Patent Application
20250205386
This patent application claims the benefit and priority of Chinese Patent Application No. 202311782845.6, filed with the China National Intellectual Property Administration on Dec. 22, 2023, the disclosure of which is incorporated by reference herein in its entirety as part of the present application.
The present disclosure belongs to the technical field of biomaterials and hydrogels, and in particular relates to a glucogalactan-based injectable subcutaneous filling hydrogel, and a preparation method and use thereof.
Tumor resection, traumatic injury, lipoatrophy, congenital defects, and aging can lead to loss of the normal structure of soft tissues such as subcutaneous fat, collagen, and muscle. In order to repair defects, many artificial fillers have been widely used in clinical soft tissue filling.
An ideal soft tissue filler should have desirable biocompatibility, flexibility, and biostability. Polysaccharide-based hydrogels are abundant in natural sources. Hyaluronic acid is an important component of the natural extracellular matrix and dominates the health and cosmetics market. However, the hyaluronic acid is easily degraded in vivo due to hyaluronidase. Existing commercial hyaluronic acid-based hydrogels are made by combining the hyaluronic acid with a cross-linking agent under certain conditions. Although such hydrogels have a longer degradation time, there is still a demand of repeated injection within one year, increasing the pain of patients.
The applicant has disclosed in patent CN111286466A a strain of Agrobacterium and a method for producing and preparing an anti-inflammatory exopolysaccharide produced by the Agrobacterium. At the same time, a paper published by the applicant has provided structural analysis of the exopolysaccharide (Anti-tumor activity and immunogenicity of a succinoglycan riclin. Carbohydr Polym. 2021 Mar. 1; 255:117370.). Glucogalactan is a polysaccharide prepared by treating the exopolysaccharide with alkali heat and removing a succinyl group.
In order to solve the problems in the prior art, an objective of the present disclosure is to provide an injectable polysaccharide hydrogel with high safety, excellent mechanical properties, and desirable biocompatibility to meet the demands of subcutaneous filling.
To achieve the above objective, the present disclosure provides the following technical solutions:
The present disclosure provides a preparation method of a glucogalactan-based injectable subcutaneous filling hydrogel, including the following steps:
Further, the succinoglycan Riclin solution has a concentration of 0.5 wt % to 2 wt %, NaOH has a concentration of 0.1 wt %, and the treating is conducted at 105° C. for 10 min in step (1).
Further, the transparent glucogalactan solution has a concentration of 8 wt % to 10 wt % and the NaOH aqueous solution has a concentration of 0.1 M to 0.2 M in step (2).
Further, poly (ethylene glycol) diglycidyl ether (PEGDE) is used as the cross-linking agent, and the transparent glucogalactan solution and the cross-linking agent are at a volume ratio of 1:0.036 to 1:0.108 in step (3).
Further, the cross-linking in step (3) is conducted at 30° C. to 60° C. for 8 h to 16 h.
Further, the acidic solution in step (4) is an HCl solution of 0.1 M to 0.2 M.
Further, the neutral glucogalactan hydrogel in step (4) has 20 mg/ml of the glucogalactan.
Further, the sterilizing in step (5) is conducted at 121° C. for 20 min.
Another objective of the present disclosure is to provide a glucogalactan-based injectable subcutaneous filling hydrogel that is maintained subcutaneously for a long time.
Another objective of the present disclosure is to provide use of the glucogalactan hydrogel in preparation of a subcutaneous soft tissue filling material or a joint cavity lubricating fluid.
The present disclosure has the following beneficial effects.
Polyethylene glycol (PEG) is a non-toxic and FDA-approved amphiphilic polyether compound. PEG with a low molecular weight (Mw<1,000) can be degraded and cleared in vivo. A novel polysaccharide-based hydrogel is prepared by cross-linking of PEGDE and glucogalactan under alkaline conditions. The results show that glucogalactan hydrogel is a promising biomaterial for soft tissue augmentation.
(1) The present disclosure provides a novel microbial polysaccharide-based chemically cross-linked injectable hydrogel. The microbial polysaccharide-based hydrogel has desirable biocompatibility, superior mechanical properties, and long in vivo duration, showing a great potential in cosmetic medicine.
(2) In the present disclosure, the preparation method has the advantages of simple process, mild reaction conditions, and easy synthesis, and is suitable for popularization and use.
Unless otherwise specified, all technical and scientific terms used in the present disclosure have the same meaning as commonly understood by one of ordinary skill in the technical field to which the present disclosure belongs. Unless otherwise specified, the reagents or materials used in the following examples can be purchased commercially or synthesized by referring to existing methods.
The foregoing is detailed description of the preferred specific examples of the present disclosure. Apparently, the described examples are merely a part rather than all of the examples of the present disclosure. It should be understood that a person of ordinary skill in the art can make various modifications and variations according to the concept of the present disclosure without creative efforts. Therefore, all technical solutions that a person skilled in the art can obtain based on the prior art through logical analysis, reasoning, or finite experiments according to the concept of the present disclosure shall fall within the protection scope defined by the appended claims.
