Patent Application
20170275429
The present invention relates generally to sizing compositions for glass fibers and, in particular, to sizing compositions for glass fibers suitable to reinforce polyolefin articles, including dicyclopentadiene (DCPD) resins.
The invention relates to a curable composition, a method of manufacturing a molded article of the curable composition, as well as a molded article comprising the composition. The invention in particular relates to a composition comprising a cyclic polyolefin. The composition provides a desirable combination of good workability, high toughness and high heat resistance.
Glass fibers are produced by flowing molten glass via gravity through a multitude of small openings in a precious metal device, called a bushing. Typical formulations of glass fibers are disclosed in K. Loewenstein, The Manufacturing Technology of Continuous Glass Fibres, (3d Ed. 1993).
After the fibers have cooled very shortly after their issuance from the bushing and usually in close proximity to the bushing, these fibers are treated with a chemical treating formulation usually referred to in the art as a sizing composition, sizing, or size. The sizing composition serves to make the fibers more compatible with the material they will ultimately be used to reinforce and to make the fibers easier to process. The sizing composition can be applied by sprayers, rollers, belts, metering devices or any similar application device. The sized glass fibers are gathered into bundles or strands comprising a plurality of individual fibers, generally from 200 to more than 4000.
After their formation and treatment, the strands can be wound into a spool or “forming package” and/or may be chopped. The forming packages or chopped strands are usually dried in either an oven or at room temperature to remove some of the moisture from the fibers. Strands from the forming packages may also be wound into rovings.
The strands of treated fibers can be used to reinforce various materials such as thermoplastic polymers and thermosetting polymers. One example of a commercially important use of treated fibers is to reinforce olefinic thermosetting polymers, especially polymers of cycloolefins. It would be desirable to have commercial fiber glass materials that are effective reinforcements for cycloolefinic resins that cure by the ring-opening metathesis polymerization (“ROMP”) reaction. In particular, it would be desirable to have commercial fiber glass materials that are effective reinforcements for polymers formed from dicyclopentadiene (“DCPD”) monomer.
There is a growing need for an effective fiber glass reinforcement for DCPD resins. These resins have a number of advantages over more conventional thermoset resins, especially the widely used polyester resins that have styrene as a co-monomer and diluent. In addition, DCPD resins may provide unique toughness and corrosion properties as compared to conventional thermoset resins.
Polymer matrix composites offer good mechanical and physical properties at relatively low weight. Composites may be based on either thermosetting or thermoplastic polymer matrix materials in which reinforcing fibers are embedded. The properties of composites are controlled by those of the fibers and the polymer matrix, whereby the interfacial region between the reinforcing fibres and the polymer matrix plays a special role. Indeed, a sufficient interface bonding between the reinforcing fibres and the polymer matrix to ensure adequate load transfer from the polymer matrix to the fibers is generally required for making effective use of the reinforcing fiber properties.
Composite properties, in particular toughness, are not easily predictable on the basis of constituent properties, and good properties of a polymer matrix material may not translate into good properties of the composite.
The present invention relates to sizing compositions, to glass fibers at least partially coated with such sizing compositions, to a variety of fiber glass products at least partially coated with such sizing compositions, and to composites formed from cycloolefins and reinforced with glass fibers at least partially coated with sizing compositions of the present invention. The present invention also relates to methods of forming fiber glass strands and methods of forming polyolefin composites.
Fiber glass strands at least partially coated with sizing compositions of the present invention may impart desirable or improved strength when used to reinforce polyolefin articles, such as cycloolefins that cure by ring opening metathesis polymerization. Sizing compositions of the present invention, in some embodiments, are believed to improve the adhesion between a fiber glass reinforcement coated with the sizing composition and the polyolefin resin. In addition, because a ROMP catalyst is often used to cure cycloolefins, the sizing compositions of the present invention are also adapted to not poison the ROMP catalysts.
In one embodiment of the present invention, a sizing composition for glass fibers comprises a film-former comprising a polymer, wherein the repeating unit of the polymer comprises at least four carbon atoms and at least one carbon-carbon double bond, and a silane. In one non-limiting embodiment, the at least one carbon-carbon double bond is in the backbone chain of the polymer.
In some embodiments, the film-former comprises a polymer, wherein the repeating unit of the polymer comprises four to six carbon atoms and one carbon-carbon double bond. In other embodiments, the film-former comprises at least one of polybutadiene, polypentadiene, and polyhexadiene. In some embodiments, one or more repeating units in the polymer comprises at least one pendant group. In some embodiments, the one or more pendant groups comprise at least one vinyl group. The one or more pendant groups in some embodiments comprise at least one cyclic pendant group. In some embodiments, the one or more pendant groups include others disclosed herein as well as combinations thereof.
The film-former, in some embodiments, comprises at least about 60 weight percent of the sizing composition on a total solids basis (e.g., up to about 90 weight percent of the sizing composition on a total solids basis). In some embodiments, the film-former comprises between about 70 and about 85 weight percent of the sizing composition on a total solids basis. In other embodiments, the film-former comprises at least about 20 weight percent of the sizing composition on a total solids basis.
Non-limiting embodiments of the present invention may also comprise a second film-former. In some embodiments, the second film-former can be present in an amount of at least 20 weight percent on a total solids basis. In some such embodiments, the film-former comprising a polymer, wherein the repeating unit of the polymer comprises at least four carbon atoms and at least one carbon-carbon double bond, can be present in an amount of at least about 20 weight percent of the sizing composition on a total solids basis, and the second film-former comprises at least about 20 weight percent of the sizing composition on a total solids basis. The second film-former, in some embodiments, comprises paraffin wax and polymers or copolymers of propylene, ethylene, isobutylene, styrene, maleic anhydride, acrylate, or combinations thereof.
In one non-limiting embodiment, the film-former comprises polybutadiene. In these embodiments, the sizing composition may comprise at least about 60 weight percent polybutadiene on a total solids basis (e.g., up to about 90 weight percent polybutadiene on a total solids basis). In some embodiments, the sizing composition comprises between about 70 and about 85 weight percent polybutadiene on a total solids basis. The polybutadiene, in some embodiments, has a number average molecular mass of less than 20,000. In other embodiments, the polybutadiene has a number average molecular mass of less than 10,000. In some embodiments, the sizing composition comprises at least about 20 weight percent polybutadiene on a total solids basis. In some embodiments comprising at least about 20 weight percent polybutadiene, the sizing compositions may further comprise a second film-former in an amount of at least about 20 weight percent on a total solids basis. The second film-former, in some embodiments, comprises paraffin wax and polymers or copolymers of propylene, ethylene, isobutylene, styrene, maleic anhydride, acrylate, or combinations thereof.
Silanes that can be used in various embodiments of the present invention include, silanes that comprise a terminal vinyl group including, for example, a vinylbenzyl group, a methacryloxypropyltrialkoxysilane, and combinations thereof. In some embodiments, the silane may comprise at least about 2 weight percent of the sizing composition on a total solids basis. In some embodiments, the silane may comprise at least about 5 weight percent of the sizing composition on a total solids basis. In other embodiments, the silane may comprise up to about 25 weight percent of the sizing composition on a total solids basis. The silane may comprise between about 5 and about 25 weight percent of the sizing composition in some embodiments. In a further embodiment, the silane may comprise between about 10 and about 20 weight percent of the sizing composition on a total solids basis.
Non-limiting embodiments of the present invention may also comprise an antioxidant and/or a surfactant. In some embodiments, the surfactant comprises less than about 10 weight percent of the sizing composition on a total solids basis.
In some embodiments, the sizing composition is an aqueous sizing composition.
Another embodiment of a sizing composition for glass fibers of the present invention comprises a film-former comprising a polymer, wherein the repeating unit of the polymer comprises four to six carbon atoms and one carbon-carbon double bond, in an amount between about 60 and about 90 weight percent on a total solids basis; and a silane comprising a terminal vinyl group in an amount between about 5 and about 25 weight percent on a total solids basis.
A further embodiment of a sizing composition for glass fibers of the present invention consists essentially of a film-former comprising a polymer, wherein the repeating unit of the polymer comprises four to six carbon atoms and one carbon-carbon double bond; a silane comprising a terminal vinyl group; and one or more surfactants.
The present invention also relates to fiber glass strands comprising at least one glass fiber at least partially coated with any of the sizing compositions of the present invention.
The present invention also relates to polyolefin composites. In one embodiment, a polyolefin composite of the present invention comprises: (a) a plurality of glass fibers at least partially coated with any of the sizing compositions of the present invention; and (b) a polyolefin prepared by polymerizing a cycloolefin using a ring-opening metathesis polymerization catalyst. The polyolefin, in one non-limiting embodiment, may comprise polymers formed by polymerizing dicyclopentadiene.
It is an aim of the present invention to provide a composition having a desirable combination of good workability, high toughness and high heat resistance. It is a further aim to provide a composition that when used as a polymer matrix material in a composite retains the desirable combination of properties. It is a further aim to provide a cyclic polyolefin composition having the above described advantages.
This and other aims are provided by a curable composition, comprising (A) a cyclic olefin; (B) a metathesis catalyst for polymerizing the cyclic olefin; (C) 0.1-30 wt. % of a compound comprising at least one vinyl group; and (D) 0.1-10 wt. % of a curing agent for compound (C), wherein the wt. % are relative to the total weight of the composition.
In an embodiment of the invention, compound (C) has a Hildebrandt solubility parameter δT comprised between 15.4 and 19.8 MPa1/2. The Hildebrandt solubility parameters are calculated based on the three parameter system developed by Charles M. Hansen:
δT=δD2+δP2+δH2
wherein:
δT=Total Hildebrand parameter
δD=dispersion components
δP=polar component
δH=hydrogen bonding component
Calculations are performed by using HSPiP software, which can be found at http://hansen-solubility.com.
In an embodiment of the invention, a composition is provided comprising 3-20 wt. % of the compound (C), more preferably 3-15 wt. % of the compound (C), and most preferably 4-12 wt. % of the compound (C).
Yet another embodiment relates to a composition wherein compound (C) comprises a (meth)acrylate compound.
Another embodiment of the invention provides a composition comprising 0.01-8 wt. % of the curing agent, more preferably 0.1-7 wt. % of the curing agent, even more preferably 0.2-1 wt. % of the curing agent, and most preferably 0.2-0.8 wt. % of the curing agent.
In yet another embodiment of the invention a composition is provided wherein the curing agent comprises a radical initiator.
Another embodiment of the invention relates to a composition wherein the radical initiator comprises a non-cyclic peroxide.
A further embodiment according to the invention provides a composition wherein the at least one cyclic olefin comprises a dicyclopentadiene.
Yet another embodiment of the invention provides a composition comprising reinforcing fibers provided with a sizing composition.
The sizing composition comprises at least a coupling agent and a film former. A useful embodiment of the invention provides a curable composition wherein a film former of the sizing composition has a Hildebrandt solubility parameter δT comprised between 15.9 and 19.9 MPa1/2.
In another embodiment of the invention, the film former in the sizing composition comprises a (co)polymer of monomer units having from four to six carbon atoms and one carbon-carbon double bond, more preferably a polybutadiene.
Yet another embodiment of the invention provides a sizing composition wherein a film former comprises paraffin wax. It is also possible to provide the sizing compositions with more than one film former, a combination of polybutadiene and paraffin wax being a preferred embodiment.
Still another embodiment in accordance with the invention offers a composition wherein the coupling agent comprises a silane compound having unsaturations.
