Patent Application
20180037966
The disclosure relates to a grain-oriented electrical steel sheet having excellent iron loss property and a method for producing the grain-oriented electrical steel sheet, and is particularly intended to obtain a grain-oriented electrical steel sheet having excellent magnetic property at low cost.
A grain-oriented electrical steel sheet is a soft magnetic material used as an iron core material of a transformer or generator, and has crystal texture in which <001> orientation which is the easy magnetization axis of iron is highly accumulated into the rolling direction of the steel sheet. Such texture is formed through secondary recrystallization of preferentially causing the growth of giant crystal grains in (110)[001] orientation which is called Goss orientation, when secondary recrystallization annealing is performed in the process of producing the grain-oriented electrical steel sheet.
A conventional process of producing such a grain-oriented electrical steel sheet is as follows.
A slab containing about 4.5 mass % or less Si and an inhibitor component such as MnS, MnSe, and AlN is heated to 1300° C. or more to dissolve the inhibitor component. The slab is then hot rolled, and optionally hot band annealed. The hot rolled sheet is then cold rolled once, or twice or more with intermediate annealing therebetween, to final sheet thickness. The cold rolled sheet is then subjected to primary recrystallization annealing in a wet hydrogen atmosphere, to perform primary recrystallization and decarburization. After this, an annealing separator having magnesia (MgO) as a main ingredient is applied to the primary recrystallization annealed sheet, and then final annealing is performed at 1200° C. for about 5 h to develop secondary recrystallization and purify the inhibitor component (for example, the specification of U.S. Pat. No. 1,965,559 A (PTL 1), JP S40-15644 B2 (PTL 2), and JP S51-13469 B2 (PTL 3)).
PTL 1: U.S. Pat. No. 1,965,559 A
PTL 2: JP S40-15644 B2
PTL 3: JP S51-13469 B2
PTL 4: JP 2000-129356 A
PTL 5: JP 2004-353036 A
As described above, the grain-oriented electrical steel sheet is conventionally manufactured by the process of containing a precipitate (inhibitor component) such as MnS, MnSe, and AlN in the slab stage, heating the slab at a high temperature exceeding 1300° C. to dissolve the inhibitor component, and causing fine precipitation in the subsequent step to develop secondary recrystallization. Thus, high-temperature slab heating exceeding 1300° C. is necessary in the conventional grain-oriented electrical steel sheet manufacturing process, which requires very high manufacturing cost. The conventional process therefore has a problem of being unable to meet the recent demands to reduce manufacturing costs.
To solve this problem, a technique (inhibitorless method) for enabling secondary recrystallization without containing any inhibitor component was developed in JP 2000-129356 A (PTL 4). This method involves a completely different technical idea from that of the conventional grain-oriented electrical steel sheet producing method.
In detail, while the conventional grain-oriented electrical steel sheet producing method develops secondary recrystallization using a precipitate (inhibitor) such as MnS, AlN, and MnSe, the inhibitorless method develops secondary recrystallization by texture (texture control) through high purification without using such an inhibitor. The inhibitorless method does not require high-temperature slab heating and high-temperature and long-duration secondary recrystallization annealing, and so enables the manufacture of the grain-oriented electrical steel sheet at low cost.
However, the inhibitorless method cannot necessarily achieve sufficient magnetic property and stability, although it is advantageous in that the grain-oriented electrical steel sheet can be manufactured at low cost.
To solve this problem, we further studied the technique of developing secondary recrystallization without containing any inhibitor component in the slab. As a result, we developed and proposed a technique (sulfurization method) that can stably develop secondary recrystallization by increasing the amount of S in the steel substrate after the primary recrystallization annealing and before the completion of secondary recrystallization, even in the case where no inhibitor component is contained in the slab (JP 2004-353036 A (PTL 5)).
