Graft polyblend flow improvers for PVC

BACKGROUND OF THE INVENTION
This invention relates to polymeric flow and impact modifiers for PVC resin, and to PVC compositions. More particularly, the invention relates to graft polyblends prepared by polymerizing acrylate ester monomers or mixtures of acrylate ester monomers and vinyl aromatic monomers in the presence of a rubbery, saturated hydrocarbon polymer substrate, which are useful as modifiers for PVC to impart improved flow and impact properties thereto, and to PVC compositions having improved flow properties.
Polyvinyl chloride (PVC) resins are commonly fabricated from powders or pellets by thermal processes including extrusion and injection molding, during which the particles must be fused into a molten mass. In conventional processing, the fusion and subsequent processing is aided by incorporation of plasticizers. These plasticizers also improve the flow and shear characteristics of the PVC resins by reducing the melt viscosity, thus enhancing the overall processability. Plasticizers, however, are not entirely satisfactory for many purposes inasmuch as they materially reduce the rigidity and heat distortion temperature of the resin when employed in amounts sufficient to improve processability.
A further method for improving processability has been to employ a blend of PVC with a second polymeric resin together with a monomeric plasticizer to compatibilize the blend. The second polymeric resin, for example, may be a block copolymer having both rigid and rubbery segments, such as those disclosed in U.S. Pat. No. 3,801,529. The presence of large amounts of plasticizer in these compositions again reduces rigidity and the heat distortion temperature of the resin. It is desirable, therefore, to provide a processing aid which can be blended with a PVC resin to improve processability of the resin without materially reducing the heat distortion temperature of the product composition.
SUMMARY OF THE INVENTION
It has now been found that particular graft polyblend compositions, when blended with PVC resins, impart a major improvement in flow properties and thus facilitate processing without a marked reduction of heat distortion temperatures. More particularly, graft polyblends prepared by polymerizing an acrylate ester, optionally together with a vinyl aromatic monomer, in the presence of a rubbery saturated hydrocarbon polymer substrate such as, for example, rubbery polymers or copolymers of mono-olefins, hydrogenated 1,2-polybutadiene or copolymers thereof, and the like, impart excellent flow properties and impact properties to PVC resins without the requirement for monomeric plasticizers, thus resulting in processable compositions which retain the heat distortion characteristics of unmodified PVC.
DETAILED DESCRIPTION
The graft polyblend compositions of this invention are prepared by copolymerizing a vinyl aromatic monomer and/or an acrylate ester monomer in the presence of a rubbery, saturated hydrocarbon polymer substrate.
The rubbery saturated hydrocarbon polymers useful as substrates for the purposes of this invention include the rubbery polymers and copolymers of two-to-six carbon atom mono-olefins such as the copolymers of ethylene and propylene known as EPR rubbers, copolymers of ethylene and 1-butene, and the polymers of isobutylene as well as the rubbery hydrogenated homopolymers and copolymers of conjugated dienes, such as hydrogenated 1,3-butadiene polymers having greater than 40% of the butadiene monomer units in the form of 1,2-polymerized units and the hydrogenated polymers of isoprene. Rubbery copolymers including both random and block copolymers of butadiene containing 1,2-polymerized butadiene units together with up to 60% of a second vinyl monomer such as styrene, vinyl toluene and the like, when hydrogenated to remove the ethylenic unsaturation, are also useful as substrates.
Hydrogenation of the conjugated diene polymers may be carried out by a variety of well-established processes, including hydrogenation in the presence of such catalysts as Raney Nickel, noble metals such as platinum, palladium and the like or the "soluble" transition metal catalysts. The preferred process is one wherein the polymer is dissolved in an inert hydrocarbon diluent such as cyclohexane and hydrogenated by reaction with hydrogen in the presence of a soluble hydrogenation catalyst. These and similar low pressure hydrogenation processes are rapidly and conveniently carried out to give virtually complete removal of aliphatic unsaturation from the diene-derived portion of polymeric substrates. In the practice of the instant invention, the hydrogenation is preferably carried out until little or no aliphatic unsaturation remains insofar as can be detected by ordinary infrared spectroscopic techniques. The technique employed for the preparative examples suffices for detecting levels of unsaturation greater than about 0.1%-0.2% by weight, corresponding to one C.dbd.C group in 1,000 to 2,000 carbon atoms.