The invention also relates to a method of manufacturing a molded article of the invented composition, the method comprising:
A further embodiment of the method comprises the additional steps of:
Yet another embodiment relates to a method comprising the step of injecting the composition into a closed mold, preferably by providing the mold with reinforcing fibers prior to injecting the composition.
In another embodiment of the method, the conditions comprise heating at a temperature of between 120° C.-150° C. during at most 60 minutes. Such an embodiment of the method surprisingly yields a polymerized composition having a glass transition temperature above 180° C., notwithstanding the relatively low curing temperature range and duration.
The invention in another aspect relates to a molded article comprising a composition in accordance with the invention. In a particular embodiment a molded article of a composite material is provided, wherein the composite material comprises (a) a matrix polymer prepared by polymerizing the curable composition in accordance with any one embodiment thereof; and (b) reinforcing fibers in accordance with any one embodiment thereof, as disclosed in the present application.
The invention in an embodiment further relates to a molded composite article wherein the matrix polymer has a volatile content of less than 5 wt. %, more preferably less than 3 wt. % and most preferably less than 2 wt. % relative to the total weight of the matrix polymer. The relatively low volatile content of a polymerized composition in accordance with the invention offers environmental and other advantages. Volatiles may for instance be due to unreacted monomers or oligomers, originating from the curable composition components and/or sizing composition components. Volatile content is conveniently determined by subjecting a molded article to a temperature of 200° C. in a nitrogen environment and determining weight loss after a ½ hour period.
The invention further relates to a molded composite article obtainable by the method of the invention, wherein the composite material properties at least satisfy one of:
In more preferred embodiments, the composite material properties at least satisfy two, and most preferably three of the listed properties.
These and other embodiments of the present invention are described in greater detail in that follows.
For the purposes of this specification, unless otherwise indicated, all numbers expressing quantities of ingredients, reaction conditions, and so forth used in the specification are to be understood as being modified in all instances by the term “about.” Accordingly, unless indicated to the contrary, the numerical parameters set forth in the following specification are approximations that can vary depending upon the desired properties sought to be obtained by the present invention. At the very least, and not as an attempt to limit the application of the doctrine of equivalents to the scope of the claims, each numerical parameter should at least be construed in light of the number of reported significant digits and by applying ordinary rounding techniques.
Notwithstanding that the numerical ranges and parameters setting forth the broad scope of the invention are approximations, the numerical values set forth in the specific examples are reported as precisely as possible. Any numerical value, however, inherently contains certain errors necessarily resulting from the standard deviation found in their respective testing measurements. Moreover, all ranges disclosed herein are to be understood to encompass any and all subranges subsumed therein. For example, a stated range of “1 to 10” should be considered to include any and all subranges between (and inclusive of) the minimum value of 1 and the maximum value of 10; that is, all subranges beginning with a minimum value of 1 or more, e.g. 1 to 6.1, and ending with a maximum value of 10 or less, e.g., 5.5 to 10. Additionally, any reference referred to as being “incorporated herein” is to be understood as being incorporated in its entirety.
It is further noted that, as used in this specification, the singular forms “a,” “an,” and “the” include plural referents unless expressly and unequivocally limited to one referent.
In some embodiments, the present invention relates to sizing compositions for coating materials used to reinforce composites. While a number of reinforcing materials may be used to reinforce composites, including, for example, polyester fibers, polyolefin fibers, and polyamide fibers, embodiments of sizing compositions of the present invention are particularly suitable for use in coating glass fibers.
Embodiments of the present invention are directed to sizing compositions for glass fibers. The sizing compositions in non-limiting embodiments of the present invention are useful in coating glass fibers to be used as reinforcement for cycloolefins that cure by the ring-opening metathesis polymerization (“ROMP”) reaction. The polymerization of cycloolefins via ROMP reactions usually requires the presence of a ROMP catalyst to cure the composite. Examples of ROMP catalysts for polymerization of cycloolefins include, for example, ruthenium, osmium, and molybdenum metal carbene catalysts as known to those of skill in the art.
In non-limiting embodiments, the sizing compositions of the present invention are useful with fiber glass reinforcements in dicyclopentadiene (“DCPD”) resins. While sizing compositions are primarily discussed herein in connection with their use on fiber glass reinforcements for reinforcing DCPD resins, it should be understood that the sizing compositions may also be used to at least partially coat glass fibers for reinforcing other cycloolefins that can be polymerized by a ring opening metathesis polymerization reaction, including those reactions set forth in U.S. Pat. No. 6,436,476 and U.S. Pat. No. 6,323,296, which are hereby incorporated by reference. The sizing compositions may also be useful with fiber glass products used to reinforce other unsaturated, free radical cure resins that do not necessarily cure by ROMP, such as polyester.
The general reaction mechanism for polymerization of DCPD using ROMP is as follows:
One difficulty in producing compatible and effective fiber glass for use as reinforcement with polymers formed from DCPD is that the various ingredients typically used in fiber glass sizing compositions may inhibit polymerization by “poisoning” the ROMP catalyst. As used herein, the term “poisoning”, when used in connection with a sizing composition or components of a sizing composition, refers to a sizing composition or a component thereof that negatively affects the polymerization of a cycloolefin by, for example, inhibiting, slowing, preventing, or terminating the desired polymerization process. For example, a component of a sizing composition may react with the ROMP catalyst to produce a species that is not a catalyst, and thereby prevent the ROMP catalyst from polymerizing the monomer. Consequently, there have been continuing efforts by catalyst suppliers to reduce the sensitivity of the ROMP catalyst chemistry to sizing components. It would be desirable to have a sizing composition that would not limit curing of the DCPD, while still producing composites with an acceptable shear strength.
The present invention advantageously provides sizing compositions that are compatible with ROMP catalysts, such that the sizing compositions do not substantially inhibit polymerization by poisoning the ROMP catalyst. The sizing compositions of the present invention, when at least partially coated on glass fibers used to reinforce polymerized cycloolefins, also provide composites having adequate or desirable shear strengths in some embodiments. The selection of components and their relative amounts can provide such features and others.
In one non-limiting embodiment, a sizing composition of the present invention comprises at least one film-former comprising a polymer, wherein the repeating unit of the polymer comprises at least four carbon atoms and at least one carbon-carbon double bond, and at least one silane.
Film-formers useful in non-limiting embodiments of the present invention have relatively low potentials for poisoning the ROMP catalyst used to polymerize cycloolefinic resins. In some embodiments, film-formers useful in non-limiting embodiments of the present invention may be free from (i.e., may not include) primary amines, thiols, terminal epoxides, functional groups having active oxygen groups (e.g., hydroperoxides and activated epoxides), acetylenes, and vinyl ethers. To avoid poisoning ROMP catalysts, film-formers useful in non-limiting embodiments of the present invention may be substantially free from, or may only include in a limited way (i.e., less than 1 weight percent, less than 0.5 weight percent, less than 0.1 weight percent, less than 0.05 weight percent, or less than 0.01 weight percent by weight), the following functional groups: primary amines, thiols, terminal epoxides, functional groups having active oxygen groups (e.g., hydroperoxides and activated epoxides), acetylenes, and vinyl ethers. Such structures are believed to poison and/or adversely affect the operation of the ROMP catalyst. As noted below, silanes used in embodiments of the present invention may also not include these functional groups. Certain constituents that can act as Lewis bases may also not be desirable for use as a film-former in embodiments of the present invention. Film-formers useful in embodiments of the present invention can also assist in holding fiber glass filaments together to form a strand that can be wet out by liquid resins.
The film-formers, in some embodiments, comprise a polymer that includes at least one carbon-carbon double bond in the backbone chain of the polymer. In some embodiments, the repeating unit (i.e., the monomeric unit) of the polymer comprises four to six carbon atoms and one carbon-carbon double bond. The film-formers, in some embodiments, can comprise at least one of polybutadiene, polypentadiene, and polyhexadiene. Other common film-formers that would not poison the ROMP catalyst (e.g., by reacting with the ROMP catalyst to form a non-catalytic species) can also be used as additional film-formers in some embodiments.
In some embodiments, the backbone chain of the polymer can include the following polybutadiene repeating unit comprising four carbon atoms and one carbon-carbon double bond, according to one of the structures shown below:
(—CR1R2—CR3═CR4—CR5R6—)n;
(—CR1═CR2—CR3R4—CR5R6—)n; or
(—CR1R2—CR3R4—CR5═CR6—)n.
In the polybutadiene repeating unit, “n” is an integer greater than 1. In some embodiments, “n” is an integer from 20 to 400. Also in the polybutadiene repeating unit, R1, R2, R3, R4, R5, and R6 are each independently hydrogen, an aliphatic moiety, a heteroaliphatic moiety, a carbocyclic moiety, or a heterocyclic moiety. In some embodiments, each of R1-R6 is hydrogen. In some embodiments, one or more of R1, R2, R3, R4, R5, and R6 can be a pendant group or a linking molecule that connects the backbone to a pendant group. Optionally, the polybutadiene repeating unit has a trans configuration.
Optionally, one or more groups can be pendant from the backbone chain of the polymer. In some embodiments, one or more pendant groups can be attached to one or more of the repeating units. For example, for a polymer with 100 repeating units (i.e., n is 100), pendant groups could be attached to from 0 to 100 of the units. In other words, the percentage of pendant group-containing repeating units in the polymer can be 100% or less (e.g., 90% or less, 80% or less, 70% or less, 60% or less, 50% or less, 40% or less, 30% or less, 20% or less, 10% or less, 5% or less, or 1% or less), based on the total number of repeating units in the polymer. In some embodiments, one or more of R1, R2, R3, R4, R5, and R6 can include a pendant group. In other embodiments, two R groups on adjacent carbons (e.g., R1 and R3, R3 and R4, or R4 and R5) can combine together, forming a carbocyclic moiety or a heterocyclic moiety. In some non-limiting embodiments, the pendant group can include a vinyl group. In other non-limiting embodiments, the pendant group can include a cyclic group, such as a cyclopentene group. In some non-limiting embodiments, the pendant group can include maleic anhydride. Different pendant groups can be present in the polymer in varying amounts. For example, for a polymer with 100 repeating units (i.e., n is 100), a vinyl pendant group can be attached to from 15-25% of the repeating units in the polymer and the remainder of the repeating units in the polymer can be unmodified (i.e., no pendant groups attached). In another embodiment, for a polymer with 100 repeating units (i.e., n is 100), a vinyl pendant group can be attached to from 40-55% of the repeating units in the polymer, a cyclic pendant group can be attached to from 15-20% of the repeating units in the polymer, and the remainder of the repeating units in the polymer can be unmodified (i.e., no pendant groups attached). In one non-limiting embodiment, the at least one film-former may be a functionalized polymer, such as a maleic anhydride functionalized polymer. For example, the at least one film-former may be a maleic anhydride functionalized polybutadiene. The maleic anhydride functionalized polymers can be prepared by reacting maleic anhydride with a carbon-carbon double bond of the backbone chain of the polymer under thermal conditions to form a maleic anhydride adduct.
In one non-limiting embodiment, the at least one film-former comprises a polybutadiene having a number average molecular mass of less than 20,000. For example, the polybutadiene can have a number average molecular mass of 17,500 or less; 15,000 or less; 12,500 or less; 10,000 or less; 7,500 or less; 5,000 or less; or 3,000 or less in various embodiments.
