Golf ball cover

Information

  • Patent Grant
  • 5321089
  • Patent Number
    5,321,089
  • Date Filed
    Tuesday, March 30, 1993
    31 years ago
  • Date Issued
    Tuesday, June 14, 1994
    30 years ago
Abstract
A composition useful to produce a golf ball cover of a blend of ethylene-methyl acrylate and an ionomer resin and a compatabilizer. The composition produces a cover material having hardness and feel comparable to Balata, but having improved resilience, durability and cut resistance over Balata.
Description

BACKGROUND OF THE INVENTION
This invention relates in general to golf balls and, more particularly, to a golf ball having an improved cover material.
The assembly of a golf ball generally involves molding a cover around a solid or wound core. Golf balls with wound cores are typically referred to as "three piece" balls because they consist of three basic components: (1) a solid or liquid-filled center; (2) rubber winding around the center, and (3) the cover. Similarly, solid cores are referred to as having a "two piece" construction, since they consist solely of a solid core and a cover. A third type of ball, known as a "one-piece" ball is also known in the art. As the name suggests, one piece balls are solid balls of homogeneous construction made by any conventional molding method suitable for the purpose.
The composition of the golf ball cover has proven to be a factor in overall golf ball performance. Historically, three piece balls had covers made of Balata, a natural resin obtained from trees in South and Central America and is essentially made up of transpolyisoprene.
Balata is still used today as a cover material because of the "click" and "feel" provided by the balata cover to the golfer. "Click" is the sound made by a golf club head when it hits the ball. "Feel" is the overall sensation transmitted to the golfer after hitting the ball. Balata covered golf balls are also used because of the excellent playability and good flight performance qualities. These balls give good flight distance and skilled golfers can impart desirable spin to the ball, enabling it to draw or fade in flight. Also, especially with high-lofted clubs, the backspin allows the ball to stop abruptly on approach shots.
However, balata type materials are expensive and the manufacturing procedures required are time-consuming, labor-intensive and therefore expensive.
The majority of modern golf balls use a two piece construction with covers made of a durable synthetic thermoplastic resin such as Surlyn, a product of E. I. DuPont de Nemours Company, Incorporated. Synthetic thermoplastic cover materials have been used with limited success. They are durable and produce satisfactory flight distance. Additionally, they are less costly to manufacture than balata covers. However, these materials are hard and therefore lack the "click" and "feel" of a balata ball. Moreover, it is not possible to impart to such balls the desirable spin characteristics required by skilled golfers. It is desirable, however, to utilize a synthetic cover material for improved process manufacturing and to increase desirability and resilience performance.
In an attempt to overcome the negative factors of the hard ionomer covers, DuPont introduced low modulus SURLYN ionomers in the early 1980's. These SURLYN ionomers have a flexural modulus of from about 3000 to about 7000 PSI and a hardness of from 25 to about 40 as measured on the Shore D scale - ASTM 2240. The low modulus ionomers are terpolymers of ethylene, methacrylic acid and n- or iso-butylacrylate, neutralized with sodium and zinc cations. E. I. DuPont De Nemours & Company has disclosed that the low modulus ionomers can be blended with other grades of previously commercialized ionomers of high flexural modulus of from about 30,000 to 55,000 PSI to produce balata-like properties.
The low modulus ionomers when used without blends produced covers with very similar physical properties to those of balata, including poor cut resistance. Worse, such covers tend to go "out-of-round" quicker than balata covers. Blending with hard SURLYN ionomers was found to improve these properties.
However, the relatively high cost of the soft SURLYN ionomers, together with the need to blend several grades of hard and soft ionomers to achieve the desired properties, militates against the use of soft/hard ionomer blends in the commercial manufacture of a golf ball.
Accordingly, it is an object of the present invention to provide a golf ball having a synthetic cover material.
Another object of the present invention is to provide an improved synthetic cover material for a golf ball.
It is another object of the present invention to provide a golf ball having a synthetic cover material that achieves the click, feel, playability and flight performance qualities of Balata covered golf balls.
A further object of the present invention is to provide a golf ball having a cover material that has improved process manufacturing as well as durability and resilience.