The polyblends are made by polymerizing an acrylic ester monomer optionally together with a vinyl aromatic monomer, in the presence of the rubbery substrate. Vinyl aromatic monomers useful for these purposes include styrene, substituted styrenes such as alpha-methyl styrene, the halostyrenes such as p-chlorostyrene, and the alkyl vinyl benzenes such as vinyl toluene and vinyl ethyl benzene. The acrylic ester monomers include acrylic and methacrylic esters of C.sub.1 -C.sub.11 alcohols, exemplified by methyl methacrylate, ethyl acrylate and the like.
The composition of the graft polyblends may be varied, however, in order to be useful as a processing aid in blends with PVC, the graft polyblends will comprise from 50 to 90% by weight of rubbery substrate, and correspondingly from 50 to 10% rigid or graft phase. The graft phase will consist of from 0 to 70% by weight vinyl aromatic grafting monomer, preferably styrene, and from 100 to 30% by weight acrylate monomer, preferably methyl methacrylate. It is necessary that the content of rubbery substrate be greater than about 50% to maintain improvement in impact properties of the final PVC blend, while selection of the particular proportion of vinyl aromatic monomer and acrylic ester monomer within the given ranges will be based upon the type of rubbery substrate employed and upon the particular end use envisioned for the PVC blend composition.
The polyblends of this invention are particularly compatable with PVC, and their inclusion in PVC formulations is not detrimental to other physical properties including tensile properties. Further, the refractive index of these polyblends will depend upon the relative proportions of rubber, acrylic monomer and vinyl aromatic monomer in both the substrate and superstrate. Polyblend modifiers may thus be prepared with refractive indicies matching that of PVC and employed to provide transparent PVC formulations where desired for particular end-uses.
Conventional free-radical graft polymerization methods may be employed for preparation of these polyblend modifiers, including solution, suspension and emulsion processes. The preferred process is one whereby the rubbery substrate is converted to a cross-linked latex, and the polymerization of the grafting monomers is then carried out in the presence of this latex utilizing an oil-soluble free-radical initiator.

EXAMPLE 1
PREPARATION AND HYDROGENATION OF 1,2-POLYBUTADIENE
A sealed beverage bottle was charged with 700 ml. of cyclohexane, degassed, then pressurized with dry nitrogen. A hypodermic syringe needle was inserted through the seal, and 30.0 grams (0.56 moles) of butadiene-1,3-monomer, followed by 0.33 m. moles of N,N,N',N'-tetramethylethylene diamine and 0.3 m. moles of sec-butyl lithium (0.1 M. in cyclohexane). The bottle was then placed in a water bath at 50.degree. C. and maintained for 16 hours. An aliquot of the mixture was removed after quenching with isopropanol, from which it was determined that the polybutadiene had .eta.=1.63 (toluene, 25.degree. C.) and a microstructure corresponding to 69% content of 1,2-polymerized units.
Hydrogenation of the polybutadiene was carried out on the above polymer solution after diluting with dry cyclohexane to a concentration of 20 g/liter of solution.
A two-layer stirred reactor was charged with 1500 ml. of the above cyclohexane solution of 1,2-polybutadiene, together with 0.3 mole percent (based on double bonds) of a "soluble cobalt" catalyst.
"Soluble cobalt" catalysts may be prepared by adding 14.1 g. of a cobalt (II) octoate solution containing 12.0 weight percent cobalt over a period of 90 minutes to 287 ml. of a cyclohexane solution containing 0.0854 moles of s-butyl lithium. The product is a 0.091 m. solution of "soluble cobalt" catalyst having a Li/Co molar ratio of 3.0/1. An alternative preparation of "soluble cobalt" catalysts involves the addition of 23.6 g. of cobalt (II) octoate solution over a period of 90 minutes to a solution of 18.8 g. of triethyl aluminum in 494.6 g. of cyclohexane. The product is a 0.081 M solution of soluble cobalt catalyst having a 3.0/1 Al/Co molar ratio.
