The present disclosure relates to a glass panel unit and a method for manufacturing the glass panel unit.
Patent Literature 1 discloses a multi-pane glazing unit which includes a pair of glass panes facing each other with a predetermined gap distance left between the glass panes and a method for manufacturing the same.
In the method for manufacturing the multi-pane glazing unit disclosed in Patent Literature 1, in a first melting step, the temperature is set at a temperature equal to or higher than a softening point of a glass frit which is used for a frit seal and boundary walls. This allows peripheral portions of the pair of glass panes to be sealed to form a space to be hermetically sealed. After a gas is exhausted from this space, a second melting step is performed to seal an exhaust port by heating the pair of glass panes and the glass frit.
The multi-pane glazing unit disclosed in Patent Literature 1 is provided with no through holes. For this reason, the multi-pane glazing unit is difficult to be mounted onto a stationary structure such as a building or a vehicle, and is also difficult to be provided with a handle, for example. Therefore, the multi-pane glazing unit of Patent Literature 1 is difficult to handle.
It is therefore an object of the present disclosure to provide a glass panel unit and a method for manufacturing the glass panel unit, both of which are designed to overcome the problem of poor handleability of known glass panel units with no through holes.
A glass panel unit according to an aspect of the present disclosure includes a first panel, a second panel, a seal, and a boundary wall. The first panel includes a first glass pane. The second panel includes a second glass pane and is arranged to face the first panel. The seal has a frame shape and hermetically bonds respective peripheral edge portions of the first panel and the second panel to create an internal space between the first panel and the second panel. The boundary wall hermetically bonds the first panel and the second panel together to partition the internal space into a first space as a hermetically sealed evacuated space and a second space spatially separated from the first space.
The first panel has a first through hole provided through a portion, corresponding to the second space, of the first panel. The second panel has a second through hole provided through a portion, corresponding to the second space and facing the first through hole, of the second panel.
A method for manufacturing a glass panel unit according to another aspect of the present disclosure includes a glue arrangement step, a glass composite producing step, an internal space forming step, an evacuation step, and an evacuated space forming step. The glue arrangement step includes arranging a hot glue on either a first panel or a second panel. The hot glue is to form a seal or a partition. The first panel includes a first glass pane and has a first through hole. The second panel includes a second glass pane and has a second through hole. The glass composite producing step includes producing a glass composite that includes the first panel, the second panel, and the hot glue by arranging the second panel with respect to the first panel such that the second panel faces the first panel with the first through hole aligned with the second through hole. The internal space forming step includes heating the glass composite to melt the hot glue and thereby form the seal and the partition. The seal has a frame shape and hermetically bonds respective peripheral edge portions of the first panel and the second panel to create an internal space between the first panel and the second panel. The partition hermetically bonds the first panel and the second panel together to partition the internal space into a first space and a second space. The partition has an exhaust path that allows the first space and the second space to communicate with each other. The first space is sealed except the exhaust path. The second space is spatially separated from the first space and communicates with the first through hole and the second through hole. The evacuation step includes evacuating the first space by exhausting a gas from the first space via the exhaust path. The evacuated space forming step includes sealing the first space by closing the exhaust path with the partition deformed while keeping the first space evacuated and thereby turning the first space into a hermetically sealed evacuated space.
A method for manufacturing a glass panel unit according to still another aspect of the present disclosure includes a glue arrangement step, a glass composite producing step, an internal space forming step, an evacuation step, an evacuated space forming step, and a through hole forming step. The glue arrangement step includes arranging a hot glue on either a first panel or a second panel. The hot glue is to form a seal or a partition. The first panel includes a first glass pane and has a first through hole. The second panel includes a second glass pane. The glass composite producing step includes producing a glass composite that includes the first panel, the second panel, and the hot glue by arranging the second panel with respect to the first panel such that the first panel and the second panel face each other. The internal space forming step includes heating the glass composite to melt the hot glue and thereby form the seal and the partition. The seal has a frame shape and hermetically bonds respective peripheral edge portions of the first panel and the second panel to create an internal space between the first panel and the second panel. The partition hermetically bonds the first panel and the second panel together to partition the internal space into a first space and a second space. The partition has an exhaust path that allows the first space and the second space to communicate with each other. The first space is sealed except the exhaust path. The second space is spatially separated from the first space. The evacuation step includes evacuating the first space by exhausting a gas from the first space via the exhaust path. The evacuated space forming step includes sealing the first space by closing the exhaust path with the partition deformed while keeping the first space evacuated and thereby turning the first space into a hermetically sealed evacuated space. The through hole forming step includes providing a second through hole through a portion, corresponding to the second space and facing the first through hole, of the second panel.