By increasing the amount of S in the steel substrate using the sulfurization method, the amount of S segregating to grain boundaries increases, as a result of which the movement of grain boundaries surrounding orientations other than the Goss orientation is further suppressed. This stabilizes secondary recrystallization, and enhances the sharpness of secondary grains to the Goss orientation, with it being possible to improve magnetic property.
However, there is a problem in that the addition of a large amount of sulfurization agent causes excessive oxidation reaction during the secondary recrystallization annealing, and leads to the formation of a base film defective part called sparkle or frost.
As is well known, grain-oriented electrical steel sheets are mainly used as transformer iron cores. Transformers are broadly classified into stacked iron core transformers and wound iron core transformers, depending on their iron core structures.
A stacked iron core transformer has an iron core formed by stacking steel sheets cut to a desired shape. A wound iron core transformer has an iron core formed by winding a steel strip slit to a desired width. As large-capacity transformers, stacked iron core transformers are used exclusively.
An important property required of transformers is transformer core loss. Transformer core loss is energy loss when a transformer iron core is excited. Higher transformer core loss leads to higher power loss, and so transformer core loss needs to be as low as possible.
However, iron loss can degrade as a result of processing a steel sheet into a transformer.
For example, there are instances where low iron loss cannot be maintained when pinch rolls for conveying the steel sheet or measuring rolls for measuring the length of the steel sheet are pressed against the steel sheet.
In such instances, even when a transformer is formed using a steel sheet whose iron loss is lowered by a magnetic domain refining effect such as a linear flaw, its iron loss value may not be as low as expected. Particularly in the case of using the steel sheet for a stacked iron core transformer, stress relief annealing is not performed after processing the steel sheet into the iron core, and so problems such as degraded iron loss and increased noise can arise.
The conventional technique of adding a sulfurization agent has difficulty in forming the base film, and therefore has a problem in that the influence of strain associated with processing into a transformer is significant and transformer core loss degrades.
It could be helpful to propose a grain-oriented electrical steel sheet that has excellent magnetic property and can be produced at low cost with no need for high-temperature slab heating and whose transformer core loss is effectively improved by reducing the influence of strain associated with processing into a transformer, and an advantageous method for producing the grain-oriented electrical steel sheet.
We closely examined the technique of developing secondary recrystallization without containing any inhibitor component in a slab and improving magnetic property by sulfurization treatment.
As a result, we developed a technique that can stably realize favorable base film formation by optimizing material components even in the case where sulfurization treatment is performed.
The following describes the experimental results that led to the disclosure. In the following description, “%” with regard to components denotes mass % unless otherwise stated.
A silicon steel slab containing, in mass %, Si: 3.3%, C: 0.03%, Mn: 0.07%, S: 0.002%, Al: 0.006%, and N: 0.003% and further containing P and Sb in the ranges of P: 0% to 0.2% and Sb: 0% to 0.2% was heated at 1220° C. for 30 minutes, and then hot rolled to obtain a hot rolled sheet of 2.5 mm in thickness. The hot rolled sheet was hot band annealed at 1025° C. for 1 minute, and then cold rolled to final sheet thickness.
Following this, the cold rolled sheet was primary recrystallization annealed, and then an annealing separator having MgO as a main ingredient and containing 10% magnesium sulfate was applied at 12.5 g/m2 to the primary recrystallized sheet and dried. The primary recrystallized sheet was then secondary recrystallization annealed under the following condition: heating rate: 15° C./h, atmosphere gas: N2 gas up to 900° C., and H2 gas at 900° C. or more, and soaking treatment: 1160° C. for 5 h.
As illustrated in
Although the effect of adding P and Sb in combination is not clear, we assume the following:
P is a grain boundary segregation element, and has a function of suppressing recrystallization nucleation from the grain boundaries and facilitating recrystallization nucleation from inside the grains to increase the Goss orientation in the primary recrystallized texture. P thus has an effect of stabilizing secondary recrystallization nucleation and improving magnetic property. However, the addition of P has an adverse effect of facilitating surface oxidation during the secondary recrystallization annealing and hindering the sulfurization effect and also hindering normal base film formation.