Examples of suitable polybutadienes useful as film-formers in a non-limiting embodiment of the present invention include functionalized and non-functionalized polybutadienes, such as those polybutadienes commercially available from Synthomer, Inc. (Harlow, United Kingdom), under the Lithene product name. For example, suitable non-functional polybutadienes include, without limitation, Lithene Ultra AL, a polybutadiene having a number average molecular mass of 1,000 and containing vinyl and cyclic pendant groups; Lithene Ultra AH, a polybutadiene having a number average molecular mass of 1,800 and containing vinyl and cyclic pendant groups; Lithene Ultra PH, a polybutadiene having a number average molecular mass of 2,600 and containing vinyl pendant groups; Lithene Ultra PM4, a polybutadiene having a number average molecular mass of 1,500 and containing vinyl pendant groups; Lithene Ultra P4-25P, a polybutadiene having a number average molecular mass of 2,600 and containing vinyl pendant groups; Lithene Ultra P4-150P, a polybutadiene having a number average molecular mass of 3,200 and containing vinyl pendant groups; Lithene Ultra N4-5000, a polybutadiene having a number average molecular mass of 5,000 and containing vinyl pendant groups; and Lithene Ultra N4-9000, a polybutadiene having a number average molecular mass of 9,000 and containing vinyl pendant groups.
Suitable functionalized polybutadienes include maleic acid functionalized polybutadienes, such as Lithene Ultra AL-15MA, a maleic acid functionalized polybutadiene having a number average molecular mass of 1,300; Lithene Ultra PM4-7.5MA, a maleic acid functionalized polybutadiene having a number average molecular mass of 1,600; Lithene Ultra N4-5000-15MA, a maleic acid functionalized polybutadiene having a number average molecular mass of 5,750; Lithene Ultra N4-B-10MA, a maleic acid functionalized polybutadiene having a number average molecular mass of 8,200; and Lithene Ultra N4-9000-10MA, a maleic acid functionalized polybutadiene having a number average molecular mass of 9,500.
In another non-limiting embodiment, the at least one film-former may comprise a copolymer. For example, the at least one film-former may comprise a copolymer formed from a first monomer unit and one or more additional monomer units. The first monomer unit may comprise at least four carbon atoms (e.g., from four to six carbon atoms). The one or more additional monomer units may be any copolymerizable monomer, as known to those of skill in the art. For example, the one or more additional monomer units may include vinylaromatic monomer units (e.g., styrene), acrylate monomer units, methacrylate monomer units, acrylonitrile monomer units, and/or olefin monomer units.
Optionally, the at least one film-former may comprise a styrene-butadiene copolymer. An example of a styrene-butadiene copolymer useful as a film-former in a non-limiting embodiment of the present invention comprises Plextol X-9110, commercially available from PolymerLatex GmbH. of Marl, Germany.
Optionally, the at least one film-former may comprise a styrene-acrylate copolymer. An example of a styrene-acrylate copolymer useful as a film-former in a non-limiting embodiment of the present invention comprises Plextol X-4020 and Plextol X-4545, both commercially available from PolymerLatex GmbH. of Marl, Germany.
The sizing composition can include one film former in some embodiments, or multiple film-formers in others. The one or more film-formers are generally present in the sizing composition in an amount of at least 60 weight percent, the percentages based on the total solids of the sizing composition. Optionally, the one or more film-formers are present in the sizing composition in an amount of at least 65 weight percent, at least 70 weight percent, at least 75 weight percent, at least 80 weight percent, or at least 85 weight percent in other embodiments. The one or more film-formers are present in the sizing composition in an amount of up to about 90 weight percent, the percentages based on the total solids of the sizing composition in some embodiments. In some embodiments, the one or more film-formers are present in the sizing composition in an amount of between about 70 and about 85 weight percent.
In some non-limiting embodiments, the sizing composition includes a first film-former and a second film-former, wherein the first film-former comprises a polymer, wherein the repeating unit of the polymer comprises at least four carbon atoms and at least one carbon-carbon double bond (including, for example, any such polymers described above). In one non-limiting embodiment, the first film-former comprises at least about 20 weight percent of the sizing composition on a total solids basis. Optionally, the first film-former can comprise at least about 25 weight percent, at least 30 weight percent, at least 35 weight percent, at least 40 weight percent, or at least 45 weight percent of the sizing composition on a total solids basis in various embodiments.
Suitable second (and other additional) film-formers include, for example, a non-reactive polymer. In some embodiments, the second film-former can include paraffin wax and polymers or copolymers of propylene, ethylene, isobutylene (e.g., polyisobutylene), styrene (e.g., polystyrene), maleic anhydride, acrylate (e.g., polymethylmethacrylate), or combinations thereof. Examples of suitable second film-formers in a non-limiting embodiment of the present invention comprise MichemLub 723, a paraffin wax dispersion commercially available from Michelman, Inc. of Cincinnati, Ohio; Aquacer 1605, a polypropylene dispersion commercially available from Byk of Wesel, Germany; Novacer 1200, a polyethylene dispersion commercially available from Byk; and ML 93135, a polyethylene dispersion commercially available from Michelman, Inc. The second (or additional) film-formers can be present in the sizing composition in an amount of less than about 50 weight percent (e.g., less than about 45 weight percent, less than about 40 weight percent, less than about 30 weight percent, less than about 25 weight percent, or less than about 20 weight percent) on a total solids basis. In some embodiments, a first film-former comprising polybutadiene is present in an amount of at least about 20 weight percent of the sizing composition on a total solids basis and a second film-former comprising paraffin wax is present in an amount of at least about 10 weight percent of the sizing composition on a total solids basis. In other embodiments, a first film-former comprising polybutadiene is present in an amount of at least about 50 weight percent of the sizing composition on a total solids basis and a second film-former comprising paraffin wax is present in an amount of at less than about 45 weight percent of the sizing composition on a total solids basis. In some embodiments, a first film-former comprising polybutadiene is present in an amount of at least about 50 weight percent of the sizing composition on a total solids basis and a second film-former comprising paraffin wax is present in an amount of at less than about 30 weight percent of the sizing composition on a total solids basis. A first film-former comprising polybutadiene is present in an amount of at least about 50 weight percent of the sizing composition on a total solids basis and a second film-former comprising paraffin wax is present in an amount of at less than about 20 weight percent of the sizing composition on a total solids basis in some embodiments.
Sizing compositions of the present invention further comprise one or more silanes. The one or more silanes are capable of reacting or otherwise interacting with cyclic olefinic resins, such as dicyclopentadiene (“DCPD”), during cure. Silanes that are capable of reacting with DCPD, in some non-limiting embodiments, can participate in the polymerization and cross-linking mechanism of the DCPD resin. The silanes can have a relatively low potential to poison the ROMP catalyst. The one or more silanes are also capable of reacting or otherwise interacting with the film-former, such as the polybutadiene film-former described herein.
In some non-limiting embodiments, silanes useful in the sizings of the present invention comprise a terminal vinyl group. As understood to those of skill in the art, a “terminal” vinyl group means that the double bond occurs at the end of the hydrocarbon radical opposite from the end bonded to the silicone atom in the silane.
In some embodiments, suitable silanes comprising a terminal vinyl group can include silanes comprising a vinylbenzyl group. An example of a commercially available silane comprising a vinylbenzyl group is DYNASYLAN® 1172 N-2-(vinylbenzylamino)-ethyl-3-aminopropyltrimethoxysilane from Degussa AG of Dusseldorf, Germany, which has the following structure:
Another example of a commercially available silane comprising a vinylbenzyl group is DYNASYLAN® 1175 from Degussa AG of Dusseldorf, Germany, which is believed to have the same structure as DYNASYLAN® 1172. Another example of a commercially available silane comprising a vinylbenzyl group is Z-6032 N-2-(vinylbenzylamino)-ethyl-3-aminopropyltrimethoxysilane from Dow Corning. DYNASYLAN 1172 is provided in acetic acid while DYNASYLAN 1175 and Z-6032 are provided in hydrochloric acid. Another example of a commercially available silane comprising a vinylbenzyl group is KBM-974, which is a [3-[[2-[(vinylbenzyl)amino]ethyl]amino]propyl]trimethoxysilane commercially available from Shin-Etsu Chemical Co., Ltd. of Tokyo, Japan.
In some non-limiting embodiments, silanes useful in the sizings of the present invention comprise shorter chain silanes having terminal vinyl groups that may provide less adhesion between the fiber flass reinforcement and the polyolefin. Examples of suitable silanes include, for example, vinyltrialkoxysilanes. In some embodiments, a suitable vinyltrialkoxysilane includes Silquest A-151, a vinyltriethoxysilane commercially available from Momentive Performance Materials, Inc. (Columbus, Ohio). A further example of a suitable silane, in some embodiments, includes methacryloxypropyltrialkoxy silanes such as 3-methacryloxypropyltrialkoxysilane, commercially available as Silquest A-174 from Momentive Performance Materials, Inc. (Columbus, Ohio).
In another non-limiting embodiment, a silane useful in a sizing of the present invention comprises a norbornenyl-functional silane. Norbornenyl-functional silanes useful in the present invention may include, for example, norbornenyl trimethoxysilanes and norbornenyl triethoxysilanes having four or more carbon atoms in a chain between the silicon atom and the norbornenyl group.
Other potentially useful silanes may include carbons in the chain having functional groups attached, although any such functionality would preferably not poison the ROMP catalyst. Examples of undesirable functional groups are set forth above in connection with the film-former. Such undesirable functional groups may, for example include: primary amines, thiols, terminal epoxides, hydroperoxides, activated epoxides, acetylenes, and vinyl ethers.
The at least one silane can generally be present in the sizing composition in an amount from at least about 5 weight percent up to about 25 weight percent, the percentages based on the total solids of the sizing composition. The at least one silane, in a further non-limiting embodiment, may be present in an amount from 5 weight percent to 15 weight percent or from 10 weight percent to 20 weight percent, the percentages based on the total solids of the sizing composition.
Embodiments of sizing compositions of the present invention may comprise multiple silanes as described herein. In these embodiments, at least one of the silanes is capable of reacting with cyclic olefinic resins, such as dicyclopentadiene (“DCPD”), during cure. When multiple silanes are used, each silane can have a low potential to poison the ROMP catalyst (e.g., react with the ROMP catalyst to produce a species that is not a catalyst). The potential to avoid poisoning the ROMP catalyst can be avoided by not using silanes that include, for example, the following functional groups: primary amines, thiols, terminal epoxides, hydroperoxides, activated epoxides, acetylenes, and vinyl ethers.
Depending on the particular film-former used, one or more emulsifying agents or surfactants may be used to assist in dispersing the film-former in water or an aqueous solution. Emulsifying agents can also assist in emulsifying or dispersing other components of the sizing compositions in some embodiments. For example, when the film-former comprises a polymer, wherein the repeating unit of the polymer comprises at least four carbon atoms and at least one carbon-carbon double bond (including, for example, any such polymers described above), it may be beneficial to utilize one more emulsifying agents or surfactants to assist in dispersing the polymer in an aqueous sizing composition.