Embodiments of a glass panel unit and method for manufacturing the glass panel unit according to the present disclosure will now be described. Note that the embodiments to be described below are only exemplary ones of various embodiments of the present disclosure and should not be construed as limiting. Rather, the exemplary embodiments may be readily modified in various manners without departing from a true spirit and scope of the present disclosure.
The glass panel unit 10 includes a first panel 20, a second panel 30, a seal 40, boundary walls 42, and an evacuated space 50. In the first embodiment, the glass panel unit 10 further includes a gas adsorbent 60 and a plurality of the pillars 70.
The seal 40 has a frame shape and hermetically bonds respective peripheral edge portions of the first panel 20 and the second panel 30 to create an internal space 500 (including the evacuated space 50) between the first panel 20 and the second panel 30.
The boundary walls 42 hermetically bond the first panel 20 and the second panel 30 together to partition the internal space 500 into a first space 510 that is the hermetically sealed evacuated space 50 and second spaces 520, which are spatially separated from the first space 510.
The first panel 20 has first through holes 25 provided through portions, corresponding to the second spaces 520, of the first panel 20. The second panel 30 has second through holes 35 provided through portions, corresponding to the second spaces 520 and facing the first through holes 25, of the second panel 30. In the first embodiment, the boundary walls 42 surround the first through holes 25 and the second through holes 35 when viewed in the direction in which the first panel 20 and the second panel 30 face each other.
The (final product of the) glass panel unit 10 is obtained by subjecting an assembly 100 shown in
The assembly 100 includes the first panel 20, the second panel 30, a first part 410 of a hot glue, the internal space 500, second parts 420 of the hot glue, an exhaust path 600 that allows the first space and one of the second spaces to communicate with each other, an exhaust port 700, the gas adsorbent 60, and the plurality of pillars 70.
The first panel 20 includes a first glass pane 21 that defines a planar shape of the first panel 20 and a coating 22.
The first glass pane 21 is a rectangular flat plate and has a first surface (i.e., the lower surface in
The coating 22 is formed on the first surface of the first glass pane 21. The coating 22 may be an infrared reflective film, for example. Note that the coating 22 does not have to be an infrared reflective film but may also be a film with desired physical properties. Optionally, the first panel 20 may consist of the first glass pane 21 alone. In short, the first panel 20 includes the first glass pane 21 to say the least.
The second panel 30 includes a second glass pane 31 that defines the planar shape of the second panel 30. The second glass pane 31 is a rectangular flat plate and has a first surface (i.e., the upper surface in
The second glass pane 31 may have the same planar shape and planar dimensions as the first glass pane 21. That is to say, the second panel 30 has the same planar shape as the first panel 20. In addition, the second glass pane 31 has the same thickness as the first glass pane 21. Examples of materials for the second glass pane 31 include soda lime glass, high strain point glass, chemically tempered glass, alkali-free glass, quartz glass, Neoceram, and thermally tempered glass.
The second panel 30 consists of the second glass pane 31 only. That is to say, the second glass pane 31 is the second panel 30 itself. Optionally, the second panel 30 may have a coating on either surface thereof. The coating is a film having desired physical properties such as an infrared reflective film. In that case, the second panel 30 is made up of the second glass pane 31 and the coating. In short, the second panel 30 includes the second glass pane 31 to say the least.
The second panel 30 is arranged to face the first panel 20. Specifically, the first panel 20 and the second panel 30 are arranged such that the first surface of the first glass pane 21 and the first surface of the second glass pane 31 face each other and are parallel to each other.