Sb is a surface segregation element, and has a function of suppressing oxidation during the secondary recrystallization annealing to optimize the oxidation quantity and stabilize secondary recrystallization and base film formation. Sb thus has an effect of lessening the adverse effect of the addition of P.
Accordingly, adding Sb and P in combination is very effective in achieving the aforementioned texture improving effect by the addition of P.
The phenomenon of improving magnetic property by sulfurization is specific to the case where the steel slab contains no inhibitor component. In the case where there is no inhibitor (precipitate) such as AlN and MnS in the steel, the grain boundaries surrounding the Goss-oriented grains in the primary recrystallized texture have higher mobility than the grain boundaries surrounding the grains in the other orientations, as a result of which the Goss orientation undergoes preferential growth (secondary recrystallization).
Although the reason why magnetic property is improved by increasing the amount of S in the steel substrate after primary recrystallization is not clear, we assume the following:
When the amount of S in the steel substrate is increased, the amount of S segregating to grain boundaries increases, as a result of which the movement of the grain boundaries surrounding the orientations other than the Goss orientation is further suppressed. This stabilizes secondary recrystallization, and enhances the sharpness of secondary grains to the Goss orientation. The coexistence of P and S which are elements having a strong tendency to segregate to grain boundaries further enhances the magnetic property improving effect.
Moreover, regarding the method of reducing the influence of strain associated with processing into a transformer, we studied the condition of the flattening annealing atmosphere, and discovered that the magnetic property in the rolling transverse direction (the direction orthogonal to the rolling direction) changes, and there is a very high correlation between the magnetic property in the transverse direction and the influence of strain associated with processing into a transformer.
We then discovered a preferable range of the magnetic property in the transverse direction effective in reducing the influence of strain, as described below.
A silicon steel slab containing, in mass %, Si: 3.3%, C: 0.03%, Mn: 0.07%, S: 0.002%, Al: 0.006%, N: 0.003%, P: 0.05%, and Sb: 0.05% was heated at 1220° C. for 30 minutes, and then hot rolled to obtain a hot rolled sheet of 2.5 mm in thickness. The hot rolled sheet was hot band annealed at 1025° C. for 1 minute, and then cold rolled to final sheet thickness.
Following this, the cold rolled sheet was primary recrystallization annealed, and then an annealing separator having MgO as a main ingredient and containing 10% magnesium sulfate was applied at 12.5 g/m2 to the primary recrystallized sheet and dried. The primary recrystallized sheet was then secondary recrystallization annealed under the following condition: heating rate: 15° C./h, atmosphere gas: N2 gas up to 900° C., and H2 gas at 900° C. or more, and soaking treatment: 1160° C. for 5 h.
Further, an insulating coating mainly composed of colloidal silica and magnesium phosphate was applied. An experiment of changing the soaking temperature (soaking time of 10 s) and the H2 partial pressure (the rest being N2 atmosphere) in the annealing atmosphere in flattening annealing was then conducted under the conditions shown in Table 1.
The magnetic property of the obtained product in each of the rolling direction and the transverse direction was measured. In the rolling direction, the iron loss (W17/50) when exciting the product to 1.7 T at 50 Hz was measured. In the transverse direction, the magnetizing force (TD-H10) and iron loss (TD-W10) when exciting the product to 1.0 T at 50 Hz were measured. Strain sensitivity was evaluated based on the change (ΔW) in iron loss W17/50 value when passing the sheet while pressing it by measuring rolls, which were made up of steel rolls of 100 mm in diameter and 50 mm in width, with a rolling reduction force of 1.5 MPa (15 kgf/cm).
Table 1 shows the obtained results.