SUMMARY OF THE INVENTION
The present invention is a cover material for a golf ball, especially a three piece liquid center golf ball. The cover material includes ethylene-methyl acrylate (E-MA) blended with an ionomer resin, such as SURLYN and a compatabilizer. The result is a golf ball cover with cover hardness and feel comparable to balata, but yielding improved resilience, durability and cut resistance over balata.
These and other objects and features of the present invention will be apparent from a reading of the following detailed description of the invention.





DETAILED DESCRIPTION OF THE INVENTION
The cover composition of the present invention includes blends of Ethylene-Methyl Acrylate (E-MA) with an ionomer resin and a compatabilizer.
For the purpose of the present invention, E-MA is defined as a copolymer of 65-94% by weight of ethylene and 35-6% by weight methyl-acrylate. Suitable for use in the present invention are Optema.RTM. copolymers, a trademark of Exxon Chemical Company of Houston, Tex. for ethylene methyl acrylate (EMA) copolymers. Three versions of Optema.RTM. are useful in the present invention and have the following physical properties:
______________________________________ Flexural ShoreMaterial % M.A. Modulus D M.I.______________________________________Optema XS 11.04 6.5 19,500 psi 45 6.0 g/10 minOptema XS 55.08 27.0 2,825 psi 28 5.0 g/10 minOptema XS 53.04 35.0 3,020 psi 17 4.0 g/10 min______________________________________ M.I.= melt index using test methods according to ASTM D 1238.
The term "ionomer resin" as used herein means a copolymer of ethylene with a metal salt of methacrylic acid, a metal salt of acrylic acid or a mixture thereof. Preferred metal salts are those of lithium, sodium, zinc and magnesium. Specifically, the ionomer resin will be a copolymer of 75-95% of an olefin, preferably ethylene, and 5-25% of an alpha, beta, ethnically unsaturated carboxylic acid, such as acrylic or methacrylic acid, with 10%-90% of the carboxylic acid groups being neutralized with sodium, zinc, lithium or magnesium ions. For example, Surlyn, available from E. I. DuPont deNemours Company, Incorporated of Wilmington, Del. is acceptable for use in the present invention as the ionomer resin. Also suitable is Iotek resin, available from Exxon Chemical Company of Houston, Tex.
Certain ionomer resins useful in the present invention have the following physical properties:
______________________________________ Acid Ion FlexMaterial Type Type % Acid Modulus Shore "D"______________________________________Surlyn 8240 MAA Na 20 75,000 75Surlyn 8920 MAA Na 15 55,000 66Surlyn 9910 MAA Zn 15 48,000 64Surlyn MAA Mg 15 44,000 61AD 8172Surlyn 7940 MAA Li 15 61,000 68Iotek 8030 AA Na 15 49,000 59Iotek 7010 AA Zn 15 26,000 57______________________________________ Acid type: MAA Methacrylic Acid AA Acrylic Acid
In a preferred embodiment, the cover material of the present invention includes 30-90% ethylene-methyl acrylate copolymer, consisting of 94-65% by weight of ethylene and 6-35% by weight of methyl-acrylate, having a flexural modulus of 2,800-19,000 psi, Shore "D" hardness of 17-45 and melt flow index of 0.7-20.0 g/10 min; and 70-10% of an ionomer resin containing 95-75% by weight of ethylene and 5-25% by weight of a carboxylic acid, 10-90% of which are neutralized with one of the metal ions Na, Zn, Li, or Mg, having a flexural modulus of 10,000-90,000 psi, and a melt index of 0.5-5.0 g/10 min.
Preferably, the blend for the cover material of the present invention includes a compatabilizer to improve the miscibility of the E-MA/Ionomer blend. The compatabilizer shall consist of a copolymer containing 80-95% by weight of an olefin, preferably ethylene, 20-5% by weight of an alpha, beta ethnically unsaturated carboxylic acid, preferably acrylic or methacrylic acid, and possibly containing a small amount of an n-alkyl acrylate, such as n-butyl acrylate. A suitable compatabilizer is Escor.RTM., a trademark of Exxon Chemical Company of Houston, Tex. for a terpolymer of ethylene, acrylic acid and n-butyl acrylate having the following physical properties:
______________________________________Material Flex Modulus Shore "D" M.I.______________________________________Escor ATX 310 11,700 44 6.0 g/10 min.______________________________________
For blends of the cover material that include a compatabilizer, a preferred embodiment is:
30 to 90 php of EMA
10 to 70 php of ionomer resin
5 to 15 php of compatabilizer--copolymer/terpolymer.
