Patent Grant
8637414
1. Field of the Invention
The present invention relates to a padding material for acoustic applications. In particular, the present invention relates to a gradient density padding material, wherein the density of a portion of the thickness of the padding material is increased to increase the air flow resistance of the padding material. In view of this, the acoustic properties of the padding material can be tuned to a particular application.
2. Description of Background Art
There is a growing trend in today's acoustical insulation market for lightweight materials. The transportation industry is a good example of where there is a need for lightweight acoustical insulation. Traditional interior and exterior acoustical insulators have used heavy layers in decoupled mass systems to reduce interior noise levels. A recent trend in this market has been to eliminate these heavy layer systems and use lightweight fiber or foam based padding systems. There are a variety of these materials out in the market today. All of these fiber systems utilize a multilayer fiber pad to produce a lightweight padding system with good acoustic absorption in the range of 100-5000 Hz and little or no sound level degradation in the interior of a vehicle when compared to heavy layer systems. It is known in the acoustic field that acoustic absorption performance is dependent in part on the airflow resistance of materials. It is also known that by increasing the airflow resistance of an acoustic material, the low to mid frequency (100-2500 Hz) absorption performance can be increased. Maximum acoustic absorption in this frequency range occurs when that material has an airflow resistance of 800-1200 MKS Rayls. This frequency range is often the most difficult to combat in vehicle systems where weight, cost, and packaging space (thickness) are limited. All of today's multilayer systems require 2 or more separate layers, where each layer is produced independently with specific stiffness, strength, and airflow resistance properties. These independent layers must then be bonded together in a secondary operation.
One example of a multilayer system according to the background art is described in U.S. Pat. No. 6,145,617. In this patent, a compressed nonwoven fiber layer is bonded to an uncompressed fiber layer. A second example is described in U.S. Pat. No. 6,296,075. In this patent, a high flow resistant facing or coverstock material is attached to the surface of a low density fiber web. A third example is described in U.S. Pat. No. 5,824,973. In this patent, a low density fiber web includes a microporous film attached to a surface thereof. A fourth example is described in U.S. Pat. No. 5,334,338. In this patent, a dense foam layer with low open cell count is produced on top of a porous, low density open cell foam layer.
The present invention is based on the discovery that enhanced performance properties can be produced using a single layer of nonwoven fibrous padding material. The present invention is directed to a single layer of nonwoven fibrous padding material with enhanced properties and a process for making the same. By producing a single layer of nonwoven fibrous padding and applying significant heat and pressure to one side of the material, a single layer of acoustic padding material is produced with enhanced performance properties. As shown in
The enhancements provided by the increased density top portion include:
All of the above are performance benefits of the single layer product of the present invention when compared with the multi layer products of the background art.
The increased material strength enables the padding material to be processed through secondary operations, such as die-cutting and molding operations. Many nonwoven and foam padding materials have low strength in their X-Y planes. In particular, many of the lightweight padding systems utilize low density materials with tensile and tear strength properties that are not great enough for the intended processes and final applications. Therefore, these materials must include strengthening layers in order to provide the strength necessary for most automotive applications. The present invention provides increased strength in the X-Y plane of a lightweight padding material. The density and thickness of the top surface portion of the single layer of nonwoven material can be designed so that the material will meet most automotive strength requirements without the use of additional strengthening layers. Of course, it should be understood that it is also possible to add other functional or non-functional layers of material to the single layer of nonwoven fibrous padding material in order to further increase the material strength, if necessary for a particular application, or to affect other properties or aesthetic characteristics of the padding material.
The increased airflow resistance of the increased density top surface greatly increases the low to mid frequency acoustic absorption. Due to the limited packaging space available in a vehicle for acoustical products, the thickness of these materials is usually limited to 1″ or less. Low to mid frequency sound waves (100-2500 Hz) are the most difficult acoustic waves to absorb with materials less than 1″ thick. This is mainly because the wavelength of sound in this frequency range is much greater than the thickness of the acoustical insulation. The increased airflow resistance of the increased density top surface of the single layer of nonwoven fibrous padding material of the present invention greatly improves the acoustic absorption in these frequencies.