The hydrogenation reaction was maintained at 50.degree. C. and hydrogen gas was bubbled into the reactor at 50 psi until no detectable unsaturation remained as determined for an aliquot sample by infrared analysis. The mixture was then removed from the reactor, extracted with dilute aqueous acid to remove catalyst residues, coagulated by pouring into isopropanol, collected and dried at 40.degree. C. in a vacuum oven.
EXAMPLE 2
PREPARATION OF POLYBLENDS BY SOLUTION--PRECIPITATION POLYMERIZATION
A solution of hydrogenated 1,2-polybutadiene, prepared by dissolving 50 g. of hydrogenated 1,2-polybutadiene obtained as in Example 1 in 500 ml. of 1:1 (w/w) benzenehexane solvent mixture, were charged to a resin kettle, together with 25 g. of styrene monomer, 25 g. of methyl methacrylate monomer and 2.0 g. of benzoyl peroxide. The resin kettle was placed in a thermostated water bath heated to 72.degree. C. and the mixture was stirred for 20 hours. The product is observed to precipitate during polymerization in this solvent mixture, giving a swollen polymer/solvent mixture. The mixture was coagulated in isopropanol and the solid, when collected by filtration, dried at 60.degree. C. under vacuum and weighed, amounted to 100 g.
EXAMPLE 3
PREPARATION OF POLYBLENDS BY LATEX POLYMERIZATION
A solution of 80 g. of hydrogenated 1,2-polybutadiene in 800 ml. of cyclohexane prepared as in Example 1 was added to 800 ml. of water containing 1.6 g. of benzoyl peroxide and a surfactant and stirred using a Premier Mill Dispersator device. The resulting mixture was then passed immediately through a homogenizer to produce a latex.
The resulting latex was heated 20 hours at 72.degree. C. to effect substrate crosslinking. Solvent was removed by distillation to give a solvent-free aqueous latex. Coagulation during this step amounted to less than 1/2%. Any coagulum present was removed by filtration through cheese cloth.
A mixture containing 10 g. of styrene monomer, 10 g. of methyl metacrylate and 2.0 g. of benzoyl peroxide was added to the latex. The reaction mixture was stirred at 72.degree. C. for 20 hours, and poured into isopropanol to effect product coagulation. The solid, collected, dried at 60.degree. C. in a vacuum oven, and weighed, amounted to 100 g.
EXAMPLE 4
GRAFT POLYBLEND WITH A COPOLYMER RUBBER SUBSTRATE
A styrene 1,2-polybutadiene rubber was prepared by anionic polymerization of a mixture of 50 parts styrene and 50 parts 1,3-butadiene substantially as shown in U.S. Pat. No. 3,598,886, Example 1. The rubbery product was hydrogenated by the method of Example 1 to provide a hydrogenated rubber having no detectable unsaturation.
A solution of 80 g. of hydrogenated styrene-high-vinyl butadiene rubber in 800 ml. of cyclohexane was added to 800 ml. of water containing 1.6 g. of benzoyl peroxide, converted to a latex and crosslinked by heating at 72.degree. C. as in Example 3. A mixture containing 10 g. of styrene monomer, 10 g. of methyl methacrylate and 2.0 g. of benzoyl peroxide was added to the latex, the mixture was stirred at 72.degree. C. for 20 hours and then poured into isopropanol to effect coagulation. The solid, collected, dried at 60.degree. C. in a vacuum oven, and weighed, amounted to 100 g.
The PVC resin employed may be any of the conventional extrusion and injection molding PVC resins, including vinyl chloride polymers and copolymers wherein the major component of the resin is vinyl chloride. The blends of PVC with the processing aids of this invention will comprise from about 3 to about 25 parts by weight of graft polyblend flow improver per 100 parts by weight of PVC. The blends may be further compounded to include stabilizers, pigments, lubricants and the like.