As illustrated in
As illustrated in
As illustrated in
As illustrated in
The aforementioned experiment revealed that the flattening annealing temperature and the hydrogen partial pressure in the flattening annealing atmosphere influenced the iron loss (W17/50) in the rolling direction, the iron loss degradation (ΔW) upon measuring roll rolling reduction, the iron loss (TD-W10) in the transverse direction, and the magnetizing force (TD-H10) in the transverse direction. We then studied their correlations.
As illustrated in
In other words, the iron loss in the transverse direction serves as an index of residual strain.
The results in
As illustrated in
In other words, the magnetizing force in the transverse direction serves as an index of film tension.
The results in
It is assumed that, by increasing the flattening annealing temperature and introducing the hydrogen atmosphere, the water content in the coating mainly composed of phosphate is reduced to strengthen the coating film tension.
The disclosure is based on the results of the two experiments described above and further studies.
In detail, we provide the following:
1. A grain-oriented electrical steel sheet having a composition containing (consisting of), in mass %, C: 0.005% or less, Si: 2.0% to 4.5%, and Mn: 0.5% or less, and also containing Sb and P in respective ranges satisfying 0.01%≦[% Sb]≦0.20% and 0.02%≦[% P]≦2.0×[% Sb], with a balance being Fe and incidental impurities,
wherein when the steel sheet is excited to 1.0 T at 50 Hz in a rolling transverse direction, a magnetizing force (TD-H10) and an iron loss (TD-W10) are respectively (TD-H10)≧200 A/m and (TD-W10)≧1.60 W/kg.
2. The grain-oriented electrical steel sheet according to 1, wherein the composition further contains, in mass %, one or more selected from Ni: 0.005% to 1.50%, Sn: 0.03% to 0.20%, Cu: 0.02% to 0.50%, Cr: 0.02% to 0.50%, Mo: 0.01% to 0.50%, and Nb: 0.002% to 0.01%.
3. A method for producing a grain-oriented electrical steel sheet, comprising:
providing a steel slab having a composition containing, in mass %, C: 0.08% or less, Si: 2.0% to 4.5%, and Mn: 0.5% or less, containing each of S, Se, and O: less than 50 ppm, N: less than 60 ppm, and sol.Al: less than 100 ppm, and also containing Sb and P in respective ranges satisfying 0.01%≦[% Sb]≦0.20% and 0.02%≦[% P]≦2.0×[% Sb], with a balance being Fe and incidental impurities;
optionally reheating the steel slab;
thereafter hot rolling the steel slab to obtain a hot rolled sheet;
optionally hot band annealing the hot rolled sheet;
thereafter cold rolling the hot rolled sheet either once, or twice or more with intermediate annealing performed therebetween, to obtain a cold rolled sheet having a final sheet thickness;
thereafter performing decarburization and primary recrystallization annealing on the cold rolled sheet, to obtain a decarburization and primary recrystallization annealed sheet;
thereafter applying an annealing separator mainly composed of MgO to the decarburization and primary recrystallization annealed sheet;
thereafter performing secondary recrystallization annealing on the decarburization and primary recrystallization annealed sheet, to obtain a secondary recrystallization annealed sheet; and
further performing flattening annealing on the secondary recrystallization annealed sheet,
wherein 2.0 mass % to 15.0 mass % magnesium sulfate is contained in the annealing separator,
the flattening annealing is performed at a temperature of 830° C. or more in an atmosphere having a H2 partial pressure of 0.3% or more, and
when the steel sheet is excited to 1.0 T at 50 Hz in a rolling transverse direction, a magnetizing force (TD-H10) and an iron loss (TD-W10) are respectively (TD-H10)≧200 A/m and (TD-W10)≧1.60 W/kg.
It is thus possible to produce a grain-oriented electrical steel sheet having excellent transformer core loss industrially stably at low cost, which is of great industrial value.
In the accompanying drawings:
One of the disclosed embodiments is described in detail below.
The reasons for limiting the chemical composition of a steel slab to the aforementioned range in this embodiment are described first.