It may be desirable for the cover material of the present invention to include a colorant. The colorant may be present in the composition in an amount up to 5 parts per hundred polymer (p.h.p.) of the composition. Typically, the colorant will consist of titanium dioxide, ultramarine blue, ultramarine violet and an ionomeric carrier. A suitable colorant is available from AMERICHEM Inc. of Cuyahuga, Ohio.
The blends are made and produced into a golf ball cover by processes known in the art for producing golf ball covers, processes such as extrusion molding or injection molding. It is within the skill of those in this field to produce a blend from the components of the present invention.
The present invention will be described by way of the following examples, which are provided for illustration but are not to be considered as limiting. A control example was included, ID No. 12 consisting of a Maxfli HT-90 balata covered golf ball, for comparison purposes.
TABLE I__________________________________________________________________________ (d) (a) (b) (c) SHORE (e) (f) (g)ID BLEND SIZE PGA WEIGHT D REB COR DUR__________________________________________________________________________1 Optema XS11.04/ 1.6828 88 45.46 62 71.8 0.730 159 Surlyn 8240 @ 30/702 Optema XS11.04/ 1.6800 84 45.13 58 70.5 0.726 182 Surlyn 8240 @ 50/503 Optema XS11.04/ 1.6811 83 45.12 52 70.1 0.725 170 Surlyn 8240 @ 70/304 Optema XS11.04/ 1.6797 81 44.75 49 68.8 0.724 145 Surlyn 8240 @ 90/105 Optema XS55.08/ 1.6843 86 45.56 60 72.8 0.737 181 Surlyn 8240 @ 30/706 Optema XS55.08/ 1.6828 81 45.39 51 71.2 0.731 173 Surlyn 8240 @ 50/507 Optema XS55.08/ 1.6820 82 45.47 47 71.8 0.734 160 Surlyn 8240 @ 70/308 Optema XS55.08/ 1.6805 77 45.34 37 70.8 0.733 100* Surlyn 8240 @ 90/109 Optema XV53.04/ 1.6848 86 45.57 57 72.8 0.738 168 Surlyn 8240 @ 30/7010 Optema XV53.04/ 1.6841 80 45.57 44 72.2 0.735 112* Surlyn 8240 @ 50/5011 Optema XV53.04/ 1.6840 76 45.68 35 73.2 0.732 98* Surlyn 8240 @ 70/3012 Maxfli HT-90 1.6795 88 45.25 52 70.6 0.721 -- (control)__________________________________________________________________________ - 5% Americhem #33370R2 color concentrate added to each blend. - 10 phr Escor ATX added to each blend for compatiblization purposes. (a) Size = diameter in inches (b) PGA measures deformation under a fixed static load of 200 lbs (d) Shore D hardness, ASTM 2240 (e) REB = rebound (inches) from 100inch drop test (f) COR = coefficient of restitution = rebound velocity/forward velocity (g) DUR = durability, number of hits before mechanical failure of sample.
The following physical properties of compositions ID Nos. 1-11 were also measured:
TABLE II__________________________________________________________________________ TENSILE STRENGTH ELONG. TENSILE ELONG. TENSILE FLEXURALID kg/cm.sup.2 YIELD % BK, PSI BK, % MOD, PSI MOD, PSI__________________________________________________________________________1 2,315 11 2,858 227 26,305 53,1392 1,793 10 2,468 270 20,510 34,2993 1,288 9 1,753 254 14,655 23,4354 930 8 1,420 425 9,857 15,1675 1,842 13 3,462 351 22,175 44,7036 1,433 9 2,285 286 15,561 27,6037 746 13 1,692 413 6,240 10,0718 372 18 961 616 2,027 2,1969 2,067 13 3,048 279 22,996 48,21410 1,266 9 1,796 198 13,101 24,65511 718 14 1,411 308 5,075 10,418__________________________________________________________________________ -Tensile Yield, Elongation Yield, Tensile Break, Elongation Break and Tensile Modulus Tests performed according to ASTM procedure D638. -Flexural Modulus Testing performed according to ASTM D790 procedure.