The following examples illustrate the preparation of blends typical of this invention. All blends shown were prepared by a standard procedure in which the following masterbatch formulation, in combination with the indicated amount of graft polyblend, was mill-mixed at 360.degree. F. for 10 minutes, then a portion was compression molded at 450.degree. F. for 4 to 10 minutes to provide test specimens.
EXAMPLE 5
PVC MASTERBATCH FORMULATION
______________________________________Material Tradename and Source Parts by Weight______________________________________PVC Geon 93, B. F. Goodrich 100 Chemical Co.Processing Acrylic K120N, Rohm and Haas. 2.0Aid Co.Tin Mark 1414A, Argus Chemical 2.0Stabilizer Corp.Lubricant Hoechst Wax E, Farbwerke 0.4 Hoechst, AGLubricant Aldo MS, Glyco Chemicals, Inc. 0.9Toner 0.075______________________________________
The graft polyblends used as modifiers were prepared in accordance with Examples 2-4, using the amount of styrene and/or methyl methacrylate and the particular substrates shown in the tables below.
TABLE I______________________________________Example Modifier.sup.1 HDT.sup.2 .eta.a.sup.3No. Type Parts .degree.C. 200 .gamma. 10.sup.3 .gamma.______________________________________5 None 0 69 0.35 0.00946 20 (S/MMA) 5.8 68 0.14 0.050 80 PBd-R7 50 (S/MMA) 5.8 70 0.13 0.054 50 PBd-R8 20 (S/MMA) 5.8 69 0.25 0.017 80 (50SBd-R)9 Diphenyl 5.8 58 0.19 0.058 phthalate10 Dicyclohexyl 5.8 58 0.20 0.064 phthalate______________________________________ Notes: .sup.1 20 (S/MMA)80PBdR = 20 parts styrene/methyl Methacrylate (1:1) polymerized in presence of 80 parts hydrogenated 1,2polybutadiene. See Example 3. 20 (S/MMA) 80(50SBdR) = 20 parts (S/MMA) (1:1) polymerized in presence of 80 parts hydrogenated 50% styrene50% 1,2butadiene copolymer. See Example 4. Wt. % of total composition using masterbatch of Example 5. Parts = Parts polyblend per 100 parts PVC .sup.2 HDT 264 psi heat distortion temperature, 10 mil deflection. .sup.3 .eta.a = apparent viscosity at low shear (200 .gamma.) and high shear (10.sup.3 .gamma.), Monsanto automatic Capillary Rheometer, 375.degree. F., L/D 20 Cap No. 201.
It will be seen from the viscosity data in TABLE I that the modifiers of this invention produce marked lowering of apparent melt viscosity. In Example 5, the PVC masterbatch without modifier has a high shear apparent viscosity nearly twice as great as those of the modified blends, Examples 6-8. The two low-molecular weight commercial flow modifiers shown in Examples 9 and 10 also effect a decrease in melt viscosity. However, the heat distortion temperature is depressed more than 10.degree. C. for the commercial compositions of Examples 9 and 10, while the modifiers of the instant invention, in Examples 6-8 do not significantly affect heat distortion temperature as compared with the unmodified masterbatch, Example 5.
TABLE II______________________________________Example Modifier.sup.1 Izod.sup.2 Melt.sup.3No. Type Parts Impact Flow______________________________________ 5 None 0 0.4 8.711 15 (S/MMA) 19.4 0.4 Too fast 80 PBd-R12 20 (S/MMA) 19.4 0.7 516 85 PBd-R13 35 (S/MMA) 19.4 1.2 516 65 PBd-R14 50 (S/MMA) 19.4 1.5 Too fast 50 PBd-R15 20 MMA 19.4 14.1 207 80 PBd-R______________________________________ Notes: .sup.1 See Note 1., TABLE I. .sup.2 Notched Izod Impact, 23.degree. C., ft lb/in notch. .sup.3 Melt Flow, cc/10 min., Monsanto Capillary Rheometer, L/D = 20/1, 140 psi, 375.degree. F. Too Fast = flow rate too fast to measure.
