The present invention generally relates to hard disk drives and, in particular, relates to glass substrates for hard disk drives and methods of annealing the same.
Glass substrates are frequently used in the fabrication of information storage media, such as magnetic recording media for hard disk drives. Glass substrates enjoy a number of advantages when compared with substrates formed from aluminum alloys, which may be prone to deformation.
Because the information storage media may be rotated at high speeds, the substrate on which it is disposed must have sufficient mechanical strength to withstand the forces generated by this rotation. One approach to strengthening glass substrates involves chemically strengthening the glass thereof, by exchanging sodium ions near the surface of the substrate with larger potassium ions in order to provide a compressive stress, which offsets tensile stress and improves the toughness of the glass.
This chemical strengthening, however, does not address a fundamental limitation to the mechanical strength of glass, which arises due to cracks formed in the glass when the substrate is manufactured (e.g., cracks formed by scribing the inner and outer diameter of an annuls-shaped substrate). When stressed, these cracks can initiate a breakage that can propagate through a large region of the substrate, causing catastrophic failure of the information storage medium formed thereon. Such cracks are depicted in the glass substrate 101 illustrated in
Various embodiments of the present invention solve the foregoing problem by providing methods for forming glass substrates with greater resistance to breakage caused by cracks.
According to one embodiment of the present invention, a method for forming a glass substrate comprises the steps of forming a glass blank with opposing substantially planar surfaces and at least one edge, coating the glass blank in silica-alumina nanoparticles, the silica-alumina nanoparticles comprising an inner core of silica with an outer shell of alumina, annealing the coated glass blank to form a conformal coating of silica-alumina around the glass blank, and polishing the coated glass blank to remove the conformal coating of silica-alumina from the opposing substantially planar surfaces thereof.
According to another embodiment of the present invention, a method for forming a plurality of glass substrates comprises the steps of forming a plurality of glass blanks, each glass blank having opposing substantially planar surfaces and at least one edge, coating the plurality of glass blanks in silica-alumina nanoparticles, the silica-alumina nanoparticles comprising an inner core of silica with an outer shell of alumina, stacking the plurality of coated glass blanks directly upon one another, annealing the stacked plurality of coated glass blanks to form a conformal coating of silica-alumina around each glass blank, and polishing each glass blank to remove the conformal coating of silica-alumina from the opposing substantially planar surfaces thereof.
According to yet another embodiment of the present invention, a glass substrate comprises a glass structure with opposing substantially planar surfaces and at least one edge, wherein the at least one edge is coated with a conformal layer of silica-alumina nanoparticles, the silica-alumina nanoparticles comprising an inner core of silica with an outer shell of alumina.
It is to be understood that both the foregoing summary of the invention and the following detailed description are exemplary and explanatory and are intended to provide further explanation of the invention as claimed.
The accompanying drawings, which are included to provide further understanding of the invention and are incorporated in and constitute a part of this specification, illustrate embodiments of the invention and together with the description serve to explain the principles of the invention. In the drawings:
In the following detailed description, numerous specific details are set forth to provide a full understanding of the present invention. It will be apparent, however, to one ordinarily skilled in the art that the present invention may be practiced without some of these specific details. In other instances, well-known structures and techniques have not been shown in detail to avoid unnecessarily obscuring the present invention.
One approach to strengthening glass substrates involves coating the surfaces thereof with silica particles. Since the surface of the glass substrate is also primarily silica, both the particles and the surface have the same charge (i.e., a negative charge). Accordingly, evenly dispersing the particles over the surface requires a mechanical dispersion technique, which may not provide an acceptable level of smoothness and/or evenness.
Therefore, in accordance with one aspect of the subject disclosure, positively-charged nanoparticles are used to coat a glass substrate. Because of the different charge between the nanoparticles and the surface of the glass substrate, the dispersion of the nanoparticles is easily accomplished by, for example, dipping a glass substrate in a solution/colloidal suspension of the positively-charged nanoparticles.
According to one aspect of the subject disclosure, silica-alumina nanoparticles may be used to coat the surfaces of a glass substrate. According to one aspect of the subject disclosure, nanoparticles comprising inner core of silica with an outer shell of alumina may be used in this application. For example, one such commercially-available colloidal suspension of silica-alumina nanoparticles is the LUDOX® CL colloidal suspension of SiO2 and Al2O3 manufactured by W.R. Grace & Co. Using such positively-charged nanoparticles with a diameter of less than about 50 nm (or even less than about 20 nm) allows the nanoparticles to more easily penetrate into micro-cracks in the glass substrate (e.g., without any additional mechanical dispersion).
While commercially-available preparations of silica-alumina nanoparticles are available in a variety of concentrations, it may be preferable to dilute the solutions to a weight concentration of between about 0.01 weight percent and 0.30 weight percent silica-alumina nanoparticles before immersing a glass substrate therein, according to one aspect of the subject disclosure. According to another aspect of the subject disclosure, a colloidal suspension of silica-alumina nanoparticles may be diluted to a concentration of between about 0.08 weight percent and 0.10 weight percent silica-alumina nanoparticles before soaking a glass substrate therein. These ranges of concentration has been determined to facilitate better crack penetration and more even coatings. The soaking operation may be timed to provide a conformal layer of silica-alumina nanoparticles less than about 1 micron thick around the glass substrate.
To adhere the nanoparticles to the substrate, an annealing step may be performed after dispersing the particles on the substrate surface, in accordance with one aspect of the subject disclosure. The high temperature of the annealing process helps to adhere the nanoparticles to the surfaces of the glass substrate and to seal the micro cracks therein. According to one aspect of the subject disclosure, the annealing step may comprise heating the coated substrate to a temperature at or above a glass transition temperature thereof, for a period ranging from about 0.5 to about 10 hours. For example, for a borosilicate glass substrate with a glass transition temperature of 525° C., the annealing step may involve soaking the substrate at an annealing temperature of 560° C. for a period of 5 to 8 hours.