Non-limiting examples of suitable emulsifying agents can include polyoxyalkylene block copolymers, ethoxylated alkyl phenols, polyoxyethylene octylphenyl glycol ethers, ethylene oxide derivatives of sorbitol esters, polyoxyethylated vegetable oils, ethoxylated alkylphenols, and nonylphenol surfactants. Examples of commercially available emulsifying agents useful in embodiments of the present invention can include Pluronic F-108, which is a polyoxyalkylene block copolymer and which is commercially available from BASF Corp. (Florham Park, N.J.); Alkamuls EL-719, which is an ethoxylated castor oil and which is commercially available from Rhodia (Courbevoie, France); Genapol UD 050 from Clariant Corporation of Mt. Holly, N.C.; and Lutensol OP-10, which is an octylphenol ethoxylate and which is commercially available from BASF Corp.
As indicated above, embodiments of the present invention can utilize one or more emulsifying agents or surfactants. Multiple emulsifying agents can be used in some embodiments to assist in providing a more stable emulsion. Multiple emulsifying agents can be used in amounts effective to disperse hydrophobic components, such as certain film-formers, in water or an aqueous solution. For example, when the film-former comprises a polymer, wherein the repeating unit of the polymer comprises at least four carbon atoms and at least one carbon-carbon double bond (including, for example, any such polymers described above), it may be beneficial to utilize multiple emulsifying agents or surfactants to assist in dispersing the polymer in an aqueous sizing composition. In some non-limiting embodiments of sizing compositions that include one or more emulsifying agents or surfactants, the total amount of emulsifying agents or surfactants can comprise up to 20 weight percent of the sizing composition based on total solids. In other non-limiting embodiments, the total amount of emulsifying agents can comprise up to 17 weight percent of the sizing composition based on total solids. In other non-limiting embodiments, the total amount of emulsifying agents can comprise up to 16 weight percent of the sizing composition based on total solids. In some embodiments, the total amount of emulsifying agents can comprise 10 or more weight percent of the sizing composition based on total solids. The total amount of emulsifying agents, in some embodiments, can comprise between 10 and 20 weight percent of the sizing composition based on total solids.
In some non-limiting embodiments, sizing compositions of the present invention may further include one or more antioxidants. One or more antioxidants can be used in some embodiments to prevent oxidative drying of film-formers in dried products. The one or more antioxidants can also be useful in suppressing skin formation and discoloration of certain film-formers, such as polybutadiene and similar film-formers. Non-limiting examples of suitable antioxidants can include sterically hindered phenols, hindered amine light stabilizers (HALS), and phosphites. Examples of commercially available antioxidants useful in embodiments of the present invention can include butylated hydroxytoluene (BHT); sodium hypophosphite; N,N′-diphenyl-p-phenylenediamine (DPPD), commercially available from Westco (Western Reserve Chemical Corporation, Stow, Ohio); ethylenebis(oxyethylene) bis[3-(5-tert-butyl-4-hydroxy-m-tolyl)propionate], commercially available as Irganox 245 from BASF; 4,6-bis (octylthiomethyl)-o-cresol, commercially available as Irganox 1520 from BASF; 4,6-bis(dodecylthiomethyl)-o-cresol, commercially available as Irganox 1726 from BASF; Octadecyl-3-(3,5-di-tert.butyl-4-hydroxyphenyl)-propionate, commercially available as Irganox 1076 from BASF; Irgastab PVC 76, a heat stabilizer commercially available from BASF; tris(2,4-ditert-butylphenyl)phosphite, commercially available as Irgafos 168 from BASF; Tinuvin 765, a liquid hindered amine light stabilizer commercially available from BASF; Aquanox TD, a water-based antioxidant commercially available from Aquaspersions Ltd. (Halifax, United Kingdom); and Chimasorb 119, a hindered amine light stabilizer commercially available from Sabo S.p.A. (Levate, Italy). Non-limiting examples of phosphites that can be used in some embodiments of the present invention also include those disclosed in U.S. Pat. No. 6,207,737, which is hereby incorporated by reference.
The one or more antioxidants can generally be present in the sizing composition in an amount of up to about 10 weight percent based on the total solids of the sizing composition. The one or more antioxidants, in a further non-limiting embodiment, may be present in an amount from 0.1 weight percent to 10 weight percent or from 1 weight percent to 5 weight percent, the percentages based on the total solids of the sizing composition.
In addition to at least one film-former and at least one silane, sizing compositions of the present invention may further comprise one or more lubricants. In one non-limiting embodiment, the lubricant comprises at least one non-ionic lubricant. As used herein, the term “non-ionic” is used in a manner normally appreciated by those of ordinary skill in the art. Non-ionic lubricants useful in embodiments of the present invention preferably do not include reactive groups or other structures that might poison the ROMP catalyst or negatively affect the polymerization of the cycloolefins as described herein.
Examples of non-ionic lubricants useful in embodiments of the present invention comprise ethoxylated fatty alcohols, such as ethoxylated monooleate, ethoxylated di-oleate, ethoxylated monotallate and ethoxylated di-tallate. An example of a suitable ethoxylated di-tallate is available from BASF Corporation under the product name MAPEG 600 DOT. MAPEG 600 DOT is a polyethylene glycol ditallate having an average molecular weight of 600. An example of a suitable ethoxylated di-oleate is available from BASF Corporation under the product name MAPEG 600 DO. MAPEG 600 DO is a polyethylene glycol di-oleate having an average molecular weight of 600. Other examples of ethoxylated di-tallates and ethoxylated di-oleates, as well as ethoxylated monooleates and ethoxylated monotalates, are also available from BASF Corporation under the MAPEG product line. A further example of a non-ionic lubricant useful in embodiments is polyethylene glycol monolaurate, which is commercially available from The HallStar Company as HALLSTAR PEG 600 ML.
The at least one non-ionic lubricant can generally be present in the sizing composition in an amount from 10 weight percent to 55 weight percent, the percentages based on the total solids of the sizing composition. The at least one non-ionic lubricant, in a further non-limiting embodiment, may be present in an amount from 25 weight percent to 35 weight percent, the percentages based on the total solids of the sizing composition.
The sizing composition of the present invention may further comprise at least one cationic lubricant. In another non-limiting embodiment, the sizing composition may comprise at least one cationic lubricant without a non-ionic lubricant. As used herein, the term “cationic” is used in a manner normally appreciated by those of ordinary skill in the art. Cationic lubricants advantageously protect against fiber-to-fiber abrasion. In one non-limiting embodiment, the concentration of the cationic lubricant is sufficiently low to avoid poisoning the ROMP catalyst. While the cationic lubricant may include functional groups that may poison the ROMP catalyst (e.g., secondary amines), some cationic lubricant may be needed to protect against fiber-to-fiber abrasion. Accordingly, embodiments may use cationic lubricants in amounts that protect against fiber-to-fiber abrasion without significantly affecting the function of the ROMP catalyst.
The loss on ignition of the cationic lubricant in one non-limiting embodiment is 0.01% or less. While generally most cationic lubricants used in fiber glass sizing compositions will be suitable for use in the present invention, examples of cationic lubricants useful in non-limiting embodiments of the present invention include carboxylic acid salts of amidoamines. Examples of suitable carboxylic acid salts of amidoamines include Emery 6717L, available from Cognis Corporation, Cat X available from Rhone Poulenc, and Alubraspin 261 available from BASF Corp. Further examples of suitable cationic lubricants include Lubril Cat-X/VC, commercially available from Rhodia of Cranbury, N.J., and Katax 6717, commercially available from Pulcra Chemical of Geretsried, Germany.
The at least one cationic lubricant may be present in the sizing composition in an amount from 0 weight percent to 5 weight percent, the percentages based on the total solids of the sizing composition. Smaller amounts of amine-containing cationic lubricants may be used in such embodiments due to the potential to poison the ROMP catalyst in some embodiments. In some non-limiting embodiments, the at least one cationic lubricants may be generally present in the sizing composition in an amount from 0 weight percent to 2 weight percent, the percentages based on the total solids of the sizing composition. The at least one cationic lubricant, in other non-limiting embodiments, may be generally present in the sizing composition in an amount from 0 weight percent to 1 weight percent, the percentages based on the total solids of the sizing composition.
The sizing composition of the present invention may further comprise at least one anionic lubricant. In another non-limiting embodiment, the sizing composition may comprise at least one anionic lubricant without a cationic lubricant or a non-ionic lubricant. As used herein, the term “anionic” is used in a manner normally appreciated by those of ordinary skill in the art. Example of a suitable anionic lubricant for use in the present invention include partial esters of a branched carboxylic acid copolymer, such as Ketjenlube 522 partial ester (also sold as Dapral GE202). Ketjenlube 522 partial ester is commercially available from Akzo Chemie America of Chicago, Ill.
The sizing composition can also optionally contain other ingredients which are known to those skilled in the art to be useful in fiber glass sizing compositions, such as antifoaming agents, biocides, humectants and the like. The sizing composition can be prepared by any method known to those skilled in the art, and applied to the fibers and/or fillers by any method known in the art.
The present invention also relates to fiber glass products comprising a plurality of glass fibers at least partially coated with a sizing composition of the present invention. In one non-limiting embodiment, the fiber glass product is a fiber glass strand. The fiber glass strand may be wound into a cylindrical package and dried using techniques known to those of ordinary skill in the art. These individual packages may be shipped to a composite manufacturer to make a reinforced composite. Composite manufacturers typically use strands from a plurality of packages to make a composite. In another non-limiting embodiment, a glass fiber strand may be directly wound into a fiber glass roving, dried, and shipped to a composite manufacturer. In non-limiting embodiments, a roving may comprise 4000 or more fibers, the fibers having diameters between 13 and 35 microns. In other non-limiting embodiments, the rovings are assembled rovings comprising as many as 10,000 or more fibers, the fibers having diameters between 10 and 23 microns. In some applications, chopped fiber glass strands and fiber glass mats can be used.
In non-limiting embodiments of the present invention, the loss on ignition of the sizing on the fiber glass can generally be between 0.1 and 2.0%. In other non-limiting embodiments, the loss on ignition can generally be between 0.1 and 1.5%. The loss on ignition of the sizing on the fiber glass, in other non-limiting embodiments, can generally be between 0.1% and 0.8%.
The present invention also relates to methods of forming a plurality of glass fibers having sizings of the present invention applied thereon. Any glass fiber suitable for reinforcing can suitably be treated in accordance with the present invention. Non-limiting examples of glass fibers suitable for use in the present invention can include those prepared from fiberizable glass compositions such as “E-glass”, “A-glass”, “C-glass”, “S-glass”, “ECR-glass” (corrosion resistant glass), and fluorine and/or boron-free derivatives thereof.
The glass fibers of the present invention can be formed in any suitable method known in the art, for forming glass fibers. For example, glass fibers can be formed in a direct-melt fiber forming operation or in an indirect, or marble-melt, fiber forming operation. In a direct-melt fiber forming operation, raw materials are combined, melted and homogenized in a glass melting furnace. The molten glass moves from the furnace to a forehearth and into fiber forming apparatuses where the molten glass is attenuated into continuous glass fibers. In a marble-melt glass forming operation, pieces or marbles of glass having the final desired glass composition are preformed and fed into a bushing where they are melted and attenuated into continuous glass fibers. If a premelter is used, the marbles are fed first into the premelter, melted, and then the melted glass is fed into a fiber forming apparatus where the glass is attenuated to form continuous fibers. In the present invention, the glass fibers can be formed by the direct-melt fiber forming operation. For additional information relating to glass compositions and methods of forming the glass fibers, see K. Loewenstein, The Manufacturing Technology of Continuous Glass Fibres, (3d Ed. 1993), at pages 30-44, 47-103, and 115-165, which are specifically incorporated by reference herein. Immediately after formation, the filaments are at least partially coated with an embodiment of the sizing composition described above. The application of sizing to glass fibers is well known in the art and can be accomplished by conventional methods such as a belt applicator, a “kiss-roll” applicator or by spraying. The glass fibers are then gathered into at least one strand, and collected into a forming package on a winder. See generally K. Loewenstein, The Manufacturing Technology of Continuous Glass Fibres, (3d Ed. 1993).
