In addition, when the content of the cellulose fibers is within the above range, air permeability can be suitably maintained, thereby advantageously realizing excellent absorption performance without deterioration in strength and the like.


Further, the base material may further include synthetic organic fibers. Here, the content of the synthetic organic fibers may range from 2 wt % to 10 wt %. The synthetic organic fibers are formed of a synthetic organic material, which is chemically synthesized from low molecular substances, such as petroleum, coal, limestone, chlorine and the like, instead of natural cellulose or protein, by spinning the synthetic organic fibers into elongated polymeric fibers. Since the base material contains the synthetic organic fiber within the above content range, the base material has flexibility which minimizes damage to the base material when subjected to physical force such as folding or twisting force.


The synthetic organic fiber may include at least one selected from the group consisting of polyester, polyethylene (PE), polypropylene (PP), ethylene-styrene copolymer (ES), cycloolefin, polyethylene terephthalate (PET), polyvinyl alcohol (PVA), ethylene-vinyl-acetate (EVA), polyethylene naphthalate (PEN), polyetheretherketone (PEEK), polycarbonate (PC), polysulfone, polyimide (PI), polyacrylonitrile (PAN), styrene acrylonitrile (SAN), and polyurethane (PU), without being limited thereto.


Preferably, the synthetic organic fiber is composed of polyvinyl alcohol (PVA) or polyethylene terephthalate (PET).


More preferably, the base material include polyvinyl alcohol (PVA), which has at least one unit selected from the group consisting of C1 or more α-olefin units and C1 to C4 alkylvinylether units, in terms of securing flexibility.


Preferably, the base material has a basis weight from 50 g/m2 to 150 g/m2. In the present invention, when the basis weight is less than 50 g/m2, absorption performance can be degraded, and when the basis weight is more than 150 g/m2, manufacturing costs can be considerably increased.


Preferably, the base material has a thickness from 0.1 mm to 0.7 mm When the thickness of the base material is not within this range, non-woven fabrics can exhibit excessively high or low porosity, thereby causing deterioration in absorption performance.


Preferably, the sound absorbing sheet has an air permeability from 100 L/m2/s to 1000 L/m2/s at a pressure of 200 Pa. According to the present invention, when the air permeability at 200 Pa is not within this range, the fabrics can exhibit excessively high or low porosity, thereby causing deterioration in absorption performance.


Preferably, the sound absorbing sheet has an average pore size from 10 μm to 50 μm.


In the present invention, when the average pore size is not within this range, the absorption performance may be degraded.


Next, the present invention will be explained in more detail with reference to some examples. However, it should be understood that these examples are provided for illustration only and are not to be in any way construed as limiting the present invention.


EXAMPLES AND COMPARATIVE EXAMPLES

To prepare test samples, non-woven fabrics were prepared using glass fibers and cellulose fibers under conditions of Table 1.












TABLE 1







Diameter of Fiber
Length of Fiber


















Glass Fibers (90 wt % or more)
 5-20 μm
1-50 mm


Cellulose Fibers (90 wt % or more)
5-100 μm
1-50 mm









Sound absorption sheets of Examples and Comparative Examples were prepared from the non-woven fabrics prepared with the fibers by adjusting thickness, fiber composition, and basis weight thereof (see Tables 2 and 3).













TABLE 2








Fiber Composition (Cellulose




Thickness
Fiber:Glass Fiber:Synthetic
Basis Weight



(mm)
organic fiber) (wt %)
(g/m2)



















Example 1
0.38
55:40:5 (Polyester)
80


Example 2
0.39
60:35:5 (Polypropylene)
90


Example 3
0.36
50:45:5 (Polyvinyl alcohol)
70




















TABLE 3








Fiber Composition (Cellulose




Thickness
Fiber:Glass Fiber:Synthetic
Basis Weight



(mm)
organic fiber) (wt %)
(g/m2)



















