Graft copolymers of polyolefins and a method of producing same

Abstract

Disclosed are graft copolymers of polyolefins and a method of preparing the graft copolymers. The method includes irradiating a mass of olefin polymer particles and thereafter treating the mass of particles with a vinyl monomer in liquid form. A nonoxidizing environment is maintained throughout the process while free radicals produced in the olefin polymer by the irradiation are present, thereby preventing degradation of the polymer. In a final step, residual free radicals are deactivated, and any unreacted monomer is removed.

Description

Claims

1. A method of making a graft copolymer of an olefin polymer comprising the steps of:

(a) irradiating a particulate olefin polymer material at a temperature in the range of about from 10.degree. to 85.degree. C. with high-energy ionizing radiation to produce free radical sites without causing gelation of the particulate olefin polymer material;

(b) treating the irradiated particulate olefin polymer material at a temperature up to about 100.degree. C. for a period of at least about 3 minutes, with about from 5 to 80 percent by weight, based on the total weight of olefin polymer and vinyl monomer used, of at least one vinyl monomer capable of being polymerized by free radicals;

(c) simultaneously or successively in optional order,

(1) beating the resultant grafted particulate olefin polymer material to a temperature of at least 110.degree. C., thereby deactivating substantially completely all residual free radicals therein, and

(2) removing any unreacted vinyl monomer from said material;

the particulate olefin polymer material being maintained in a substantially non-oxidizing environment throughout steps (a) to (c) at least until after the deactivation of residual free radicals has been completed.

2. The method of claim 1 wherein the particulate material of (b) is agitated and treated with monomer at a rate which is low enough to keep the material free-flowing.

3. The method of claim 2 wherein the treatment with monomer is by releasing a mist of liquid droplets onto the agitated particles.

4. The method of claim 1 wherein said irradiated particulate material is treated with vinyl monomer at a temperature in the range of about from 10.degree. to 50.degree. C.

5. The method of claim 1 wherein (b) is performed within at least two hours after the completion of (a).

6. The method of claim 1 wherein the particulate material of (a) has a pore volume fraction of at least about 0.04.

7. The method of claim 1 wherein said vinyl monomer is selected from the group consisting of vinyl-substituted aromatic, heterocyclic, and alicyclic compounds, unsaturated aliphatic carboxylic acids and derivatives thereof, unsaturated aliphatic nitriles, vinyl esters of aromatic and saturated aliphatic carboxylic acids, divinyl compounds and mixtures therof.

8. The method of claim 7 wherein said vinyl monomer is selected from the group consisting of styrene, alkyl-substituted styrenes, esters of acrylic and methacrylic acids, vinyl acetate, and mixtures therof.

9. The method of claim 8 wherein the monomer is styrene.

10. The method of claim 1 wherein the residual free radicals are deactivated by heating the grafted olefin polymer particles at a temperature of about 110.degree. C. to about 150.degree. C.

11. The method of claim 1 wherein said olefin polymer material is a homopolymer of propylene or 1-butene.