C: 0.08% or less
C is an element useful in improving primary recrystallized texture. If the C content is more than 0.08%, however, the primary recrystallized texture degrades. The C content is therefore limited to 0.08% or less. The C content is desirably in the range of 0.01% to 0.06%, in terms of magnetic property. In the case where the required level of magnetic property is not so high, the C content may be 0.01% or less in order to omit or simplify decarburization in primary recrystallization annealing.
Moreover, it is essential to reduce the C content to 0.005% or less in the steel sheet after final annealing, in order to prevent magnetic aging.
Si: 2.0% to 4.5%
Si is an element useful in improving iron loss by increasing electrical resistance, and so the Si content is 2.0% or more. If the Si content is more than 4.5%, however, cold rolling manufacturability decreases significantly. The upper limit of the Si content is therefore 4.5%. The addition of Si may be omitted depending on the required iron loss level.
Mn: 0.5% or less
Mn has an effect of improving hot workability during manufacture.
If the Mn content is more than 0.5%, however, the primary recrystallized texture deteriorates and leads to lower magnetic property. The Mn content is therefore limited to 0.5% or less. The lower limit of the Mn content is preferably 0.05%.
S, Se, and O: less than 50 ppm each
If the content of each of S, Se, and O is 50 ppm or more, secondary recrystallization is difficult. This is because a coarse oxide or MnS or MnSe coarsened due to slab heating makes the primary recrystallized texture non-uniform. The content of each of S, Se, and O is therefore limited to less than 50 ppm.
N: less than 60 ppm
Excessive N also makes secondary recrystallization difficult, as with S, Se, and O. Particularly if the N content is 60 ppm or more, secondary recrystallization is unlikely to occur, and the magnetic property degrades. The N content is therefore limited to less than 60 ppm.
sol.Al: less than 100 ppm
Excessive Al also makes secondary recrystallization difficult. Particularly if the sol.Al content is 100 ppm or more, secondary recrystallization is unlikely to occur under the low-temperature slab heating condition, and the magnetic property degrades. Al is therefore limited to less than 100 ppm in sol.Al content.
Sb and P: 0.01%≦[% Sb]≦0.20% and 0.02%≦[% P]≦2.0×[% Sb] respectively
In this embodiment, it is important to contain Sb and P in combination in these respective ranges. By adding Sb and P in combination in these ranges, the desired sulfurization effect in this embodiment is effectively achieved, and magnetic property degradation due to surface oxidation is suppressed. As a result, favorable magnetic property and base film property can be obtained throughout the coil length. If the Sb content or the P content is less than the aforementioned range, the effect cannot be achieved. If the Sb content or the P content is more than the aforementioned range, not only the magnetic property degrades, but also the formation of the base film is difficult.
While the essential components have been described above, the following elements may be contained as appropriate as components for improving the magnetic property industrially more stably in this embodiment.
Ni has a function of improving the magnetic property by enhancing the uniformity of the hot rolled sheet texture. To do so, the Ni content is preferably 0.005% or more. If the Ni content is more than 1.50%, secondary recrystallization is difficult, and the magnetic property degrades. Accordingly, the Ni content is desirably in the range of 0.005% to 1.50%.
Sn: 0.03% to 0.20%
Sn has a function of suppressing the nitriding or oxidation of the steel sheet during secondary recrystallization annealing and promoting the secondary recrystallization of crystal grains having favorable crystal orientation to effectively improve the magnetic property, in particular the iron loss property. To do so, the Sn content is preferably 0.03% or more. If the Sn content is more than 0.20%, cold rolling manufacturability decreases. Accordingly, the Sn content is desirably in the range of 0.03% to 0.20%.
Cu: 0.02% to 0.50%
Cu is a useful element that suppresses the nitriding or oxidation of the steel sheet during secondary recrystallization annealing and promotes the secondary recrystallization of crystal grains having favorable crystal orientation to effectively improve the magnetic property. To do so, the Cu content is preferably 0.02% or more. If the Cu content is more than 0.50%, cold rolling manufacturability decreases. Accordingly, the Cu content is desirably in the range of 0.02% to 0.50%.