The present invention also relates to polyolefin composites reinforced with sized glass fibers, wherein the sizing comprises a sizing composition of the present invention. In one non-limiting embodiment, the polyolefin comprises polymers formed from cyclic olefins. In a further non-limiting embodiment, the cyclic olefins are cured by ROMP catalysts. In another non-limiting embodiment, the polyolefin comprises polymers formed from DCPD. In a further non-limiting embodiment, the DCPD monomer is cured by ROMP catalysts. In another non-limiting embodiment, the sizing compositions of the present invention can be used to at least partially coat glass fibers for use in reinforcing composites formed through other unsaturated polymerization reactions, such as reactions involving unsaturated polyesters, acrylics, and the like, as known to those of skill in the art.
In embodiments where the composite comprises polymers formed from cyclic olefins, such as pDCPD, glass fibers comprising embodiments of sizing compositions of the present invention can be added to a curable composition. The curable composition can comprise, in some such embodiments, a cyclic olefin (e.g., DCPD), a metathesis catalyst for polymerizing the cyclic olefin, a modifier compound, and a curing agent for the modifier compound. The modifier compound can be present in the curable composition in amount between about 0.1 and 30 weight percent based on the total weight of the composition in some embodiments. The modifier compound, in some embodiments, can be present in the curable composition in amount between about 3 and 20 weight percent based on the total weight of the composition. The curing agent can be present in an amount between about 0.1 and about 10 weight percent based on the total weight of the curing composition in some embodiments. The curing agent, in some embodiments, can be present in an amount between about 0.2 and about 1 weight percent based on the total weight of the curing composition. The curing agent can comprise a radical initiator such as a non-cyclic peroxide in some embodiments. In some embodiments, the curable composition comprises a cyclic olefin (e.g., DCPD), a metathesis catalyst for polymerizing the cyclic olefin, 0.1-30 wt. % of a modifier compound based on the total weight of the composition, and 0.1-10 wt. % of a curing agent for the modifier compound based on the total weight of the composition. Composites formed from such curable compositions and glass fibers at least partially coated with sizing compositions of the present invention can be formed using techniques known to those of skill in the art.
In other non-limiting embodiments, composites of the present invention have a bonding strength of greater than 4,000 pounds per square inch (psi) as determined by short-beam shear (SBS) testing. In other non-limiting embodiments, the composites have a bonding strength of greater than 5,000 psi as determined by SBS testing. Composites of the present invention, in other non-limiting embodiments, have a bonding strength of greater than 6,000 psi as determined by SBS testing.
It was observed that composites utilizing rovings coated with sizings of the present invention can exhibit improved glass-matrix resin bonding strengths over composites utilizing conventional fiber glass reinforcements. Short-beam shear testing in accordance with ASTM 2344 is one way in which glass-matrix resin bonding strength can be measured.
The curable composition of the present invention comprises a cyclic olefin, a cyclic olefin metathesis polymerization catalyst, an compound (C) comprising a multifunctional unsaturated compound adapted to promote adhesion to an adhering substrate, and a curing agent for the compound (C).
The cyclic olefin used in the present invention comprises cyclic olefin monomer units that may be arranged to form a cyclic olefin polymer, obtained by polymerizing cyclic olefin monomer units. Any polymer of cyclic olefin monomer units known in the art may in principle be used in the invention. The cyclic olefin polymer comprises cyclic monomer units of a saturated cyclic hydrocarbon (cycloalkane) structure, and/or of an unsaturated cyclic hydrocarbon (cycloalkene) structure. The number of carbon atoms forming the cyclic structure in a monomer unit also is not particularly limited, but in preferred embodiments ranges from 4 to 30, more preferably from 5 to 20, and most preferably from 5 to 15.
The amount of cyclic olefin monomer units in the cyclic olefin polymer may be selected within a broad range, but is preferably 50 wt. % or more, more preferably 70 wt. % or more, and most preferably 90 wt. % or more, exclusive of any filler in the composition. A combination of different cyclic monomers may also be used. The cyclic olefin polymer of the composition may comprise an addition polymer of cyclic olefin monomer units, optionally copolymerized with another olefin monomer, and/or may comprise a ring-opening polymer of cyclic olefin monomer units, the latter being preferred.
A cyclic olefin monomer unit forms a cyclic structure of carbon atoms and carbon-carbon double bonds, examples whereof include but are not limited to norbornene based monomer units and monocyclic monomer units, a norbornene based monomer unit being preferred. The norbornene based monomer unit has a norbornene ring, and may for instance include 2-norbornene, norbomadiene and other bicyclic compounds; dicyclopentadiene (DCPD), dihydrodicyclopentadiene and other tricyclic compounds; tetracyclododecene, ethylidenetetracyclododecene, phenyltetracyclododecene and other tetracyclic compounds; tricyclopentadiene and other pentacyclic compounds; tetracyclopentadiene and other heptacyclic compounds; alkyl substituted compounds, such as methyl, ethyl, propyl and butyl substituted compounds, alkylidene substituted compounds, such as ethylidene substituted compounds, andaryl substituted compounds, such as phenyl and tolyl substituted compounds; and derivatives thereof having for instance an epoxy group, a methacryl group, a hydroxyl group, an amino group, a carboxyl group, a cyano group, a halogen atom, and others.
Monocyclic cyclic olefin monomer units may also be employed, suitable examples thereof comprising cyclobutene, cyclopentene, cyclooctene, cyclododecene, 1,5-cyclooctadiene and other monocyclic cyclic olefins, and substitution compounds and derivatives having polar groups like those mentioned as examples for the norbornene based monomer units. Such cyclic olefin monomers may be used alone or in combination with another or more types. Suitable linear olefin monomer units that may be addition-copolymerized with the above cyclic olefin monomer units include but are not limited to ethylene, propylene, I-butene, 1-pentene, 1-hexene, 1-octene, I-butene, 2-pentene, and 1,4-hexadiene for instance. The amount of the linear olefin monomer units used is preferably lower than 50 wt %, more preferably lower than 20 wt %, and more preferably lower than 10 wt % of the total amount of the cyclic olefin and linear olefin monomer units.
Apart from the cyclic olefin monomer units, the curable composition further comprises a cyclic olefin metathesis polymerization catalyst in an amount of 30-1000 ppm relative to the total weight of the composition. The metathesis polymerization catalyst of the invention comprises a catalyst capable of metathesis ring-opening polymerization of cyclic olefin monomer units. Such a catalyst may comprise a complex having a transition metal atom as center atom and a plurality of ions, atoms, and/or compounds bonded thereto. Transition metal atoms may be used to advantage, of which tantalum, molybdenum, tungsten, ruthenium and osmium may be mentioned in particular. Suitable catalyst systems are for instance disclosed in the following patent publications EP1468004, EP2280017, EP2151446, EP1757613, and EP1577282, incorporated herein.
Particularly useful catalytic systems comprise mono and bis-Schiff base catalysts, such as those depicted below:
Examples of the above mentioned precatalysts comprising two Schiff base ligands are disclosed in European patent application EP2280017:
Other examples of catalysts which may be used in the present invention are disclosed below:
Particularly suitable catalysts also comprise Mo—W catalysts such as:
The olefin metathesis polymerization catalyst may be used in any suitable form, including a form in which it is dissolved or suspended in a solvent. Suitable solvents include linear aliphatic hydrocarbons such as n-pentane, n-hexane, n-heptane, or liquid paraffin, as well as alicyclic hydrocarbons such as cyclopentane, cyclohexane, alkyl substituted cyclohexane, di- and tricycloheptane, and cyclooctane to name a few, aromatic hydrocarbons such as benzene, toluene, xylene and others; nitrogen-containing solvents such as nitromethane, nitrobenzene, and acetonitrile, and oxygen-containing solvents such as diethyl ether and tetrahydrofuran.
The curable composition preferably also contains a catalyst retarder capable of extending working life time before curing starts. Suitable polymerization reaction retarders include but are not limited to phosphite compounds, such as those disclosed in EP2460587.
The composition may also comprise a chain transfer agent, for instance a linear olefin having substituted groups. Suitable chain transfer agents include vinylnorbornene, 1-hexene, 2-hexene and other aliphatic olefins; styrene, divinylbenzene, and other vinyl aromatic olefins; olefins having alicyclic hydrocarbon groups such as vinylcyclohexane; vinylethers; methylvinylketone, as well as substituted (meth)acrylic acids and their salts, such as vinyl(meth)acrylate, allyl(meth)acrylate, and compounds such as allyltrivinylsilane, allylmethyldivinylsilane, allyldimethylvinylsilane, and 4-vinylaniline. Such chain transfer agents may be used alone or in combination and are generally added in an amount ranging from 0.01 to 10 pbw, and preferably 0.1 to 5 pbw with respect to 100 parts by weight of the cyclic olefin monomer units.
The composition in accordance with the invention further comprises 1-30 wt. % of a compound (C). Compound (C) comprises at least one vinyl group and may be monofunctional. A multifunctional compound comprising at least one vinyl group is also possible. Compound (C) is preferably configured to promote adhesion to an adhering substrate and capable of forming a polymeric structure. In preferred embodiments, the compound (C) does not substantially influence the catalytic activity of the metathesis polymerization catalyst in the composition, and is compatible with the cyclic olefin monomer units, i.e. does not give rise to phase separation. The compound (C) in a preferred embodiment has a Hildebrand solubility parameter comprised between 15.4 and 19.8 MPa1/2, as calculated from Hansen parameters (http://hansen-solubility.com). The compound (C) in other preferred embodiments comprises a bi- or trifunctional compound, having two, respectively three carbon-carbon unsaturated bonds.
Preferred unsaturated compounds comprise ethylenically unsaturated compounds, which are here understood to mean vinyl aromatic compounds such as styrene, alpha-methylstyrene, para-methylstyrene, aminostyrene, hydroxystyrene, divinyl benzene, vinyl toluene; allyl compounds such as monoallyl esters and/or ethers and diallyl esters and/or ethers; vinyl ether and vinyl ester compounds such as vinyl benzoate; and (meth)acrylic compounds such as (meth)acrylic acids and their esters. Particularly preferred multifunctional unsaturated compounds comprise an acrylic and/or methacrylic compound. Suitable (meth)acrylic compounds include but are not limited to ethyleneglycol di(meth)acrylate, propanediol di(meth)acrylate, butanediol di(meth)acrylate, diethyleneglycol di(meth)acrylate, triethyleneglycol di(meth)acrylate, tetraethyleneglycol di(meth)acrylate, polyethyleneglycol di(meth)acrylate and other bifunctional compounds, as well as trimethylolpropane tri(meth)acrylate, trimethylolethane (tri)methacrylate, trimethylolpropanepropyleneoxide-modified tri (meth)acrylate and other trifunctional compounds. Combinations of unsaturated compounds may also be used.
Examples of suitable compounds (C) according to the present invention are depicted in Table 1. Table 1 provides the solubility parameters for DCPD, butadiene acrylate, and methacrylate monomers calculated based on Hansen Solubility Parameters. The calculations were done by using: HSPiP software from http://hansen-solubility.com.