Balls having cover compositions of Examples 1 to 11 above were also tested for torsional modulus at various temperatures and the results are below:
TABLE III______________________________________TORSIONAL MODULUS (PSI) -10.degree. C.ID -10.degree. C. 0.degree. C. 10.degree. C. 25.degree. C. 35.degree. C. vs 35.degree. C.______________________________________1 27,451 27,805 19,251 13,499 10,516 16,9352 22,498 16,874 12,816 9,353 6,466 16,0323 17,209 13,089 9,053 6,552 4,777 12,4324 3,681 10,046 7,138 4,405 3,375 10,3065 18,408 15,819 13,499 11,301 8,037 10,3716 12,289 11,068 8,670 6,129 4,053 8,2367 5,360 3,724 2,734 2,351 1,268 4,0928 2,584 1,755 1,267 839 527 2,0579 21,724 18,951 15,905 12,559 9,358 12,36610 12,736 7,710 4,812 2,985 2,127 10,60911 3,883 2,888 2,089 1,504 1,001 2,882______________________________________ - Torsional modulus testing performed according to ASTM D1043 procedure.
Three piece wound golf balls having covers made from the compositions of Examples 1 to 12 above were driven by a TRUE TEMPER machine and measured for carry, total distance and trajectory. The results are given below.
TABLE IV______________________________________ (c) (a) (b) REAR (d) (e)ID CARRY TOTAL TRAJ DISP/ACCY I.V.______________________________________1 252.8 266.7 7.7 4.6 R/176 235.42 246.9 260.7 7.8 2.9 R/196 234.73 249.4 261.1 7.9 2.9 R/263 234.74 249.4 258.0 8.2 4.1 R/276 234.65 254.7 267.2 7.9 3.6 R/285 235.66 252.1 260.1 8.3 6.1 R/226 235.27 250.7 256.4 8.4 6.5 R/305 235.88 250.2 254.1 9.1 9.2 R/171 235.79 254.5 264.6 8.0 4.8 R/116 235.510 254.0 261.3 8.5 5.3 R/91 235.611 253.4 260.0 8.7 6.7 R/135 235.812 247.6 260.6 7.7 7.9 R/239 232.9______________________________________ - Driver club used was Tour Ltd Metal Wood with 8.5.degree. loft. - Club head velocity was constant @ 161.8 163.1 ft/sec. (a), (b) Measured in yards (c) Measured by observing rearpeak trajectory using adapted trajectory boards similar to those of the US Golf Association. (d) Dispersion/Accuracy (e) Initial Velocity (in ft/sec) of the ball when struck by a driver.
Balls having covers of the compositions of Examples 1 to 12 above were tested for spin-rate at various launch angles using a Driver, No. 5 iron and pitching wedge. Spin rate was measured by observing the ball in flight using stop action strobe photography and the results are given below.
TABLE V______________________________________ PITCHINGDRIVER 5-IRON WEDGEID L.A. SPIN L.A. SPIN L.A. SPIN______________________________________1 9.3 3,767 18.7 6,134 18.3 7,4252 9.1 3,914 18.7 6,072 18.4 7,8033 9.3 3,983 19.0 6,153 16.5 8,8984 9.1 4,036 19.2 6,319 15.6 9,3165 9.2 3,7899.5 6,350 16.1 8,7046 9.3 4,237 19.5 6,706 14.8 9,5097 9.1 4,284 19.2 7,178 14.0 9,4178 9.0 4,736 18.7 7.545 14.8 9,1349 8.9 3,883 19.3 6,267 17.7 8,21710 8.8 4,175 18.5 7,042 12.8 9,06711 9.1 4,500 18.3 7,631 15.4 9,07012 9.6 3,808 19.8 5,861 17.2 8,920______________________________________ - Driver clubs used: Tour Ltd. Metal Wood with 8.5.degree. loft - 5iron club used: Tour Ltd. 5Iron with 28.degree. loft - Pitching Wedge club used: Tour Ltd. Pitching Wedge with 50.degree. loft
Balls having cover compositions of Examples 1 to 11 above and having the torsional modulus values shown in Table III were tested for loss of properties over temperature changes and the results are below. Values calculated represent the loss in torsional modulus against previous temperature value.