The first part 410 of the hot glue is arranged between the first panel 20 and the second panel 30 to hermetically bond the first panel 20 and the second panel 30 together as shown in
The first part 410 is formed of a hot glue (i.e., a first hot glue having a first softening point). The first hot glue may be a glass frit, for example. The glass frit may be a low-melting glass frit, for example. Examples of the low-melting glass frits include bismuth-based glass frits, lead-based glass frits, and vanadium-based glass frits.
The first part 410 is arranged to form a rectangular frame shape in a plan view as shown in
The first panel 20 and the second panel 30 are hermetically bonded together via the first part 410 by once melting the first hot glue of the first part 410 at a predetermined temperature (first melting temperature) Tm1, which is equal to or higher than the first softening point.
The second parts 420 of the hot glue are arranged in the internal space 500. The second parts 420 are partitions for partitioning the internal space 500 into a first space 510 to be a hermetically sealed space (i.e., a space to define an evacuated space 50 by being hermetically sealed when the glass panel unit 10 is completed) and second spaces 520, one of which will be an exhaust space (i.e., a space communicating with the exhaust port 700). The second parts 420 are parts that will serve as the boundary walls 42. The second parts 420 are formed such that the first space 510 is larger than any of the second spaces 520.
The second parts 420 are formed of a hot glue (i.e., a second hot glue having a second softening point). The second hot glue may be a glass frit, for example. The glass frit may be a low-melting glass frit, for example. Examples of the low-melting glass frits include bismuth-based glass frits, lead-based glass frits, and vanadium-based glass frits. The second hot glue is the same as the first hot glue. The second softening point is equal to the first softening point.
The exhaust port 700 is a hole that allows one of the second spaces 520 to communicate with the external environment. The exhaust port 700 is used to exhaust a gas from the first space 510 via the second space 520 and the exhaust path 600. The exhaust port 700 is provided through the second panel 30 to allow the second space 520 to communicate with the external environment. Specifically, the exhaust port 700 is located at a corner portion of the second panel 30. Note that although the exhaust port 700 is provided through the second panel 30 in the first embodiment, the exhaust port 700 may be provided through the first panel 20. In the first embodiment, a second through hole 351 to be described later also serves as the exhaust port 700.
The gas adsorbent 60 is arranged in the first space 510. Specifically, the gas adsorbent 60 has an elongate shape and provided at a longitudinal end of the second panel 30 so as to extend along a shorter side of the second panel 30. That is to say, the gas adsorbent 60 is arranged at an end of the first space 510 (evacuated space 50). This may make the gas adsorbent 60 much less conspicuous. In addition, this also reduces the chances of the gas adsorbent 60 obstructing exhausting the gas from the first space 510.
The gas adsorbent 60 is used to adsorb unnecessary gases (such as a residual gas). The unnecessary gases are released from the first part 410 and the second parts 420 when the first part 410 and the second parts 420 are heated to the first melting temperature Tm1, for example.
The gas adsorbent 60 includes a getter. The getter is a material having the property of adsorbing molecules, of which the size is smaller than a predetermined size. The getter may be an evaporative getter, for example. The evaporative getter has the property of releasing the adsorbed molecules when heated to a predetermined temperature (activation temperature) or more. This allows, even if the adsorption ability of the evaporative getter has declined once, the evaporative getter to recover its adsorption ability by heating the evaporative getter to the activation temperature or more. The evaporative getter may be either zeolite or an ion-exchanged zeolite (e.g., zeolite exchanged with copper ions).
The gas adsorbent 60 includes a powder of this getter. Specifically, the gas adsorbent 60 is formed by applying a solution in which a powder of the getter is dispersed. This allows the gas adsorbent 60 to have a reduced size. In that case, the gas adsorbent 60 may still be arranged even in a narrow, evacuated space 50.
The plurality of pillars 70 is used to maintain a predetermined gap distance between the first panel 20 and the second panel 30. That is to say, the plurality of pillars 70 serves as a spacer for maintaining a desired gap distance between the first panel 20 and the second panel 30.