By producing the increased airflow resistance section with densely packed fibers, absorption performance is increased even beyond much of the background art on this subject. Much of the background art teaches the addition of a separate microporous film, nonwoven, or similar lightweight cover layer to provide the airflow resistance. In the present invention; however, the increased density top portion of the single layer of nonwoven fibrous padding material provides the airflow resistance throughout the entirety of the densified portion. The densified portion will have an airflow resistivity that is lower than much of the background art. Airflow resistivity is the total airflow resistance of a material divided by its thickness. Acoustic materials with high airflow resistivity will generally have poor high frequency absorption. A greater portion of the high frequency acoustic waves will be reflected off of the surface of a material if it has high airflow resistivity. In contrast, the padding material of the present invention provides the necessary total airflow resistance of the material without having a portion of material with high airflow resistivity. Therefore, a material is produced from a single layer with increased low and mid frequency absorption, without loss of absorption in the higher frequencies (2500-10,000 Hz). Also, since the airflow resistance of the material is provided by a densified fiber portion, the acoustic waves must travel through a tortuous path with a large amount of fiber surface area. This tortuous path increases the surface area to increase the acoustic absorption of the present invention over the background art concepts that utilize separate microporous films, nonwovens, or similar lightweight cover layers.
The increased density of the top portion of the padding material produces a decoupled mass system helping to reduce vibration transmission. This property is even further enhanced when the material is used with additional top layers such as a carpet. This type of decoupled mass system will generally limit the amount of vibration that is transferred through the material. This property greatly increases the acoustic performance of the product in applications where the material is mounted against vibrating panels such as vehicle floorpans. Producing a single layer padding material with enhanced performance as described above provides a lightweight acoustical material at a very cost effective price. This enhanced padding system can be used in lieu of traditional decoupled mass acoustic systems to provide a significant cost and system weight savings. This system will also cost less to produce than other multi-layer lightweight systems.
The product and method of the present invention also avoids the occurrence of delamination during secondary processing. This is a common occurrence in the multilayer structures according to the background art. The shear stresses that are experienced in, for example, molding of the product can separate the individual layers of material. In the present invention; however, the material is formed from a single layer of material having an increased density portion. Accordingly, there is no attachment line that can be separated during secondary processing.
The above aspects of the present invention are accomplished by a gradient density padding material, comprising a single layer of nonwoven material, said single layer of nonwoven material having at least one surface thereof processed to form a portion of a thickness thereof having a density increased with respect to a remaining portion of the thickness thereof, said single layer of nonwoven material after processing having an airflow resistance within the range of 200-4000 MKS Rayls, wherein said single layer of nonwoven material has an enhanced acoustic performance.
The above aspects of the present invention are also accomplished by a method of making a gradient density padding material having an enhanced acoustic performance, said method comprising the steps of providing a single layer of nonwoven material; and processing at least one surface of said single layer of nonwoven material to form a portion of a thickness thereof having a density increased with respect to a remaining portion of the thickness thereof, said single layer of nonwoven material after processing having an airflow resistance within the range of 200-4000 MKS Rayls.
Further scope of applicability of the present invention will become apparent from the detailed description given hereinafter. However, it should be understood that the detailed description and specific examples, while indicating preferred embodiments of the invention, are given by way of illustration only, since various changes and modifications within the spirit and scope of the invention will become apparent to those skilled in the art from this detailed description.
The present invention will become more fully understood from the detailed description given hereinbelow and the accompanying drawings which are given by way of illustration only, and thus are not limitative of the present invention, and wherein:
The present invention will now be described with reference to the accompanying drawings. Referring to
In order to produce a gradient density padding material 3 as described above, the nonwoven material 1 must be originally manufactured using a significant percentage of thermoplastic fibers. The material can be a blend of any fibers as long as the material is made up of at least 20% thermoplastic fiber. Preferably, the nonwoven material would be made from a blend of 65-80% thermoplastic fibers and 20-35% non-melting fibers. However, it is also possible to construct the nonwoven material from 100% thermoplastic fibers if the application so demands. The thermoplastic fibers can be constructed, for example, from polyesters, polyamides or polyolefins or a blend of two or more different thermoplastic fibers. The non-thermoplastic fibers can be inorganic, natural or synthetic materials. For example, the inorganic material fibers can be constructed from glass, ceramic, mineral, basalt, silica, etc. The natural material fibers can be cotton, wool, hemp, ramie, kenaf, flax, etc. Furthermore, the synthetic material fibers can be constructed from acrylics, aramids, sulfars (PPS), PBI, Peek, Melamine, Phenolic, Carbon Preox, etc.