The marked improvement of melt flow properties in PVC compositions is again demonstrated at the 19.4 phr level as shown in TABLE II, where melt flow is given in cc/10 min. The modifiers of this invention clearly effect a many-fold increase in melt flow as compared with that of the unmodified masterbatch of Example 5.
Improvement in impact properties does not appear to be a function of rubber alone, in that the high rubber content of the modifier in Examples 11 and 12 produce little or no impact modification, while the comparable high-rubber, styrene-free modifier of Example 15 gave a markedly-enhanced Izod impact. That other factors are involved in impact improvement is further demonstrated by the data shown in TABLE III.
TABLE III______________________________________Example Modifier.sup.1 Izod.sup.2No. Type Parts Impact______________________________________16 20 (S/MMA) 19.4 2.9 80 PBd-R (Low Peroxide)17 5 (S/MMA) 19.4 5.1 95 (52SBd-R)18 20 (S/MMA) 19.4 12.7 80 (52 SBd-R)______________________________________ Notes: .sup.1 See Note 1. of TABLE I. .sup.2 See Note 2 of TABLE II.
The impact improvement with Example 16 was considerably greater than with Example 12. The major difference in the modifier being that only 0.5 wt. % of peroxide was used in the preparation of the modifier of Example 16, while in all other examples 1.0 wt. % peroxide was employed to prepare the modifier. Examples 17 and 18, using a hydrogenated high styrene (52%) rubber as the substrate, also gave much better impacts than resulted with most of the modifiers based on hydrogenated high vinyl polybutadiene substrates. Thus it will be apparent that optimization of a particular modifier composition will be necessary where both high impact and high melt flow properties are sought.
In the following Examples a masterbatch was again formulated employing Geon 103 EP as the PVC. The following masterbatch formulation, together with 5 parts of the indicated graft polyblend, was mill-mixed at 360.degree. F. for 10 minutes, then compression molded at 450.degree. for 4 to 10 minutes.
EXAMPLE 19
PVC MASTERBATCH FORMULATION
______________________________________Material Tradename Parts by Weight______________________________________PVC Geon 103 EP 100Processing Aid Acryloid K-120N 3.0Tin Stabilizer Mark 1414A 3.0Lubricant Hoechst Wax E 0.5Lubricant Hoechst Wax PA-190 0.15______________________________________
TABLE IV__________________________________________________________________________Example 19No. (Control) 20 21 22__________________________________________________________________________Modifier.sup.1 None 20 S/MMA 20 (S/MMA) 35 (S/MMA) 80 PBd-R 80 (52 SBd-R) 65 (52 SBd-R)HDT, .degree.F..sup.2 177 182 183 183Izod Impact.sup.3 0.89 1.7 1.4 0.94Transmission %.sup.4 84.4 34.7 82.1 72.8Haze %.sup.4 10.3 97.7 14.6 33.1Tensile Str. psi 7900 6600 6650 6900E % >100 >100 85 45Tensile Mod. psi 4.3 .times. 10.sup.5 3.8 .times. 10.sup.5 3.7 .times. 10.sup.5 3.8 .times. 10.sup.5Melt Viscosity.sup.5at 30 sec.sup.-1 13.0 .times. 10.sup.5 5.0 .times. 10.sup.5 10.8 .times. 10.sup.5 9.4 .times. 10.sup.5at 200 sec.sup.-1 3.20 .times. 10.sup.5 1.59 .times. 10.sup.5 2.60 .times. 10.sup.5 2.85 .times. 10.sup.5at 1000 sec.sup.-1 0.74 .times. 10.sup.5 0.54 .times. 10.sup.5 0.64 .times. 10.sup.5 0.79 .times. 10.sup.5__________________________________________________________________________ Notes: .sup.1 See Table I, note 1. .sup.2 See Table I, note 2. .sup.3 See Table II, note 2. .sup.4 Transmission and Haze for 70 mil molded plaques. .sup.5 Melt Viscosity by SieglaffMcKelvey Capillary Melt Rheometer at 390.degree. F., r = 0.4949 cm.