The plurality of pillars 70 are placed in the first space 510. Specifically, the pillars 70 are placed at respective intersections of a rectangular (or square) grid. The plurality of pillars 70 may have an interval of 2 cm, for example. However, this is only an example and should not be construed as limiting. Rather, the size, number, spacing, and placement pattern of the pillars 70 may be selected appropriately.
The pillars 70 are made of a transparent material in this embodiment. Alternatively, the pillars 70 may also be made of an opaque material as long as the size of the pillars 70 is sufficiently small. The material for the pillars 70 is selected such that the pillars 70 will not be deformed in the internal space forming step (to be described later). The material for the pillars 70 is selected so as to allow the pillars 70 to have a softening point (softening temperature) higher than the first softening point of the first hot glue and the second softening point of the second hot glue, for example.
In such an assembly 100, the first space 510 is turned into the evacuated space 50 by exhausting, at a predetermined temperature (exhaust temperature) Te, the gas from the first space 510 through a path made up of the exhaust path 600, one of the second spaces 520, and the exhaust port 700 and allowing the gas to be exhausted into the external environment. The exhaust temperature Te is set at a temperature higher than the getter activation temperature of the gas adsorbent 60. This enables not only exhausting the gas from the first space 510 but also letting the getter recover its adsorption ability at a time.
In addition, as shown in
The second parts 420 are deformed to close the exhaust path 600 as shown in
The (final product of the) glass panel unit 10 thus obtained includes the first panel 20, the second panel 30, the seal 40, the evacuated space 50, the second space 520, the gas adsorbent 60, and the plurality of pillars 70 as shown in
The evacuated space 50 is formed by exhausting the gas from the first space 510 through one of the second spaces 520 and the exhaust port 700 as described above. In other words, the evacuated space 50 is the first space 510, of which the degree of vacuum is equal to or less than a predetermined value. The predetermined value may be 0.1 Pa, for example. The evacuated space 50 is perfectly hermetically sealed by the first panel 20, the second panel 30, and the seal 40, and therefore, is separated from the second spaces 520 and the exhaust port 700.
The seal 40 not only surrounds the evacuated space 50 entirely but also hermetically bonds the first panel 20 and the second panel 30 together. The seal 40 includes the part 41 which has a frame shape and (spatially) separates the first space 510 from the external environment and the boundary walls 42 that separate the first space 510 from the second spaces 520. The boundary walls 42 are formed by deforming the second parts 420.
Next, a method for manufacturing the glass panel unit 10 according to the first embodiment will be described with reference to
A method for manufacturing the glass panel unit 10 according to the first embodiment includes at least a glue arrangement step, a glass composite producing step, an internal space forming step, an evacuation step, and an evacuated space forming step. The method may further include other process steps, which are optional ones. This method will now be described step by step sequentially.
In the first embodiment, first, a substrate forming step is performed although not shown. The substrate forming step is the process step of forming the first panel 20 and the second panel 30. Specifically, the substrate forming step includes making the first panel 20 and the second panel 30, for example. In addition, the substrate forming step may further include cleaning the first panel 20 and the second panel 30 as needed.
Next, the process step of providing first through holes 25, second through holes 35, and an exhaust port 700 (hereinafter referred to as an “exhaust port providing step”) is performed. This process step includes providing first through holes 25 through portions, corresponding to the second spaces 520, of the first panel 20. In the first embodiment, two first through holes 25, namely, one first through hole 251 and the other first through hole 252, are provided (see
Next, as shown in
In the first embodiment, one second part 4201 is formed to surround the second through hole 351 almost entirely (see
Optionally, the glue arrangement step may include calcining the respective materials for the first part 410 and the second parts 420 while drying these materials. For example, the glue arrangement step may include heating the second panel 30 on which the material for the first part 410 and the material for the second parts 420 are applied and may also include heating the first panel 20 along with the second panel 30. That is to say, the first panel 20 may be heated under the same condition as the second panel 30. This may reduce the difference in the degree of warpage between the first panel 20 and the second panel 30.
Subsequently, a pillar forming step is performed. Specifically, the pillar forming step includes forming a plurality of pillars 70 in advance and placing the plurality of pillars 70 at predetermined locations on the second panel 30 by using a chip mounter, for example. Optionally, the plurality of pillars 70 may be formed by photolithography and etching techniques. In that case, the plurality of pillars 70 may be made of a photocurable material, for example. Alternatively, the plurality of pillars 70 may also be formed by a known thin film forming technique.