Cr: 0.02% to 0.50%
Cr has a function of stabilizing the formation of the forsterite base film. To do so, the Cr content is preferably 0.02% or more. If the Cr content is more than 0.50%, secondary recrystallization is difficult, and the magnetic property degrades. Accordingly, the Cr content is desirably in the range of 0.02% to 0.50%.
Mo: 0.01% to 0.50%
Mo has a function of suppressing high-temperature oxidation and reducing surface defects called scab. To do so, the Mo content is preferably 0.01% or more. If the Mo content is more than 0.50%, cold rolling manufacturability decreases. Accordingly, the Mo content is desirably in the range of 0.01% to 0.50%.
Nb: 0.002% to 0.01%
Nb is a useful element that inhibits the growth of primary recrystallized grains and promotes the secondary recrystallization of crystal grains having favorable crystal orientation to improve the magnetic property. To do so, the Nb content is desirably 0.002% or more. If the Nb content is more than 0.01%, Nb remains in the steel substrate and degrades the iron loss. Accordingly, the Nb content is desirably in the range of 0.002% to 0.01%.
The following describes a production method in this embodiment.
A steel slab adjusted to the aforementioned chemical composition range is, after or without being reheated, hot rolled. In the case of reheating the slab, the reheating temperature is desirably about 1000° C. or more and 1300° C. or less. Slab heating exceeding 1300° C. is meaningless in this embodiment in which the slab contains no inhibitor, and not only causes an increase in cost but also significantly degrades the magnetic property due to the growth of giant crystal grains. If the reheating temperature is less than 1000° C., the rolling load increases, making the rolling difficult.
Following this, the hot rolled sheet is optionally hot band annealed. The hot rolled sheet is then cold rolled once, or twice or more with intermediate annealing therebetween, to obtain a final cold rolled sheet. The cold rolling may be performed at normal temperature. Alternatively, the cold rolling may be warm rolling with the steel sheet temperature being higher than normal temperature, e.g. about 250° C.
The final cold rolled sheet is then subjected to decarburization/primary recrystallization annealing. A first objective of the decarburization/primary recrystallization annealing is to cause the primary recrystallization of the cold rolled sheet having rolled microstructure to adjust it to an optimal primary recrystallized texture for secondary recrystallization. For this objective, the annealing temperature in the primary recrystallization annealing is desirably about 800° C. or more and less than about 950° C. The annealing atmosphere is desirably a wet hydrogen nitrogen atmosphere or a wet hydrogen argon atmosphere.
A second objective is decarburization. If more than 0.005% carbon is contained in the product sheet, the iron loss degrades. The carbon content is therefore desirably reduced to 0.005% or less.
A third objective is to form a subscale made up of an internal oxidation layer of SiO2 which is the raw material of the base film mainly composed of forsterite. If the upstream-stage temperature of decarburization annealing is less than 800° C., oxidation reaction and decarburization reaction do not progress sufficiently, and necessary oxidation and decarburization cannot be completed.
After the decarburization/primary recrystallization annealing, an annealing separator mainly composed of magnesia (MgO) is applied to the surface of the steel sheet. Here, magnesium sulfate is added to the annealing separator mainly composed of MgO, in order to improve the magnetic property by the sulfurization treatment of increasing the amount of S in the steel substrate after the primary recrystallization annealing and before the completion of secondary recrystallization.
If the additive amount of magnesium sulfate is less than 2.0%, the magnetic property improving effect is insufficient. If the additive amount of magnesium sulfate is more than 15.0%, the grain growth is suppressed excessively, and the magnetic property improving effect is insufficient and also the formation of the base film is adversely affected.
The expression “mainly composed of magnesia” in this embodiment means that 50% or more magnesia is contained in the annealing separator. Sub-components such as Na2S2O3 and TiO2 may be added to the annealing separator in small amounts, according to conventional methods.