Because it may not be desirable to have alumina particles, such as the nuclei of the silica-alumina nanoparticles, on a planar surface of the glass substrate (e.g., as those surfaces may be subsequently coated with one or more layers for magnetic recording), in accordance with one aspect of the subject disclosure, a polishing process may be performed after annealing to remove the nanoparticles from the opposing surfaces of the substrate. The nanoparticles on the inner and outer edges, however, remain on the glass substrate, providing a conformal coating less than about 1 micron thick that penetrates into any micro-cracks on these edges. The coating may remain on the substrate even into a final product (e.g., a recording media) without any adverse effect on the properties thereof. For example, in accordance with one aspect of the subject disclosure, a magnetic recording media comprising the glass substrate thus produced may enjoy improved strength (e.g., due to the coating on the inner and outer edges thereof) without any degradation of the magnetic properties thereof, and without compromising the function of a hard disk drive comprising the magnetic recording media.
According to one aspect of the subject disclosure, the step of polishing the opposing substantially planar surfaces of the glass substrate may comprise removing between about 5 and 50 microns of material from each of the opposing surfaces (e.g., removing both the conformal coating of nanoparticles and some portion of the substrate material).
One benefit of deferring the polishing of the planar surfaces of the substrate until after the annealing step is that the layer of nanoparticles on the planar surfaces prevent substrates from sticking to one another when stacked, without the need for a separator between them. This effect can be exploited to allow a stack of coated substrates to be annealed in a single operation. As an additional benefit, the pressure exerted by stacked substrates upon one another during annealing may beneficially increase the flatness thereof. In this regard, in accordance with one aspect of the subject disclosure, additional weight may also be placed on top of one or more substrates during the annealing process to further increase the flatness thereof. In this regard,
The description of the invention is provided to enable any person skilled in the art to practice the various embodiments described herein. While the present invention has been particularly described with reference to the various figures and embodiments, it should be understood that these are for illustration purposes only and should not be taken as limiting the scope of the invention.
There may be many other ways to implement the invention. Various functions and elements described herein may be partitioned differently from those shown without departing from the spirit and scope of the invention. Various modifications to these embodiments will be readily apparent to those skilled in the art, and generic principles defined herein may be applied to other embodiments. Thus, many changes and modifications may be made to the invention, by one having ordinary skill in the art, without departing from the spirit and scope of the invention.
A reference to an element in the singular is not intended to mean “one and only one” unless specifically stated, but rather “one or more.” The term “some” refers to one or more. Underlined and/or italicized headings and subheadings are used for convenience only, do not limit the invention, and are not referred to in connection with the interpretation of the description of the invention. All structural and functional equivalents to the elements of the various embodiments of the invention described throughout this disclosure that are known or later come to be known to those of ordinary skill in the art are expressly incorporated herein by reference and intended to be encompassed by the invention. Moreover, nothing disclosed herein is intended to be dedicated to the public regardless of whether such disclosure is explicitly recited in the above description.
Number | Name | Date | Kind |
---|---|---|---|
5576282 | Miracle et al. | Nov 1996 | A |
5654057 | Kitayama et al. | Aug 1997 | A |
5681609 | Kitayama et al. | Oct 1997 | A |
5686014 | Baillely et al. | Nov 1997 | A |
5733622 | Starcke et al. | Mar 1998 | A |
5910371 | Francel et al. | Jun 1999 | A |
5916656 | Kitayama et al. | Jun 1999 | A |
6363599 | Bajorek | Apr 2002 | B1 |
6374640 | Fotheringham et al. | Apr 2002 | B1 |
6395634 | Miyamoto | May 2002 | B1 |
6801397 | Yamamoto et al. | Oct 2004 | B2 |
6908870 | Kawai | Jun 2005 | B2 |
7001669 | Lu et al. | Feb 2006 | B2 |
7040953 | Matsuno et al. | May 2006 | B2 |
20010029752 | Natan et al. | Oct 2001 | A1 |
20020022682 | Wallace et al. | Feb 2002 | A1 |
20020176982 | Rohrbaugh et al. | Nov 2002 | A1 |
20030077982 | Takizawa | Apr 2003 | A1 |
20030096078 | Horisaka et al. | May 2003 | A1 |
20030228415 | Bi et al. | Dec 2003 | A1 |
20040092396 | Glazer et al. | May 2004 | A1 |
20050096210 | Kawai | May 2005 | A1 |
20050223744 | Horisaka et al. | Oct 2005 | A1 |
20060286550 | Montagu et al. | Dec 2006 | A1 |
20070039353 | Kamiya | Feb 2007 | A1 |
20070104922 | Zhai et al. | May 2007 | A1 |
20070142498 | Brennan et al. | Jun 2007 | A1 |
20070178305 | Papazoglou | Aug 2007 | A1 |
20070238174 | Cousins et al. | Oct 2007 | A1 |
20080028986 | Futterer et al. | Feb 2008 | A1 |
20080043301 | Lewis | Feb 2008 | A1 |
20080085412 | Ortiz | Apr 2008 | A1 |
20090057661 | Siddiqui et al. | Mar 2009 | A1 |
20090098366 | Smoukov et al. | Apr 2009 | A1 |
20090104369 | Rajala et al. | Apr 2009 | A1 |
20090252993 | Kawai et al. | Oct 2009 | A1 |
Number | Date | Country |
---|---|---|
H02-301017 | Dec 1990 | JP |
Number | Date | Country | |
---|---|---|---|
20110104427 A1 | May 2011 | US |