Next, a gas adsorbent forming step is performed. Specifically, the gas adsorbent forming step includes forming the gas adsorbent 60 by applying a solution, in which a getter powder is dispersed, onto a predetermined location on the second panel 30 and drying the solution. Note that the glue arrangement step, the pillar forming step, and the gas adsorbent arrangement step may be formed in an arbitrary order.
Thereafter, the glass composite producing step is performed. The glass composite producing step is the process step of producing a glass composite by arranging the second panel 30 with respect to the first panel 20 such that the second panel 30 faces the first panel 20 with the first through holes 25 aligned with the second through holes 35 as shown in
The first panel 20 and the second panel 30 are arranged and laid one on top of the other such that the first surface of the first glass pane 21 and the first surface of the second glass pane 31 face each other and are parallel to each other. The hot glue comes into contact with the first panel 20 and the second panel 30, thus forming the glass composite.
Then, the internal space forming step is performed. The internal space forming step is the process step of heating the glass composite to melt the hot glue and thereby form the first part 410 that will serve as the seal 40 and the second parts 420 (partitions) that will be boundary walls 42. Specifically, the internal space forming step includes bonding the first panel 20 and the second panel 30 together to prepare the assembly 100. That is to say, the internal space forming step is the process step of hermetically bonding the first panel 20 and the second panel 30 together with the first part 410 and the second parts 420 (i.e., a bonding step).
The seal 40 is a frame-shaped member for hermetically bonding the respective peripheral edge portions of the first panel 20 and the second panel 30 to form the internal space 500 between the first panel 20 and the second panel 30. The first part 410 serves as the seal.
The second parts 420 (partitions) partition the internal space 500 into the first space 510 that is hermetically sealed except the exhaust path 600 and the second spaces 520 that are spatially separated from the first space 510 and communicate with the first through holes 25 and the second through holes 35. The second parts 420 hermetically bond the first panel 20 and the second panel 30 together. One second part 4201 has the exhaust path 600. The other second part 4202 has no exhaust paths but is a boundary wall 422 (42) that serves as a seal.
The internal space forming step includes once melting the first hot glue at a predetermined temperature (first melting temperature) Tm1 equal to or higher than the first softening point and thereby hermetically bonding the first panel 20 and the second panel 30 together. Specifically, the glass composite is arranged in a melting furnace and heated to the first melting temperature Tm1 for a predetermined period (first melting period) tm1.
The first melting temperature Tm1 and the first melting period tm1 are set such that the first panel 20 and the second panel 30 are hermetically bonded with the first part 410 and the second parts 420 but that the exhaust path 600 is not closed with one of the second parts 420. That is to say, the lower limit of the first melting temperature Tm1 is the first softening point, while the upper limit of the first melting temperature Tm1 is set such that the exhaust path 600 is not closed by that one of the second parts 420. For example, if the first softening point and the second softening point are 290° C., then the first melting temperature Tm1 is set at 300° C. Also, the first melting period tm1 may be 10 minutes, for example. Note that in the internal space forming step, a gas is released from the first part 410 and the second parts 420 but is adsorbed into the gas adsorbent 60.
In the internal space forming step, the first part 410 and second parts 420 yet to be softened of the glass composite soften and the first part 410 and second parts 420 thus softened bond the first panel 20 and the second panel 30 together. As a result, the assembly 100 shown in
Next, the evacuation step is performed. The evacuation step is the process step of evacuating the first space 510 by exhausting the gas from the first space 510. Specifically, the evacuation step is the process step of evacuating the first space 510 by exhausting, at a predetermined temperature (exhaust temperature) Te, the gas from the first space 510 via the exhaust path 600, one of the second spaces 520, and the exhaust port 700 (second through hole 351).
As shown in
The evacuation step includes exhausting the gas from the first space 510 at an exhaust temperature Te for a predetermined period (exhaust period) te through the exhaust path 600, the one of the second spaces 520, and the exhaust port 700.