Particularly useful catalytic systems comprise mono and bis-Schiff base catalysts, such as those depicted below:
The composition in accordance with the invention further comprises 0.1-10 wt. % of a curing agent for compound (C). The curing agent for compound (C) in an embodiment is configured to produce radicals and initiate a radical polymerization reaction of compound (C) monomer or oligomer units to form a cross-linked compound (C) polymer.
Suitable curing agents include a radical source such as a peroxide, a hydroperoxide, a perester and/or a perketone compound, including cyclic and linear compounds. A linear (hydro) peroxide is particularly preferred as curing agent for the compound (C). Suitable peroxides include but are not limited to alkylperoxides, arylperoxides, and aralkyl or alkaryl peroxides. Secondary and tertiary aliphatic and aromatic hydroperoxides, such as tert-butyl hydroperoxide, tert-amyl hydroperoxide, and cumene hydroperoxide, are particularly preferred.
The peroxide compounds can generally be added to the reaction mixture at any point prior to the onset of a gel state, and are added to the composition in an amount of 0.01-8 wt. %, more preferably 0.1-7 wt. %, even more preferably 0.2-1 wt. %, and most preferably 0.2-0.8 wt. %. Alternatively, the peroxide compound can be added to compound (C) first and delivered to the composition during the metathesis catalyzation step.
Other additives may also be added to the composition such as flame retardants, light stabilizers, pigments, dyes and other colorants, as well as foaming agents for instance. Suitable flame retardants include but are not limited to phosphorus, nitrogen and halogen containing flame retardants, metal hydroxides such as aluminum hydroxide for instance, and antimony compounds such as antimony trioxide.
In preferred embodiments, fillers may be added to the composition of the present invention as substrate materials. Both inorganic and organic fillers may be used without any limitation, whereby an inorganic filler is preferred. Suitable inorganic fillers for instance include metal particles of iron, copper, nickel, gold, silver, aluminum, lead, and tungsten; carbon particles such as carbon black, graphite, activated carbon, carbon micro-balloons and the like; inorganic oxide particles such as silica, alumina, titanium oxide, iron oxide, zinc oxide, magnesium oxide, and the like; inorganic carbonate particles such as calcium carbonate and magnesium carbonate; calcium sulfate; inorganic silicate particles such as talc, clay, mica, kaolin, fly ash, montmorillonite, calcium silicate, and glass particles; as well as particles of titanate, aluminum nitride and silicon carbide.
Suitable organic fillers may for instance comprise wood, starch, lignin, organic pigment, and polymer particles such as those of polystyrene, polyamide, polyolefins such as polyethylene and polypropylene, polyvinylchloride, elastomers and/or waste polymers. It is also possible to add functional fillers, such as piezoelectric ceramics, fillers that change static/conductive properties such as carbon nanotubes, and rheology modifiers. The fillers may be provided with a sizing composition in accordance with the invention.
According to certain embodiments of the invention the composition comprises reinforcing fibers as an adhering substrate. Suitable reinforcing fibers to be used in the present invention can be chosen within wide ranges. It is possible for instance to use inorganic fibers, such as glass fibers, carbon and graphite fibers, alumina fibers, tungsten fibers, molybdenum fibers, titanium fibers, steel fibers, boron fibers, silicon carbide fibers, and silica fibers. Other suitable fibers include organic fibers such as aramid fibers, ultra high molecular weight polyethylene fibers, liquid crystalline and other polyester fibers, and the like, as well as natural fibers and reinforcements. Preferred reinforcing fibers comprise glass and carbon fibers, of which E-glass, R-glass, S-glass and S2-glass fibers are used most preferably. Newer fibers like Advancetex/Hipertex and Innofiber from PPG may also be used.
The reinforcing fibers can be applied in any physical form, i.e. as mono- and multifilaments, or in the form of strands and yarns, as woven fabric or according to any other textile structure, as short fibers or as continuous fibers, or in the form of a preimpregnated sheet (‘prepreg’). Any combination of different types of fibers is also possible. The amount of the reinforcing fibers may be chosen within wide ranges but suitable amounts generally range from 30-70 vol. %, a fiber volume fraction of 55-65 vol. % being preferred in most applications.
In other embodiments of the invention, the reinforcing fibres are provided with a coupling agent that is incorporated in a sizing composition. The sizing composition is configured to provide an improved adhesion of the composition to an adhering substrate material, such as reinforcing fibers. The adhering substrate material is preferably sized with commercially available silane compounds that do not interfere with the used olefin metathesis catalysts, and are compatible with cyclic olefin polymers, in particular polydicyclopentadiene.
In useful embodiments of the invention, a silane, thiol and/or titanate coupling agent is added to the sizing composition. Non-limiting examples of suitable silane coupling agents include methacrylate, acrylate, amino, or epoxy functionalized silanes, as well as alkyl, alkenyl, and norbornyl silanes. Particularly preferred silane coupling agents comprise allyltrimethoxy silane, styryltrimethoxy silane. N-vinylbenzyl-aminoethyl-γ-aminopropyltrimethoxy silane and salts thereof, as well as vinyltris(2-methoxyethoxy) silane, α-methacryloxybutyltrimethoxy silane, γ-mercaptopropyltrimethoxy silane, and aminoethyl-γ-aminopropyltrimethoxy silane.
The sizing formulation applied onto the adhering substrate, in particular the reinforcing fibers, typically further comprises a film former apart from the coupling agent and optionally a lubricant. The film former typically comprises a film forming polymer. Any components of a sizing formulation that do not substantially interfere with the metathesis catalyst operation and/or substantially decreases the cyclic olefin polymerization reaction are considered to be compatible with the composition and may generally be used in the invention.
Film formers that are compatible with and/or do not interfere with ring opening metathesis polymerization (ROMP) are preferably used and comprise epoxies, polyesters, polyurethanes, polyolefins, and/or polyvinyl acetates. Other common film formers that do not adversely affect the performance of the cyclic olefin metathesis catalyst may also be used. Film formers are typically used as nonionic, aqueous emulsions, and combinations of different film formers may be used if desired.
Particularly useful film formers of the sizing composition have a Hildebrandt solubility parameter δT comprised between 15.9 and 19.9 MPa1/2.
In a particularly preferred embodiment of the invention, the sizing formulation, and the film former in particular. comprises a polyolefin. Suitable polyolefins include but are not limited to polyethylenes, polypropylenes, polybutylenes, and copolymers thereof, and the polyolefins may be oxidized, maleated, or otherwise treated for effective film former use. In a preferred embodiment of the invention, the film former comprises comprises a (co)polymer of monomer units having from four to six carbon atoms and one carbon-carbon double bond, and more preferably a polybutadiene, which may be functionalized or comprise a butadiene-styrene co-polymer for instance. The polybutadiene-based film former preferably comprises a polymer emulsion, wherein the polybutadiene has a weight average molecular weight between 300 and 20000 and has a solubility parameter δT calculated from 3 Hansen parameters of at least 15.9 MPa1/2 and not more than 19.9 MPa1/2. Examples of suitable polybutadiene-based film formers are available from Cray Valley and Synthomer under the tradenames of RICON, Krasol and Lithene.
A nonionic lubricant as well as an anti-static agent may also be added to the sizing composition. Suitable nonionic lubricants that are compatible with ROMP compositions include but are not limited to esters of polyethylene glycols and block copolymers of ethylene oxide and propylene oxide. More than one nonionic lubricant may be used in a given sizing formulation if desired. Suitable nonionic lubricants include but are not limited to block copolymers of ethylene oxide and propylene oxide. Cationic lubricants may also be added to the sizing composition, such as polyethyleneimines for instance. The sizing composition may further comprise pH modifiers, such as acetic acid. The sizing composition may further comprise other useful additives, such as emulsifiers, defoaming agents and cosolvents, as well as biocides and antioxidants for instance. The sizing composition can be prepared by any method known in the art and applied to the adhering substrate and to the reinforcing fibers in particularly useful embodiments by any method, known in the art.
The invention is also directed to molded articles manufactured from the invented composition comprising a cyclic olefin, a cyclic olefin metathesis catalyst, such as a ROMP catalyst, a compound (C), a curing agent for the compound (C), and optionally an adhering substrate, such as, for example reinforcing glass fibers. Molded articles according to the invention are obtained by a method comprising combining at least the components (A) to (D) to form the composition; subjecting the composition to conditions effective to promote an olefin metathesis reaction of the cyclic olefin and a radical polymerization of compound (C), preferably comprising the additional step of contacting the composition with an adhering substrate; and subjecting the composition to the conditions to provide a bond between the composition and the adhering substrate.
Methods of manufacturing the molded articles may include but are not limited to those formed by state of the art composite manufacturing techniques, such as casting, centrifugal casting, pultrusion molding, injection pultrusion molding, filament winding, rotational molding, and open mold molding. In an embodiment of the invention, a method is provided comprising the step of injecting the composition into a closed mold, wherein the mold is preferably provided with reinforcing fibers prior to the injection of the composition. Such techniques include reaction injection molding (RIM), resin transfer molding (RTM), vacuum assisted resin infusion (VARI), Seeman's Composite Resin Infusion Molding Process (SCRIMP), Reinforced Reaction Injection Molding (RRIM), Structural Reaction Injection Molding (SRIM), thermal expansion transfer molding (TERM), resin injection recirculation molding (RICM), controlled atmospheric pressure resin infusion (CAPRI), and the like.
Subjecting the composition to conditions effective to promote an olefin metathesis reaction of the cyclic olefin and a radical polymerization of the compound (C), generally involves heating the composition to a suitable curing temperature during a suitable time interval, optionally at a pressure above 0.1 MPa. The heating temperature in an embodiment of the method is in a range of RT to 200° C., more preferably 50° C. to 200° C., even more preferably 120° C. to 150° C. The heating times preferably are in a range of 0.1 to 180 minutes, more preferably 1 to 120 minutes, even more preferably 10 to 60 minutes. The pressure applied during molding may be selected in accordance with the manufacturing method used and may be as low as a 0.1 to 0.5 MPa, for instance when using RTM. Vacuum or reduced pressures may also be used.
A particularly preferred embodiment relates to a method wherein the conditions comprise heating at a temperature between 120° C.-150° C. during at most 60 minutes.
Molded article may be used in a variety of applications, including but not limited to aerospace components, marine components, automotive components, sporting goods, electrical components, medical components, and military components. In useful embodiments the molded article may be a turbine component such as a turbine blade component or turbine blade. Examples of aerospace components may include but are not limited to fuselage skins, wings, fairings, doors, access panels, and stiffeners for instance. Examples of automotive components may include but are not limited to body panels, fenders, spoilers, protective plates, hoods, pillars, leaf springs and doors. Other examples of suitable articles include bridges, pipes, pressure vessels, containers, and so on. Examples of military components include but are not limited to ballistic resistant armor plates and other structures for protecting personnel or equipment. Suitable sporting goods may include tennis rackets, hockey sticks, golf club shafts and the like.
A molded article in accordance with the invention and made form a PDCPD composition in particular shows an unprecedented combination of properties, in particular a relatively high toughness, even at very low temperatures, a relatively high chemical corrosion resistance, and a relatively high heat deflection temperature or glass transition temperature Tg, the properties being relative to the state of the art PDCPD molded articles. Also, the (matrix) polymer has a volatile content of less than 3 wt. % relative to the total weight of the matrix polymer in certain preferred embodiments.
