This invention relates to a glass sealing structure of electric lamps, more particularly to a hermetic sealing between the internal chamber of the lamps and the environment. The invention also relates to lamps manufactured with such sealing.
High electric resistance lead glasses are used to manufacture parts for hermetic sealing and electric insulation in electric lamps. Lead-free glasses have recently replaced lead glasses due to environment protection requirements.
U.S. Pat. No. 5,391,523 discloses several lamp constructions using high electric resistance lead-free glass compositions with specified SiO2 matrix as sealing glass. The sealing parts and the stem or mount of lamps are made of the lead-free glass compositions. In case of wedge-base lamps, the entire bulb or envelope is made of lead-free glass composition.
U.S. Pat. No. 3,723,790 discloses electric articles such as electric lamps and electric tubes having dumet current conductors and a glass enclosure sealed to the conductors. Dumet wire is a known type of wire employed in the production of electrical conductors, composed of a nickel-iron alloy core portion and a copper coating on external portion. The copper coating is designed to absorb stresses that may develop during the sealing operation. There are different dumet metals, depending on the particular composition of the core alloy. The glass enclosure and the stem are composed entirely of a specified electric sealing glass composition and may be composed of a soda lime glass envelope joined to the conductors with the electric sealing glass stem as intermediate components.
In the constructions described in the patents above, the entire volume of the sealing glass part such as the entire envelope or the stem was made of expensive high electric resistance glass composition. This feature involves a glass composition of high lead content or equivalent insulating lead-free glasses, but both are considerably more expensive than the common soda lime glass.
There is a particular need for decreasing the cost of material used for manufacturing glass parts of electric lamps. At the same time high electric resistance between the lead-in wires is required to be maintained.
In an exemplary embodiment of the invention, a glass sealing for electric lamps is comprised of a sealing glass body, lead-in wires passing through the sealing glass body, a high electric resistance glass layer encapsulating each of the lead-in wires and separating them from the sealing glass body. The high electric resistance glass layer is joined both with the lead-in wires and with the sealing glass body in a manner providing hermetic enclosure of the glass sealing.
In an exemplary embodiment of another aspect of the invention, an electric lamp is comprised of an envelope, a stem and a glass sealing determined above. The sealing glass body is integral with the stem of the electric lamp and the stem is joined to the envelope.
In an exemplary embodiment of a further aspect of the invention, an electric lamp is comprised of an envelope and a glass sealing determined above. The sealing glass body is integral with the envelope of the electric lamp.
The glass sealing proposed has several advantages over the prior art. It was found that only a thin layer of expensive high electric resistance glass material is required for suitable electric insulation between the lead-in wires of the lamps. A thin layer of high electric resistance glass allows the use of low cost glass compositions as sealing glass material in lamp constructions consisting of soft glasses. The required volume of the low cost sealing glass is much higher than that of the high electric resistance glass of thin layer. In case of lamps, in which the glass part is made of one glass composition, such as wedge-base lamps, the glass part can be made of low cost glass, such as soda lime glass, instead of expensive lead-free or lead glass materials. In lamps consisting of envelope and stem, both the envelope and the stem can be made of low cost glass material such as soda lime glass.
The invention will now be described with reference to enclosed drawings where:
In the context of this invention, the term glass sealing is used as a part of a lamp structure for hermetic enclosure between atmospheric environment and lamp internal chamber. The glass sealing can be connected to a glass envelope of a lamp or an envelope of a lamp can be formed integrally with the glass sealing.
In electric lamps consisting of soft glasses such as incandescent lamps, fluorescent lamps, low wattage high intensity discharge lamps and wedge-base lamps, lead glass or high electric resistance lead-free glass is used to make parts, such as pinching or sealing, which encapsulate the lead-in wires.
Essential reason for the application of these high electric resistance glasses is to provide proper glass-to-metal sealing that prohibits air leakage into the lamp. The electric potential difference between the lead-in wires causes ion movement, primarily alkali ions movement, which results in composition change by electrolysis on the metal surface of the lead-in wires and in the surrounding glass area. The specific thermal expansion altered by the change of composition results in expansion mismatch between the lead-in wires and the glass. The expansion mismatch leads to cracks and air leakage in the lamps. Alkali ion movement appears particularly in lamps driven by DC voltage, but this ion movement also appears in lamps, to which AC voltage is applied. Electric insulation property of the material surrounding the lead-in wires is required to decrease ion movement. For the electric insulation and the proper glass-to-metal sealing, lead glass or high electric resistance lead-free glass is used.
Turning now to
The thickness of the glass layer 6 and its thermal expansion coefficient are selected or adjusted so that a crack-free cooperation of the sealing body 4 and the glass layer 6 is accomplished. For this purpose, the thermal expansion coefficient of the glass layer 6 is in the range of 85-115 10−7 1/K. The crack-free cooperation may be more likely if the thermal expansion coefficient is in the range of 90-110 10−7 1/K.
The high electric resistance glass layer 6 can be deposited on the lead-in wires 5 or it can be pulled over the lead-in wires 5 in the form of low diameter tube. The thickness of the tube wall, which is the thickness of the high electric resistance glass layer 6, can be in the range of 100-500 microns for example. In order to provide a sufficient electric resistance in the entire region around the lead-in wires, the deposited covering layer has to be at least 10 microns thick. The deposited glass layer 6 or pulled over tube is melted to the lead-in wires 5 and to the sealing glass body 4 both for providing hermetic enclosure of the glass sealing 1.
The material for high electric resistance glass layer 6 can be selected from a wide range of glass materials, preferably of SiO2 matrix lead-free glass material.
Dumet is a structured material composition frequently used for configuring lead-in wires 5. The dumet has a structure of FeNi core, Cu layer and Cu2O layer. In special cases, a Ni layer is additionally applied to the surface of the dumet. In one embodiment of the invention, the high electric resistance glass layer 6 is deposited on the surface of dumet lead-in wires 5.
Depending on manufacturing and working conditions of electric lamps, the sealing glass body 4 can be made of several different glass materials. For most of the lamp constructions, soda lime glass is an economic and well-known selection for the material of the sealing glass body 4.
In the prior art, sealing part of an envelope or a stem of a lamp plays dual role: hermetic sealing and electric insulation. In the embodiments of this invention, an envelope or a stem as sealing glass body 4 has only one role: hermetic sealing. The sealing glass body 4 serves as hermetic sealing of the lamp, while the high electric resistance glass layer 6 around the lead-in wires 5 provide both electric insulation and hermetic sealing.
An incandescent automotive lamp built up with a stem made of the glass sealing can be seen in the
In
A festoon lamp as a further embodiment of the invention is shown in
As a further possible embodiment of the invention, a commonly used incandescent lamp of
The invention can be adapted for any other kind of lamps having lead-in wires. The economic aspect results in a much less quantity of expensive special glass to be used for manufacturing and this is a substantial advantage in any field of the lighting industry.