TABLE VI______________________________________ -10.degree. C. to 35.degree. C. OVERALLID -10.degree. C. 0.degree. C. 10.degree. C. 25.degree. C. 35.degree. C. LOSS______________________________________1 -- 16.9% 15.6% 29.9% 22.1% 61.7%2 -- 25.0% 24.0% 27.0% 30.9% 70.5%3 -- 23.9% 30.8% 27.6% 27.1% 72.2%4 -- 26.6% 28.9% 38.3% 23.4% 75.3%5 -- 14.1% 14.7% 16.3% 28.9% 56.3%6 -- 9.9% 21.7% 29.3% 33.9% 67.0%7 -- 30.5% 26.6% 14.0% 46.1% 76.3%8 -- 32.1% 27.8% 33.8% 37.2% 79.6%9 -- 12.8% 16.1% 21.0% 25.5% 56.9%10 -- 39.4% 37.6% 38.0% 28.7% 83.3%11 -- 25.6% 27.7% 28.0% 33.4% 74.2%______________________________________
Each of the compositions ID No. 1-11 and the Maxfli HT Balata (12) were then the subject of an impact deflection study, testing procedures completed in accordance with Dunlop golf standards. The results are below:
TABLE VII__________________________________________________________________________IMPACT DEFLECTION STUDYID TEMP. 0.degree. C. TEMP. 10.degree. C. TEMP. 25.degree. C. TEMP. 35.degree. C.NO 125 150 CHNG. 125 150 CHNG. 125 150 CHNG. 125 150 CHNG.__________________________________________________________________________1 1 1/32 1 1/32 0 1 1/16 1 1/16 0 1 3/32 1 5/32 +1/16 1 5/32 1 1/8 -1/322 1 1 1/32 +1/32 1 1/32 1 1/32 0 1/8 1 5/32 +1/32 1 1/8 1 5/32 +1/323 1 1/32 1 1/32 0 1 3/32 1 1/16 -1/32 1 5/32 1 5/32 0 1 5/32 1 3/16 +1/324 1 1/16 1 1/8 +1/16 1 1/16 1 1/16 0 1 1/8 1 3/16 +1/16 1 5/32 1 5/32 05 1 1 1/32 +1/32 1 3/32 1 1/16 -1/32 1 1/8 1 5/32 +1/32 1 5/32 1 5/32 06 1 1/16 1 1/16 0 1 1/8 1 1/8 0 1 3/16 1 1/4 +1/16 1 1/4 1 1/4 07 1 3/32 1 1/16 -1/32 1 5/32 1 1/8 -1/32 1 7/32 1 7/32 0 1 9/32 1 5/16 +1/328 1 3/32 1 3/32 0 1 1/8 1 1/8 0 1 3/16 1 1/4 +1/16 1 7/32 1 1/4 +1/329 1 1/16 1 1/16 0 1 3/32 1 3/32 0 1 1/8 1 7/32 +3/32 1 3/16 1 3/16 010 1 1/8 1 3/32 -1/32 1 1/8 1 5/32 +1/32 1 7/32 1 7/32 0 1 9/32 1 9/32 011 1 1/8 1 5/32 +1/32 1 5/32 1 1/4 +3/32 1 1/4 1 5/16 +1/16 1 11/32 1 9/32 -1/1612 1 1/32 1 1/32 0 1 1/16 1 1/32 -1/32 1 1/8 1 7/32 +3/32 1 3/16 1 5/32 -1/32__________________________________________________________________________
Blends I.D. Nos. 1-11 shown in Table I all contain 30-90% ethylene-methyl acrylate with 70-10% ionomer. These blends show significantly improved durability and COR versus the Example ID No. 12, the prior art Balata control. Table IV illustrates the carry distance and initial velocity improvements during flight testing vs. Maxfli HT control. Table V illustrates spin comparativeness of E-MA/ionomer blends with respect to Balata control.