A useful embodiment of the invention provides a molded article wherein the composite material properties at least satisfy one of a glass transition temperature Tg according to ASTM D7028-07e1 above 180° C.; a transverse 3 point bending strength according to ISO 14125 above 50 MPa; and a G1c according to ISO 15024 above 800 J/m2.
Embodiments of the present invention will now be illustrated in the following specific, non-limiting examples.
Sizing compositions were prepared in accordance with the formulations set forth in Table 2. These formulations represent non-limiting embodiments of sizing compositions of the present invention. Example 1 is one embodiment of a sizing composition that can be used, for example, on glass fibers in applications where a strong level of adhesion is desired. Example 2 is another embodiment of a sizing composition that can be used, for example, on glass fibers in applications where a less strong level of adhesion to a substrate, such as in ballistics operations, is desired.
1DYNASYLAN 1175 from Degussa AG.
2SILQUEST A-151 from Momentive Performance Materials, Inc.
3LITHENE P4-25P from Synthomer, Inc.
4PLURONIC F-108 polyoxyalkylene block copolymer from BASF Corp.
5GENAPOL UD 050 from Clariant Corporation.
Additional formulations representing non-limiting embodiments of sizing compositions of the present invention are provided in Tables 3 and 4 as Examples 3-15.
6DYNASYLAN 1175 from Degussa AG.
7SILQUEST A-151 from Momentive Performance Materials, Inc.
8LITHENE P4-25P from Synthomer, Inc.
9LITHENE P4-150P from Synthomer Inc.
10LITHENE AL-15MA from Synthomer Inc.
11PLEXTOL X9110 from PolymerLatex GmbH.
12SYNPERONIC PE/F108 ethoxylated polypropylene oxide from Croda International.
13Blend MPG (monopropylene glycol) from Chemische Werke Kluthe GMBH.
75 g (15.5%)
14Hot water is at 82° C.
15DYNASYLAN 1175 from Degussa AG.
16SILQUEST A-151 from Momentive Performance Materials, Inc.
17DYNASYLAN MEMO from Degussa AG.
18SILBLOCK WMS from Momentive Performance Materials, Inc.
19LITHENE P4-25P from Synthomer, Inc.
20SYNPERONIC PE/F108 ethoxylated polypropylene oxide from Croda International.
21Blend MPG (monopropylene glycol) from Chemische Werke Kluthe GMBH.
To prepare the sizing compositions shown as Examples 1-6, 8, and 10-15 in Tables 2-4, the specified amount of the Polybutadiene Polymer, Emulsifying Agent, and Nonionic Surfactant were added to a side mix tank. The contents were heated to 150° F. Under high shear mixing conditions, the indicated amount of hot deionized water was slowly added to the side mix tank. During the water addition, the mixture inverted from a water-in-oil emulsion to an oil-in-water emulsion. For Example 7, Polybutadiene Polymer C was added under continuous stirring to a side mix tank containing the indicated amounts of hot water and ammonia to form a clear solution that was added to the main mix tank. The Styrene-butadiene Copolymer of Example 9 was supplied as an emulsion that was directly added to the main mix tank.
For all examples, deionized water was added to the main mix tank and, while agitating, the specified amount of Silane was added. The Silane was mixed until hydrolysis occurred (approximately 30 minutes). The contents of the side mix tank were then added to the main mix tank, while stirring. The main mix tank was then agitated while enough deionized water was added to bring the sizing composition to its desired volume.
Each of the sizing compositions in Tables 2-4 was applied to a fiber glass strand in the following manner. Fiber glass filaments, having a nominal filament diameter of 16 microns were formed using a bushing and then at least partially coated with one of the sizing compositions in Tables 2-4 using a sizing applicator. The nominal loss on ignition of the fiber glass was 0.5 weight percent. The fiber glass filaments were gathered into a strand and then wound into a forming package on a winder. For Examples 1 and 2, each strand comprised 4,000 filaments with a nominal weight of 1984 tex. The strands were dried using dielectric drying. For Examples 3-15, each strand comprised 1,200 filaments with a nominal weight of 600 tex. The strands were dried at 40° C.
Two types of glass fibers were used: Sample 1, at least partially coated with sizing composition Example 1 from Table 2 and which is compatible with pDCPD resin and Comparative Example A, at least partially coated with PPG's commercial 1383 binder and which is compatible with epoxy resin. The nominal loss on ignition of the fiber glass was 0.55 weight percent. Both types of glass were prepared as rovings (direct draw) from fibers having a nominal filament diameter of 16 microns that had a nominal weight of 1984 tex. The rovings were dried using dielectric drying. A plurality of the rovings were woven into a plain woven fabric with an areal density of 827 g/m2. The matrix materials used were a pDCPD formulation (indicated below as F2.06), supplied by Telene SAS, and a standard epoxy resin (Epikote 828 LVEL with Dyteck DCH 99 hardener).
Unidirectional (UD) samples for bending tests were produced by means of a hand pultrusion process by pulling impregnated fiber bundles through a mold. Woven fabric laminates were produced by vacuum infusion of 4 layers of glass fiber weave with the F2.06 pDCPD resin and also with the epoxy resin. The composite fiber volume fractions for the different types of samples are in Table 5.
Adhesion Assessment with Three Point Bending Test
Transverse three point bending (3pb) tests on unidirectional samples were done according to the ISO 14125 standard to provide an indication of the quality of the bond between fibers and matrix, for three combinations of fiber sizing/matrix: the Sample 1 glass combined with the F2.06 pDCPD matrix, and the Comparative Example A glass, combined with the epoxy matrix, as well as with the F2.06 pDCPD resin. A crosshead displacement rate of 1 mm/min was used.
To investigate the quality of the fiber-matrix adhesion of the pDCPD F2.06/Sample 1 glass combination as compared to the epoxy/Comparative Example A glass combination, which is known to have sufficient adhesion, a series of transverse three point bending tests was done on unidirectional samples. For completion, this was also done on pDCPD F2.06/Comparative Example A composites. Visual inspection of the latter samples suggested poor impregnation quality, but they were still tested for completeness.
Table 6 shows the average obtained transverse three-point bending strength for the three materials. The obtained strength for all three materials was significantly different. The highest values were obtained for the F2.06/Sample 1 combination, followed by the EP/Comparative Example A combination. Since the latter is known to have good adhesion, adhesion between fibres and matrix in the pDCPD F2.06/T73 material can therefore be considered to be also very good.
Samples cut from the woven fabric laminates by water-cooled diamond saw, were used for static and fatigue tensile tests according to the ASTM D3039 and D3479 standards. Strain measurements during the static tests were done by means of digital image correlation. A test speed of 2 mm/min was used. Fatigue tests were done in load-controlled mode on a 160 kN hydraulic Schenck. The fatigue frequency was 5 Hz, and the R-ratio was 0.1. The chord modulus was determined as the ratio of the difference in load over the difference in displacement for each cycle.
The results from the tensile tests on the woven fabric composite samples are shown in Table 7. Final failure was in the gauge section for all tested samples. No significant difference between the two materials was measured in terms of stiffness or strength. The failure strain for the epoxy samples was found to be marginally larger than that of the pDCPD composite. This may be explained by the pronounced loss in stiffness of the epoxy samples near the end of the test, caused by the build-up of extensive delamination damage.
Pictures taken during the test with transmitted light do reveal a markedly different damage development.
Tensile fatigue tests were run at load levels of 250, 200 and 150 MPa. Since the tensile strength of both materials was approximately 500 MPa, this corresponds to 50, 40 and 30% of the tensile strength. At least five samples of each material were tested for each load level. The fatigue life data are shown on the graph of
As shown in the data, no statistical significant difference in fatigue life was found between the two materials, although the fatigue life data for the pDCPD composite clearly seems to be situated in the higher end of the epoxy composite results range.
For all tested load levels, the variation in fatigue life for the pDCPD composite is much smaller than that for the epoxy composite. For a certain fatigue load level, the difference between the lowest and highest observed fatigue life is about a factor ten for the epoxy composite (i.e., one order of magnitude, which is in line with what is commonly observed for epoxy composites), while for the pDCPD laminate this difference is less than a factor three.
Because of these observations, for both materials the 95% confidence interval was determined. The 95% interval is also indicated on
The graph in
This is supported by the observed evolution of damage in this type of samples during tensile fatigue as shown in
Drop weight impact tests were done on 10×10 cm2 samples cut from the woven laminates with a semi-hemispherical impacter with a diameter of 16 mm and a weight of 3.120 kg. The drop height was 49 cm and 81.5 cm, i.e., a potential impact energy of 15 and 25 joules, respectively. Assessment of the impact damage was done by means of visual inspection with the aid of transmitted light, as well as by ultrasonic C-scan.
Drop weight impact tests were performed on the pDCPD F2.06/Sample 1 and epoxy/Comparative Example A laminates with impact energies of 15 and 25 joules. Due to the transparent nature of the samples, visual inspection of the impact damage was possible. An example of a transmitted light photograph of two specimens impacted with an energy of 25 J is shown in
C-scan ultrasonic imaging was used to determine the size of the delaminations in the impacted samples. Since this is a transmission type of scan, the result of the scan is not the sum of all delamination surfaces present in the material, but rather the projected surface of all superposed delaminations. The results of the scans for both impact energy levels of the two materials are shown in
All the obtained data from the impact tests indicate a significant difference in delamination size between the pDCPD and the epoxy laminates for equal impact energy. For both impact energy levels tested, the measured delamination size is found to be about two times larger for the epoxy laminate than for the pDCPD laminate, indicating a tougher behavior of the pDCPD composite.
Measurement of Mechanical Properties for Examples from Tables 3 and 4
The interlaminal shear strength (ILSS), flexural strength, and/or flexural modulus of the sized fiber glass strands were measured. The interlaminal shear strength was measured using the ISO 14130 test method. The flexural strength was measured using the. The flexural modulus was measured using the ISO 3597 test method. Table 8 provides the results.
Desirable characteristics, which can be exhibited by the present invention, include, but are not limited to the provision of: sizing compositions which are suitable for fiber glass that may be used to reinforce cycloolefinic resins cured by ROMP catalysts; sizing compositions which are suitable for fiber glass to reinforce DCPD resins cured by ROMP catalysts; sizing compositions that can potentially participate in the polymerization and cross-linking mechanism of the DCPD resin; sizing compositions that utilize ingredients having a low potential to deactivate the ROMP catalyst; fiber glass that is effective reinforcement for cycloolefinic resins that cure by the ROMP reaction; fiber glass that is effective reinforcement for DCPD resins that cure by the ROMP reaction; DCPD composites having desirable shear strengths; DCPD composites having SBS values that substantially approach the SBS value of un-reinforced cured DCPD resin; and a cost-competitive, low viscosity resin system (e.g., a resin system developed from DCPD monomer) that cures without styrene co-monomer/diluent.
The present invention will now be described more specifically with reference to examples and comparative examples, without however being limited to these examples. It is to be noted that, in the examples and comparative examples, “parts” and “%” are based on weight basis unless otherwise noted.