The exhaust temperature Te is set at a temperature higher than the getter activation temperature (of 240° C., for example) of the gas adsorbent 60 but lower than the first softening point and the second softening point (of 290° C., for example). The exhaust temperature Te may be 250° C., for example.
This may prevent the first part 410 and the second parts 420 from being deformed. In addition, the getter of the gas adsorbent 60 is activated and the molecules (of a gas) that have been adsorbed into the getter are released from the getter. Then, the molecules (i.e., the gas) released from the getter are exhausted through the first space 510, the exhaust path 600, the one of the second spaces 520, and the exhaust port 700. Thus, in the internal space forming step, the gas adsorbent 60 recovers its adsorption ability.
The exhaust period te is set to create an evacuated space 50 with a desired degree of vacuum (e.g., a degree of vacuum of 0.1 Pa or less). The evacuation period te may be set 120 minutes, for example.
Optionally, the evacuation step may start being performed either after, or during, the internal space forming step, whichever is appropriate. In the latter case, the evacuation step is performed in parallel with the internal space forming step.
Next, the evacuated space forming step (sealing step) is performed. The evacuated space forming step is the process step of sealing the first space 510 by closing the exhaust path 600 with the partitions deformed while keeping the first space 510 evacuated and thereby turning the first space 510 into a hermetically sealed evacuated space 50.
Specifically, in the first embodiment, the evacuated space forming step is the process step of forming a boundary wall 421 (42) (see
In the first embodiment, the gas is continuously exhausted in the evacuated space forming step with the same vacuum pump as the one used in the evacuation step still used in the evacuated space forming step. However, this is only an example and should not be construed as limiting. Alternatively, the gas does not have to be exhausted continuously in the evacuated space forming step with the same vacuum pump as the one used in the evacuation step used continuously, as long as a desired degree of vacuum may be maintained.
In this manner, a glass panel unit 10 is obtained. The glass panel unit 10 has through holes (first through holes 25 and second through holes 35). Therefore, the glass panel unit 10 is easily mounted onto a stationary structure such as a building or a vehicle. Moreover, the glass panel unit 10 may be easily provided with, for example, a handle 900 as shown in
Next, a glass panel unit 10 according to a second embodiment will be described with reference to
In the second embodiment, the size and location of a gas adsorbent 60 are different from those of the gas adsorbent 60 described for the first embodiment. In the other respects, the second embodiment is the same as the first embodiment.
The gas adsorbents 60 are arranged around the second through hole 351.
Specifically, a total of four gas adsorbents 60 are provided around the second through hole 351 at regular intervals of 90 degrees. The gas adsorbents 60 are each placed in an associated one of recesses provided on the surface of the second panel 30. Note that the number of the gas adsorbents 60 to be provided around the second through hole 351 is not limited to any particular number. Alternatively, the gas adsorbents 60 may be arranged around the first through holes 25 (251, 252) or the second through hole 352.
If the glass panel unit 10 is mounted onto a stationary structure such as a building or a vehicle or if a handle, for example, is attached to the glass panel unit 10, a portion surrounding the first through holes 25 or the second through holes 35 is easily hidden by the stationary structure or the handle. In that case, arranging the gas adsorbents 60 around the first through holes 25 or the second through holes 35 makes the gas adsorbents 60 inconspicuous.
Next, some variations will be enumerated one after another.
In the embodiments described above, the glass panel unit 10 has a rectangular shape. However, this is only an example and should not be construed as limiting. Alternatively, the glass panel unit 10 may also have a circular, polygonal, or any other desired shape. That is to say, the first panel 20, the second panel 30, and the seal 40 do not have to be rectangular but may also have a circular, polygonal, or any other desired shape. Also, the respective shapes of the first panel 20, the second panel 30, the part 41 corresponding to the evacuated space 50, and the boundary walls 42 do not have to be the ones used in the embodiments described above but may also be any other shapes that allow a glass panel unit 10 of a desired shape to be obtained. Note that the shape and dimensions of the glass panel unit 10 may be determined according to the intended use of the glass panel unit 10.