Other blends were prepared and tested for various physical properties as follow:
TABLE VIII__________________________________________________________________________ BLEND # 13 14 15 16__________________________________________________________________________Optema XS 11.04 70 70 70 70Surlyn 8240 30 30 30 30Escor ATX 310 5 10 15 --Americhem #33370-R2 CC 5 5 5 5Physical PropertiesASTM D-638 Tensile yield, psi 1,500 1,500 1,400 1,500ASTM D-638 Tensile break, psi 1,300 1,300 1,400 1,400ASTM D-638 Elongation yield, % 70 80 90 60ASTM D-638 Elongation break, % 170 200 240 90ASTM D-790 Flexural modulus, psi 30,300 29,000 28,300 30,100__________________________________________________________________________
Example blends I.D. Nos. 13-16 (Table VIII) demonstrate the effective need of a compatabilizer in E-MA/ionomer blends. Blends I.D. Nos. 13-15 contain 5-15 phr Escor compatabilizing copolymer, while blend 16 contains only the E-MA/ionomer blend. Physical property testing results show blend No. 16 yields significant decrease in elongation break vs. blends No. 13-15. This indicates a separation of materials if compatabilizer is not present.
TABLE IX__________________________________________________________________________ BLEND # 17 18 19 20 21__________________________________________________________________________Optima XS 11.04 100 80 75.0 66.7 50.0Surlyn 8240 20 24.0 33.3 50.0Escor ATX 310 10 11.1 11.1 11.1Americhem #33370-R2 CC 5 5 5.0 5.0 5.0Physical PropertiesASTM D-638 Tensile Yield, psi 1,300 1,500ASTM D-638 Tensile Break, psi 1,740 1,200 1,400ASTM D-638 Elongation yield, % 90 50ASTM D-638 Elongation Break, % 1,400 310 210ASTM D-790 Flexural Modulus, psi 19,500 23,600 28,000Golf Ball PropertiesPGA Compression 84 85 88 89 91Shore "D" Hardness 46 51 51 53 54C.O.R. 0.729 0.737 0.741 0.743 0.745Durability 267 177 152 172 181__________________________________________________________________________
TABLE X__________________________________________________________________________ BLEND # 22 23 24 25 26 27 28 29__________________________________________________________________________Optima XS 11.04 50 50 50 50 50 50 50 50Surlyn 8240 50Surlyn 8920 50Surlyn 9910 50Surlyn AD 8172 50Surlyn 7940 50Iotek 8030 50 50Iotek 7010 50Escor ATX 310 10 10 10 10 10 10 10Americhem #33370-R2 CC 5 5 5 5 5 5 5 5Golf Ball PropertiesPGA Compression 89 85 84 84 85 88 88 84Shore "D" Hardness 54 54 54 54 54 55 54 50C.O.R. 0.743 0.738 0.733 0.731 0.734 0.727 0.738 0.734Durability 160 168 180 175 179 36 142 192__________________________________________________________________________
The E-MA/ionomer resin blends of the present invention yield comparable or improved coefficient of restitution properties compared to Balata covered golf balls. Moreover, these properties did not change as cover hardness changed.
Cover blends in the hardness range of 47-62 Shore "D" yield superior durability properties compared to Balata, in the range of 145-182 hits. This is comparable to a standard Surlyn covered golf ball. Cover blends with Shore "D" hardness in range of 35-47 yielded lower durability than a harder blend, but still yielded significantly improved durability in comparison with Balata covered balls.
Example ID No. 17 is a cover consisting of 100% ethylene-methyl acrylate. Ball properties are acceptable, however, cut resistance durability is significantly lower than blends containing the ionomer resin. Thus, the blends of present invention are shown to be superior to a cover of EMA alone.
Example blends ID Nos. 18-21 support observations regarding ID Nos. 1-11, covering ratio of ionomer from 20-50% by weight.