Each property in the examples and comparative examples was measured and evaluated in accordance with the following methods:
Three point bending: ISO 14125
Glass transition temperature Tg: ASTM D7028-07e1
Tensile tests: ASTM 3039
Wettability: by visual inspections
Quality assessment: X-ray tomography (nanotom)
Compressive strength: ASTM 3410
Solubility parameters were calculated by using: “HSPiP—Hansen Solubility Parameters in Practice (HSPiP)” software (http://hansen-solubility.com) based on Charles Hansen's Hansen Solubility Parameters, A User's Handbook, 2nd Edition from 2007
Tensile fatigue tests: ASTM 3479
Interlaminar fracture toughness (G1c): ISO 15024
Compression after impact: ISO 18352
Hand-pultruded samples (F1 PDCPD—T48 glass) were analysed with X-ray tomography (nanotom) to assess the quality of the production process (voids, fibre orientation etc.).
Transverse Three Point Bending Tests
Transverse 3 point bending tests were done to provide an indication of the adhesion strength between fibres and matrix, for four combinations of fibre sizing/matrix. The test samples were cut from wide unidirectional rods by means of a water-cooled diamond saw, and the edges were sanded to eliminate damage resulting from the cutting. Eight samples were tested for each material combination.
The solubility parameters for selected polymers are shown in Table 9. The parameters were calculated based on the three parameter system developed by Charles M. Hansen. Calculations were done by using HSPiP software (http://hansen-solubility.com).
A DCPD formulation was prepared by mixing 89.9 g of DCPD monomer units, 10 g of 2,2-Bis[(methacryloyloxy)methyl]butyl methacrylate (TMPTMA, Sigma-Aldrich) (10%) and 0.1 wt. % of a tert-butyl peroxide (TBP, Sigma-Aldrich). Then 1.2 g of the ruthenium salicylaldimine catalyst solution comprising 0.02 g of triisopropyl phosphite was added. The resulted solution was stirred 5 min at RT.
The curing behaviour of the ensuing curable composition was determined by obtaining a DSC thermogram of the composition. The DSC was taken with a Universal V4.5A of TA Instruments and the heating rate was 10° C./minute.
A composition was obtained in the same manner as in Example 1, except that 1 wt. % of a tert-butyl peroxide (Sigma-Aldrich) and 30% of TMPTMA was added.
The curing behaviour of the ensuing curable composition was again determined by obtaining a DSC thermogram of the composition. The DSC was taken with a Universal V4.5A of TA Instruments and the heating rate was 10° C./minute.
A composition was obtained in the same manner as in Example 1, except that 0.6 wt. % of a tert-butyl peroxide (TBP, Sigma-Aldrich) was added.
A composite plate was prepared by a vacuum infusion method in which about 59 vol. % of a woven fabric of T48 glass fibers was impregnated with the composition at room temperature. T48 glass fibers are obtainable from PPG and carry an optimized sizing (T48) comprising polybutadiene or a polybutadiene derivative (ex. Lithene Ultra) as a film former which turned out to be highly soluble and compatible with DCPD and to allow achieving a good fibre wetting at room temperature. Furthermore a commercially available silane: N-Vinylbenzyl-N′-aminoethyl-3-aminopropylpolysiloxane, hydrochloride was used in the sizing formulation, which is a styrene derivative possessing a double bond available for the cross metathesis reaction. This enables to create a covalent bond between PDCPD matrix and the glass surface in the presence of the metathesis polymerization catalyst.
After resin infusion, the plate was formed by curing the composition at a temperature of around 90° C. during 20 minutes. A postcure was conducted at 190° C. during 60 minutes.
A composition was obtained in the same manner as in Example 1, except that 1.5 wt. % of a tert-butyl peroxide was added.
A composite plate was prepared in the same manner as in Example 3, except that the composite plate comprised about 62 vol. % of the woven fabric. Cure and postcure were the same as in Example 3.
A composition was obtained in the same manner as in Example 1, except that 3.0 wt. % of a tert-butyl peroxide was added.
A composite plate was prepared in the same manner as in Example 3, except that the composite plate comprised about 61 vol. % of the woven fabric. Cure and postcure were the same as in Example 3.
A composition was obtained in the same manner as in Example 1, except that 0.6 wt. % of a tert-butyl peroxide was added.
A composite plate was prepared in the same manner as in Example 3, and the composite plate comprised about 59 vol. % of the woven fabric. The applied cure cycle was the same as in Example 3. Postcure however was conducted at 120° C. during 60 minutes.
A composition was obtained in the same manner as in Example 1, except that 1.5 wt. % of a tert-butyl peroxide (Sigma-Aldrich) was added.
A composite plate was prepared in the same manner as in Example 3, and the composite plate comprised about 59 vol. % of the woven fabric. The applied cure cycle was the same as in Example 3. Postcure however was conducted at 120° C. during 60 minutes.
A composition was obtained in the same manner as in Example 1, except that 5 wt. % of a trimethyl propane trimethacrylate (TMPTMA, Sigma-Aldrich) and 0.3 wt. % of a tert-butyl peroxide (Sigma-Aldrich) were added to the composition.
A composite plate was prepared in the same manner as in Example 3, and the composite plate comprised about 60 vol. % of the woven fabric. The applied cure cycle was the same as in Example 3. Postcure was also conducted at 190° C. during 60 minutes.
A composition was obtained in the same manner as in Example 1, except that 5 wt. % of a trimethyl propane trimethacrylate (TMPTMA, Sigma-Aldrich) and 0.6 wt. % of a tert-butyl peroxide (Sigma-Aldrich) were added to the composition.
A composite plate was prepared in the same manner as in Example 3, and the composite plate comprised about 61 vol. % of the woven fabric. The applied cure cycle was the same as in Example 3. Postcure was also conducted at 190° C. during 60 minutes.
A composition was obtained in the same manner as in Example 1, except that 10 wt. % of a Poly(2-(acryloyloxymethyl)-2-ethylpropane-1,3-diyl diacrylate) (TMPTA, Sartomer SR 351) and 0.6 wt. % of a tert-butyl peroxide (Sigma-Aldrich) were added to the composition.
A composite plate was prepared in the same manner as in Example 3, and the composite plate comprised about 60 vol. % of the woven fabric. The applied cure cycle was the same as in Example 3. Postcure was also conducted at 190° C. during 60 minutes.
A composition was obtained in the same manner as in Example 1, except that 10 wt. % of a Tricyclo[5.2.1.02,6]decane-3,3-diylbis(methylene) bis(2-methylacrylate) (TCDDMDMA, Sartomer SR 834) and 0.6 wt. % of a tert-butyl peroxide (Sigma-Aldrich) were added to the composition.
A composite plate was prepared in the same manner as in Example 3, and the composite plate comprised about 60 vol. % of the woven fabric. The applied cure cycle was the same as in Example 3. Postcure was also conducted at 190° C. during 60 minutes
A composition was obtained in the same manner as in Example 1, except that 10 wt. % of a Tricyclo[5.2.1.02,6]decanedimethanol diacrylate (TCDDMDA, Sartomer SR 833S) and 0.6 wt. % of a tert-butyl peroxide (Sigma-Aldrich) were added to the composition.
A composite plate was prepared in the same manner as in Example 3, and the composite plate comprised about 60 vol. % of the woven fabric. The applied cure cycle was the same as in Example 3. Postcure was also conducted at 190° C. during 60 minutes
A composition was obtained in the same manner as in Example 1, except that trimethyl propane trimethacrylate (TMPTMA) and the tert-butyl peroxide were not added to the composition.
A composite plate was prepared in the same manner as in Example 3, and the composite plate comprised about 60 vol. % of the woven fabric. The applied cure cycle was the same as in Example 3. Postcure was also conducted at 190° C. during 60 minutes.
A composition was obtained in the same manner as in Example 3, except that the glass fibers were obtained from PPG carrying a standard sizing (1383).
A composite plate was prepared in the same manner as in Example 3, and the composite plate comprised about 60 vol. % of the woven fabric. The applied cure cycle was the same as in Example 3. Postcure was also conducted at 190° C. during 60 minutes.
An Epikote 828 epoxy resin and diaminocyclohexane hardener composition was used as a matrix material in a composite plate.
The composite plate was prepared in the same manner as in Example 3, and the composite plate comprised about 60 vol. % of the woven fabric, the glass fibers of which were coated with a 1383 sizing, obtainable from PPG. The applied cure and postcure cycle were those advised for Epikote 828.
Table 10 represents the composition of the composite samples and results related to thermal resistance.
As can be seen in Table 10, all samples according to the invention show a glass transition temperature Tg above that of the reference sample (Comparative Experiment A). Peroxide content appears to determine the Tg values and the highest Tg of 260° C. was measured for the sample containing 3% of TBP. At the same time all samples in accordance with the invention, and particularly those containing 0.6-3% of peroxide, showed a good wettability, substantially independent from the TMPTMA loading and the post cure temperature.
The mechanical properties of composite samples according to Example 3 were compared with those of Comparative Experiments A, B and C (Table 11).
The obtained 3-point bending strengths show that a composite plate based on the composition of Example 3 shows the highest values, even higher than those obtained for the Epikote 828/3832 combination. Adhesion between the glass fibers and the matrix in these materials can be considered to be very good. The bending strength observed for the composite plate based on a composition of Comparative Experiment is very low, indicating a poor adhesion. This is due to the fact that the sizing composition on the glass fibers was not compatible with the PDCPD matrix.
The compression strength of the composites of Example 3 and of Comparative Experiment C does not differ significantly. The compression strength of the composites of Comparative Experiment A however is significantly lower. This confirms a significantly improved fibre-matrix adhesion of Example 1 composites, as compared to a Comparative Experiment A composite.
The results of drop weight impact tests with impact energies of 15 and 25 Joules show that the delamination damage in the epoxy laminates according to Comparative Experiment C is more severe for both impact energy levels. For the same impact energy, the measured delamination size is about 2 times larger for the epoxy laminate according to Comparative Experiment C than for the laminate in accordance with Example 3.
A central delaminated region is visible on the impact site. In the epoxy samples according to Comparative Experiment C this region is surrounded by matrix cracks. These are not visible in a laminate according to Example 3. Example 3 laminates do not show a lot of damage up to around 1% of strain, after which a limited amount of short localized transverse and longitudinal cracks are found to develop. Final failure is very localized and occurs by transverse fiber failure, accompanied by very limited delamination.
In the epoxy laminates of Comparative Experiment C however, after 0.5% of strain, a multitude of transverse matrix cracks can already be seen. The numbers of cracks increases rapidly and longitudinal cracks are found to develop between 1 and 2% strain. The first delamination occurs between 2 and 2.5% strain and are localized on the ‘cross-over’ points of the fibre bundles (as is normal in a woven laminate). Many delamination's are then formed, which coalesce and finally cause final failure by extensive delamination and fibre failure.
The noted difference in behavior is remarkable and confirms the high toughness of composite laminates according to the invention, and a good resistance against delamination.
Double cantilever beam tests were done to determine the mode I interlaminar fracture toughness GI. The results (
Various embodiments of the invention have been described in fulfillment of the various objects of the invention. It should be recognized that these embodiments are merely illustrative of the principles of the present invention. Numerous modifications and adaptations thereof will be readily apparent to those skilled in the art without departing from the spirit and scope of the present invention.
That which is claimed:
| Number | Date | Country | Kind |
|---|---|---|---|
| 14306252.9 | Aug 2014 | EP | regional |
This application claims priority to U.S. Provisional Patent Application Ser. No. 62/034,414, filed on Aug. 7, 2014, which is hereby incorporated by reference as though fully set forth herein. This application also claims priority to European Patent Application Serial No. 14306252.9, filed on Aug. 7, 2014, which is hereby incorporated by reference as though fully set forth herein.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2015/043922 | 8/6/2015 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 62034414 | Aug 2014 | US |