The nonwoven material 1 can originally be almost any weight and thickness prior to the surface densification process. Preferably, the nonwoven material 1 would be a lightweight web in the range of 0.5-9 oz/ft2, preferably 1.5-6 oz/ft2. A thickness of the nonwoven material 1 should be within the range of 5-40 mm, preferably 10-35 mm before processing.
Referring again to
The gradient density padding material 3 of the present invention is an acoustically tunable material. Specifically, the air flow resistance can be manipulated under a predetermined amount of heat and pressure in order to obtain a product which has improved performance in a particular frequency range. Accordingly, the gradient density padding material 3 of the present invention can be easily designed to a particular application, depending on the results that are intended to be achieved.
Referring to
It should be noted that the padding material 3 of the present invention is referred to as a “gradient density” padding material, since the density of the densified portion does not have to be a uniform density throughout a thickness thereof. As described above, heat and pressure is applied to the top surface of the nonwoven material 1 in order to increase the density of the increased density portion 5 to change the air flow resistance of the resulting padding material 3. In view of this process, the top most surface of the nonwoven material 1, which is closest to the source of heat, becomes more dense than a portion spaced from the top most portion (the bottom most portion of the increased density portion 5). In addition, the non-densified base portion 7 has a density after processing, which is substantially the same as the original density of the nonwoven material 1. Accordingly, the padding material 3 has a “gradient density.”
As an alternative, heated rolls or belts can be used on both the top and bottom surfaces of the nonwoven padding material to produce a dual-walled product having increased density portions on the top and bottom of the padding material. This padding material can be used in this manner to provide a padding material having two portions with an increased density. Specifically, the top and bottom surfaces of the gradient density padding material 3 will have increased density portions, while the middle of the material 3 does not have an increased density. It should also be noted that the top and bottom of the material 3 can be processed at different temperature and/or temperature in order to form three portions having a different density.
In addition, the above-described gradient density padding material, which has two increased density portions can be cut in half in the machine direction of the padding material to form two padding materials having a single increased density portion. As will be described below, each of the two padding materials will have an increased density portion and a less dense portion. The padding materials can then be used in any of the applications mentioned in the present disclosure. By cutting the padding material having two increased density portions in half, the processing time and therefore the cost of production of the padding material can be substantially decreased.
A thickness of the increased density portion should be within the range of T=5-80%, preferably 5-30% of the total thickness of the nonwoven material after processing. As mentioned above, the total thickness after processing should be approximately 25.4 mm or less in most applications.
Referring to
The gradient density padding material 3 of the present invention can be used in any interior or exterior acoustic applications for vehicles. For example, the gradient density padding material 3 of the present invention can be used for interior application, such as dash interior and under carpet applications, or exterior application, such as tunnel shields. However, it should be understood that the gradient density padding material 3 of the present invention can be used in any application that calls for high acoustic performance other than automotive.
The gradient density padding material 3 of the present invention can be molded after the initial processing into complex shapes to fit the necessary geometry in many different automotive and non-automotive applications. Accordingly the padding material 3 of the present invention can be used anywhere that fibrous or foamed acoustic products are being used today. For example, the gradient density padding material 3 of the present invention can be used in molded carpets, molded exterior, etc.
Referring to
Although
Referring to
The gradient density padding material 3 of the present invention can also be used to produce an aesthetic as well as an acoustic product. As mentioned above, the padding material 3 of the present invention can be processed with heat and pressure on both the top and bottom of the material. The material can then be cut in half to obtain two separate products having the acoustic properties of the present invention. Each of the two products can be used in conjunction with other functional or non-functional layers of material or can be used alone. When used alone, it is preferable that the fibers used in the making of the padding material be colored in order to increase the aesthetic appeal of the resulting product. In this way, the padding material can be used as, for example, a carpet or headliner, which has increased acoustic performance without the necessity of additional layers of material.
With specific regard to the gradient density padding material of the present invention being used as a carpet, the use of the above-mentioned vertically lapped material is particularly advantageous. First, the fibers are fused together in the process of making the vertically lapped material. Accordingly, the carpet has increased wear characteristics. Second, the fibers are generally vertical, eliminating the necessity of a secondary process of straightening the fibers as in other nonwoven carpet processes. Third, the increased density portion of the padding material performs the dual function of increasing the acoustic performance of the carpet, as well as locking the fibers together. Accordingly, there is no need for a backing layer to secure the fibers.