It is again apparent from these data that the melt flow properties of PVC are markedly altered by incorporating small amounts of the modifiers of this invention. Both clear (Example 21) and translucent (Example 20) PVC compositions may be prepared by selection of modifiers with the appropriate refractive indicies, and the compatability of these modifiers with PVC will be seen to provide good retention of tensile properties.
EXAMPLE 23
A graft polyblend was prepared according to the process of Example 3, but using as the rubbery substrate 80 parts of a hydrogenated styrene-diene-styrene block copolymer, obtained from Shell Chemical Co. as Kraton G. The product, a 20 S/MMA 80 Kraton G graft polyblend (5 parts) was added to the PVC masterbatch formulation of Example 19 and the composition was milled and molded as before. This blend had an Izod impact of 1.2 ft. lbs/in. notch and an HDT of 180.degree. F. The Melt Viscosity, measured by capillary rheometer as described for the Examples in Table IV was 10.9.times.10.sup.5 at 30 sec.sup.-1, 2.99.times.10.sup.5 at 200 sec.sup.-1, and 0.73 at 1000 sec.sup.-1, again demonstrating that significant improvement in melt flow properties is imparted to PVC compositions by the polyblends of this invention.
EXAMPLE 24
A graft polyblend was prepared by the process of Example 3, but employing as the rubbery substrate 80 grams of an ethylene-propylene copolymer rubber (EPR), obtained as EPCAR 505 from the B. F. Goodrich Co. The product, a 20 (S/MMA) 80 EPR polyblend, was then blended at levels of 5.8 and 19.4 phr with the PVC masterbatch formulation of Example 5. The property data are given in Table V.
EXAMPLE 25
A graft polyblend was prepared by the method of Example 3, but 80 g. of polyisobutylene (PIB) obtained as Vistanex L140 from Enjay Chemical Co., were used as the rubbery substrate. The product, a 20 (S/MMA) 80 PIB polyblend, was then blended at 5.8 and 19.4 phr levels with the PVC masterbatch formulation of Example 5. The property data are given in Table V.
TABLE V______________________________________Example Modifier.sup.1 HDT.sup.2 .eta.a.sup.3 Melt.sup.4No. Type Parts .degree.C. 200 .gamma. 10.sup.3 .gamma. Flow______________________________________ 5 None 0 69 0.35 0.0094 8.724 20 (S/MMA) 5.8 76 0.20 0.062 -- 80 EPR24 20 (S/MMA) 19.4 74 -- -- 129 80 EPR25 20 (S/MMA) 5.8 76 0.19 0.046 -- 80 PIB25 20 (S/MMA) 19.4 76 -- -- Too 80 PIB Fast______________________________________ Notes: .sup.1 Modifiers from Examples 24 and 25 in blend compositions with PVC masterbatch formulation of Example 5. .sup.2 See note 2, Table I. .sup.3 See note 3, Table I. .sup.4 See note 3, Table II.
It will be apparent from these data that graft polyblends employing rubbery polymers and copolymers of monoolefins as the rubbery saturated hydrocarbon polymer substrate are also effective as melt flow modifiers for PVC.
The instant invention will thus be seen to be graft polyblends prepared by polymerizing from 0 to 35 parts by weight vinyl aromatic monomer and from 3.7 to 50 parts by weight acrylic or methacrylic ester monomer in the presence of a rubbery saturated hydrocarbon polymer. These graft polyblends are modifiers for PVC, and when employed in amounts of from 3 to 25 parts polyblend per 100 parts of PVC, markedly improve the melt flow properties of the resin.
While the examples provided amply illustrate the practice of this invention, it will be apparent to one skilled in the art that further modifications and variations are possible and the examples therefore are provided by way of illustration and not for limitation of the scope of the invention, which is defined solely by the appended claims.

Number	Name	Date	Kind
3316327	Baer et al.	Apr 1967
4021510	Ueshima et al.	May 1977

	Number	Date	Country
Parent	100624	Dec 1979
Parent	690112	May 1976

Graft polyblend flow improvers for PVC

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Parent Case Info

US Referenced Citations (2)

Divisions (1)

Continuations (2)