Abstract
Granules useful for highly thermal-conductive resin composition are provided. The Granules have a number average particle diameter of 0.5 to 5 mm, obtained by granulating fibers mainly containing fibers selected from alumina fibers and carbon fibers, wherein the fibers to be granulated have a number average fiber diameter of 1 to 50 μm.
Claims
- 1. A granule having a number average particle diameter of 0.5 to 5 mm and comprising fibers, wherein the fibers have a number average fiber diameter of 1 to 50 μm and are selected from a group consisting of carbon fibers and alumina fibers mainly containing alumina.
- 2. The granule according to claim 1, wherein the fibers to be granulated have a bulk density of 0.2 to 1 g/cm3.
- 3. The granule according to claim 1 or 2, wherein the granule is a granule obtained by granulating the fibers while stirring.
- 4. An agent comprising the granule according to claim 1 or 2.
- 5. A resin composition comprising the granule according to claim 1 and a resin selected from a thermosetting resin and a thermoplastic resin.
- 6. The resin composition according to claim 5, which comprises 10 to 300 parts by volume of the granule on the basis of 100 parts by volume of the thermosetting resin.
- 7. The resin composition according to claim 5, which comprises 10 to 100 parts by volume of the granule on the basis of 100 parts by volume of the thermoplastic resin.
- 8. The resin composition according to claim 5, wherein the resin is a thermoplastic resin.
- 9. The resin composition according to claim 8, wherein the thermoplastic resin is polyphenylene sulfide.
- 10. The resin composition according to claim 8, wherein the thermoplastic resin is a liquid crystal polyester.
- 11. The resin composition according to claim 10, wherein the liquid crystal polyester has a flow-beginning temperature of not less than 280° C.
- 12. The resin composition according to claim 10, wherein the liquid crystal polyester comprises:
30 to 80% by mol of repeating structural unit derived from p-hydroxybenzoic acid and/or 2-hydroxy-6-naphthoic acid;10 to 35% by mol of repeating structural unit derived from hydroquinone and/or 4,4′-dihydroxybiphenyl; and10 to 35% by mol of repeating structural unit derived from at least one compound selected from the group consisting of terephthalic acid, isophthalic acid and 2,6-naphthalenedicarboxylic acid;on the basis of 100% by mol of the total amounts of the repeating structural units that constructing the liquid crystal polyester.
- 13. A molded article obtainable by molding the resin composition according to any of claims 5, 9 and 10.
Priority Claims (3)
Number |
Date |
Country |
Kind |
2006-080240 |
Mar 2006 |
JP |
national |
2006-267176 |
Sep 2006 |
JP |
national |
2006-298612 |
Nov 2006 |
JP |
national |