(1) A succinoglycan Riclin powder was dissolved in pure water to obtain a Riclin polysaccharide solution with a concentration of 0.5 wt %.
(2) 0.1 wt % NaOH was added into the Riclin polysaccharide solution, mixed well by stirring, and reacted at 105° C. for 10 min.
(3) A reacted polysaccharide solution was filtered with a 1 μm fiber membrane, a pH value of an obtained filtrate to neutral, and alcohol was added to obtain a polysaccharide precipitate, namely the glucogalactan; where the glucogalactan had a structural formula as follows:
n is 1,000 to 2,000.
(1) The glucogalactan polysaccharide powder prepared in Example 1 was dissolved in a 0.1 M NaOH aqueous solution at a room temperature to obtain a transparent solution with a sugar concentration of 8 wt %, which was a glucogalactan solution.
(2) A certain amount of PEGDE cross-linking agent was added into the glucogalactan solution, such that the polysaccharide solution and the cross-linking agent were at a volume ratio of 1:0.036, 1:0.072, and 1:0.108. A resulting mixture was mixed uniformly by stirring at a room temperature, and a glucogalactan hydrogel was obtained by cross-linking at 40° C. for 8 h.
(3) The glucogalactan hydrogel was neutralized with a 0.1 M HCl solution, and then washed with neutral deionized water 8 to 15 times to obtain a neutral glucogalactan hydrogel with a glucogalactan content of 20 mg/mL.
(4) The neutral glucogalactan hydrogel was sterilized at 121° C. under high pressure for 20 min to obtain a sterile neutral glucogalactan hydrogel.
According to the above preparation method, 8 wt % of glucogalactan polysaccharide solution was cross-linked with PEGDE at volume ratios of 1:0.036, 1:0.072, and 1:0.108, and then R-0.5 hydrogel, R-1.0 hydrogel, and R-1.5 hydrogel with a glucogalactan polysaccharide content of 20 mg/mL were obtained after swelling, respectively.
The R-0.5 hydrogel, R-1.0 hydrogel, and R-1.5 hydrogel were tested in sequence, and the injectability of the glucogalactan hydrogel was characterized by a rheometer. The viscosity of the hydrogels was measured as a function of shear rate (0.1-1000 1/s) in the complex viscosity test. The R-0.5 hydrogel, R-1.0 hydrogel, and R-1.5 hydrogel were loaded into 1 mL syringes using 25-gauge and 27-gauge needles, respectively, for injectability testing.
As shown in
As shown in
During the modeling, the mice were randomly divided into 4 groups, namely R-0.5, R-1.0, R-1.5, and control groups. The back of the mice was depilated, and the glucogalactan hydrogel or commercial hyaluronic acid hydrogel (Bloomage Biotech, BIOHYALUX®, modified sodium hyaluronate gel for injection, production license number: Shandong Food and Drug Administration Machinery Production License No. 20120123) was injected into the back of the mice. The mice were sacrificed at 1 week, 6 weeks, and 16 weeks after hydrogel injection, and the skin tissue and hydrogel in the hydrogel area were cut off to observe the appearance and size of the hydrogel and measure the changes in weight of the hydrogel.
As shown in
As shown in
In this study, the MTT assay and live/dead imaging were conducted to evaluate the in vitro cytotoxicity of glucogalactan and glucogalactan hydrogel. L929 cells were seeded in a 96-well plate and cultured for 24 h. 1 mL of hydrogel was incubated in DMEM for 48 h, a glucogalactan hydrogel extract was prepared at 37° C., and then transferred into a regular DMEM medium containing different concentrations of glucogalactan hydrogel extracts to allow culture for another 24 h. After MTT treatment, cell viability was measured at 570 nm.
In this study, the in vivo degradation and biocompatibility of glucogalactan hydrogels were evaluated by subcutaneous implantation in the back of Balb/c mice. 200 μL of sterile hydrogel was injected subcutaneously into the dorsal flank of the mouse using a 27-gauge needle. Mice were euthanized 7 d after implantation. The main organs (heart, liver, spleen, lung, and kidney) were taken for H&E staining and Masson staining to analyze whether the glucogalactan hydrogel was toxic to the internal organs of mice.
As shown in
As shown in
From the above examples, it can be seen that a polysaccharide glucogalactan is dissolved in a NaOH aqueous solution and then mixed evenly by stirring, a proper amount of a cross-linking agent is added and then stirred evenly, and a glucogalactan hydrogel is prepared by a reaction under appropriate conditions. The preparation method has mild conditions, simple process, few reagents, no violent reactions, and low cost, and is easy to achieve industrial production. The polysaccharide hydrogel prepared shows high degradation resistance, excellent mechanical properties, desirable biocompatibility, and long duration in vivo. The glucogalactan hydrogel is suitable for scenarios such as subcutaneous filling, wrinkle removal, and joint cavity lubricating fluid replacement.
Although the present disclosure is described in detail in conjunction with the foregoing examples, they are only a part of, not all of, the examples of the present disclosure. Other examples can be obtained based on these examples without creative efforts, and all of these examples shall fall within the protection scope of the present disclosure.