After this, secondary recrystallization annealing is performed. During the secondary recrystallization annealing, magnesium sulfate decomposes and exerts the sulfurization effect, thus realizing crystal texture highly aligned with the Goss orientation. Favorable magnetic property can be obtained in this way.
The secondary recrystallization annealing is effectively performed by diffusing S into the steel substrate with a heating rate of 30° C./H or less, as disclosed in JP 4321120 B. The annealing atmosphere may be any of N2, Ar, and mixed gas thereof. Here, H2 is not used as atmosphere gas until the completion of secondary recrystallization. This is because S in the annealing separator goes out of the system as H2S (gas), causing lower sulfurization effect especially in the coil edges.
After the secondary recrystallization annealing, an insulating coating is further applied to the surface of the steel sheet and baked. The type of the insulating coating is not particularly limited, and may be any conventionally well-known insulating coating. For example, a method of applying an application liquid containing phosphate-chromate-colloidal silica described in JP S50-79442 A and JP S48-39338 A to the steel sheet and baking it to also perform flattening annealing is preferable.
Flattening annealing is then performed. This flattening annealing is important in this embodiment.
The flattening annealing temperature needs to be 830° C. or more. If the flattening annealing temperature is less than 830° C., strain for shape adjustment remains, which decreases the iron loss in the TD direction and simultaneously degrades the iron loss in the RD direction. The iron loss in the TD direction for preventing degradation in the iron loss in the RD direction in the product sheet is 1.60 W/kg or more.
Moreover, 0.30% or more hydrogen needs to be introduced into the flattening annealing atmosphere. If the hydrogen partial pressure in the atmosphere is less than 0.30%, the coating film tension decreases, and the magnetizing force in the TD direction decreases. This results in higher degradation of transformer core loss due to the application of strain associated with processing into a transformer. To reduce the iron loss degradation caused by the application of strain associated with processing into a transformer and improve the transformer core loss, the magnetizing force when exciting the product sheet to 1.0 T in the TD direction needs to be 200 A/m or more.
A continuously cast slab having a composition containing C: 0.03%, Si: 3.5%, Mn: 0.08%, sol.Al: 75 ppm, N: 45 ppm, S: 30 ppm, Se: 1 ppm, O: 9 ppm, P: 0.06%, and Sb: 0.10% with the balance being Fe and incidental impurities was reheated to 1230° C., and then hot rolled to obtain a hot rolled sheet of 2.5 mm in sheet thickness. The hot rolled sheet was then hot band annealed at 1050° C. for 10 s, and subsequently cold rolled at 200° C. to a sheet thickness of 0.27 mm. The cold rolled sheet was then subjected to primary recrystallization annealing also serving as decarburization at 850° C. for 120 s in an atmosphere of H2: 55%, N2: 45%, and dew point: 55° C., with the heating rate from 500° C. to 700° C. being 20° C./s. The C content after this annealing was 30 ppm.
A sample was collected from the obtained primary recrystallization annealed sheet, and an annealing separator having MgO as a main ingredient and containing magnesium sulfate in the proportion shown in Table 2 was applied at 12.5 g/m2 to the sheet surface and dried. The sample was then subjected to secondary recrystallization annealing under the condition of heating to 800° C. at a heating rate of 15° C./h, heating from 800° C. to 850° C. at a heating rate of 2.0° C./h, retaining at 850° C. for 50 h, and then heating to 1160° C. at a heating rate of 5.0° C./h and soaking for 5 h. As the atmosphere gas, N2 gas was used up to 850° C., and H2 gas was used at 850° C. or more.
A treatment liquid containing phosphate-chromate-colloidal silica at a mass ratio of 3:1:3 was applied to the surface of the secondary recrystallization annealed sheet obtained under the aforementioned condition, and subsequently flattening annealing was performed under the condition shown in Table 2.