Comparative
0.37
15:85:0
50


Example 1


Comparative
0.39
15:85:0
70


Example 2


Comparative
0.38
20:80:0
70


Example 3


Comparative
0.41
30:20:50 (Polyvinyl alcohol)
100


Example 4









Evaluation: Absorption Performance through Adjustment of Air Permeability and Porosity


I. Test method


1. Test method


Pipe method (KS F 2814)


2. Measurement device (Device name: Model name (Manufacturing Company/Country)


Pipe method: HM-02 I/O (Scein/South Korea)


3. Measurement of Temperature/Humidity: (19.4 error range 0.3)° C./(59.4 error range 1.9)% R.H


In the pipe method, a sound absorption coefficient of a sound absorption material is obtained by measuring a standing wave generated when a plane wave propagating in a specific direction is vertically incident. In addition, as a simple method that can be carried out when it is difficult to obtain test samples, a precise size sample is fabricated and repeatedly tested, thereby obtaining test results with minimized error.

NRC=(a250+a500+a1,000+a2,000)/4   <Equation>


aX: sound absorption coefficient of X Hz (X is a numeral)


Here, NRC (Noise Reduction Coefficient) is a single index representing a sound absorption coefficient of a certain material. Since a sound absorption material exhibits different sound absorption coefficients depending upon frequencies, such a single index of NRC is used to express absorption performance of the sound absorption material.


II. Test Results


1. Test Results of Normal Incidence-Noise Reduction Coefficient obtained by Pipe Method (background space 50 mm)


Test results are shown in Tables 4 and 5.











TABLE 4









Frequency (Hz)



















200
250
315
400
500
630
800
1000
1250
1600
2000






















Example 1
.05
.11
.24
.2
.45
.48
.8
.93
.96
.91
.78


Example 2
.05
.09
.15
.25
.38
.49
.75
.92
.98
.95
.8


Example 3
.09
.1
.11
.18
.39
.45
.59
.81
.91
.92
.79


















TABLE 5









Frequency (Hz)



















200
250
315
400
500
630
800
1000
1250
1600
2000






















Com.
.02
.01
.05
.05
.11
.11
.12
.18
.28
.32
.33


Example 1


Com.
.01
.04
.07
.08
.11
.14
.23
.31
.42
.49
.46


Example 2


Com.
.04
.04
.07
.12
.16
.22
.32
.47
.56
.6
.55


Example 3


Com.
.05
.06
.06
.06
.1
.15
.22
.3
.36
.39
.4


Example 4









2. Noise Reduction Coefficient according to Air Permeability and Average Pore Size


Test results of noise reduction coefficients in Examples and Comparative Examples according to air permeability and average pore size are shown in Tables 6 and 7.


As shown in Table 6, it can be seen that, when non-woven fabrics have the same fiber composition as in Examples 1 to 3, the non-woven fabrics had an air permeability ranging from 100 L/m2/s to 1000 L/m2/s at a pressure of 200 Pa and an average pore size ranging from 10 μm to 50 μm, and the sound absorbing sheet has a noise reduction coefficient of 0.4 or more in a frequency range from 200 Hz to 2000 Hz.


As shown in Table 7, it can be seen that, in Comparative Examples 1 to 4, non-woven fabrics had a very high air permeability at 200 Pa that could not be measured, an average pore size above 50 μm, and the sound absorbing sheet has a noise reduction coefficient of less than 0.3.














TABLE 6








Average pore

Noise



Permeability
Size (Capillary Flow
Basis
Reduction



at 200 Pa
Poremeter/Model:
Weight
Coefficient



(L/m2/s)
CFP-1200 AEIL) (μm)
(g/m2)
(NRC)




















Example 1
493
30
80
0.5675


Example 2
470
31
90
0.5475


Example 3
510
39
70
0.5225





















TABLE 7








Average pore

Noise



Permeability
Size (Capillary Flow
Basis
Reduction



at 200 Pa
Poremeter/Model:
Weight
Coefficient



(L/m2/s)
CFP-1200 AEIL) (μm)
(g/m2)
(NRC)




















Com.