Also, neither the first surface nor the second surface of the first glass pane 21 of the first panel 20 has to be a plane. Likewise, neither the first surface nor the second surface of the second glass pane 31 of the second panel 30 has to be a plane.
The first glass pane 21 of the first panel 20 and the second glass pane 31 of the second panel 30 do not have to have the same planar shape and planar dimensions. The first glass pane 21 and the second glass pane 31 do not have to have the same thickness, either. In addition, the first glass pane 21 and the second glass pane 31 do not have to be made of the same material, either.
Optionally, the first panel 20 may further include a coating having desired physical properties and formed on the second surface of the first glass pane 21. Alternatively, the first panel 20 may include no coating 22. That is to say, the first panel 20 may consist of the first glass pane 21 alone.
Optionally, the second panel 30 may further include a coating having desired physical properties. The coating may include, for example, at least one of a thin film formed on the first surface of the second glass pane 31 or a thin film formed on the second surface of the second glass pane 31. Examples of the coating include an infrared reflective film and an ultraviolet reflective film, both of which reflect light having a particular wavelength.
In the embodiment described above, the internal space 500 is partitioned into a single first space 510 and a single second space 520. However, this is only an example and should not be construed as limiting. Alternatively, the internal space 500 may also be partitioned into one or more first spaces 510 and one or more second spaces 520.
In the embodiment described above, the second hot glue is the same as the first hot glue and the second softening point is equal to the first softening point. However, this is only an example and should not be construed as limiting. Alternatively, the second hot glue may also be a different material from the first hot glue. For example, the second hot glue may have a second softening point which is different from the first softening point of the first hot glue.
Furthermore, the first hot glue and the second hot glue do not have to be a glass frit but may also be a low-melting metal or a hot-melt adhesive, for example.
In the substrate forming step, the second through holes 35 do not have to be provided through the second panel 30. In that case, a through hole forming step is performed after the evacuated space forming step. The through hole forming step is the process step of providing the second through holes 35 through portions, corresponding to the second spaces 520 and facing the first through holes 25, of the second panel 30.
The glass panel unit 10 with the first through holes 25 and the second through holes 35 is applicable for use in glass windows for stationary structures such as buildings, electrical equipment including refrigerator showcases for general consumers and storekeepers, and automobiles and other vehicles in the field of mobility.
As can be seen from the foregoing description of exemplary embodiments and their variations, a glass panel unit (10) according to a first aspect of the present disclosure includes a first panel (20), a second panel (30), a seal (40), and a boundary wall (42). The first panel (20) includes a first glass pane (21). The second panel (30) includes a second glass pane (31) and is arranged to face the first panel (20). The seal (40) has a frame shape and hermetically bonds respective peripheral edge portions of the first panel (20) and the second panel (30) to create an internal space (500) between the first panel (20) and the second panel (30). The boundary wall (42) hermetically bonds the first panel (20) and the second panel (30) together to partition the internal space (500) into a first space (510) as a hermetically sealed evacuated space (50) and a second space (520) spatially separated from the first space (510). The first panel (20) has a first through hole (25) provided through a portion, corresponding to the second space (520), of the first panel (20). The second panel (30) has a second through hole (35) provided through a portion, corresponding to the second space (520) and facing the first through hole (25), of the second panel (30).
The glass panel unit (10) according to the first aspect may overcome the problem of poor handleability of known glass panel units with no through holes.
A glass panel unit (10) according to a second aspect of the present disclosure may be implemented in conjunction with the first aspect. In the glass panel unit (10) according to the second aspect, the boundary wall (42) surrounds the first through hole (25) and the second through hole (35) when viewed in a direction in which the first panel (20) and the second panel (30) face each other.
The glass panel unit (10) according to the second aspect allows forming the boundary wall (42) easily.