The magnetic property of the obtained product sheet was then examined. The magnetic property was evaluated based on the magnetic flux density B8 when exciting the sheet at 800 A/m in the rolling direction and the iron loss W17/50 when exciting the sheet to 1.7 T at 50 Hz in an alternating magnetic field in the rolling direction, the magnetizing force (TD-H10) and iron loss (TD-W10) when exciting the sheet to 1.0 T at 50 Hz in the transverse direction, and the strain sensitivity.
The strain sensitivity was evaluated based on the change (ΔW) in iron loss W17/50 value when passing the sheet while pressing it by measuring rolls, which were made up of steel rolls of 100 mm in diameter and 50 mm in width, with a rolling reduction force of 1.5 MPa (15 kgf/cm).
Table 2 shows the obtained results. Magnetic flux density B8 of 1.94 T or more, iron loss W17/50 of 0.82 W/kg or less, and ΔW of 0.005 W/kg or less are regarded as excellent properties.
188
20.0
800
1.503
0
180
As is clear from Table 2, by using the material containing P and Sb in combination, applying the annealing separator mainly composed of MgO and containing 2.0% or more magnesium sulfate, and performing secondary recrystallization annealing according to the disclosure, favorable magnetic flux density was obtained. Moreover, by setting the flattening annealing temperature to 830° C. or more, the iron loss in the TD direction was 1.60 W/kg or more, resulting in favorable iron loss in the rolling direction. Further, by introducing 0.30% or more a hydrogen atmosphere into the flattening annealing atmosphere, the magnetizing force when exciting the sheet to 1.0 T in the transverse direction was ensured to be 200 A/m or more, as a result of which the iron loss degradation caused by the application of strain associated with processing into a transformer was reduced.
A continuously cast slab composed of various components shown in Table 3 was reheated to 1230° C., and then hot rolled to obtain a hot rolled sheet of 2.2 mm in sheet thickness. The hot rolled sheet was then hot band annealed at 1050° C. for 10 s, and subsequently cold rolled at 200° C. to a sheet thickness of 0.23 mm. The cold rolled sheet was then subjected to decarburization annealing at 850° C. for 120 s in an atmosphere of H2: 55%, N2: 45%, and dew point: 55° C., with the heating rate from 500° C. to 700° C. being 20° C./s. The C content after the decarburization annealing was 30 ppm.
A sample was collected from the decarburization annealed sheet, and an annealing separator having MgO as a main ingredient and containing magnesium sulfate in the proportion shown in Table 4 was applied at 12.5 g/m2 to the sheet surface and dried. The sample was then subjected to secondary recrystallization annealing under the condition of heating to 800° C. at a heating rate of 15° C./h, heating from 800° C. to 850° C. at a heating rate of 2.0° C./h, retaining at 850° C. for 50 h, and then heating to 1160° C. at a heating rate of 5.0° C./h and soaking for 5 h. As the atmosphere gas, N2 gas was used up to 850° C., and H2 gas was used at 850° C. or more.
A treatment liquid containing phosphate-chromate-colloidal silica at a mass ratio of 3:1:3 was applied to the surface of the secondary recrystallization annealed sheet obtained under the aforementioned condition, and subsequently flattening annealing was performed under the condition shown in Table 4.
The magnetic property of the obtained product sheet was then examined. The method of evaluating the magnetic property is the same as that in Example 1.
Table 4 shows the obtained results.
0.001
0.001
0.001
0.001
0.024
0.021
0.011
0.023
0.008
188
160
1.432
145
1.382
138
1.432
165
1.543
As is clear from Table 4, by using the material containing appropriate amounts of P and Sb in combination, applying the annealing separator having MgO as a main ingredient and containing 2.0% or more magnesium sulfate, performing secondary recrystallization annealing, and further applying an appropriate flattening annealing condition according to the disclosure, not only favorable magnetic flux density was obtained, but also iron loss degradation caused by the application of strain associated with processing into a transformer was reduced.