51
50
0.1575


Example 1


Com.

51
70
0.23


Example 2


Com.

50
70
0.305


Example 3


Com.

61
100
0.175


Example 4








Claims
  • 1. A sound absorbing sheet comprising a base material, and having a noise reduction coefficient of 0.4 or higher in a frequency range from 200hertz (Hz) to 2000 Hz obtained by Pipe Method (KS F 2814), wherein the base material comprises 30 weight percent (wt %) to 60 wt % glass fibers, 40 wt % to 70 wt % cellulose fibers and 2 wt % to 10 wt % synthetic organic fibers,wherein 90 wt % or more of the cellulose fibers have a diameter from 5 μm to 100 μm and a length from 1 mm to 50 mm,wherein the base material has a thickness from 0.1 mm to 0.7 mm, andwherein the sound absorbing sheet further comprises pores having an average pore diameter size from 10 μm to 50 μm.
  • 2. The sound absorbing sheet according to claim 1, wherein the synthetic organic fibers comprise at least one selected from the group consisting of polyester, polyethylene (PE), polypropylene (PP), ethylene-styrene copolymer (ES), cycloolefin, polyethylene terephthalate (PET), polyvinyl alcohol (PVA), ethylene-vinyl-acetate (EVA), polyethylene naphthalate (PEN), polyetheretherketon (PEEK), polycarbonate (PC), polysulfone, polyimide (PI), polyacrylonitrile (PAN), styrene acrylonitrile (SAN), and polyurethane (PU).
  • 3. The sound absorbing sheet according to claim 2, wherein the polyvinyl alcohol (PVA) has at least one unit selected from the group consisting of C1 or more α-olefin units and C1 to C4 alkylvinylether units.
  • 4. The sound absorbing sheet according to claim 1, wherein the base material has a basis weight from 50 grams per square meter (g/m2) to 150 g/m2.
  • 5. The sound absorbing sheet according to claim 1, wherein the sound absorbing sheet has an air permeability from 100 liters per square meter per second (L/m2/s) to 1000 L/m2/s at a pressure of 200 pascals (Pa).
  • 6. The sound absorbing sheet according to claim 1, wherein the glass fibers have a diameter ranging from 5 μto 20 μm.
Priority Claims (1)
Number Date Country Kind
10-2011-0080338 Aug 2011 KR national
PCT Information
Filing Document Filing Date Country Kind 371c Date
PCT/KR2012/006425 8/13/2012 WO 00 1/15/2014
Publishing Document Publishing Date Country Kind
WO2013/022323 2/14/2013 WO A
US Referenced Citations (6)
Number Name Date Kind
6613424 Putt et al. Sep 2003 B1
8133354 Baig Mar 2012 B2
20040050619 Bargo, II Mar 2004 A1
20040071947 Hwang et al. Apr 2004 A1
20060277996 Kuroda et al. Dec 2006 A1
20080050565 Gross et al. Feb 2008 A1
Foreign Referenced Citations (15)
Number Date Country
10-268871 Oct 1998 JP
11-212579 Aug 1999 JP
2002164690 Jun 2002 JP
2006-524626 Nov 2006 JP
2007-308583 Nov 2007 JP
2008-520849 Jun 2008 JP
2008534812 Aug 2008 JP
2002-0044600 Jun 2002 KR
1020130077893 Jul 2013 KR
02053510 Jul 2002 WO
03057465 Jul 2003 WO
2004024440 Mar 2004 WO
2006107847 Oct 2006 WO
2009067300 May 2009 WO
2009088797 Jul 2009 WO
Non-Patent Literature Citations (4)
Entry
International Search Report for PCT/KR2012/006425 mailed on Oct. 25, 2012.
Extended European Search Report dated Feb. 13, 2015.
Chinese Office Action dated Feb. 25, 2015.
Japanese Office Action dated May 12, 2015 in connection with the counterpart Japanese Patent Application No. 2014-522760.
Related Publications (1)
Number Date Country
20140138182 A1 May 2014 US