Example blends ID Nos. 22-26 cover usage of ionomers of methacrylic acid neutralized with Na, Zn, Li or Mg metal ions. All examples in this group yield desirable properties, comparable to Example ID No. 12 (prior art Balata). The present invention is therefore shown to be valid for all types of metal ion ionomers mentioned.
Example ID Nos. 27-28 further support the conclusions mentioned in Examples 13-16, regarding effectiveness of a compatabilizer. A significant decrease in both COR and ball durability are observed on Example ID No. 27, without compatabilizer.
Example ID Nos. 28-29 indicate that the present invention yields comparable properties to Example 12 (prior art Balata) when ionomer used contains acrylic acid as the carboxylic acid.
In short, the compositions of the present invention produce a cover for a golf ball that is cost effective to produce, and yet yields the playability and flight performance qualities of a Balata covered ball.
It will be appreciated that the instant specification and claims are set forth by way of illustration and not limitation and that various changes and modifications may be made without departing from the spirit and scope of the present invention.
Claims
  • 1. A golf ball having a molded cover wherein the cover comprises a blend of:
  • (a) 30-90% of a non-neutralized binary copolymer of 65-94% by weight ethylene and 35-6% by weight methyl-acrylate
  • (b) 10-70% of a partially neutralized copolymer of 75-95% of an olefin and 5-25% of na alpha, beta, ethnically unsaturated carboxylic acid with 10-90% of the carboxylic acid groups being neutralized with a metal salt
  • (c) 5-15 parts per hundred based on polymers (a) and (b) of a non-neutralized copolymer selected from a member of the group of copolymers consisting of a copolymer of 80-95% by weight ethylene and 20-5% by weight of a carboxylic acid and a terpolymer of 70-95% ethylene by weight, 20-5% by weight of a carboxylic acid and 25.0% by weight an alkyl-acrylate for compatabilization purposes.
  • 2. The golf ball of claim 1 wherein in the blend said partially neutralized copolymer is selected from the group consisting of copolymers of ethylene with a metal salt of methacrylic acid, copolymers of ethylene with a metal salt of acrylic acid and mixtures of said copolymers.
  • 3. The golf ball of claim 2 wherein in the blend said metal salt is selected from the group consisting of lithium salts, sodium salts, magnesium salts and zinc salts and said
  • 4. The golf ball of claim 1 wherein the blend comprises 50% of polymer (a), 50% of the partially neutralized copolymer (b) and 10 parts per hundred of polymer (c).
  • 5. The golf ball of claim 1 wherein the blend comprises 30% of polymer (a), 70% of the partially neutralized copolymer (b) and 10 parts per hundred of polymer (c).
  • 6. The golf ball of claim 1 wherein the blend comprises 70% of polymer (a), 30% of the partially neutralized copolymer (b) and 10 parts per hundred of polymer (c).
  • 7. The golf ball of claim 1 wherein the blend comprises 90% of polymer (a), 10% of the partially neutralized copolymer (b) and 10 parts per hundred of polymer (c).
  • 8. The golf ball of claim 1 wherein in the blend said copolymer (c) comprises a terpolymer of ethylene, acrylic acid and n-butyl acrylate.
US Referenced Citations (14)
Number Name Date Kind
2074803 Rickey Mar 1937
2322140 Kalowski Jun 1943
3365520 Foster et al. Jan 1968
3490770 Satchell et al. Jan 1970
3789035 Iwami et al. Jan 1974
4323247 Keches et al. Apr 1982
4801649 Statz Jan 1989
4838556 Sullivan Jun 1989
4884814 Sullivan Dec 1989
4911451 Sullivan Mar 1990
4943332 Sakaguchi et al. Jul 1990
4956414 Muehlenbernd et al. Sep 1990
5033749 Kakiuchi Jul 1991
5187013 Sullivan Feb 1993
Foreign Referenced Citations (7)
Number Date Country
58-217533 Dec 1983 JPX
3-71148 Nov 1991 JPX
645311 Oct 1950 GBX
655525 Jul 1951 GBX
1209316 Oct 1970 GBX
1383422 Feb 1975 GBX
2032286 May 1980 GBX