The invention being thus described, it will be obvious that the same may be varied in many ways. Such variations are not to be regarded as a departure from the spirit and scope of the invention, and all such modifications as would be obvious to one skilled in the art are intended to be included within the scope of the following claims.
This non-provisional application claims priority under 35 U.S.C. §119(e) on U.S. Provisional Patent Application No. 60/374,140, filed on Apr. 22, 2002, the entirety of which is incorporated herein by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3652377 | Helmick | Mar 1972 | A |
| 3660222 | Fleming et al. | May 1972 | A |
| 4131664 | Flowers et al. | Dec 1978 | A |
| 4196245 | Kitson et al. | Apr 1980 | A |
| 4213516 | Sulewsky | Jul 1980 | A |
| 4474846 | Doerer et al. | Oct 1984 | A |
| 4568581 | Peoples, Jr. | Feb 1986 | A |
| 4661132 | Thornton et al. | Apr 1987 | A |
| 4950355 | Klose | Aug 1990 | A |
| 5334338 | Kittel et al. | Aug 1994 | A |
| 5456872 | Ahrweiler | Oct 1995 | A |
| 5554238 | English | Sep 1996 | A |
| 5591289 | Souders et al. | Jan 1997 | A |
| 5759927 | Meeker | Jun 1998 | A |
| 5811178 | Adam et al. | Sep 1998 | A |
| 5824973 | Haines et al. | Oct 1998 | A |
| 5841081 | Thompson et al. | Nov 1998 | A |
| RE36323 | Thompson et al. | Oct 1999 | E |
| 6048809 | Brow et al. | Apr 2000 | A |
| 6145617 | Alts | Nov 2000 | A |
| 6165921 | Nagata et al. | Dec 2000 | A |
| 6217691 | Vair et al. | Apr 2001 | B1 |
| 6296075 | Gish et al. | Oct 2001 | B1 |
| 6355079 | Sorvari et al. | Mar 2002 | B1 |
| 6358592 | Vair et al. | Mar 2002 | B2 |
| 6376396 | Thorn et al. | Apr 2002 | B1 |
| 6454048 | Alts et al. | Sep 2002 | B1 |
| 6534145 | Boyles | Mar 2003 | B1 |
| 6572723 | Tilton et al. | Jun 2003 | B1 |
| 6602581 | Aneja | Aug 2003 | B2 |
| 6631785 | Khambete et al. | Oct 2003 | B2 |
| 6659223 | Allison et al. | Dec 2003 | B2 |
| 6669265 | Tilton et al. | Dec 2003 | B2 |
| 6713150 | Alts et al. | Mar 2004 | B2 |
| 6720068 | Venbemmel et al. | Apr 2004 | B1 |
| 6726980 | Staelgraeve et al. | Apr 2004 | B2 |
| 6797653 | Fay | Sep 2004 | B2 |
| 20010050139 | Vair, Jr. et al. | Dec 2001 | A1 |
| 20020160682 | Zeng et al. | Oct 2002 | A1 |
| 20030060113 | Christie et al. | Mar 2003 | A1 |
| 20030106741 | Tompson et al. | Jun 2003 | A1 |
| 20030146545 | Wenstrup | Aug 2003 | A1 |
| 20030168146 | Wenstrup et al. | Sep 2003 | A1 |
| Number | Date | Country |
|---|---|---|
| 22 49 138 | Apr 1974 | DE |
| 0795916 | Sep 1997 | EP |
| 1 154 087 | Nov 2001 | EP |
| 59186750 | Oct 1984 | JP |
| 10-207469 | Aug 1998 | JP |
| 2001-513217 | Aug 2001 | JP |
| 2002-505209 | Feb 2002 | JP |
| WO 99 44817 | Sep 1999 | WO |
| WO 0209089 | Jan 2002 | WO |
| Entry |
|---|
| “Horizontal lapping”, Textiles Intelligence Glossary, www.textilesintelligence.com. |
| “Polypropylene fibers”, Complete Textile Glossary, Celanese Acetate, 2001 (3 pages). |
| Tortora, Phyllis et al. “Understanding Textiles”, Prentice Hall, 1997, pp. 38-39. |
| PI 0309489-8—Brazilian Office Action mailed on Sep. 1, 2011. |
| Number | Date | Country | |
|---|---|---|---|
| 20030199216 A1 | Oct 2003 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60374140 | Apr 2002 | US |