A method for manufacturing a glass panel unit (10) according to a third aspect of the present disclosure includes a glue arrangement step, a glass composite producing step, an internal space (500) forming step, an evacuation step, and an evacuated space (50) forming step. The glue arrangement step includes arranging a hot glue on either a first panel (20) or a second panel (30). The hot glue is to form a seal (40) or a partition. The first panel (20) includes a first glass pane (21) and has a first through hole (25). The second panel (30) includes a second glass pane (31) and has a second through hole (35). The glass composite producing step includes producing a glass composite that includes the first panel (20), the second panel (30), and the hot glue by arranging the second panel (30) with respect to the first panel (20) such that the second panel (30) faces the first panel (20) with the first through hole (25) aligned with the second through hole (35). The internal space (500) forming step includes heating the glass composite to melt the hot glue and thereby form the seal (40) and the partition. The seal (40) has a frame shape and hermetically bonds respective peripheral edge portions of the first panel (20) and the second panel (30) to create an internal space (500) between the first panel (20) and the second panel (30). The partition hermetically bonds the first panel (20) and the second panel (30) together to partition the internal space (500) into a first space (510) and a second space (520). The partition has an exhaust path that allows the first space (510) and the second space (520) to communicate with each other. The first space (510) is sealed except the exhaust path. The second space (520) is spatially separated from the first space (510) and communicates with the first through hole (25) and the second through hole (35). The evacuation step includes evacuating the first space (510) by exhausting a gas from the first space (510) via the exhaust path. The evacuated space (50) forming step includes sealing the first space (510) by closing the exhaust path with the partition deformed while keeping the first space (510) evacuated and thereby turning the first space (510) into a hermetically sealed evacuated space (50).
The method for manufacturing a glass panel unit (10) according to the third aspect may overcome the problem to be caused by the absence of through holes from the glass panel unit (10) manufactured.
A method for manufacturing a glass panel unit (10) according to a fourth aspect of the present disclosure may be implemented in conjunction with the third aspect. In the method for manufacturing a glass panel unit (10) according to the fourth aspect, the evacuation step includes using: an exhaust port portion (800) to be hermetically connected to one through hole selected from the first through hole (25) and the second through hole (35); a closing member (810) to close the other through hole out of the first through hole (25) and the second through hole (35); and a clip (820) to clamp the exhaust port portion (800) and the closing member (810) such that the exhaust port portion (800) and the closing member (810) are close to each other.
The method for manufacturing a glass panel unit (10) according to the fourth aspect allows the evacuation step to be performed easily.
A method for manufacturing a glass panel unit (10) according to a fifth aspect of the present disclosure includes a glue arrangement step, a glass composite producing step, an internal space (500) forming step, an evacuation step, an evacuated space (50) forming step, and a through hole forming step. The glue arrangement step includes arranging a hot glue on either a first panel (20) or a second panel (30). The hot glue is to form a seal (40) or a partition. The first panel (20) includes a first glass pane (21) and has a first through hole (25). The second panel (30) includes a second glass pane (31). The glass composite producing step includes producing a glass composite that includes the first panel (20), the second panel (30), and the hot glue by arranging the second panel (30) with respect to the first panel (20) such that the first panel (20) and the second panel (30) face each other. The internal space (500) forming step includes heating the glass composite to melt the hot glue and thereby form the seal (40) and the partition. The seal (40) has a frame shape and hermetically bonds respective peripheral edge portions of the first panel (20) and the second panel (30) to create an internal space (500) between the first panel (20) and the second panel (30). The partition hermetically bonds the first panel (20) and the second panel (30) together to partition the internal space (500) into a first space (510) and a second space (520). The partition has an exhaust path that allows the first space (510) and the second space (520) to communicate with each other. The first space (510) is sealed except the exhaust path (600). The second space (520) is spatially separated from the first space (510). The evacuation step includes evacuating the first space (510) by exhausting a gas from the first space (510) via the exhaust path. The evacuated space (50) forming step includes sealing the first space (510) by closing the exhaust path with the partition deformed while keeping the first space (510) evacuated and thereby turning the first space (510) into a hermetically sealed evacuated space (50). The through hole forming step includes providing a second through hole (35) through a portion, corresponding to the second space (520) and facing the first through hole (25), of the second panel (30).
The method for manufacturing a glass panel unit (10) according to the fifth aspect may overcome the problem to be caused by the absence of through holes from the glass panel unit (10) manufactured.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2019-068231 | Mar 2019 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2020/009300 | 3/5/2020 | WO | 00 |